CN104911459A - Preparation method of wear-resisting steel main cutting board for excavator - Google Patents
Preparation method of wear-resisting steel main cutting board for excavator Download PDFInfo
- Publication number
- CN104911459A CN104911459A CN201510222993.1A CN201510222993A CN104911459A CN 104911459 A CN104911459 A CN 104911459A CN 201510222993 A CN201510222993 A CN 201510222993A CN 104911459 A CN104911459 A CN 104911459A
- Authority
- CN
- China
- Prior art keywords
- resisting steel
- wear
- excavator
- preparation
- main cutting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of a wear-resisting steel main cutting board for an excavator; the wear-resisting steel main cutting board is obtained by smelting the following raw materials by the weight percentage: 2.2-2.5% of C, 8.5-11% of V, 5-6.5% of Cr, 2-3% of Ni, 1.5-2.5% of B, 0.8-1.1% of W, 0.6-0.8% of Si, and the balance Fe, wherein the content of an impurity P is not more than 0.03%, and the content of an impurity S is not more than 0.02%. The wear-resisting steel main cutting board prepared by the method has the advantages of good hardness, good toughness and excellent wear resistance.
Description
Technical field
The present invention relates to the preparation method of a kind of excavator wear resisting steel operator plate.
Background technology
Excavator is one of engineering machinery main in earthwork, wearing and tearing are one of major ways causing this kind of machinery operator blackboard newspaper useless, in use not only to be subject to the strong wear of the abrasive particles such as sandstone, but also the intense impact of large stone will be subject to, therefore, when select materials, need hardness and the toughness of considering material, to reduce wearing and tearing and the fracture of material.
Summary of the invention
The technical problem to be solved in the present invention overcomes existing defect, provides the preparation method of a kind of excavator wear resisting steel operator plate.
In order to solve the problems of the technologies described above, the invention provides following technical scheme:
A kind of preparation method of excavator wear resisting steel operator plate, the raw material melting of consumption as following weight percent obtains the operator of described wear resisting steel plate: C 2.2 ~ 2.5%, V 8.5 ~ 11%, Cr 5 ~ 6.5%, Ni 2 ~ 3%, B 1.5 ~ 2.5%, W 0.8 ~ 1.1%, Si 0.6 ~ 0.8%, surplus is Fe, wherein, impurity P≤0.03%, impurity S≤0.02%.
Further, the weight percent of described raw material is as follows: C 2.3 ~ 2.5%, V 8.5 ~ 11%, Cr 6 ~ 6.5%, Ni 2.5 ~ 3%, B 1.5 ~ 2%, W 1 ~ 1.1%, Si 0.7 ~ 0.8%, and surplus is Fe, impurity P≤0.03%, impurity S≤0.02%.
Operate compared with plate with the wear resisting steel of existing excavator, wear resisting steel operator plate prepared by the inventive method can significantly improve hardness and the toughness of material, alleviates the wearing and tearing of knife plate.
Embodiment
Below the preferred embodiments of the present invention are described, should be appreciated that preferred embodiment described herein is only for instruction and explanation of the present invention, is not intended to limit the present invention.
embodiment 1
Raw material is by feeding into stove containing following weight percentage proportioning: C 2.2%, V 9%, Cr 5%, Ni 2%, B 2.5%, W 0.8%, Si 0.6%, surplus are Fe, melting, cast molding, obtains described wear resisting steel operator plate.Phosphorus, sulphur are inevitable impurity, should control P≤0.03% in final finished, S≤0.02%.
The hardness of described wear resisting steel operator plate is 70.4HRC, and impelling strength is 42J/cm
2.
embodiment 2
Raw material is by feeding into stove containing following weight percentage proportioning: C 2.3%, V 8.5%, Cr 6%, Ni 2.5%, B 1.5%, W 1.1%, Si 0.7%, surplus are Fe, melting, cast molding, obtains described wear resisting steel operator plate.Phosphorus, sulphur are inevitable impurity, should control P≤0.03% in final finished, S≤0.02%.
The hardness of described wear resisting steel operator plate is 76.1HRC, and impelling strength is 64J/cm
2.
embodiment 3
Raw material is by feeding into stove containing following weight percentage proportioning: C 2.5%, V 11%, Cr 6.5%, Ni 3%, B 2%, W 1%, Si 0.8%, surplus are Fe, melting, cast molding, obtains wear resisting steel operator plate.Phosphorus, sulphur are inevitable impurity, should control P≤0.03% in final finished, S≤0.02%.
The hardness of described wear resisting steel operator plate is 78.4HRC, and impelling strength is 58J/cm
2.
Last it is noted that the foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, although with reference to previous embodiment to invention has been detailed description, for a person skilled in the art, it still can be modified to the technical scheme described in foregoing embodiments, or carries out equivalent replacement to wherein portion of techniques feature.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (2)
1. the excavator preparation method of wear resisting steel operator plate, the raw material melting of consumption as following weight percent obtains the operator of described wear resisting steel plate: C 2.2 ~ 2.5%, V 8.5 ~ 11%, Cr 5 ~ 6.5%, Ni 2 ~ 3%, B 1.5 ~ 2.5%, W 0.8 ~ 1.1%, Si 0.6 ~ 0.8%, surplus is Fe, wherein, impurity P≤0.03%, impurity S≤0.02%.
2. preparation method according to claim 1, it is characterized in that: the weight percent of described raw material is as follows: C 2.3 ~ 2.5%, V 8.5 ~ 11%, Cr 6 ~ 6.5%, Ni 2.5 ~ 3%, B 1.5 ~ 2%, W 1 ~ 1.1%, Si 0.7 ~ 0.8%, surplus is Fe, impurity P≤0.03%, impurity S≤0.02%.