CN104862709A - Steel material anticorrosion conditioning fluid - Google Patents
Steel material anticorrosion conditioning fluid Download PDFInfo
- Publication number
- CN104862709A CN104862709A CN201510207093.XA CN201510207093A CN104862709A CN 104862709 A CN104862709 A CN 104862709A CN 201510207093 A CN201510207093 A CN 201510207093A CN 104862709 A CN104862709 A CN 104862709A
- Authority
- CN
- China
- Prior art keywords
- parts
- steel material
- steel
- conditioning fluid
- sodium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to steel material anticorrosion conditioning fluid. The steel material anticorrosion conditioning fluid is formed by preparing following components comprising, in parts by weight, 12 parts to 16 parts of sodium nitrite, 22 parts to 35 parts of n-butyl alcohol, 12 parts to 15 parts of tetramethoxysilane, 9 parts to 15 parts of etidronic acid, 6 parts to 10 parts of edetic acid, 14 parts to 18 parts of ethylene glycol monomethyl ether, 6 parts to 8 parts of mica powder, 22 parts to 25 parts of sodium pyrophosphate, 3 parts to 7 parts of ammonium chloride, 7 parts to 10 parts of sodium allysulfonate, 9 parts to 15 parts of chloride 1-butyl-3-methylimidazole and 3 parts to 5 parts of potassium chloride. Steel material conditioning fluid forms a protection film on the surface of a steel material, the surface of the steel material has the good corrosive protection performance, and the processing method is simple.
Description
Technical field
The invention belongs to chemical processing agent field, be specifically related to a kind of steel fungicidal wash.
Background technology
Anticorrosion is exactly by taking various means, protects the metal of easy corrosion, reaches the object extending its work-ing life, usually adopt physical preservation, Chemical Preservation, the methods such as electrochemical anti-corrosive.The old paint film that usual metallic surface can have dust, greasy dirt, oxide skin, corrosion layer, pollutent, salt or get loose.Wherein oxide skin is more common but the easiest uncared-for part.Oxide skin is one deck compact oxidation layer produced when high-temperature steel forging forming, and attachment is relatively more firm usually, but it is then more crisp to compare iron and steel itself, and itself is negative electrode, can accelerate metallic corrosion.If do not remove the direct application of these materials, sticking power and the antiseptic power of whole coating will certainly be affected.The fungicidal wash cost of present use is high, and toxicity is stronger.
Summary of the invention
The object of this invention is to provide a kind of steel fungicidal wash, to favorable anti-corrosion effect after steel surface process, cost is low, and toxicity is low.
The present invention is achieved through the following technical solutions:
A kind of steel fungicidal wash, formulated by following component by weight: Sodium Nitrite 12-16 part, propyl carbinol 22-35 part, tetramethoxy-silicane 12-15 part, 1-Hydroxy Ethylidene-1,1-Diphosphonic Acid 9-15 part, ethylenediamine tetraacetic acid (EDTA) 6-10 part, ethylene glycol monomethyl ether 14-18 part, mica powder 6-8 part, trisodium phosphate 22-25 part, ammonium chloride 3-7 part, sodium allyl sulfonate 7-10 part, chlorination 1-butyl-3-Methylimidazole 9-15 part, Repone K 3-5 part.
Preferably, a kind of steel fungicidal wash, formulated by following component by weight: Sodium Nitrite 15 parts, propyl carbinol 28 parts, tetramethoxy-silicane 14 parts, 1-Hydroxy Ethylidene-1,1-Diphosphonic Acid 12 parts, ethylenediamine tetraacetic acid (EDTA) 8 parts, ethylene glycol monomethyl ether 15 parts, mica powder 8 parts, trisodium phosphate 24 parts, ammonium chloride 6 parts, sodium allyl sulfonate 9 parts, chlorination 1-butyl-3-Methylimidazole 12 parts, 4 parts, Repone K.
Treatment solution can be adjusted to the treatment solution that PH is 5.6-6 during use.
Beneficial effect of the present invention: steel treatment solution of the present invention can form protective membrane at steel surface; steel surface is made to have good anti-corrosion capability; treatment process is simple; after process, steel will normally use the lower protection against corrosion time to reach more than 3 years; and treatment agent cost provided by the invention is low; toxicity is low, applied widely, has and widely uses value.
Embodiment
Embodiment 1
A kind of steel fungicidal wash, formulated by following component by weight: Sodium Nitrite 16 parts, propyl carbinol 32 parts, tetramethoxy-silicane 14 parts, 1-Hydroxy Ethylidene-1,1-Diphosphonic Acid 15 parts, ethylenediamine tetraacetic acid (EDTA) 9 parts, ethylene glycol monomethyl ether 15 parts, mica powder 8 parts, trisodium phosphate 23 parts, ammonium chloride 6 parts, sodium allyl sulfonate 9 parts, chlorination 1-butyl-3-Methylimidazole 12 parts, 3 parts, Repone K.
Embodiment 2
A kind of steel fungicidal wash, formulated by following component by weight: Sodium Nitrite 15 parts, propyl carbinol 28 parts, tetramethoxy-silicane 14 parts, 1-Hydroxy Ethylidene-1,1-Diphosphonic Acid 12 parts, ethylenediamine tetraacetic acid (EDTA) 8 parts, ethylene glycol monomethyl ether 15 parts, mica powder 8 parts, trisodium phosphate 24 parts, ammonium chloride 6 parts, sodium allyl sulfonate 9 parts, chlorination 1-butyl-3-Methylimidazole 12 parts, 4 parts, Repone K.
Embodiment 3
A kind of steel fungicidal wash, formulated by following component by weight: Sodium Nitrite 13 parts, propyl carbinol 26 parts, tetramethoxy-silicane 12 parts, 1-Hydroxy Ethylidene-1,1-Diphosphonic Acid 12 parts, ethylenediamine tetraacetic acid (EDTA) 8 parts, ethylene glycol monomethyl ether 17 parts, mica powder 8 parts, trisodium phosphate 25 parts, ammonium chloride 5 parts, sodium allyl sulfonate 8 parts, chlorination 1-butyl-3-Methylimidazole 12 parts, 4 parts, Repone K.
Claims (2)
1. a steel fungicidal wash, it is characterized in that, formulated by following component by weight: Sodium Nitrite 12-16 part, propyl carbinol 22-35 part, tetramethoxy-silicane 12-15 part, 1-Hydroxy Ethylidene-1,1-Diphosphonic Acid 9-15 part, ethylenediamine tetraacetic acid (EDTA) 6-10 part, ethylene glycol monomethyl ether 14-18 part, mica powder 6-8 part, trisodium phosphate 22-25 part, ammonium chloride 3-7 part, sodium allyl sulfonate 7-10 part, chlorination 1-butyl-3-Methylimidazole 9-15 part, Repone K 3-5 part.
2. a kind of steel fungicidal wash according to claim 1, it is characterized in that, formulated by following component by weight: Sodium Nitrite 15 parts, propyl carbinol 28 parts, tetramethoxy-silicane 14 parts, 1-Hydroxy Ethylidene-1,1-Diphosphonic Acid 12 parts, ethylenediamine tetraacetic acid (EDTA) 8 parts, ethylene glycol monomethyl ether 15 parts, mica powder 8 parts, trisodium phosphate 24 parts, ammonium chloride 6 parts, sodium allyl sulfonate 9 parts, chlorination 1-butyl-3-Methylimidazole 12 parts, 4 parts, Repone K.