CN1039400A - The oil field preparation method of flocculation-inhibiter - Google Patents
The oil field preparation method of flocculation-inhibiter Download PDFInfo
- Publication number
- CN1039400A CN1039400A CN 89103016 CN89103016A CN1039400A CN 1039400 A CN1039400 A CN 1039400A CN 89103016 CN89103016 CN 89103016 CN 89103016 A CN89103016 A CN 89103016A CN 1039400 A CN1039400 A CN 1039400A
- Authority
- CN
- China
- Prior art keywords
- parts
- flocculation
- inhibiter
- oil field
- gained
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention contains the glue plant and amount of starch is a raw material so that the South China is resourceful, by alkalization, reactions such as carboxymethylation and sulfonation, introducing-COO
--CONH
2With-SO
3 -The chemical modification method of isoreactivity group etc. is produced the oil field that has flocculating and purifying and corrosion inhibition concurrently the flocculation-inhibiter of being made up of the derivative of materials such as saccharan, Mierocrystalline cellulose, xylogen and tannin.Adopt the medicament of this law preparation, in wastewater treatment process, can be by original flocculation agent of interpolation respectively and inhibiter, change into once and adding, not only saved the expense of medicament itself, and made water treatment process simplification, handled easily.Service life of equipment prolongs.
Description
The invention belongs to a kind of natural polymer chemical modification method.
Oil-containing wastewater is handled and is used various medicaments such as flocculation, inhibition respectively.In recent years, the developing direction that oil field waste is handled medicament is high effect, and is multi-functional, but the preparation difficulty of multifunctional water treating agent is very big.The patent that relates to flocculation and inhibition aspect has:
A kind of quaternary ammonium thiazine compounds is disclosed at US-713666 and US-4113709, a kind of polyelectrolyte of nitrogen atom is disclosed at US-436419, a kind of siliceous aminomethyl phosphonic acid salt compound is disclosed at US-3716569, disclose two kinds of polyquaternium compounds at GB-2126579 and US-4581058, their purpose all is the multi-functional water conditioner of preparation.Though above-mentioned water conditioner both can be used as flocculation agent and had used, can be used as inhibiter again and use, but they are synthetic medicament, see the molecular weight all lower (less than 60,000) of these organic medicaments from report, so the flocculating and purifying effect is undesirable, and can judge that being not easy dosing time realizes flocculation.The inhibition double effects.Do not see that up to now commodity flocculation-inhibiter comes out.
The present invention passes through the research to multiple different components action function in the natural polymer, the mutual synergy in the grasp oil field waste treating processes between flocculation and the corrosion inhibitor.In the oil field waste treating processes, once add a kind of flocculation-inhibiter that forms through chemical modification with natural polymer, just can demonstrate good purification and corrosion mitigating effect.Up to now, do not see similarly and successfully report, through the database of international online retrieval centre retrieves " United States Patent (USP) " (nineteen fifty~now), " Chinese patent " (1985~now) and " world patent " (1967~now), do not find that any document relevant with the present invention put down in writing (see Guangdong Province's scientific information research testimonial material and last machine printout).
The objective of the invention is to propose a kind of preparation and have the novel method of the oil field of flocculation and inhibition double effects concurrently with water conditioner.Adopt the water conditioner of this method preparation, strengthen solid-liquid separation and slow down equipment and Corrosion of Pipeline as long as dosing time in water treatment process, just can play, thereby reach the simplification water treatment process, minimizing equipment, handled easily is saved purposes such as water conditioner.
Purpose of the present invention can reach by following measure:
Contain the glue plant and amount of starch is a main raw material so that the South China is resourceful, by alkalization, carboxymethylation and sulfonation reaction, introducing-Coo
-,-CoNH
2And So
3 -The chemical modification method of isoreactivity group etc. is produced the oil field that has flocculating and purifying and corrosion inhibition concurrently the flocculation-inhibiter of being made up of the derivative of materials such as saccharan, Mierocrystalline cellulose, xylogen and tannin.
Its principal reaction mechanism is seen following reaction formula:
In the formula (R(OH)
3)
nRepresent natural polymers such as Mierocrystalline cellulose, saccharan.
Represent xylogen.
Accompanying drawing is the preparation technology schematic flow sheet of oil field with flocculation-inhibiter.Its preparation method comprises following four steps:
1. alkalization
Take by weighing and contain glue plant powder and 100 parts of starch (accounting for 3~10%) (by weight, as follows), 130~210 parts of adding industrial spirit, add 37~49 parts in caustic soda (NaoH) (using earlier water dissolution) after moistening 3 minutes, fully stirring also, temperature control reacted 30 minutes at 30 ℃~38 ℃
2. carboxymethylation:
Take by weighing monochloroacetic acid (ClCH
2CooH) 40~55 parts, with adding in the material of step 1 gained after the water dissolution, be warming up to 56 ℃~66 ℃ then, and carried out stirring reaction 1 hour, products therefrom is standby,
3. sulfonation:
Take by weighing Sodium Persulfate (Na
2S
2O
8) 28~58 parts, S-WAT (Na
2SO
3) 32~62 parts and iron trichloride (FeCl
3) 0.5~8 part be dissolved in water, in the material with its aqueous solution impouring step 2 gained, stir then, be warming up to 50 ℃~65 ℃ simultaneously, insulation reaction 1 hour,
4. slaking:
With the product of step 3 gained, add 20~50 parts of Sunmorl N 60Ss, 0.1~1 part in 5~8 parts of partially hydrolyzed polyacrylamides and formaldehyde, temperature control stirs slaking 3 hours under 40 ℃~45 ℃ situations then, obtains finished product oil field flocculation-inhibiter.
The oil field that method makes in the employing is pale brown look colloid with flocculation-inhibiter, water-soluble is good, the relative viscosity of 0.5% aqueous solution is 6.8~7.2, pH value 8.0~8.4, product carboxyl substituted degree 55~65%, sulfonic group substitution value 48~62%, the molecular weight decomposition range is wide, greater than 1,500,000 account for approximately 32%, molecular weight is 5~1,000,000 to account for approximately 38%, molecular weight accounts for about 30% below 50,000.
The oil field with the chemical structural formula of the main component of flocculation-inhibiter is:
The oil field will be described in further detail in conjunction with following embodiment with the preparation method of flocculation-inhibiter:
1. alkalization:
Take by weighing main raw material Chinese bandoline wood powder 95 gram and starch 5 grams, add 150 milliliters of industrial spirit, add concentration after moistening 3 minutes and be 120 milliliters of 30% alkali lye (NaoH), fully stirring also, temperature control reacted 30 minutes at 30~38 ℃.
2. carboxymethylation
It is 50% monochloroacetic acid (ClCH that the material of step 1 gained is added concentration
2CooH) 84 milliliters, be warming up to 56 ℃~66 ℃ then, and carried out stirring reaction 1 hour, products therefrom is standby,
3. sulfonation:
Take by weighing Sodium Persulfate (Na
2S
2O
8) 40 the gram, S-WAT (Na
2SO
3) 36 gram and iron trichloride (FeCl
3) 0.5 gram, water-soluble 50 milliliters, stirring and dissolving in the material of its aqueous solution impouring step 2 gained, stirs then, is warming up to 60 ℃~65 ℃ simultaneously, insulation reaction 1 hour,
4. slaking:
With the product of step 3 gained, add 1 milliliter in Sunmorl N 60S 42 gram (water-soluble 100 milliliters) partially hydrolyzed polyacrylamides, 7 grams and formaldehyde, temperature control stirs slaking 3 hours under 40~45 ℃ of situations then, obtains finished product oil field flocculation-inhibiter.
The present invention compared with prior art has following advantage:
1. the present invention adopts the method for natural polymer chemical modification to prepare used in oil field for flocculated-etching-retarding agent, fully developed each different component in the natural plants, preparation process need not separated, the complicated procedures of forming such as purification, thereby equipment investment is few, flow process is simple, easy to operate, and the medicament relative cost is low.
2. this law is carried out graft reaction, introducing-COO according to the requirement of flocculation and inhibition difference in functionality simultaneously to each component of different molecular weight in the raw material-、-SO
- 3、-CONH
2The isoreactivity group makes agent molecule amount size suitably, and the active group ratio is appropriate, the macromolecular derivatives that contains carboxyl and sulfonic group etc., to purifying, it is effective especially to remove ultramicro powder, and than the compounds such as carboxyl, sulfonic group that contain of small-molecular weight inhibition is had good result.
3. the multifunctional water treating agent that has flocculate and clarify and inhibition concurrently that is made by this law only needs once to add purification and the corrosion inhibition that can play oil field waste in water treatment process. After oil-polluted water adds the used in oil field for flocculated-etching-retarding agent of 2~3ppm, process waste water quality and reach reinjection standard, to slowing down pipeline, the resultant effect of equipment corrosion is good (test situation: rotary hanging plate 5,10,20,30,40 days, the test strip pitting factor is stabilized in 0.32mmpy, and blank rotating hanging test, the test piece pitting factor reaches 2.53mmpy). Medicament also has corresponding effect to other industrial wastewaters.
4. in the disposing polluted water in oil process, adopt the flocculation-corrosion inhibiter of this law preparation, changed into once by two kinds of medicaments of original respectively interpolation and to add, not only saved the expense of medicament itself, and water treatment process is simplified, Energy Intensity Reduction, service life of equipment prolongs, thereby has improved the economic benefit of wastewater treatment. The medicament retention is good.
Claims (1)
1, a kind of oil field preparation method of flocculation-inhibiter, the change of the main ingredient of this medicament
It is characterized in that adopting the method for natural polymer chemical modification, the preparation method comprises following four steps:
1. alkalization
Take by weighing and contain 100 parts of glue plant powder and starch (accounting for 3%~7%) (by weight, as follows), add 130~210 parts of industrial spirit, add abundant stirring of 37~49 parts in caustic soda (NaOH) (using earlier water dissolution) and temperature control after moistening 3 minutes at 30 ℃~38 ℃, reacted 30 minutes
2. carboxymethylation
Take by weighing monochloroacetic acid (ClCH
2COOH) 40~55 parts, with adding in the material of step 1 gained after the water dissolution, be warming up to 56 ℃~66 ℃ then, and carry out stirring reaction 1 and advance for a short time, products therefrom is standby,
3. sulfonation
Take by weighing Sodium Persulfate (Na
2S
2O
8) 28~58 parts, 32~62 parts of S-WATs (Na2SO3) and iron trichloride (FeCl
3) 0.5~8 part, be dissolved in water, in the material with its aqueous solution impouring step 2 gained, stir then, be warming up to 50 ℃~65 ℃ simultaneously, insulation reaction 1 hour,
4. slaking
With the product of step 3 gained, add 0.1~1 part in 5~8 parts of 20~50 parts of partially hydrolyzed polyacrylamides of Sunmorl N 60S and formaldehyde, temperature control stirs slaking 3 hours down at 40 ℃~45 ℃ then, obtains finished product oil field flocculation-inhibiter.