CN102912522A - Elastic fabric taking biology base PDT as raw material and production method of elastic fabric - Google Patents
Elastic fabric taking biology base PDT as raw material and production method of elastic fabric Download PDFInfo
- Publication number
- CN102912522A CN102912522A CN2012104514861A CN201210451486A CN102912522A CN 102912522 A CN102912522 A CN 102912522A CN 2012104514861 A CN2012104514861 A CN 2012104514861A CN 201210451486 A CN201210451486 A CN 201210451486A CN 102912522 A CN102912522 A CN 102912522A
- Authority
- CN
- China
- Prior art keywords
- fiber
- elastic fabric
- pdt
- raw material
- bio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an elastic fabric taking biology base PDT as the raw material and a production method of the elastic fabric. The elastic fabric is formed by weaving of warp yarns and weft yarns, wherein the warp yarns and the weft yarns are formed by weaving of synthetic fiber, and the mass percentages of the raw material are as follows: 10-40% of biology base PDT, 5-20% of spandex fiber, 1-5% of lycra fiber and the balance of cross bamboo charcoal polyester fibre, or 20%-30% of the biology base PDT (25% preferably), 8-15% of the spandex fiber (10% preferably), and 2-4% of the lycra fiber (3% preferably). The raw materials provided by the invention come from biological materials, so that the energy is saved, the environment pollution is reduced, and the low-carbon environment-friendly requirement is met; the elastic fabric containing the biology base PDT fiber is provided so that the fabric is closer to a human body and has good comfort; and the fabric contains the spandex fiber and the lycra fiber so as to improve the elasticity of the fabric.
Description
Technical field
The present invention relates to the fabric technical field, specifically, is a kind of elastic fabric take bio-based PDT as raw material.
Background technology
Exploitation and the application of PDT bio-based polyester---with bio-based ethylene glycol directly as the raw material of polyester three autoclave apparatus for continuous polycondensation at 1000 ton/years, carry out esterification with the p-phthalic acid, again polycondensation, make than the existing more excellent novel polyphenyl dioctyl phthalate component of the manying binary alcohol esters PDT polyester of polyester, and the processed and applied of successful confession downstream POY, FDY, DTY is in woven and knit fabric, and excellent spinning properties and dyeability result from that to contain mass fraction in the bio-based ethylene glycol be 2.5% multicomponent binary alcohols such as propylene glycol, butanediol and pentanediol.Petroleum law PET polyester 99.5%EG, (petroleum law)+PTA → PET, (Polyethylene Terephthalate) polyphenyl dioctyl phthalate second diester petroleum law PTT polyester, (CORTERRA:Brand by SHELL) PDO, (petroleum law)+PTA → PET, (Polytrimethylene Terephthalate) polyphenyl dioctyl phthalate propylene diester bioanalysis PTT polyester, (Sorona: Brand by Du Pont) PDO, (by corn with bioanalysis)+PTA → PTT, (Poly trimethylene Terephthalate) polyphenyl dioctyl phthalate propylene diester
Socorna is the trade name of day a kind of novel PDT (bio-based PET) fiber, yarn and the textiles in sea.
Summary of the invention
The object of the invention is to overcome the deficiencies in the prior art, a kind of elastic fabric and production method thereof take bio-based PDT as raw material is provided.
The objective of the invention is to be achieved through the following technical solutions:
A kind of elastic fabric take bio-based PDT as raw material is formed by warp thread and weft yarn braiding;
Described warp thread and weft yarn are formed by the blended fiber braiding, and its material quality percentage is:
Bio-based PDT fiber 10~40%
Spandex fibre 5~20%
Lycra fiber 1~5%
Cross bamboo carbon dacron fiber surplus.
The mass percent of described bio-based PDT fiber is 20~30%, most preferably is 25%.
The mass percent of described spandex fibre is 8~15%, most preferably 10%; Spandex fibre is altogether by the two different propylhomoserin enzymes of fragrance and the block copolymer that contains the polyester segment of hydroxyl (being called for short the polyester-type spandex).
The mass percent of described Lycra fiber is 2~4%, most preferably 3%.
Compared with prior art, good effect of the present invention is:
(1) raw material sources biomaterial of the present invention, energy savings reduces the pollution of environment, meets the requirement of low-carbon environment-friendly;
(2) the present invention proposes the elastic fabric of the PDT fiber of the bio-based contain, makes fabric more get close to human body, and comfort is better;
(3) the present invention contains spandex fibre and Lycra fiber, to increase the elasticity of fabric.
The specific embodiment
Below provide the present invention a kind of take bio-based PDT as raw material elastic fabric and the specific embodiment of production method.
Embodiment 1
A kind of elastic fabric take bio-based PDT as raw material is formed by warp thread and weft yarn braiding;
Described warp thread and weft yarn are formed by the blended fiber braiding, and its material quality percentage is:
Bio-based PDT fiber 10%
Spandex fibre 5%
Lycra fiber 1%
Cross bamboo carbon dacron fiber 74%.
Embodiment 2
A kind of elastic fabric take bio-based PDT as raw material is formed by warp thread and weft yarn braiding;
Described warp thread and weft yarn are formed by the blended fiber braiding, and its material quality percentage is:
Bio-based PDT fiber 20%
Spandex fibre 8%
Lycra fiber 2%
Cross bamboo carbon dacron fiber 70%.
Embodiment 3
A kind of elastic fabric take bio-based PDT as raw material is formed by warp thread and weft yarn braiding;
Described warp thread and weft yarn are formed by the blended fiber braiding, and its material quality percentage is:
Bio-based PDT fiber 25%
Spandex fibre 10%
Lycra fiber 3%
Cross bamboo carbon dacron fiber 62%.
Embodiment 4
A kind of elastic fabric take bio-based PDT as raw material is formed by warp thread and weft yarn braiding;
Described warp thread and weft yarn are formed by the blended fiber braiding, and its material quality percentage is:
Bio-based PDT fiber 30%
Spandex fibre 15%
Lycra fiber 4%
Cross bamboo carbon dacron fiber 51%.
Embodiment 5
A kind of elastic fabric take bio-based PDT as raw material is formed by warp thread and weft yarn braiding;
Described warp thread and weft yarn are formed by the blended fiber braiding, and its material quality percentage is:
Bio-based PDT fiber 40%
Spandex fibre 20%
Lycra fiber 5%
Cross bamboo carbon dacron fiber 35%.
Embodiment 6
A kind of elastic fabric take bio-based PDT as raw material is formed by warp thread and weft yarn braiding;
Described warp thread and weft yarn are formed by the blended fiber braiding, and its material quality percentage is:
Bio-based PDT fiber 30%
Spandex fibre 15%
Lycra fiber 1%
Cross bamboo carbon dacron fiber 54%.
Embodiment 7
A kind of elastic fabric take bio-based PDT as raw material is formed by warp thread and weft yarn braiding;
Described warp thread and weft yarn are formed by the blended fiber braiding, and its material quality percentage is:
Bio-based PDT fiber 15%
Spandex fibre 10%
Lycra fiber 5%
Cross bamboo carbon dacron fiber 70%.
The above only is preferred embodiment of the present invention; should be pointed out that for those skilled in the art, without departing from the inventive concept of the premise; can also make some improvements and modifications, these improvements and modifications also should be considered within the scope of protection of the present invention.
Claims (7)
1. the elastic fabric take bio-based PDT as raw material is characterized in that, described fabric is formed by warp thread and weft yarn braiding; Described warp thread and weft yarn are formed by the blended fiber braiding, and its material quality percentage is:
Bio-based PDT fiber 10~40%
Spandex fibre 5~20%
Lycra fiber 1~5%
Cross bamboo carbon dacron fiber surplus.
2. a kind of elastic fabric take bio-based PDT as raw material as claimed in claim 1 is characterized in that, the mass percent of described bio-based PDT fiber is 20~30%.
3. a kind of elastic fabric take bio-based PDT as raw material as claimed in claim 2 is characterized in that, the mass percent of described bio-based PDT fiber is 25%.
4. a kind of elastic fabric take bio-based PDT as raw material as claimed in claim 1 is characterized in that, the mass percent of described spandex fibre is 8~15%.
5. a kind of elastic fabric take bio-based PDT as raw material as claimed in claim 4 is characterized in that, the mass percent of described spandex fibre is 10%.
6. a kind of elastic fabric take bio-based PDT as raw material as claimed in claim 1 is characterized in that, the mass percent of described Lycra fiber is 2~4%.
7. a kind of elastic fabric take bio-based PDT as raw material as claimed in claim 6 is characterized in that, the mass percent of described Lycra fiber is 3%.