CN101885599A - 使用煤矸石炉渣替代部分天然砂的预拌混凝土 - Google Patents

使用煤矸石炉渣替代部分天然砂的预拌混凝土 Download PDF

Info

Publication number
CN101885599A
CN101885599A CN2009100512564A CN200910051256A CN101885599A CN 101885599 A CN101885599 A CN 101885599A CN 2009100512564 A CN2009100512564 A CN 2009100512564A CN 200910051256 A CN200910051256 A CN 200910051256A CN 101885599 A CN101885599 A CN 101885599A
Authority
CN
China
Prior art keywords
coal gangue
water
gangue slag
slag
mixed concrete
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2009100512564A
Other languages
English (en)
Inventor
李丽霞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CMTCC Shanghai Shisanye Construction Co Ltd
Original Assignee
CMTCC Shanghai Shisanye Construction Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CMTCC Shanghai Shisanye Construction Co Ltd filed Critical CMTCC Shanghai Shisanye Construction Co Ltd
Priority to CN2009100512564A priority Critical patent/CN101885599A/zh
Publication of CN101885599A publication Critical patent/CN101885599A/zh
Pending legal-status Critical Current

Abstract

一种使用煤矸石炉渣代替部分天然砂的预拌混凝土，其特征在于，其组分按重量百分比为：普通42.5级水泥8.5～10％，煤矸石炉渣8～10％，砂石67～71％，减水剂0.15～0.2％，水7.5～7.6％，掺合料余量。本发明的使用煤矸石炉渣代替部分天然砂的预拌混凝土具有增加废弃物的利用途径，节约能源、保护耕地、改善环境；能达到泵送施工要求和普通混凝土C 30强度，以及经济效益、社会效益十分显著的优点。

Description

使用煤矸石炉渣替代部分天然砂的预拌混凝土
技术领域
本发明属混凝土领域，特别是涉及使用工业废渣煤矸石炉渣代替天然砂的预拌混凝土。
背景技术
煤矸石是煤炭开采和洗选加工过程中产生的固体废弃物，是目前我国排放量最大的工业固体废弃物之一。开展煤矸石炉渣再利用技术的研究，对节约能源、保护耕地、改善环境都具有重要意义。使用煤矸石作为燃烧物体，燃烧后有效成分挥发，收集到的剩余废弃物即为煤矸石炉渣。考虑选择煤矸石炉渣代替部分天然砂用于混凝土进行试验研究、开发与应用，一方面增加废弃物的利用途径，另一方面也能够缓解混凝土日趋紧张的原材料货源，减少对天然材料的使用量。
煤矸石炉渣主要矿物组分在混凝土中具有稳定性，不会再发生化学反应，煤矸石炉渣形状似黄砂颗粒；多由5mm以下的颗粒组成，能够满足建筑用砂标准中的要求，可以在普通混凝土中用做细集料。因此，如何寻求廉价的煤矸石炉渣代替部分天然砂用于混凝土是目前建筑材料研制中急需解决的问题。
发明内容
本发明的目的，在于提出一种在普通混凝土中的天然砂用量以煤矸石炉渣替代30％，以聚羧酸高效减水剂作为外加剂，达到普通混凝土C30的强度、和易性等技术要求的使用煤矸石炉渣代替部分天然砂的预拌混凝土。
为实现上述目的，本发明的技术解决方案是：
一种使用煤矸石炉渣代替部分天然砂的预拌混凝土，其特征在于，其组分按重量百分比为：
普通42.5级水泥    8.5～10％
煤矸石炉渣        8～10％
砂石              67～71％
减水剂            0.15～0.2％
水                7.5～7.6％
掺合料            余量。
本发明的使用煤矸石炉渣代替部分天然砂的预拌混凝土还可以采用以下的技术措施来进一步实现。
前述的预拌混凝土，其中所述煤矸石炉渣是粒径为5mm以下的煤矸石烧结渣颗粒；所述砂石主要由细度2.3的中砂34％～37(wt)％和5mm～25mm的碎石63～66(wt)％组成。
前述的预拌混凝土，其中所述掺合料为粉煤灰和矿粉，所述粉煤灰为F类II级粉煤灰，其细度为12％，需水量比为101％；所述矿粉为高炉矿渣微粉。
前述的预拌混凝土，其中所述减水剂为聚羧酸高效减水剂，减水率大于25％。
采用上述技术方案后，本发明的使用煤矸石炉渣代替部分天然砂的预拌混凝土具有以下优点：
1.增加废弃物的利用途径，节约能源、保护耕地、改善环境。
2.用掺量为30％的煤矸石烧结渣替代天然砂，能达到泵送施工要求以及普通混凝土C30强度要求。
3.经济效益和社会效益十分显著。
具体实施方式
以下结合实施例对本发明作更进一步说明。
实施例1
一种煤矸石炉渣代替部分天然砂的预拌混凝土，由强度等级42.5水泥9(wt)％，煤矸石10(wt)％，细度2.3的中沙23(wt)％，5mm～25mm的碎石46(wt)％，高效减水剂0.2(wt)％，水7.6(wt)％，煤灰粉(wt)2％和矿粉2.2(wt)％搅拌混合而成。
实施例2
一种煤矸石炉渣代替部分天然砂的预拌混凝土，由强度等级42.5水泥10(wt)％，煤矸石9(wt)％，细度2.3的中沙26(wt)％，5mm～25mm的碎石44(wt)％，高效减水剂0.15(wt)％，水7.5(wt)％，煤灰粉1.5(wt)％和矿粉1.85(wt)％搅拌混合而成。
实施例3
一种煤矸石炉渣代替部分天然砂的预拌混凝土，由强度等级42.5水泥8.5(wt)％，煤矸石8(wt)％。细度2.3的中沙25(wt)％，5mm～25mm的碎石44(wt)％，高效减水剂0.15(wt)％，水7.6(wt)％，煤灰粉3(wt)％和矿粉3.75(wt)％搅拌混合而成。
最后的产品坍落度、凝结时间及强度要求按下表进行控制。
Figure B2009100512564D0000031
以上实施例仅供说明本发明之用，而非对本发明的限制，有关技术领域的技术人员，在不脱离本发明的精神和范围的情况下，还可以作出各种变换或变化。因此，所有等同的技术方案也应该属于本发明的范畴，应由各权利要求限定。

Claims (4)

1.一种使用煤矸石炉渣代替部分天然砂的预拌混凝土，其特征在于，其组分按重量百分比为：
普通42.5级水泥    8.5～10％
煤矸石炉渣        8～10％
砂石              67～71％
减水剂            0.15～0.2％
水                7.5～7.6％
掺合料            余量。
2.如权利要求1所述的预拌混凝土，其特征在于，所述煤矸石炉渣是粒径为5mm以下的煤矸石烧结渣颗粒；所述砂石主要由细度2.3的中砂34％～37(wt)％和5mm～25mm的碎石63～66(wt)％组成。
3.如权利要求1所述的预拌混凝土，其特征在于，所述掺合料为粉煤灰和矿粉，所述粉煤灰为F类II级粉煤灰，其细度为12％，需水量比为101％；所述矿粉为高炉矿渣微粉。
4.如权利要求1所述的预拌混凝土，其特征在于，所述的减水剂为聚羧酸高效减水剂，减水率大于25％。
CN2009100512564A 2009-05-14 2009-05-14 使用煤矸石炉渣替代部分天然砂的预拌混凝土 Pending CN101885599A (zh)