AU2006200826A1 - A stable solid state raman laser and a method of operating same - Google Patents

Description

S&FRef: 512107AUD1

AUSTRALIA

PATENTS ACT 1990 COMPLETE SPECIFICATION FOR A STANDARD PATENT Name and Address of Applicant: Actual Inventor(s): Address for Service: Invention Title: Macquarie Research Ltd, an Australian company, ACN 003 849 198, of 2nd Floor, Becton Dickinson Building, Research Park Drive, Macquarie University, New South Wales, 2109, Australia Helen Margaret Pask James Austin Piper Spruson Ferguson St Martins Tower Level 31 Market Street Sydney NSW 2000 (CCN 3710000177) A stable solid state raman laser and a method of operating same The following statement is a full description of this invention, including the best method of performing it known to me/us:- 5845c OD 1 c A STABLE SOLID STATE RAMAN LASER AND A METHOD OF SOPERATING SAME Technical Field The present invention relates to a stable solid-state Raman laser and a method of maintaining stable operation of a solid-state Raman laser.

C Background of the Invention 8 Solid-state Raman lasers are a practical and efficient approach to optical cI frequency down conversion offering high (up to 70-80%) conversion efficiencies with Srespect to the pump laser power, excellent beam quality and ease of alignment. In recent io years use of crystals for stimulated Raman scattering (SRS) has been gaining interest because, in comparison with high-pressure gaseous and dye (liquid) Raman lasers, crystalline Raman lasers offer better gain, better thermal and mechanical properties, better reliability and the ability to operate at high pulse-repetition frequency. Further they are compatible with compact all-solid state laser technology.

The potential of crystalline Raman lasers for efficient frequency conversion was first reported by E. 0. Ammann and C.D. Dekker, "0.9 W Raman oscillator", J. Appl.

Phys., vol. 48, no. 5, pp1973-1975, 1977 who obtained 0.9W at the first Stokes wavelength employing SRS in crystalline lithium iodate (LiIO 3 inside the resonator of a Nd:YALO laser with optical to optical conversions of up to 77%. Other suitable crystals include various tungstates, .molybdate, and barium nitrate. By selecting the nature of the crystal used it is possible for frequency conversion to particular discrete wavelengths.

The output beam at the Raman wavelength (or its second harmonic) typically has very good beam quality and spatial characteristics and pointing stability and can be efficiently (80-90%) coupled into optical fibres (typically 50-600 pim diameter) as required for many applications.

Solid-state Raman laser systems suffer from the problem however that they are complex in design and operation and it is generally difficult to design a solid-state Raman laser which is capable of being operated with stability from initial current input to the optical power pump source up to maximum current and over a long period of time. If the laser system is not effectively stable, alignment and power drifts result. It would be desirable to find a simple method to design solid-state lasers for a particular operating point within various power regimes including low power regimes (about 10mW output power) and higher power regimes (greater than 1W) which are able to be operated with stability. It would also be desirable to design a solid-state Raman laser system which is .4 efficient, has low sensitivity to misalignment, good beam quality and can generate output d) of up to several Watts of Stokes output or when applicable, its second harmonic.

Object of the Invention It is the object of the present invention to overcome or substantially ameliorate at least one of the above disadvantages or at least provide a suitable alternative.

N Summary of the Invention O According to a first aspect, the present invention consists in a stable solid-state Raman laser, the solid-state Raman laser including: a resonator cavity defined by at least two reflectors, a laser material located in the resonator cavity and- capable ofgeer ng a cavity laser beam which propagates within the resonator cavity, a solid Raman medium located in the resonator cavity for shifting the frequency of the cavity laser beam to produce a Raman laser beam which propagates within the resonator cavity; and an output coupler for coupling and outputting the Raman laser beam from the resonator cavity, wherein at least 'one parameter selected from the group consisting of the position of the laser material relative to the position of the Raman medium in the cavity, (ii) the length of the cavity and (iii) the curvature of at least one of the reflectors, is selected such that changes in the focal lengths of both the laser material and the Raman medium as a result of thermal effects in the laser material and ti i' AnitM' uring operation of the laser do not substantially cause instability in the power, of the output Raman laser beam.

Suitably the at least one parameter is selected to provide the output Raman laser beam with optimum power output.

Suitably the laser further includes a non-linear medium for frequency doubling the Raman laser beam, the non-linear medium being located at a position selected from the group consisting of internal to the resonator cavity and external to the resonator cavity.

Suitably in addition, at least one additional parameter selected from the group consisting of (iv) the separation between the reflectors, the laser material and the Raman medium and if present, a non-linear medium; the transmission characteristics of the output coupler; and (vi) the pulse repetition frequency of the output; are selected such that changes in the focal lengths of both the laser material and the Raman medium as a result of thermal effects in the laser material and the Raman medium during operation of the Slaser do not substantially cause instability in the power of the output Raman laser beam.

Suitably the at least one additional parameter is selected to provide the output Raman laser beam with optimum power output.

s Suitably the beam waist and resonator mode sizes in the laser material and the 00oo Raman medium and a non-linear medium, if present, are such that, in use, the laser Sprovides an output Raman laser beam in an output power range whilst avoiding optical damage of the laser material and the Raman medium. Suitably the output power range corresponds to a single output power. Suitably the output power range is a range selected from thegroup consisting of the optimal output power, a near optimal output power and a below optimal output power.

Suitably the at least one parameter is selected whereby in use the beam waist and resonator mode sizes in the laser material and the Raman medium and in a non-linear medium, if present, are optimised for an output power range of the output Raman laser beam whilst maintaining the cavity stability and avoiding optical damage to the laser material and the Raman medium.

Suitably the laser material, the Raman medium and if present, a non-linear medium are present as non-discrete elements, one component performing the dual function selected from the group consisting of both the laser material and non-linear medium; (ii) both the laser material and the Raman medium; and (iii) both the Raman medium and the non-linear medium.

Suitably the laser material is selected from the group consisting of Nd:YAG, Nd:YVO 4 and Nd:YLF; and the Raman medium is selected from the group consisting of LiIO0 3 CaWO 4 KGW and Ba(N0 3 2 Suitablye the non-linear medium is selected from the group consisting of LBO, BBO and KTP.

Suitably the laser further includes a pumping laser source for pumping the laser material and Raman medium so as to produce a fundamental laser beam and Raman laser beam which propagate within the cavity. Suitably the laser includes means to vary the frequency of the pumping laser source so as to vary the output power of the output Raman laser beam.

According to a second aspect, the present invention consists in a method of maintaining stable operation of a solid state Raman laser, the solid state Raman laser including a resonator cavity defined by at least two reflectors, a laser material located in the resonator cavity and capable of generating a 9 cavity laser beam which propagates within the resonator cavity, a solid Raman medium located in the resonator cavity for shifting the frequency of the cavity laser beam to produce a Raman laser beam which propagates within the resonator cavity; and 00o an output coupler for coupling and outputting the Raman laser beam from the 0 0resonator cavity, I\O the method including at least one step selected from the group consisting of 0(i) positioning the laser material relative to the Raman medium in the cavity, (ii) altering the length of the cavity and (iii) selecting a curvature of at least one of the reflezfArsuch that changes in the focal lengths of both the laser material and the Raman medium as a result of thermal effects in the laser material and the Raman medium during operating of the laser do not substantially cause instability in the power of the output Raman laser beam; and pumping the laser material and the Raman medium with a pumping beam to provide an output Raman laser beam with stable power output.

Suitably the method includes determining the focal lengths of the laser material and the Raman medium.

Suitably in the method step comprises selecting the parameter so as to provide the output Raman laser beam with optimum output power.

Suitably in the method the laser further includes a non-linear tehdium'i'Y6ifretluency doubling the Raman laser beam to produce an output at its second harmonic or other subfrequency or different frequency wavelength, the non-linear medium being present in the resonator cavity or external to resonator cavity, the method including frequency doubling the Raman laser beam to produce said output. Suitably the frequency doubling produces an output at a wavelength selected from the group consisting of about 532 nm, 578-580 nm, 632-636 nm, about 598nm and combinations thereof.

Suitably in the method step includes optimising the beam waist and resonator mode sizes of the laser material and the Raman medium and a non-linear medium, if present, for a desired output power range whilst maintaining cavity stability and avoiding optical damage of the resonator components.

According to a third aspect, the present invention consists in a stable solid-state Raman laser, the solid-state Raman laser including: a resonator cavity defined by at least two reflectors, "1 a laser material located in the resonator cavity and capable of generating a Scavity laser beam which propagates within the resonator cavity, a solid Raman medium located in the resonator cavity for shifting the frequency of the cavity laser beam to produce a Raman laser beam which propagates IND 5 within the resonator cavity; and 0(d) an output coupler for coupling and outputting the Raman laser beam from the resonator cavity, wherein the beam waist and resonator mode sizes in the laser material and the Raman medium in the cavity are selected such that in use changes in the focal lengths of both the laser material and the Raman medium as a result of thermal effects in the laser material and the Raman medium during operation of the laser do not substantially cause instability in the power of the output Raman laser beam.

SAccording to a fourth aspect, the present invention consists in a method of maintaining stable operation of a solid state Raman laser, the solid state Raman laser including a resonator cavity defined by at least two reflectors, a laser material located in the resonator cavity and capable of generating a cavity laser beam which propagates within the resonator cavity, a solid Raman medium located in the resonator cavity for shifting the frequency of the cavity laser beam to produce a Raman laser beam which propagates witinthe resonator cavity; and an output coupler for coupling and outputting the Raman laser beam from the resonator cavity, wherein the beam waist and resonator mode sizes in the laser material and the Raman medium in the cavity are selected such that in use changes in the focal lengths of both the laser material and the Raman medium as a result of thermal effects in the laser material and the Raman medium during operation of the laser do not substantially cause instability in the power of the output Raman laser beam, the method including the step of pumping the laser material and the solid Raman medium with a pumping beam to-provide an output Raman laser beam with stable output power.

Suitably in the method the laser further further includes a non-linear medium positioned in the cavity or external to the cavity for frequency doubling the Raman laser beam to produce an output, the method including operating the laser to produce said frequency-shifted output wherein the beam waist and resonator modes size in the non- Slinear medium is selected such that in use changes in the focal lengths of both the laser material and the Raman medium as a result of thermal effects in the laser material and the Raman medium during operation of the laser do not substantially cause instability in the ,O S5 power of the output Raman laser beam.

00According to a fifth aspect, the present invention consists in a stable solid-state Raman laser, the solid-state Raman laser including: IND a resonator cavity defined by at least two reflectors, S(b) a laser material located in the resonator cavity and capable of generating a cavity laser beam which propagates within the resonator cavity, a solid Raman medium located in the resonator cavity for shifting the frequency of the cavity laser beam to produce a Raman laser beam which propagates within the resonator cavity; and an output coupler for coupling and outputting the Raman laser beam from the is resonator cavity, wherein a beam waist and resonator mode sizes of the laser material and the Raman medium are such that the Raman laser operates in a desired output power range whilst maintaining cavity stability and avoiding optical damage of the resonator components.

Suitably the Raman laser further includes a non-linear medium positioned in the cavity or external to the cavity for frequency doubling the Raman laser beam to produce an output at its second harmonic or other subfrequency or different frequency wavelength, the beam waist and resonator mode size of the non-linear medium being such that the Raman laser operates in the desired output power range whilst maintaining cavity stability and avoiding optical damage of the resonator components. Suitably the beam waist and resonator mode size of the non-linear medium is optimised for optimum power output.

Suitably the position of the non-linear medium is selected such that during operation of the laser, the beam waist and resonator mode sizes of the laser material, Raman medium and non-linear medium are such that the Raman laser operates in the desired output power range whilst maintaining cavity stability and avoiding optical damage of the resonator components.

Suitably at least one parameter selected from the group consisting of a position of the laser material and a position of the Raman medium and optionally, if present a position of a non-linear medium in the cavity, (ii) a length of the cavity or (iii) a curvature of at least one of the reflectors is selected such that the Raman laser operates in Sthe desired output power range whilst maintaining cavity stability and avoiding optical damage of the resonator components. Suitably the at least one parameter is selected to N provide the output power beam with optimum power output.

Suitably in addition at least one additional parameter selected from the group N, consisting of (iv) the separation between one or more of the reflectors, the laser material 00 O and the Raman medium and optionally if present a non-linear medium; the \,transmission characteristics of the output coupler; and (vi) the pulse repetition frequency Sof the output; are selected such that during operation of the laser, the beam waist and i 10 resonator mode sizes of the laser material, the Raman medium and if present the nonlinear medium are such that the Raman laser operates in the desired output power range whilst maintaining cavity stability and avoiding optical damage of the resonator components. Suitably the at least one additional parameter is selected to provide the output beam with optimum power output.

is According to a sixth aspect, the present invention consists in a method of maintaining stable operation of a solid state Raman laser, the solid state Raman laser including a resonator cavity defined by at least two reflectors, a laser material located in the resonator cavity and capable of generating a cavity laser beam which propagates within the resonator cavity, a solid Raman medium located in the resonator cavity for shifting the frequency of the cavity laser beam to produce a Raman laser beam which propagates within the resonator cavity; and an output coupler for coupling and outputting the Raman laser beam from the resonator cavity, the method including operating the laser such that a beam waist and resonator mode sizes of the laser material and the Raman medium are such that the Raman laser operates in a desired output power range whilst maintaining cavity stability and avoiding optical damage of the resonator components.

Suitably the method includes determining the beam waist and resonator mode sizes of the laser material and the Raman medium and if present a non-linear medium.

Brief Description of the Drawings A preferred form of the present invention will now be described by way of example with reference to the accompanying drawings wherein: NZ Figure 1 is a schematic drawing of a suitable Raman laser configuration for use Sin the present invention; Figure 2 is a graph of average output power of a Raman laser configuration C, optimised for operation at 15A and Figure 3 is a graph of average output power of a Raman laser configuration at NO various currents using three different crystal lengths; SFigure 4 is a graph of average output power of a Raman laser configuration at Svarious currents using three different output-coupling transmissions; O Figure 5 is a graph of average output power of a Raman laser configuration at i 10 various currents using various pulse repetition frequencies; Figure 6 is a stability diagram for a two-mirror Raman laser; Figure 7 is a stability diagram for the Raman laser configuration used in Figure 2 operating at a diode current of Figure 8 is the predicted resonator mode of the Raman laser configuration used in Figure 2 optimised at Figure 9 is a stability diagram for the Raman laser configuration used in Figure 2 operating at a diode current of Figure 10 is the predicted resonator mode of the Raman laser configuration used in Figure 2 optimised at Figure 11 is a schematic drawing of another suitable Raman laser configuration for use in the present invention in which a frequency-doubled, single-end-pumped Raman laser is used; Figure 12 is a stability diagram showing how the resonator stability varies with various combinations of thermal lens powers of an Nd:YAG and Raman crystal using the laser of Figure 11; Figure 13 is a diagram of an ABCD resonator analysis which predicts the relative beam waist at all points of the resonator of Figure 11 for operation at the desired operating point.

Figure 14 is a diagram showing the average output power at 578 nm as a function of diode laser current using the laser of Figure 11.

Detailed Description of the Preferred Embodiments The present inventors have discovered that the resonator stability problems associated with operation of Raman solid-state lasers can be solved by designing a solidc1 state Raman laser taking into account the thermal lensing power of the laser material and the Raman medium.

Thermal lenses are formed in the laser material in the following way. In the ci process of generating laser output at the fundamental wavelength in the laser material, heat is deposited in the laser material and a temperature distribution is established.

,1N Through the thermo-optic coefficient, a variation in refractive index develops across the 00 0 laser material, which acts to focus light passing through the material, the laser material acting as a converging lens this is a thermal lensing effect having a focal length fL. The 0 magnitude of fL decreases with increasing absorbed pump power and for maximum C, io absorbed pump power fL=fL(min) i.e. from initial start-up current to maximum operating current, there is a decrease in focal lengths of the laser medium.

Thermal lenses are also generated in the Raman medium. With frequency conversion by SRS (stimulated Raman scattering) there is a generation of phonons in the Raman medium which decay rapidly such that there is a uniform generation of heat inside the Raman medium leading to significant lensing effects and a focal length fR. These effects arise from the inelastic nature of the nonlinear, nonuniform process and for every scattering event, a small fraction of the photon energy in the case of LiIO 3 is deposited as heat in the Raman medium. The degree of heating increases with the power generated at the Stokes wavelengths, more specifically for every first or second Stokes photon generated inside the laser cavity, a small but fixed amount of heat is deposited inside the medium. The resulting temperature distribution which is affected by the thermal conductivity of the crystal and the size of the laser beam inside the resonator cavity causes a variation of refractive index across the medium. While the positive thermal lens in for example a Nd:YAG laser medium scales approximately linearly with absorbed power from a laser diode, the thermal lens in for example LilO 3 depends on the intracavity power density at the first-Stokes wavelength. For LiIO 3 the thermo-optic coefficient (dn/dT) is -84.9x106K' at a wavelength of I micron (according to Optical Society of America Handbook of Optics, ed. Bass, 1995) (over ten times larger than in Nd:YAG and of opposite sign). This means that light passing through the Raman medium is caused to diverge as though passing through a conventional lens with focal length Based on measurement of the thermal lens by the, inventors in an arclamppumped LilO 3 Raman laser, the size of the negative thermal lens in LilO 3 may be as short as -10cm (comparable to that in the Nd:YAG medium).

c-1 Both the thermal lenses in the laser material and in the Raman medium impact substantially on the stability characteristics of the resonator in a dynamic way. Suitably the position of the laser material and the Raman medium in the cavity and/or reflector Cl (mirror) curvatures is such that the laser is capable of stable operation over a sufficientlywide range of combinations for FL and FR including the special case where fL--fR=infmite C, (so that laser action can be initiated) and also fR=infinite, fL>fjmin) (so that laser action 00 desirably does not cease if SRS ceases).

C Suitably a curvature of at least one of the reflectors and/or the positions of the laser material and the Raman medium relative to the cavity configuration are such that the C, lo focal lengths of the laser material at pump input powers and the focal lengths of the Raman medium at the desired Raman laser output power range are maintained within a stable and preferably efficient operating region. In preferred embodiments this can be achieved by optimising the cavity configuration as a function of the focal lengths by in addition to positioning the laser material and Raman medium within the cavity and/or selecting a curvature of at least one of the reflectors, optimising one of more of: a separation between one or more of the reflectors, the laser material and the Raman medium; transmission characteristics of the output coupler; and the pulse repetition frequency.

Additional effects such as gain focussing and self-focussing of the Raman and/or laser beams may affect the resonator stability but these are considered to be of lesser importance than the effects already discussed.

In preferred embodiments the laser is also optimised for given pump powers for optimum mode sizes in the laser gain material and in the Raman gain medium and if present a non-linear medium and optimum laser output power so as to obtain efficient energy extraction from the laser material as well as efficient conversion through stimulated Raman scattering (SRS) in the Raman crystal and if present the non-linear medium whilst maintaining cavity stability and avoiding optical damage of the laser components the various components are matched on the basis of their associated mode sizes. The optimum spot size and power density in the Raman medium is typically a compromise between maximising the conversion efficiency and avoiding optical damage. The cavity .is suitably optimised so that the relative mode size in each of the materials present in the cavity is such so as to provide efficient stable output. Suitably C1 conversion efficiencies of greater than 40%, more preferably greater than 50% are Qobtainable at output powers up to 3W or greater.

In order for the Raman laser to operate with suitable optimal efficiency the key C1 design parameters (ie mirror curvatures, cavity length, positioning of the various components) are suitably chosen so that the resonator mode sizes in the laser material C, the Raman medium and if present the non-linear medium (frequency-doubling 00 crystal) are near-optimum at a desired operating point. One can denote the beam ¢C waists in these media as WA, C

O

B and (oc respectively. (oA is suitably mode-matched to the Sdimension of the pumped region of the laser material the pump spot size (cop). cop can 10 vary according to the power of the pump laser source a diode laser) and the pumping configuration. For example a laser crystal end-pumped with a low power 1 W) laser diode will typically have a cop of approximately 100 pm. A laser crystal endpumped with a 15-25 W laser diode will typically have a cop in the range 250 to 350 um, more usually of approximately 300 pm. A laser crystal side-pumped by one or more laser diodes will typically have a cop in the range of about 500 to 1500 Pm. Optimal modematching of Cop and (A is a suitable pre-requisite for enabling efficient extraction of the gain in the laser material.' If OA is too small, then laser gain typically will not be extracted efficiently into the TEMoo resonator mode and (ii) the laser may oscillate on higher-order modes which are generally not desirable. If oA is too large, then diffraction losses can occur in the resonator due to aberrations in the thermal lens associated with the laser crystal. This effect is undesirable and deleterious for pumping powers approximately 3 W. Typically is suitably in the range 0.8 to 1.2. .oB is suitably COp optimised for high conversion through the SRS process, while at the same time optical damage to the Raman media is suitably avoided. The optimum value for COB varies from crystal to crystal because different Raman-active crystals have different Raman gains and different thresholds for optical damage. If w(o is too large, then the conversion efficiency of the SRS process will be lower than optimum. If (oB is too small, then the optical power density in the Raman crystal can approach the threshold for optical damage in that crystal and (ii) the thermal lens associated with the Raman crystal may become more aberrated, resulting in increased resonator losses (due to diffraction). Typical values for (oB are in the range 200 300 gtm. coc is suitably optimised for efficient frequency conversion through the frequency doubling process. The optimum value for oc varies according to the type of crystal used. Different crystals have different non-linear CI coefficients, walk-off angles and damage thresholds. If oc is too large, then (i) conversion efficiency will be lower than optimum; (ii) the optical field at the Stokes frequency can be "under-coupled" in this case, unwanted non-linear processes such as

C

1 higher-order Stokes generation and self-focussing can occur. If oc is too small then (i) optical damage can occur to the crystal, (ii) the effective length of the non-linear N interaction can become too short due to "walk-off' effects and (iii) the optical field at the 00 0 Stokes wavelength can be "over-coupled" which can result in reduced conversion Nc efficiency of the SRS process. This discussion assumes that the mode size in A, B and C 0 is the same for optical fields at different wavelengths. In practice OA, (OB and Qc may be CN to slightly different (by 10%) owing to effects such as gain-guiding and self-focussing.

Suitably the mode size in the laser material is approximately equal to the pump spot size. Suitably in a LiIO 3 crystal the spot size COB is optimised for stable operation and efficient conversion such that the spot size in the laser material COA is greater than the spot size in the Raman media CoB which in turn is greater than the spot size in the non-linear medium Oc, if present WA OB oCC.

In preferred embodiments the thermal lens focal lengths for the laser material at the laser input powers and the thermal lens focal lengths of the Raman medium at the laser output powers are determined and the position of the laser material and the Raman medium in the cavity are selected to ensure that during operation of the laser the resonator is stable. Suitably the thermal lenses for the laser material can be calculated and then confirmed by cavity stability measurement. Alternatively the thermal lenses can be determined by standard measurement techniques such as lateral shearing interferometry measurements which can also provide information on any aberrations. A suitable interferometric technique is described in M. Revermann, H.M. Pask, J.L. Blows, T.

Omatsu "Thermal lensing measurements in an intracavity LilO 3 Laser", ASSL Conference Proceedings February 2000; in J.L. Blows, J.M. Dawes and T. Omatsu, "Thermal lensing measurement in line-focus end-pumped neodymium yttrium aluminium garnet using holographic lateral shearing interferometry", J. Applied Physics, Vol. 83, No. 6, March 1998; and in H.M Pask, J.L. Blows, J.A. Piper, M. Revermann, T. Omatsu, "Thermal lensing in a barium nitrate Raman laser", ASSL Conference Proceedings February 2001.

Suitably at least the position of the laser material and the Raman medium in the cavity are selected such that the combination of the thermal lens powers for the laser and Raman media fall within a stable operating region of a stability plot. A suitable stability plot for a two-mirror resonator can be determined as follows. The ray transfer matrix is N, calculated for a transit of the optical resonator. The elements of this matrix M I4 enable an equivalent (two-mirror) resonator to be defined with equivalent g-parameters gi A, g2* D and L* B. Texts describing this method are N. Hodgson and A. Weber, "Optical Resonators", Springer-Verlag London Limited, 1997 and W. Koechner, "Solidstate Laser Engineering", Springer-Verlag, 1992.

00 The dynamic nature of the Raman laser resonator as the diode current is increased can be simulated by calculating gl* and gz* for suitable combinations of the ND thermal lenses in the laser and Raman crystals. When plotted on a stability plot, a curve can be defined. In a well-designed resonator, this curve will lie in a stable region of the to stability plot from the point where laser action is initiated to the point corresponding to the desired operating current.

In example of a stability diagram is shown in Figure 6. On the stability plot shown the hatched regions corresponds to a stable operating region. Each point on the graph corresponds to a different combination of thermal lens powers for the laser material DL and Raman media DR. The heavy solid line shows an example how the resonator stability varies in a well-designed Raman laser as the pump diode is increased from zero to the desired operating point. In preferred embodiments a computer model is used to determine suitable cavity configurations for a particular power regime using different combinations of media. In such an embodiment the thermal lensing power for a variety of Raman media crystals can be measured over a wide parameter space of Raman laser output powers and mode sizes and thermally modelled. A standard resonator design program using 2-mirror configurations to more complex folded resonators can then be used to determine the fundamental and Raman laser mode sizes as a function of pump power enabling stable resonators to be designed to produce output powers in specified regions from mWs to multiwatt outputs.

The laser material can be pumped/stimulated by a pulsed or continuous arclamp, flashlamp or diode (semiconductor) laser using a side-pumped, single end-pumped or double end-pumped geometry. End pumping of the laser crystal is a very efficient approach to generating Raman laser output or its second harmonic. For example the inventors have demonstrated optical to optical conversion efficiencies as high as 7% for end pumping with a 20W output from a fibre-coupled diode laser to produce 1.42W frequency-doubled Raman laser output at 578nm. Compared to side-pumped laser crystals, end-pumped laser crystals generally have high gain and give rise to short Q- C1 switched pulses, and the pump spot size in the laser crystal can be adjusted to match the resonator mode size. However end-pumped laser crystals can also give rise to strong (and abberated) thermal lensing, and this ultimately limits the scalability of end-pumped Cl Raman lasers.

Side-pumping of the laser crystal may not result in such high optical-optical C conversion efficiency, but it is a cheaper approach, is more easily scalable and enables 00 0 greater flexibility in where the resonator components can be placed.

Typically the laser beam is Q-switched in order to obtain sufficiently high peak O powers for efficient frequency conversion. The resonator cavity may have a folded or S 10 linear configuration or other suitable configuration. The position of the laser material and Raman medium in a chosen configuration are suitably chosen to provide cavity stability for a wide range of combinations of fL and fR.

The laser material suitably generates laser beams at a fundamental wavelength (1064nm for Nd:YAG) when stimulated by pump light of an appropriate wavelength, and the fundamental laser beam then propagates inside the laser resonator. Suitably the laser material is formed by one of the following crystals: Nd:YAG, Nd:YLF, Nd:glass, Tisapphire, Erbium:glass, Ruby, Erbium:YAG, Erbium:YAB, Nd:YAIO 3 Yb:YA10 3 Nd:SFAP, Yb:YAG, Yb:YAB, Cobalt:MgF 2 Yb:YVO 4 Nd:YAB, Nd:YVO 4 Nd:YALO, Yb:YLF, Nd:YCOB, Nd:GdCOB, Yb:YCOB, Yb:GdCOB or other suitable laser material. Typically the laser material is broadband AR-coated for the 1-1.2 micron region to minimise resonator losses. Optionally the laser material is wavelength tunable and capable of generating high power output which can be mode-locked.

The Raman medium suitably enables the fundamental radiation to be converted to first (or higher) Stokes wavelength through the nonlinear process Stimulated Raman Scattering (SRS). Depending on application, the Raman medium suitably converts the fundamental wavelength to the first Stokes wavelength, to the second Stokes wavelength or to a higher Stokes wavelength. Typically the Raman medium is broadband AR-coated for the 1-1.2 micron region to minimise resonator losses. The Raman medium is suitably chosen on the basis of high transmission at the fundamental and Stokes wavelengths, useful Raman shift, fairly high Raman gain, high damage threshold and availability in lengths exceeding 1cm and chosen such that the Raman gain is adequate. Typically the Raman medium is a crystal, typically a single crystal. Typically the length of the crystal is 1-7cm long. A typical dimension of the crystal is 0.5x0.5xy cm where y is crystal length and is in the range 1-7cm. Longer crystal lengths are typically used where higher CN output powers are desired since the Raman gain coefficient is proportional to the length of Sthe Raman gain medium. Alternatively a longer path through the Raman crystal can be achieved using a multipass of zigzag geometry such as described in Byer patent US C1 5673281. Suitably the Raman medium is a single crystal of LiIO 3 or Ba(N0 3 2 or other suitable Raman active material such as KDP (potassium dihydrogen phosphate), KD*P C (deuterated), lithium niobate, and various tungstates (KGW, CaWO 4 and molybdate 00 0 crystals. Other suitable Raman active crystals are described in the CRC Handbook of 0 CN Laser or the text "Quantum Electronics" by Pantell and Puthoff. LiIO 3 and Ba(N0 3 2 are C preferred. Ba(N0 3 2 is an isotropic crystal with a high gain coefficient (llcm/GW with C1 to 1064nm pump) leading to low threshold operation and can provide a Raman shift of 1048.6cm'. LiIO 3 is a polar uniaxial crystal with a complex Raman spectrum which depends on the crystal cut and orientation with respect to the pump propagation direction and polarisation vectors and can provide Raman shifts of between 745 cm 1 and 848cm l (which are useful when targeting wavelengths for specific applications for example Is 578nm which is useful for medical applications including ophthalmology and dermatology) but has a lower damage threshold (about 100MWcm- 2 compared with Ba(N0 3 2 (about 400MWm' 2 Both Ba(N0 3 2 and LilO3 have good slope efficiencies (determined by the ratio of Stokes to pump photon energies) with optical to optical conversion efficiencies of 70-80% being reported for both Ba(N0 3 2 and LiIO 3 The following laser material/Raman medium combinations are particularly desirable: Nd:YAG/LiI0 3 Nd:YAG/Ba(N0 3 2 and Nd:YLF/CaWO 4 In one embodiment the laser may further include a non-linear medium for frequency doubling the Raman laser beam to produce an output at its second harmonic or other subfrequency or different frequency wavelength, the non-linear medium being present in the resonator cavity or external to resonator cavity.

Optionally a solid non-linear medium is used for frequency doubling the Raman laser beam to produce an output at its second harmonic or other subfrequency or different frequency wavelength. The solid non-linear medium can be located in the cavity (intra cavity doubled doubling crystal located inside the resonator) or external to the cavity (extra cavity doubled doubling crystal located outside of the laser resonator). Suitably a folded resonator is used. Suitable solid non-linear mediums include a second harmonic generator (SHG), a sum frequency generator (SFG) or a difference frequency generator (DFG). As examples of non-linear medium mention can be made of LBO, CTP, BBO, LiIO 3 KDP, KD*P, KBs, KBsOs, KTP, ADP, LN (lithium niobate) or periodically-poled

C

LN or combinations thereof to generate green and yellow lasers simultaneously).

Suitably a LBO, BBO or KTP crystal is used. The light can be frequency doubled by S angle-tuning and/or controlling the temperature of the solid non-linear medium. In 1 preferred embodiments the light is frequency doubled so as to generate yellow light.

Typical variations in the visible wavelength with a LBO crystal cut for type 1 non-critical -N phase-matching with temperature tuning to approximately 149 0 C, 40 0 C or 0°C include 00 oO 0 532nm (green), 578-580nm (yellow) and 632-636nm (red) (with two doubling crystals 1 simultaneous 532nm and 578nm output is possible). By such frequency doubling it is O possible to generate wavelengths typically in the yellow or orange spectral region suitable C1 to for dermatological, ophthalmic and visual display applications. The resonator design is such that the size of the waist in the doubling medium is typically sufficiently small to allow efficient conversion and high output powers but large enough to avoid optical damage. Suitably the solid non-linear medium is AR-coated to minimise losses in the 1- 1.2 micron region and in the visible where possible. A suitable AR coated LBO crystal is for intracavity use is 4x4xl0mm and for extracavity use is 4x4xl0mm although other sizes can be used.

For intracavity doubling, the crystal is suitably placed near a beam waist. For extracavity doubling, the Raman laser output is focussed by lenses into the crystal for maximum conversion.

o Preferably the resonator cavity is defined by at least two reflectors which can be two mirrors at least one of which is preferably curved to provide a stable output laser beam (the other mirror may be flat). Other suitable reflectors that can be used in the present invention include prisms or gratings. More preferably at least two curved mirrors are used, although it is possible to use more than two mirrors, different sets of mirrors reflecting the propagating laser beam and the propagating Raman beam such as in a bowtie resonator. When a solid non-linear medium is used, another mirror may be present such as in a dichroic cavity. Suitable reflectors defining the resonator cavity are well known in the art and can be coated to enable operation at lower Raman thresholds for the first Stokes order thereby helping to suppress higher-order Stokes generation and selffocussing. The mirrors are also typically coated to have high transmission at the wavelengths of interest. Reflectors can be provided with special dielectric coating for any desired frequency. In this way the resonator cavity can be tuned to the Stokes wavelength, the pump wavelength or both. The mirrors can provide for the laser output to be coupled out of the cavity such as by use of a broadband dichroic mirror transmissive at the frequency of the output beam but suitably highly reflective as other frequencies so as to Scause build-up of the power intensities of the beams in the cavity. Alternatively a r polarisation beam splitter can be used to outcouple the laser output. The radius of curvature and separation between the reflectors (cavity length) and transmission S s characteristics of the outcoupling mirror are suitably chosen to provide cavity stability for 00 a sufficiently wide range of combinations of fL and fR. The radius of curvature of the Oreflectors are appropriately selected on the basis of the Raman and laser crystal used (for IDsome Raman crystals +ve effective lens powers of the reflector are desirable and for others -ve effective lens powers of the reflectors are desirable). Suitably the mirrors are i0 chosen so as to be greater than 99% reflective at the laser wavelengths. The output mirror is typically chosen (to optimise the first Stokes output) to be 10 to 90% reflective at the Raman wavelength with the other mirror being greater than 99% reflective at the Raman wavelengths. The laser resonator cavity is suitably a stable resonator which supports the TEMoo 00 mode. For the intracavity-doubled laser, all mirrors/reflectors are suitably chosen Is to be >99% reflective at the fundamental wavelength and the Raman wavelength. The frequency-doubled laser beam is suitably coupled out of the resonator through a dichroic mirror a mirror which has high transmission at the frequency-doubled wavelength but high reflectivity at the fundamental and Raman wavelengths. Preferably the resonator has three or more mirrors/reflectors and is configured so that the frequency-doubled beams which are generated in both directions in the non-linear medium can be extracted efficiently in a single beam. In such a configuration, the end mirror closest to the nonlinear medium will have high reflectivity at the frequency-doubled wavelength.

Suitably the transmission characteristics, radius of curvatures and separation of the reflectors are tailored to achieve efficient and stable operation of the Raman laser and when a solid non-linear medium is used, to generate output at the visible wavelengths.

Suitably the curvature of the reflectors and cavity length are optimised to obtain the desired mode diameter such that near-optimum beam waists are achieved simultaneously in the laser material, the Raman medium and when present, the solid non-linear medium such that changes in the focal lengths of the laser material and the Raman medium as a result of thermal effects in the laser material and the Raman medium during operation of the laser do not substantially cause instability in the power of the output Raman laser beam. The laser material, Raman medium and when present, the non-linear medium can be positioned in the cavity as discrete elements. Alternatively one or more of the components can be non-discrete, one component performing the dual function of both the C1 laser material and the non-linear medium (such as self-frequency doubling or self doubling materials such as Yb:YAB and Nd:YCOB) or performing the dual function of the laser material and the Raman medium (Nd:KGW) or the dual function of the Raman C medium and the non-linear medium (such as by use of a non-centrosymmetric crystal s such as LiIO 3

ID

The pulse repetition frequency of the output can be varied by using a Q-switch 00 0 such as an active Q-switch or a passive Q switch. An acousto-optic Q-switch, an electrooptic Q-switch or passive Q-switches (Cr:YAG) can be used. Alternatively a cavity Sdumping configuration or other suitable means can be adopted (see "The Laser Guidebook" by Jeff Hecht, 2 nd Edition, McGraw-Hill 1992, the whole content of which is incorporated by cross reference). The Q-switch causes fundamental laser output to occur in a pulsed format with high peak powers as required to achieve efficient Raman conversion. Typically the Q-switch is broadband AR-coated for the 1-1.2 micron region to minimise resonator losses. The selection and alignment of the Q-switch is tailored to is achieve a high-Q resonator for the fundamental. The pulse frequency is suitably chosen to provide cavity stability for a wide range of combinations of fL and fR. Selection of the pulse repetition frequency affects the conversion efficiency to the Stokes wavelength, and therefore the Stokes output power and therefore also the thermal lens in the Raman medium. It is a useful parameter to vary because (to first-order) it affects the thermal lens in the Raman crystal while having very little effect on the thermal lens in the laser crystal.

Use of Q-switch pulse repetition frequency (prf) varies the laser output power and affects the "transit" through the stability diagram as shown in Figure 6. The prf is a useful parameter of the laser system. The SRS process depends strongly on the peak power at the fundamental wavelength, and as the prf is increased, the peak power generally decreases. Varying the prfhas two effects: because the Raman gain varies in proportion to the peak power at the fundamental wavelength, an increase of the prf will typically result in a decrease of the average output power at the Stokes wavelength (or its second harmonic); (ii) varying the prf has very little effect on the thermal lens power associated with the laser crystal (that power is determined by the power density of the diode laser pump light). However as stated in above, varying the prf does impact on the output power at the Stokes wavelength. Because the thermal lens power in the Raman crystal is proportional to power density at the Stokes frequency, a variation in prf also changes the thermal lens power in the Raman crystal (independently of the thermal lens power in the cN laser crystal). This can be useful in optimising the region of the stability where the Q system is desired to operate, and also the "transit" through the stability diagram.

At least one polariser can be included in the cavity and can be one or two plates of glass C at Brewsters angle and/or a cube polariser. Such polarisers cause the fundamental to lase on only one linear polarisation. Some polarisation discrimination can also be introduced C through the use of mirrors at non-normal incidence.

00 With reference to Figure 1 a Raman laser 1 in accordance with the invention C comprises a resonator cavity defined by at least two reflectors Ml and M2, a laser material 2A located in the resonator cavity, a solid Raman medium 7 located in the C 10 resonator cavity for shifting the frequency of the cavity laser beam to produce a Raman laser beam which propagates within the resonator cavity and an output coupler M2 for coupling and outputting the Raman laser beam from the resonator cavity. A Q-switch 6, dichroic mirrors 3 and 4 and polariser 5 are also provided in the cavity. In use a current is applied to two diode lasers (not shown) which pump both ends of laser crystal 2A in the cavity via dichroic mirrors 3 and 4. The positions of the laser crystal 2A and Raman medium 7 are selected such that the focal lengths of both the laser crystal 2A and the Raman medium 7 as a result of thermal effects in the laser crystal 2A and Raman medium 7 do not substantially cause instability in the power of the output Raman laser beam whereby the resonator operates in a stable mode. The ways of selecting these parameters to achieve this result are described elsewhere in the specification.

With reference to Figure 11, a laser in accordance with another embodiment of the invention is shown. The laser of this embodiment is a frequency-doubled, single-endpumped Raman laser. As shown in the drawing the laser comprises a diode laser 1, a fibre end receptacle 2, a collimating lens 3, a focussing lens 4, a laser crystal 5, an optional polarising element 6, an acousto-optic Q switch 7, a Raman-active crystal 8, a turning mirror 9 suitably at 45 degree angle of incidence, a frequency-doubling crystal and a resonator end mirror 11. In use a current is applied to the diode laser 1 which pumps laser crystal 5 in the cavity. The positions of the laser crystal 5 and Raman medium 8 are selected such that the focal lengths of both the laser crystal 5 and the Raman medium 8 do not substantially cause instability in the power of the output Raman laser beam whereby the resonator operates in a stable mode and can be further optimised by ensuring the beam waist in the laser crystal 5, the Raman medium 8 and frequencydoubling crystal 10 are optimised for a desired operating point. The current applied to diode laser 1 can be continuous or pulsed. If a pulsed current is applied then the N frequency of the pulse can be altered to change the power of the output Raman laser beam within a range whereby the laser still operates in a stable mode.

The invention will now be described with respect to the following examples.

CN EXAMPLE 1 Experiments were conducted using a Raman Laser configuration as shown in IND Figure 1. The Raman Laser 1 included a diode-pumped Nd:YAG laser employing a 0 commercial pump module (Light Solutions LightLab 1010) 2. The module contained a Nd:YAG rod which was double-end pumped through dichroic turning mirrors 3 and 4.

I The mirror coatings for Ml, M2, 3 and 4 were chosen to provide a higli-Q resonator for Sto the fundamental and a lower Q for the first Stokes. Mirror Ml had high reflectivity at 1064-1160nm and various output coupling mirrors M2 were used with high reflectivity at 1064nm and transmissions from 8 to 50% at approximately 1155nm. The laser was polarised using a one or two Brewster plates 5 and acousto-optically Q-switched 6 at 5-25KHz to produce pulses at 1064nm typically of duration of 20-50ns depending on cavity configuration. A LilO 3 Raman crystal 7 was also located within the cavity to provide a Stokes wavelength of approximately 1155nm (1155.2-1155.5nm as measured using a calibrated Anritsu. optical spectrum analyser) corresponding to a frequency shift of about 740-745cm 1 the Stokes wavelength increasing slightly with increasing Stokes output power for a given output coupling and attributed to the effect of thermal loading of LilO 3 which causes thermal expansion of the crystal lattice and a shift in the Raman spectrum. The average Stokes output power at 1155nm depended on cavity configuration, pulse repetition frequency and diode current. The wavelength of 1155nm was chosen for the experiments because it can be easily frequency doubled to generate yellow light at 578nm, a wavelength which coincides with an absorption band of haemoglobin and which is used for various applications in dermatology. The LilO3 crystal 7 had previously been cut for propagation along the a-axis and oriented so that both the pump and Stokes waves propagated as o-waves in the crystal. The spontaneous Raman spectra for the Raman crystal 7 had an intense peak at about 770cm and a linewidth of 5-6cm 1 In the Raman laser configuration used, the fundamental (1064nm) and first Stokes (1155nm) optical fields shared the same resonator. The cavity design used may alter in certain circumstances, for example the position of some elements such as the Nd:YAG rod and the Q-switch are interchangeable. A variety of configurations is within the scope of the present invention.

Experiment 1 c A 34 cm long cavity with a 30cm radius of curvature high reflector, Ml, a flat output coupler, M2, with near-optimum transmission at the fundamental of 12% and an aperture (750pm diameter) to confine oscillation to the TEMoo mode was used (for diode currents t"- CI up to 18A the fundamental beam profile is generally singly moded and fairly free of aberration, as the diode current is increased however the fundamental profile generally IN becomes strongly aberrated and may consist of several transverse modes however the 00 0 Stokes output almost always occurs in a single traverse mode (TEMoo) indicating Raman beam-cleanup). The output power at 1064nm was in the range 5.5-6.6W at the maximum 0 diode operating current (25A) depending on the exact Q-switch repetition frequency. The

O

C 10o optimally-coupled conditions at 1064nm in this experiment provide the optimum performance baseline to which the output from the Raman laser is compared in order to evaluate optical to optical conversion efficiency. It is not possible to compare the results in terms of the pump power from the diodes because they are inaccessible within the sealed pump module. The iositive thermal lens in the Nd:YAG crystal varied with pump diode current and was estimated to have a focal length of near 8cm (at maximum current).

The focal length of the LiIO 3 crystal was negative and was estimated to be as short as (at maximum first Stokes output power).

In the following experiments, the performance of a LiIO 3 Raman laser was investigated as a function of diode current, Q-switch pulse repetition frequency, output coupler transmission at the Stokes wavelength and the length of the Raman crystal. It is important to note that in the Experiments the turning mirrors inside the sealed pump module had some transmission at the first Stokes wavelength. Using a probe beam at 1155nm from another laser source, it was determined that there was an 18% round trip loss at 1155nm. Given that output coupler transmissions between 8% and 50% were used, the collection efficiencies are broadly consistent with the experimentally-observed decrease of output power when the LiIO 3 crystal was placed on the other side of the pump module. All powers reported in the following experiments are those measured directly after the outcoupling mirror and not corrected for the collection efficiency.

Experiment 2 The Raman resonator cavities were optimised for the highest Stokes output at a specific diode current. The optimisation was basically empirical, a variety of resonators were evaluated using a variety of combinations of cavity lengths, mirror curvatures, output couplings and positioning of the key cavity elements. Figure 2 shows the measured output power of the Raman laser at approximately 1155 nm using two separate cavity configurations optimised for operation at 15A and 25A diode current. In both Scases a 5cm length of LiIO 3 was used.

The first resonator configuration optimised at 15A incorporated two flat end C, mirrors, the high reflectivity mirror was placed 9.5cm and the output coupler transmitting) placed 12cm from the centre of the pump module. A maximum power of IN 1.45W at 1155nm was obtained at 10kHz corresponding to a conversion efficiency of 00 57% (78% accounting for collection efficiency) with respect to the base laser performance at 1064nm As the diode current was increased above 16A, the N Stokes output became very unstable and quickly decreased to zero. Lasing also ceased at 0 0 the fundamental (beyond 16A) indicating that the resonator had become unstable.

For a diode current of 15A the thermal lens in the Nd:YAG is estimated to be about 23cm. In the absence of stimulated Raman scattering and for the cavity length of about 23cm one expects the cavity to be stable. ABCD resonator analysis of the laser incorporating a variable negative lens at the location of the Raman crystal shows that the stability limit for the resonator occurs when the lens in the Raman crystal becomes as short as -20cm. The size of the mode in the Raman crystal is about 280Pm and the Raman power is 1.5W at 1155nm. Preliminary measurements of thermal lensing in a LiIO 3 Raman laser indicate a thermal lens of approximately this size.

A second resonator configuration was optimised for operation with a diode current of 25A. The configuration consisted of a 30cm concave mirror placed 25cm from the centre of the pump module and a 10cm concave output coupler with 50% transmission placed 10cm from the pump module. The pulse repetition frequency was 15kHz. An' average power at 1155nm of 2.62W was obtained corresponding to a conversion efficiency of 42% (56% accounting for collection efficiency) with respect to the base laser performance at 1064nm. A maximum output power of 3.0W using this resonator was achieved by reducing the pulse repetition frequency to 10Hz corresponding to a conversion efficiency of 54% (72% accounting for collection efficiency). Under these conditions however frequent damage to the volume of the LiIO 3 crystal occurred demonstrating that optimum spot-size (approximately 200gm in this case) and powerso density in the LiIO 3 crystal is a compromise between maximising conversion efficiency and avoiding optical damage. An ABCD analysis of this cavity shows it to be less sensitive to thermal lensing (than the resonator configuration optimised for a diode current of 15A) the Raman laser remaining stable for negative thermal lens focal lengths longer than 4cm.

C1 Figures 7 and 9 show stability diagrams for each laser, Figure 7 shows the Q Raman laser operating at approximately 1155 nm and where the diode current was increased to 15A (the cavity including two flat mirrors). Figure 9 shows the Raman laser C, operating at approximately 1155 nm and where the diode current was increased to (the cavity configuration including a 30 cm radius of curvature mirror and a 10 cm radius C of curvature mirror). Figure 8 shows the predicted resonator mode at the optimum 00 0 operating point of the laser operating at approximately 1155 nm with a diode current of 15 A. Figure 10 shows the predicted resonator mode at the optimum operating point of the laser operating at approximately 1155 nm with a diode current of 25 A.

Cl 10 Experiment 3 A number of Raman Laser parameters were studied. A resonator was used consisting of a 30cm concave highly reflecting mirror placed about 25cm from the centre of the pump module and a flat output coupler placed 8cm from the pump module. The LiIO 3 was placed close to the pump module where the resonator mode was largest (approximately 320p.m). A maximum output of 2.3W at a first Stokes wavelength was obtained with this cavity configuration slightly lower than for the 25A resonator of Experiment 2 but with a far lower incidence of crystal damage.

In Figure 3 the average power of the first Stokes wavelength as a function of diode current for crystal lengths 2, 4 and 5cm was studied. The pulse repetition frequency was 15kHz and a 50% transmitting output coupler was used. Higher output powers were achieved with longer crystals as expected since Raman gain coefficient is proportional to the length of the Raman gain medium. The output at 1155nm obtained using the 4cm long crystal was twice that obtained using the 2cm long crystal. Slightly higher powers were obtained using the 5cm long crystal. The effect of output coupling on the Raman laser performance can be seen in Figure 4 where output couplings of 25% and were investigated. The pulse repetition frequency was 15kHz and the LiIO 3 crystal was long. Higher output powers are achieved for larger output couplings. Because of the intracavity losses (due to the turning mirrors) at 1155nm, the collection efficiency for the Stokes photons varies with output coupling and is only 31% when using the 8% transmitting output coupler, 58% with the 25% transmitting output coupler and 74% with the 50% transmitting output coupler. The total Stokes output from the resonators using 25% and 50% transmitting output couplers is respectively 1.7W, 2.5W and The data suggests that higher Raman output powers would be possible by choosing an output coupler with transmission greater than cN The effect of pulse repetition frequency is shown in Figure 5 where the dependence of first Stokes average power is plotted as a function of diode current for Spulse repetition frequencies of 10, 15, 20 and 25kHz. The LilO 3 crystal was 5cm long CN and output coupling was 50%. For a given diode current, higher average powers are obtained for lower repetition rates as is consistent with the dependence of Raman gain on IN peak pump power.

00 0 The experiments show that by optimising cavity design, efficient conversion up to 54%(72% accounting for the collection efficiency) is achieved with multiwatt average C powers of up to 2.7W at the first Stokes wavelength (1155nm) with a low incidence of

O

N 10 optical damage. The electrical to optical conversion efficiency with respect to the power consumed by the diodes is estimated to be about 3.3%.

EXAMPLE 2 With reference to Figure 11, the output of the pump laser diode 1 which is a W fibre-coupled diode laser is launched via fibre end receptable 2 for 600 p.m diameter, .22NA fibre, two lenses 3 and 4 into the laser crystal 5 which is a Nd:YAG (5mm x diameter laser crystal with mirror coatings on end 1 (5A):HR at 1064-1160 nm, HT at 805 nm and end2 5B: AR@1064-1160 nm). The pump spot size (beam radius) in the laser crystal is approximately 300 microns. The laser resonator is defined by the first coated plane face of the Nd:YAG laser crystal 5, the plane dichroic mirror 9 at 45 degrees (HR at 10 6 4-1160nm, HT@578 rnm, and the end mirror 11 (HR at 578, 1064 and approx 1155 nm) which has a radius of curvature of 300 mm. An LBO 4x4x15 mm crystal is used as the frequency doubling crystal and a LiI0 3 crystal is used as the Raman-active crystal. to The optimum lengths of the two arms of the resonator are 150 mm (YAG crystal to degree mirror) and 90 mm (45 degree mirror to end mirror). This folded cavity design is effective in enabling most of the yellow light generated in the LBO crystal to be collected in a single beam. The maximum laser output power at 578nm using this configuration was 1.42 W.

Figure 12 is another diagram showing how the resonator stability varies with the possible combinations of thermal lens powers in the Nd:YAG and Raman crystals. The heavy line shows how the resonator stability changes as the pump diode current is increased from zero to the desired operating point.

Figure 13 shows ABCD resonator analysis which predicts the relative beam waist at all positions in the resonator, for operation at the desired operating point. The numbers denote the following 0- laser crystal, 2- Raman crystal, 3 end mirror.

c, Figure 14 shows the average output power at 578 nm as a function of diode laser Scurrent.

EXAMPLE 3 C, A small-scale Raman laser operating at 1197nm was used. In the system used, the pump laser diode had relatively low output power. 1.6 W of 808 nm diode pump light I was focused into a 2x2x1 mm Nd:YVO 4 crystal. An acousto-optic Q-switch was used to 0 produce the necessary high peak powers for the SRS process. The Raman-active crystal was Ba(N0 3 2 which provided one of the highest Raman gains, having a Raman shift of I 1047 The optimum arrangement for the intra-cavity SRS conversion included using io a 10 cm long cavity, with 10% output coupling at 1197 nm and a pulse repetition frequency of 32 kHz. The First Stokes output occurred at 1197 nm and up to 120 mW of output power was obtained.

A frequency-doubled small-scale Raman laser operating at 1197 nm was used.

Preliminary measurements were made of intracavity-doubled First Stokes output using a 10 mm long piece of LBO cut for type one phase matching. Up to 6 mW at 598 nm was achieved under non-optimised conditions. The cavity was not optimised for collection of the output at 598 nm, the output was only able to be measured from one end of the cavity.

By use of the apparatus and method of the invention it is possible to optimise the cavity including determining where to position components in the cavity so as to get high power output and power stability over a reasonable working range from initial power input up to maximum power and can be scaled up or down for various power regimes.

The invention particularly when frequency-doubling medium is used has application in hospitals, specialist clinics and in general practitioner/single specialist surgeries where solid state Raman lasers could be used for ophthalmology and/or dermatology.

Specifically the 578nm output for a frequency-doubled Nd:YAG LiI03 Raman laser closely matches a strong optical absorption peak of haemoglobin (human blood); this source may be applied in various forms of retinal surgery, treatment of varicose veins and removal of port-wine stains (birth marks), spider veins (telangectasia) and other dermatological therapies. Frequency-doubled solid-state Raman lasers may be used for a variety of spectroscopic sensing applications including biomedical diagnostics, atmospheric and underwater sensors. A further example is the use of such sources as laser guidestars associated with astronomical observations or other forms of optical characterisation of the atmosphere. Such sources may also be used for various forms of illumination in the orange-yellow spectral region including illumination of holographic C plates, as an element in colour projection systems and as laser pointers (such illumination t applications stem from the lack of alternative solid-state lasers operating in the yellow C spectral region where the human eye is most sensitive.

s It will be appreciated by those skilled in the art that the invention can be (N embodied in other forms.

00

(N

OD

Claims (15)

1. A stable solid-state Raman laser, the solid-state Raman laser including: S(a) a resonator cavity defined by at least two reflectors, r a laser material located in the resonator cavity and capable of generating a cavity laser beam which propagates within the resonator cavity, IoN a solid Raman medium located in the resonator cavity for shifting the 00 frequency of the cavity laser beam to produce a Raman laser beam which propagates within the resonator cavity; and I\O an output coupler for coupling and outputting the Raman laser beam from the 0 10 resonator cavity, wherein at least one parameter selected from the group consisting'of the position of the laser material relative to the position of the Raman medium in the cavity, (ii) the length of the cavity and (iii) the curvature of at least one of the reflectors, is selected such that changes in the focal lengths of both the laser material and the Raman medium as a result of thermal effects in the laser material and the Raman medium during operation of the laser do not substantially cause instability in the power of the output Raman laser beam.

2. A laser according to claim 1 wherein the at least one parameter is selected to provide the output Raman laser beam with optimum power output.

3. A laser according to claim 1 wherein the laser further includes a non- linear medium for frequency doubling the Raman laser beam, the non-linear medium being located at a position selected from the group consisting of internal to the resonator cavity and external to the resonator cavity.

4. A laser according to claim 1 wherein, in addition, at least one additional parameter selected from the group consisting of(iv) the separation between the reflectors, the laser material and the Raman medium and if present, a non-linear medium; the transmission characteristics of the output coupler; and (vi) the pulse repetition frequency of the output; are selected such that changes in the focal lengths of both the laser material and the Raman medium as a result of thermal effects in the laser material and the Raman medium during operation of the laser do not substantially cause instability in the power of the output Raman laser beam. A laser according to claim 4 wherein the at least one additional parameter is selected to provide the output Raman laser beam with optimum power output. CN 6. A laser according to claim 1 wherein the beam waist and resonator Smode sizes in the laser material and the Raman medium and a non-linear medium, if present, are such that, in use, the laser provides an output Raman laser beam in an output C1 power range whilst avoiding optical damage of the laser material and the Raman medium.

7. A laser according to claim 6 wherein the output power range N corresponds to a single output power. 0 8. A laser according to claim 6 wherein the output power range is a range C. selected from the group consisting of the optimal output power, a near optimal output Spower and a below optimal output power. C 10 9. A laser according to claim 1 wherein the at least one parameter is selected whereby in use the beam waist and resonator mode sizes in the laser material and the Raman medium and in a non-linear medium, if present, are optimised for an output power range of the output Raman laser beam whilst maintaining the cavity stability and avoiding optical damage to the laser material and the Raman medium.

10. A laser according to claim 1 wherein the laser material, the Raman medium and if present, a non-linear medium are present as non-discrete elements, one component performing the dual function selected from the group consisting of both the laser material and non-linear medium; (ii) both the laser material and the Raman medium; and (iii) both the Raman medium and the non-linear medium.

11. A laser according to claim 1 wherein the laser material is selected from the group consisting of Nd:YAG, Nd:YVO 4 and Nd:YLF; and the Raman medium is selected from the group consisting of LiIO 3 CaWO 4 KGW and Ba(N0 3 2

12. A laser according to claim 3 wherein the non-linear medium is selected from the group consisting ofLBO, BBO and KTP.

13. A laser according to claim 3 or 12 wherein the laser material is selected from the group consisting of Nd:YAG, Nd:YVO 4 and Nd:YLF; and the Raman medium is selected from the group consisting of LiIO 3 CaWO 4 KGW and Ba(N0 3 2

14. A laser according to claim 1 further including a pumping laser source for pumping the laser material and Raman medium so as to produce a fundamental laser beam and-Raman laser beam which propagate within the cavity. A laser according to claim 14 including means to vary the frequency of the pumping laser source so as to vary the output power of the output Raman laser beam.

16. A method of maintaining stable operation of a solid state Raman laser, the solid state Raman laser including c a resonator cavity defined by at least two reflectors, Q(b) a laser material located in the resonator cavity and capable of generating a cavity laser beam which propagates within the resonator cavity, C1 a solid Raman medium located in the resonator cavity for shifting the frequency of the cavity laser beam to produce a Raman laser beam which propagates NI within the resonator cavity; and 00 S(d) an output coupler for coupling and outputting the Raman laser beam from the resonator cavity, Sthe method including at least one step selected from the group consisting of io positioning the laser material relative to the Raman medium in the cavity, (ii) altering the length of the cavity and (iii) selecting a curvature of at least one of the reflectors, such that changes in the focal lengths of both the laser material and the Raman medium as a result of thermal effects in the laser material and the Raman medium during operating of the laser do not substantially cause instability in the power of the output Raman laser beam; and pumping the laser material and the Raman medium with a pumping beam to provide an output Raman laser beam with stable power output.

17. A method according to claim 16 wherein step comprises selecting the parameter so as to provide the output Raman laser beam with optimum output power.

18. A method according to claim 16 wherein the laser further includes a non-linear medium for frequency doubling the Raman laser beam to produce an output at its second harmonic or other subfrequency or different frequency wavelength, the non- linear medium being present in the resonator cavity or external to resonator cavity, the method including frequency doubling the Raman laser beam to produce said output.

19. A method according to claim 18 wherein the frequency doubling produces an output at a wavelength selected from the group consisting of 578-580 nm,

632-636 nm, about 598nm and combinations thereof. A method according to claim 16 wherein step includes optimising the beam waist and resonator mode sizes of the laser material and the Raman medium and a non-linear medium, if present, for a desired output power range whilst maintaining cavity stability and avoiding optical damage of the resonator components. 21. A stable solid-state Raman laser, the solid-state Raman laser including: a resonator cavity defined by at least two reflectors, C a laser material located in the resonator cavity and capable of generating a cavity laser beam which propagates within the resonator cavity, a solid Raman medium located in the resonator cavity for shifting the C- frequency of the cavity laser beam to produce a Raman laser beam which propagates within the resonator cavity; and IND an output coupler for coupling and outputting the Raman laser beam from the 00 o resonator cavity, Swherein the beam waist and resonator mode sizes in the laser material and the I Raman medium in the cavity are selected such that in use changes in the focal lengths of t0 both the laser material and the Raman medium as a result of thermal effects in the laser material and the Raman medium during operation of the laser do not substantially cause instability in the power of the output Raman laser beam. 22. A method of maintaining stable operation of a solid state Raman laser, the solid state Raman laser including a resonator cavity defined by at least two reflectors, a laser material located in the resonator cavity and capable of generating a cavity laser beam which propagates within the resonator cavity, a solid Raman medium located in the resonator cavity for shifting the frequency of the cavity laser beam to produce a Raman laser beam which propagates within the resonator cavity; and an output coupler for coupling and outputting the Raman laser beam from the resonator cavity, wherein the beam waist and resonator mode sizes in the laser material and the Raman medium in the cavity are selected such that in use changes in the focal lengths of both the laser material and the Raman medium as a result of thermal effects in the laser material and the Raman medium during operation of the laser do not substantially cause instability in the power of the output Raman laser beam, the method including the step of pumping the laser material and the solid Raman medium with a pumping beam to provide an output Raman laser beam with stable output power. 23. A method according to claim 22 further including a non-linear medium positioned in the cavity or external to the cavity for frequency doubling the Raman laser beam to produce an output, the method including operating the laser to produce said frequency-shifted output wherein the beam waist and resonator modes size in the non- linear medium is selected such that in use changes in the focal lengths of both the laser material and the Raman medium as a result of thermal effects in the laser material and the SRaman medium during operation of the laser do not substantially cause instability in the power of the output Raman laser beam. Dated 27 February, 2006 SMacquarie Research Ltd SPatent Attorneys for the Applicant/Nominated Person 0SPRUSON FERGUSON IO OD