WO2022244110A1 - リチウム２次電池及びその使用方法、並びにリチウム２次電池の製造方法 - Google Patents

リチウム２次電池及びその使用方法、並びにリチウム２次電池の製造方法 Download PDF

Info

Publication number
WO2022244110A1
WO2022244110A1 PCT/JP2021/018822 JP2021018822W WO2022244110A1 WO 2022244110 A1 WO2022244110 A1 WO 2022244110A1 JP 2021018822 W JP2021018822 W JP 2021018822W WO 2022244110 A1 WO2022244110 A1 WO 2022244110A1
Authority
WO
WIPO (PCT)
Prior art keywords
lithium
secondary battery
lithium secondary
positive electrode
negative electrode
Prior art date
Application number
PCT/JP2021/018822
Other languages
English (en)
French (fr)
Inventor
剛輔 大山
健 緒方
Original Assignee
ＴｅｒａＷａｔｔ Ｔｅｃｈｎｏｌｏｇｙ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ＴｅｒａＷａｔｔ Ｔｅｃｈｎｏｌｏｇｙ株式会社 filed Critical ＴｅｒａＷａｔｔ Ｔｅｃｈｎｏｌｏｇｙ株式会社
Priority to JP2023522051A priority Critical patent/JPWO2022244110A1/ja
Priority to EP21940727.7A priority patent/EP4343895A4/en
Priority to PCT/JP2021/018822 priority patent/WO2022244110A1/ja
Publication of WO2022244110A1 publication Critical patent/WO2022244110A1/ja
Priority to US18/507,206 priority patent/US20240154114A1/en

Abstract

本発明は、エネルギー密度が高く、サイクル特性及び生産性に優れるリチウム２次電池及びリチウム２次電池の製造方法等を提供する。本発明は、正極と、負極活物質を有しない負極とを備え、前記正極が、正極活物質と、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物とを含む、リチウム２次電池に関する。本発明は、また、正極活物質と、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物とを含む正極、及び負極活物質を有しない負極を準備する工程と、前記正極と前記負極とを両者が対向するように配置する工程と、前記正極と前記負極との間に電圧を印加して、カットオフ電圧が４．３Ｖ以上５．０Ｖ以下である充電条件により初期充電する工程と、を含む、リチウム２次電池の製造方法に関する。

Description

リチウム２次電池及びその使用方法、並びにリチウム２次電池の製造方法
　本発明は、リチウム２次電池及びその使用方法、並びにリチウム２次電池の製造方法に関する。
　近年、太陽光又は風力等の自然エネルギーを電気エネルギーに変換する技術が注目されている。これに伴い、安全性が高く、かつ多くの電気エネルギーを蓄えることができる蓄電デバイスとして、様々な２次電池が開発されている。
　その中でも、正極及び負極の間をリチウムイオンが移動することで充放電を行うリチウム２次電池は、高電圧及び高エネルギー密度を示すことが知られている。典型的なリチウム２次電池として、正極及び負極にリチウム元素を保持することのできる活物質を有し、当該正極活物質及び負極活物質の間でのリチウムイオンの授受によって充放電をおこなうリチウムイオン２次電池（ＬＩＢ）が知られている。
　また、高エネルギー密度化の実現を目的として、負極活物質として、炭素材料のようなリチウムイオンを挿入することができる材料に代えて、リチウム金属を用いるリチウム２次電池（リチウム金属電池；ＬＭＢ）が開発されている。例えば、特許文献１には、負極としてリチウム金属をベースとする電極を用いる充電型電池が開示されている。
　また、更なる高エネルギー密度化や生産性の向上等を目的として、炭素材料やリチウム金属といった負極活物質を有しない負極を用いるリチウム２次電池が開発されている。例えば、特許文献２には、正極、負極、これらの間に介在された分離膜及び電解質を含むリチウム２次電池において、前記負極は、負極集電体上に金属粒子が形成され、充電によって前記正極から移動され、負極内の負極集電体上にリチウム金属を形成する、リチウム２次電池が開示されている。特許文献２は、そのようなリチウム２次電池は、リチウム金属の反応性による問題と、組み立ての過程で発生する問題点を解決し、性能及び寿命が向上されたリチウム２次電池を提供することができることを開示している。
特表２００６－５００７５５号公報 特表２０１９－５０５９７１号公報
　しかしながら、本発明者らが、上記特許文献に記載のものを始めとする従来の電池を詳細に検討したところ、エネルギー密度及びサイクル特性の少なくともいずれかが十分でないことがわかった。
　例えば、負極活物質を有する負極を備えるリチウム２次電池は、その負極活物質の占める体積や質量に起因して、エネルギー密度を十分高くすることが困難である。また、負極活物質を有しない負極を備えるアノードフリー型リチウム２次電池についても、従来型のものは、充放電を繰り返すことにより負極表面上にデンドライト状のリチウム金属が形成されやすく、短絡及び容量低下が生じやすいため、サイクル特性が十分でない。
　ところで、リチウム２次電池について、生産性を向上させるために種々の検討が行われている。例えば、リチウム２次電池の各構成の材料、特に正極の材料は大気下での安定性が低い場合があり、そのような場合には、通常の工程で使用されるドライルーム以上に湿度等を精密に管理して電池を製造しなければならないという問題がある。
　本発明は、上記問題点に鑑みてなされたものであり、エネルギー密度が高く、サイクル特性及び生産性に優れるリチウム２次電池及びその使用方法、並びにリチウム２次電池の製造方法を提供することを目的とする。
　本発明の一実施形態に係るリチウム２次電池は、正極と、負極活物質を有しない負極とを備え、上記正極が、正極活物質と、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物とを含む。
　かかるリチウム２次電池は、負極活物質を有しないため、負極活物質を有するリチウム２次電池と比較して、電池全体の体積及び質量が小さく、エネルギー密度が原理的に高い。そのような電池は、リチウム金属が負極の表面に析出し、及び、その析出したリチウム金属が電解溶出することによって充放電が行われる。
　また、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物は、通常の正極活物質の充放電電位範囲において、酸化反応を生じ得るのに対して還元反応を実質的に生じない。したがって、上記のリチウム含有化合物を含むリチウム２次電池において、リチウム含有化合物は電池の初期充電時に酸化反応を生じる（すなわち、リチウムイオンを放出する。）一方で、その後の放電時には還元反応を実質的に生じず（すなわち、放電前のリチウム含有化合物が再形成されない。）、当該リチウム含有化合物に由来するリチウム元素は、負極表面上にリチウム金属として残留する。そして、そのように初期充電後に負極表面上にリチウム金属が残留することとなったリチウム２次電池では、当該残留リチウム金属がその後の充電時において、更なるリチウム金属が負極表面上に析出する際の足場となると考えられ、リチウム金属が負極表面上に均一に析出することを補助すると考えられる。以上のことから、本発明の一実施形態に係るリチウム２次電池は、負極上にデンドライト状のリチウム金属が成長することが抑制され、当該リチウム２次電池はサイクル特性に優れたものとなる。ただし、本発明の一実施形態に係るリチウム２次電池がサイクル特性に優れる要因はこれに限定されない。
　さらに上記のリチウム含有化合物は大気中の微量水分に対する安定性に優れるため、経済的に合理的な方法で（生産性高く）エネルギー密度が高く、サイクル特性に優れたリチウム２次電池を提供可能である。
　上記のリチウム２次電池は、好ましくは、カットオフ電圧が４．３Ｖ以上５．０Ｖ以下である充電条件により初期充電されたものである。
　Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物は電池の電圧が４．３Ｖ程度となる条件で酸化反応を生じ始めるため、上記の態様によれば、上記のリチウム含有化合物の上記で詳述した犠牲正極剤としての機能が一層好ましく奏され、リチウム２次電池はサイクル特性が一層向上する傾向にある。
　上記リチウム含有化合物の含有量は、好ましくは、上記正極の総質量に対して１．０質量％以上１５．０質量％以下である。この態様によれば、上記のリチウム含有化合物の犠牲正極剤としての機能が一層好ましく奏され、リチウム２次電池はサイクル特性が一層向上する傾向にある。
　上記リチウム含有化合物は、好ましくは、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０．２≦ｘ≦０．８）で表される化合物である。この態様によれば、上記のリチウム含有化合物の犠牲正極剤としての機能が一層好ましく奏され、リチウム２次電池はサイクル特性が一層向上する傾向にある。また、リチウム２次電池の生産性も一層向上する傾向にある。
　上記負極は、Ｃｕ、Ｎｉ、Ｔｉ、Ｆｅ、その他Ｌｉと合金化しない金属、及びこれらの合金、並びに、ステンレス鋼（ＳＵＳ）からなる群より選択される少なくとも１種からなる電極であってよい。この態様によれば、リチウム２次電池は一層安全性及び生産性に優れる傾向にある。
　上記のリチウム２次電池は、好ましくは、エネルギー密度が３５０Ｗｈ／ｋｇ以上である。
　本発明の一実施形態に係るリチウム２次電池は、リチウム２次電池の使用方法であって、４．３Ｖ以上５．０Ｖ以下のカットオフ電圧で充電した後に、少なくとも１回の放電工程と少なくとも１回の充電工程とをこの順に含む充放電サイクルを実施することを含み、上記充放電サイクルにおける充電工程のカットオフ電圧が、４．３Ｖ以上５．０Ｖ以下のカットオフ電圧で実施される第１回目の初期充電のカットオフ電圧未満となるように実施される使用方法により、使用されることが好ましい。
　本発明の一実施形態に係るリチウム２次電池の製造方法は、正極活物質と、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物とを含む正極、及び負極活物質を有しない負極を準備する工程と、上記正極と上記負極とを両者が対向するように配置する工程と、上記正極と上記負極との間に電圧を印加して、カットオフ電圧が４．３Ｖ以上５．０Ｖ以下である充電条件により初期充電する工程と、を含む。
　そのような製造方法によれば、負極が負極活物質を有しないことに起因してエネルギー密度が高い電池を製造することができる。また、そのような製造方法において、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物は上記で詳述したような犠牲正極剤としての機能を有効かつ確実に奏するため、そのような方法により製造されたリチウム２次電池はサイクル特性も優れる。さらに、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物は大気中の微量水分に対する安定性に優れ、厳密に湿度等の制御をすることなしに取り扱うことができるため、上記の製造方法は生産性が高い。
　上記の製造方法において、上記リチウム含有化合物の含有量は、好ましくは、上記正極の総質量に対して１．０質量％以上１５．０質量％以下である。この態様によれば、一層サイクル特性の優れたリチウム２次電池を製造できる傾向にある。
　上記の製造方法において、上記リチウム含有化合物は、好ましくは、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０．２≦ｘ≦０．８）で表される化合物である。この態様によれば、一層サイクル特性の優れたリチウム２次電池を生産性高く製造できる傾向にある。
　上記の製造方法において、上記負極は、好ましくは、Ｃｕ、Ｎｉ、Ｔｉ、Ｆｅ、その他Ｌｉと合金化しない金属、及びこれらの合金、並びに、ステンレス鋼（ＳＵＳ）からなる群より選択される少なくとも１種からなる電極である。この態様によれば、一層安全性及び生産性に優れたリチウム２次電池を製造できる傾向にある。
　本発明によれば、エネルギー密度が高く、サイクル特性及び生産性に優れるリチウム２次電池及びその使用方法、並びにリチウム２次電池の製造方法を提供することができる。
第１の本実施形態に係るリチウム２次電池の概略断面図である。 第１の本実施形態に係るリチウム２次電池の使用の概略断面図である。 第２の本実施形態に係るリチウム２次電池の概略断面図である。 第２の本実施形態に係るリチウム２次電池における緩衝機能層の概略断面図であり、（Ａ）は緩衝機能層の一実施形態であるファイバ状の緩衝機能層を示し、（Ｂ）はファイバ状の緩衝機能層にリチウム金属が析出する析出態様を示し、（Ｃ）はファイバ状の緩衝機能層を構成する部材の一実施形態を示す。
　以下、必要に応じて図面を参照しつつ、本発明の実施の形態（以下、「本実施形態」という。）について詳細に説明する。なお、図面中、同一要素には同一符号を付すこととし、重複する説明は省略する。また、上下左右等の位置関係は、特に断らない限り、図面に示す位置関係に基づくものとする。さらに、図面の寸法比率は図示の比率に限られるものではない。また、以下、複数の本実施形態について詳述するが、各実施形態における記載中、「本実施形態」として記載された内容は、当該実施形態以外の実施形態にも適用することができる。例えば、第１の本実施形態において、「本実施形態の負極は、負極活物質を有しないものである」との記載がある場合、それ以外の実施形態においても当該記載を適用することができる。
［第１実施形態］
（リチウム２次電池）
　図１は、第１の本実施形態（以下、「第１実施形態」という。）に係るリチウム２次電池の概略断面図である。図１に示すように、第１実施形態のリチウム２次電池１００は、正極１１０と、負極活物質を有しない負極１３０とを備える。正極１１０は、正極活物質と、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物とを含むものである。
　また、リチウム２次電池１００は、正極１１０と負極１３０との間にセパレータ１２０を備え、正極１１０は、セパレータ１２０に対向する面とは反対側の面に正極集電体１４０を有する。
　なお、本明細書に開示される本実施形態のリチウム２次電池は、典型的には、電解液を備える液体電解質系リチウム２次電池（特に非水電解液系リチウム２次電池）、ポリマー電解質を備える固体若しくは半固体電解質系リチウム２次電池、又はゲル電解質を備えるゲル電解質系リチウム２次電池である。ただし、本発明の課題を解決する限りにおいて、本実施形態のリチウム２次電池は、それ以外の、例えば無機固体電解質を備える全固体電池であってもよい。
　以下、各構成について詳細に説明する。
（負極）
　本実施形態の負極は、負極活物質を有しないものである。本明細書において、「負極活物質」とは、負極において電極反応、すなわち酸化反応及び還元反応を生じる物質である。具体的には、本明細書における負極活物質としては、リチウム金属、及びリチウム元素（リチウムイオン又はリチウム金属）のホスト物質が挙げられる。リチウム元素のホスト物質とは、リチウムイオン又はリチウム金属を負極に保持するために設けられる物質を意味する。そのような保持の機構としては、特に限定されないが、例えば、インターカレーション、合金化、及び金属クラスターの吸蔵等が挙げられ、典型的には、インターカレーションである。
　本実施形態のリチウム２次電池は、電池の初期充電前に負極が負極活物質を有しないため、負極上にリチウム金属が析出し、及び、その析出したリチウム金属が電解溶出することによって充放電が行われる。したがって、本実施形態のリチウム２次電池は、負極活物質を有するリチウム２次電池と比較して、負極活物質が占める体積及び負極活物質の質量が削減され、電池全体の体積及び質量が小さくなるため、エネルギー密度が原理的に高い。
　上記のとおり本実施形態のリチウム２次電池は、電池の初期充電前に負極が負極活物質を有せず、電池の充電により負極上にリチウム金属が析出し、電池の放電によりその析出したリチウム金属が電解溶出する。したがって、本実施形態のリチウム２次電池において、負極は負極集電体として働く。
　本実施形態のリチウム２次電池をリチウムイオン電池（ＬＩＢ）及びリチウム金属電池（ＬＭＢ）と比較すると、以下の点で異なるものである。
　リチウムイオン電池（ＬＩＢ）において、負極はリチウム元素（リチウムイオン又はリチウム金属）のホスト物質を有し、電池の充電によりかかる物質にリチウム元素が充填され、ホスト物質がリチウム元素を放出することにより電池の放電が行われる。ＬＩＢは、負極がリチウム元素のホスト物質を有する点で、本実施形態のリチウム２次電池とは異なる。
　リチウム金属電池（ＬＭＢ）は、その表面にリチウム金属を有する電極か、あるいはリチウム金属単体を負極として用いて製造される。すなわち、ＬＭＢは、電池を組み立てた直後、すなわち電池の初期充電前に、負極が負極活物質であるリチウム金属を有する点で、本実施形態のリチウム２次電池とは異なる。ＬＭＢは、その製造に、可燃性及び反応性が高いリチウム金属を含む電極を用いるが、本実施形態のリチウム２次電池はリチウム金属を有しない負極を用いて製造されるため、より安全性及び生産性に優れるものである。また、本実施形態のリチウム２次電池は、ＬＭＢに比べてもエネルギー密度及びサイクル特性に優れるものである。
　本明細書において、負極が「負極活物質を有しない」とは、負極が負極活物質を有しないか、実質的に有しないことを意味する。負極が負極活物質を実質的に有しないとは、負極における負極活物質の含有量が、負極全体に対して１０質量％以下であることを意味する。負極における負極活物質の含有量は、負極全体に対して、好ましくは５．０質量％以下であり、１．０質量％以下であってもよく、０．１質量％以下であってもよく、０．０質量％以下であってもよい。負極が負極活物質を有せず、又は、負極における負極活物質の含有量が上記の範囲内にあることにより、リチウム２次電池のエネルギー密度が高いものとなる。
　本明細書において、「負極活物質を有しない負極を備えるリチウム２次電池」とは、電池の初期充電前に、負極が負極活物質を有しないことを意味する。したがって、「負極活物質を有しない負極」との句は、「電池の初期充電前に負極活物質を有しない負極」、「電池の充電状態に依らずリチウム金属以外の負極活物質を有せず、かつ、初期充電前においてリチウム金属を有しない負極」、又は「初期充電前においてリチウム金属を有しない負極集電体」等と換言してもよい。また、「負極活物質を有しない負極を備えるリチウム電池」は、アノードフリーリチウム電池、ゼロアノードリチウム電池、又はアノードレスリチウム電池と換言してもよい。
　本明細書において、電池が「初期充電前である」とは、電池が組み立てられてから第１回目の充電をするまでの状態を意味する。また、電池が「放電終了時である」とは、それ以上電池の電圧を低下させても正極活物質が関与する放電反応が実質的に生じない状態を意味し、その際の電池の電圧は、例えば１．０～３．５Ｖ、２．０～３．２Ｖ、又は２．５～３．０Ｖである。
　本実施形態の負極は、電池の充電状態によらず、リチウム金属以外の負極活物質の含有量が、負極全体に対して１０質量％以下であり、好ましくは５．０質量％以下であり、１．０質量％以下であってもよく、０．１質量％以下であってもよく、０．０質量％以下であってもよく、０質量％であってもよい。
　また、本実施形態の負極は、初期充電前において、リチウム金属の含有量が、負極全体に対して１０質量％以下であり、好ましくは５．０質量％以下であり、より好ましくは１．０質量％以下、又は０．１質量％以下である。本実施形態の負極は、特に好ましくは、初期充電前においてリチウム金属を有せず、すなわち、リチウム金属の含有量が、負極全体に対して０質量％である。
　本実施形態のリチウム２次電池は、電池の電圧が２．５Ｖ以上３．５Ｖ以下である場合において、リチウム金属の含有量が、負極全体に対して１０質量％以下であってもよく（好ましくは５．０質量％以下であり、１．０質量％以下であってもよい。）；又は、電池の電圧が２．５Ｖ以上３．０Ｖ以下である場合において、リチウム金属の含有量が、負極全体に対して１０質量％以下であってもよい（好ましくは５．０質量％以下であり、１．０質量％以下であってもよい。）。
　また、本実施形態のリチウム２次電池において、電池の電圧が４．２Ｖの状態において負極上に析出しているリチウム金属の質量Ｍ４．２に対する、電池の電圧が３．０Ｖの状態において負極上に析出しているリチウム金属の質量Ｍ３．０の比Ｍ３．０／Ｍ４．２は、好ましくは３０％以下であり、より好ましくは２５％以下であり、更に好ましくは２０％以下である。比Ｍ３．０／Ｍ４．２は、１．０％以上であってもよく、２．０％以上であってもよく、３．０％以上であってもよく、４．０％以上であってもよい。
　本明細書における負極活物質の例としては、リチウム金属及びリチウム金属を含む合金、炭素系物質、金属酸化物、並びにリチウムと合金化する金属及び該金属を含む合金が挙げられる。上記炭素系物質としては、特に限定されないが、例えば、グラフェン、グラファイト、ハードカーボン、メソポーラスカーボン、カーボンナノチューブ、及びカーボンナノホーンが挙げられる。上記金属酸化物としては、特に限定されないが、例えば、酸化チタン系化合物、酸化スズ系化合物、及び酸化コバルト系化合物が挙げられる。上記リチウムと合金化する金属としては、例えば、ケイ素、ゲルマニウム、スズ、鉛、アルミニウム、及びガリウムが挙げられる。
　本実施形態の負極としては、負極活物質を有せず、集電体として用いることができるものであれば特に限定されないが、例えば、Ｃｕ、Ｎｉ、Ｔｉ、Ｆｅ、その他Ｌｉと合金化しない金属、及びこれらの合金、並びに、ステンレス鋼（ＳＵＳ）からなる群より選択される少なくとも１種からなる電極が挙げられ、好ましくは、Ｃｕ、Ｎｉ、及びこれらの合金、並びに、ステンレス鋼（ＳＵＳ）からなる群より選択される少なくとも１種からなる電極が挙げられる。このような負極を用いると、電池のエネルギー密度、及び生産性が一層優れたものとなる傾向にある。
　なお、負極にＳＵＳを用いる場合、ＳＵＳの種類としては従来公知の種々のものを用いることができる。上記のような負極材料は、１種を単独で又は２種以上を併用して用いられる。なお、本明細書中、「Ｌｉと合金化しない金属」とは、リチウム２次電池の動作条件においてリチウムイオン又はリチウム金属と反応して合金化することがない金属を意味する。
　本実施形態の負極の平均厚さは、好ましくは４μｍ以上２０μｍ以下であり、より好ましくは５μｍ以上１８μｍ以下であり、更に、好ましくは６μｍ以上１５μｍ以下である。そのような態様によれば、リチウム２次電池における負極の占める体積が減少するため、リチウム２次電池１００のエネルギー密度が一層向上する。
　なお、本明細書において、「平均厚さ」とは、対象の部材を走査型電子顕微鏡や光学顕微鏡を用いて拡大観察し、３箇所以上の部分の厚さを測定したときの相加平均を意味する。
（正極）
　本実施形態の正極は、正極活物質と、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物とを含む。正極が正極活物質を含むため、本実施形態のリチウム２次電池は、安定性に優れ、高い出力電圧を有するものとなる。
　本明細書において、「正極活物質」とは、正極において電極反応、すなわち酸化反応及び還元反応を生じる物質である。具体的には、リチウム元素（典型的には、リチウムイオン）のホスト物質が挙げられる。本明細書における正極活物質は、典型的には、本実施形態のリチウム２次電池の電圧が３．０～４．２Ｖの範囲である条件において酸化還元反応を生じる物質であるか、あるいは、３．０～４．２Ｖ（ｖｓ．Ｌｉ／Ｌｉ＋基準電極）の電位範囲において酸化還元反応を生じる物質である。
　そのような正極活物質としては、特に限定されないが、例えば、金属酸化物及び金属リン酸塩が挙げられる。金属酸化物としては、特に限定されないが、例えば、酸化コバルト系化合物、酸化マンガン系化合物、及び酸化ニッケル系化合物が挙げられる。上記金属リン酸塩としては、特に限定されないが、例えば、リン酸鉄系化合物、及びリン酸コバルト系化合物が挙げられる。
　典型的な正極活物質としては、ＬｉＣｏＯ２、ＬｉＮｉｘＣｏｙＭｎｚＯ（ｘ＋ｙ＋ｚ＝１）、ＬｉＮｉｘＣｏｙＡｌｚＯ（ｘ＋ｙ＋ｚ＝１）、ＬｉＮｉｘＭｎｙＯ（ｘ＋ｙ＝１）、ＬｉＮｉＯ２、ＬｉＭｎ２Ｏ４、ＬｉＦｅＰＯ、ＬｉＣｏＰＯ、ＬｉＦｅＯＦ、ＬｉＮｉＯＦ、及びＬｉＴｉＳ２が挙げられる。上記のような正極活物質は、１種を単独で又は２種以上を併用して用いられる。本実施形態の正極活物質は、好ましくは、ＬｉＣｏＯ２、ＬｉＮｉｘＣｏｙＭｎｚＯ（ｘ＋ｙ＋ｚ＝１）、ＬｉＮｉｘＣｏｙＡｌｚＯ（ｘ＋ｙ＋ｚ＝１）、ＬｉＮｉｘＭｎｙＯ（ｘ＋ｙ＝１）、ＬｉＮｉＯ２、及びＬｉＭｎ２Ｏ４からなる群より選択される少なくとも１種である。
　本実施形態の正極は、正極活物質に加えて、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物を含む。
　Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物は、上述したような正極活物質の充放電電位範囲において、酸化反応を生じ得る一方、還元反応を実質的に生じない。したがって、本実施形態のリチウム２次電池を初期充電すると、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物は酸化反応を生じると共にリチウムイオンを放出し、外部回路を通じて負極に電子を放出する。その結果、上記リチウム含有化合物に由来するリチウムイオンは、リチウム金属として負極の表面に析出する。また、本実施形態のリチウム２次電池を初期充電完了後に放電する（すなわち、初期放電する）と、負極表面に析出したリチウム金属が電解溶出し、外部回路を通じて負極から正極に電子が移動するものの、上記リチウム含有化合物は、通常の放電条件では還元反応を実質的に生じず、酸化反応を生じる前の状態に戻ることが実質的に不可能である。
　したがって、本実施形態のリチウム２次電池を初期充電の後に放電させると、上記リチウム含有化合物に由来するリチウム金属は、そのほとんどが負極上に残留することとなり、電池の放電完了後においても、負極上に一部のリチウム金属が残留することとなる。当該残留リチウム金属は、初期放電に続く充電ステップにおいて、更なるリチウム金属が負極表面上に析出する際の足場となると考えられ、リチウム金属が負極表面上に均一に析出することを補助すると考えられる。その結果、本実施形態のリチウム２次電池では負極上にデンドライト状のリチウム金属が成長することが抑制され、本実施形態のリチウム２次電池はサイクル特性に優れたものとなる。ただし、本実施形態に係るリチウム２次電池がサイクル特性に優れる要因はこれに限定されない。
　電池の分野において、一般的に、正極に添加される添加剤であって、正極活物質の充放電電位範囲において酸化反応を生じ、かつ、還元反応を実質的に生じない添加剤を犠牲正極剤という。犠牲正極剤としては各種の電池において様々な材料が提案されている。
　本発明者らは、負極活物質を有しない負極を備えるリチウム２次電池（アノードフリー２次電池）において、そのような犠牲正極剤の中でも、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物を用いるとサイクル特性が一層向上することを見出した。
　また、本発明者らは、その要因として少なくとも以下のことを見出した。
（１）グラファイト材料等の負極活物質を有する負極を用いたリチウムイオン電池では、カットオフ電圧が４．３Ｖを超えないように初期充電を行うことが通常であり、それを超えて充電を行った場合には、電解液及び／又は活物質が分解等することによりサイクル特性が低下する。他方、負極活物質を有しない負極を備えるリチウム２次電池（アノードフリー２次電池）では、初期充電においてカットオフ電圧が４．３Ｖを超えて５．０Ｖ程度に到達するまで充電したとしてもサイクル特性の低下が生じないことを本発明者らは見出した。これは、アノードフリー２次電池では、負極電位が相対的に低いことが寄与しているものと考えられる。
（２）Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物を、負極活物質を有しない負極を備えるリチウム２次電池（アノードフリー２次電池）に犠牲正極剤として含有させた場合、初期充電において電池の電圧が４．３Ｖ程度となる条件で当該リチウム含有化合物がリチウムイオンを放出することを見出した。
　また、本発明者らは、（３）Ｌｉ６ＭｎＯ４で表されるリチウム含有化合物を犠牲正極剤として用いる場合、カットオフ電圧を５．０Ｖ程度としても十分にリチウムの放出反応が生じず、Ｌｉ６ＭｎＯ４は犠牲正極剤としての機能を十分に発揮しないこと、（４）Ｌｉ６ＣｏＯ４で表されるリチウム含有化合物を犠牲正極剤として用いる場合、当該リチウム含有化合物が大気中に含まれる微量水分に対して不安定であること、（５）驚くべきことにＬｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物であれば上記の（３）及び（４）に記載の問題が生じないことを見出した。特に、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物はＬｉ６ＣｏＯ４で表されるリチウム含有化合物に比べて大気中における安定性が高い。具体的には、Ｌｉ６ＣｏＯ４のようなアルカリ性が高い材料を使用して正極を作製しようとすると、ポリフッ化ビニリデン（ＰＶＤＦ）等のバインダーと混錬して正極合材スラリーを作製する際に、Ｌｉ６ＣｏＯ４が大気中の水分を吸収することで、正極合材スラリーが急激な粘度上昇及び／又はゲル化を生じてしまうが、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物はそのような問題が生じにくい。
　したがって、本実施形態のリチウム２次電池は、犠牲正極剤として大気中における安定性が高いＬｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物を用いるため、正極を作製する際に大気中の湿度等を厳密に調整する必要がなく、通常のドライルーム及び／又はグローブボックスにて製造することができ、生産性を高めることができる。なお、本明細書中、「生産性が高い」とは、時間当たりに製造できるリチウム２次電池の数が多いことだけでなく、特別な装置及び／又は環境を必要とせずにリチウム２次電池を製造することができることをも包含するものとする。
　本実施形態の正極中、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物のｘは、０より大きい値であれば特に限定されないが、リチウム２次電池の生産性向上の観点から、好ましくは０．１以上である。同様の観点から上記ｘの値は、より好ましくは０．２以上、更に好ましくは０．３以上であり、０．４以上、０．５以上、又は０．６以上であってもよい。
　また、上記ｘの値は、１より小さい値であれば特に限定されないが、リチウム２次電池のサイクル特性向上の観点から、好ましくは０．９以下、より好ましくは０．８以下、更に好ましくは０．７以下である。上記ｘの値は、０．６以下、０．５以下、又は０．４以下であってもよい。
　上記ｘの値は、上記の上限値及び下限値を任意に組み合わせて得られる範囲内としてもよく、例えば０．１≦ｘ≦０．９、０．２≦ｘ≦０．８、又は０．３≦ｘ≦０．７であってよい。
　本実施形態の正極は、組成が異なる上記リチウム含有化合物を２種以上含んでいてもよく、１種のリチウム含有化合物のみを含んでいてもよい。また、上記リチウム含有化合物は、市販のものを用いてもよく、従来公知の方法により製造してもよい。上記リチウム含有化合物の具体的な製造方法は後述する。
　上記のとおり、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物は、初期充電において電池の電圧が４．３Ｖ程度となる条件でリチウムイオンを放出し始める傾向にある。したがって、本実施形態のリチウム２次電池は、好ましくはカットオフ電圧が４．３Ｖ以上５．０Ｖ以下である充電条件により初期充電されたものである。そのような条件で初期充電をすることにより、リチウム２次電池のサイクル特性が一層向上する傾向にある。
　ここで、本明細書において、「カットオフ電圧が値Ｘである充電条件により初期充電される」とは、電池が組み立てられてから第１回目の充電をする際に、電池の電圧が値Ｘになるまで充電を続けることを意味する。
　リチウム２次電池のサイクル特性が一層向上する観点から、本実施形態のリチウム２次電池は、より好ましくはカットオフ電圧が４．３Ｖ超、又は４．４Ｖ以上である充電条件により初期充電される。初期充電におけるカットオフ電圧は、４．５Ｖ以上、４．６Ｖ以上、又は４．７Ｖ以上としてもよい。
　また、本実施形態のリチウム２次電池は、好ましくはカットオフ電圧が５．０Ｖ以下である充電条件により初期充電される。そのような条件で初期充電をすることにより、正極活物質及び／又は電解質の分解が確実に抑制されるため、リチウム２次電池のサイクル特性が一層向上する傾向にある。
　リチウム２次電池のサイクル特性が一層向上する観点から、本実施形態のリチウム２次電池は、カットオフ電圧が、より好ましくは５．０Ｖ未満、又は４．９Ｖ以下、更に好ましくは４．８Ｖ以下、更により好ましくは４．７Ｖ以下である充電条件により初期充電される。初期充電におけるカットオフ電圧は、４．６Ｖ以下、又は４．５Ｖ以下としてもよい。
　上記初期充電におけるカットオフ電圧は、上記の上限値及び下限値を任意に組み合わせて得られる範囲内としてもよく、例えば４．３Ｖ超５．０Ｖ未満、４．４Ｖ以上４．９Ｖ以下、又は４．４Ｖ以上４．７Ｖ以下であってよい。
　なお、本実施形態のリチウム２次電池は、初期充電後に使用者に提供されてもよく、初期充電前に使用者に提供されてもよい。初期充電前に使用者に提供される場合、本実施形態のリチウム２次電池は、後述する本実施形態のリチウム２次電池の使用方法に従って、使用されることが好ましい。具体的には、最初の使用の際に、カットオフ電圧が４．３Ｖ以上５．０Ｖ以下である充電条件により充電されることが好ましい。
　上記のとおり、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物は、上述したような正極活物質の充放電電位範囲において、酸化反応を生じ得る一方、還元反応を実質的に生じない。本明細書において、「正極活物質の充放電電位範囲において酸化反応を生じ得る」とは、正極活物質の充放電電位範囲において、酸化反応を生じてリチウムイオン及び電子を放出すること（酸化反応により分解され、リチウムイオンを放出することも含む。）が可能であることを意味する。また、「正極活物質の充放電電位範囲において還元反応を実質的に生じない」とは、正極活物質の充放電電位範囲において、当業者にとって通常の反応条件では、還元反応を生じてリチウムイオン及び電子を受け取ること、又は還元反応を介して生成することが不可能、又は実質的に不可能であることを意味する。「当業者にとって通常の反応条件」とは、例えば、リチウム２次電池を放電する際の条件を意味する。
　ただし、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物は、電池の電圧を通常の電池の作動電圧領域よりも十分小さくすることにより還元反応を生じてリチウムイオン及び電子を受け取ることができる。そのような条件としては、電池の電圧が例えば２．０Ｖ以下である条件が挙げられる。
　本実施形態のリチウム２次電池の初期充電において、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物は、容量比で、製造時の添加量の例えば５０％以上、６０％以上、７０％以上、８０％以上、９０％以上、９５％以上、又は９９％以上がリチウムイオンを放出した酸化状態となる。
　本実施形態のリチウム２次電池の初期放電において、初期充電により酸化状態となったリチウム含有化合物は、実質的に還元されない。リチウム含有化合物における、初期充電の容量に対する初期放電の容量は、例えば２０％以下（例えば、２０％以下、１５％以下、１０％以下、５％以下、１％以下、又は０％）である。
　なお、本明細書において、「正極活物質の充放電電位範囲」とは、正極に含まれる正極活物質の酸化反応及び還元反応が行われ得る電位範囲を意味する。具体的な値は、正極活物質の種類に依存するが、典型的には、Ｌｉ／Ｌｉ＋基準電極に対して、２．５Ｖ以上、２．７Ｖ以上、３．０Ｖ以上、３．２Ｖ以上、又は３．５Ｖ以上であり、かつ、４．６V以下、４．５Ｖ以下、４．４Ｖ以下、４．３Ｖ以下、４．２Ｖ以下、４．１Ｖ以下、又は４．０Ｖ以下である。正極活物質の充放電電位範囲の代表的な範囲は、３．０Ｖ以上４．２Ｖ以下（ｖｓ．Ｌｉ／Ｌｉ＋基準電極）であり、その上限値及び下限値は、上述した任意の数値に、独立に置き換えることができる。
　上述したＬｉ／Ｌｉ＋基準電極に対する正極活物質の充放電電位範囲は、リチウム２次電池の動作電圧範囲を参照してもよく、例えば、リチウム２次電池の動作電圧が３．０Ｖ以上４．２Ｖ以下である場合、Ｌｉ／Ｌｉ＋基準電極に対する正極活物質の充放電電位範囲を３．０Ｖ以上４．２Ｖ以下と見積もることができる。
　すなわち、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物は、リチウム２次電池の動作電圧範囲において、酸化反応を生じ得る一方、還元反応を実質的に生じないと換言してもよい。なお、典型的には、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物は、リチウム２次電池の動作電圧範囲よりもより高電圧側で主たる酸化反応を生じる傾向にある。
　本実施形態の正極は、正極活物質及びＬｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物以外の成分を含んでいてもよい。そのような成分としては、特に限定されないが、例えば、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物以外の犠牲正極剤、導電助剤、バインダー、及び電解質が挙げられる。
　Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物以外の犠牲正極剤としては、特に限定されないが、例えば、Ｌｉ２Ｏ２のようなリチウム酸化物；Ｌｉ３Ｎのようなリチウム窒化物；Ｌｉ２Ｓ－Ｐ２Ｓ５、Ｌｉ２Ｓ－ＬｉＣｌ、Ｌｉ２Ｓ－ＬｉＢｒ、及びＬｉ２Ｓ－ＬｉＩのようなリチウム硫化物系固溶体；Ｌｉ１＋ｘ（Ｔｉ１－ｙＦｅｙ）１－ｘＯ２（０＜ｘ≦０．２５、０．４＜ｙ≦０．９）、Ｌｉ２－ｘＴｉ１－ｚＦｅｚＯ３－ｙ（０≦ｘ＜２、０≦ｙ≦１、０．０５≦ｚ≦０．９５）、及びＬｉ５ＦｅＯ４のような鉄系リチウム酸化物等が挙げられる。上記のようなリチウム含有化合物以外の犠牲正極剤は、１種を単独で又は２種以上を併用して用いられる。
　導電助剤としては、特に限定されないが、例えば、カーボンブラック、シングルウォールカーボンナノチューブ（ＳＷＣＮＴ）、マルチウォールカーボンナノチューブ（ＭＷＣＮＴ）、カーボンナノファイバー（ＣＦ）、及びアセチレンブラックが挙げられる。
　また、バインダーとしては、特に限定されないが、例えば、ポリビニリデンフロライド、ポリテトラフルオロエチレン、スチレンブタジエンゴム、アクリル樹脂、及びポリイミド樹脂等が挙げられる。上記のような導電助剤及びバインダーは、それぞれ、１種を単独で又は２種以上を併用して用いられる。
　本実施形態の正極が含み得る電解質としては、例えばポリマー電解質、ゲル電解質、及び無機固体電解質等が挙げられ、典型的にはポリマー電解質又はゲル電解質である。ポリマー電解質及びゲル電解質としては、後述するものを用いることができる。上記のような電解質は、１種を単独で又は２種以上を併用して用いられる。
　本実施形態の正極における各成分の含有量は特に限定されない。正極における各成分の含有量は電池の充電状態によっても変わり得るが、例えば製造時における各成分の配合比によって規定することができる。あるいは、放電状態（放電終了時）における各成分の含有量によって規定してもよい。
　本実施形態の正極の製造時において、正極活物質及びＬｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物の配合量の合計は、正極の総質量に対して、例えば５０質量％以上１００質量％以下、又は７０質量％以上９９質量％以下であってよい。当該正極活物質及びリチウム含有化合物の配合量の合計は、正極の総質量に対して、好ましくは６０質量％以上であり、より好ましくは７０質量％以上であり、更に好ましくは８０質量％以上であり、更により好ましくは９０質量％以上である。当該正極活物質及びリチウム含有化合物の配合量の合計は、正極の総質量に対して、好ましくは９９質量％以下であり、より好ましくは９８質量％以下である。
　本実施形態のリチウム２次電池の放電終了時における正極活物質及びＬｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物の含有量の合計は、正極の総質量に対して、例えば５０質量％以上１００質量％以下、又は７０質量％以上９９質量％以下であってよい。当該正極活物質及びリチウム含有化合物の含有量の合計は、正極の総質量に対して、好ましくは６０質量％以上であり、より好ましくは７０質量％以上であり、更に好ましくは８０質量％以上であり、更により好ましくは９０質量％以上である。当該正極活物質及びリチウム含有化合物の含有量の合計は、正極の総質量に対して、好ましくは９９質量％以下であり、より好ましくは９８質量％以下である。
　本実施形態の正極の製造時において、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物の配合量は、正極の総質量に対して、例えば１．０質量％以上１５質量％以下であってよい。当該リチウム含有化合物の含有量は、正極の総質量に対して、好ましくは１．０質量％以上であり、より好ましくは２．０質量％以上であり、更に好ましくは３．０質量％以上である。また、当該リチウム含有化合物の含有量は、正極の総質量に対して、好ましくは１５質量％以下であり、より好ましくは１２質量％以下であり、更に好ましくは１０質量％以下であり、８．０質量％以下又は５．０質量％以下であってもよい。
　電池の初期充電によって、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物の少なくとも一部はリチウムイオン及び電子を放出して酸化状態となるものの、電池内部におけるＬｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物の酸化状態及び還元状態の総和は初期充電の前後で一定であり、かつ、電池の充電状態にもよらず一定である。
　したがって、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物の酸化状態及び還元状態の含有量の合計は、正極の総質量に対して、例えば１．０質量％以上１５質量％以下であってよい。当該酸化状態及び還元状態の含有量の合計は、正極の総質量に対して、好ましくは１．０質量％以上であり、より好ましくは２．０質量％以上であり、更に好ましくは３．０質量％以上である。また、当該酸化状態及び還元状態の含有量の合計は、正極の総質量に対して、好ましくは１５質量％以下であり、より好ましくは１２質量％以下であり、更に好ましくは１０質量％以下であり、８．０質量％以下又は５．０質量％以下であってもよい。
　Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物の酸化状態及び還元状態の含有量の合計は正極の製造時における当該リチウム含有化合物の配合量と同等である。また、電池を通常の充放電サイクルにおける電圧範囲よりも低電圧（例えば１．０Ｖ程度）まで掃引して当該リチウム含有化合物をＬｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表される還元状態に戻した後、従来公知の方法でＬｉ６ＭｎｘＣｏ１－ｘＯ４の含有量を測定することにより当該酸化状態及び還元状態の含有量の合計を算出することも可能である。
　なお、正極における正極活物質及びＬｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物の含有量は、例えばＸ線回折測定（ＸＲＤ）でピークの相対強度を比較する方法、もしくはＲｉｅｔｖｅｌｄ法により測定することができる。
　導電助剤について、本実施形態の正極の製造時の配合量及び電池の放電終了時における含有量は、正極の総質量に対して、例えば、０．５質量％３０質量％以下、１．０質量％２０質量％以下、又は１．５質量％１０質量％以下であってもよい。
　バインダーについて、本実施形態の正極の製造時の配合量及び電池の放電終了時における含有量は、正極の総質量に対して、例えば、０．５質量％３０質量％以下、１．０質量％２０質量％以下、又は１．５質量％１０質量％以下であってもよい。
　電解質について、本実施形態の正極の製造時の配合量及び電池の放電終了時における含有量は、正極の総質量に対して、例えば、０．５質量％３０質量％以下、１．０質量％２０質量％以下、又は１．５質量％１０質量％以下であってもよい。
　Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物以外の犠牲正極剤について、本実施形態の正極の製造時の配合量は、正極の総質量に対して、例えば、０．５質量％３０質量％以下、１．０質量％２０質量％以下、又は１．５質量％１０質量％以下であってもよい。
　本実施形態の正極の平均厚さは、例えば１０μｍ以上３００μｍ以下であり、好ましくは３０μｍ以上２００μｍ以下、又は５０μｍ以上１５０μｍ以下である。ただし、正極の平均厚さは、所望する電池の容量に応じて適宜調整することができる。
（正極集電体）
　正極１１０の片側には、正極集電体１４０が形成されている。本実施形態の正極集電体は、電池においてリチウムイオンと反応しない導電体であれば特に限定されない。そのような正極集電体としては、例えば、アルミニウムが挙げられる。
　本実施形態の正極集電体の平均厚さは、好ましくは４μｍ以上２０μｍ以下であり、より好ましくは５μｍ以上１８μｍ以下であり、更に、好ましくは６μｍ以上１５μｍ以下である。そのような態様によれば、リチウム２次電池における正極集電体の占める体積が減少するため、リチウム２次電池のエネルギー密度が一層向上する。
（セパレータ）
　本実施形態のセパレータは、正極と負極とを隔離することにより電池が短絡することを防ぎつつ、正極と負極との間の電荷キャリアとなるリチウムイオンのイオン伝導性を確保するための部材である。すなわち、セパレータ１２０は、正極１１０と負極１３０を隔離する機能、及びリチウムイオンのイオン伝導性を確保する機能を有する。このようなセパレータとして、上記の２つの機能を有する１種の部材を単独で用いてもよいし、上記の１つの機能を有する部材を２種以上組み合わせて用いてもよい。セパレータとしては、上述した機能を担うものであれば特に限定されないが、例えば、絶縁性を有する多孔質の部材、ポリマー電解質、ゲル電解質、及び無機固体電解質が挙げられ、典型的には絶縁性を有する多孔質の部材、ポリマー電解質、及びゲル電解質からなる群より選択される少なくとも１種である。
　セパレータが絶縁性を有する多孔質の部材を含む場合、かかる部材の細孔にイオン伝導性を有する物質が充填されることにより、かかる部材はイオン伝導性を発揮する。充填される物質としては、電解液、ポリマー電解質、及びゲル電解質が挙げられる。
　本実施形態のセパレータは、絶縁性を有する多孔質の部材、ポリマー電解質、若しくはゲル電解質を１種単独で、又はそれらを２種以上組み合わせて用いることができる。ただし、セパレータとして絶縁性を有する多孔質の部材を単独で用いる場合、イオン伝導性を確保するためにリチウム２次電池は電解液を更に備える必要がある。
　上記の絶縁性を有する多孔質の部材を構成する材料としては、特に限定されないが、例えば絶縁性高分子材料が挙げられ、具体的には、ポリエチレン（ＰＥ）、及びポリプロピレン（ＰＰ）が挙げられる。すなわち、本実施形態のセパレータは、多孔質のポリエチレン（ＰＥ）膜、多孔質のポリプロピレン（ＰＰ）膜、又はこれらの積層構造であってよい。
　上記のポリマー電解質としては、特に限定されないが、例えば高分子及び電解質を主に含む固体ポリマー電解質、並びに高分子、電解質、及び可塑剤を主に含む半固体ポリマー電解質が挙げられる。
　上記のゲル電解質としては、特に限定されないが、例えば高分子及び液体電解質（すなわち、溶媒と電解質）を主に含むものが挙げられる。
　ポリマー電解質及びゲル電解質が含み得る高分子としては、特に限定されないが、例えばエーテル及びエステル等の酸素原子を含む官能基、ハロゲン基、並びにシアノ基のような極性基を含む高分子が挙げられる。具体的には、ポリエチレンオキサイド（ＰＥＯ）のような主鎖及び／又は側鎖にエチレンオキサイドユニットを有する樹脂、ポリプロピレンオキサイド（ＰＰＯ）のような主鎖及び／又は側鎖にプロピレンオキサイドユニットを有する樹脂、アクリル樹脂、ビニル樹脂、エステル樹脂、ナイロン樹脂、ポリビニリデンフロライド（ＰＶＤＦ）、ポリアクリロニトリル（ＰＡＮ）、ポリシロキサン、ポリホスファゼン、ポリメタクリル酸メチル、ポリアミド、ポリイミド、アラミド、ポリ乳酸、ポリウレタン、ポリアセタール、ポリスルホン、ポリエチレンカーボネート、ポリプロピレンカーボネート、及びポリテトラフロロエチレンが挙げられる。上記のような樹脂は、１種を単独で又は２種以上を併用して用いられる。
　ポリマー電解質及びゲル電解質に含まれる電解質としては、Ｌｉ、Ｎａ、Ｋ、Ｃａ、及びＭｇの塩等が挙げられる。典型的には本実施形態において、ポリマー電解質及びゲル電解質はリチウム塩を含む。
　リチウム塩としては、特に限定されないが、例えば、ＬｉＩ、ＬｉＣｌ、ＬｉＢｒ、ＬｉＦ、ＬｉＢＦ４、ＬｉＰＦ６、ＬｉＡｓＦ６、ＬｉＳＯ３ＣＦ３、ＬｉＮ（ＳＯ２Ｆ）２、ＬｉＮ（ＳＯ２ＣＦ３）２、ＬｉＮ（ＳＯ２ＣＦ３ＣＦ３）２、ＬｉＢ（Ｏ２Ｃ２Ｈ４）２、ＬｉＢ（Ｃ２Ｏ４）２、ＬｉＢ（Ｏ２Ｃ２Ｈ４）Ｆ２、ＬｉＢ（ＯＣＯＣＦ３）４、ＬｉＮＯ３、及びＬｉ２ＳＯ４が挙げられ、好ましくはＬｉＮ（ＳＯ２Ｆ）２、ＬｉＮ（ＳＯ２ＣＦ３）２、及びＬｉＮ（ＳＯ２ＣＦ３ＣＦ３）２からなる群より選択される少なくとも１種である。上記のような塩、又はリチウム塩は、１種を単独で又は２種以上を併用して用いられる。
　ポリマー電解質及びゲル電解質における高分子とリチウム塩との配合比は、高分子の有する極性基と、リチウム塩の有するリチウム原子の比によって定めてもよい。例えば高分子が酸素原子を有する場合、高分子の有する酸素原子の数と、リチウム塩の有するリチウム原子の数の比（［Ｌｉ］／［Ｏ］）によって定めてもよい。ポリマー電解質及びゲル電解質において、高分子とリチウム塩との配合比は、上記比（［Ｌｉ］／［Ｏ］）が、例えば、０．０２以上０．２０以下、０．０３以上０．１５以下、又は０．０４以上０．１２以下になるように調整することができる。
　ゲル電解質に含まれる溶媒としては、特に限定されないが、例えば後述する電解液に含まれ得る溶媒を、１種単独で又は２種以上を組み合わせて用いることができる。好ましい溶媒の例についても後述する電解液におけるものと同様である。
　半固体ポリマー電解質に含まれる可塑剤としては、特に限定されないが、例えばゲル電解質に含まれ得る溶媒と同様の成分、及び種々のオリゴマーが挙げられる。
　本実施形態のセパレータは、セパレータ被覆層により被覆されていてもよい。セパレータ被覆層は、セパレータの両面を被覆していてもよく、片面のみを被覆していてもよい。セパレータ被覆層は、リチウムイオンと反応しない部材であれば特に限定されないが、セパレータと、セパレータに隣接する層とを強固に接着させることができるものであると好ましい。そのようなセパレータ被覆層としては、特に限定されないが、例えば、ポリビニリデンフロライド（ＰＶＤＦ）、スチレンブタジエンゴムとカルボキシメチルセルロースの合材（ＳＢＲ－ＣＭＣ）、ポリアクリル酸（ＰＡＡ）、ポリアクリル酸リチウム（Ｌｉ－ＰＡＡ）、ポリイミド（ＰＩ）、ポリアミドイミド（ＰＡＩ）、及びアラミドのようなバインダーを含むものが挙げられる。セパレータ被覆層は、上記バインダーにシリカ、アルミナ、チタニア、ジルコニア、酸化マグネシウム、水酸化マグネシウム、及び硝酸リチウム等の無機粒子を添加させてもよい。
　本実施形態のセパレータの平均厚さは、好ましくは２０μｍ以下であり、より好ましくは１８μｍ以下であり、更に好ましくは１５μｍ以下である。そのような態様によれば、リチウム２次電池におけるセパレータの占める体積が減少するため、リチウム２次電池のエネルギー密度が一層向上する。また、セパレータの平均厚さは、好ましくは５μｍ以上であり、より好ましくは７μｍ以上であり、更に好ましくは１０μｍ以上である。そのような態様によれば、正極と負極とを一層確実に隔離することができ、電池が短絡することを一層抑制することができる。
（電解液）
　リチウム２次電池１００は、電解液を更に備えると好ましい。
　電解液は、溶媒及び電解質を含む液体であり、イオン伝導性を有する。電解液は、液体電解質と換言してもよく、リチウムイオンの導電経路として作用する。このため、リチウム２次電池が電解液を有すると、内部抵抗が一層低下し、エネルギー密度、容量、及びサイクル特性が一層向上する傾向にある。
　電解液は、セパレータ１２０に浸潤させてもよく、負極、セパレータ、正極及び正極集電体の積層体と共に電解液を封入したものをリチウム２次電池１００の完成品としてもよい。
　電解液に含まれる電解質としては、ポリマー電解質及びゲル電解質に含まれ得る電解質、特に上述のリチウム塩を１種単独で又は２種以上組み合わせて用いることができる。好ましいリチウム塩は、ポリマー電解質及びゲル電解質におけるものと同様である。
　電解液に含まれる溶媒としては、例えばフッ素原子を有する非水溶媒（以下、「フッ素化溶媒」という。）及びフッ素原子を有しない非水溶媒（以下、「非フッ素溶媒」という。）が挙げられる。
　フッ素化溶媒としては、特に限定されないが、例えば、１，１，２，２－テトラフルオロエチル－２，２，３，３－テトラフルオロプロピルエーテル、１，１，２，２－テトラフルオロエチル－２，２，２－トリフルオロエチルエーテル、及び１Ｈ，１Ｈ，５Ｈ－オクタフルオロペンチル－１，１，２，２－テトラフルオロエチルエーテル等が挙げられる。
　非フッ素溶媒としては、特に限定されないが、例えば、トリエチレングリコールジメチルエーテル、テトラエチレングリコールジメチルエーテル、１，２－ジメトキシエタン、ジメトキシエタン、ジメトキシプロパン、ジメトキシブタン、ジエチレングリコールジメチルエーテル、アセトニトリル、炭酸ジメチル、炭酸ジエチル、炭酸エチルメチル、エチレンカーボネート、プロピレンカーボネート、クロロエチレンカーボネート、メチルアセテート、エチルアセテート、プロピルアセテート、メチルプロピオネート、エチルプロピオネート、リン酸トリメチル、リン酸トリエチル、及び１２－クラウン－４が挙げられる。
　上記フッ素化溶媒及び／又は非フッ素溶媒は１種を単独で、又は２種以上を任意の割合で自由に組み合わせて用いることができる。フッ素化溶媒と非フッ素溶媒の含有量は特に限定されず、溶媒全体に対するフッ素化溶媒の割合が０～１００体積％であってもよく、溶媒全体に対する非フッ素溶媒の割合が０～１００体積％であってもよい。
（リチウム２次電池の使用）
　図２に第１実施形態のリチウム２次電池の１つの使用態様を示す。リチウム２次電池１００には、正極集電体１４０及び負極１３０に、リチウム２次電池１００を外部回路に接続するための正極端子２２０及び負極端子２１０がそれぞれ接合されている。負極端子２１０を外部回路の一端に、正極端子２２０を外部回路のもう一端に接続することにより、リチウム２次電池１００は充放電される。
　より具体的には、正極端子２２０及び負極端子２１０に外部電源を繋ぎ、負極端子２１０（負極１３０）から外部電源を通り正極端子２２０（正極１１０）へと電流が流れるような電圧を印加すると、リチウム２次電池１００が充電され、負極表面にリチウム金属の析出が生じる。充電後のリチウム２次電池１００について、所望の外部回路を介して正極端子２２０及び負極端子２１０を接続するとリチウム２次電池１００が放電される。これにより、負極表面に生じたリチウム金属の析出が電解溶出する。
　上述のとおり、本実施形態の正極に含まれる上記リチウム含有化合物は、電池の電圧が４．３Ｖ程度となる条件でリチウムイオンを放出する。したがって、本実施形態のリチウム２次電池は、以下の方法により使用されることが好ましい。
　すなわち、本実施形態のリチウム２次電池の使用方法は、４．３Ｖ以上５．０Ｖ以下のカットオフ電圧で充電した後に、少なくとも１回の放電工程と少なくとも１回の充電工程とを含む充放電サイクルを実施することを含み、上記充放電サイクルにおける充電工程のカットオフ電圧が、４．３Ｖ以上５．０Ｖ以下のカットオフ電圧で実施される第１回目の充電におけるカットオフ電圧未満となるように実施される。
　そのような使用方法によれば、本実施形態のリチウム２次電池が確実に４．３Ｖ以上５．０Ｖ以下のカットオフ電圧で充電されるため、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物が有効かつ確実に犠牲正極剤として作用する。また、その後の充放電サイクルにおける充電工程において、カットオフ電圧を第１回目の充電時のカットオフ電圧未満とすることによりリチウム２次電池内の各構成（特に正極活物質及び電解液を含む場合は電解液中の溶媒）が分解されることを有効かつ確実に抑制することができ、サイクル特性を一層向上させることができる。
　本実施形態のリチウム２次電池の使用方法において、充放電サイクルを実施する前の第１回目の充電におけるカットオフ電圧は、好ましくは４．３Ｖ超であり、より好ましくは４．４Ｖ以上であり、４．５Ｖ以上、４．６Ｖ以上、又は４．７Ｖ以上としてもよい。また、当該カットオフ電圧は、好ましくは５．０Ｖ未満であり、より好ましくは４．９Ｖ以下であり、更に好ましくは４．８Ｖ以下であり、更により好ましくは４．７Ｖ以下である。
　上記第１回目の充電におけるカットオフ電圧は、上記の上限値及び下限値を任意に組み合わせて得られる範囲内としてもよく、例えば４．３Ｖ超５．０Ｖ未満、４．４Ｖ以上４．９Ｖ以下、又は４．４Ｖ以上４．７Ｖ以下であってよい。充放電サイクルを実施する前の第１回目の充電におけるカットオフ電圧を上記の範囲内とすることにより、リチウム２次電池のサイクル特性を一層高めることができる傾向にある。
　４．３Ｖ以上５．０Ｖ以下のカットオフ電圧で充電した後に実施される充放電サイクルの回数は特に限定されず、例えば放電容量が上記第１回目の充電の直後に行われる第１回目の充放電サイクルの放電工程における放電容量の８０％以下、７０％以下、又は６０％以下になるまで充放電サイクルを繰り返してもよい。
　上記充放電サイクルは、充電工程のカットオフ電圧が上記第１回目の充電時のカットオフ電圧未満となるように実施される限りどのような条件であってもよい。充電工程のカットオフ電圧は、例えば上記第１回目の充電時のカットオフ電圧より０．１Ｖ、０．２Ｖ、又は０．３Ｖ小さいカットオフ電圧としてもよい。
　また、上記充放電サイクルは、好ましくは、さらにＬｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物が還元反応を生じない電圧範囲内で実施される。すなわち、上記充放電サイクルは、好ましくは、充電工程のカットオフ電圧が上記第１回目の充電時のカットオフ電圧未満であり、かつ、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物が還元反応を生じない電圧範囲内で実施される。そのような電圧の範囲としては、例えば２．５Ｖ以上４．６Ｖ以下、好ましくは２．５Ｖ以上４．３Ｖ以下、より好ましくは３．０Ｖ以上４．２Ｖ以下である。
　なお、本実施形態のリチウム２次電池の使用方法として上記した内容は本実施形態のリチウム２次電池を使用する際の好適な方法を示すものに過ぎず、本実施形態のリチウム２次電池の使用方法を限定するものではない。例えば、本実施形態のリチウム２次電池の初期充電においてカットオフ電圧は４．３Ｖ以上５．０Ｖ以下の範囲外としてもよく、その後の充放電サイクルの電圧範囲が第１回目の充電時のカットオフ電圧以上となってもよい。
（リチウム２次電池の製造方法）
　図１に示すようなリチウム２次電池１００の製造方法としては、上述の構成を備えるリチウム２次電池を製造することができる方法であれば特に限定されないが、例えば以下のような方法が挙げられる。なお、本実施形態のリチウム２次電池、特に本実施形態の正極は、一定程度湿度が排除された環境、例えば露点－５０～－１０℃のドライルーム等によって製造されることが好ましい。
　正極１１０は例えば以下のようにして、正極集電体１４０上に形成する。上述した正極活物質、及びＬｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物に加えて、任意選択的に、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物以外の犠牲正極剤、導電助剤、バインダー、及び／又は電解質を混合し、正極混合物を得る。その配合比は、各成分が上述した範囲内となるように適宜調整すればよい。
　得られた正極混合物を、所定の厚さ（例えば、５μｍ以上１ｍｍ以下）を有する正極集電体としての金属箔（例えば、Ａｌ箔）の片面に塗布し、プレス成型する。得られた成型体を、打ち抜き加工により、所定のサイズに打ち抜き、正極１１０を得る。
　なお、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物は、Ｌｉ２Ｏ、ＭｎＯ、及びＣｏＯの粉末を粉砕、混合したものを、例えば６００～１０００℃の条件にて、５～１００時間焼成することで製造することができる。焼成時の雰囲気条件はアルゴン及び窒素ガス等の不活性ガス雰囲気であることが好ましく、さらに微量の水素ガスを含ませてもよい。水素ガスの割合は例えば体積比で０．１～１０％とすることができる。
　Ｌｉ２Ｏ、ＭｎＯ、及びＣｏＯの粉末は市販されているものを用いればよく、その混合比（モル比）は、Ｌｉ２Ｏ：（ＭｎＯ、ＣｏＯ）＝３：１となるようにすることが好ましい。また、ＭｎＯとＣｏＯの配合比を適宜調整することによりＬｉ６ＭｎｘＣｏ１－ｘＯ４における値ｘを制御することができる。
　あるいは、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物は、共沈法により製造してもよい。
　次に、上述した構成を有するセパレータ１２０を準備する。セパレータ１２０は従来公知の方法で製造してもよく、市販のものを用いてもよい。
　次に、上述した負極材料、例えば１μｍ以上１ｍｍ以下の金属箔（例えば、電解Ｃｕ箔）を、スルファミン酸を含む溶剤で洗浄した後に所定の大きさに打ち抜き、更に、エタノールで超音波洗浄した後、乾燥させることにより負極１３０を得る。
　以上のようにして得られる、正極集電体１４０を片面に備える正極１１０、セパレータ１２０、及び負極１３０を、この順に積層することで積層体を得る。得られた積層体を、電解液と共に密閉容器に封入することでリチウム２次電池１００を得ることができる。密閉容器としては、特に限定されないが、例えば、ラミネートフィルムが挙げられる。
　上記のようにして得られたリチウム２次電池１００は、その後初期充電された後に使用される。初期充電は電池が使用者に提供される前に実施されてもよく、電池が使用者に提供された後に使用者が実施してもよい。本実施形態のリチウム２次電池の効果を有効かつ確実に奏する観点からは、初期充電は電池が使用者に提供される前に実施されることが好ましく、すなわち、本実施形態のリチウム２次電池は、製造工程の一工程として電池を初期充電させる工程を含んでいることが好ましい。
　したがって、リチウム２次電池１００の製造方法は、上記のようにして得られた電池を初期充電する工程を含むことが好ましい。
　初期充電はＣＣ充電（定電流充電）又はＣＶ充電（低電圧充電）であってもよく、ＣＣ－ＣＶ充電、ＣＶ－ＣＣ充電、又はＣＣ－ＣＶ－ＣＣ充電であってもよい。また、初期充電はカットオフ電圧が４．３Ｖ以上５．０Ｖ以下である充電条件により実施されることが好ましい。
　上記の初期充電において、カットオフ電圧は、好ましくは４．３Ｖ超であり、より好ましくは４．４Ｖ以上であり、４．５Ｖ以上、４．６Ｖ以上、又は４．７Ｖ以上としてもよい。また、当該カットオフ電圧は、好ましくは５．０Ｖ未満であり、より好ましくは４．９Ｖ以下であり、更に好ましくは４．８Ｖ以下であり、更により好ましくは４．７Ｖ以下である。
　上記初期充電におけるカットオフ電圧は、上記の上限値及び下限値を任意に組み合わせて得られる範囲内としてもよく、例えば４．３Ｖ超５．０Ｖ未満、４．４Ｖ以上４．９Ｖ以下、又は４．４Ｖ以上４．７Ｖ以下であってよい。充放電サイクルを実施する前の初期充電におけるカットオフ電圧を上記の範囲内とすることにより、製造されるリチウム２次電池のサイクル特性を一層高めることができる傾向にある。
［第２の本実施形態］
（リチウム２次電池）
　図３は第２の本実施形態のリチウム２次電池（以下、「第２実施形態」という。）に係るリチウム２次電池の概略断面図である。第２実施形態のリチウム２次電池３００は、第１実施形態のリチウム２次電池１００と同様、正極１１０と、負極活物質を有しない負極１３０とを備える。正極１１０は、正極活物質と、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物とを含むものである。また、リチウム２次電池１００は、正極１１０と負極１３０との間にセパレータ１２０を備え、正極１１０は、セパレータ１２０に対向する面とは反対側の面に正極集電体１４０を有する。
　第２実施形態のリチウム２次電池３００は、セパレータ１２０の負極１３０に対向する表面に形成されているファイバ状又は多孔質状のイオン伝導性及び電気伝導性を有する緩衝機能層３１０を備える点でリチウム２次電池１００と異なるものである。
　リチウム２次電池３００において、正極集電体、正極、セパレータ、及び負極の構成及びその好ましい態様は、第１実施形態のリチウム２次電池１００と同様であり、これらの構成について、第２実施形態のリチウム２次電池は、第１実施形態のリチウム２次電池と同様の効果を奏する。また、第２実施形態のリチウム２次電池は、リチウム２次電池１００と同様に、上述したような電解液を含んでいてもよい。
（緩衝機能層）
　図３に示すように、緩衝機能層３１０は、セパレータ１２０の負極１３０に対向する表面に形成されている。緩衝機能層は、ファイバ状又は多孔質状のイオン伝導性及び電気伝導性を有するものである。ここで、緩衝機能層３１０は、ファイバ状又は多孔質状であるため、イオン伝導性及び電気伝導性を有する固体部分と、該固体部分の隙間により構成される空孔部分（「間隙部分」と同意。以下、本明細書中において同じである。）を有する。なお、本明細書において、緩衝機能層における「固体部分」とは、ゲル状の部分を含むものとする。
　緩衝機能層３１０は上述のように構成されているため、リチウム２次電池を充電すると、固体部分に負極からの電子とセパレータ及び／又は電解液からのリチウムイオンとが供給される。その結果、上記固体部分の表面では、上述のようにして供給される電子及びリチウムイオンが反応し、空孔部分（固体部分の表面）にリチウム金属が析出する。したがって、緩衝機能層３１０は電池を充電した際のリチウム金属析出に起因する電池の体積膨張を抑制する効果を奏する。すなわち、リチウム２次電池３００は、リチウム２次電池１００に比べて充放電に起因する体積膨張あるいは体積変化を一層抑制できるものである。
　本発明者らは、本実施形態のリチウム２次電池では、第２実施形態のリチウム２次電池のように緩衝機能層を導入したとしても、電池のサイクル特性が低下しないか、むしろ向上し得ることを見出した。その要因として、本発明者らは、緩衝機能層の導入によりリチウム金属が析出し得る場の表面積が増加するために、リチウム金属析出反応の反応速度が緩やかに制御され、デンドライト状に成長したリチウム金属の形成が一層確実に抑制されるからであると推察している。
　なお、第２実施形態において、「リチウム金属が負極上に析出する」とは、特に断りがない限りにおいて、負極の表面、及び緩衝機能層の固体部分の表面の少なくとも１箇所に、リチウム金属が析出することを意味する。したがって、第２実施形態のリチウム２次電池において、リチウム金属は、例えば、負極の表面（負極と緩衝機能層との界面）に析出してもよく、緩衝機能層の内部（緩衝機能層の固体部分の表面）に析出してもよい。
　緩衝機能層３１０としては、ファイバ状又は多孔質状であり、イオン伝導性及び電気伝導性を有するものであれば特に限定されない。緩衝機能層３１０の非限定的な例示としては、例えば、ファイバ状又は多孔質状のイオン伝導層の表面の全部又は一部に、電気伝導層を被覆したもの；ファイバ状又は多孔質状の電気伝導層の表面の全部又は一部に、イオン伝導層を被覆したもの；並びに、ファイバ状のイオン伝導層と、ファイバ状の電気伝導層とを交絡させたもの等が挙げられる。
　イオン伝導層としては、イオンを伝導することができるものである限り限定されないが、例えば第１実施形態のリチウム２次電池のセパレータにおける電解質として例示したポリマー電解質及びゲル電解質が挙げられる。
　電気伝導層としては、電子を伝導することができるものであればよく、例えば、金属膜が挙げられる。電気伝導層に含まれ得る金属の非限定的な例示としては、例えば、ＳＵＳ、Ｓｉ、Ｓｎ、Ｓｂ、Ａｌ、Ｎｉ、Ｃｕ、Ｓｎ、Ｂｉ、Ａｇ、Ａｕ、Ｐｔ、Ｐｂ、Ｚｎ、Ｉｎ、Ｂｉ－Ｓｎ、及びＩｎ－Ｓｎ等が挙げられる。電気伝導層に含まれる金属としては、リチウム金属との親和性を高める観点から、Ｓｉ、Ｓｎ、Ｚｎ、Ｂｉ、Ａｇ、Ｉｎ、Ｐｂ、Ｓｂ、及びＡｌが好ましい。上記のような金属は、１種を単独で又は２種以上を併用して用いてもよい。
　緩衝機能層３１０の一実施形態として、ファイバ状の緩衝機能層が挙げられる。図４（Ａ）にファイバ状の緩衝機能層の概略断面図を示す。図４（Ａ）に示す緩衝機能層３１０は、イオン伝導性及び電気伝導性を有するファイバであるイオン電気伝導ファイバ４１０からなる。すなわち、本実施形態において、「緩衝機能層がファイバ状である」とは、緩衝機能層がファイバを含むか、あるいは、ファイバにより構成されていることで、固体部分と、該固体部分の隙間により構成される空孔部分を有することを意味する。
　図４（Ａ）に示す緩衝機能層３１０を有するリチウム２次電池を充電すると、緩衝機能層の固体部分の表面、すなわち、イオン電気伝導ファイバ４１０の表面に、リチウム金属が析出する。したがって、そのような態様によれば、図４（Ｂ）にその概略断面図を示すように、緩衝機能層の固体部分であるイオン電気伝導ファイバ４１０の表面に、緩衝機能層の空孔部分を埋めるようにしてリチウム金属４２０が析出する。
　イオン電気伝導ファイバ４１０の一実施形態を、図４（Ｃ）に概略断面図として示す。図４（Ｃ）に示すように、一実施形態において、イオン電気伝導ファイバ４１０は、ファイバ状のイオン伝導層４３０と、イオン伝導層４３０の表面を被覆する電気伝導層４４０とを備える。イオン伝導層４３０は、例えばイオン伝導層として上述したような構成を備えていてもよく、電気伝導層４４０は、例えば電気伝導層として上述したような構成を備えていてもよい。
　ファイバ状のイオン伝導層４３０のファイバ平均直径は、好ましくは３０ｎｍ以上５０００ｎｍ以下であり、より好ましくは５０ｎｍ以上２０００ｎｍ以下であり、更に好ましくは７０ｎｍ以上１０００ｎｍ以下であり、更により好ましくは８０ｎｍ以上５００ｎｍ以下である。イオン伝導層のファイバ平均直径が上記の範囲内にあることにより、リチウム金属が析出できる反応場の表面積が一層適切な範囲となるため、サイクル特性が一層向上する傾向にある。
　電気伝導層４４０の平均厚さは、好ましくは１ｎｍ以上３００ｎｍ以下であり、より好ましくは５ｎｍ以上２００ｎｍ以下であり、更に好ましくは１０ｎｍ以上１５０ｎｍ以下である。電気伝導層の平均厚さが上記の範囲内にあることにより、イオン電気伝導ファイバ４１０の電気伝導性を一層適切に保つことができるため、サイクル特性が一層向上する傾向にある。
　別の実施形態において、緩衝機能層３１０は、多孔質状であってもよい。多孔質状の緩衝機能層は、例えば、多孔質状、特に連通孔を有するイオン伝導層と、イオン伝導層の表面を被覆する電気伝導層とを備えるものであってもよい。
　緩衝機能層３１０は、ファイバ状又は多孔質状であるため、空孔を有する。緩衝機能層の空孔率は、特に限定されないが、体積％で、好ましくは５０％以上、より好ましくは６０％以上、更に好ましくは７０％以上である。緩衝機能層の空孔率が上記の範囲内にあることにより、リチウム金属が析出できる反応場の表面積が一層上昇するため、サイクル特性が一層向上する傾向にある。また、そのような態様によれば、セル体積膨張を抑制する効果が一層有効かつ確実に奏される傾向にある。緩衝機能層の空孔率は、特に限定されないが、体積％で、９９％以下であってもよく、９５％以下であってもよく、９０％以下であってもよい。
　緩衝機能層３１０の平均厚さは、好ましくは１００μｍ以下であり、より好ましくは５０μｍ以下であり、更に好ましくは３０μｍ以下である。緩衝機能層の平均厚さが上記の範囲内にあることにより、リチウム２次電池３００における緩衝機能層３１０の占める体積が減少するため、電池のエネルギー密度が一層向上する。また、緩衝機能層の平均厚さは、好ましくは１μｍ以上であり、より好ましくは４μｍ以上であり、更に好ましくは７μｍ以上である。緩衝機能層の平均厚さが上記の範囲内にあることにより、リチウム金属が析出できる反応場の表面積が一層上昇するため、サイクル特性が一層向上する傾向にある。また、そのような態様によれば、セル体積膨張を抑制する効果が一層有効かつ確実に奏される傾向にある。
　ファイバ状のイオン伝導層のファイバ直径、電気伝導層の厚さ、緩衝機能層の空孔率、及び緩衝機能層の厚さは、公知の測定方法により測定することができる。例えば、緩衝機能層の厚さは、緩衝機能層の表面を集束イオンビーム（ＦＩＢ）でエッチングして、その断面を露出させ、露出した切断面における緩衝機能層の厚さを電子顕微鏡により観察することにより測定することができる。
　ファイバ状のイオン伝導層のファイバ直径、電気伝導層の厚さ、及び緩衝機能層の空孔率は、電子顕微鏡で緩衝機能層の表面を観察することにより測定することができる。なお、緩衝機能層の空孔率は、画像解析ソフトを用いて、緩衝機能層の表面の観察画像を２値解析し、画像の総面積に対して緩衝機能層が占める割合を求めることで算出すればよい。
　上記の各測定値は３回以上、好ましくは１０回以上測定した測定値の平均を求めることにより算出される。
　なお、緩衝機能層３１０がリチウムと反応し得る金属を含む場合、負極１３０及び緩衝機能層３１０の容量の合計は、正極１１０の容量に対して十分小さく、例えば、２０％以下、１５％以下、１０％以下、又は５％以下である。なお、正極１１０、負極１３０、及び緩衝機能層３１０の各容量は、従来公知の方法により測定することができる。
（リチウム２次電池の製造方法）
　第２実施形態のリチウム２次電池の製造方法において、緩衝機能層以外の構成の製造及び各構成の組み立て、並びにそれに続く初期充電は、第１実施形態のリチウム２次電池の製造方法と同様に実施することができる。
　緩衝機能層３１０の製造方法は、ファイバ状又は多孔質状のイオン伝導性及び電気伝導性を有する層を得られる限り特に限定されないが、例えば以下のようにすればよい。
　図４（Ｃ）に示すような、ファイバ状のイオン伝導層４３０と、イオン伝導層４３０の表面を被覆する電気伝導層４４０とを備えるイオン電気伝導ファイバ４１０を有するファイバ状の緩衝機能層は以下のように製造することができる。
　まず、上述した樹脂（例えば、ＰＶＤＦ）を適当な有機溶媒（例えば、Ｎ－メチルピロリドン）に溶解させた溶液を、事前に準備したセパレータ１２０の表面にドクターブレードを用いて塗布する。次いで、樹脂溶液を塗付したセパレータ１２０を、水浴に浸漬した後、室温で十分乾燥させることで、セパレータ１２０上にファイバ状のイオン伝導層を形成する（なお、イオン伝導層は例えば電池の組立時に電解液が注液されることでイオン伝導機能を発揮するようにしてもよい）。続いて、ファイバ状のイオン伝導層が形成されたセパレータに対して、真空条件下で適当な金属（例えば、Ｎｉ）を蒸着させることにより、ファイバ状の緩衝機能層を得ることができる。
　また、多孔質状のイオン伝導層と、イオン伝導層の表面を被覆する電気伝導層とを備える多孔質状の緩衝機能層は以下のように製造することができる。
　まず、上述した樹脂（例えば、ＰＶＤＦ）を適当な溶媒（例えば、Ｎ－メチルピロリドン）に溶解させた溶液を用いて、従来公知の方法により（例えば、溶媒との相分離を用いる方法、及び発泡剤を用いる方法等。）、連通孔を有する多孔質状のイオン伝導層をセパレータ１２０の表面に形成する（なお、イオン伝導層は例えば電池の組立時に電解液が注液されることでイオン伝導機能を発揮するようにしてもよい）。続いて、多孔質状のイオン伝導層が形成されたセパレータに対して、真空条件下で適当な金属（例えば、Ｎｉ）を蒸着させることにより、多孔質状の緩衝機能層を得ることができる。
［リチウム２次電池の製造方法］
　本発明は、リチウム２次電池の製造方法も提供する。以下、本実施形態のリチウム２次電池の製造方法（以下、「本実施形態の製造方法」という。）について詳述する。
　本実施形態の製造方法は、正極活物質と、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物とを含む正極、及び負極活物質を有しない負極を準備する工程と、上記正極と上記負極とを両者が対向するように配置する工程と、上記正極と上記負極との間に電圧を印加して、カットオフ電圧が４．３Ｖ以上５．０Ｖ以下である充電条件により初期充電する工程とを含む。
　上述のとおり、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物は、初期充電において電池の電圧が４．３Ｖ程度となる条件でリチウムイオンを放出し始め、犠牲正極剤として作用する傾向にある。したがって、カットオフ電圧が４．３Ｖ以上５．０Ｖ以下である充電条件により初期充電する工程を含む本実施形態の製造方法によれば、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物の犠牲正極剤としての機能を有効かつ確実に発揮させることができ、サイクル特性に優れるリチウム２次電池を製造することができる。さらに、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物は大気中における安定性に優れ、厳密に湿度等の制御をすることなしに取り扱うことができるため、上記の製造方法は生産性が高い。
　以下、各工程について説明する。なお、本実施形態の製造方法、特に正極準備工程は、一定程度湿度が排除された環境、例えば露点－５０～－１０℃のドライルーム等において実施されることが好ましい。
（正極及び負極準備工程）
　本実施形態の製造方法では、まず正極活物質と、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物とを含む正極、及び負極活物質を有しない負極を準備する工程が実施される。
　正極及び負極の構成及び好ましい態様は、上記本実施形態のリチウム２次電池におけるものと同様である。また、正極に含まれる正極活物質及びＬｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物の構成及び好ましい態様も、上記本実施形態のリチウム２次電池におけるものと同様である。
　本工程では、そのような構成を有する正極及び負極を準備するが、当該正極及び負極は市販のものを購入することにより得てもよいし、本実施形態のリチウム２次電池の説明において記載した方法により製造してもよい。また、正極及び負極の準備は同時に行ってもよく、別々に行ってもよい。正極及び負極の準備を別々に実施する場合、その順番は特に限定されない。
（正極及び負極配置工程）
　本実施形態の製造方法では、正極及び負極準備工程の後、正極と負極とを両者が対向するように配置する工程が実施される。
　本工程では、正極と負極とを両者が対向するように配置される限り特に限定されず、正極及び負極のみを配置してもよいし、上記リチウム２次電池１００及び３００のように、セパレータ及び／又は緩衝機能層を介して正極及び負極を対向させてもよい。ただし、正極及び負極は物理的又は電気的に接触させないものとする。
　正極及び負極配置工程では、正極及び負極の組み合わせを複数セット配置してもよい。その場合、正極及び負極が交互に積層されるように配置することが好ましい。
　セパレータ及び／又は緩衝機能層を配置する場合、セパレータ及び緩衝機能層の構成及び好ましい態様は、上記本実施形態のリチウム２次電池におけるものと同様であり、本実施形態のリチウム２次電池の説明において記載した方法により入手又は製造することができる。
（初期充電工程）
　本実施形態の製造方法では、正極及び負極配置工程の後、正極と負極との間に電圧を印加して、カットオフ電圧が４．３Ｖ以上５．０Ｖ以下である充電条件により初期充電する工程を実施する。
　初期充電はＣＣ充電（定電流充電）又はＣＶ充電（低電圧充電）であってもよく、ＣＣ－ＣＶ充電、ＣＶ－ＣＣ充電、又はＣＣ－ＣＶ－ＣＣ充電であってもよい。
　初期充電工程において、カットオフ電圧は、好ましくは４．３Ｖ超であり、より好ましくは４．４Ｖ以上であり、４．５Ｖ以上、４．６Ｖ以上、又は４．７Ｖ以上としてもよい。また、当該カットオフ電圧は、好ましくは５．０Ｖ未満であり、より好ましくは４．９Ｖ以下であり、更に好ましくは４．８Ｖ以下であり、更により好ましくは４．７Ｖ以下である。
　上記初期充電におけるカットオフ電圧は、上記の上限値及び下限値を任意に組み合わせて得られる範囲内としてもよく、例えば４．３Ｖ超５．０Ｖ未満、４．４Ｖ以上４．９Ｖ以下、又は４．４Ｖ以上４．７Ｖ以下であってよい。カットオフ電圧を上記の範囲内とすることにより、一層サイクルに優れるリチウム２次電池を製造できる傾向にある。
（その他工程）
　本実施形態の製造方法は、正極及び負極準備工程、正極及び負極配置工程、並びに初期充電工程以外の工程を含んでいてもよい。そのような工程としては、例えば、正極及び負極配置工程の前に必要に応じて実施されるセパレータ準備工程、及び緩衝機能層準備工程、並びに正極及び負極配置工程と初期充電工程との間に必要に応じて実施される電解液注入工程、及びそれに続く封止工程が挙げられる。これらの工程は、第１実施形態又は第２実施形態のリチウム２次電池の説明に記載した事項に基づいて実施することができる。
　具体的には、電解液注入工程、及びそれに続く封止工程は以下のように実施すればよい。まず、正極及び負極配置工程により得られた正極及び負極を含む積層体を、少なくとも一端が開口された密閉容器に保持する。その後密閉容器に、本実施形態のリチウム２次電池が含み得る電解液を注入することにより、電解液注入工程を実施する。次いで、当該密閉容器の開口部分を封止することにより製品としての電池を得る封止工程を実施する。
［変形例］
　上記本実施形態は、本発明を説明するための例示であり、本発明をその本実施形態のみに限定する趣旨ではなく、本発明は、その要旨を逸脱しない限り、様々な変形が可能である。
　本実施形態のリチウム２次電池は、負極表面において、当該負極に接触するように配置される集電体を有していてもよく、有していなくてもよい。そのような集電体としては、特に限定されないが、例えば、負極材料に用いることのできるものが挙げられる。また、本実施形態のリチウム２次電池は、正極集電体を有していなくてもよい。なお、リチウム２次電池が正極集電体、及び負極集電体を有しない場合、それぞれ、正極、及び負極自身が集電体として働く。
　本実施形態のリチウム２次電池は、正極集電体及び／又は負極に、外部回路へと接続するための端子を取り付けてもよい。例えば１０μｍ以上１ｍｍ以下の金属端子（例えば、Ａｌ、Ｎｉ等）を、正極集電体及び負極の片方又は両方にそれぞれ接合してもよい。接合方法としては、従来公知の方法を用いればよく、例えば超音波溶接を用いてもよい。
　リチウム２次電池１００において、セパレータ１２０を省略してもよい。その場合、正極１１０及び負極１３０が物理的又は電気的に接触しないように、両者を十分離した状態で固定することが好ましい。
　リチウム２次電池３００備える緩衝機能層３１０において、イオン伝導層及び電気伝導層は、層状のものに限られず、ファイバ状、塊状、又は多孔質状であってもよい。したがって、本明細書中、イオン伝導層、電気伝導層との語は、それぞれイオン伝導相、電気伝導相と換言してもよい。
　なお、本明細書において、「エネルギー密度が高い」又は「高エネルギー密度である」とは、電池の総体積又は総質量当たりの容量が高いことを意味するが、好ましくは７００Ｗｈ／Ｌ以上又は３００Ｗｈ／ｋｇ以上であり、より好ましくは８００Ｗｈ／Ｌ以上又は３５０Ｗｈ／ｋｇ以上であり、更に好ましくは９００Ｗｈ／Ｌ以上又は４００Ｗｈ／ｋｇ以上である。
　また、本明細書において、「サイクル特性に優れる」とは、通常の使用において想定され得る回数の充放電サイクルの前後において、電池の容量の減少率が低いことを意味する。すなわち、初期充放電の後の１回目の放電容量と、通常の使用において想定され得る回数の充放電サイクル後の容量とを比較した際に、充放電サイクル後の容量が、初期充放電の後の１回目の放電容量に対してほとんど減少していないことを意味する。ここで、「通常の使用において想定され得る回数」とは、リチウム２次電池が用いられる用途にもよるが、例えば、３０回、５０回、７０回、１００回、３００回、又は５００回である。また、「充放電サイクル後の容量が、初期充放電の後の１回目の放電容量に対してほとんど減少していない」とは、リチウム２次電池が用いられる用途にもよるが、例えば、充放電サイクル後の容量が、初期充放電の後の１回目の放電容量に対して、６０％以上、６５％以上、７０％以上、７５％以上、８０％以上、又は８５％以上であることを意味する。
　本明細書において、好ましい範囲等として記載した数値範囲は、記載した上限値及び下限値を任意に組み合わせて得られる数値範囲に置き換えてもよい。例えば、あるパラメータが、好ましくは５０以上、より好ましくは６０以上であり、好ましくは１００以下、より好ましくは９０以下である場合、当該パラメータは、５０以上１００以下、５０以上９０以下、６０以上１００以下、又は６０以上９０以下のいずれであってもよい。
　以下、本発明を実施例及び比較例を用いてより具体的に説明する。本発明は、以下の実施例によって何ら限定されるものではない。
［リチウム含有化合物の不可逆容量密度の測定方法］
　各例で用いた犠牲正極剤としてのリチウム含有化合物の不可逆容量密度、すなわち、充電容量密度と放電容量密度との差は、以下のようにして測定した。まず、各リチウム含有化合物と、ポリビニリデンフロライドと、カーボンブラックと、Ｎ－メチルピロリドン（ＮＭＰ）とを混合することでスラリーを作製し、その後アルミ箔上に塗布、乾燥、プレスした。この電極を作用極とし、対極をリチウム金属とするテストセルを作製し、０．２ｍＡｈ／ｃｍ２の電流で、カットオフ電圧を所定の値としてＣＣ充電した後、電圧が３．０ＶになるまでＣＣ放電した。測定された充電容量密度及び放電容量密度の差を計算することにより不可逆容量密度（ｍＡｈ／ｇ）を求めた。
［リチウム２次電池の作製及び性能評価］
［実施例１］
　以下のようにして、実施例１のリチウム２次電池を作製した。
（負極の準備）
　１０μｍの電解Ｃｕ箔を、スルファミン酸を含む溶剤で洗浄した後に所定の大きさ（４５ｍｍ×４５ｍｍ）に打ち抜き、更にエタノールで超音波洗浄した後、乾燥させることにより負極を準備した。
（正極の作製）
　露点－３０℃のドライルーム内で、正極活物質として９２．７質量部のＬｉＮｉ０．８５Ｃｏ０．１２Ａｌ０．０３Ｏ２を、リチウム含有化合物として３．３質量部のＬｉ６Ｍｎ０．５Ｃｏ０．５Ｏ４を、導電助剤として２．０質量部のカーボンブラックを、及びバインダーとして２．０質量部のポリビニリデンフロライド（ＰＶＤＦ）を、溶媒としてのＮ－メチルピロリドン（ＮＭＰ）に混合することにより正極混合物を得た。得られた正極混合物を正極集電体としての１２μｍのＡｌ箔の片面に塗布しプレス成型した後、打ち抜き加工により、所定の大きさ（４０ｍｍ×４０ｍｍ）に打ち抜き、正極を得た。
　Ｌｉ６Ｍｎ０．５Ｃｏ０．５Ｏ４は以下のようにして製造した。まず、市販のＬｉ２Ｏ、ＭｎＯ、及びＣｏＯ粉末をモル比６：１：１にて容器に添加し、粉砕、混合した。アルゴンガス９９体積％及び水素ガス１体積％からなるガス気流下、得られた混合物を８００℃の条件にて１２時間焼成することで、Ｌｉ６Ｍｎ０．５Ｃｏ０．５Ｏ４を得た。
（セパレータの準備）
　セパレータとして、１２μｍのポリエチレン微多孔膜の両面に２μｍのポリビニリデンフロライド（ＰＶＤＦ）がコーティングされた所定の大きさ（５０ｍｍ×５０ｍｍ）のセパレータを準備した。
（電池の組み立て）
　電解液として、４．０Ｍ　ＬｉＮ（ＳＯ２Ｆ）２（ＬＦＳＩ）のジメトキシエタン（ＤＭＥ）溶液を準備した。
　次いで、正極集電体、正極、セパレータ、及び負極がこの順になるように各構成を積層することで積層体を得た。さらに正極集電体及び負極に、それぞれ１００μｍのＡｌ端子及び１００μｍのＮｉ端子を超音波溶接で接合した後、ラミネートの外装体に挿入した。次いで、上記の電解液を上記の外装体に注入した。外装体を封止することにより、リチウム２次電池を得た。
（初期充電）
　その後、リチウム２次電池を２．０ｍＡ（０．０５Ｃ；０．１２５ｍＡ／ｃｍ２）で、カットオフ電圧を４．７ＶとしてＣＣ充電することにより初期充電した。
［実施例２～３］
　リチウム含有化合物の組成を表１に記載のものとしたこと以外は実施例１と同様にしてリチウム２次電池を作製し、その後初期充電を行った。なお、Ｌｉ６Ｍｎ０．７Ｃｏ０．３Ｏ４はＬｉ２Ｏ、ＭｎＯ、及びＣｏＯ粉末の添加比率をモル比で３０：７：３として、Ｌｉ６Ｍｎ０．３Ｃｏ０．７Ｏ４はＬｉ２Ｏ、ＭｎＯ、及びＣｏＯ粉末の添加比率をモル比で３０：３：７とすることにより製造した。
［比較例１］
　リチウム含有化合物としてＬｉ６ＭｎＯ４を用いたこと以外は実施例１と同様にしてリチウム２次電池を作製し、その後初期充電を行った。なお、Ｌｉ６ＭｎＯ４はＬｉ２Ｏ、及びＭｎＯ粉末の添加比率をモル比で３：１とすることにより製造した。
［比較例２］
　リチウム含有化合物としてＬｉ６ＣｏＯ４を用いたこと以外は実施例１と同様にしてリチウム２次電池の作製を試みた。しかしながら、Ｌｉ６ＣｏＯ４を用いた場合、正極混合物がゲル化してしまい、同条件ではリチウム２次電池を作製することができなかった。
　なお、Ｌｉ６ＭｎＯ４はＬｉ２Ｏ、及びＣｏＯ粉末の添加比率をモル比で３：１とすることにより製造した。
［サイクル特性の評価］
　以下のようにして、各実施例及び比較例で作製したリチウム２次電池のエネルギー密度及びサイクル特性を評価した。
　上記のとおり初期充電した各例のリチウム２次電池を２．０ｍＡ（０．０５Ｃ；０．１２５ｍＡ／ｃｍ２）で、電圧が３．０ＶになるまでＣＣ放電した（初期放電）。次いで、２０ｍＡ（０．５Ｃ；１．２５ｍＡ／ｃｍ２）で、電圧が４．２Ｖになるまで充電した後、２０ｍＡ（０．５Ｃ；１．２５ｍＡ／ｃｍ２）で、電圧が３．０Ｖになるまで放電する充放電サイクルを、温度２５℃の環境で更に９９サイクル繰り返した。初期充放電サイクルを１サイクル目と数えたときの２サイクル目における放電から求められる放電容量に対する、１００サイクル目における放電から求められる放電容量の比を、容量維持率（％）として計算し、サイクル特性の指標として用いた。容量維持率が高いほど、サイクル特性に優れることを意味する。各例における容量維持率を表１に示す。
Figure JPOXMLDOC01-appb-T000001
　表１中、不可逆容量密度は、充電のカットオフ電圧を４．７Ｖとして上記の方法で測定したときの値である。また、添加率は電池の初期放電から求められるセル容量に対するリチウム含有化合物の不可逆容量の割合を意味する。なお、比較例２においては上述のとおりリチウム２次電池を安定的に作製できなかったため電池の性能評価は行わなかった。
　表１から、犠牲正極剤であるリチウム含有化合物としてＬｉ６ＭｎＯ４又はＬｉ６ＣｏＯ４を用いた比較例に比べて、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）を用いた実施例はサイクル特性及び生産性に優れることがわかった。
［初期充電時のカットオフ電圧がサイクル特性に与える影響の評価］
　次に、実施例１～３で作製したリチウム２次電池において、初期充電のカットオフ電圧を変化させたときに容量維持率がどのように変化するかを調べた。
［試験例１～５］
　まず、組成がＬｉ６Ｍｎ０．５Ｃｏ０．５Ｏ４であるリチウム含有化合物を含む実施例１のリチウム２次電池について、カットオフ電圧を４．２Ｖ、４．３Ｖ、４．４Ｖ、４．７Ｖ、又は５．０Ｖとした以外は実施例１と同様に初期充電した。その後上記と同様の方法により容量維持率を測定した。各例における容量維持率を表２に示す。
［試験例６～７］
　組成がＬｉ６Ｍｎ０．７Ｃｏ０．３Ｏ４であるリチウム含有化合物を含む実施例２のリチウム２次電池について、カットオフ電圧を４．４Ｖ、又は４．７Ｖとした以外は実施例１と同様に初期充電した。その後上記と同様の方法により容量維持率を測定した。各例における容量維持率を表２に示す。
［試験例８～９］
　組成がＬｉ６Ｍｎ０．３Ｃｏ０．７Ｏ４であるリチウム含有化合物を含む実施例３のリチウム２次電池について、カットオフ電圧を４．４Ｖ、又は４．７Ｖとした以外は実施例１と同様に初期充電した。その後上記と同様の方法により容量維持率を測定した。各例における容量維持率を表２に示す。
Figure JPOXMLDOC01-appb-T000002
　試験例１～５の結果から、本実施形態のリチウム２次電池は、カットオフ電圧を所定の範囲とする初期充電をした場合にサイクル特性が一層高くなることがわかった。また、試験例６～９の結果から、犠牲正極剤としてのリチウム含有化合物の組成によらず、カットオフ電圧を所定の範囲とする初期充電をした場合にサイクル特性が一層高くなることがわかった。
［緩衝機能層の導入］
　次に、本実施形態のリチウム２次電池において、緩衝機能層を導入したときにサイクル特性がどのように変化するかを調べた。
［実施例４］
　以下のようにして、実施例４のリチウム２次電池を作製した。まず、実施例３と同様の方法で正極集電体を有する正極、負極、セパレータ、及び電解質を準備した。次いで以下のようにして緩衝機能層をセパレータの片面に形成した。
　ＰＶＤＦ樹脂をＮ－メチルピロリドン（ＮＭＰ）に溶解させた樹脂溶液をセパレータ上にバーコーターを用いて塗布した。次いで、樹脂溶液を塗付したセパレータを、水浴に浸漬した後、室温で十分乾燥させることで、セパレータ上にファイバ状のイオン伝導層を形成した（なお、イオン伝導層は、電池の組立時に後述する電解液（４Ｍ　ＬｉＮ（ＳＯ２Ｆ）２（ＬＦＳＩ）のジメトキシエタン（ＤＭＥ）溶液）が注液されることでイオン伝導機能を発揮する。）。
　セパレータ上に形成されたファイバ状のイオン伝導層のファイバ平均直径を走査型電子顕微鏡（ＳＥＭ）で観察して測定したところ、１００ｎｍであった。
　続いて、ファイバ状のイオン伝導層が形成されたセパレータに対して、真空条件下でＮｉを蒸着させた。エネルギー分散型Ｘ線分析装置（ＥＤＸ）付ＳＥＭを用いて、Ｎｉ蒸着後のイオン伝導層を観察したところ、Ｎｉはファイバ状のイオン伝導層を覆うように分布していることが確認され、ファイバ状のイオン伝導層の表面が電気伝導層に覆われているファイバ状の緩衝機能層が得られたことが確認された。
　また、緩衝機能層の断面をＦＩＢで作製してＳＥＭで観察したところ、緩衝機能層の平均厚さは１０μｍであった。透過型電子顕微鏡で緩衝機能層を観察したところ、電気伝導層であるＮｉ薄膜の平均厚さ、及び緩衝機能層の空孔率は、それぞれ、２０ｎｍ、及び９０％であった。
　次いで、正極集電体、正極、緩衝機能層が形成されたセパレータ、及び負極を、この順に積層することで積層体を得た。なお、緩衝機能層が負極と対向するようにして積層を実施した。さらに正極集電体及び負極に、それぞれ１００μｍのＡｌ端子及び１００μｍのＮｉ端子を超音波溶接で接合した後、ラミネートの外装体に挿入した。次いで、電解液を上記の外装体に注入した。外装体を封止することにより、リチウム２次電池を得た。
　その後、リチウム２次電池を２．０ｍＡ（０．０５Ｃ；０．１２５ｍＡ／ｃｍ２）で、カットオフ電圧を４．４ＶとしてＣＣ充電することにより初期充電した。作製した実施例４のリチウム２次電池について、上記と同様の方法により容量維持率を測定した。測定した容量維持率を、試験例８の結果と併せて表３に示す。
Figure JPOXMLDOC01-appb-T000003
　表３から、本実施形態のリチウム２次電池において緩衝機能層を導入した場合でも容量維持率が維持されることがわかった。すなわち、実施例４のリチウム２次電池は、エネルギー密度が高く、サイクル特性及び生産性に優れ、さらに電池の充放電による体積膨張率が低いことがわかった。
　本発明のリチウム２次電池は、エネルギー密度が高く、サイクル特性及び生産性に優れるため、様々な用途に用いられる蓄電デバイスとして、産業上の利用可能性を有する。
　１００，３００…リチウム２次電池、１１０…正極、１２０…セパレータ、１３０…負極、１４０…正極集電体、２１０…負極端子、２２０…正極端子、３１０…緩衝機能層、４１０…イオン電気伝導ファイバ、４２０…リチウム金属、４３０…イオン伝導層、４４０…電気伝導層。

Claims (11)

  1. 　正極と、負極活物質を有しない負極とを備え、
    　前記正極が、正極活物質と、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物とを含む、
    　リチウム２次電池。
  2. 　カットオフ電圧が４．３Ｖ以上５．０Ｖ以下である充電条件により初期充電された、請求項１に記載のリチウム２次電池。
  3. 　前記リチウム含有化合物の含有量が、前記正極の総質量に対して１．０質量％以上１５．０質量％以下である、請求項１又は２に記載のリチウム２次電池。
  4. 　前記リチウム含有化合物が、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０．２≦ｘ≦０．８）で表される化合物である、請求項１～３のいずれか１項に記載のリチウム２次電池。
  5. 　前記負極は、Ｃｕ、Ｎｉ、Ｔｉ、Ｆｅ、その他Ｌｉと合金化しない金属、及びこれらの合金、並びに、ステンレス鋼（ＳＵＳ）からなる群より選択される少なくとも１種からなる電極である、請求項１～４のいずれか１項に記載のリチウム２次電池。
  6. 　エネルギー密度が３５０Ｗｈ／ｋｇ以上である、請求項１～５のいずれか１項に記載のリチウム２次電池。
  7. 　請求項１～６のいずれか１項に記載のリチウム２次電池の使用方法であって、
    　４．３Ｖ以上５．０Ｖ以下のカットオフ電圧で充電した後に、少なくとも１回の放電工程と少なくとも１回の充電工程とを含む充放電サイクルを実施することを含み、
    　前記充放電サイクルにおける充電工程のカットオフ電圧が、４．３Ｖ以上５．０Ｖ以下のカットオフ電圧で実施される第１回目の充電時のカットオフ電圧未満となるように実施される、使用方法。
  8. 　正極活物質と、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０＜ｘ＜１）で表されるリチウム含有化合物とを含む正極、及び負極活物質を有しない負極を準備する工程と、
    　前記正極と前記負極とを両者が対向するように配置する工程と、
    　前記正極と前記負極との間に電圧を印加して、カットオフ電圧が４．３Ｖ以上５．０Ｖ以下である充電条件により初期充電する工程と、
    を含む、リチウム２次電池の製造方法。
  9. 　前記リチウム含有化合物の含有量が、前記正極の総質量に対して１．０質量％以上１５．０質量％以下である、請求項８に記載のリチウム２次電池の製造方法。
  10. 　前記リチウム含有化合物が、Ｌｉ６ＭｎｘＣｏ１－ｘＯ４（０．２≦ｘ≦０．８）で表される化合物である、請求項８又は９に記載のリチウム２次電池の製造方法。
  11. 　前記負極は、Ｃｕ、Ｎｉ、Ｔｉ、Ｆｅ、その他Ｌｉと合金化しない金属、及びこれらの合金、並びに、ステンレス鋼（ＳＵＳ）からなる群より選択される少なくとも１種からなる電極である、請求項８～１０のいずれか１項に記載のリチウム２次電池の製造方法。
PCT/JP2021/018822 2021-05-18 2021-05-18 リチウム２次電池及びその使用方法、並びにリチウム２次電池の製造方法 WO2022244110A1 (ja)