WO2021150552A1 - Metals recovery from spent catalyst - Google Patents
Metals recovery from spent catalyst Download PDFInfo
- Publication number
- WO2021150552A1 WO2021150552A1 PCT/US2021/014098 US2021014098W WO2021150552A1 WO 2021150552 A1 WO2021150552 A1 WO 2021150552A1 US 2021014098 W US2021014098 W US 2021014098W WO 2021150552 A1 WO2021150552 A1 WO 2021150552A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- group
- metal
- metal compound
- group vib
- potassium carbonate
- Prior art date
Abstract
Description
Claims