WO2020160565A1 - Systems and methods for dewatering and drying nanocellulose - Google Patents
Systems and methods for dewatering and drying nanocellulose Download PDFInfo
- Publication number
- WO2020160565A1 WO2020160565A1 PCT/US2020/024093 US2020024093W WO2020160565A1 WO 2020160565 A1 WO2020160565 A1 WO 2020160565A1 US 2020024093 W US2020024093 W US 2020024093W WO 2020160565 A1 WO2020160565 A1 WO 2020160565A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- nanocellulose
- slurry
- dispersion
- twin
- drying agent
- Prior art date
Abstract
Description
Claims