WO2020102748A1 - Multifunctional paints and caulks with controllable electromagnetic properties - Google Patents
Multifunctional paints and caulks with controllable electromagnetic properties Download PDFInfo
- Publication number
- WO2020102748A1 WO2020102748A1 PCT/US2019/061845 US2019061845W WO2020102748A1 WO 2020102748 A1 WO2020102748 A1 WO 2020102748A1 US 2019061845 W US2019061845 W US 2019061845W WO 2020102748 A1 WO2020102748 A1 WO 2020102748A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- metal
- electrically conductive
- nickel
- conductive paint
- fiber
- Prior art date
Abstract
Description
Claims