WO2020019026A1 - "caustic conversion process " - Google Patents
"caustic conversion process " Download PDFInfo
- Publication number
- WO2020019026A1 WO2020019026A1 PCT/AU2019/050773 AU2019050773W WO2020019026A1 WO 2020019026 A1 WO2020019026 A1 WO 2020019026A1 AU 2019050773 W AU2019050773 W AU 2019050773W WO 2020019026 A1 WO2020019026 A1 WO 2020019026A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- lithium
- rich
- process according
- pregnant liquor
- solution
- Prior art date
Abstract
Description
Claims