WO2019075469A1

WO2019075469A1 - Mining unexplored chemistries for phosphors for high-color-quality white-light-emitting diodes

Info

Publication number: WO2019075469A1
Application number: PCT/US2018/055897
Authority: WO
Inventors: Shyue Ping ONG; Jungmin Ha; Zhenbin WANG; Joanna MCKITTRICK; Won Bin IM; Yoon Hwa KIM
Original assignee: University of California Berkeley; University of California San Diego UCSD
Current assignee: University of California Berkeley; University of California San Diego UCSD
Priority date: 2017-10-13
Filing date: 2018-10-15
Publication date: 2019-04-18
Anticipated expiration: 2020-04-13
Also published as: US20210193880A1; US11532770B2

Abstract

Cette invention concerne un ensemble diode électroluminescente (DEL) comprenant une source de lumière à DEL ayant une première sortie de lumière ayant un spectre caractéristique et au moins une substance luminescente à travers laquelle passe la première sortie de lumière. La substance luminescente comprend le composé quaternaire M-Li-Al-O, où M est du Ba, du Sr ou du Ca, activé par Eu2+ ou Ce3+.A light emitting diode (LED) assembly includes an LED light source having a first light output having a characteristic spectrum and at least one luminescent substance through which the first light output passes. The phosphor comprises the quaternary compound M-Li-Al-O, where M is Ba, Sr or Ca, activated by Eu2 + or Ce3 +.

Description

Mining Unexplored Chemistries for Phosphors for High-Color-Quality White-Light- Emitting Diodes

Government Funding

[0001] This invention was made with Government support under 141 1 192 awarded by the National Science Foundation. The Government has certain rights in the invention.

Background

[0002] Phosphor-converted white-light-emitting diodes (pc-WLEDs) are among the most promising solid-state lighting (SSL) technologies due to their high-energy efficiency and superior durability and reliability. For general illumination, we need a warm white light with excellent quantum efficiency, resistance to thermal quenching, and color quality, i.e., a low color-correlated temperature (CCT) < 3000 K and a high color rendering index (CRI) > 85. Typical commercial WLEDs based on blue-emitting (-450 nm) LED chips combined with a yellow-emitting phosphor (Y₃Al₅0i₂:Ce³⁺) have poor CRI < 80 and high CCT > 5000 K. To improve the CRI and CCT, an alternative approach is to use near-ultraviolet (near-UV, 380-420 nm) or blue LED chips with a mixture of red, green and blue phosphors. Lu Al₅0i2:Ce ⁺ and (Ba,Sr)₂Si04:Eu²⁺ are two well-known green emitters with good photoluminescence (PL) properties used for these phosphor mixtures. Unfortunately, the former requires the rare-earth Lu in large quantities, while the latter suffers from severe thermal quenching. Meanwhile, most commercial red-emitters are Eu²⁺-activated nitrides, such as CaAlSiN :Eu²⁺ and Sr₂Si5N8:Eu²⁺, which are synthesized under harsh conditions (high temperature and high pressure). Yet another way to generate white light with high color quality is to leverage on a single-phase broad-band emitter that covers a wide range of the visible spectrum (400 ~ 700 nm). Bao.9₃Euo.o7Al₂04 is an example of a recently discovered broad-band phosphor with good CRI > 80 and CCT < 4000 K, but its synthesis requires a high temperature of 1450°C and a low pressure of 667 Pa.

[0003] There is therefore a need to discover new earth-abundant phosphors with reasonably facile synthesis for pc-WLED applications. Hitherto, the discovery of phosphor materials has largely taken place through painstaking experiments, such as using exploratory crystal growth, combinatorial chemistry screening and single particle-diagnosis, in an Edisonian fashion. In recent years, high-throughput density functional theory (DFT) calculations have emerged as a powerful complementary tool to experiments to accelerate materials discovery, with successes having been demonstrated in the many application areas. By enabling rapid evaluation across multiple application-specific properties, DFT calculations can be used to effectively screen thousands of materials to identify a small subset of candidates for subsequent synthesis and experimental evaluation. Nevertheless, there have been no successful demonstrations of in silico phosphor discovery to date, no doubt due in part to extensive experimental efforts in the field as well as the difficulty in predicting optical properties with DFT.

Summary

[0004] An earth-abundant phosphor host Sr₂LiA104 is presented, which is believed to be the first known Sr-Li-Al-0 quaternary compound. Sr₂LiA104 was identified via a carefully-targeted data- driven structure prediction and DFT screening effort guided by statistical analysis of known phosphors in the Inorganic Crystal Structure Database (ICSD). We demonstrate that Sr₂LiA104 is predicted by DFT calculations to be thermodynamically and dynamically stable and to have the necessary band gap, structural rigidity and near-UV excitation wavelength when activated with either Eu²⁺ or Ce ⁺. High purity Sr₂Li AIO4 was synthesized via industrially-scalable methods and characterized using X-ray diffraction and photoluminescence spectroscopy. The Eu²⁺- and Ce ⁺- activated Sr₂LiA104 phosphors exhibit broad emissions of Amax - 512 nm (green-yellow) and Amax ~ 434 nm (blue), respectively, with excellent thermal quenching resistance of > 88%

intensity at 150°C. A prototype pc-WLED utilizing Sr₂LiA10₄:Eu²⁺ yields an excellent CRI > 90.

Brief Description of the Drawings

[0005] FIG. 1 A shows the frequency at which each element appears in compounds having the word "phosphor" in the publication title in the 2017 version of ICSD; FIG. IB shows the calculated phase diagram, which indicates that Sr₂LiA104 is predicted to be a stable phase at OK; and FIG. 1C shows the crystal structure of Sr₂LiA104 (spacegroup: P2₁/m).

[0006] FIG. 2 shows the number of known materials in the Inorganic Crystal Structure Database in the ternary M-X-0 and quaternary M-L-X-0 (M = Ba/Sr/Ca; L = Li/Mg/Y; X=P/Si/Al/B) chemical spaces.

[0007] FIG. 3 is a computational high throughput screening workflow for identifying promising broad-band emitters. [0008] FIG. 4 shows a table (Table 1) of four known compounds in the Sr-Li-P-O, Ba/Sr-Y-P-0 and Ba-Y-Al-0 chemical spaces, their derivations, computed energy above ehull (£½//) and the relevant phosphors.

[0009] FIG. 5 shows the calculated phonon spectrum for the predicted Sr₂LiA104 (P2₁/m) crystal structure.

[0010] FIG. 6 shows a table (Table 2) of the calculated and experimental structural parameters of Sr₂LiA104, where the experimental values were obtained from XRD Rietveld refinement of the solid-state reaction samples.

[0011] FIGs. 7A and 7B respectively show the calculated absorption spectra for

Sr₂LiAlO₄:0.0625Eu²⁺ and Sr₂LiAlO₄:0.125Ce³⁺.

[0012] FIG. 8 shows the simulated and measured X-ray diffraction patterns of Sr₂LiA104, Sr₂LiAlO₄:0.005Eu²⁺ and Sr₂LiAlO₄:0.005Ce³⁺.

[0013] FIG. 9 is a table (Table 3) showing the calculated lattice parameters and Rietveld refinement parameters of the X-ray diffraction profile of Sr₂LiA104 synthesized with a solid-state reaction.

[0014] FIG. 10A shows the measured PL spectrum of the Sr₂LiAlO4:0.005Eu²⁺ phosphor excited at 394 nm; FIG. 10B shows the PL spectrum of the Sr₂LiAlO4:0.005Ce ⁺ phosphor measured at 384 nm excitation; FIG. IOC shows the normalized emission intensity of Sr₂LiA104:xEu²⁺ (under 394 nm excitation, circular values) with respect to the Eu²⁺ (x) concentration and

(under 384 nm excitation, square values) with respect to the Ce ⁺ (y) concentration; and FIG. 10D shows the schematic energy level diagram for Eu²⁺/Ce ⁺ ions in the Sr₂LiA104 host crystal structure.

[0015] FIG. 1 1 A shows the excitation spectra and FIG. 1 IB shows the emission spectra of Sr₂LiA104:xEu²⁺ phosphors; FIG. 1 1C shows the normalized excitation spectra and FIG. 1 ID shows the emission spectra of Sr₂LiA104:xEu²⁺ phosphors with respect to Eu²⁺concentration.

[0016] FIGs. 12A and 12B show the deconvoluted photoluminescence emission spectra of Sr₂LiAlO₄:0.005Eu²⁺ at 10 K and 298 K, respectively; and FIGs. 12C and 12D show the deconvoluted photoluminescence emission spectra of Sr₂LiAlO4:0.005Ce ⁺ phosphors at 10 K and 298 K, respectively.

[0017] FIG. 13 shows the projected density of states of Sr₂LiAlO₄:0.028Eu²⁺. [0018] FIG. 14A shows the excitation spectra and FIG. 14B shows the emission spectra of

phosphors with respect to Ce ⁺ concentration; and FIGs. 14C and 14D show the normalized excitation and emission spectra, respectively, of

phosphors with respect to Ce ⁺ concentration.

[0019] FIG. 15A shows the measured temperature-dependent emission spectra for

Sr2LiAlO4:0.005Eu²⁺ under 394 nm excitation in the temperature range of 25-200°C; and FIG. 15B shows the normalized temperature dependent emission intensity under the peak emission wavelength of 559 nm and the integrated emission intensity (total area) with a temperature interval of 25°C.

[0020] FIG.16A shows the temperature-dependent emission spectra of Sr2LiAlO4:0.005Ce ⁺ under 382 nm excitation in the temperature range of 25-200°C and FIG.16B shows the temperature-dependent normalized emission spectra of Sr2LiAlO4:0.005Ce ⁺ under the peak emission wavelength, 460 nm and integrated emission intensity with a temperature interval of 25°C.

[0021] FIG. 17 shows a table (Table 4) of the optical properties of a white light-emitting diode (WLED) fabricated using Sr₂LiAlO₄:0.005Eu²⁺ phosphor with a blue LED (λ_ηαχ = 450 nm) excitation).

[0022] FIG. 18 shows a table (Table 5) of the optical properties of a WLED fabricated using the mixed Sr₂LiAlO₄:0.005Ce ⁺ and Sr₂LiAlO₄:0.005Eu²⁺ phosphor with a near-UV LED ( _max = 400 nm) excitation.

[0023] FIG. 19 shows a table (Table 6) the internal quantum efficiency (IQE) and

photoluminescence (PL) intensity of several phosphors and correlated color temperature (CCT), color rendering index (CRI) and luminous efficacy (LE) of a WLED constructed with these phosphors.

[0024] FIG. 20A shows the electroluminescence (EL) spectra and a photograph of the InGaN LED ( max = 400 nm) + Sr₂LiAlO₄:0.005Ce ⁺ phosphor; FIG. 20B shows the EL spectra and photograph of the InGaN LED (X_max = 400 nm) + Sr₂LiAlO₄:0.005Ce ⁺ + Sr₂LiAlO₄:0.005Eu²⁺ phosphor; FIG. 20C shows the EL spectra and photograph of the InGaN LED ( _max = 450 nm) + Sr2LiAlO4:0.005Eu²⁺ phosphor; FIG. 20D shows a photograph of WLEDs packaged with Sr2LiAlO4:0.005Eu²⁺ phosphor; and FIG. 20E shows the CIE chromatic coordinated of the fabricated Sr2LiA104-based phosphors WLED under various forward bias currents. [0025] FIG. 21 shows a schematic diagram of one example of an exemplary LED assembly 100 according to the disclosed embodiments.

Detailed Description

Data-driven Discovery of New Phosphors

[0025] As shown in FIG. 1 A, the search for new phosphor hosts began by constructing a "solid- state lighting" periodic table from a statistical analysis of all compounds in the 2017 version of the ICSD with the word "phosphor" in the publication title. FIG. 1 A shows the frequency at which each element appears in compounds having the word "phosphor" in the publication title in the 2017 version of ICSD. Only non-rare-earth elements are shown. Elements with frequency 0 are shaded in gray. The high frequency of elements N, S, F and CI can be ascribed to the fact that (oxy)nitrides, (oxy)halides and sulfides are some of the most well-studied phosphor materials. Nevertheless, oxides are overwhelmingly preferred in practical SSL applications due to their typically more facile synthesis and better chemical stability under ambient conditions; therefore, these other anion types will not be further considered in this work. We may observe a

preponderance of the alkaline-earth metals (Mg/Ca/Sr/Ba), alkali metals (Li/Na/K) and main group elements (Al/Si/P/B) among known phosphors. The presence of Ca and Sr is not surprising, given that the ionic radii of Ca²⁺ and Sr²⁺ are similar to those of the common Ce ⁺ and Eu²⁺ activators. Na⁺ also presents a high frequency in phosphor hosts due to its similar size to Eu²⁺. However, activation via aliovalent substitution of Eu²⁺ on Na⁺ would require the identification of the most stable charge-compensating defect and the use of large-supercell DFT calculations. Therefore, we have chosen to focus on systems containing Sr²⁺/Ba²⁺/Ca²⁺ in this work as these are isovalent with Eu²⁺. Given that phosphates, silicates, aluminates and borates are among the most commonly studied oxides in SSL, we then proceeded to identify opportune chemistries for novel phosphor host discovery in the ternary M-X-0 (M=Ba/Sr/Ca,

X=P/Si/Al/B) and quaternary M-L-X-0 (M=Ba/Sr/Ca, L=Li/Mg/Y, X=P/Si/Al/B) oxides.

[0026] We find that while ternary M-X-0 oxides have been relatively well-explored, significant opportunities exist in quaternary M-L-X-0 oxides. In particular, there are no reported

compounds in the ICSD in seven chemistries - Ba/Sr/Ca-Li-Al-O, Sr-Li-P-O, Ba/Sr-Y-P-O, and Ba-Y-Al-0 (FIG. 2). A further search of the larger Pauling File database turned up one known compound each in the Sr-Li-P-O, Ba/Sr-Y-P-0 and Ba-Y-Al-0 chemistries, and still no compounds in the Ba/Sr/Ca-Li-Al-0 chemistries. We generated 918 new crystal structure candidates in these seven unexplored chemical systems by applying a data-mined ionic substitution algorithm on the entire ICSD (see Methods). As shown in FIG. 3, these candidates were then systematically evaluated via an efficiently-tiered series of DFT property calculations. FIG. 3 is a computational high throughput screening workflow for identifying promising broadband emitters. E_G is the host band gap calculated with both Perdew-Burke-Ernzerhof (PBE) functional and Heyd-Scuseria-Ernzerhof (HSE) functional. (¾> is calculated Debye temperature. GW+ SE denotes the Bethe-Salpeter equation (BSE) calculation performed on top of GoWo.

[0027] The first criterion that any technological material must satisfy is synthesizability and stability. Thermodynamic stability is estimated by calculating the energy above the linear combination of stable phases in the 0 K DFT phase diagram, also known as EMi. A typical threshold for synthesizability used in previous DFT screening works is an huii < 30-50 meV/atom. We find that the four known compounds in Sr-Li-P-O, Ba/Sr-Y-P-0 and Ba-Y-Al-0 chemistries are indeed among the candidates generated by the structure prediction algorithm, and all four compounds have a calculated EMU < 35 meV/atom. Table 1 in FIG. 4 shows four known compounds in the Sr-Li-P-O, Ba/Sr-Y-P-0 and Ba-Y-Al-0 chemical spaces, their derivations, computed energy above ehull {EMU) and the relevant phosphors. Known compounds are retrieved from Pauling File database.

[0028] The successful "prediction" of these "unseen" known phosphors gives us confidence that viable candidates are identified via the combination of the data-mined ionic substitution algorithm and DFT calculations. Among the remaining Ba/Sr/Ca-Li-Al-0 chemical systems with no known compounds, we will focus primarily on on the Sr-Li-Al-0 chemistry due the fact that Sr²⁺ has an ionic radius (1.26 A) that is closes to Eu²⁺ (1.25A), compared to Ba²⁺(1.42A) or Ca²⁺(1.12A). Also, Li and Al are inexpensive, earth-abundant elements that tend to form rigid bonds in crystals.

[0029] FIG. IB shows the calculated 0 K SrO-Li₂0-Al₂0 phase diagram. The circles represent known stable phases in the Materials Project database and the square represents a new stable quaternary phase, Sr₂LiA104. We find that one of the new candidates, Sr₂LiA104, is predicted to be thermodynamically stable {EMU = 0). The computed phonon spectrum, shown in FIG. 5, confirms it to be also dynamically stable. The crystal structure of Sr₂LiA104 (spacegroup:

Pl-i/m) is shown in FIG. 1C, and the structural parameters are provided in Table 2 of FIG. 6. The numbers in FIG. 1C indicate Sr-0 bond length in angstroms. Sr₂LiA104 is derived from Ba₂LiReN₄ (ICSD No. 411453) via a multi-species substitution of Ba²⁺ with Sr²⁺, Re⁷⁺ with Al³⁺, and N^3" with O^2". This is clearly a non-trivial crystal prediction that cannot be obtained easily replicated using traditional chemical intuition.

[0030] We evaluated the potential PL properties of the stable Sr₂LiA104 host by calculating its electronic structure and Debye temperature ((¾>). The calculated band gap E_g of Sr₂LiA104 using the Perdew-Burke-Ernzerhof (PBE) functional is 4.19 eV, which suggests that it would yield a green-yellow emission with Eu²⁺ activation based on the inverse relationship between

experimental wavelength and the PBE E_g previously reported by the current authors. In general, host materials that have a large photoionization barrier, defined as the energy gap between conduction band minimum (CBM) and excited 5d level, and are rigid tend to exhibit excellent thermal quenching resistance. The calculated bandgaps of Sr₂LiA104 using the more accurate Heyd-Scuseria-Ernzerhof (HSE) functional and GoWo are 5.91 eV and 6.00 eV, respectively. This large bandgap suggests a strong likelihood of a large photoionization barrier. The calculated 0D of Sr₂LiA104 is 466 K, indicating that it has rigid crystal structure.

[0031] There are two symmetrically distinct Sr crystallographic sites (labelled as Sri and Sr2 in Figure 1C) in Sr₂LiA104, both of which are eight-fold coordinated with oxygen atoms. By performing an isovalent substitution a single Eu²⁺ into a 2 x 2 x 2 supercell of Sr₂LiA104 (16 formula units), we determined using DFT calculations that the Eu²⁺ activator prefers the Sri site to the Sr2 site by about 35 meV. For Ce ⁺ activation, we comprehensively evaluated various charge-neutral defect configurations, taking into account typical experimental synthesis conditions such as excess Li from its volatility at elevated temperature. We find that the

2Ce_s ^" _r+Li_A1 defect combination (Kroger- Vink notation) has the lowest defect formation energy compared to 2Ce_s ^" _r+Vs_r (0.22 eV/Ce ⁺ higher) and Ce_s ^' _r+Lis_r (1.48 eV/Ce ⁺ higher). Hence, we conclude that the substitution of Ce ⁺ on Sr²⁺ is likely to be charge compensated by excess Li⁺ on the Al ⁺ tetrahedra, as opposed to vacancy formation or excess Li⁺ on the Sr²⁺ site. This is consistent with the fact that the small Li⁺ ion (ionic radius = 0.9 A) is likely to prefer the AIO4 tetrahedron rather than the much larger SrOs site. Henceforth, we will use the shorthand notation commonly used in the phosphor community, Sr₂LiA104:xEu²⁺ and

to denote the activated structures with compositions Sr_2-xEuxLiA104 and Sr₂-yCeyLii+y/₂Ali-y/₂04, respectively. All subsequent DFT results on activated hosts, unless otherwise stated, were performed using the configuration with the lowest defect formation energy.

[0032] For efficient conversion, a phosphor should have absorption spectrum peaking at the maximum emission of LEDs chips. The absorption spectra for Sr2LiAlO4:0.0625Eu²⁺ and Sr2LiAlO4:0.125Ce ⁺were calculated using the Bethe-Salpeter equation (BSE) method on top of GoWo. FIGs. 7A and 7B respectively show the calculated absorption spectra for

Sr₂LiAlO₄:0.0625Eu²⁺ and Sr₂LiAlO₄:0.125Ce³⁺. In FIG. 7A Eu²⁺ is located at the most stable site, Sri and Sr₂LiAlO4:0.125Ce ⁺ in FIG. 7B has the lowest energy 2Ce_s"_r+Li j configuration. For both activated phosphors, the main absorption peaks are observed at 380-420 nm, which can be attributed to 4f→ f5d^l transition in Eu²⁺ or 4f → 4f5d^l transition in Ce ⁺. These findings suggest that both Eu²⁺- and Ce ⁺-activated Sr₂LiA104 can be efficiently excited by near-UV LED chips.

Synthesis and Photoluminescence Properties

[0033] The Sr₂LiA104 host and the Eu²⁺- and Ce ⁺-activated phosphors were successfully produced using solid-state reaction as well as combustion synthesis. Here, we will discuss primarily the results from the samples synthesized via solid-state reaction, given that this is the preferred approach in commercial applications due to its low cost, availability of precursors, and potential for production on an industrial scale. In general, other than a higher purity (94% versus 86%) for solid-state reaction), the measured structural parameters and PL properties of the combustion-synthesized samples are very similar. FIG. 8 shows the simulated and measured XRD profiles of the host and activated phosphors, which are in excellent agreement and confirm the successful synthesis of the predicted Sr₂LiA104 compound. The residual factors of Rietveld refinement analysis of the XRD profile (see Table 3 in FIG. 9) are R_Wp = 9.11%, R_p = 6.69%, and goodness of fit (GOF) = 2.79. Table 3 shows the calculated lattice parameters and Rietveld refinement parameters of the X-ray diffraction profile of Sr₂LiA104 synthesized with a solid-state reaction. ^: is the expected residual factor, K_wp: is the weighted profile residual factor, K_p: is the profile residual factor and GOF is the goodness of fit. Values in parentheses are the estimated standard deviations of the last significant figure. As indicated from Tables 2 and 3, the refined structure parameters are also in excellent agreement with those from the DFT relaxed structure. [0034] FIGs. 10A and 10B show the measured excitation and emission spectra of Sr₂LiAlO₄:0.005Eu²⁺ and Sr₂LiAlO₄:0.005Ce³⁺ phosphor, respectively. The measured PL spectrum of the Sr₂LiAlO4:0.005Eu²⁺ phosphor excited at 394 nm (FIG. 10A) shows a green- yellow emission peaking at 512 nm with a shoulder peak of 559 nm. The emission spectrum is broad (FWUM = 73.6 nm) and asymmetric, indicating that Eu²⁺ ions occupy two distinct sites in the Sr₂LiA104 host. The excitation spectrum monitored at 512 nm shows a broad band with two main peaks at 310 nm and 394 nm. The PL spectrum of the Sr₂LiAlO4:0.005Ce ⁺ phosphor measured at 384 nm excitation (FIG. 10B) shows a broad blue emission with a main peak at 434 nm and a FWUM of 70.3 nm. The PL excitation recorded at 434 nm also presents two peaks - one major peak at 384 nm and one minor peak at 291 nm. The measured excitation spectra are consistent with the 4f-5d transitions of Eu²⁺/Ce ⁺ ions, and the BSE-computed excitation wavelengths in FIG. 7.

[0035] A careful optimization of the PL properties of Sr₂LiA104:xEu²⁺ and Sr₂LiA104:.yCe ⁺ was carried out with respect to activator concentration (x, y). FIG. IOC shows the normalized emission intensity of Sr₂LiA104:xEu²⁺ (under 394 nm excitation, circular values) with respect to the Eu²⁺ (x) concentration and

(under 384 nm excitation, square values) with respect to the Ce ⁺ (y) concentration. As FIG. IOC indicates, the emission intensity slightly increases and then decreases with increasing activator concentration, with the maximum emission intensity occurring at x or y = 0.005 for both activators. The measured internal quantum efficiencies of the Sr₂LiAlO₄:0.005Eu²⁺ and Sr₂LiAlO₄:0.005Ce ⁺ phosphors are 25% { _ex = 394 nm) and 32% { _ex = 392 nm), respectively.

[0036] FIG. 1 1 presents the unnormalized and normalized PL spectra of Sr₂LiA104:xEu²⁺ with respect to a series of Eu²⁺ concentrations (0.0025 < x < 0.0500) measured at room temperature. In particular, FIG. 1 1(A) shows the excitation and FIG. 1 1(B) shows the emission spectra of Sr₂LiA104:xEu²⁺ phosphors. Likewise, FIG. 1 1(C) shows the normalized excitation spectra and FIG. 1 1(D) shows the emission spectra of Sr₂LiA104:xEu²⁺ phosphors with respect to

Eu²⁺concentration. With increasing Eu²⁺ concentration, the relative intensity of short excitation wavelength (at 320 nm) gradually decreases, while the relative intensity of long wavelength (at 480 nm) slightly increases, as shown in FIG. 1 1(C). At the same time, a corresponding increase of emission intensity at 559 nm is also observed with increasing of Eu²⁺ concentration when normalized based on emission intensity at 512 nm, as shown in FIG. 1 ID. We believe the lower energy emission (longer wavelength) peaks are associated with more Eu²⁺ occupying the energetically more favorable Sri site. The calculated average bond length (/_av) of EuOs polyhedron in the Sri site and Sr2 site are 0.269 nm and 0.272 nm, respectively, while the distortion indices (D) (see Methods for definitions) are 0.056 and 0.044, respectively. A shorter /_av and larger D is associated with a larger crystal field splitting (CFS). The larger CFS of Eu²⁺ in the Sri site leads to a red shift in emission, as illustrated in FIG. 10D, which shows the schematic energy level diagram for Eu²⁺/Ce ⁺ ions in the Sr₂LiA104 host crystal structure.

A£^" _neand £_c^_sdenote the centroid shift due to the nephelauxetic effect and the crystal field splitting of Eu²⁺/Ce ⁺ ions in the Sr₂LiA104 host, respectively. ΔΕ_Α is the photoionization barrier.

[0037] These conclusions are further supported by deconvolution of the PL emission spectra of Sr₂LiAlO₄:0.005Eu²⁺ at 10 K and 298 K, which are shown in FIGs. 12A and 12B. FIGs. 12A and 12B show the deconvoluted photoluminescence emission spectra of Sr₂LiAlO4:0.005Eu²⁺ at 10 K and 298 K, respectively. FIGs. 12C and 12D show the deconvoluted photoluminescence emission spectra of Sr₂LiAlO4:0.005Ce ⁺ phosphors at 10 K and 298 K, respectively. As the figures indicate, there is a significant decrease in the long wavelength emission at room temperature. The lower thermal stability of the Eu in the Sri site is also a consequence of its larger CFS, which leads to a smaller barrier for photoionization (ΔΕ_Α). To obtain further support for these conclusions, we calculated the HSE projected density of states (FIG. 13) for a

Sr₂LiA104:Eu²⁺ structure where Eu is introduced into both Sri and Sr2 simultanenously. In FIG. 13 a 3 x 3 x 2 supercell of Sr₂LiA104 (72 formula units) was constructed with two Eu atoms, one on the Sri site and the other on the Sr2 site. We find that Eu in the Sri site has a smaller gap (longer excitation wavelength) between the 4f and 5d states compared to Eu in the Sr2 site.

[0038] In contrast, there are no significant changes in the relative intensities of both the excitation and emission peaks at different wavelengths with increasing of Ce ⁺ concentration in

FIG. 14 shows the photoluminescence excitation and emission spectra of

phosphors. In particular, FIG. 14(A) shows the excitation spectra and FIG. 14(B) shows the emission spectra of

phosphors with respect to Ce ⁺

concentration. Likewise, FIGs. 14C and 14D show the normalized excitation and emission spectra, respectively, of

phosphors with respect to Ce ⁺ concentration. The emission spectra of Sr₂LiAlO4:0.005Ce ⁺ can be deconvoluted into four Gaussian peaks at 10 K with position of 433 (peak 1 : 23,095 cm^"1), 468 (peak 2: 21,368 cm^"1), 497 (peak 3 : 20, 121 cm^"1), and 532 nm (peak 4: 18,797 cm^"1), as shown in FIG. 12C. The energy difference between peak 1 and peak 3 is about -2,974 cm^"1 (0.37 eV), and between peak 2 and peak 4 is about -2,571 cm^"1 (0.32 eV). These values correspond to the spin-orbit splitting energy of the lowest 4 level (²Fsn and ²Fjn) in Ce ⁺. However, at 298 K (FIG. 12D), only two Gaussian peaks are observed at 427 nm (23,419 cm^"1) and 460 (21,739 cm^"1). These observations again suggest that the Sri site, associated with the long wavelength emission, is thermally unstable with no PL at room temperature.

Thermal Stability

[0039] In practical applications, WLEDs typically operate at elevated temperatures (~150°C), and a key metric of phosphor performance is its resistance to thermal quenching. FIG. 15A shows the measured temperature-dependent emission spectra for Sr2LiAlO4:0.005Eu²⁺ under 394 nm excitation in the temperature range of 25-200°C. FIG. 15B shows the normalized temperature dependent emission intensity under the peak emission wavelength of 559 nm and the integrated emission intensity (total area) with a temperature interval of 25°C. At 150°C, the emission intensity of the main peak { _em = -512 nm) is about 88% of that at room temperature. The emission intensity of secondary peak { _em = -559 nm), which is associated with Eu²⁺ in the thermally less stable Sri site on the other hand, reduces significantly with increasing

temperature. Overall, Sr2LiAlO4:0.005Eu²⁺ exhibits excellent resistance to thermal quenching. The Sr2LiAlO4:0.005Ce ⁺ phosphor is found to have a slightly better resistance to thermal quenching, retaining 91% of room-temperature peak emission intensity at 150°C. This is illustrated in FIG. 16, which shows in FIG.16A the temperature-dependent emission spectra under 382 nm excitation in the temperature range of 25-200°C and in FIG.16B shows the temperature-dependent normalized emission spectra under the peak emission wavelength, 460 nm and integrated emission intensity with a temperature interval of 25°C.

Performance of WLEDs

[0040] Finally, we constructed a prototype WLED device using Sr₂LiA104:Eu²⁺, Sr₂LiA104:Ce ⁺ as well as a mixture of Sr₂LiA104:Eu²⁺/Ce ⁺. The electroluminescence (EL) spectra of these WLEDs are shown in FIGs. 20A-20C. FIG. 20(A) shows the electroluminescence (EL) spectra and photograph of the InGaN LED (_max = 400 nm) + Sr₂LiAlO₄:0.005Ce³⁺ phosphor. FIG. 20(B) shows the EL spectra and photograph of the InGaN LED (_max = 400 nm) +

Sr₂LiAlO₄:0.005Ce³⁺ + Sr₂LiAlO₄:0.005Eu²⁺ phosphor. FIG. 20(C) shows the EL spectra and photograph of the InGaN LED (_max = 450 nm) + Sr₂LiAlO₄:0.005Eu²⁺ phosphor. FIG. 20(D) shows a photo of WLEDs packaged with Sr₂LiAlO₄:0.005Eu²⁺ phosphor. FIG. 20(E) shows the CIE chromatic coordinated of the fabricated Sr₂LiA10₄-based phosphors WLED under various forward bias currents.

[0041] The prototype WLED using Sr₂LiA10₄:Eu²⁺ exhibits CIE color coordinates of 0.301 and 0.323, with high CRI of 93 and a CCT of 7527 K at a forward bias current of 60 mA (see Table 4 in FIG. 17, which shows the optical properties of a WLED fabricated using a

Sr₂LiAlO₄:0.005Eu²⁺ phosphor with a blue LED (_max = 450 nm) excitation). The excellent CRI of the Sr₂LiA10₄:Eu²⁺ phosphor can be attributed to the feature of its broad band emission by two Sr sites. The CCT of the WLED can be further lowered by using a mixture of

Sr₂LiA10₄:Eu²⁺/Ce ⁺, as shown in Table 5 in FIG. 18, as well as via the addition of a red component. Table 5 shows the optical properties of WLED fabricated using the mixed

Sr₂LiAlO :0.005Ce³⁺ and Sr₂LiAlO :0.005Eu²⁺ phosphor with near-UV LED (_max = 400 nm) excitation. For instance, the recently reported SrLiAl N₄:Eu²⁺ narrow-band red phosphor¹ would be a particularly interesting option, which would allow for the construction of an oxide + nitride device using the same earth-abundant elements. The measured luminous efficacy of WLEDs with Sr₂LiA10₄:Eu²⁺/Ce ⁺ phosphors are 19-36 lm/W, which is comparable to WLEDs utilizing some recently reported novel phosphors, but still somewhat lower than that of commercial WLEDs utilizing the Y Al₅0i₂:Ce ⁺ phosphor. Table 6 in FIG. 19 shows the internal quantum efficiency (IQE) and photoluminescence (PL) intensity of several phosphors and correlated color temperature (CCT), color rendering index (CRI) and luminous efficacy (LE) of a white light- emitting diode (WLED) constructed with these phosphors. To further improve the quantum efficiency of Sr₂LiA10₄, crystal-site engineering techniques, e.g., co-doping with Ba or Ca, may be used to shift the energetic preference and/or tune the CFS of the two Sr sites.

[0042] To conclude, we have identified a new earth-abundant Sr₂LiA10₄ phosphor host - the first known Sr-Li-Al-0 quaternary compound - by composing a "solid-state lighting" periodic table based on statistical analysis of the ICSD to identify unexplored, yet promising chemical spaces with data-mined structure prediction and high-throughput DFT property computations. Sr₂LiA104 comprises inexpensive, earth-abundant elements (other than the rare-earth activator, which is required in small quantities), and the DFT and PL results show Sr₂LiA104:Eu²⁺/Ce ⁺ to have efficient near-UV excitation, good thermal quenching resistance and broad green-yellow/blue emission. High purity Sr₂LiA104-based phosphors can be synthesized with scalable, industrially-relevant methods. We therefore believe the new Sr₂LiA104:Eu²⁺/Ce ⁺ phosphors to be highly promising candidates for low-cost, high- CRI WLED applications.

Experimental Procedures

[0043] New crystal structure candidates for the target chemistries were generated by applying a retrained version of the ionic substitution algorithm developed by Hautier et al, "Data Mined Ionic Substitutions for the Discovery of New Compounds," Inorg. Chem. 50, 656-663, on the Inorganic Crystal Structure Database (ICSD). This algorithm codifies data-mined probabilities for substitution of one species by another. New candidates are generated by performing high- probability substitutions on a list of known crystal structures, in this case, all ordered crystal structures in the 2017 version of the ICSD.

[0044] All density functional theory (DFT) calculations were carried out using the Vienna ab initio simulation package (VASP) within the projector-augmented wave method. The generalized gradient approximation Perdew-Burke-Ernzerhof (PBE) functional was used for structural relaxations and energy calculations. The plane wave energy cutoff was 520 eV, and the Brillouin zone was integrated with a &-point grid at least of 100 per A^"3 (reciprocal lattice volume). All host crystal structures were relaxed with parameters in line with Materials Project. The

Eu²⁺/Ce ⁺-activated phosphor structures were fully relaxed until the energies and forces were converged to 10^"5 eV and 0.01 eV/ A, respectively. All crystal structure manipulations and data analysis were carried out using the Python Materials Genomics package.

[0045] The phase stabilities of the predicted Sr-Li-Al-0 compounds were estimated by calculating the energy above the linear combination of stable phases in the 0 K DFT phase diagram, also known as the energy above hull, EMU. Previous studies have shown that -60% of ICSD oxides have Ehuii less than 30 meV/atom; we therefore use this threshold as a reasonable cutoff for synthesizability. For phase diagram construction, the energies of all compounds other than those of direct interest in this work were obtained from the Materials Project via the Materials Application Programming Interface. Further, the dynamical stability of the identified Sr₂LiA104 host was evaluated by computing the phonon spectrum using density functional perturbation theory as implemented in the Phonopy code in conjunction with VASP as the force calculator. More stringent energy and force criteria of 10^"8 eV and 10^"4 eV/A, respectively, were used for these calculations.

[0046] Defect formation energies were calculated using the formalism presented by Wei et al.:

where i¾_t ^and E _ot are the total energies of the structure with and without the defect(s), respectively; μ, is the atomic chemical potential of species i; n, indicates the number of atoms of species i being added (n, > 0) or removed (n, < 0) to form the defect, μ, is estimated based on the chemical pontentials for each specie based on the relevant region of the 0 K DFT phase diagram. The host band gaps were calculated using PBE for the initial rapid screening, and more detailed investigations of the electronic structure of Sr₂Li AIO4 were carried out using the more computationally expensive and accurate screened hybrid Heyd-Scuseria-Ernzerhof (HSE) functional and single-shot GW method. The Bether-Salpeter equation (BSE) simulation was performed on top of G0W0 to calculate the absorption spectrum of Eu²⁺/Ce ⁺-activated Sr₂LiA104 phosphors. A large supercell model (2^χ2^χ2, 128-atoms) was adopted to mimic the relatively low Eu²⁺/Ce ⁺ concentrations in experiment, and to avoid interactions between periodic images of activators.

[0047] The Debye temperature, Θο, was evaluated using the quasi-harmonic model. The elastic tensor was calculated with more stringent electronic convergence criterion of 10^"6 eV, and the elastic moduli were calculated using the Voigt-Reuss-Hill approximation.

[0048] The local environment of the Eu²⁺ activator was characterized using the average Eu-0 bond length (l_av) and the distortion index (D) of the EuOs coordination polyhedron. As per previous works, D is defined given by D = -∑₌₁ ^lav^ , where l_t is the distance from the

n l_av

center atom to the z^'th coordinating atom, and n is the total number of Eu-0 bonds (n = 8 in this case).

[0049] Solid state reaction synthesis was performed using SrO (Kojundo, 99.9%), Li₂C0₃ (Kojundo, 99.9%), α-Α1₂0₃ (Kojundo, 99.9%), and Eu₂0₃ (Kojundo, 99.9%) or Ce0₂ (Kojundo, 99.99%)). Stoichiometric amounts of the starting materials were ground in agate mortar, placed in alumina crucibles, and fired at 900°C for 4 h in a horizontal tube furnace using a 25% H2/N2 gas mixture to obtain Sr₂LiA10 :xEu²⁺ and Sr₂LiA10 :yCe ⁺ (0.0025 < x, y < 0.0500). After heat treatment, the samples were cooled to room temperature and ground well with agate mortar into fine powders for further analysis. Excess Li source of up to 10 wt% was introduced to compensate for Li evaporation during synthesis.

[0050] Combustion reaction synthesis was performed using Sr₂(N0 )₂ (99.99%, Sigma Aldrich), LiN0 (ReagentPlus, Sigma Aldrich), Α1(Ν0₃)₃·9Η₂0 (ACS reagent, J. T. Baker), Eu(N0₃)₃ from Eu₂0₃ (99.99%, Alfa Aesar) with nitric acid (69.3%, Fisher Scientific), and Ce(N0₃)₃ (99.99%), Alfa Aesar) as precursors, assisted by the exothermal reaction between urea (Certified ACS, Fisher Scientific) and ammonium hydroxide (Certified ACS, Fisher Scientific) at 600°C. A post-annealing condition was 800°C for five hours in a 5%>H₂/95%>N₂ atmosphere to transform Eu³⁺ to Eu²⁺to obtain Sr₂LiA10₄:xEu²⁺ and Sr₂LiA10 :yCe ⁺ (0.001 < x, y < 0.040). Excess Li source of up to 25 wt%> was introduced to compensate for Li sublimation during synthesis.

[0051] The powders by combustion reaction were analyzed by X-ray diffraction (XRD, Bruker D2 Phaser, Karlsruhe, Germany) using CuKa radiation and a step size of 0.014° over a 2Θ range of 20 to 80°. X-ray diffraction (XRD) data of powders by solid state reaction were obtain using CuKa radiation (Philips X'Pert). XRD data were collected over angles of 10° < 2Θ < 120° with a step size of 0.026°. Structural information of the synthesized samples was derived by refinement using the TOPAS software suite from the XRD result. The VESTA program was used to draw the crystal structure.

[0052] Photoluminescence of the solid-state-reaction synthesized samples was measured using a Hitachi F-4500 fluorescence spectrophotometer over a wavelength range of 200-700 nm. The quantum yield was measured with 394 nm and 450 nm excitation using a xenon laser

(Hamamatsu C9920-02) at the Korea Photonics Technology Institute (KOPTI), Gwangju, South Korea. The thermal quenching characteristics were measured in the temperature range of 25- 200°C, connected to the Hitachi F-4500 fluorescence spectrophotometer with the integrated heater, temperature controller, and thermal sensor. Low-temperature PL spectra were obtained under excitation at 325 nm He-Cd laser connected to the cryostat system at the temperature of 10 K in the KOPTI, Gwangju, South Korea.

[0053] The white LED device prototype was fabricated by integrating the Sr₂LiAlO₄:0.005Ce ⁺ and mixed Sr₂LiAlO :0.005Ce ⁺/Eu²⁺ phosphors on a InGaN near UV LED chip (λ_ηαχ = 400 nm) and the Sr2LiAlO4:0.005Eu²⁺ phosphor on a InGaN blue LED chip _max = 450 nm). The device was then encapsulated in a phosphor/silicon resin mixture, with the mixture placed directly on the headers of LED chip and cured at 150°C for 1 h. After the packaging was completed, the WLED device was measured in an integrating sphere under direct current forward bias condition.

[0054] FIG. 21 shows a schematic diagram of one example of an exemplary LED assembly 100 according to the disclosed embodiments. The LED assembly may include a semiconductor UV or blue radiation source, such as a light emitting diode (LED) chip 105 and leads 110 electrically attached to the LED chip 105. The leads 110 may provide power to the LED chip 105 that may cause the LED chip 105 to emit radiation.

[0055] In one embodiment, the LED assembly 100 may include any semiconductor blue or UV light source that is capable of producing white light when its emitted radiation is directed through a luminescent material 115. In at least one embodiment, the semiconductor light source may include a blue emitting LED chip doped with various impurities. For example, the LED chip 105 may have at least one semiconductor layer including GaN, ZnSe or SiC. In some

embodiments, the LED chip may be a UV or blue emitting LED having a peak emission wavelength from about 400 to about 470 nm.

[0055] The LED chip 105 may be encapsulated within a shell 120 which encloses the LED chip. The shell 120 may be made of, for example, a glass or plastic material and may be transparent or substantially optically transmissive with respect to wavelengths of light produced by the LED chip 105 and the luminescent material 115. The LED chip 105 and the shell 120 may be mounted on a substrate 125.

[0056] According to some of the disclosed embodiments, the luminescent material 115 may include any combination of one or more of the phosphors described herein. In particular, the phosphor may include a quaternary compound M-Li-Al-O, where M is Ba, Sr, or Ca, activated by Eu²⁺ or Ce ⁺. For instance, the quaternary compound is M2L1AIO4, ML13AIO4 or ML1AIO3.

Claims

1. A light emitting diode (LED) assembly, comprising:

an LED light source having a first light output with a characteristic spectrum; and at least one phosphor through which the first light output passes, the at least one phosphor including a quaternary compound M-Li-Al-O, where M is Ba, Sr, or Ca, activated by Eu²⁺ or

Ce³⁺.

2. The LED assembly of claim 1 wherein the quaternary compound is M2L1AIO4.

3. The LED assembly of claim 1 wherein the quaternary compound is ML13AIO4.

4. The LED assembly of claim 1 wherein the quaternary compound is ML1AIO3.

5. The LED assembly of claim 1 wherein the quaternary compound is a Sr-Li.Al-0 compound activated with Eu².

6. The LED assembly of claim 5 wherein the LED light source is a blue LED.

7. The LED assembly of claim 5 wherein the at least one phosphor includes a plurality of phosphors, a first phosphor including Sr₂LiA104 activated by Eu²⁺ and a second phosphor including Sr₂LiA104 activated by Ce ⁺.

8. The LED assembly of claim 7 wherein the LED light source is a near ultraviolet (UV) LED.

9. A light emitting diode (LED) assembly, comprising:

an LED light source having a first light output with a characteristic spectrum with a peak emission at a blue or near ultraviolet wavelength; and

at least one phosphor through which the first light output passes, the at least one phosphor including a quaternary compound Sr-Li-Al-O, activated by Eu²⁺ or Ce ⁺.