WO2019069232A1 - Scr catalyst compositions, catalysts, and catalyst systems incorporating such catalysts - Google Patents
Scr catalyst compositions, catalysts, and catalyst systems incorporating such catalysts Download PDFInfo
- Publication number
- WO2019069232A1 WO2019069232A1 PCT/IB2018/057650 IB2018057650W WO2019069232A1 WO 2019069232 A1 WO2019069232 A1 WO 2019069232A1 IB 2018057650 W IB2018057650 W IB 2018057650W WO 2019069232 A1 WO2019069232 A1 WO 2019069232A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- oxide
- treatment system
- catalyst
- substrate
- scr catalyst
- Prior art date
Abstract
Description
Claims