WO2019058313A1 - Accelerating admixture for hydraulic compositions - Google Patents
Accelerating admixture for hydraulic compositions Download PDFInfo
- Publication number
- WO2019058313A1 WO2019058313A1 PCT/IB2018/057284 IB2018057284W WO2019058313A1 WO 2019058313 A1 WO2019058313 A1 WO 2019058313A1 IB 2018057284 W IB2018057284 W IB 2018057284W WO 2019058313 A1 WO2019058313 A1 WO 2019058313A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- cement
- hydration
- admixture
- accelerating admixture
- product
- Prior art date
Abstract
Description
Claims