WO2019056361A1 - Aqueous polymer composition - Google Patents
Aqueous polymer composition Download PDFInfo
- Publication number
- WO2019056361A1 WO2019056361A1 PCT/CN2017/103161 CN2017103161W WO2019056361A1 WO 2019056361 A1 WO2019056361 A1 WO 2019056361A1 CN 2017103161 W CN2017103161 W CN 2017103161W WO 2019056361 A1 WO2019056361 A1 WO 2019056361A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- weight
- polymer composition
- aqueous polymer
- aqueous
- polymer
- Prior art date
Abstract
Description
Sample name | n | m |
PP-7025 | 0 | 3 |
UCAN-5 | 0 | 5 |
UCAN-6 | 5 | 0 |
UCAN-7 | 4 | 5 |
COPS-3 | 4 | 0 |
UCAN-9 | 0 | 8 |
Claims (9)
- An aqueous polymer composition, comprising,(i) a polymer comprising, based on the weight of the polymer, from 0.1%to 10%by weight of structural units of an allyl alkoxylated phosphate monomer having the structure of formula (I) ,wherein m is from 2 to 5, n is from 0 to 10, l is 1 or 2, and Y is -OH or -O-M+, where M is a metal ion or ammonium ion;(ii) a functional silane selected from an epoxy functional polysiloxane oligomer, an epoxy functional silane compound, an ethylenically unsaturated compound carrying at least one alkoxysilane functionality, or mixtures thereof; and(iii) a phosphate surfactant having the structure of formula (V) ,wherein R is a C8-C30 alkyl, AO is an alkoxylated group, b is from 1 to 2, a is from 1 to 30, and N+ is a metal ion or ammonium ion.
- The aqueous polymer composition of claim 1, wherein, in formula (I) , m is from 3 to 5, n is from 0 to 5, and Y is -O-M+, where M is a metal ion or ammonium ion.
- The aqueous polymer composition of claim 1, wherein the polymer comprises, based on the weight of the polymer, from 0.5%to 3%by weight of structural units of the allyl alkoxylated phosphate monomer.
- The aqueous polymer composition of claim 1, wherein the functional silane is selected from the group consisting of 3-glycidyloxypropyl trimethoxysilane, 3-glycidyloxypropyl triethoxysilane, 3-glycidyloxypropyl methyldiethoxysilane, 3-glycidyloxypropyl methyldimethoxysilane, vinyltrialkoxysilanes, alkylvinyldialkoxysilanes, and (meth) acryloxyalkyltrialkoxysilanes.
- The aqueous polymer composition of claim 1, wherein the functional silane is present in an amount of from 0.1%to 3%by weight, based on the weight of the polymer.
- The aqueous polymer composition of claim 1, wherein the polymer further comprises, based on the weight of the polymer, from 0.1%to 5%by weight of structural units of an ethylenically unsaturated alkoxylated (meth) acrylate monomer.
- The aqueous polymer composition of claim 1, comprising from 0.1%to 5%by weight of the phosphate surfactant, based on the weight of the polymer.
- An aqueous coating composition having a VOCs content of 5 g/L or less, comprising an aqueous polymer composition of any one of claims 1-8, and at least one component selected from the group consisting of a dispersant, a coalescent, a wetting agent, a thickener, a defoamer, a pigment, and an extender.