WO2018230417A1 - 立毛調人工皮革 - Google Patents
立毛調人工皮革 Download PDFInfo
- Publication number
- WO2018230417A1 WO2018230417A1 PCT/JP2018/021748 JP2018021748W WO2018230417A1 WO 2018230417 A1 WO2018230417 A1 WO 2018230417A1 JP 2018021748 W JP2018021748 W JP 2018021748W WO 2018230417 A1 WO2018230417 A1 WO 2018230417A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polyurethane
- napped
- artificial leather
- raised
- less
- Prior art date
Abstract
Description
立毛調人工皮革の立毛面に対して、JIS L 1096(6.17.5E法 マーチンデール法)に準じ、押圧荷重12kPa(gf/cm2)、摩耗回数5万回でマーチンデール摩耗試験機を用いて摩耗試験を行った。そして、SEMにより50倍で摩耗試験後のマーチンデール摩耗試験をした部分の立毛面の写真を撮影した。図1に実施例1で得られた立毛調人工皮革の立毛面のSEM写真、図2に比較例2で得られた立毛調人工皮革の立毛面のSEM写真を示す。そして、その写真をA4サイズに拡大して印刷し、ポリウレタンが現れた部分を赤く塗った。そして、赤く塗った部分を切り抜いた。そして、観察領域全体の全体重量と切り抜き後の重量を測定して、ポリウレタンが現れた部分の面積割合を算出した。なお、測定は平均的な部分の画像を3枚測定し、3枚の平均値とした。
立毛調人工皮革の立毛面のL*a*b*表色系に基づくL*値は、分光光度計((株)日立製作所製 U-3010)を用いて測定された。はじめに、立毛調人工皮革の立毛面のL*値を測定した。そして、その立毛調人工皮革の立毛面に対して、JIS L 1096(6.17.5E法 マーチンデール法)に準じ、押圧荷重12kPa(gf/cm2)、摩耗回数5万回でマーチンデール摩耗試験機を用いて摩耗試験を行った。そして、摩耗試験後の立毛面のL*値を測定した。そして、摩耗試験前の立毛面のL*値と、摩耗試験後のマーチンデール摩耗試験をした部分の立毛面のL*値との差である明度差ΔL*を算出した。
立毛調人工皮革の立毛面の表面状態は、非接触式の表面粗さ・形状測定機である「ワンショット3D測定マクロスコープ VR-3200」((株)キーエンス製)を用いてISO 25178(面粗さ測定)に準じて測定した。具体的には、立毛調人工皮革の立毛面を立毛が寝る方向である順目方向にシールブラシで整毛した。そして、整毛された立毛面の18mm×24mmの範囲を高輝度LEDから照射された構造化照明光により、400万画素モノクロC-MOSカメラで12倍の倍率で歪みの生じた縞投影画像撮影を行い、平均高さから100μm以上の高さを有する山頂点密度(Spd)を求めた。測定は3回行い、その平均値を各数値として採用した。
各例における不織布を製造するために紡糸した海島型複合繊維の複数本を、若干たるませた状態でポリエステルフィルムの表面にセロハンテープで貼り付けた。そして、95℃の熱水中に30分間以上浸漬させて海成分を抽出除去することにより極細繊維を得た。次に、極細繊維を固定したポリエステルフィルムをPot染色機で120℃×20分間染色処理し、染色糸を得た。そして、染色糸の中から海島型複合繊維1本に対応する極細繊維束をまとめてオートグラフで強伸度を測定し、極細繊維の繊維束の強伸度をオートグラフで測定した。そして、得られたSSカーブのピークトップから破断強力と破断伸度を読み取り、染色後の糸タフネス(cN・%)=破断強力(cN)×破断伸度(%)/極細繊維の本数の式から糸タフネスを算出した。
各例で用いた第1のポリウレタンまたは第2のポリウレタンのフィルムを作成し、2.5cm幅に切り出したものをオートグラフで強伸度測定した。得られたSSカーブの伸度100%の強力を読み取り、フィルム厚みと2.5cm幅から得られた断面積で割り、100%モジュラスを算出した。
水溶性ポリビニルアルコール樹脂(PVA:海成分)と、カーボンブラックが1.5質量%添加された変性度6モル%のイソフタル酸変性ポリエチレンテレフタレ-ト(島成分)とを、海成分/島成分が25/75(質量比)となるように260℃で溶融複合紡糸用口金(島数:12島/繊維)より単孔吐出量1.5g/minで吐出した。紡糸速度が3700m/minとなるようにエジェクター圧力を調整し、平均繊度3.0デシテックスの長繊維をネット上に捕集して、繊維ウェブを得た。
極細繊維を形成する島成分中のカーボンブラックの配合割合を1.5質量%から1.0質量%に変更し、第1のポリウレタンの含有割合を10質量%から13質量%に変更した以外は、実施例1と同様にして黒色のスエード調人工皮革を得、評価した。結果を表1に示す。
極細繊維を形成する島成分中のカーボンブラックの配合割合を1.5質量%から1.0質量%に変更し、第1のポリウレタンの含有割合を10質量%から13質量%に変更し、第2のポリウレタンとして、溶剤系ポリウレタンである100%モジュラス4.5MPaのポリカーボネート系ポリウレタン樹脂の溶液を塗布する代わりに、溶剤系ポリウレタンである100%モジュラス12.5MPaの溶剤系ポリウレタンの溶液を塗布した以外は、実施例1と同様にして黒色のスエード調人工皮革を得、評価した。結果を表1に示す。
極細繊維を形成する島成分中のカーボンブラックを1.5質量%配合する代わりに、カーボンブラックを配合しなかった以外は実施例1と同様にして茶色のスエード調人工皮革を得、評価した。結果を表1に示す。
第2のポリウレタンとして、100%モジュラス5.0MPaである水分散エマルジョンを塗布した以外は、実施例1と同様にして黒色のスエード調人工皮革を得、評価した。
結果を表1に示す。
0.30dtexの極細繊維の不織布の代わりに、0.33dtexの極細繊維の不織布に変更し、極細繊維を形成する島成分中のカーボンブラックを1.5質量%配合する代わりに、カーボンブラックを配合しなかった以外は実施例1と同様にして茶色のスエード調人工皮革を得、評価した。結果を表1に示す。
極細繊維を形成する島成分中のカーボンブラックの配合割合を1.5質量%から1.0質量%に変更し、繊維基材中の不織布に含浸させたポリウレタンの割合を10質量%から13質量%に変更し、表面に100%モジュラス4.5MPaのポリカーボネート系ポリウレタン樹脂を塗布する代わりに、100%モジュラス16MPaのポリウレタンを塗布した以外は、実施例1と同様にして黒色のスエード調人工皮革を得、評価した。結果を表1に示す。
極細繊維を形成する島成分中のカーボンブラックの配合割合を1.5質量%から1.0質量%に変更し、第1のポリウレタンの含有割合を10質量%から13質量%に変更し、第2のポリウレタンとして、溶剤系ポリウレタンである100%モジュラス4.5MPaのポリカーボネート系ポリウレタン樹脂の溶液を塗布する代わりに、溶剤系ポリウレタンである100%モジュラス3.25MPaのポリウレタンを塗布した以外は、実施例1と同様にして黒色のスエード調人工皮革を得、評価した。結果を表1に示す。
極細繊維を形成する島成分中のカーボンブラックの配合割合を1.5質量%配合する代わりに、カーボンブラックを配合せず、第1のポリウレタンの含有割合を10質量%から20質量%に変更し、第2のポリウレタンを塗布しなかった以外は、実施例1と同様にしてピンク色のスエード調人工皮革を得、評価した。結果を表1に示す。
Claims (10)
- 極細繊維を含む不織布とポリウレタンとを含み、表面の前記極細繊維を立毛させた立毛面を備える立毛調人工皮革であって、
前記立毛面は、JIS L 1096(6.17.5E法 マーチンデール法)に準じた、押圧荷重12kPa(gf/cm2)、摩耗回数5万回のマーチンデール摩耗試験の後において、電子顕微鏡による表面観察により前記マーチンデール摩耗試験をした部分に観察されるポリウレタンの面積割合が4.0%以下である立毛調人工皮革。 - 前記立毛面は、ISO 25178に準じた面粗さ測定において、平均高さから100μm以上の高さを有する山頂点密度(Spd)が25/432mm2以上である請求項1に記載の立毛調人工皮革。
- 前記極細繊維は、糸タフネスが平均25.0cN・dtex以下である請求項1または2に記載の立毛調人工皮革。
- 前記極細繊維は、顔料を0.1~10質量%含有する請求項1~3の何れか1項に記載の立毛調人工皮革。
- 前記立毛面のL*a*b*表色系に基づくL*値(明度)が35以下である請求項1~4の何れか1項に記載の立毛調人工皮革。
- 前記マーチンデール摩耗試験の前後における、前記立毛面における前記マーチンデール摩耗試験をした部分のL*a*b*表色系に基づくL*値(明度)の差ΔL*が6.0以下である請求項1~5の何れか1項に記載の立毛調人工皮革。
- 前記ポリウレタンは前記不織布に含浸付与された第1のポリウレタンを含み、前記不織布と前記第1のポリウレタンとの合計量に対して前記第1のポリウレタンの含有割合が15質量%以下である請求項1~6の何れか1項に記載の立毛調人工皮革。
- 前記第1のポリウレタンは、水系ポリウレタンである請求項7に記載の立毛調人工皮革。
- 前記ポリウレタンは、前記立毛面に偏在する第2のポリウレタンをさらに含み、前記第2のポリウレタンの100%モジュラスが4.5~12.5MPaである請求項7または8に記載の立毛調人工皮革。
- 前記第2のポリウレタンは、溶剤系ポリウレタンである請求項9に記載の立毛調人工皮革。