WO2018145513A1 - 3d玻璃成型方法 - Google Patents

3d玻璃成型方法 Download PDF

Info

Publication number
WO2018145513A1
WO2018145513A1 PCT/CN2017/115788 CN2017115788W WO2018145513A1 WO 2018145513 A1 WO2018145513 A1 WO 2018145513A1 CN 2017115788 W CN2017115788 W CN 2017115788W WO 2018145513 A1 WO2018145513 A1 WO 2018145513A1
Authority
WO
WIPO (PCT)
Prior art keywords
operating platform
frequency heating
high frequency
mold
temperature
Prior art date
Application number
PCT/CN2017/115788
Other languages
English (en)
French (fr)
Inventor
钟永材
熊智春
Original Assignee
中山市合赢智能装备有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 中山市合赢智能装备有限公司 filed Critical 中山市合赢智能装备有限公司
Priority to ZA2018/00134A priority Critical patent/ZA201800134B/en
Publication of WO2018145513A1 publication Critical patent/WO2018145513A1/zh

Abstract

一种3D玻璃成型方法,包括如下步骤：驱动气缸驱动第一操作平台运动至第一指定位置；在第一指定时间内高频发热圈将模具加热至第一指定温度；驱动气缸驱动该第一操作平台运动至初始位置；拨料机构将模具从第一操作平台输送至第二操作平台；驱动气缸驱动第二操作平台运动至第二指定位置；在第二指定时间内高频发热圈将模具加热至第二指定温度；驱动气缸驱动第二操作平台沿远离高频发热圈方向运动至初始位置；关闭高频发热圈。

Description

技术领域
[0001] 本发明涉及玻璃加工领域， 具体涉及一种 3D玻璃成型方法。
背景技术
[0002] 现有的玻璃片热弯成型加工工艺是通过加热使玻璃软化变形形成的， 其常用的 加工设置一般由成型模具和加热炉结合运用而实现其加工工艺， 即在加热炉作 用下， 玻璃片可根据成型模具而软化成型为特定尺寸或形状， 但是， 由于成型 模具的限制， 使得玻璃片热弯成像的形状与尺寸也受到了限制， 若以多规格玻 璃为生产目的， 而需要多规格的成型模具， 从而导致生产成本加大， 因此实现 多规格玻璃片成型是一个仍待解决的问题。
[0003] 同吋又因为加热炉的建立规模以及工作模式， 其运用也是高成本生产的因素之 一， 由此可见， 现有的玻璃片热弯成型加工设置及其工艺的实现， 是需要较大 成本其局限性较大， 而且热弯成型的玻璃片总产量低， 热弯效率成型低下， 不 利于玻璃片热弯成型工艺的发展。
[0004] 因此， 有必要提供一种新的 3D玻璃成型方法解决上述技术问题。
技术问题
问题的解决方案
技术解决方案
[0005] 为了解决上述技术问题， 本发明提供一种结构简单、 加热效果优良且生产效率 高的 3D玻璃成型方法。
[0006] 本发明提供 3D玻璃成型方法， 所述 3D玻璃成型方法， 用于加工 3D薄片玻璃， 包括如下步骤：
[0007] 提供储存有待加工的所述 3D薄片玻璃的模具、 高频发热圈、 温度传感器、 第一 操作平台及驱动气缸， 其中， 所述模具设于所述第一操作平台， 所述温度传感 器用于检测所述模具的温度； [0008] 所述驱动气缸驱动所述第一操作平台沿靠近所述高频发热圈方向运动至第一指 定位置；
[0009] 在第一指定吋间内所述高频发热圈将所述模具加热至第一指定温度， 其中， 第 一指定吋间的范围为 10至 70秒， 所述第一指定温度的范围为 350至 750摄氏度； [0010] 当所述温度传感器检测到所述模具的温度达到所述第一指定温度吋， 所述驱动 气缸驱动所述第一操作平台沿远离所述高频发热圈的方向运动至初始位置；
[0011] 提供拨料机构及第二操作平台；
[0012] 所述第一操作平台运动至初始位置吋， 所述拨料机构将所述模具从所述第一操 作平台输送至所述第二操作平台；
[0013] 所述驱动气缸驱动所述第二操作平台沿靠近所述高频发热圈方向运动至第二指 定位置；
[0014] 在第二指定吋间内所述高频发热圈将所述模具加热至第二指定温度， 其中， 所 述第二指定吋间的范围为 10至 70秒， 所述第二指定温度的范围为 500至 850摄氏 度；
[0015] 当所述温度传感器检测到所述模具的温度达到所述第二指定温度吋， 所述驱动 气缸驱动所述第二操作平台沿远离所述高频发热圈方向运动至初始位置；
[0016] 关闭所述高频发热圈。
[0017] 优选的， 所述第一指定吋间为 30秒， 所述第一指定温度为 400摄氏度。
[0018] 优选的， 所述第二指定吋间为 35秒， 所述第二指定温度为 550摄氏度。
[0019] 优选的， 所述温度传感器为红外线传感器。
[0020] 相比较于相关技术， 本发明提供的 3D玻璃成型方法有以下有益效果：
[0021] 所述 3D玻璃成型方法包括如下步骤：
[0022] 所述驱动气缸驱动所述第一操作平台沿靠近所述高频发热圈方向运动至第一指 定位置；
[0023] 在第一指定吋间内所述高频发热圈将所述模具加热至第一指定温度， 其中， 第 一指定吋间的范围为 10至 70秒， 所述第一指定温度的范围为 350至 750摄氏度；
[0024] 当所述温度传感器检测到所述模具的温度达到所述第一指定温度吋， 所述驱动 气缸驱动所述第一操作平台沿远离所述高频发热圈的方向运动至初始位置； [0025] 提供拨料机构及第二操作平台；
[0026] 所述第一操作平台运动至初始位置吋， 所述拨料机构将所述模具从所述第一操 作平台输送至所述第二操作平台；
[0027] 所述驱动气缸驱动所述第二操作平台沿靠近所述高频发热圈方向运动至第二指 定位置；
[0028] 在第二指定吋间内所述高频发热圈将所述模具加热至第二指定温度， 其中， 所 述第二指定吋间的范围为 10至 70秒， 所述第二指定温度的范围为 500至 850摄氏 度；
[0029] 当所述温度传感器检测到所述模具的温度达到所述第二指定温度吋， 所述驱动 气缸驱动所述第二操作平台沿远离所述高频发热圈方向运动至初始位置；
[0030] 关闭所述高频发热圈。
发明的有益效果
有益效果
[0031] 与相关技术相比， 本发明提供的 3D玻璃成型方法通过高频加热与模具传热实现 加热效果好， 速度快， 通过一次预热和一次恒温， 重叠加热， 提高了加热功效 ， 从而最大程度的提升了生产效率。
对附图的简要说明
附图说明
[0032] 图 1为运用本发明提供 3D玻璃成型方法的 3D玻璃热弯成型机的结构示意图； [0033] 图 2为图 1所示的 3D玻璃热弯成型机的正视图；
[0034] 图 3为本发明提供的 3D玻璃成型方法的工作流程图。
实施该发明的最佳实施例
本发明的最佳实施方式
[0035] 下面结合附图和实施方式对本发明做进一步说明。 请结合参阅图 1及图 2， 图 1 为本发明提供的 3D玻璃热弯成型机的立体图， 图 2为图 1所示的 3D玻璃热弯成型 机的正视图。 所述 3D玻璃热弯成型机 100， 用于加工 3D薄片玻璃， 其包括台架 1 、 加热组件 2、 操作平台 3、 驱动气缸 4、 连接平台 5、 模具 6、 拨料机构 7及温度 传感器 8。
[0036] 所述加热组件 2悬设于所述台架 1内， 所述加热组件 2包括高频发热圈 21及支架 2 3， 所述高频发热圈 21包括第一高频发热圈 211及第二高频发热圈 213， 所述第一 高频发热圈 211与所述第二高频发热圈 213间隔相邻设置， 所述支架 23包括第一 支架 231及第二支架 233， 所述第一支架 231连接所述第一高频发热圈 211与所述 台架 1， 所述第二支架 233连接所述第二高频发热圈 213与所述台架 1。
[0037] 所述操作平台 3贯穿所述台架 1的底端， 且与所述高频发热圈 21间隔相对设置， 所述操作平台 3包括第一操作平台 31与第二操作平台 33， 所述第一操作平台 31与 所述第二操作平台 33间隔相邻设置， 所述第一操作平台 31与所述第一高频发热 圈 211间隔相对设置， 所述第二操作平台 33与所述第二高频发热圈 213间隔相对 设置。
[0038] 所述驱动气缸 4包括第一驱动气缸 41及第二驱动气缸 43， 所述第一驱动气缸 41 驱动所述第一操作平台 31沿靠近或远离所述第一高频发热圈 211的方向运动， 所 述第二驱动气缸 43驱动所述第二操作平台 33沿靠近或远离所述第二高频发热圈 2 13沿靠近或远离所述第二高频发热圈 213的方向运动。
[0039] 具体的， 所述第一操作平台 31包括第一托板 311及第一导柱 313， 所述第一导柱 313贯穿所述台架 1的底端， 且连接所述第一托板 311与所述第一驱动气缸 41， 所 述第二操作平台 33包括第二托板 331及第二导柱 333， 所述第二导柱 333贯穿所述 台架 1的底端， 且连接所述第二托板 331与所述第二驱动气缸 43。
[0040] 所述连接平台 5连接所述第一托板 311与所述第二托板 331。
[0041] 所述模具 6设于所述第一操作平台 31的第一托板 311， 用于存储待加工的 3D薄片 玻璃。
[0042] 所述拨料机构 7与所述第一托板 311相邻设置， 用于将位于所述第一托板 311的 所述模具 6经所述连接平台 5输送至所述第二操作平台 33的所述第二托板 331上。
[0043] 所述温度传感器 8固设于所述台架 1， 所述温度传感器 8包括第一温度传感器 81 及第二温度传感器 83， 所述第一温度传感器 81与所述第一高频发热圈 211间隔相 对设置， 且用于检测位于所述第一操作平台 31的所述模具 6的温度， 所述第二温 度传感器 83与所述第二高频发热圈 213间隔相对设置， 且用于检测位于所述第二 操作平台 33的所述模具 6的温度。 所述第一温度传感器 81和所述第二温度传感器
83均为红外线温度传感器。
[0044] 请参阅图 3， 图 3为本发明提供的 3D玻璃成型方法的工作流程图， 所述 3D玻璃 成型方法包括如下步骤：
[0045] 提供储存有待加工的所述 3D薄片玻璃的模具 6、 高频发热圈 21、 温度传感器 8、 第一操作平台 31及驱动气缸 4， 其中， 所述模具 6设于所述第一操作平台 31， 所 述温度传感器 8用于检测所述模具 6的温度；
[0046] 所述驱动气缸 4驱动所述第一操作平台 31沿靠近所述高频发热圈 21方向运动至 第一指定位置；
[0047] 具体的， 所述第一驱动气缸 4驱动所述第一操作平台 31沿靠近所述第一高频发 热圈 211方向运动至第一指定位置；
[0048] 在第一指定吋间内所述高频发热圈 21将所述模具 6加热至第一指定温度， 其中
， 第一指定吋间的范围为 10至 70秒， 所述第一指定温度的范围为 350至 750摄氏 度；
[0049] 具体的， 在第一指定吋间内所述第一高频发热圈 211将所述模具 6加热至第一指 定温度；
[0050] 当所述温度传感器 8检测到所述模具 6的温度达到所述第一指定温度吋， 所述驱 动气缸 4驱动所述第一操作平台 31沿远离所述高频发热圈 21的方向运动至初始位 置；
[0051] 具体的， 所述第一驱动气缸 4驱动所述第一操作平台 31沿远离所述第一高频发 热圈 211的方向运动至初始位置；
[0052] 提供拨料机构 7及第二操作平台 33；
[0053] 所述第一操作平台 31运动至初始位置吋， 所述拨料机构 7将所述模具 6从所述第 一操作平台 31输送至所述第二操作平台 33；
[0054] 所述驱动气缸 4驱动所述第二操作平台 33沿靠近所述高频发热圈 21方向运动至 第二指定位置；
[0055] 具体的， 所述第二驱动气缸 43驱动所述第二操作平台 33沿靠近所述第二高频发 热圈 213方向运动至第二指定位置； [0056] 在第二指定吋间内所述高频发热圈 21将所述模具 6加热至第二指定温度， 其中 ， 所述第二指定吋间的范围为 10至 70秒， 所述第二指定温度的范围为 500至 850 摄氏度；
[0057] 具体的， 在第二指定吋间内所述第二高频发热圈 213将所述模具 6加热至第二指 定温度；
[0058] 当所述温度传感器 8检测到所述模具 6的温度达到所述第二指定温度吋， 所述驱 动气缸 4驱动所述第二操作平台 33沿远离所述高频发热圈 21方向运动至初始位置
[0059] 具体的， 所述第二驱动气缸 43驱动所述第二操作平台 33沿远离所述第二高频发 热圈 213方向运动至初始位置；
[0060] 关闭所述高频发热圈 21。
[0061] 本实施例中所述第一指定吋间为 30秒， 所述第一指定温度为 400摄氏度， 所述 第二指定吋间为 35秒， 所述第二指定温度为 550摄氏度。
[0062] 相比较于相关技术， 本发明提供的 3D玻璃成型方法有以下有益效果：
[0063] 所述 3D玻璃成型方法， 用于加工 3D薄片玻璃， 包括如下步骤：
[0064] 提供储存有待加工的所述 3D薄片玻璃的模具 6、 高频发热圈 21、 温度传感器 8、 第一操作平台 31及驱动气缸 4， 其中， 所述模具 6设于所述第一操作平台 31， 所 述温度传感器 8用于检测所述模具 6的温度；
[0065] 所述驱动气缸 4驱动所述第一操作平台 31沿靠近所述高频发热圈 21方向运动至 第一指定位置；
[0066] 在第一指定吋间内所述高频发热圈 21将所述模具 6加热至第一指定温度， 其中 ， 第一指定吋间的范围为 10至 70秒， 所述第一指定温度的范围为 350至 750摄氏 度；
[0067] 当所述温度传感器 8检测到所述模具 6的温度达到所述第一指定温度吋， 所述驱 动气缸 4驱动所述第一操作平台 31沿远离所述高频发热圈 21的方向运动至初始位 置；
[0068] 提供拨料机构 7及第二操作平台 33；
[0069] 所述第一操作平台 31运动至初始位置吋， 所述拨料机构 7将所述模具 6从所述第 一操作平台 31输送至所述第二操作平台 33；
[0070] 所述驱动气缸 4驱动所述第二操作平台 33沿靠近所述高频发热圈 21方向运动至 第二指定位置；
[0071] 在第二指定吋间内所述高频发热圈 21将所述模具 6加热至第二指定温度， 其中 ， 所述第二指定吋间的范围为 10至 70秒， 所述第二指定温度的范围为 500至 850 摄氏度；
[0072] 当所述温度传感器 8检测到所述模具 6的温度达到所述第二指定温度吋， 所述驱 动气缸 4驱动所述第二操作平台 33沿远离所述高频发热圈 21方向运动至初始位置
[0073] 关闭所述高频发热圈 21。
[0074] 与相关技术相比， 本发明提供的 3D玻璃成型方法通过高频加热与模具 6传热实 现加热效果好， 速度快， 通过一次预热和一次恒温， 重叠加热， 提高了加热功 效， 从而最大程度的提升了生产效率。
[0075] 以上所述仅为本发明的实施例， 并非因此限制本发明的专利范围， 凡是利用本 发明说明书及附图内容所作的等效结构或等效流程变换， 或直接或间接运用在 其它相关的技术领域， 均同理包括在本发明的专利保护范围内。

Claims

权利要求书
[权利要求 1] 一种 3D玻璃成型方法， 用于加工 3D薄片玻璃， 其特征于，
包括如下步骤：
提供储存有待加工的所述 3D薄片玻璃的模具、 高频发热圈、 温度传 感器、 第一操作平台及驱动气缸， 其中， 所述模具设于所述第一操作 平台， 所述温度传感器用于检测所述模具的温度； 所述驱动气缸驱动所述第一操作平台沿靠近所述高频发热圈方向运动 至第一指定位置；
在第一指定吋间内所述高频发热圈将所述模具加热至第一指定温度， 其中， 第一指定吋间的范围为 10至 70秒， 所述第一指定温度的范围为 350至 750摄氏度；
当所述温度传感器检测到所述模具的温度达到所述第一指定温度吋， 所述驱动气缸驱动所述第一操作平台沿远离所述高频发热圈的方向运 动至初始位置；
提供拨料机构及第二操作平台；
所述第一操作平台运动至初始位置吋， 所述拨料机构将所述模具从所 述第一操作平台输送至所述第二操作平台；
所述驱动气缸驱动所述第二操作平台沿靠近所述高频发热圈方向运动 至第二指定位置；
在第二指定吋间内所述高频发热圈将所述模具加热至第二指定温度， 其中， 所述第二指定吋间的范围为 10至 70秒， 所述第二指定温度的范 围为 500至 850摄氏度；
当所述温度传感器检测到所述模具的温度达到所述第二指定温度吋， 所述驱动气缸驱动所述第二操作平台沿远离所述高频发热圈方向运动 至初始位置；
关闭所述高频发热圈。
[权利要求 2] 根据权利要求 1所述的 3D玻璃成型方法， 其特征在于： 所述第一指定 吋间为 10至 70秒， 所述第一指定温度为 350至 750摄氏度。
[权利要求 3] 根据权利要求 2所述的 3D玻璃成型方法， 其特征在于： 所述第二指定 吋间为 10至 70秒， 所述第二指定温度为 500至 850摄氏度。
[权利要求 4] 根据权利要求 1所述的 3D玻璃成型方法， 其特征在于： 所述温度传感 器为红外线传感器。
PCT/CN2017/115788 2017-02-13 2017-12-13 3d玻璃成型方法 WO2018145513A1 (zh)