WO2018009645A1 - Methods and structures of electrochromic devices - Google Patents
Methods and structures of electrochromic devices Download PDFInfo
- Publication number
- WO2018009645A1 WO2018009645A1 PCT/US2017/040876 US2017040876W WO2018009645A1 WO 2018009645 A1 WO2018009645 A1 WO 2018009645A1 US 2017040876 W US2017040876 W US 2017040876W WO 2018009645 A1 WO2018009645 A1 WO 2018009645A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- electrochromic
- substrate
- coloration
- electrolyte
- Prior art date
Abstract
An integrated window structure having opposing substrates that sandwich an electrochromic coating, a dye layer and an ion-isolating mechanism. In some embodiments, this is a selective ion-conductive layer and other embodiments incorporate nanostructures and polymers to tether the dye ions; these methods prevent dye ions from transporting into the electrochromic layer during redox activity. Control and systems to integrate the electrochromic elements in windows is provided.
Description
Methods and Structures of Electrochromic Devices
Inventors: Anoop Agrawal, Lori Adams, John Cronin, Maha Achour, Woody Smith and
Jamal Alrawi
Field of the Invention
[0001] The present invention relates to electrochromic glass and devices, having ability to control the color and transparency of the glass, and specifically to electrochromic glass devices having inorganic and organic layers, incorporating dye and structures to improve performance.
Priority
[0002] The present application for patent hereby claims priority to, and
incorporates by reference in entirety, the following eight provisional applications:
• US Provisional Application No62/358,935, having attorney docket number
MA010PROV1 filed 07-06-2016, entitled "Low-cost and low-power
consuming electrochromic devices;"
• US Provisional Application No. 62/372,810, having attorney docket number
MA010PROV2, filed 8/10/2016, entitled "Low-cost and low-power
consuming electrochromic devices;"
• US Provisional Application No. 62/405,837, having attorney docket number
MA010PROV3, filed 10/7/2016, entitled "System and Network Integration of Smart Windows;"
• US Provisional Application No62/425,567, having attorney docket number
MA010PROV4, filed 11/22/2016, entitled "Low-cost and low-power consuming
electrochromic devices;"
• US Provisional Application No. 62/441,888, having attorney docket number
MA010PROV5, filed 1/3/2017, entitled "Low-cost and low-power consuming
electrochromic devices;"
• US Provisional Application No. 62/449,560, having attorney docket number MA010PROV6, filed 1/23/2017, entitled "Low-cost and low-power consuming
electrochromic devices;"
• US Provisional Application No. 62/501,607, having attorney docket number
MA010PROV7, filed 5/4/2017, entitled "Low-cost and low-power consuming
electrochromic devices;" and
• US Provisional Application No. 62/501,659, having attorney docket number
MA010PROV8, filed 5/4/2017, entitled "System and Network Integration of Smart
Windows."
Background of Invention
[0003] Electrochromic (EC) devices is based on the electrochromic characteristic of materials. When applied to glass, or other substrate, allow the color, opacity, and/or transparency of the substrate to change. Such devices are referred to as "smart glass" or "smart windows" as the characteristics of the glass, or other substrate, is changed by electronic switching. Used in buildings, these smart windows may provide shade, energy savings, privacy, partitions and so forth. The user may control the heat or light that passes through the glass using electronic switching, rather than shade, blinds or drapes. There is a great interest in the use of EC devices for energy saving; however, EC devices may be used for variable transmission windows, automotive mirrors for controlling reflectivity and displays.
[0004] Used in construction of buildings and in elements in transportation, these windows result in energy efficient building envelopes by regulating the solar energy penetration through the windows. For building glazing applications, wide acceptance will mean that the smart windows are available at an acceptable cost and that smart windows operate on low-power. Current EC designs incur costs due to the
installation of extensive wiring network throughout the building windows.
[0005] It is desirable to design such EC devices to reduce the power requirements, and thus the power consumption, using local power source(s) or generation device(s), such as a rechargeable battery circuitry or the use of small solar cells mounted on the window frames, respectively. The present invention provides methods and apparatuses for design, fabrication, installation and power supply for EC structures and devices that achieve these goals. A brief description of
conventional EC devices is provided in the section entitled "Conventional
Construction Methods and Configurations," as several of the materials and
compositions may be used in the present invention.
Brief Description of Figures
[0006] Figure 1 illustrates an EC panel for use in a smart window Integrated Glass
Unit (IGU) and color transitions, according to embodiments of the present invention, including a side-view of the smart window 1.
[0007] Figures 2 and 3 illustrate electrochromic (EC) devices in IGUs, according to embodiments of the present invention.
[0008] Figure 4 illustrates a circuit equivalents of an EC device as in Figure 3,
according to embodiments of the present invention;
[0009] Figures 5 and 6 illustrate EC device constructions incorporating a lamination of a multilayer electrolyte film according to embodiments of the present invention;
[00010] Figure 7 illustrates operation of an EC device and system to according to embodiments of the present invention;
[00011] Figures 8 and 9 illustrate smart window IGUs in various configuration and their reaction to incident light according to embodiments of the present invention.
[00012] Figures 10 illustrates a smart window system in a multistoried building structure with glass exterior and having an integrated solar energy solution of a solar-cell power source and power storage recharging circuits, according to embodiments of the present invention.
[00013] Figures 11-13 illustrate an Integrated Glass Unit (IGU) configuration of an
EC window according to embodiments of the present invention.
[00014] Figure 14 illustrates operation of a smart window system in a building
according to embodiments of the present invention;
[00015] Figure 15 illustrates operation of a smart window system according to
embodiments of the present invention;
[00016] Figure 16 Illustrates a control system for window system according to
embodiments of the present invention;
[00017] Figure 17 Shows experimental data on voltage, coloration and charge
consumption of an EC element produced by an embodiment of the present invention;
[00018] Figure 18 illustrates spectral characteristics of soda-lime glass substrates coated with transparent conductors corresponding to an embodiment of the present invention.
[00019] Figure 19 illustrates an EC device having a multilayer film with an
electrolyte and dye containing layer (ferrocene-containing layer) prior to lamination together with substrates according to embodiments of the present invention.
Detailed Description
[00020] An object of this invention is to teach Electrochromic devices for glazing which are durable, have low power consumption and can be fabricated at lower cost by electing specific device construction selection of certain substrates, materials in coatings and in electrolytes so that the devices can be fabricated at a lower cost.
[00021] Another objective of the invention is to lower the fabrication cost of the EC devices by eliminating procedures requiring pre-reduction of coatings and lowering the number of coatings and their thicknesses.
[00022] Yet another objective of the invention is to disclose electronic control and powering systems which lend to a low-cost installation of the EC windows.
[00023] Further objective is construction of an Integrated Glass Unit (IGU) unit with an EC unit and integration of such units with photovoltaic units.
[00024] Even further objective is to disclose powering schemes of EC panels and being able to remotely detect if these require maintenance.
EC device Construction
[00025] For architectural use, windows used in building envelops, not for interior partitions, the EC devices or panels are typically incorporated in windows using integrated glass unit (IGU) type of construction. The structure positions two structures approximately parallel to each other, in a smart window application one of these may be an EC panel and another being a glass panel with optional coatings. The EC panel or EC glass of some embodiments of this invention is formed by taking two transparent substrates such as glass and coating these. For windows, the coatings on each substrate are electronically conductive and transparent
(transparent conductors, TCs). There may be optional coatings deposited on these
TCs, on one or both substrates. With the substrates positioned in largely a parallel configuration and the coatings facing each other, an electrolyte is sandwiched (or formed, or injected) between the coated substrates and the perimeter is sealed. A coloration potential is applied between the conducting portions of the substrate coatings. Application of the coloration potential alters the color of at least one of the coatings and/or the electrolyte.
[00026] Figure 1 illustrates color transitions of a prior art smart window 1 having electrochromic glass; the smart glass transitions between bleached/transparent and colored/opaque. A side-view of smart window 1 is illustrated in Figure 1, having a multi-layer structure, wherein a smart window may have any number of layers, including sacrificial layers that exist during fabrication but do not remain in the final product. Please note that Figure 1 illustrates a prior art EC smart panel for use in a building envelop and will be part of an IGU configuration of a complete window system 1. The primary electrode 4 is an EC material that enables electronic control of the coloration of the window system 1. Figure 1 illustrates an exemplary configuration of prior art smart window constructions; there are a variety of current solutions and configurations, and for sake of clarity, the EC smart panel 9 of smart window 1 is illustrated in isolation. Other components are not shown, such as a configuration having opposite substrates, incorporating an EC smart portion, and having a small gap therebetween to form an IGU unit.
[00027] As illustrated in Figure 1, a side-view of EC smart panel 9 of smart window 1 is configured with two opposing substrates 2, 8, having layers therebetween. For a window application, the substrates 2, 8 are transparent. In the illustrated example, both substrates 2, 8 have a Transparent Conductive (TC) layer 3, 7, respectively. Other layers include layers 4,6, which provide primary and counter electrodes,
respectively. Between the electrodes 4, 6, is an ion-conducting material, which in this configuration is electrolyte 5. When electrodes 4, 6, are being reduced or oxidized, such as when the window is being colored or bleached, the potential difference causes lithium ions (Li+) move into the primary electrode 4, and out of counter electrode 6. In this example, a primary electrode 4 is formed by an electrochromic (EC) material; and a counter electrode 6 is also formed by an EC material, wherein the EC material of the counter electrode 6 has complementary redox properties to those of the primary electrode 4.
[00028] Complementary redox properties wherein the counter electrode is also electrochromic means that the counter electrode 6 will also color (e.g. will oxidize) under the applied coloration potential while the primary electrode 4 also colors (by reduction).
[00029] Construction of the smart window 1 is detailed below as Example 1 of the Conventional Construction Methods and Configurations. The process involves various steps to build the illustrated EC device. The configuration of smart window 1 includes the counter electrode 6, wherein the primary EC electrode 4 is cathodic and operates to color the smart window 1 by reduction. In operation, the coloration of smart window 1 is produced by redox activity, where a voltage is applied between two electronically conducting layers electrodes, 3, 7. The voltage applied to conductive layer 3 results in the reduction of the material in electrode 4 by an injection of ions from the layer 3 which travel via the electrolyte layer. This causes the EC device (or the window) to color or darken.
[00030] This oxidation occurs by removal of ions from layer 6 into the electrolyte layer 5 and transported to the other side of the structure with expulsion of electrons through the TC layer 7. The oxidation of material in layer 6 may also cause this layer
to color such that simultaneous coloration is seen from both the EC layer 4 and the counter electrode 6. In some cases, the optical change in the counter electrode is low, wherein most of the coloration is from the EC layer. The former situation effecting coloration of both EC layer 4 and counter electrode 6 is a more effective configuration, as the same amount of charge colors both layers (colors or bleaches) simultaneously, resulting in faster kinetics and deeper coloration. There are several optical configurations to achieve varying levels of darkening or coloration of smart window 1, each requiring a different maximum voltage and/or range of voltages. In some embodiments, the voltage application is continuously applied to maintain the desired optical state. Operation of such configurations consumes significant power to achieve window coloration control.
031] There are several differences in composition, structure, manufacture and performance of EC devices and their use in smart windows. These differences in performance are often due to selection of specific layers and the specific
configuration used, as well as proximity within the smart windows. The method of fabrication may incorporate custom processes and machines, or may incorporate sensitive conditions for operation. These differences affect the electrochromic reaction and resultant behavior of the smart window. Several of these are described hereinbelow in the Conventional Construction Methods. This section is provided to facilitate understanding of the various methods, configurations, components, chemicals, processes and operations of smart devices and their use in IGUs. These constructions are typically used to fabricate electrochromic panels or devices;
however, there are drawbacks to conventional methods. Many of these incorporate specific processing equipment and methods that incur additional cost. For example, some smart devices incorporate reduction of at least one layer, such as the EC layer,
the counter electrode, or an auxiliary electrode, during fabrication. This is an expensive process and is more readily subject to variation in results and performance of the smart device. During the reduction process a fixed number of ions are inserted which are expected to reversibly shuttle back and forth between the EC layer and the counter electrode layer during coloration and bleach of the finished device. Often, reduction processes incorporate lengthy processing times for chemical reactions to treat the films and components and then cleaning any surface residues. Further, there may be a need to fabricate the device within an inert environment, else the results and yield are not consistent and stable. Such tight parameters may incorporate complex machinery and an esoteric fabrication set up, thus reducing the flexibility of design and increasing the difficulty of fabrication. This is further complicated when different sizes and shapes of windows are specified for a project.
[00032] Once these devices are fabricated, a next step may be to cycle, or exercise, the devices between states, such as between a bleached state and a deeply colored state; this ensures that there will be ion movement during actual operation; this ensures that the inserted ions are not permanently bound within these layers where they were first inserted and thus available when the devices are powered during use. This incorporates additional steps, space, equipment, and so forth, and increases fabrication costs.
[00033] Further, some devices must be cycled, otherwise the ions are routinely permanently bound or trapped within the layers of the EC device. This may occur, for example, while the devices are stored for long periods prior to installation or even if after the installation the building is unoccupied and the devices are left or
maintained in one state.
[00034] Additionally, conventional EC devices also offer a challenge in meeting UV, thermal and cycling durability. UV durability refers to being exposed to the UV radiation (in bleached or in colored states, or while transitioning from one state to the other) and still being able to cycle between various coloration states, for example from a color state to a bleached state and back consistently and within acceptable kinetics. Thermal and the cycling durability also means that after the devices are subjected to elevated temperature (including thermal shock) and repeated cyclability that their characteristics of coloration and bleaching are still acceptable. Since the EC electrode and the counter electrode are made of different materials with inherently different aging characteristics (such as aging due to repeated cycling), temperature and light (such as in response to UV), it is difficult to maintain their pristine state with time, and/or to ensure that both layers will change at the same rate when aged, and/or that the fixed number of ions inserted during the manufacturing process are not lost due to any undesirable reactions. In practice, these problems occur, and the loss of ions causes faster failure, such as failure in terms of the device's ability to color to the same level and/or to bleach to the same level with aging. This is often overcome with expensive electronic designs so that the devices can be continuously monitored for their electrical characteristics so that the driving conditions (voltage, time, current, and so forth) can be continuously changed.
[00035] These shortcomings are overcome in the devices being taught in the
current disclosure. Material selection for devices being taught in this invention is also a significant design step; the electrochemical or the ionic capacity of the electrode and the counter electrode does not have to be precisely coordinated with each other, and in this way, provides flexibility in design. There may be no pre-reduction of layers incorporated during fabrication and the device is not exercised, such as to
transition from color to bleach several times, after manufacture or in some embodiments and applications, even during use, if the device is not operated for long periods of time. In addition, some of the layers where the redox activity takes place are incorporated into the electrolytic layer so as not to incur the expense of a substrate coating and to further simplify manufacturing. For example, as discussed herein below, hydrophobic ionic liquids may be used in the electrolyte of an EC device. The desirable Ionic liquids for example, have a high electrochemical stability range and low ultraviolet (UV) susceptibility; and these are insensitive to moisture absorption and provide high inertness. These characteristics lead to more durable EC devices.
Embodiments of the Present Invention
[00036] The present invention provides methods and apparatuses of EC devices for use in glazing applications, such as architectural and transportation, where the EC devices reversibly cycle between various optical states. The optical states are various desired levels of darkening and lightening of a window; in some applications, the native state is the clear or the bleached state.
[00037] There are a variety of ways to specify a smart window, including the various energy spectrums from the sun. Electromagnetic energy from the sun is broken into a variety of categories based on the wavelength of the energy, and includes ultraviolet, UV, visible light, VL, and near-infrared, NIR, energy. The present invention provides methods and apparatuses for providing control of privacy but also control of the building environments and conditions. UV and NIR energy are not visible to the human eye, but influence the conditions under which the smart window is to operate. The smart window may be specified as to how the window
responds to various measures of these energies from the sun, and over what range of energy values the window has stable performance.
[00038] Much energy is filtered or reflected by the earth's atmosphere and does not reach the smart window. Some UV energy is rejected by conventional double- pane glass windows. Some UV energy may be blocked by films or coatings that reflect or absorb the energy. There are many benefits to this beyond those enumerated hereinabove, including the ability to reduce or prevent fading and deterioration of furniture, art work, wall paint, fabric and so forth. The measure of the UV transmission is the percentage of UV light or energy that will pass through a window, glass, !GU, or in this case, a smart window.
[00039] VL is the portion of the sun's spectrum that human eyes can see, and includes natural daylight and rainbow colors. For privacy, the smart window is specified to reduce the amount of VL passing through the window. Reducing VL reduces glare and eye strain. Control of VL enables a building or home to have natural light enhancing the environment and reducing the cost of lighting. A window in a darker or colored optical state will have lower LV transmission value.
[00040] Solar radiation from NIR energy is not visible to the human eye; however, we do feel the heat. When NIR energy hits a window surface, it can transmit through the glass pane, or substrate, and increase the temperature inside a building. Embodiments of the present invention enable control of the amount of NIR that passes into the building by decreasing the infrared transmission. This is referred to as the infrared transmission value, and is particularly important in summer months and hot climates. Similarly, the control is desired to capture that heat during winter months and in cold climates. The present invention thus improves the comfort of those inside the building while reducing carbon emissions and costs of air
conditioning, cooling and heating. The ability of a smart window to control the infrared transmission value is related to the Solar Heat Gain Coefficient (SHGC) of the window.
[00041] The EC devices and smart windows of the present invention may also be kept in any of the colored states over time without application of continuous power, wherein this ability is referred to as having "memory" as the device holds its optical state with no, or in some cases, low, current consumption. The "memory length" is the time that an EC device will maintain its optical state and may be temperature dependent, for example, where the memory length decreases inversely with temperatures.
[00042] Characterization of the memory of an EC device considers the transmission percentage, the change in transmission percentage over time and under a range of temperature conditions. Typically, a good measure to characterize this is photopic transmission or transmission at 550nm.
[00043] As an example, the memory of an EC smart window device is considered stable when the memory maintains a transmission range of 2% in a colored state at a 550nm wavelength. This is based on the photopic eye response, at a given
temperature. The memory length is the time during which the memory maintains the 2% transmission range. In this example, application of power to an EC device 40, such as the device illustrated in Figure 3, causes the device to color (darken) resulting in 10% light transmission through the window. At the 2% transmission range, the EC device is specified as not allowing more than 12% light transmission for the memory length, tj. The window will not bleach such that it would exceed 12% light
transmission over a specific time period at a given temperature. In the example, the temperature for the memory specification is given as 25±3°C and the time period is
specified as 30±2 minutes. Thus, a device which is colored to 10% and then its power is removed, will continue to stay colored to 12% or lower at the above temperature and time. Similarly, a device colored to 5% upon removal of power will stay colored to 7% or less under similar temperature and temporal conditions. Since the devices color in a broad spectral range, the above example transmission values correspond to the pea k of photopic eye response at 550nm.
[00044] In some embodiments, the EC device has a controller that responds to the memory length, such as by a timer or electrical input or an optical input or a combination of any of these, and will activate sufficient electricity to renew the electro-chemical reaction within the EC device and restore or maintain the specified memory length for the transmission range. In this way, the EC smart window maintains a coloration state without disruption. The materials used and the configuration of the EC device determine the transmission range(s) and
corresponding memory length.
[00045] In some embodiments, the EC device has a controller that responds to the memory length, such as by a timer or electrical input or an optical input or a combination of any of these, and will activate sufficient electricity to renew the electro-chemical reaction within the EC device and restore or maintain the specified memory length for the transmission range. In this way, the EC smart window maintains a coloration state without disruption. The materials used and the configuration of the EC device determine the transmission range(s) and
corresponding memory length(s).
[00046] The present invention provides embodiments of an EC device for use in glazing applications that allow smart windows to reversibly cycle between various optical state, also referred to as coloration states such as darkening of a window and
changes in transparency. These are applicable in architectural building, such as multi-story and multi-use buildings, transportation, such as airplane windows and vehicle windows, manufacturing, such as production of light-sensitive or energy- sensitive products, and so forth. In some applications, it is desired that the default state of these devices is the clear or the bleached state; however, the original or default state is determined by the type of device and the desired application.
[00047] Further, these may also be kept in any of the colored states over time without continuous application of power. This ability to hold a coloration state, and in some embodiments, to return to a default state, is referred to as having "memory." An EC device having memory consumes little-to-no power in a coloration state. The memory may also allow the EC device to transition to a default state by removing a voltage potential between layers of the EC device, such as to short layers, or electrodes, together. This may be done mechanically without electrical input, or may be implemented electronically. The memory length may be temperature dependent, such as where the memory length reduces with increasing temperatures. Characterization of a device considers the temperature and time duration under which the smart window is to operate and the conditions that would impact such operation and ability to maintain the specified memory length. For example, in some embodiments of the present invention, memory of an EC device is specified to be less than a percentage change in light transmission for a specific time at a given temperature.
[00048] In one example, stability of an EC device is specified for various memory characteristics. The EC light transmission range of no more than 2% in light transmission at 550nm or based on photopic eye response. This specification also defines a given temperature over a given time period. For example, an EC device
colored by applying power to a darker state to a transmission of 10%, will not change or bleach more than 12% transmission under a specific time period at a given temperature. This temperature for such memory definition is selected as 25±3°C and the time period is selected as 30+2 minutes. Thus, a device which is colored to 10% and then its power is removed, will continue to stay colored to 12% or lower at the above temperature and time. Similarly, a device colored to 5% upon removal of power will stay colored to 7% or less under similar temperature and temporal conditions. Since the devices color in a broad spectral range, the transmission ranges may correspond to the peak of photopic eye response, e.g., at 550nm.
[00049] These embodiments may incorporate UV light stabilizers to ensure a dependable, sturdy EC device having consistent, predictable operation. These and other aspects of the present inventions improve the performance of smart windows and EC devices for a variety of applications while providing streamlined processing and fabrication.
[00050] In some embodiments of the present invention, EC devices incorporate an inorganic EC layer and a redox dye containing layer, wherein the redox dye is isolated from the EC layer. During operation, the dye ions are reduced or oxidized, and the EC layer is oxidized or reduced, respectively. The dye in the reduced or the oxidized state is prevented from contacting the EC layer. The redox dye may also have complimentary EC properties, wherein they dye ions color or bleach as the EC layer colors or bleaches. In some configurations, the dye molecules are immobilized within a layer in the EC device.
[00051] In another configuration, a multilayer film is formed comprising at least one dye containing layer and an electrolyte layer. This multilayer film having an electrolytic layer and a dye containing layer film is sandwiched between a pair of
coated substrates. The dye-containing layer also has ion-conducting properties. In one configuration, one of the substrates has an EC layer deposited on one of the substrates which has a pre-deposited transparent conductor coating and the second substrate has a transparent conductor coating. The multilayer film is then assembled between these substrates.
[00052] These and other embodiments of the present inventions isolate redox dye, or the reduced or oxidized ions, from the EC layer such that they do not interact with the opposing electrode. This isolation is implemented with a redox isolation mechanism, wherein oxidized (or reduced) dye ions are separated from the reduced (or oxidized) EC layers, and thereby maintains the coloration state achieved by redox activity without continuing to apply the electrical potential to maintain this coloration or optical state.
[00053] This redox isolation may also be maintained by incorporating an additional layer coated over the EC layer, for those cases where the dye ions are not chemically tethered in the dye layer and may move into the electrolytic layer. This overcoat will allow small ions such as lithium to pass through and reduce the EC layer, but block the larger dye ions to penetrate. Since this layer blocks the larger dye ions and allow the transportation of small ions, this is called a selective ion conduction layer (SICL). Further, in these example embodiments, the small ions are generated in the dye layer only to the extent accommodated in the opposing electrode (EC layer). For some embodiments, this obviates the process of matching capacities of the two electrodes during manufacturing. The dye containing layer is designed to have a very high capacity compared to the opposing EC electrode coating, such as by a factor of two or more, and in another embodiment by a factor of about 5 or more. This means that one of the electrochemically active layers, or layers where the redox
activity takes place, has a higher capacity of reduction or oxidation sites as compared to the other layer. The ability to trigger the redox reactions, such as with an applied voltage, and to maintain isolation of the dye ions, results in a stable state of coloration without continuous voltage. In one embodiment, an EC device configuration incorporates an inorganic EC layer and a dye containing layer; the capacity of the dye containing layer is higher as compared to the inorganic EC layer.
[00054] To reverse the coloration state, the redox ions are allowed to return to their original respective states by either electronically shorting the two opposing electrodes (the leads connecting the two TC layers) and/or applying a reverse potential.
[00055] In some embodiments incorporating dye ions as oxidizing coloration agents and an EC layer as inorganic cathodic electrode, the redox isolation mechanism may be a layer that keeps the dye ions isolated from the EC layer. Alternatively, the dye is tethered within the dye layer. The dye may be tethered in the dye layer in at least one of two ways. The dye may be reacted or bound to the polymer which is used to make the matrix of this layer; or the dye is bound to a larger additive present in this layer which has no or low mobility. An additive to the ion-conducting dye layer is designed to be electronically conductive, having larger particles than the dye molecules. In some embodiments, these additives have at least one dimension in the nano-sized range to keep light scattering low and allow good visibility. The isolation of the dye ions, or restriction from coming into contact with opposing electrode, maintains the coloration state without the continuous application of voltage to the device. In some embodiments, a redox isolation mechanism effectively prevents movement of oxidized ions from contacting reduced layers, to prevent reversion of ions to their original state.
[00056] As described herein, the redox action oxidizes dye and reduces EC layer resulting in color transition of the EC device. In some applications, the EC device's original or ambient state is transparent or bleached, wherein a voltage applied across the electrodes triggers a redox reaction that causes the EC device to color or darken. Without the redox isolation mechanism, the oxidized and the reduced species would come in contact with each other, the species react, and return to their original states. Where the original state is clear, this will bleach the device. An isolation scheme keeps these species apart without continuous application of voltage and power, will be incorporated to keep the device in the colored state.
[00057] In some embodiments, a smart EC window reduces the power consumption of the device. The isolation mechanism(s) enable the device to maintain a separation between the redox species and maintain the coloration state without continuous voltage application. The redox isolation mechanism(s) effectively prevents the dye ions from coming into contact with the reduced EC layer. In these embodiments, when the voltage may be removed once the device is colored without bleaching the EC device. The redox isolation mechanism prevents transport of dye ions transporting in contacting the cathodic EC layer. The redox isolation mechanism may include an SICL, a mechanism to tether dye ions from moving into the electrolyte layer, and other layers/mechanisms to keep separation.
[00058] Some embodiments of the present invention provide elegant solutions to reduce the complexity of prior art solutions, and provide streamlined stable methods of fabrication. These include different configurations, as well as different methods for fabricating these devices. Further the present invention incorporates ways to further enhance the use of smart windows to capture energy, reduce build time, enable off-site build with minimal on-site modification of process, and couple the
smart window technology with other energy saving techniques, including solar energy.
[00059] The present invention describes EC devices where an electrolyte is sandwiched between two conductive, largely parallel substrates. The substrates, which are generally non-conductive, are coated or pre-coated with a transparent conductive material on the inward facing surfaces. For windows, both the substrates and the coatings are transparent (at least to the eye). There are many material combinations that may be used, such as the TC layers may be composed of indium tin oxide, fluorine doped tin oxide, and so forth.
[00060] An example embodiment is illustrated in Figure 2, wherein the redox isolation mechanism includes nanostructures 16 and dye molecules 18 within a dye- conducting layer 22, wherein at least some of the dye molecules 18 tether to nanostructures 15. The ion-conducting layer 14, or electrolyte layer, is proximate the dye containing layer 22 and includes dissociable salts (e.g., lithium salts), which is are shown as Lithium ions, Li+. The dissociable salts are also present in the layer 22. The nanostructures 16 may be nanotubes, nanorods, nanodiscs, nanoparticles and so forth. The illustrated examples of Figures 2-3, have the electrolyte layer 14 separate from the dye containing layer 22 for clarity, but these may take a variety of forms, wherein the Li+ ions are able to travel between across the electrolyte layer 14. Proximate the electrolyte layer 14, and opposite the dye containing layer 22, is an EC layer 13, which may act as a primary electrode and is referred to as a cathodic EC layer. The TC layer 19 along with the layer 22 acts as a counter electrode to the cathodic EC layer 13 in contact with TC 12 through power source 24.
[00061] In some embodiments, the cathodic EC layer 13 includes tungsten oxide, wherein, as used in this disclosure, tungsten oxide is generally written as WOx
without a fixed W:0 stoichiometry, and includes doped tungsten oxide, such as is doped with one or more other metal oxides. The tungsten oxide material is coated on top of a transparent conducting layer, TC layer 12, on a substrate 11.
[00062] In some embodiments, in EC device 10, dye molecules 18 are present in electrolyte layer 14, as well as dye containing layer 22, wherein electrolyte layer 14 and dye-containing layer 22 meet the TC layer 19 coated on substrate 20. At the interface of electrolyte layer 14 and TC layer 19, the oxidized dye ions 18 are prevented from reaching the tungsten oxide layer by the nanostructures 16 as the dye molecules may be tethered within this layer, while the small ions, such as lithium, go through the electrolyte layer 14 to the cathodic layer 13 on application of a coloration potential.
[00063] The power transitions the color of the EC device, and the SICL and/or tethering of the dye molecules within the layer holds the color, and there is no-to- little back reaction. The absence of the back-reaction has another benefit for large area devices, such as windows compared to small displays and rear-view EC car mirrors. As the EC device coloration increases, the charge consumed in the colored area decreases (or current decreases) and the large areas attain a uniform coloration. The power is supplied to the EC device by way of a bus bar electrical connection. The large area coloration is possible as there is no-to-little voltage drop from a bus bar area at a perimeter to the center of the device.
[00064] Figures 2 and 3 illustrate EC devices 10, 40, according to the present inventions. Figure 2 illustrates some embodiments of an EC device 10 for use in a smart window, where opposing substrates 11, 20, each have a transparent conductive (TC) portion, TC layer 12, 19, respectively. The TC layer 12 may be a coating that is applied to a substrate 11. On one side of the EC device 10, a cathodic
EC layer 13 is configured proximate TC layer 12. The cathodic EC layer 13 is proximate the electrolyte layer (or ion conducting layer) 14, and another dye containing layer 22 (this layer also has ion-conducting properties). The layer 22 includes redox dye molecules 18, metal salt (such as lithium salt) 17 and nanostructures 16. The cathodic EC layer 13 in communication with TC 12 acts as a cathode for EC device 10, and the layer 22 in communication with the TC 19 act as an anode for EC device 10. The electrolyte layer 22 also contains lithium salts. There is a power source 24 coupled to the EC device 10 between cathodic EC layer 13 (or optionally TC 12) on the substrate 11 and the TC layer 19 on substrate 20. In this configuration, cathodic EC layer 13 along with TC layer 12 is the primary electrode and TC 19 along with the dye-containing layer 22 is the counter electrode. The power supply 24 provides energy for the redox activities that transition the coloration of the device 10.
065] The nanostructures 16 are illustrated as tubes, but may take any of a variety of shapes sufficient to achieve the purposes of the application. The nanoparticles are designed to be electronically conductive. Nanoparticles are defined as those particles which have at least one dimension (width, thickness, height, diameter) less than lOOnm, further these can have any shape, spherical, ellipsoidal, cubical, cuboids, tubular, rods, discs, and so forth. In addition, these conductive particles are percolated, which means they form a conductive network throughout this layer. Thus, dye-containing layer 22 has both electrolytic properties (ion- conductive properties) and electronically conductive properties. Therefore, the redox dye molecules in layer 22 may be oxidized throughout the bulk of this layer without having them transported onto the surface of the TC 12. Even further, in another embodiment the redox dye molecules may be fixed or tethered in layer 22
either within the matrix or on the surface of the conductive nanoparticles. In this way, the oxidized ions do not move and do not enter the electrolytic layer 14; and they do not travel toward the EC layer 13, which isolates the oxidized ions from getting close and/or touching the EC layer 13. This arrangement enhances the kinetics of the device as the large ions do not have to move through the layers. Further, this arrangement stops a back-reaction that could lead to self-bleaching. In addition, in one embodiment the EC layer 13 is made of an EC material, such as tungsten oxide described above. For low-haze and clear optical properties suitable for windows, it is not desirable for the EC layer to have particles of inorganic materials such as tungsten oxide disposed in an organic ion conductive matrix along with conductive nanoparticles. In this way, the EC layer 13 is different from the dye containing layer 22. This is because the EC particles are larger in size than the dye molecules and it is difficult to form transparent coatings with high loading in a polymeric (ion-conductive) binder. Further, most inorganic EC materials have a high refractive index as compared to the ion-conductive binder, and will lead to excessive light scattering or haziness for use in a window application. Thus layer 13 essentially comprises only a particle free composition (organic or inorganic), such as a clear (with haze less than 0.5%) coating of tungsten oxide or doped tungsten oxide (doped with mainly with other metal oxides) when cathodic EC layers are desired.
066] Fabrication of EC device 10 involves configuring the layers in the desired proportions and positions to enable control based on environmental conditions or in response to user control. As illustrated in Figure 2, the configuration of layers for an EC device 10 is designed for use in a smart window, and the substrates 11, 20 are transparent, such as glass (e.g., soda-lime glass), plastic (e.g., polyester, polycarbonate, acrylic, fluoropolymer), or other transparent material. The EC device
10 of Figure 2 creates opposing electrodes with two coated substrates and then assembles these with an electrolyte sandwiched between them. The process used to build the EC device 10 starts with a first substrate 11 and forms or places TC 12 on the substrate 11, wherein TC 12 is capable to conduct an electric charge. The two substrates 11, 20 are may be pre-coated with TC materials. The surface 12 is further coated with the EC layer 13. The combination of substrate 11 and TC layer 12 in collaboration with the EC layer 13 forms the first electrode. Similarly, the combination of substrate 20 and TC layer 19 forms the foundation of the second electrode. In one embodiment, layer 22 may be coated on TC 19 and then the two are assembled using the electrolyte 14. Electrolyte 14 may be a polymer containing solid. In another embodiment, a multi-layered solid film comprising of layers 22 and 14 which is then laminated between the two coated substrates, for example, substrate 11 coated with layer 12 and layer 13; the substrate 20 is coated with layer 19. The electrodes oppose each other and coloration potential may be applied across the electrodes to initiate coloring of EC layer 13 and thus color the window 10. During the coloring operation, in one embodiment which uses a cathodic EC layer 13, the dye ions 18 oxidize and lithium (or other small ions) are released to travel through the electrolyte layer 14 into the cathodic EC layer 13. The electrons from TC layer 19 travels through the external circuit to cathodic EC layer 13, which reduces and colors the EC layer 13.
067] The embodiments illustrated in Figure 3 include a redox isolation mechanism, which may be incorporated into the device 10 of Figure 2, or may be used without the nanostructures 16. The combination of the two redox isolation layers enhance performance and improve the EC memory of a device. In the illustrated example, EC device 40, the redox isolation mechanism is SICL 36 as a
redox isolation layer that filters out larger ions and allows the smaller ions to pass. SICL 36 is formed on, or positioned proximate, EC layer 34, which is a material that will allow the transport of lithium ions, or other small cations, such as protons, sodium, potassium. The SICL 36 acts as a filter to enable specific ions to transfer but prevent other ions from passing. The lithium cations (Li+) 52 are relatively small compared to the dye cations 54 formed by the oxidation of the dye in the electrolyte. The SICL 36 allows the Li* ions to pass through to EC layer 34, these are intercalated with the EC layer 34 for coloration; the SICL 36 blocks the oxidized dye cations 54. In this example, the dye ions 54 are tethered to the nanostructures 50 in the dye- containing layer 59; however, in applications without this dye-tethering mechanism (e.g. nanostructures), SICL 36 acts to separate the cathodic EC layer 34 from the electrolyte layer 38. This separation enhances performance of the EC device in another unique way by enhancing its durability, as when a semiconductor material is use in EC layer 34. In some examples described herein EC layer 34 incorporates tungsten oxide, which is a semiconductor. When the semiconductor contacts an organic electrolyte in presence of solar radiation, there may be charged species generated in the semiconducting layer and promote an irreversible reaction therebetween. In such a device, this irreversible reaction would occur at the interface of electrolyte layer 38 and EC layer 34 when no SICL is present. When subjected to solar radiation, these devices have a potential to decrease the EC device lifetime. Thus, an inorganic SICL layer which is not a semiconductor will prevent direct interactions between the electrolyte layer 38 and the semiconducting EC layer 34. This means that the charged species generated in the semiconductor are quenched in the SICL layer and do not reach the organic electrolytic layer.
[00068] Continuing with Figure 3, embodiments of the present invention further incorporate reduction and oxidation agents such as a dye material in the dye- containing layer 59 proximate electrolyte layer 38 and the EC layer 34 which acts as a cathode. The EC material reversibly colors when oxidized (or reduced depending on materials and configuration) by an electric stimulus, such as a voltage applied to the electrode formed by EC layer 34 and/or TC layer 32. The dye molecules 54 provide a balancing reaction and create the other electrode in combination with TC layer 56. The dye-containing layer 59 may also have complimentary coloration properties to those of the EC layer 34. In some examples, the cathodic EC layer 34 uses a tungsten oxide-containing layer, while the dye molecules 54 are designed to possess anodic properties and they color on oxidation.
[00069] Anodic and cathodic dye compounds for EC devices of the types illustrated in Figures 1, 2 and 3 may be chosen from various candidate materials to achieve complementary relationships. In other words, coloration is enhanced when material at one electrode colors on reduction, while a material at the opposite electrode colors on oxidation. Examples of anodic dyes include compounds with pyrazoline, metallocene, phenylenediamine, benzidine, phenoxadine, phenothiazine, tetrafulvalene and phenazine; and cathodic compounds that comprise viologen and anthraquinones.
[00070] These EC devices may be fabricated by positioning opposing substrates with a gap therebetween; the gap is later filled with an electrolyte. The substrates may have layers developed thereon such that one substrate has layers forming a cathode and the other substrate has layers forming an anode. In some embodiments, the layers are built up on each substrate, including the electrolyte layer, and then they are laminated together. In still other embodiments, the layers are built on a
substrate, wherein during assembly an electrolyte is sandwiched between the two substrates, wherein the substrates may have multiple layers as described herein.
[00071] The cathodic EC layer 13, 34 is formed of a material that will act as a cathode into which ions are injected from the electrolyte layer 14, 38 when a coloration potential is applied across by the electrodes via coloration potential source 24, 26. The magnitude of the coloration potential applied across the electrodes (cathode to anode) determines the amount of dye molecules oxidized as well as the resulting Li+ ions transported via the electrolyte layer 14, 38 and injected into the EC layer 13, 34. Further, in EC device 40, the magnitude of the coloration potential applied at potential source 26 determines the amount of ions created and then transported through the SICL layer 36. Similarly, the coloration potential source 24, 26 controls the level of coloration in EC device 10, 40. The redox dye molecules 18, 54 are expressed as filled circles (·) in Figures 2 and 3. The lithium salt in electrolyte layer 14, 38 and dye-containing layer 22, 59 is expressed as Li+A", where A" is the anion of the lithium salt, for simplicity the figure only shows lithium ions as "+" although the salt is present along with its anions. Assuming the EC material is tungsten oxide (WOx). One may express the coloration reactions in the various layers as follows, the symbol <→ shows that the reactions reverse when the device is bleached, e" stands for an electron:
In layer 22, 59: yD +y Li+A" <→· yD+A' (oxidized dye anion) +yLi+ + ye' (1)
In Layer 13, 34: WOx (bleached) + yLi+ + ye" LiyWOx (colored) (2)
[00072] Reaction 1 above is the oxidation reaction for the dye, as in dye-containing layer 59 if Figure 2. Reaction 2 is the reduction reaction, as in the EC layer 34 of Figure 3. The Li+ ions are transported via electrolyte layer 38 and SICL 36 into
tungsten oxide, wherein the electron is transferred into the tungsten oxide- containing layer 34 via the external electrical circuit. The oxidized dye anions may also change to a more colored state.
[00073] In some embodiments, a substrate configuration is assembled with
substrates are spaced apart, forming an empty cavity therebetween that is enclosed with a perimeter sealant (not shown). An electrolyte material is then introduced in this cavity, such as through a hole in the sealant or the substrate which is later sealed. Alternatively, an electrolytic sheet is laminated between the two coated substrates and then the perimeter is sealed.
[00074] In operation, application of a coloration potential across the electrodes (cathode to anode) will act to color the EC device when the cathode is connected to the negative terminal. From the colored state, reversing the polarity or short circuiting the electrodes together will bleach the EC device. It is noted that the maximum potential to color may be very different from the maximum bleach potential when the polarity is reversed.
[00075] In some embodiments, once the EC device achieves a desired coloration state, whether colored, bleached or partially colored, the voltage applied to the electrodes may be opened and the EC device will maintain that coloration state. This is one aspect of EC memory. The ability to discontinue application of voltage means that the power consumption of the device is reduced. In some embodiments, this may be controlled manually by a user, wherein when a desired coloration state is achieved, the user may flip a switch to turn off the voltage to hold the coloration state.
[00076] Manufacture of an example EC device as in Figure 2 or Figure 3, reduces at least some of the elements and processes of a conventional configuration
manufacture, such as the use of a counter-electrode that uses a sensitive reduction process of prior devices and methods, and even balancing the capacity of the electrochromic material in the EC layer and the amount of the redox material in the opposing electrode. Some embodiments incorporate stoichiometrically more dye material in the dye-containing layer as compared to the electrochemical capacity of the EC layer so that the latter is not starved of lithium ions for reduction. Since lithium is present as a salt and the lithium ions are generated when the dye oxidizes (see Reaction 1 above), the lithium salt may also be present in excess of what is used to reduce the EC layer. Furthermore, if the two layers 22 and 14, and the two layers 59 and 39, are each made as a single multi-layered film, then a separate deposition step of layers 22 and 59 on the respective TCs may be avoided; this has the potential to considerably simplify the manufacturing process.
[00077] The electrical power for coloration is provided by source 24, 26, which is illustrated as a power source (voltage or a current source with a voltage limitation), representing the various circuit configurations, connected power source, open circuit and short circuit.
[00078] The EC devices 10, 40 of Figures 2 and 3 may be oriented between the
outside and inside of a building, and specifically, one side of substrate 11, 30 is external to the building, and one side of substrate 20, 58 is internal to the building.
[00079] Figure 3 illustrates an EC device 40 for use in a smart window. The
configuration of device 40 is similar to that of device 10, having opposing substrates 30, 58, each having respective layers 32, 56, layers and/or films. Sandwiched in the center are layers including a cathodic EC layer 13, 38, which includes tungsten oxide, a redox isolation mechanism, SICL 36, an electrolyte layer 38, and a dye containing layer 59. The dye-containing layer 59 includes Lithium ions 52, dye ions 54, and
nanostructures 50. In operation, SICL 36 acts to isolate the oxidizing agents from the reducing agents during redox action, and/or at least protects the organic electrolyte layer from coming in contact with a semiconducting EC layer 34. As discussed earlier, SICL 36 may also serve as a UV protector, which may be in addition to adding UV stabilizers (or absorbers) to the other layers, specifically the electrolyte and/or the dye containing layer.
[00080] The redox isolation mechanism is illustrated clearly in Figure 3, and the
isolation is due to the presence of SICL 36, which acts as a filter to prevent dye ions (D+) from passing through to the cathodic EC layer 34, while allowing the Li+ ions to pass. The dye ions 54 tether to nanostructures 50; those dye molecules that do not tether to nanostructures 50 in layer 42 are blocked by the SICL 36, which transports lithium ions but blocks untethered dye ions. In addition, the SICL layer 36 is designed to have poor electronic conduction, such that no redox activity takes place at the interface of SICL 36 and electrolyte layer 38.
[00081] For specific examples of materials used in devices 10, 40, some anodic dyes suitable for use with a cathodic layer are ferrocenes, phenazines, phenothiazines, TEMPO (2,2,6,6-tetramethyl-lpiperidinyloxy derivative), and so forth. An effective SICL material is selected to reduce the leakage current in order to impart memory. Leakage current refers to the current required to maintain the desired coloration state, or the current required to overcome self-bleaching of the device. Examples of SICL materials suitable for use in an EC device include options such as polystyrene sulfonate, lithium or sodium salts (abbreviated as PSSIMa or PSSLi).
[00082] In EC device 40 of Figure 3, SICL materials enable EC device 40 to maintain or hold a coloration state for extended periods of time. Some embodiments of EC device 40 have a configuration enabling reduction of leakage current by a factor of
100 to 1,000 times, as compared to a conventional EC device without an SICL and without the dye-containing mechanism where dye molecules are untethered and free to move without hindrance in and out of an electrolyte layer 14 and the dye containing layer 22.
[00083] In one construction similar to EC device 40 of Figure 3, there are no dye- containing mechanisms, such as nanostructures 50. In such embodiment, the SICL enables reduction in leakage currents even without structures or mechanisms to hold the dye ions in place. The SICL 36 isolates the dye ions and allows the Li* ions to pass through to a cathodic EC layer.
[00084] Figure 4 illustrates states and relationships in the coloration processes of EC device 40 of Figure 3 and the equivalent circuits in the operational sequence.
[00085] State 102 has the EC device configured as an open circuit in an original bleached stat. This corresponds to an equivalent circuit similar to circuit 76.
[00086] To transition to a desired coloration state, a coloration potential voltage is applied across the electrodes, state 108. The equivalent circuit corresponds to circuit 75. This condition results in the redox activity that causes the EC layer to reduce (redox reaction) and transition to the desired color. The dye in the ion conducting layer oxidizes and transitions to a color in response to the coloration potential. As discussed hereinabove, the dye may have a complementary behavior to that of the EC layer, so that a negative voltage applied to the cathode, has a similar behavior as applying a positive voltage to the anode. As illustrated in state 108, they both darken.
[00087] Once the device transitions to a desired color, the state 106 removes the applied voltage. The equivalent electrical relationship is an open circuit, where the
coloration state is maintained. This can be thought of as a hold step, where the EC memory causes the ions to stay in their transitioned locations.
[00088] To transition to a bleach state, state 104, a reverse coloration potential is applied across the electrodes. Once the bleach state is reached, the circuit equivalent is again an open circuit, state 102, which maintains the bleached state. Alternatively, to cause a faster transition to a bleached state, from state 106, the electrodes are short circuited, state 105, which pushes the redox relationships to return to their original states, specifically, the EC layer oxidizes and the dye ions reduce.
[00089] In the EC devices of various embodiments of the present invention, the configuration is designed to achieve efficient power consumption. This enables such device to be kept in a desired state of coloration with little-to-no additional applied power. The ability to reduce the power consumption makes these inventive configurations particularly applicable to large buildings, where the EC devices may be powered by a rechargeable battery or a capacitor, which in turn is powered by a solar cell or other energy harvest module. This option is illustrated in Figure 10-13 where an energy harvest unit operate in coordination with the EC device. The energy harvest unit may be much smaller than the size of a window, especially in a large multistory building with large active window area. These may be solar panels, window capture devices and so forth. An optional energy storage unit may be coupled to the energy harvest unit and configured to provide power to the EC device for coloration operations.
[00090] The present invention provides methods and apparatuses for EC devices that consume less electrical current than conventional window controllers, as the amount of current sufficient to maintain the optical state of the device is low, and in
some cases no power. As the energy harvest continues to store power, such as in a battery, the EC device may use this stored energy without incurring additional power. For power coming from a battery or an energy harvest unit, such as a solar cell, the reduced power consumption enables energy storage of the excess power.
[00091] Materials used for EC devices according to some embodiments, are
described in US patents 6,178,034 and 6,317,248, which are included herein by reference. Electrolyte 14, 38 of EC device 10, 40 may be a solid comprising one or more electrolytic plasticizers, wherein the plasticizers are stable in the
electrochemical range in which the window is powered. The plasticizers include material such as propylene carbonate, Y- butyrolactone, tetraglyme, sulfolane, monofluoroethylene carbonate, difluoroethylene carbonate, hydrophobic ionic liquids, and so forth. Polymers that enable the electrolyte to solidify include poly methylmethacrylate, aliphatic polyurethanes, fluorinated polymers and copolymers such as copolymers of polyvinylidene fluoride. Other additives in the electrolyte include UV stabilizers, tinting dyes, rheology modifiers (such as fumed silica), and dissociable salts such as lithium salts.
[00092] The use of nanoparticles provides a mechanism to provide electronic
conductivity in the dye-containing layer. These may also be bonded to, or reacted with, the dye molecules. Nanoparticles are defined as having at least one dimension about lOOnm or smaller. The other dimensions may be larger, and in some examples at least one dimension of the nanoparticles is approximately lnm to lOOnm.
[00093] One method of forming the solid electrolytes and their compositions is outlined in US patent 6,361,709 the disclosure of which is incorporated herein by reference.
[00094] The electrolyte may be a liquid or a solid, but for large area windows, such as for buildings, solid electrolyte is desirable. The electrolyte may be solidified by adding appropriate amounts of polymers. The electrolyte with a monomeric component may be positioned in the configured IGU and then polymerized.
Polymerization also includes crosslinking. For example, when a monomer in an electrolyte formulation is polymerized, the fabrication may form a cross-linked polymer, or one may crosslink the oligomeric or polymeric materials already present in a liquid electrolytic formulation. A thermoplastic electrolyte may also be processed above its melting or softening point temperature, and then solidified by cooling. In the case where crystallization of the polymeric component takes place upon cooling, the selection of material considers the resulting crystal size to facilitate visibility. In some applications, the crystal size will be less than the wavelength of light, and typically less than 500nm. Crystal size may be measured by X-ray
diffraction or by microscopy. In some embodiments, the crystal size is smaller than about lOOnm, so that the visibility through the window is not compromised due to light scattering.
[00095] As an example, in some embodiments an EC device 10, 40 used in a smart window is designed to reduce power consumption and may implement a smart controller. The reduced power is not only during transition from one optical state to the other, but also to maintain its optical state. In this way, once the EC device transitions to a colored state, the EC device will stay in that state until further control action is taken to change the potential across the electrodes. According to the present invention, EC devices may be designed so that approximately no power is consumed when the device is in the bleached state, or transparent state.
[00096] In some embodiments, a smart control mechanisms determines when the redox reactions are reversing. This smart control mechanism measures parameters of the EC device, such as leakage current, temperature, color, transparency, and so forth. When the smart controller detects a deterioration in the current state of the EC device, the smart controller acts to correct this. In one instance, the smart controller detects an increase in leakage current indicating the EC device is bleaching; in response, the smart controller applies a correction voltage to the EC device, sufficient to return to the desired coloration state. In some embodiments, the correction voltage applied is found in a look up table that has a variety of scenarios. In some embodiments, the correction voltage is fixed depending on the desired optical or coloration state.
[00097] In one exa mple, application of approximately 1.0V to 2.5V across the
electrodes of an EC device is sufficient coloration potential to color the EC device 10, 40 sufficiently to provide privacy or reduce sunlight to save energy. In the colored state, there is a leakage current that may flow to reverse coloration. The goal is to eliminate the leakage current completely if possible; however, in some
configurations there may be a leakage current due to the mobility and the physical nature of the redox materials and SICL layer in the EC device. To manage the leakage current, and thus maintain a desired coloration, the EC device may be specified to refresh the coloration potential application. In one example, the leakage current in the fully colored state may be less than approximately ΙμΑ/cm2 in the active area of the device, which is a combination of EC layer, SICL, electrolyte and/or dye- containing layer; the leakage current is measured at room temperature, such as 25°C, wherein other environmental parameters may be specified, such as humidity, level of coloration, and so forth. For an EC device where application of a coloration
potential darkens the EC device, the darker the coloration, the more the EC device is susceptible to leakage current. For an example EC device used in a smart window, where the window dimensions are approximately 1 square meter, the steady state current consumption was measured at approximately 10mA. This leakage current may be conveniently supplied by a small rechargeable battery for a long period. The small current drain is not significantly impacted when the power is removed after coloration is achieved and there would be little discernible change observed by the eye for several hours.
[00098] In some embodiments, EC devices may be bleached by shorting the
electrodes and therefore, this means that the system does not need to apply a reverse potential, wherein the reverse potential is opposite the coloration potential or charging polarity. When shorted the charge previously accumulated to color the device is leaked, and rather than wasting this charge, the system may use this to recharge the power source where energy is directed to a secondary energy storage unit, such as rechargeable battery. This increases the efficiency of these glazings and configurations.
[00099] As some dyes tend to degrade more rapidly when subjected to UV light, particularly in the colored form (or oxidized or reduced state). For example, ferrocenium, the oxidized state of the ferrocene dye is not UV stable. The UV stability of ferrocenes may be improved by attaching electron-donating groups to the cyclopentadienyl rings, such as alkanes and cycloalkanes. For example, consider tertiary butyl ferrocenes, n-butyl ferrocenes, and decamethyl ferrocenes. Stability may be better in dyes with radicals such as 2,2,6,6-Tetramethyl-l-piperidinyloxy (TEMPO), which are stable due to their structure. However, the UV stability of the
bridged dyes discussed below are examples of dyes with particularly good UV performance in these applications.
0100] Dyes that provide UV stability are those with accepter-donor type structures, such as ferrocene-viologen, phenazine-viologen, bis-phenazine, phenazine-phenothiazinetriarylamine-phenothiazine. These tend to belong to a class of bridged dyes where the accepter and the donors are linked. Bridged dyes typically contain at least two moeities with different functionalities which are linked together. These may be two different dye structures with different redox properties or even similar redox properties. However, the linked system may exhibit redox properties which are different from the moieties when they are not linked. A nonconjugated bridge, such as σ-type -(CH2)n- chains or a conjugated moiety link the two groups. The photoexcited states formed in the accepter-donor of these linked dye systems can transfer photoelectrons internally and relax without causing damage to the dye structures or to the other materials nearby. In this description ferrocene-viologen means that a ferrocene or a ferrocene derivative is covalently linked to a viologen or a viologen derivative; ferrocene may also have additional substitutions on the cyclopentadiene rings discussed above. Similarly, in bisphenazine, two phenazines are linked (e.g., 2,2'-bis-5,10-dimethyl-5,10-dihydrophenazine), and in phenazine- viologen, phenazine and viologen are linked. In addition, ferrocenes and
phenazines show an anodic coloration character, which means that they can oxidized electrochemically in the device. Viologen shows a cathodic character, which means that it colors when it reduces electrochemically in the device. Thus, in many of these examples, the bridged dyes have both an anodic and a cathodic character in the same molecule; however, since the bridged dyes, or their anions, are blocked by the SICL layer, one of their cathodic or anodic part may not participate in the redox
reactions. For example, when tungsten oxide comprising coating is overcoated with an SICL layer and the electrolyte or a layer in contact with an opposing electronically conducting layer, and a voltage is applied to color tungsten oxide, the cathodic part of the dye does not participate in the redox activity, but still such bridged dyes may be used as their anodic component will participate in the redox activity.
[000101] As discussed earlier many of the bridged dyes provide superior UV
resistance. Tungsten oxide coatings show EC behavior in both visible and near infrared (NI ) region of the solar spectrum (about 400 to 2,500nm). For EC devices designs having high contrast in both regions, dyes which also color both in the visible and in the NIR spectrum may be used with these type coatings. The bridged dyes which show activity in both the visible and the NIR regions may incorporate at least two similar or disparate anodic groups, such as bisphenazines and triarylamine- phenothiazines respectively.
[000102] Another type of redox dye that may be used in these systems (which is not bridged) are iodine (or iodide) containing materials such as Lil, Nal, Kl and other iodide salts containing photostable cations, even if they are organic. In the electrolyte, one may also use materials that can complex with iodide ions along with iodine containing salts. Materials used for this purpose include polyvinylpyrolidone (PVP), as well as monomers and copolymers comprising PVP.
[000103] UV stability of an EC device and system is further improved in embodiments of the present invention using UV stabilizers incorporated in the electrolyte and the dye containing layers. Different types of UV stabilizer, each having different mechanisms to thwart the UV threat and each with activity in different wavelength ranges, such as those covering about 280 to 400nm, may be mixed or combined to achieve composite or hybrid characteristics. UV absorbers include benzotriazoles,
triazines, benzophenones, cyanoacrylates salicyclates and others (e.g., Tinuvin® 1130 is a benzotriazole and Tinuvin® 400 is a triazine from BASF (Germany)). Hindered amine light stabilizers (HALS) may be used along with the above absorbers (e.g., BASF's Tinuvin® 123 and Tinuvin® 292), wherein generally, specific HALs are much more effective in preventing degradation when such HALS have substitution on the hindered nitrogen by hydrogen or alkyl. US patent 7595011 provides additional details on specific type of materials, combinations and their use. One may also use nitroxyls, hydroxylamines and hydroxylamine salts (see US patent 7718096) along with other UV absorbers. The presence of these HALS also extends the usable lifetime of the UV absorbers. Usually the concentration by molarity of each of the UV absorbers/stabilizers (including HALS) is about 0.1 to 20 times that of the EC dye being used, and in some embodiments, are in the range that is between 1 to 10 times of that of EC dye used.
0104] Another source of degradation is the formation of the photoexcited states in the semiconducting materials such as tungsten oxide when it is exposed to solar radiation. These excited states can degrade dyes or organic materials such as electrolytes or organic SICL layers which contact them. One way to reduce this is by doping the EC layer with other components (dopants) to the tungsten oxide coating so that its absorption edge in the UV is blue shifted so that it shifts to lower wavelengths, as the semiconducting activity is eliminated or decreased when exposed to solar radiation. A mild effect on blue shifting was measured by measuring photocurrent of devices containing EC layers with doped tungsten oxide, such as described in US patent 6,266,177, where the dopants used include cobalt oxide and chromium oxide (also see the dopants and characteristics of this layer in Example 1 of conventional devices). One may also add organic dopants, such as UV
absorbers/stabilizers and quenchers, which inhibit photo-excited states, or both types of materials to such coatings. These are collectively referred to as the UV agents. The EC coatings may be deposited and then a solution containing the UV agents is applied on these coatings so that they are absorbed into the porous structure of such layers. When using an organic SICL layer, one may also add appropriate UV stabilizers to reduce the degradation caused by the interaction of the photoexcited states originating from the EC layer. This is discussed in more detail below. The SICL may also be made of inorganic materials which are inherently stable to UV and do not have any semiconducting properties, so there is =no UV activation in this layer and blocks any activated species formed in the EC layer to cross over. Thus, this layer acts as a barrier between the organic containing electrolyte and the semiconducting EC layer, such as W03. As mentioned earlier, the SICL is specified to conduct the ions used to reduce or oxidize the underlying EC layer. In most devices lithium ion is used for this purpose.
0105] Since in this construction the SICL layer is in contact with the EC layer, in some embodiments particularly when SICL layers with organic content are used they also contain UV stabilizers to quench any photoactivity at the interface. In these designs, the UV agents (UV stabilizers/photo quenchers) are compatible with the SICL layer, but are not soluble in the electrolyte. This is to reduce the possibility of substantial amounts of UV agents leaving the SICL layer into the electrolyte. For example, when anionic polymers are used as SICL layers (e.g., polystyrene sulfonate - sodium or lithium salts), one can also use ionic, and may use anionic UV agents. An example of an anionic UV absorber is sodium benzotriazolyl butylphenol sulfonate and a compatible photo-quencher is tetramethylhydroxypiperidinol citrate. These two may be used together. The electrolyte may have a different set of UV absorbers
which have superior compatibility with it. In the SICL layer the concentration of the UV absorbers (or quenchers if used) is per the above described guidelines is about 10% or lower by weight, and in some cases 5% or lower by weight. When photo- quenchers are included in these components, the characteristics of the photo- quenchers are matched with the characteristics of the EC dyes so the materials do not interact with the dyes to kill/reduce their desired EC activity. Care is taken in design incorporating photo-quenchers (or antioxidants) in the electrolyte to ensure that the dye ions produced by the electrochromic reaction are not reduced by the quenchers leading to irreversible reactions. Prior to the deposition of SICL layers one may optionally treat the EC coatings with UV agents as discussed before, unless the deposition of SICL layers from solutions containing the UV agents will also cause the UV agents to intercalate in a sufficient quantity within the pores of the EC layers.0106] The US patents (6,853,472 and 7,300,166) also teach the use of
hydrophobic ionic liquids in electrolytes, wherein ionic liquids may also be considered as a part of the plasticizer component, (part of the liquid component to dissolve the salt) to further increase the device durability. The full disclosures of the US patents 6,853,472 and 7,300,166 are included herein by reference. The ionic liquids may be used for partial or complete replacement of the plasticizers discussed earlier. Ionic liquids include quartenary ammonium cations, such as pyridinium, pyrrolidinium, pyridazinium, pyrimidinium, pyrazinium, imidazolium, pyrazolium, thiazolium, oxazolium, and triazo!ium. These can have various substitutions or substituents, such as H, F, phenyl and alkyl groups with 1 to 15 carbon atoms. Rings may even be bridged. Some embodiments incorporate anions that are fluorine containing such as triflate (CF3S03 ~), imide (N(CF3S02)2 Ί, beti ((C2F5S02)2N~), methide (CF3S02)3C"), tetraflouroborate (BF4 "), hexaflourophosphate (PF6 -),
hexafluoroantimonate (SbF6 -), bis(fluorosulfonyl)imide (N(FS02)2 ") and
hexafluoroarsenate (AsF6 -). Of these, imide, beti bis(fluorosulfonyl)imide and methide anions may perform better in some applications.as these are hydrobhobic. An example of an ionic liquid (IL) is l-Butyl-3-Methyl Pyrrolidinium
bis(trifluoromethanesulfonyl)imide (BMP). When ionic liquids and lithium salts are used, in some embodiments the anion for both are similar. The electrolyte may contain both the ionic liquids and non-ionic plasticizers. Typically, the electrolyte contains dissociable salts, particularly lithium or sodium salts, ionic liquids and redox materials (includes electrochromic dyes). Ionic liquids, lithium salts. In those devices where the electrolyte layer contains redox dyes which have salt structures with anions and cations, this anion may be the same as that of the ionic liquid and for the lithium salt. For example, use of bis(trifluoromethanesulfonyl) imide anions in the ionic liquid, lithium salt and the dye (for dyes with salt structure) the EC device has shown good performance in some applications. In those devices where the dye- containing layer is separate from the electrolyte layer, the redox dyes, lithium salt, ionic liquid, and other plasticizers are also present in this layer. As discussed above, the dye molecules are restrained in the dye-containing layer, which may have electronically conductive nanoparticles at or above the percolation threshold. In other words, the dye containing layer when separate from the electrolyte layer has both ionic and electronic conductivity properties.
0107] EC devices with an SICL layer, which is ion-conductive and non- electronically conductive, experience low leakage current. As seen from the detailed disclosure contained in US patents 6,178,034 and 6,317,248, the lowest currents are obtained when the SICL layer has an ionic nature. In an example using a cationic polymer PSSNa or PSSLi in the SICL layer, the leakage current was measured at about
10 to 100 times lower compared to the other SICL layers used, including lithium niobate, known as inorganic lithium, as an ion conductor. However, in this example, use of the above polymers incorporated a small amount of water in the electrolyte for the devices to work properly; the addition of water is not desirable for a high durability device as water interacts electrochemically, which reduces cyclability and UV performance. Other ionic SICL may be fabricated using acidic polymers which are neutralized with alkali metal bases. For example, acrylic acid and poly(2-acrylamido- 2-methyl-l-propanesulfonic acid) (POLYAMPS® available from Lubrizol Corporation, Wickliffe, OH) can be converted to lithium or sodium salts by reacting them with bases such as lithium hydroxide and sodium hydroxide respectively. For use with EC coatings containing tungsten oxide the SICL layers where the acidic polymers are converted to their salt state (including partial conversion) their specified pH is in the range of 3 and 8 and more desirably between 5 and 7. pH of the converted polymers can be measured by forming a 5% (by weight) solution in water and measuring its pH.
0108] Cationic polymers are fluorinated polymers which have inherently high durability to UV radiation. Some specific examples of these are Aquivion® materials from Solvay (Brussels, Belgium) which are lithium salts of perfluorosulfonic acid (e.g., PFS03Li represents the lithium salt form (-SO3L1) of PFSA or perfluorosulfonic acid). Some of the grades that work for some applications are D79-25BS Li and PW79S Li. Another example of a material is Flemion™ from AGC Chemicals (Tokyo, Japan). Another example is lithiated Nafion® called Lithion™ (available from Ion Power, New Castle, DE). The SICL layer may also be formed using a monomer which is
polymerized and/or crosslinked after deposition.
[000109] Thus, to achieve high device durability in addition to using UV stable dyes, hydrophobic ionic liquids and proper UV stabilizers in the electrolyte, in some embodiments, a highly durable hydrophobic SICL layers does not require
incorporation of water to the electrolytic layer. In some embodiments, SICL is made from hydrophobic inorganic materials. This means those layers which can conduct lithium ions without water added to the electrolyte. SICL layers may also be formed of inorganic materials including inorganic fluorides which are not semi-conductors and have ionic conductivity. Examples are cryolite (materials containing lithium fluoride and aluminum fluoride) and other inorganic lithium conductors discussed above for the traditional kinds EC of devices.
[000110] Although there are many methods of measuring UV stability of EC devices, but one widely used standard method for window devices in an IGU configuration is ASTM E2141.
[000111] In some embodiments, the solid electrolyte sheets (or multilayer
electrolytic sheets containing the electrolyte and the dye layers discussed earlier) are fabricated first (cast, extruded, and so forth) and then incorporated into the EC devices. For solid electrolytes, transparency should be high and with low optical haze. Both transparency and haze are measured on a laminate which is formed by laminating the electrolytic film of the thickness to be used in the devices between two clear pieces of soda-lime glass substrates with a thickness in a range of about 2.1 to 2.3mm. Transparency is specified to be greater than 75% at 550nm. Typically, the haze is specified less than 0.5% as measured by ASTMD1003 method, in another embodiment the haze is specified lower than about 0.2 %. The ionic conductivity of the electrolyte, and the dye layer without electronically conductive particles, at 25°C is specified equal to or more than about 10"6 S/cm. Use of solid electrolytes also
reduces the hydrostatic pressure at the perimeter seals of the EC devices. The solid electrolyte is specified to resist deformation within the EC laminate due to wind loads, thermal or other stresses, such as in large window sizes. As discussed in this disclosure part of the deformation can be reduced by using thicker substrates, but mechanical properties of the solid electrolytes also are important. To avoid deformation and keep the hydrostatic pressure in the seals low, the hardness of these electrolyte sheets is generally be in the range of Shore A10 to D55. For example, if the electrolytic sheets are thinner, then a harder sheet in the range of 0.1 to 1mm may be used as long as at least the ionic conductivity incorporatements are met. In addition, the properties and adhesion of the solid electrolytes also impart other characteristics if they are selected properly, particularly as it relates to reduction of sound transmission and improving scatter resistance. Scatter resistance is the ability to support or keeping the small pieces of the substrate when broken adhered to the electrolyte film) and this property is typically measured by a ball drop method. Reduction in sound transmission is governed by the loss or damping ability of the sound frequencies (in about 5 to 20,000 Hz range). The scatter resistance is governed both by the adhesion of the electrolyte to the substrate and by its elongation and strength. A desired adhesion to the substrate at room temperature (25°C) is specified to be at least 1.8kg/cm as measured using a peel test as described in ASTM D3167 (see US patent 6,995,891 for additional test details and mechanical incorporatements of the solid electrolytes, the disclosure of which is contained herein by reference). In some embodiments, the solid electrolyte at room
temperature is specified to have adequate strength, such as 5 kg/cm2 or greater, and an elongation to failure, such as 100% or greater, as measured by ASTM test method D638.
[000112] One method to prepare a solid thermoplastic electrolyte for a device shown in Figure 2 is discussed below. A plasticizer is used to dissolve the ion conductive salt, such as lithium salt, and the redox dye. Further, to this composition polymer(s) and UV stabilizer(s) are added. After the components are mixed properly, if used, the rheology modifying nanoparticles are also mixed in (e.g., compatible hydrophobic fumed silica in a size of about 1 to 500nm). The ingredients are mixed at elevated temperature (typically between 80 and 150°C) under inert conditions. This mixture may also contain a removable solvent to facilitate processing. The mixture is then removed and cast as sheets (and solvent removed if present) which is then used to laminate the coated substrates to form the device. Since the electrolyte is specified to be solid at all use temperatures, the application and use of the EC device determines the operating temperature range. For example, a smart window in New York City may be specified to be solid for at least 50eC above the maximum
anticipated use temperature. The maximum use temperature is the temperature which the place reaches in summer. This is because the EC glass in the colored state will heat up further due to the absorption of the solar radiation. Generally, windows which would meet temperature incorporatements in all geographic areas for architectural use are specified to be functional at least up to a temperature of 85°C, and in some embodiments up to 95°C. These may be capable of being stored to 110eC and in some embodiments to 120eC.
[000113] At low temperatures, the ion conductivity of the electrolyte, SICL, dye layer and the EC layer decreases, which results in sluggish kinetics. It is desired that the EC functionality of the windows be preserved at least to 0°C, and specified down to - 20°C even if the response is sluggish as compared to that of room temperature. The EC panels of these windows are usually constructed of both inorganic materials and
organic materials. In some embodiments using glass (e.g., soda lime glass) as the substrates, TC and the EC coating are inorganic and the other layers and seals would usually have an organic matrix. Typically, inorganic materials have a lower thermal expansion as compared to the organic materials. In addition, there is a large change in thermal expansion coefficient at glass transition temperature (Tg) of the
amorphous materials, and many of the amorphous organic compounds may have their Tg in the range of use temperature, such as from -40 to 120°C. The material selection assumes that during use at temperature there are no glass transitions of organic layers or perimeter sealant. The Tg of the electrolyte, organic SICL, the dye- containing layer and the perimeter sealant are specified lower than the use temperature. Since these compositions are plasticized, the freezing or the glass transition point of the composition is specified below -20°C or in some embodiments below -40°C. These solid electrolytes comprise 20 to 50% plasticizer, 4 to 40% polymer which also acts as a binder (thermoplastic or monomer by weight which may be later polymerized and or crosslinked under lamination conditions), ion conductive salt - such as lithium salt 1 to 10%, redox dye 0.5 to 10% and UV stabilizer 0.1 to 10%, and viscosity modifiers such as fumed silica or fumed alumina about 5 to 50% by weight of the electrolyte. One may even use a solid polymer electrolyte with inherent ion conduction (e.g., cationic polymers neutralized using lithium base) which may not incorporate plasticizers or the viscosity modifiers and will also act as a binder. Such electrolytes are formed as sheets which are then laminated between the coated substrates. One may also substitute the polymer partially or completely with a monomer which is polymerized after the sheet is formed, or after it is laminated to the coated substrates used to make the device. Polymerization may lead to the formation of thermoplastic or thermoset (crosslinked) electrolytic
component. Other components such as adhesion promoters, tinting agents, spacers, catalysts (photo or thermal catalysts) for polymerization (includes crosslinking) may be used.
0114] Another inventive method to reduce the leakage current in EC devices containing an electrochromic dye by depositing a layer of counter-electrode over the TC, shown as layer 42 in Figure 3 (or layer 22 Figure 2), rather than this layer being a part of a multi-layered electrolyte film, this is deposited as a coating on the TC 56 (or on TC 19), and then the two coated substrates are assembled with the electrolyte 38 in Figure 3 (or electrolyte 14 in Figure 2) in between. This counter-electrode layer contains an electrochromic dye which has a complimentary character to that of electrochromic coating 34 described below. If coating 34 is cathodic, then the dye is specified to exhibit an anodic character, even if it is a bridged dye with both anodic and cathodic characters. Layer 35 may be specified to have electronically conductive particles, which in some cases are nanoparticles or nanofibers or nanotubes, wherein the diameter of the nanoparticles, nanotubes or nanofibers being in the nano range. The nanoparticles maybe nano-discs having a disc thickness in the nano-range. The nanoparticles present in layer 35 have a concentration above the percolation threshold. The concentration may be specified such that the layer is still transparent. The dye is attached to these particles, or attached to the polymeric matrix, such that the dye does not have to move to an electronically conductive electrode in order undergo a redox activity; some dye molecules may be attached to the matrix and some to the conductive nanoparticles. The device in Figure 3 is assembled after coating the two substrates, one of them with dye and conductive nanoparticles containing layer and the other with containing another EC layer and then the device is formed by assembling the two coated substrates with an electrolyte layer 38. This
figure shows the two substrates 30 and 58 are coated with TC's 32 and 56 (or substrates pre-coated with TC's are used). One of these substrates is coated with an EC coating 34 such as including tungsten oxide or doped tungsten oxide. On top of the EC coating SICL layer 36 is deposited. This substrate is then assembled in a spaced apart relationship with the opposing substrate, having a gap therebetween containing an electrolyte 38 in this gap. As discussed in the description of layer 166 of Figure 6, in layer 35 the redox dyes may be incorporated by mixing these along with conductive nanofibers in an electrolytic mixture (using the electrolyte
compositions described earlier) and then solidifying by removing a solvent, cooling or by polymerizing (e.g. cross-linking) the coating after deposition (e.g., see US patent 8,593,714 the disclosure of which is incorporated herein by reference). As used herein, the conductive nanomaterials are specified to be present above the percolation threshold. However, according to some embodiments and methods, the process attaches the dye molecules to the conductive nanoparticles, as also discussed below while describing layer 166.
0115] In any of the devices described herein, an outer diameter of the conductive nanofibers (nanofibers include nanotubes) is about 25nm or less and may be about 5nm or less. The specified average length is about 500 times the diameter or more, and in some embodiments the average length is specified to 1,000 times or more. Carbon based nanotubes may be single, double or multi-walled. Single and double- walled tubes are used as these are thinner and percolate at a lower concentration and preserve better visibility of the devices. It may also be specified that the concentration of carbon nanofibers be as low as possible but to achieve percolation. The concentration of these fibers in a coating (or a layer on the electrolyte film) as in other devices discussed below, may be 2% or less by weight, and may be specified
less than about 0.5% or 0.1%. This ensures layer is still transparent, and that fibers, or conductive discs or particles, be well dispersed so that they achieve the
percolation threshold at the lowest concentration. In addition, this also keeps the cost of such layers low.
0116] When redox dyes are tethered to the conductive nanowires, then it is done prior to incorporating them into the layer composition. This ensures that a
substantial amount of the dye molecules is in contact with the conductive element; they do not have to travel to the conductive layer for the redox activity to take place. This also results in faster device kinetics, or faster color change as long as the charge is not limited by the resistance of the transparent conductor. One way of achieving this is to make or synthesize conductive nanowires with organic functional groups (or functionalized surfaces) and make dye molecules which have complimentary groups so that these can react with the functional groups on the surface of the nanowires. Some of the common functional groups that can be attached to the conductive particles are hydroxyl, amino, carboxyl, aldehyde, vinyl, and so forth. These can react (for example condense) with functional groups on the dye molecules. For example, amino or hydroxyl groups on the nanofibers can react with carboxyl groups on the dye molecules, or one could have carboxyl groups on the surface of the nanofibers which could react with hydroxyl or amino groups on the dyes. Any material may be functionalized with any group as long as it can react with a group on the other material. This reaction between the dye and the nanowires is may done prior to adding the nanowires to the polymer to form the electrochromic layer. One can mix nanowires with attached dyes and optionally nanowires with no dyes attached in the electrochromic layer. Carbon nanowires with functionalized surfaces (single and multi-walled) are also available commercially, e.g., some sources are Cheap Tubes Inc
(Grafton, VT); US Research Nanomaterials Inc (Houston, TX) and; Nanostructured and Amorphous Materials Inc (Houston, TX). One may also use functionalized graphene sheets to attach the dyes instead of the nanofibers. One may also mix graphene with nanofibers, or conductive particles of different shapes. When forming the EC layers containing the immobilized dyes reacted with conductive particles, the concentration of the conductive particles including the particles attached to the dyes are specified to be at least at or above the percolation threshold. The conductive particles are also transparent having a high visible transmission and low visible light scattering as discussed hereinabove. It is not necessary that the conductive particles be made of carbon, but that the surfaces of these nanoparticles should not be electrochemically active, save the dye molecules if they are attached to these surfaces. Some other choice of conductive nanoparticles, including fibers, sheets spherical or any other shapes, are conductive metal oxides, such as indium tin oxide, coated with carbon or conductive oxides so that metal reactivity with the electrolytic materials can be eliminated.
0117] Figure 5 illustrates EC devices 180 according to some embodiments containing multilayer electrolytic compositions. EC device 110 has two opposing substrates 112 and 124, which are respectively coated with TC layer 114, 122. In this case the multilayer electrolyte has three layers 116, 118, 120. The layers 116 and 118 have redox materials incorporated, where at least one of these materials has electrochromic properties. For example, if layer 116 has cathodic EC dye then layer 120 will have an anodic material, which may also have complimentary EC properties. Since many of the bridged dyes have both anodic and cathodic behavior, one may incorporate the same bridged dye in these layers. When this device is powered to color then anodic part of the bridged dye is activated in one layer (e.g., in layer 116)
and the cathodic part of the bridged dye is activated in the other layer (e.g., in layer 120). The US patent 8,115,984 is incorporated herein by reference and details some options for these devices.
[000118] Continuing with Figure5, the central layer 118 does not include redox
materials. The dyes or the electrochromic materials in the layers 116 and 120 are immobilized to reduce transport into layer 118. Immobilization may be done by reacting dyes with the polymers comprising the matrix of layers 116 and 120, which may be optionally crosslinked. Similarly, immobilization may be achieved by attaching the dye ions to the conductive nanoparticles present within this layer; or immobilization may be done using both methods, such as to attach some dye molecules to the conductive particles and immobilize others by reacting to the polymer or some other non-mobile component in the matrix.
[000119] In some embodiments, when dye ions attach to polymers and are
immobilized in these layers, conductive nanoparticles may form a percolated network in layers 116 and 118. In this way, the dye molecules are able to undergo redox activity; they give up or take an electron. An electron is transported via this conductive particle network to the TC layer and through an external circuit to the opposite side of the device. When the electrolyte layer 118 is laminated and combined with the substrates, the nanoparticles provide electronic conductivity into these layers and form a conductive interface with TC 114, 122
[000120] The conductive particles may also be conductive nanowires, nanofibers, nanotubes, discs, spherical, elliptical, or mixtures of these or other nanostructures having conductivity, such as those described in US patent 8,593,714, which is incorporated by reference in its entirety. The device 110 (Figure 5) is configured by laminating the electrolyte 118 and sealing the perimeter 130. The device is
connected electrically using connectors 132 and 134. The type, amount,
configuration and positioning of the nanostructures are designed such that the use of conductive nanoparticles does not produce an unacceptable visual haze or
darkening. In manufacture and production, EC device 110 is designed to have a visible haze of approximately less than 2% and often less than 1% before
incorporated into an IGU or window. For skylights or those windows which are far from where a user's vision, one may have higher amounts of haze, as sometimes the purpose of these skylights and windows is only to let the light in but not elements where a user is looking out from to appreciate the view outside.
0121] If the electronic conductivity in the outside electrolytic layers (layers 116 and 120) is high, then one may use lower conductivity TC on the substrates. One may even eliminate TC's where the substrates may be coated with a perimeter of a conductive busbar (not shown in the figure). This conductive busbar is located so that it can be used to attach the electrical connectors (like 132 and 134), but also extends into the device below the seal 130, just like the TC but is only partially into the device so that conductive network of the particles in the electrolyte 116 and 120 can make connections to these at the perimeter. The conductive busba r in contact with the electrolyte should not react with the electrolyte, and may even be coated with a conductive passivation layer if such a reaction is suspected. This is a method of using non-conductive substrates, insulating or non-conductive substrates with no electronically conductive coatings, electrically powering the cells or making electrical contact with the electrolyte, but still having the electrolyte sealed at the perimeter to be protected from the environment. Other methods may include inserting electrical connectors through sealed holes in a substrate. This type of a laminated EC device using multilayer electrolyte is particularly favorable when plastic substrates
(flexible or rigid) are used as the transparent conductors available on these substrates are not highly conductive, or may not even be present.
[000122] The thickness of the electrolyte 116, 118, 120, combined layers in some embodiments is approximately 0.1mm to 1mm, and in some embodiments, less than approximately 100 μηη and in some embodiments, less than 10 μιη. In those layers where the EC dye is present, its concentration may be approximately 0.1M or less, and in some embodiments 0.05M or less. The conductive network of the
nanoparticles in the outer layers of the electrolyte helps in reducing or oxidizing the dye molecules throughout the layer without having the dye to travel. This also improves the kinetics of the device, such as at low temperatures when mobility of large molecules/ions is limited.
[000123] The composition and concentrations of each of the three electrolytic layers, 116, 118, 120, including plasticizer and lithium salts, could be similar to encourage good ionic conductivity throughout the multilayer configuration. The other additives, such as UV stabilizers and polymers, may be different or the same in these layers. Such construction reduces the amount and expense of the dye used, as it is limited to the outer layers, which are usually thinner. Further, this type of construction reduces self-bleaching and enhances the memory of the device, where the device retains its desired color without having to continuously incorporate continued or additional power.
[000124] Figure 6 illustrates a similar configuration as in Figure 5 where the EC device 160 has an electrolyte layer having two layers, 166, 168, and one of the
electrochemically active layer 170, such as an EC layer of tungsten oxide, nickel oxide, polyaniline, is deposited on one of the substrates 174 which is coated by a TC layer 173. These layers may be made mainly EC materials, which are inorganic or
non-conjugated, for windows to be subjected to the UV. The other substrate 162 is also coated with a TC layer 164. If layer 173 is a cathodic layer, such as including tungsten oxide, then layer 166 of the electrolyte will have anodic character. In some embodiments layer 166 may have both anodic and cathodic behavior, such as when a bridged dye is used. The layer 168 is an ionic conductor (electrolytic), which means that layer 168 has high ionic conductivity with low-to-no electronic (or electrical) conductivity. The configuration may be laminated together and sealed at the perimeter with a sealant 180 to form a device which is powered by using leads 182 and 184. In both Figures 5 and 6, one may have additional perimeter busbar (not shown) attached to the TC and to which the wires 182 and 184 are attached to outside the sealant.
0125] A variation is also shown in Figure 6 which resembles Figure 5, wherein there are no transparent conductors on either side. The substrate 70a has a layer of conductive material 71a which runs substantially around the perimeter, similarly 71b runs around substantially the perimeter of substrate 140. When the film which comprises of layers of electrolyte 72b with the EC layer 72a, which is also
electronically conductive and has redox properties, and EC layer 72c, which is also electronically conductive with redox properties is laminated along with the perimeter sealant 76, the layers 72b touch layer 72a and similarly layer 72c touches 71. Since layers 72a and layers 72c also are electronically conductive they are able to transfer the charge to the perimeter conductor 71a and 71 respectively. One may have yet another busbar on top of 71a and 71 outside the sealant area (not shown) to further augment the conductivity of the perimeter conductors. The perimeter conductors should be made of materials which will not interfere with the EC redox reactions. One may extend this concept to the device illustrated in Figure 6, at least as it relates
to the side coated with transparent conductor 164; in other words, the transparent conductor 164 may be eliminated and replaced by a perimeter conductor. For small devices (typically smaller than about less than few inches (e.g., interior EC mirrors for cars) one may have the perimeter conductor only run on one side of the device rather than around the perimeter.
0126] Figure 7 illustrates a process 400 for operation of an EC system where the power system 402 initiates and receives sensor information 404. The sensor status is evaluated 406 to determine if the system is ready for operation. If the sensor status fails, the system error is identified 405 and corrective action taken 407, else the system determines if power is less than a minimum 408. If the power does not satisfy the power range, processing goes to identify the error 405, else processing continues to determine if the power is greater than the max 410. If the power is out of range, processing continues to identify the system error 405, else the system receives additional sensor information 412. The system then analyzes the sensor information to determine the information indicated 414. The sensor information is compared to a control database that includes scenarios and actions to be taken on given conditions. This is considered with respect to a control scheme predetermined for the system, or which may be adjusted dynamically in response to sequences of events or trigger conditions. The system also considers user inputs, such as where the user desires a darker room during the day to view a video. If a change is indicated by this analysis and processing, 416, processing continues to adjust the smart window control 418 and log the action in a control database, 420; else processing returns to receive more sensor information, 412, and analyze same, 414. If actions are logged into a control database, this information is available for analysis as in step 414.
[000127] In this way, the system uses the sensors available to determine operational continuity of the system. A system may be configured to take specific actions in response to various sensor levels. A room scenario is built considering a variety of environmental conditions. For example, the system may use temperature and light in the room to determine the correct shading of the window. The sensors may provide room temperature, thermostat setting, number of people in the room, the humidity in the room, as well as external conditions. External conditions may include temperature, haze, visibility, precipitation, brightness, direction of the sun relative to the window and others. Additionally, the external information may include energy harvested power, such as solar cell power, which may be used to power the smart window and where such harvested energy may be stored locally in a battery or a super capacitor for later smart window use. The electric power being harvested from the solar cell may also be used as information on the solar intensity incident on the window. This information is mapped or allocated to specific scenarios for action to take. This action may take the form of applying and/or adjusting the coloration potential across the electrodes of the smart window EC device.
[000128] Many external conditions originate from incident light from the sun, as illustrated in Figure 8 and 9. This construction shows a window for architectural use in an IGU configuration 302, outer pane having an EC panel. Another glass panel 305 includes a low-e coating or film that minimizes the UV and IR light that can pass through glass without compromising the amount of visible light. For EC devices as described herein for a variety of applications, as illustrated in Figures 2, 3, 5 and 6, one substrate will face the outside of a building and is referred to as the "outer pane." This outer pane or outer substrate contains an inorganic EC layer coating, such as example tungsten oxide. This gap may have air, or a low thermal conductivity
gas such as argon, krypton, xenon, sulfur hexa-fluoride or be even evacuated. At least one surface of the EC panel of the outer pane that faces the gap), or the inner pane is coated with a low-e coating. In this figure, the surface of the inner pane facing the gap is coated with a low-e coating. When the outer pane is dimmed, as in Figure 8, much of the incident light is blocked by the outer pane. Since most of this blockage occurs by the outer EC pane absorbing the solar light (mainly in the visible and the Near infra-red or NIR region, between 400 to 2,500nm, this energy converts to heat which raises the temperature of the outside panel and radiates the heat both outside and in the gap. Radiated heat is shown by squiggly lines of Figure 8. The low- e coating on the inner panel prevents this heat from entering the building and reflects it back towards the outer pane. Thus, only a reduced portion of energy reaches the inside of the building, such as direct solar radiation in the visible and NIR, or the energy converted to heat. Control of the solar energy is managed by control of the EC transmissivity on the outer pane. When the outer panel as in Figure 9 is clear, solar energy passes through the EC panel in the visible and NIR; this solar energy passes through the low-e coating on the inner panel into the room. This energy is not blocked by the low-e coating. Only the radiated heat energy entering the room is controlled or blocked by the low-E coating.
0129] The EC devices and their use in IGU described herein aid the design of energy efficient buildings and operations. As illustrated in Figure 10, many cities are requiring new construction to have significant levels of energy generation on site. The ability to incorporate energy harvesting techniques with the EC controls, according to the present inventions provide these energy reduction opportunities. In a building as multistoried building 500, where each story has multiple windows 502, 506 and so forth, where one or more of the windows is a smart (EC) window IGU.
The various methods and techniques described herein may be used in this building, where a single type of smart window may be used throughout or a combination of different types of smart windows may be used to optimize the flexibility and responsiveness to meet the goals of the builder. In the building example 500, the solar cells are placed in the spaces between (504) the windows. In this way, the solar cell does may not have transparent portions, but rather may be configured in a variety of ways. The ability to place the solar cells proximate the smart windows dramatically reduces the conventional methods of extensive wiring throughout the building and around the window. In the embodiments of the present invention, the wiring is configured minimally at the perimeter of the window as only a small amount of power is used for color transition and low-to-no power is used to reverse the color transition. The solar cells may generate more energy than incorporated to power the EC windows, and that may be used for other tasks in the building and/or returned to the utility grid.
[000130] FIGURES 11-13 illustrate more detailed view of a multistoried building 500, wherein the fa ade 506 is coupled to spandrels 504 configured between windows 502 and glass doors 508. The placement and configuration may be designed according to design goals and usage patterns of the building 500. The doors and windows may have electrochromic elements and the spandrels may have building integrated solar cells.
[000131] Figure 12 illustrates the window in an IGU configuration comprising an EC element 512 made by the present invention coupled to another glass pane 502, both placed in parallel with a gap 510 as discussed earlier. The EC element 512 comprises of the two substrates 512a and 512b, with various layers and electrolyte as discussed above shown collectively as 514. At least one of the surfaces 2, 3 and 4 are coated
with a low-e coating (not shown). In some embodiments, an order of construction when only one low-e coating is used, the most preferred surface is surface e 2, followed by surface 3 and then 4.
[000132] Figure 13 shows schematics of a building integrated solar cell configuration for the spandrel area. This is also integrated using an IGU type construction. Where the laminate 562 comprises of solar cells. Typically, the solar cells are placed in layer 564 with laminating films on both sides (these sub-details are not shown), and then laminated to the substrates 562a and 562b. This is assembled in an IGU configuration as discussed above for the EC panel with substrate 550 providing a gap 560 which is filled or evacuated as above. The solar cells for use in spandrel area are opaque and substrate 562b is highly transparent to maximize the amount of light hitting the solar cell. Optionally as above at least one of the surfaces 2, 3 and 4 may be coated with a low-e coating (not shown) as discussed above.
[000133] Figure 14 illustrates a method 600 to control the internal environment and the smart window operation. The process initiates for the internal environmental control 602. The process receives temperature information of the building interior and exterior 604. If the interior temperature is within range, 606, processing continues to monitor internal lighting condition 612; else processing continues to determine if there is a coloration adjustment suggested to achieve temperature change, 608. The system then determines the circuit adjustment to achieve a desired coloration, 610.
[000134] From step 612 the process determines internal light adjustment to maintain internal visibility according to a predetermined or user-adjusted lighting scheme, 614. The system then determines the circuit adjustment to achieve the desired coloration, 616. The system receives or retrieves scenario information based on the
information received so far, 618 and compares the internal environmental information to the control scheme corresponding to the scenario information, 620. If no change is indicated, 622, processing returns to A, and if a change is indicated, 622, processing continues to change environmental control scheme 624 and the action logged into control database 626. This information is fed back into step 620.
[000135] Figure 15 illustrates a process 700 for control of energy harvest control 702.
The system configures for energy harvest criteria 704. If an energy harvest trigger event is detected, 706, processing continues to initiate energy conversation mechanism, 712; else processing continues to determine coloration adjustment to achieve temperature change, 708. The energy conversion mechanism initiates to couple energy conversion mechanism to energy sink, 714. The process logs the trigger event, the activity, and energy harvesting status in an energy harvest database, 718. This is then compared to an energy harvest control scheme 720. If a scheme change is indicated, 733, the process changes the energy harvest control scheme, 724, and logs the energy harvest control in the database, 726.
[000136] Figure 16 illustrates a smart window system and energy storage control system 800 having DC-DC Convenor 804 (coupled to receive electrical energy from the energy harvesting unit to the energy storage 806), energy storage 806, DC-DC Converter 808 (coupled between the storage unit 806 and the EC panel of the window) and energy harvest database 802. The control bus 810 manages
communication within the system 800. The system 800 includes a wireless controller 812 to enable wireless control of the system by a user. A sensor Application
Programming Interface (API) 814 is configured to retrieve and receive sensor inputs from a variety of sensors in the environment. An energy scenario database 816 stores specific details of the sensor conditions and ranges that correspond to specific
control schemes. These are used to control the energy harvesting activity, storage of energy, use of energy in control of smart windows, and storing information related thereto. The system controller 818 is configured to learn from behavior of the system, including the system's response to actions taken and the incorporation of user control. In this way, the system receives feedback as to sensor input
combinations that resulted in a specific action(s) and the results of those actions. One consideration is if the user fine tunes or adjusts the automated response of the system. This information is put into the databases and part of the controller 818 analysis.
[000137] As described herein, embodiments of the present invention provide devices that immobilize the dye ions using nanoparticles and an optional isolation layer, SICL, both to encourage maintenance of color transition without additional power application. This memory effect improves the performance and efficiency of the EC device of the present inventions over those of conventional smart window and IGU constructions and configurations. The use of SICL layers prevent adverse reactions between the EC layer and the dye ions.
[000138] Substrate Considerations for Rigid Glass Windows
[000139] In various configurations, such as illustrated in Figures 1-3, particularly for use in large area devices for use in building and transportation windows where a polymer containing electrolytic layer is laminated between two substrates, and where substantial amount of color is contributed from both of the electrodes separated by the electrolyte layer or where an EC layer is present on one substrate and a redox dye in the electrolyte, it is important to maintain the rigidness of the EC structure and the electrolytic gap even when the EC panel experiences large stresses during use. These large stresses in substrates using glass may come into play due to
differential thermal expansion of components and/or wind loads and so forth. If the electrolytic gap is not maintained this can give rise to splotchy coloration or at least during the coloration and the bleaching events. "Substantial amount of color is contributed from both of the electrodes separated by the electrolyte" means that each of the electrode shows more than 20% change in their optical transmission at 550nm from their bleached to the most colored state of the device. In some embodiments, a cathodic EC electrode contains tungsten oxide which colors substantially and the anodic EC layer may have materials containing iridium oxide, nickel oxide, Prussian blue, and so forth which also color substantially. An example of this embodiment where both layers color substantially is discussed in US patent application having publication number 20140205748 for devices with tungsten oxide and nickel oxide, which is incorporated herein by reference. Large area device means where the smallest dimension, such as width or height or length, of the window is about 0.5m or more.
0140] The rigidity of the structure is improved by one or more of the following methods: making at least one of the substrates forming the EC element thicker- especially the one facing the outside of the building; by heat
strengthening/tempering these substrates; and incorporating rigid spacers within the electrolyte layer so that they can bear the stress without deforming the soft electrolytic layer in case the substrates experience deformation stresses. The glass substrates particularly if the outside substrate has an EC coating which is in colored state, that may reach a temperature of about between 65 to 90°C or higher in hot bright climatic conditions. This is because the solar energy is absorbed in this layer and converts to heat. Thus, this sheet is thick so that it may be effectively tempered or heat strengthened. Secondly if this is a thicker glass, this will hold better against
wind loads and will not deform easily and provide higher protection from deformation to the inner layers or substrates.
[000141] The glass substrates forming the EC element, particularly the one facing outside of the building having a thickness of 3.2mm or higher, may be specified 4mm or higher. A typical desired range is about 4mm to about 13mm. Substrates greater than 4mm in thickness are easier to heat strengthen to a higher degree (which includes tempering). The range between 4 and 11 mm is most desired to have the desired properties and to keep the weight of the windows reasonable. Further, this substrate is coated with that EC material or electrode that has more absorption or attenuation in the solar range, such as visible and NIR. For device containing tungsten oxide in the EC device, this substrate may be coated with this layer.
Depending on the attenuation of the solar energy from the first coated substrate, the other substrates may have similar properties (thickness or degree of strengthening) or they may be considerably thinner, as much as down to 1.6mm and not
strengthened.
[000142] In another embodiment, spacers, generally spherical in shape, are
introduced within the electrolyte to increase the rigidity of the gap, as the spacer size is close to the electrolyte thickness, and perhaps slightly smaller about 85-95% of the electrolyte thickness. The spacers may be polymeric, metal oxide or glass and having a higher rigidity or hardness as compared to the electrolyte composition within the temperature range of use. Further, in some embodiments, these spacers be porous, may have a specified pore size 5 to 300nm, or be index matched to the electrolyte. Use of porous spacers allows the electrolyte or some of the electrolytic components during processing or use to penetrate its pores so that the spacers with filled pores have a refractive index similar to that of the electrolyte. Generally, if a laminatable
polymer sheet is made, such spacers are dispersed in the electrolytic formulation prior to casting or extruding the film. Any of these methods allow spacers to be less visible while viewing through a window comprising these spacers. The Index matching means that the refractive index of the spacers and the electrolyte is within 0.05 units and may be specified within 0.02 units to reduce their visibility, such as the published US patent application 20130128333. Both methods may also be combined that is thicker substrates are used along with the above described spacer types within the EC element of the windows.
0143] Further, one of the substrates forming the EC element may have an absorptive or a reflective tint (e.g., see US patents 6373618 and 6039390), particularly the substrate facing outside, this helps in reducing the solar energy on the EC element thus protecting it and optionally even imparting a hue to the light transmission which can neutralize the color of the device. The tint will reduce the light transmission through the substrate. Substrates with visible transmission of about 30 to 80 % in visible (photopic) or may be specified about 40 to 80% in the visible are acceptable. For example, if the EC element turns to a blue color (in the colored state), combining that with a substrate with a permanent bronze hue will result in more neutral colored light passing through the window. In addition, it also changes the perception from the outside where in the colored state the windows appear to be more of the color of the outer panel (reflective or absorbative) rather than the color imparted to the EC structure by the EC element. Figure 18shows the transmissive spectrum of a TC coated fluorine doped tin oxide coated glass (surface resistivity 15 ohms/square) sold under the trade name of TEC® from Nippon Sheet Glass (Toledo, OH). Please note the different tints and the thickness of glass. These substrates could also be obtained with different surface resistivities such as 15, 10
and 6 ohms/square and lower which are useful for windows. For EC devices used for glazing that in the colored state appear blue, in some embodiments, at least one of the substrates (e.g. the one facing outside of a building envelope) should have a tint (e.g., permanent tint) such that the average light transmission in the region between 550nm to about 700nm should be greater as compared to the average light transmission in the 400 to 500nm region. The tinted substrate may be specified thicker, such as 3.2mm or greater, more may be specified 4mm or greater and is strengthened (or tempered).
[000144] One may also use a laminated substrate as one of the starting substrates but has a total thickness of greater than 4mm and has a tint. One of the laminating glass elements may have a conductive coating which will face outside the lamination region to be a part of the EC device. In the laminated substrate, the tint may come from the glass or from the lamination medium (typically a polyvinyl butyral, polyvinyl acetate or a polyurethane containing film is used in a thickness of about 0.5 to 2mm, and more generally in the range of 300 to 800μιτι). The thickness of each sheet of the glass being laminated can also be in the range of about 2.3 to 12mm, thus the total thickness of the substrate would still be greater than 3.2mm, and may be specified greater than 4mm. One may even form the electrochromic element and then laminate that to another piece of glass to obtain a stronger assembly.
Devices on Flexible Polymeric Substrates
[000145] In some cases, it is desirable to produce EC devices using flexible polymeric substrates (e.g., flexible polymeric films which are generally in a thickness of about 500 microns or less in thickness, specified at 250 microns or less) can then be retrofitted (or adhesively bonded) on existing windows., or in some cases they may
be laminated within two glass substrates. For retrofitting, these may have adhesive layer (e.g., a pressure sensitive adhesive) on one of the outer substrates, which may be protected by a release layer until the EC film is ready to be applied on the window. This adhesive and/or the substrate on which this adhesive has been applied may also have UV additives to reduce UV transmission into the rest of the device. It is specified in some embodiments to cut 90% or more, and in some embodiments, 99% or more of the solar UV energy in the wavelength range of about 280 to 400nm.0146] The polymeric substrate (or films) s may be single polymer films or multilayer film constructions to achieve better barrier properties as discussed below. Some examples of materials with better barrier properties against moisture and oxygen are polyethylene terephthalate (PET), polyethylene naphthalate,
polyacrylonitrile (PEN), polyacrlyonitrile (PAN) containing copolymers, polyvinylidene chloride and copolymers containing polyvinylidene chloride, and a multilayer structure such as Polypropylene (PP)/Polyvinylalcohol (PVOH)/Polypropylene (PP), and so forth. One may also use tie layers between various polymeric layers in a multilayered substrate to avoid any delamination. An important property of the plastics materials used are their barrier properties against water transmission and oxygen permeation, both are to be quite resistive to permeation of these materials (or the polymers should have high barrier). For example, PET, PEN, and PAN are considered to have good barrier properties against water and oxygen, whereas PP has good barrier properties against water and PVOH has high barrier properties against oxygen. For devices designed to last long the barrier properties are specified to be superior. The permeability properties at room temperature of the flexible plastics substrates used should be less than 1 xlO"17mol/(m.s.Pa) for oxygen permeability and less than 5 xlO"17mol/(m.s.Pa) for water permeability, and these
numbers may be specified less than 0.1 xlO'17 and 1 xlO'17 respectively. These can be measured using AST methods D1434-82 (for gases) and E96/E96M-16 (for water).
[000147] Further, since these devices can get hot during use, particularly under bright warm conditions, they are specified to have low activation energies, wherein their permeability increase with temperature is low. In some embodiments, the ratio of their increase in permeability from room temperature (25°C) to 65°C may be less than 3, or less than 2. The increase in permeability of the substrates with humidity should also be low, this may be specified within a factor of 2 when the humidity increases from 50% to 90%. When EC devices are made using flexible substrates they may also be bonded on to existing glass window. If the outside surface of the polymeric EC device will interact with users, and is not protected by another glass sheet, the EC device may incorporate a hard coat, or an abrasion-resistant coat, to reduce scratching. The hard coats are usually in a thickness of about 10 microns or less and may comprise inorganic oxide nanoparticles and when evaluated by ASTM method D1044 result in less than about 1% haze. Although any devices described in this disclosure may be made using flexible plastic substrate, but the devices described in Figures 5 and 6 are easier to fabricate using these substrates.
[000148] The TC's for the plastic substrates may be selected from two different categories, one where conductive oxides are used, such as doped indium oxide and doped zinc oxide (such as ITO, AZO, respectively). However, since these oxide coatings cannot be formed at high temperature on plastics, their conductivity is limited. Another way is to put down coatings which has a dielectric/metal/dielectric type of structure, the dielectric may be conductive oxides mentioned above or other materials with limited electronic conductivity but high transparency and inertness
towards electrochemical reactions (e.g., SiN). The metals used are gold, silver, and so forth. These multilayer coatings have higher conductivity.
Control and powering of EC windows:
[000149] EC devices are powered by low voltage DC power. Typical safe coloring potentials are from about 0.8V to 3V, and bleach may be carried out by shorting the devices or applying reverse potentials up to about 3V. These potentials are
dependent on the type of devices and the materials used to make them (including the type of redox dye species and the EC layers used in the device of the present invention). The devices of this invention with the redox species in the electrolyte, typically incorporate a coloring potential of about 0.8 to 2V at room temperature. At 0.8V coloration is shallow and becoming more intense with increasing potential, thus providing a gray scale capability. When using voltage as a driver one may also detect the end point and remove the voltage once the current falls below a certain level or a certain amount of charge is passed. It is usually not preferred for the longevity of the devices to keep applying a potential after the desired state has been reached.
Although one may intermittently apply the voltage to keep the device in an optical state and remove this after the current falls below a certain level or a certain amount of charge is passed, or even time the voltage application period if the device characteristics are known. All these parameters may be temperature dependent.
[000150] As the device size increases, the device kinetics slows down due to the
charge carrying limitation of the transparent conductor (or the resistivity of the transparent conductor). For most practical devices, the powering may also be done (colored and bleached) using current sources subject to a maximum safe potential. The powering safe potentials also depend on the temperature of the device and this dependence should to be established for a given type of device. Typically, lower
voltages are used with increasing temperature and higher voltages are incorporated at lower temperature for devices with redox dyes. As an example, for the devices of this invention, the maximum coloration potential at 80°C, is lowered by about 0.1 to 0.3V as compared to 25°C. Similarly, at lower temperature, 1 0eC it may be increased by about 0.1 to 0.2V as compared to 25°C to provide adequate kinetics (this is primarily due to the change in resistance of the cell, ionic movement in the electrolyte and in the electrodes and a change in redox potentials). The temperature of the EC panel or window may be measured and then a look-up table stored in the system memory is used to determine the desired powering conditions.
[000151] When one uses potential as the driver for windows then with increasing window size a step potential to color the window may cause the window to color non-uniformly during transition. That is the window will start coloring at the edges (near the perimeter busbars) more deeply and gradually the color will migrate to the center of the window. Similarly, when a bleach voltage is applied, the window may first bleach near the edges and later from the center. This is also called an iris effect and for windows it is preferred to reduce or even eliminate this.
[000152] The iris condition can be overcome by judiciously choosing the powering conditions. A voltage driving method to overcome this is disclosed. For a given device at a given temperature, a minimum voltage Vi is applied before discernable color change takes place, and V2 is the voltage at which the device is powered to achieve a desired condition. Further, had V2 been applied as a step voltage to the window (or the EC panel) for coloration while starting from the bleached state, the window would have taken time "ti" to color while showing the iris effect. Time to color means for the panel to color to 80% of the total range as measured in the center of the panel. For EC devices, this speed will decrease with increasing size, such as with
increasing distance between the edge busbars. As a first step, to reduce iris, one could use the following multistep or a ramp process; (a) apply a step of Vi, (b) apply the voltage using a linear ramp increasing at the rate of (VW /tti x f) and (c) hold the voltage at i until the end condition is reached, wherein the total amount of charge has passed or the current reduces to a certain value. The factor "f" ranges from about 0.3 to 4 to modify the time for ramp. If using f=0.3, the ramp period is 30% of the time to color when applying a step potential only. If use of f=0.3 does not reduce the iris effect to a desirable level, one can increase the value of "f" as much as four, until the desired condition is reached or may also utilize a non-linear ramp. One may also substitute ramp with a number of discrete steps. Further these conditions, ramp rates and potentials may also be changed actively with
temperature. In addition, as the device ages and its resistance changes, one may again actively measure this change and accordingly vary the powering protocols. In a section of a building where there are several windows of different shapes and sizes, which are colored at the same rate, then one can determine the condition for the slowest (largest) window, the "f" value and use that driving protocol for windows even though for some of the smaller windows the value of "f" exceeds 4. That is voltage driving condition for a set of windows in the same room or the vision area or a fa ade is carried out using the voltage-time profile of the largest window. This ensures that the windows darken uniformly and at the same rate.
0153] In the devices of this invention a substantial advantage is that during bleaching most of the charge stored in the colored state of the EC device can be removed by shorting the two opposing electrodes, which means that this discharge can take place at a controlled rate across a load to avoid iris. Figure 17 shows the potential across the two opposing electrodes of a device, coloration level and the
amount of charge (see Example 10 for device details). For those devices where a secondary (or a rechargeable) battery is used to color the device, a substantial portion of this charge may be recovered and used to recharge this battery, or recover the charge, during the bleaching operation to extend the battery life or have the option of using a smaller battery. It is desirable to recover a minimum of 20% charge during bleach, such as 40%, or 60% or more, of charge present in the colored state. In addition, the battery is also connected to an alternative power source as described below. The power storage source, the battery may also be substituted with a high capacity capacitor(s) or super capacitors. In some embodiments, a series of capacitor/supercapacitors are used to provide redundancy in case one or more of the supercapacitor fail.
[000154] Since a building structure (e.g., a skylight, roof, or windows for a particular room, or a building fa ade) may constitute of several EC window units which will work in unison, or controlled by a common signal, one may use an electronic system so that when the potential is applied for coloration or during short intervals of bleaching the power is applied so as the windows are connected in "electric parallel", when bleaching under short or very low potentials, these windows are automatically connected in "electric series" to amplify the voltage so as to eke out more
recoverable charge.
[000155] Figure 16 illustrates a smart window control according to one embodiment for control of a window as in Figure 2 and illustrates the integration and operation of the EC device and controller/power source sub-system. In Figure 2, a smart window 900 that includes the EC device 910 and the power controller 930 is shown. The frame 920 may include solar cells to harvest energy during daylight or from indoor lighting, or thermoelectric devices capitalizing on the temperature differences
between the indoor and the outdoor surfaces of the window or between the window panes, piezoelectric devices converting deformation on windows to electricity caused by wind or RF antenna and circuitry to harvest energy from RF electromagnetic waves. In EC devices, solar cells may be used which may face inside or outside the building or one may use multiple solar cells in a window where at least one faces inside and at least one faces outside. In case the harvester is an AC type device then rectifiers and appropriate circuitry will likely be incorporated from AC to DC conversion.
0156] Figure 16 illustrates a high-level block diagram of the power controller 1030. Vin is the voltage generated by the solar cell or any other harvesting circuitry 1020. The DC-to-DC converters either up-convert or down-convert voltages between the two different stages of the device: 1) from 1020 to the power storage unit (rechargeable battery or a supercapacitor), 2) from the power storage unit to the EC device 41010. The controller 1030 can be in any area around the perimeter of the window and may be wired or wireless. The value of Vout can be regulated to depend on the outdoor temperature and the desired degree of coloration incorporated in the colored state. One may also determine the state of coloration of the EC device without integrating an optical sensor by reading the open circuit potential of the EC cell and inputting this in the controller. In case there is a change in this potential over time (due to self-discharge of some of the stored charge in the device with
concomitant loss of coloration), the EC window could be powered periodically to bring the state of coloration to the desired value. For example, it is difficult for the eye to discern a change in the transmission which is about 20%, or about or lower than 10% change in transmission of the set value. For example, a window colored to 10% transmission will appear almost the same to an eye when its color changes by
20% of this transmission value, where the change is to 12% transmission. Furthermore, the user can control the window in different ways: i) manual control to transition the color to desired shade/transparency, ii) wireless control using computing or mobile devices, iii) cloud control by user, home automation services, or other entities, iv) triggered by another event such as turning on/off and audio/visual device or an alarm system, such as a wake-up alarm), v) automatically controlled by home automation system. For instance, each window may be mapped to the sun exposure timing, outdoor luminosity (which may change due to cloud cover) and outdoor temperature to automatically select the EC device state to optimize and balance between the comfort and or energy efficiency. More details on this is provided in the priority documents included by reference herein.
[000157] The state of coloration of a variable transmission window that utilizes EC panels can be electronically checked by checking the potential between the two opposing conductive coatings (transparent conductors) that make up the EC device. This helps with positively identifying the state so that appropriate command may be applied from the control system to change its state. Knowing the state helps to calculate the energy being saved by keeping the window in that state which is helpful in monitoring the economic impact of these windows (see co-filed application referenced earlier for more details on this issue and how one can adopt this idea for a subscription model to reduce the impact of capital cost on the installation of such systems).
[000158] To ascertain proper functioning of EC devices, one can monitor their l-V (current-potential) characteristics and corrected for panel temperature conditions. When powering is done using a voltage-time profile, one can monitor the current consumption. Too small of a current (as compared to a nominal initial value) may
indicate a resistance developing and the panels may not be coloring deep and/or fast enough, and too much of a current may indicate a short which may also lead to panels not coloring deep or may color non-uniformly. For an EC or a PV panel, the electrical characteristics may be sensed and monitored remotely by a company responsible for their maintenance, and if a panel malfunctions a technician may be dispatched who could service and replace the appropriate panels. If an EC cell develops strong cosmetic defects then it also should be replaced, but usually the electrical characteristics which are easier to monitor remotely do contain signals when the EC panels do not function properly. In addition to the electrical
characteristics one could also take images of the panel (or windows) at frequent intervals and compare them with previously taken images (optical monitoring). This is done using a camera located inside the building.
0159] For field installed EC panels, it is desirable that a thermistor, a capacitor or any other temperature sensor is placed (printed or bonded) on the surface and near one corner or in two (or more) positions which are at diagonally opposite corners to measure temperature of the panel. This may be placed on surface 1 or 2 (See Figures 12 and 13), although surface 2 is more preferred of the two. Multiple positions of the sensor may be incorporated in case part of the panel is shaded and may be at a different temperature. These may be wireless sensors and may derive power from a solar cell integrated with them, via RF powering, or use of thermo-electric
convertors. The electrical driving of the EC panel may be carried out at an average temperature obtained if multiple sensors are used. In an embodiment, temperature for which the driving parameters are used are those established for the highest temperature reading that is obtained from the panel, the highest temperature being recorded by any of the sensors on that panel, so that no part of the panel is damaged
by aggressive driving conditions. For large installations where several EC panels face the same direction, one may put the temperature sensors only on some of the panels to get an estimate of an average temperature profile, and again electrical driving of the EC panel may be carried out at an average temperature, but the driving be done under the conditions established for the highest temperature being experienced at that time. In case the highest temperature exceeds a point (safe temperature) where any electrical driving will damage the EC panels, then the panel is simply maintained in that state, wherein no electrical impulses are applied or no electrical driving is done until the temperature reaches, or drops to within safe limits.
[000160] For these considerations tables and charts are developed for the EC panels' performance which considers their construction, their size, temperature, and powering profiles and establishes not to exceed values, e.g., potentials, total charge, current, temperature, and so forth. These values can then be used to determine if an EC panel has failed, and servicing may be as illustrated in Figure 7, a decision flow chart for EC panels to self-identify a need for servicing. This also provides
troubleshooting to see of the problem is caused by shorts in the busbar and/or the circuitry and address them appropriately.
Integrated Glass units and Solar cells
[000161] The solar cells in a building may be integrated in several ways. Since these windows consume low power, tiny solar cells may be integrated with window frames that provide limited energy only for changing the state of windows and provide a retrofit solution for buildings which do not have wiring in the window area. One may also mount the solar cells on the window frames that face the interior of the building. These could convert the illumination available inside the room or the building to trickle charge the battery even when it is dark outside. This solution
works well for smaller installations such as residential and businesses where there are isolated windows or smaller installations.
0162] Buildings with larger glass installations, such as large atria, towers, and so forth.) one may integrate the solar cells and the variable transmission windows in a different way. Solar cells provide power to change the transmission of the windows and to supplement power used by the building for other functions to reduce its environmental footprint. For buildings with predominantly glass exteriors, the EC elements are typically located only in the view (vision) area, and may be even be limited to windows or window areas that are within the visual reach of the occupants, the height may be any depending on the size of the room or enclosure, typically a typical average height of a building floor to about 4 meters, of which about 60 to 70% is the vision area and the rest goes in ceilings, floors and duct work. From outside, the latter region (40 to 30%) between each floor is covered by a spandrel. The faςade panels and spandrel areas may contain solar cells located behind a glass sheet. These solar panels may be completely opaque, wherein the light falling on these is harvested to provide maximum electrical power. The opaque panels used in the spandrel or any non-transparent areas have a higher efficiency in converting light to energy (e.g., it is desired for these opaque panels to use photovoltaic (PV) panels with an efficiency of 10% or greater as measured under standard conditions, e.g. using methods suggested by International Electrotechnical Commission (lEC), lEC 61853-1, 2011 Ed-1- Photovoltaic module performance testing and energy rating). The solar cell panels allowing partial light transmission if used in the transparent areas of the window have less than 10% efficiency. This is because part of the light passes through these panels is not harvested.
[000163] Partial light transmission panels are created in one of two ways. In the first method, it is done by using opaque solar cells as described earlier, but they are placed in a pattern where part of the area is covered by them and part of the area is transparent giving an appearance of a mesh. Typically, when this is done using a panel which has a series or a line of opaque solar cells covering a width of about 5mm or less along with a clear spacing between these lines which is about 10mm or more in width, for example see PV-IGU-150 from Solaria. The patterns are typically opaque solar cells arranged in a lines or mesh. Another way is using thin film solar cells (such as those based on amorphous silicon) where the solar cell stack has a certain transparency. Due to high cost and increased complexity, the thin film solar cells are generally not combined with variable transmission panels and may be used by themselves in those areas of the buildings where variable transmission may not be incorporated but it is still preferred for some sunlight to come in e.g., stairwells, transoms, and so forth. Example of solar cells integrated with glass may be found at Solaria Corporation (Freemont, CA) and at Onyx Solar (New York, NY).
[000164] An example of integration of EC panels and solar cells in a multi-storied building with predominantly glass exterior is shown schematically in Figure 11. This shows a four-storied building with predominantly glass exterior. The vision area is the clear window area for that floor and the spandrel area is what hides the floors, ceilings, ducts, utilities, and so forth, between the floors. The facade may be glass or concrete or any other type of construction material. One can use EC devices for the vision area or/and on the doors. The solar cells may be deployed in the spandrel area or even in the facade if that is made of glass.
[000165] Figures 11-13 describe the use of solar cells in the spandrel/facade area.
Since these areas are opaque, wherein solar panels are designed to harvest
maximum amount of sunlight to convert that to the electrical power. The panels comprising solar cells are constructed in an IGU type of format as shown in this Figure using glass sheet 550 and 562. With a gap 560. In some embodiments, at least one of the surfaces 2 or 3 is coated with a low-e coating. The gap is about the same as for the IGU unit with an EC panel described above. Generally solar cells are prefabricated and placed between two plastic films (details not shown in the figure) and then laminated using glass sheets 562a and 562b. It is desirable to have the total thickness of this IGU to be similar to that of the EC IGU for ease of installation and more uniform appearance. When the solar cells are used in the opaque areas such as spandrel; these may be packed densely so that most of the light hitting these panels is employed to generate power.
0166] The crystalline solar cell panels are high efficiency, long lasting and if packed densely will be opaque towards light transmission (e.g., see PowerSpandrel - 350 from Solaria As mentioned above glass panel 562b may have some reflective properties (similar to EC IGUs) so that the appearance of the glass from outside looks similar in both the vision area and the spandrel. However, use of colored or partially reflective glass cuts down on the light being harvested by the solar cells, and thus the power produced is lowered. In case the building design allows one to have different exterior appearance for the spandrel and the vision areas, it is best to have a highly light transmissive glass for 562b. Typically these are low iron glasses (with iron content lower than) so that absorption of light is low. Some examples of low iron glasses are Starphire™ from PPG (Pittsburgh, PA) and Optiwhite™ from Pilkington (St. Helens, UK). The iron oxide content in low iron glasses is typically lower than about 0.02%.
[000167] The thickness for 512a and 512b in the EC panel (Figure 12) could be similar, to the thickness 562a and 562b (e.g., 3.2mm or more so that these can be strengthened or tempered), in one embodiment thickness of 502 (FIG 12) is the same as 550 of Figure 13.
[000168] Figure 17 Shows experimental data on voltage, coloration and charge
consumption of an EC element produced by an embodiment of the present invention;
[000169] Figure 18 illustrates spectral characteristics of soda-lime glass substrates coated with transparent conductors corresponding to an embodiment of the present invention.
[000170] Figure 19 illustrates an EC device having a multilayer film with an
electrolyte and dye containing layer (ferrocene-containing layer) prior to lamination together with substrates according to embodiments of the present invention.
Examples
Example 1:
[000171] Tungsten oxide containing lithium oxide was deposited by dip coating from a solution on a TEC15 substrate (obtained from Nippon Sheet Glass, Toledo, OH). The substrate size was 9.4cmxl3.3cm. The procedure to deposit tungsten oxide coating is described in US patent 6373618 (Example 1). The thickness of the finished coating was about 400nm. A SICL coating of poystyrenesulfonate (PSSNa, molecular weight lmillion) was deposited by spin coating from a 50:50 (by volume) watenethanol solution containing 3.5% by weight of the polymer. The coated substrate was heated to 110°C for 2 hours to drive off the solvent. The coating thickness was about 500nm.
[000172] The tungsten oxide and the SICL coatings were then etched from the perimeter area (about 5 mm in width from three sides and about 10mm width on one of the long sides) of the substrate. A cell was fabricated by dispensing an epoxy around the perimeter of one of the substrates. This epoxy contained 300 micrometer (diameter) spherical glass beads. The epoxy was dispensed on the etched area. The second TEC 15 substrate was lowered onto this one while providing an offset of about 5 mm along one of the long edges. This substrate had two 1.6 mm diameter holes along its diagonal about 10 mm away from these comers. Care was taken that the epoxy touched the tungsten oxide coated substrate in the etched area. The spacers provided a separation of 300 micrometers between the two substrates, which would be the thickness of the electrolyte.
[000173] The epoxy was cured at elevated temperature to yield an empty cavity. The cavity was filled with an electrolyte by injecting through one of the holes on the cell substrate. The electrolyte was made using a plasticizer containing 80% propylene carbonate and 20% l-Butyl-3-Methyl Pyrrolidinium
bis(trifluoromethanesulfonyl)imide (BMP). To this was added lwt% water, 0.025M LiN(S02CF3)2 (LiNTF) 0.025M ferrocene and 2wt% of Solef 31508 (obtained from Solvay, Princeton, NJ). The holes were then sealed with Teflon plugs followed by glass cover slides which were bonded by a UV curable adhesive and a silane. A spring clip busbar was attached to each of the two substrates along the long edge of the device to make electrical connections. The active area of the device was about 12cm x 7.6cm.
[000174] A potential of 1.3V was applied (with the EC coating as negative) to color the cell. The cell colored from 71.5% to 10.1% at 550nm. When the cell was left in the open circuit in the colored state. Its transmission changed from 10.1 to 11.2 in 18
hours. After coloration when the cell was shorted, it had bleached completely when observed after 20 minutes.
Example 2:
[000175] A cell was made as in Example 1 using smaller substrates with an active area of 36 sq. cm of about a square shaped and instead of an epoxy seal, the spacing was determined by a polyimide tape and the substrates were held together by a clamp, however, rather than ferrocene, the electrolyte contained in similar molarity 2,2,6,6-Tetramethyl-l-piperidinyloxy (TEMPO).
[000176] The cell colored at 1.5V from 78.4% to 14.5% at 550nm in five minutes.
Another cell which was identical but with having no SICL layer, or no PSSNA layer, and no water added to the electrolyte, the cell changed from 80% to 22.1% under similar conditions. In another cell without SICL layer but with water in the electrolyte a change from 80.5 to 21.1% was seen after 5 minutes of applying 1.7V and for the same cell the transmission at 550nm was 10.4% after 5 minutes at 2V. In yet another cell, TEMPO was replaced by 4-Hydroxy TEMPO benzoate and contained water in the electrolyte (cell without SICL layer). This cell changed from 78.6% to 23.1% at 550nm at 1.5V.
Example 3:
[000177] A cell was made as in Example 2, however, the electrolyte contained a
donor-acceptor dye with a ferrocene-viologen structure rather than ferrocene and the electrolyte also had 1% added water. The Dye was 4,4'-Bipyridinium, l-(4- ferrocenylbutyO-l'-methyl-, salt with NTF anion.
[000178] The cell colored at 1.3V from 77.2% to 8.8% at 550nm in five minutes. After coloration when the cell was shorted, it had bleached completely when observed
after 20 minutes. A similar cell was made with no water in the electrolyte and it colored to 23.7% under similar conditions.
Example 4:
[000179] A cell was made as in Example 3, however, the SICL layer was a 200nm thick LiAir-4. The LiAIF4 layer was deposited by thermal evaporation. This was done on an Angstrom EvoVac deposition system. The deposition of LiAIF4 was achieved by using two precursors LiF (Alfa Aesar, 99.5%) and AIF3 (Alfa Aesar, 99.5%). These precursors were individually loaded into tantalum evaporation boats. The deposition rates for LiF and AIF3 were set to 0.6 A/s and 1.4 A/s, respectively. The electrolyte contained water, the donor accepter dye was the same and in similar concentration as in the earlier example, and the Solef content was 4 wt%.
[000180] The cell colored at 1.3V from 71.7% to 15.6% at 550nm in ten minutes. The device consumed 20.7mC/cm2 (active area) in 10 minutes. A similar cell was made but without water in the electrolyte, this colored from 72% to 11.7% in 10 minutes under similar conditions, the peak current for the device was 4.6mA.
Example 5:
[000181] A cell was made as in Example 2, however, the electrolyte contained
ferrocene and the EC coating further contained molybdenum oxide (along with tungsten oxide and lithium oxide). The atomic ratio of Mo: W was 1:10. The cell colored at 1.3V from 71.7% to 5.4% at 550nm in about a minute. When shorted, the cell bleached in about 10 minutes. After coloration when the cell was left in the open circuit mode it bleached in 17 hours to about 19.5%, all at 550nm.
Example 6:
[000182] A cell was made as in Example 4, but the electrolyte did not contain any water. This cell colored to 11.6% at 550nm at 1.3V.
Example 7:
[000183] A cell was made as in Example 2; however, TEMPO was replaced with
0.05M of Lil. The cell colored from 78% to 29.9% at 550nm when powered using 1.3V for 10 minutes. It bleached completely when a potential of -0.7V was applied for 510s. Another cell was made with similar electrolyte composition but with no added water. The cell performed like the one with water with the bleach time extended to about 654s.
Example 8:
[000184] A cell cavity was made as in Example 4, however, the redox in the
electrolyte was similar to in Example 7. The electrolyte had no water and had O.lMLiI and 0.1M polyvinyl pyrrolidone (PVP). PVP was K17 obtained from BASF (Florham Park, NJ), and the molarity was calculated based on the molecular weight of the monomer. The cell colored from 79% to 39.7% at 550nm when powered using 1.3V for 5 minutes. The cell bleached completely when a reverse potential of 0.7V was applied for 746s.
Example 9:
[000185] A cell was made as in Example 1, where the SICL layer was a 150nm thick LiAIF composition and was deposited as described in Example 4. The thickness of the EC coating was 450nm and the electrolyte contained the donor-acceptor dye (as described in Example 3) instead of ferrocene. Further the electrolyte had 4 wt % of the Solef polymer and did not contain added water.
[000186] The cell colored from 76.1% to 6.8% at 550nm when powered using 1.3V in 5 minutes and bleached completely at -0.5V in 12 minutes all at room temperature, when the cell was left in the open circuit mode at 80C its transmission changed to 16.6%. The cell was cycled at room temperature for 53 cycles (1.3V to color for 300s
and -0.5V to bleach for 1,000s) followed by 105 cycles at 80°C (1.3V to color for 120s and -0.5V to bleach at 480s). The transmission of the cell in the colored and the bleached state and kinetics when tested at room temperature after cycling was unchanged as compared to before cycling.
Example 10:
[000187] A cell was made as in Example 1, with a few differences. The thickness of the EC coating was 450nm and the electrolyte contained the donor-acceptor dye (as described in Example 3) instead of ferrocene and had 4wt% of Solef polymer.
[000188] The cell colored from 76.9 to 6.2% at 550nm when powered using 1.3V and bleached in 430s when shorted. In another experiment using the same cell, the coloration voltage of 1.3 was applied for predetermined times and the cell transmission, charge consumed and the open circuit potential was recorded. The same was done when the cell was bleached by shorting in steps and almost identical amount of total charge was recovered. The transmission data while coloring was converted to optical density using the bleached state transmission as 100%. The integrated charge after each step. When optical density was plotted as a function of integrated charge a linear curve was obtained (see Figure 18 which shows the cell potential and optical density as a function of charge). Data is compiled in Table 1.
120 10.9 0.85 1.15 23.3 79%
180 8.3 0.97 1.21 26.2 89%
300 6.2 1.09 1.27 29.5 100%
[000189] The cell was colored to 6.9% and left in an open circuit mode in the colored state. The cell bleached to 7.4% after 30 minutes at room temperature, as seen this change was less than 2%, wherein the colored transmission after 30 minutes was lower than, within, 8.9% (6.9%+2%) after 30 minutes. The amount of charge leaked causing this change was estimated from the change in optical density in Figure 8. The average leakage current in the above period to cause this change in optical density, or transmission, was estimated as 0.70pA/cm2.
Example 11:
[000190] An example of a custom surface modification of single walled carbon
nanotubes with ferrocene carboxylic, incorporates a Single Walled Carbon
Nanotube structure (SWCNT) obtained from "Cheap Tubes" (Grafton, VT). The characteristics of the SWCNT are provided in Table 2.
Table 2
Purity 99%
Outer diameter l-4nm
Length 3-30 microns
Surface modified -NH2 Primary
amine
Functionality N-H, 0=C-N-H
[000191] These SWCNT's were further surface modified to attach an anodic ferrocene dye by reacting the primary amine with ferrocene carboxylic acid. To a 200ml round bottom flask fitted with a stir bar and condenser was added 60 ml of propylene carbonate (Ferro Corporation, Baton Rouge, LA) and 233mg of ferrocene carboxylic acid (Sigma Aldrich, Chemical Company Milwaukee, Wl). This mixture was heated to 80°C to form a complete solution.
[000192] To a 50ml beaker were added 50mg of SWCNT and 17ml of
propylene carbonate and dispersed using an ultrasonic probe at a power output of 64W for 5 minutes with a cycle time of 5 second on and 5 seconds off. The dispersed SWCNT's were added to the dissolved ferrocene carboxylic acid solution and stirred at 80°C for 2 hours to form the salt. The mixture was then heated to 120°C for 24 hours to form the amide with the liberation of water. Cooled to room temperature and filtered through a 0.45-micron nylon filter and washed sequentially with 50mls each of propylene carbonate, ethanol, and acetone and dried in a vacuum oven at 60°C for 5 hours. Weight of product was 91.1mg corresponding to a loading of 18Wt% ferrocene carboxylic acid on the SWCNT's.
Example 12:
[000193] An example of a modification of a single walled carbon tube structure with ferrocene carboxaldehyde, incorporates SWCNTs obtained from "Cheap Tubes," as described in Example 11 hereinabove, and reacted with ferrocene carboxaldehyde (Sigma Aldrich, Chemical Company Milwaukee, Wl) as follows. To a 125ml round bottom flask was added 60mls of anhydrous ethanol and 420mg of ferrocene carboxaldehyde. The mixture was stirred at room temperature to form a complete solution. To this was added 63.3mg of SWCNT and using an ultrasonic probe at a power output of 80W for 5 minutes with a cycle time of 5 second on and 5 seconds off to disperse the carbon
nanoparticles. The dispersion was stirred for one hour at 25°C and 410mg of sodium cyanoborohydride (Sigma Aldrich) added and the dispersion stirred for 24 hours at room temperature. The dispersion was filtered through a
0.45micron nylon filter and washed sequentially with lOOmls each of deionized water and ethanol and dried in a vacuum oven at 60°C for overnight. Weight of product was 74mg corresponding to a loading of 17Wt% ferrocene on the SWCNT's. IR analysis of the product showed the characteristic absorption peaks for ferrocene at 1405, 1060, 814 and 480 cm"1.
Example 13:
[000194] For preparation of electrolyte film containing ferrocene modified SWCNTs, a solid black electrolyte material was prepared as follows; 3.36g of polyurethane PUL446-107 (obtained from Huntsman, The Woodlands,TX) was added to a flask and 33.6mls of anhydrous tetrahydrofuran (THF). This was stirred at 60°C for two hours to form a clear colorless solution. 0.784ml of the ionic liquid,l-butyl,l-methylpyrrolidinium bis(trifluoromethanesulfonyl)imide (lolitec, Germany), 3.136ml of propylene carbonate (Sigma Aldrich) and
0.0306g of lithium trifluoromethanesulfonate (Sigma Aldrich) were added and the mixture stirred 15 minutes. To this was added 1.6mg of the ferrocene modified SWCNT' as described in Example 11 above. This was sonicated using an ultrasonic probe at a power output of 68W with a cycle time of 5 second on and 5 seconds off in four 15 minute intervals with cooling between each interval. To remove the THF, the solution was heated under vacuum in a three-step process as follows; the solution was first heated to 65°C for 30 minutes followed by 75°C for one hour and finally 95°C for 2 hours. This produced a black rubbery solid material.
Example 14:
[000195] Preparation of an electrolyte film without modified SWCNTs includes preparation of a slightly opaque solid electrolyte, as described in Example 13 hereinabove, with the difference that no ferrocene modified SWCNT's were added and no sonication was used. The solid electrolyte was placed on a sheet of polyester on a heated hot block at 125°. Once it was softened, 300-micron spacer beads (Novum Glass LLC, Rolla, MO) were sprinkled on top. Another sheet of polyester was placed on top and using a pressure roller the material was spread out into 300 microns thick. Cooled to room temperature and the polyester sheets could be removed to give a clear colorless free-standing film. Example 15:
[000196] Preparation of an EC cell using a combination of solid electrolytes prepares an electrochromic window using a combination of the electrolytes prepared in Examples 13 and 14 hereinabove. The EC window was composed of TEC 15 glass with a 360nm coating of lithium oxide doped tungsten oxide (EC layer) prepared as described in US Patents 5,216,536 and 6,266,177, laminated to another piece of TEC15 glass using a bi-layer of 300 microns of
the clear electrolyte (Example 14) and 60 microns of electrolyte containing the ferrocene modified SWCNT's (Example 13). One may have also formed a multilayer film first within the electrolyte and the dye containing layer
(ferrocene containing layer) prior to their lamination with the substrates. Schematics of such a device structure is illustrated in FIG. 19.
0197] The EC window was prepared by first placing 0.5g of the solid black electrolyte containing the ferrocene modified SWCNT's on the TEC 15 substrate and heating to 125°C. Once the electrolyte was softened it was pressure rolled into a 60-micron film using a stainless steel draw down rod. This film was thin enough that it appeared clear when placed on top of the TEC 15. A polyester protective sheet was placed on top and on top of this a second heating block at 125°C. This sandwich was kept at temperature for 15 minutes and then cooled to room temperature. The top polyester sheet was removed by pulling, exposing the electrolyte on the TEC 15 substrate. A sheet of the electrolyte prepared in example 4 was cut to the same size as the electrolyte on the TEC 15 substrate and placed on top of it. This was placed on the hot block at 125°C with the electrolyte side facing up. The lithium oxide doped tungsten oxide coated TEC 15 substrate was placed slightly offset on top pf the electrolyte with the tungsten oxide side facing the electrolyte. A second heat block at 125°C was placed on top and the two substrates were laminated by the two electrolytic layers (on of which had the ferrocene dye). The laminate was kept at 125C for 30 minutes under pressure. The system could cool to room temperature and metallic clip on busbars were applied to each electrode.
0198] The cell was colored at 2.5 volts (negative to the tungsten oxide electrode) and at 550nm the cell went from an initial % transmission of 68 to 14 in 25 minutes. Applying a reverse potential of -1.3 volts the cell went from 14%T to 68%T in 8 minutes.
Conventional Construction Methods and Configurations
Construction Method 1:
[000199] There are several methods for constructing EC devices, each with its own benefits and shortcomings. Figure 1 illustrates the side-view of one type of smart window design. A first type of conventional construction is formed on a transparent substrate, such as glass or plastic, substrate. For clarity, the following discussions consider a glass substrate. The substrate is coated with several layers of materials to produce the complete electrochromic device; the entire EC device is on one substrate. The middle layers are then laminated with another substrate to protect the coatings that form the EC device. The glass substrate used in these EC devices for windows are designed to withstand high-temperatures due to absorption of solar radiation that may be incident on the substrate in situ. The substrates prior to the deposition of the EC layer are heat strengthened or tempered so as not to crack under typical or anticipated weather conditions.
[000200] In fabrication and processing, the substrate is first coated with a
transparent conductor (TC) coating. The substrate may be tempered before the deposition of the TC layer, or after, if the TC layer is deposited during glass sheet formation then substrate tempering is done with the TC in place. In some examples, the resultant surface resistivity is approximately 1 to 20 ohms/square (or lower), with a thickness of approximately 50 to 500nm. The TC coating may be a single layer or multi-layer, or may be implemented as a multiple layer stack, such as a 3-layer stack where the central layer is a metallic layer (e.g., gold, silver, nickel and their alloys) and sandwiching layers are metal compounds such as oxides, nitrides and
oxynitrides. The last metal compound layer on top of the metallic layer is conductive. Some of the materials used for transparent conductive coatings are indium tin oxide (ITO), aluminum doped zinc oxide (AZO) and fluorine or antimony doped tin oxide and doped ruthenium oxide and nitrides and oxynitrides of tantalum and titanium. In some examples, to increase the conductivity of the TC, thin conducting lines (such as lines of metallic conductors that are approximately 100 μηη wide and less than 10 microns thick) are deposited and then covered with the transparent conductive materials listed above. In some examples, the substrate glass is pre-coated with a TC while being made on float-line (e.g., fluorine doped tin oxide) such as TEC™ glass available from Pilkington in Toledo, OH or SUNGATE™ from PPG in Pittsburgh, PA). Such TCs may provide costs savings, while remaining highly durable. Additionally, the substrate and TC layer may be heat-strengthened or heat-tempered with these coatings in place.
0201] According to this process, the TC layer is followed by a primary
electrochromic layer. Some of the most often used layers are porous coatings containing tungsten oxide which color cathodically. This means that these materials color when they are reduced. Typically, these coatings are doped with one or more other metal oxides to provide one or more of several attributes such as cyclic and/or UV durability, change in color, change in coloration potential, change in speed of ion intercalation, and so forth. Some of the common dopants for tungsten oxide are one or more of alkali metal oxides (e.g., lithium oxide, sodium oxide, potassium oxide), nickel oxide, titanium oxide, vanadium oxide copper oxide, cobalt oxide, chromium oxide, niobium oxide and molybdenum oxide. These materials exhibit cathodic coloration, which means that they darken, or color, on injection of ions (e.g., protons, lithium, sodium, potassium, and so forth), referred to as ion intercalation. Typically
for cathodically coloring doped tungsten oxide, the mole percentage of the other oxides may vary between 1 to 40% and the rest being tungsten oxide. Of this the mole percentage of the alkali metal oxides in the doped tungsten oxide may be up to 35% and the other metal oxides are typically less than about 20%. The thickness of the electrochromic layer is generally between 300 to l,000nm. This layer is then optionally intercalated with extractable lithium. In some cases, as described below the counter-electrode is intercalated or both layers are partially intercalated. Those tungsten oxides which color to a more neutral color (rather than deep blue) are often desired for EC window applications, and such color changes are implemented by selection of proper dopants. The color of the EC panels can also be manipulated by varying the thickness of the various layers making up the EC stack (interference effects) and/or by also choosing an electrochromic electrode of a different material as a counter electrode that colors in a complimentary fashion to the main
electrochromic layer but in a different region of the visible spectrum.
[000202] The primary electrochromic layer is followed by one or more ion conductive layers. Usually these are lithium ion conductors. These comprise lithium containing compounds such as nitrides, oxides, fluorides, phosphides and combinations. Some of the specific materials are lithium oxyphosphonitride (LIPON), Lithium aluminum fluoride (LiAIF), lithium niobate, lithium aluminum silicate and lithium β alumina, and so forth. These have an ion conductivity which is below 10"8 S/cm at room
temperature (e.g., at or below 10"6 S/cm) and have sufficient ion conductivity and stability in the operations range of approximately -40 to 90°C.
[000203] This layer is then followed by a counter-electrode. The thickness of this layer is in the range of 200 to 800nm. This layer may also possess electrochromic properties, wherein the EC properties are complimentary to the primary EC layer,
which means when the primary EC layer colors due to reduction (or electronic induction of lithium ions and electrons) then this layer colors upon oxidation, or the electronic removal of lithium ions and electrons. Typical counter-electrode layers are nickel oxide and doped nickel oxides, such as when mixed with other one or more metal oxides, iridium oxide and doped iridium oxide and doped titanium oxide.
Although a variety of metal oxide may be used as dopants, some of the dopants in nickel oxide are lithium oxide and tungsten oxide, where typically tungsten oxide is about 20-30 mole % of Nickel oxide. Dopants for titanium oxide are vanadium oxide and cerium oxide. After the deposition of the counter-electrode, the entire substructure may be heat treated to 90 to 200°C to stabilize and form robust interfaces. As mentioned earlier the counter-electrode layer is then reduced fully or partially by the introduction of lithium ions.
0204] Finally, to complete the device this layer is capped with another
transparent conductor layer using materials as discussed earlier. To protect this stack from the environment this may be laminated or sealed with another sheet of glass (which may also be tempered or heat strengthened) or plastic using a soft polymeric material and sealed at the edges. Not described here is deposition of busbars and attachment of electrical conductors to the two transparent conductors so that these windows can be powered as there are a variety of methods and designs for such construction. Suffice it to say that the glass needs a power source, and such power source is provided via the conducting elements of the smart glass. These EC devices are then assembled into windows in an integrated glass unit (IGU) with another glass substrate which has a low-e coating. A large expense in this design and installation is wiring the windows to provide power, as well the ability for a user to control the completed in-situ smart window. These devices have many thick oxide layers with
almost all with multiple metal oxides, along with pre-intercalation step requiring thermal diffusion (or reduction by introducing lithium). The equipment to conduct this is highly tailored, expensive and has slow throughput. Thus, the use of expensive capital equipment employed to manufacture such EC devices is not efficient.
[000205] In operation, a voltage (the coloration potential) is applied across the two electrodes (the two transparent conductors). The coloration potential is the voltage applied across the EC device and its value is a function of the desired change in at least one characteristic of the glass. Application of the coloring potential provides power to the smart glass and starts the process of ion intercalation. In the present example, the ions are inserted into the primary EC layer; such ions in this example are lithium ions. The ions are injected through the primary EC layer, such as in a doped tungsten oxide layer and are simultaneously extracted from the counter- electrode. These ions travel through the bridging ion-conducting layer. This process of ion intercalation through the ion conducting layer results in darkening or coloration of the device. For bleaching the device, the polarity is reversed to extract lithium ions from the EC layer and transport them via the ion conducting layer back to the counter-electrode.
[000206] The significant disadvantage is the cost as discussed above, too many layers (steps), slow process and use of very expensive equipment. Another disadvantage is low yield, as the process involves many steps, and one does not know if the device is functional until the very end of the process.
Construction Method 2:
[000207] In the second type of conventional construction, an EC device uses
materials similar to those described in Example 1 for the TC materials and
construction, EC layers and the counter-electrode structures; however, their fabrication is quite different. In this example, the EC device starts with two
transparent substrates (glass or plastic) and each is coated with a TC layer(s).
Optionally, one or both substrates may be pre-coated with TC layer(s). The
substrates are usually heat strengthened or heat-tempered. The advantage of these types of devices is lower capital cost, both substrates may be pre-coated with inexpensive transparent conductors and since s the two substrates are processed independently until they are combined with an electrolyte, one may use different processes for coatings, thus overall such devices end up being lower in cost as compared to the ones described in the earlier example.
0208] After application of the TC coating, the process applies an EC layer to only one of the substrates. A counter electrode layer is applied to the other substrate. The counter-electrode layer may also have EC properties. This means that when the EC layer colors, the counter electrode also colors simultaneously, and when one layer bleaches then the other also follows accordingly. In other words, if for example, the EC layers colors cathodically or upon reduction then the counter electrode colors anodically or upon oxidation. Complimentary coloration results in deeper tinting for a given amount of charge or power consumed. The process then reduces (extracts ions from) the layers on one of the substrates, or partially reduces both substrates. Reduction may be done chemically, or electrochemically by intercalating lithium ions. With the coatings facing each other (facing inwards) these substrates are assembled with a spaced apart parallel gap; the parallel gap is either filled with a polymeric electrolyte or the substrates are laminated together using a sheet of a polymeric electrolyte. The perimeter is sealed, allowing places for placement of busbars and electrical connections to the conducting portions of the smart window. Electrical
conductors are then coupled to the smart window. The busbars may also be deposited on the conductive substrates prior to the deposition of the other coatings. As an alternative, the coatings on the substrates are assembled to form an empty cavity into which a fluid is introduced to reduce at least one of the electrodes; after which the fluid is removed and the cavity is filled with electrolyte. In some examples, the reducing fluid itself forms the electrolyte (e.g., see US patent 6,373,618). The EC coatings and the counter-electrode layer may also be optionally coated with ion conducting layers as described above before they are assembled.
[000209] The electrolyte layer of example 2 is an ion conductor. This is a polymer- containing electrolyte with one or more of various additives, such as an ion
conducting salt (e.g., a dissociable lithium salt such as UCI04, Li CF3S03/ LiBF4, Li N(S02CF3)2, LiN(S02F)2, and so forth), UV stabilizer, heat and light stabilizers, plasticizer, and so forth. In some cases, water and/or acids may also be optionally added in small amounts. In some examples, the acids do not exceed approximately 0.1 based on the electrolyte volume, which is typically 0.02M or less. For windows, the thickness of such electrolyte layer is typically in the range of about 100 to about 2,000μιη, and may be specified as 300 to Ι,ΟΟΟμητι. For smaller devices, such as automotive rearview mirrors this gap could be in a range of about 10 to 200μηι. The second type of EC devices are also expensive as they may incorporate a counter- electrode layer; the reduction of layers is difficult and may incorporate additional treatments, wherein the reduced coatings are to be very carefully handled in inert atmosphere.
[000210] The above formed EC devices are then combined with another substrate as above to form an IGU unit and mounted in building windows as described earlier. The present invention provides embodiments to minimize the impact of greenhouse
emissions on the environment by providing energy control for buildings allowing reducing in peak electrical demands on lighting, cooling and heating while providing privacy through simple controls. These methods and apparatuses reduce the energy incorporated for control of smart windows by providing memory to the smart window through materials and configurations. These embodiments ensure
fabrication of low cost, high performance and durable devices. This is important for the technology to be widely disseminated for use in building and transportation which are highly price sensitive. These embodiments enable the window to maintain a coloration state without the continuous power application of conventional smart windows. Similarly, a manual switching may be used to return the window to a default coloration state. This novel method avoids the need to maintain a power supply to maintain a specific coloration condition of a device. Since there is no potential in the bleached state enables the window to return to an original state by shorting an electrical connection between layers, and may be done without electrical supply.
0211] Applications of the present invention include as use for privacy to prevent viewing between areas, including reducing visibility into a building or room. These may be used in any situation where it is desirable to control light and/or heat energy passing through a window or substrate. This may apply to hospital and medical procedure areas, such as to control X-rays from reaching technicians. Additionally, there are industrial uses for protecting light or heat-sensitive components during manufacture. These also have application to electronic device screens, where it is desired to respond to environmental conditions and reduce glare or other effects to make the viewing experience easy, comfortable and enjoyable. This may apply to projection screens and displays.
[000212] The present invention blocks damaging UV rays, reduces glare and eye strain. These are environmentally friendly methods and apparatuses having high durability and stability over a range of conditions. This is may be measured as coloration cycles.
[000213] These applications benefit from the present invention by providing fast, efficient privacy control over a range of transparency values. They provide ways to efficiently use space inside a building by creating privacy areas, or virtual
offices/cubicles.
[000214] These applications provide a comfortable work or home environment by creating private work spaces, such as are felt in large open offices. They reduce fading of the internal elements, such as carpets, furniture, and so forth.
[000215] The present invention provides low energy control of a smart window. The foregoing description of the invention has been presented for purposes of illustration and description and is not intended to be exhaustive or to limit the invention to the precise form disclosed, and obviously, many modifications and variations are possible considering the above teaching. The embodiments were chosen and described to best explain the principles of the invention and its practical application to thereby enable others skilled in the art to best utilize the invention in various embodiments and with various modifications as are suited to the use contemplated. It is intended that the scope of the invention be defined by the claims appended hereto.
[000216] Various embodiments are described herein for an electrochromic device for use in a window or other structure. The device configures multiple layers between substrates, wherein the configuration incorporates a ion isolation mechanism. In some embodiments, this mechanism is an SICL configured to prevent transport of
dye ions from an electrolyte layer to the electrochromic layer. Another mechanism is the use of nanoparticles in a dye-containing layer or portion of the electrolyte; the dye ions tether to the nanoparticles and prevent the dye ions from transporting to the electrochromic layer. A low coloration potential across multiple layers of the electrochromic device initiates a redox reaction in the electrochromic layer and the dye containing layer, wherein ions in the electrochromic layer are reduced or oxidized and dye ions are oxidized or reduces, respectively. The redox reactions change the coloration state of the electrochromic device. Once ions are
oxidized/reduced, they maintain that state as the dye ions are isolated from the electrochromic layer.
[000217] In some embodiments, an electrochromic device is incorporated into an integrated glass unit. A control system may be incorporated to provide control of the coloration state of an electrochromic device. The control system monitors status of the electrochromic device, such as to adjust the coloration potential, implement a coloration scheme, interface and react to energy harvesting and so forth.
[000218] The discussion, description, examples and embodiments presented within this disclosure are provided for clarity and understanding. A variety of materials and configurations are presented, but there are a variety of methods, configurations and materials that may be used to produce the same results.
Claims
1. An integrated window structure, comprising: a first substrate;
an electrochromic coating proximate the first substrate;
an electrolyte layer proximate the selective ion-conductive layer, the electrolyte layer having electrically conductive and at least one redox dye material; and
a second substrate proximate the electrolyte layer;
2. The integrated window structure of claim 1, wherein the electrolytic layer is a solid material and comprises: a first electrolyte layer proximate the selective ion-conductive layer; and a second electrolyte layer having a plurality of electrically conductive particles and the at least one redox dye material.
3. The integrated window structure of claim 1, wherein the electrochromic coating comprises an inorganic material
4 The integrated window structure of claim 3, wherein the electrochromic coating is cathodic.
5. The integrated window structure of claim 3, wherein the inorganic material contains tungsten oxide.
6. The integrated window structure of claim 2, wherein the conductive particles comprise carbon or inorganic oxides.
7. The integrated window structure of claim 1, wherein a selective ion- conductive coating is placed proximate to the electrochromic coating and the electrolyte layer.
8. The integrated window structure of claim 6, wherein the conductive particles are nanofibers.
9. The integrated window structure of claim 1, wherein the first substrate is coated with a transparent conductor and the transparent conductor proximate the electrochromic layer;
the second substrate is coated with a transparent conductor; and the transparent conductor proximate the electrolyte layer.
10. The integrated window structure of claim 1, wherein the dye material is a bridged dye.
11. An electrochromic device comprising: a first substrate having a first conductive coating;
an electrochromic coating proximate the first conductive layer;
an electrolyte layer proximate the electrochromic coating, the electrolyte layer having redox dye material, and electrically conductive particles: and a second substrate coated with a transparent conductive coating wherein the transparent conductor proximate the electrolyte layer;
12. The electrochromic device of claim 11, further comprising: a selective ion-conductive coating positioned between the electrochromic coating and the electrolyte layer, wherein the selective ion-conductive layer comprises an inorganic material that is not electrically conductive.
13. The electrochromic device of claim 11, wherein the electrochromic coating comprises an inorganic oxide or a conductive polymer.
14. The electrochromic device as in claim 11, wherein the electrolyte layer is adapted to conduct at least one of protons, lithium ions, sodium ions and potassium ions.
15. The electrochromic device as in claim 11, further comprising: a control module responsive to light energy incident on the
electrochromic device, wherein the control module applies a coloration potential across layers of the electrochromic device corresponding to the light energy.
16. The electrochromic device as in claim 11, wherein electrochromic properties of the redox dye material are complimentary to electrochromic properties of the electrochromic coating.
17. The electrochromic device as in claim 11, where the electrically conductive particles are selected from the group of graphene, single walled carbon nanotubes, double walled carbon nanotubes or multi-walled carbon nanotubes, inorganic oxides or mixture thereof.
18. The electrochromic device as in claim 12, wherein the selective ion- conductive coating comprises an inorganic material containing fluorine or a fluorine-containing polymer.
19. A method for manufacture of an electrochromic device, comprising: forming an electrochromic coating on a first substrate;
forming an electrolyte layer on the selective ion-conductive layer, wherein the electrolyte layer includes redox dye material and
electronically conductive particles; and
configuring an opposing second substrate to sandwich the electrolyte layer between the first substrate and the second substrate.
20. A method for manufacture of an electrochromic device, comprising: forming an electrochromic coating on a first transparent substrate;
forming an electrolyte layer, wherein the electrolyte layer includes redox dye material and electronically conductive particles and the redox dye material is tether in the electrolyte layer so as to prevent transport of the redox dye ions into the electrochromic layer; and
configuring an opposing second substrate and sandwiching the electrolyte layer between the first substrate and the second substrate.
21. The method of claim 20, wherein the redox dye material comprises ferrocene, viologen or phenazine.
22. The method of claim 20, wherein the electrolyte layer further comprises a polymer, plasticizer, polymer, UV stabilizer and a dissociable salt.
23. The method as in claim 22, wherein the dissociable salt is a lithium salt.
24. The method as in claim 22, wherein the plasticizer is selected from at least one of hydrophobic ionic liquid, propylene carbonate, Y-butyrolactone, tetraglyme and sulfolane.
25. The method as in claim 20, wherein the electrochromic coating comprises at least one of tungsten oxide, nickel oxide, titanium oxide, vanadium oxide,
copper oxide, cobalt oxide, chromium oxide, niobium oxide, iridium oxide and molybdenum oxide.
26. The method of claim 25, wherein the electrochromic coating further comprises lithium oxide, sodium oxide and potassium oxide.
27. The method as in claim 20, further comprising forming a conductive coating on the first substrate proximate followed by forming the electrochromic coating; and forming a conductive coating on the second substrate, wherein the conductive coating on the second substrate is proximate electrolyte layer.
28. The method as in claim 22, wherein the redox dye is tethered in the electrolyte layer by tethering this to at least one of the conductive particles and the polymer.
329. A smart electrochromic window, comprising: an electrochromic device, comprising: an electrochromic coating; and an electrolyte layer having redox dye and electronically conductive particles; a coloration potential source coupled to the electrochromic device and configured to apply a coloration potential to change a coloration state of the electrochromic device; an energy harvesting system, and an energy storage system configured to receive energy from the energy harvesting system and power the coloration potential source.
30. The smart electrochromic window in claim 29, where at least one of the following energy harvesting system is selected from solar cells, radio-frequency energy harvesting system, thermoelectric device and piezoelectric device.
31. The smart electrochromic window as in claim 29, where the energy storage system is selected from at least one of a rechargeable battery and a capacitor.
32. The smart electrochromic window as in claim 29, where the energy storage system is recharged by the electrochromic device during coloration transition.
33. A smart electrochromic window, comprising: an electrochromic device, a coloration potential source coupled to the electrochromic device and configured to apply a coloration potential to change a coloration state of the electrochromic device; an energy harvesting system, and an energy storage system configured to receive energy from the energy harvesting system and power the coloration state of the device, and further, the energy stored in the electrochromic device is used to recharge the energy storage system when the coloration state of the device is reversed.
34. A smart electrochromic window as in claim 33, wherein the energy storage system applies electrical potential to color the device from a bleached state, and the electrical charge stored in the colored state of the device is used to recharge the energy storage system when the device is bleached.
35. A smart electrochromic window as in claim 33, wherein the coloration potential source receives the signal to apply the coloration potential wirelessly from a user or any other device configured by a user.
36. A smart electrochromic window as in claim 35, wherein the coloration potential source further acts to apply the coloration potential after receiving input of light energy falling on the said window.