WO2018005146A1 - Low temperature sc1 strippable oxysilane-containing coatings - Google Patents
Low temperature sc1 strippable oxysilane-containing coatings Download PDFInfo
- Publication number
- WO2018005146A1 WO2018005146A1 PCT/US2017/038116 US2017038116W WO2018005146A1 WO 2018005146 A1 WO2018005146 A1 WO 2018005146A1 US 2017038116 W US2017038116 W US 2017038116W WO 2018005146 A1 WO2018005146 A1 WO 2018005146A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- oxysilane
- groups
- substituted
- composition
- unsubstituted
- Prior art date
Abstract
Description
Claims