WO2017192101A1 - A photoelectrochemical cell for wastewater treatment and method of fabricating the photoelectrochemical cell - Google Patents

Abstract

A photoelectrochemical cell and method of fabricating such a cell for wastewater treatment is disclosed. The photoelectrochemical cell for wastewater treatment comprising at least one cathode and at least one anode, wherein the anode comprises a material configured for an anodic oxidation reaction in the presence of the wastewater, wherein at least one of the anode and cathode comprises an optically pervious material, the cathode configured for cooperating with the anode to drive one or more cathodic reduction reactions in the presence of the wastewater, and wherein the anode and the cathode are disposed to allow irradiation of at least a portion of a space between the anode and the cathode by a light source through the optically pervious material to activate at least one photon based reaction in the wastewater. The invention advantageously provides multiple sources of hydroxyl radicals for wastewater treatment.

Description

A PHOTOELECTROCHEMICAL CELL FOR WASTEWATER TREATMENT AND METHOD OF FABRICATING THE PHOTOELECTROCHEMICAL CELL

Cross-Reference To Related Application

[0001] This application claims the benefit of priority of U.S. patent application no. 62/332,563 filed on 6 May 2016, the content of it being hereby incorporated by reference in its entirety for all purposes. Field of Invention

[0002] The present invention broadly relates to a photoelectrochemical cell for wastewater treatment and a method of fabricating such a photoelectrochemical cell. Background

[0003] Many countries may be densely populated with limited freshwater resources. One example being Singapore, which may be one of the most water- stressed country in the world. In order to meet the total water demand, the country has been investing heavily in advanced water treatment technologies, leading to revolutionary practices, such as water reuse, which provides about 30% of the country's water demand.

[0004] However, as such countries continue to develop their economy, their industrial sector grows rapidly and produces hard-to-degrade organic chemicals, which tend to be harmful to humans and the environment. Such chemicals are neither easily nor effectively removed by conventional water reclamation plants.

[0005] From a water security perspective, there is also a risk that some of these harmful and recalcitrant compounds may end up in freshwater reservoirs. Moreover, in an urban environment such as Singapore, which faces intense demographic pressure, additional risks of undesirable algal blooms, development of antibiotic resistance, accidental contamination (e.g. waterborne disease outbreaks, accidental or terrorist chemical spills) etc. are prone to emerge. It is therefore essential to safeguard water quality and public health.

[0006] In particular, one of the more prominent growing concerns may be the release of hazardous persistent organic pollutants (POPs) into the environment. These POPs can be detected even at low amounts in rivers, lakes, oceans, and even drinking water all over the world. As these pollutants cannot be significantly removed by conventional wastewater treatment plants, interest has been developing on total removal of POPs with a focus on exploring simple, safe, effective, and economical physico-chemical technologies. While developing such technologies, consideration has also been taken to reduce the environmental footprint of water treatment processes of POPs. In this regard, the use of renewable energy such as sunlight in physico- chemical treatment processes of POPs has been explored.

[0007] Amongst the various physico-chemical treatment processes that rely on the use of sunlight (i.e. ultraviolet (UV) reactivity), photon based advanced oxidation processes (AOPs) have gained popularity because they allow the generation of hydroxyl radical (ΌΗ), a very strong oxidizing agent (E° = 2.80 V versus (v) standard hydrogen electrode (SHE)) which is second only to fluorine but less hazardous. "OH has a very short lifetime of 10^"9 seconds and its non- selectivity allows it to oxidize many biorefractory organic compounds, especially those with double bonds, very quickly. An example of a photon based AOP is ozone photolysis (O3/UV).

[0008] However, ozone photolysis and other ozone based AOPS tend to be very energy consuming due to the low water solubility of O3. In addition, Fenton' s process generates sludge in quantities which require increased means of handling or disposal. Furthermore, ozone photolysis and other conventional photon based AOPs suffer from several other drawbacks, one of which is the high usage of chemical reagents, especially H2O2 which has a relatively weak molar absorption coefficient in the UV region and thus reduces the efficiency of UV irradiation in the presence of H2O2. Another drawback of photon based AOPs (e.g. photocatalytic oxidation) is the recovery of photocatalyst(s). With these drawbacks, scaling up such treatment processes becomes undesirably arduous.

[0009] There is thus a need to provide for a solution that ameliorates one or more of the drawbacks as mentioned above. The solution provided should be suitable for treating water and/or wastewater.

Summary

[0010] In accordance with one aspect of the present invention, there is a photoelectrochemical cell for wastewater treatment comprising at least one cathode and at least one anode, wherein the anode comprises a material configured for an anodic oxidation reaction in the presence of the wastewater, wherein at least one of the anode and cathode comprises an optically pervious material, the cathode configured for cooperating with the anode to drive one or more cathodic reduction reactions in the presence of the wastewater, and wherein the anode and the cathode are disposed to allow irradiation of at least a portion of a space between the anode and the cathode by a light source through the optically pervious material to activate at least one photon based reaction in the wastewater.

[0011] In accordance with another aspect of the present invention, there is a method of fabricating a photoelectrochemical cell, the method comprising providing at least one cathode and at least one anode, wherein the anode comprises a material configured for an anodic oxidation in the presence of the wastewater, wherein at least one of the anode and cathode comprises an optically pervious material, configuring the cathode for cooperating with the anode to drive one or more cathodic reduction reactions in the presence of the wastewater, and configuring the anode and the cathode to allow irradiation of at least a portion of a space between the anode and the cathode by a light source through the optically pervious material to activate at least one photon based reaction in the wastewater.

Brief Description of the Drawings

[0012] In the drawings, like reference characters generally refer to like parts throughout the different views. The drawings are not necessarily to scale, emphasis instead generally being placed upon illustrating the principles of the invention. In the following description, various embodiments of the present disclosure are described with reference to the following drawings, in which: [0013] FIG. 1A illustrates the design of a conventional reactor where light does not shine perpendicularly through the anode and cathode but is directed from the top of the setup.

[0014] FIG. IB illustrates a reactor design according to the embodiments disclosed herein where light (e.g. UVA light) goes through the optically pervious anode.

[0015] FIG. 1C illustrates an experimental setup of a stirred glass reactor made according to the embodiments disclosed herein.

[0016] FIG. ID illustrates a reactor-parabolic reflector system for focusing the UVA light toward the reactor, particularly through the transparent anode.

[0017] FIG. 2A shows the design of a three dimensional (3D) printed photo- electrocatalytic reactor made according to the embodiments disclosed herein. Specifically, the reactor is a closed cell reactor with 0₂ bubbling in a separate tank (the separate tank is not shown). This may be referred to as reactor (1) in the present disclosure.

[0018] FIG. 2B shows the design of a 3D printed photo-electrocatalytic reactor made according to the embodiments disclosed herein. Specifically, this reactor allowed O2 bubbling directly within the reactor. This may be referred to as reactor (2) in the present disclosure.

[0019] FIG. 2C shows the design of a 3D printed photo-electrocatalytic reactor made according to the embodiments disclosed herein. Specifically, this reactor is an open cell reactor with O2 bubbling in the reactor. This may be referred to as reactor (3) in the present disclosure.

[0020] FIG. 3 shows the polarization curves of platinum (Pt), fluorine-doped tin oxide (FTO) and boron-doped diamond (BDD) anodes in 0.5 M H₂S0₄ at 20 mV s^"1.

[0021] FIG. 4 shows transmissivity spectrum of FTO coated and uncoated glass plates.

[0022] FIG. 5 shows the transmissivity of cylindrical stirred glass reactor coated with varying T1O2 concentrations.

[0023] FIG. 6A shows the methylene blue (MB) photocatalytic (PC) degradation rate constants as a function of T1O2 concentration of thin film coating.

[0024] FIG. 6B shows the MB PC degradation rate constants as a function of transmissivity (365 nm) of thin film coating.

[0025] FIG. 7A illustrates the stability of T1O2 coating for PC degradation of MB over 6 successive runs of 90 mins each.

[0026] FIG. 7B illustrates the transmissivity (365 nm) of T1O2 coating for PC degradation of MB over 6 successive runs of 90 mins each.

[0027] Fig. 7C illustrates the stability of FTO coating using EA/AO degradation of phenol over 5 successive runs of 90 mins each.

[0028] FIG. 8A shows a comparison of phenol (1.4 mM) degradation rate. Operating conditions were at current density of 1.25 mA cm^"2, [Fe²⁺] of 0.1 mM (when required) and T1O2 concentration of 0.311 mg cm^"2 (when required). Values in parenthesis represent the number of ΌΗ sources involved in the process.

[0029] FIG. 8B shows a comparison of phenol (1.4 mM) mineralization yields after 8 hours. Operating conditions were at current density of 1.25 mA cm^"2, [Fe²⁺] of 0.1 mM (when required) and T1O2 concentration of 0.311 mg cm^"2 (when required). Values in parenthesis represent the number of ΌΗ sources involved in the process.

[0030] FIG. 9A shows a comparison of kinetic rate constants for phenol degradation in the three 3D printed reactors, given a pseudo-first order model and in four different conditions: EA/AO, EA/PAO, EA/EF/AO and EA/PEF/PAO (current density = 1.25 niA cm^"2, [Fe²⁺] = 0.1 mM (when required)).

[0031] FIG. 9B shows a comparison of the maximal H2O2 accumulation in dark conditions for the three 3D printed reactors (current density = 1.25 mA cm^"2, [Fe²⁺] = 0 mM).

[0032] FIG. 9C shows the degradation rate constant (min ¹) for various processes using 3D printed reactor (3).

[0033] FIG. 10A shows the optimization of current density (at [Fe²⁺] = 0.1 mM) based on an EA/PEF/PAO process performed in reactor (3).

[0034] FIG. 10B shows the optimization of [Fe²⁺] (at 1.9 mA cm^"2) based on an EA/PEF/PAO process performed in reactor (3).

[0035] FIG. 11 shows a comparison between the stirred glass reactor configuration and an embodiment of the 3D printed cell.

[0036] FIG. 12 shows a comparison of different T1O2 concentrations and their degradation results measured on methylene blue.

[0037] FIG. 13 shows the various hydroxyl radical pathways (6 different souces).

Detailed Description [0038] The following detailed description refers to the accompanying drawings that show, by way of illustration, specific details and embodiments in which the invention may be practiced. These embodiments are described in sufficient detail to enable those skilled in the art to practice the invention. Other embodiments may be utilized and changes may be made without departing from the scope of the invention. The various embodiments are not necessarily mutually exclusive, as some embodiments can be combined with one or more other embodiments to form new embodiments.

[0039] Features that are described in the context of an embodiment may correspondingly be applicable to the same or similar features in the other embodiments. Features that are described in the context of an embodiment may correspondingly be applicable to the other embodiments, even if not explicitly described in these other embodiments. Furthermore, additions and/or combinations and/or alternatives as described for a feature in the context of an embodiment may correspondingly be applicable to the same or similar feature in the other embodiments.

[0040] To address the drawbacks associated with conventional ozone treatments and AOPs as discussed above, one of the ways is to replace the chemicals used with a clean reagent (electrons) that enhances removal efficiency. Such processes may be known as electrochemical advanced oxidation processes (EAOPs), which are based on continuous electrochemical generation of ΌΗ. Unlike conventional AOPs as described above, EAOPs tend to be more flexible and cover a broad range of organic loads.

[0041] Photo-electro-Fenton (PEF) is one of such EAOPs. In contrast with conventional Fenton's process, the Fenton's reagent (H2O2 and/or Fe²⁺) is generated electrocatalytically and in situ at the cathode of a PEF reactor and produces ΌΗ by equation 1 below. Meanwhile, the UV irradiation of Fe(III) hydroxy complexes (Fe(OH)²⁺), the preponderant Fe(III) species at pH around 3 formed from equation 2a, brings another source of ΌΗ as shown in equation 2b below.

[0042] H2O2 + Fe²⁺ → Fe³⁺ + OH + HO^" (1) [0043] H₂0 + Fe³⁺ Fe(OH)²⁺ + H⁺ (2a)

[0044] Fe(OH)²⁺ + hv→ Fe²⁺ + ΌΗ (2b)

[0045] The mineralization of pollutants may be enhanced by UV artificial light or sunlight (having a wavelength (λ) more 300 nm) irradiation, not only by the contribution of ΌΗ induced by equation 2b, but also by the rapid photolysis of complexes of Fe(III) (e.g. Fe(OOCR)²⁺) with carboxylic acids (OOCR) (mainly oxalic acid) produced during degradation of organic contaminants, as shown in equation 3:

[0046] Fe(OOCR)²⁺ + hv → 2 Fe²⁺ + C0₂ + R^* (3)

[0047] In equation 3, R may be an alkyl group. Equation 3 may proceed regardless of the number of carbon atoms present in the alkyl group. Oxalic acid may be one of the most common short chain carboxylic acid quantified during the organic degradation process. In this regard, R may contain 2 carbon atoms. However, R is not limited to 2 carbon atoms.

[0048] Other advantages of PEF include the electrochemical regeneration of Fe²⁺ (equation 4). This means that iron can be provided at catalytic amounts if they are not naturally present in the wastewater, thereby avoiding the production of large amounts of sludge.

[0049] Fe³⁺ + e → Fe²⁺ (4)

[0050] In EAOPs, one of the factors that affects treatment efficiency may be the electrode material, and most of the time, opaque electrodes are conventionally employed. In EAOPs, the cathode responsible for in situ generation of H₂0₂ through the 0₂ reduction reaction (ORR) at its surface (equation 5) is typically made of carbon due to its high H₂ evolution overpotential and low catalytic activity for H₂0₂ decomposition.

[0051] 0₂ + 2H⁺ + 2e → H₂0₂ (5)

[0052] In this regard, 3D carbon-based electrodes such as graphite felt and carbon felt are usually used because of their high specific surface areas and efficient cathodic regeneration of Fe²⁺ (see equation 4).

[0053] Meanwhile, anode materials having high 0₂ evolution overpotential, referred to as non-active anodes (M), can also play an important role in the oxidation of pollutants through water discharge at their surface, producing weakly- adsorbed ΌΗ as shown in equations 6a and 6b:

[0054] M() + H₂0 → M('OH) + H⁺ + e^" (6a)

[0055] M('OH) + organic compound— > M() + oxidation products (6b)

[0056] In this regard, one of the most popular non-active anodes may be boron-doped diamond (BDD) which allows organics to be oxidized by BDD('OH) formed from anodic oxidation (AO).

[0057] The combination of AO (equations 6a and 6b) and PEF processes (equations 1, 2a and 2b) therefore advantageously provides three sources of ΌΗ.

[0058] The solution can also include a further (i.e. fourth) source of ΌΗ in such electrolytic processes. This may consist of H₂0₂ electro-activation (EA) through an electron transfer reaction at the carbonaceous cathode, as shown in equation 7:

[0059] H₂0₂ + e → ΌΗ + HO (7)

[0060] Another way to generate ΌΗ may be to include the use of photocatalyst in such EAOPs. Amongst the different semiconductors tested for photocatalysis (PC), titanium dioxide (T1O2) in its crystallized anatase form gave the best performance. When T1O2 is irradiated by UV light of wavelength below 380 nm, an electron from the filled valence band is promoted to the empty conduction band (e_Cb^~) with an energy gap of 3.2 eV generating a positively charged vacancy, referred to as a hole (h_vb⁺). This is depicted by equation 8. The holes produced at the T1O2 surface can oxidize either water or OH^", thus generating ΌΗ as shown in equations 9 and 10, respectively.

[0061] Ti0₂ + hv → e_cb ^" + h_vb ⁺ (8)

[0062] h_vb ⁺ + H₂0 → ΌΗ + H⁺ (9)

[0063] h_vb ⁺ + OH^" → ΌΗ + Η⁺ (10)

[0064] Ti0₂ presents the additional benefit of being potentially immobilized as a coating on a conductive material such as titanium, so that it could be employed as an anode in the so-called photo-electrocatalytic process (PEC). PEC was shown to increase the mineralization efficiency of PC by decreasing the charge recombination from equation 11 :

[0065] e_cb ^" + h_vb ⁺ → Ti0₂ + heat (11)

[0066] The coupling of PC and PEC with PEF improves the oxidation ability over treatments such as PEF/PC and PEF/PEC, wherein both only involved three sources of ΌΗ (see equations 1, 2, 9 and 10). The PEF/PC and PEF/PEC combinations increase the accumulation of H₂0₂ in the bulk solution through, respectively, photocatalytic generation of H₂0₂ (equation 12) and oxygen reduction reaction(s) (ORR) at the carbon cathode via the transfer of photo-generated electrons (e_Cb ) from the photo-anode (equation 13, also known as photo- AO, (PAO)):

[0067] 2H₂0 + 2h_vb ⁺ → H₂0₂ + 2H⁺ (12)

[0068] 0₂ + 2H⁺ + e_cb ^" → H₂0₂ (13)

[0069] These reactions provide additional H₂0₂ precursors for the Fenton reaction (equation 1) to form ΌΗ.

[0070] With the aim of further improving the efficiency of oxidation, PEF/PAO/PC combination as well as PEF/PAO/PEC have been explored. These combinations involve four sources of ΌΗ (see equations 1, 2, 6a, 6b, 9 and 10). In the latter combination, solar driven transparent electrode made of Bi₂W06 photocatalyst deposited on a fluorine-tin oxide (FTO) glass photo-anode may be employed in a semi-cylindrical quartz reactor. This apparatus enhances the quantum yield by optimizing the contact of photons with Bi₂W06. More importantly, the AO mechanisms (equations 6a and 6b) on the FTO anode, the H₂0₂ electro-activation (equation 7) and the H₂0₂ photolysis (equation 14) that could potentially occur during the treatment of organic pollutants remain conventionally elusive.

[0071] H₂0₂ + hv → 2 ΌΗ (14)

[0072] By minimizing the inter-electrode distance and by using a transparent glass anode as a wall of the device, the H2O2 photolysis (equation 14) could be implemented. In order to conceive such complex reactor design, 3D printing technology, also known as additive manufacturing or rapid prototyping, may be employed. Compared to traditional manufacturing technologies, the main advantage of 3D printing is the ability to fabricate intricate design and produce an assembly in a single-step process while reducing manufacturing cost and material wastes. There are many applications of 3D printing technology in a variety of industries, for instance, aerospace, biomedical, building and construction, marine and offshore, food industry, as well as desalination with membrane and water treatment fuel cell and microbial fuel cell. The benefit of utilizing 3D printing for EAOPs application is demonstrated in the present disclosure accordingly. [0073] With the above in mind, the present disclosure describes the implementation of six sources of ΌΗ (mechanisms are shown in equations 1, 2, 6a, 6b, 7, 9, 10 and 14) via the combination of EA, PAO, PEF and PC/PEC processes. A 3D porous carbon felt cathode and a fluorine-doped tin oxide (FTO) transparent anode may be employed in two kinds of reactor design: (i) a stirred glass photo-reactor and (ii) a 3D- printed flow-cell photo-reactor. The present disclosure also describes comprehensive characterization of the electrochemical and transmissivity properties of FTO, optimization of the T1O2 coating efficiency on glass substrate, assessment of the performance of photo-electro-catalytic Fenton in a stirred glass reactor, and evaluation and comparison with a 3D-printed flow cell.

[0074] Before going into further details of the photoelectrochemical reactor and its method of making, the definitions of certain terms are first discussed.

[0075] The terms "hydroxyl" and "hydroxy" may be interchangeably used to refer to an entity with the formula OH in the present disclosure.

[0076] In the context of the present application, the phrase "optically pervious" refers to materials that allow light to pass. This would cover materials that may be transparent or translucent but not opaque.

[0077] The word "substantially" does not exclude "completely" e.g. a composition which is "substantially free" from Y may be completely free from Y. Where necessary, the word "substantially" may be omitted from the definition of the invention.

[0078] In the context of various embodiments, the articles "a", "an" and "the" as used with regard to a feature or element include a reference to one or more of the features or elements.

[0079] In the context of various embodiments, the term "about" or "approximately" as applied to a numeric value encompasses the exact value and a reasonable variance.

[0080] As used herein, the term "and/or" includes any and all combinations of one or more of the associated listed items.

[0081] As used herein, the phrase of the form of "at least one of A and B" may include A or B or both A and B. Correspondingly, the phrase of the form of "at least one of A and B and C", or including further listed items, may include any and all combinations of one or more of the associated listed items.

[0082] Unless specified otherwise, the terms "comprising" and "comprise", and grammatical variants thereof, are intended to represent "open" or "inclusive" language such that they include recited elements but also permit inclusion of additional, unrecited elements. Meanwhile, the terms "consisting" and "consist", and grammatical variants thereof, are intended to represent "close" or "exclusive" language such that they only include recited elements but do not permit inclusion of additional, unrecited elements.

[0083] Having defined the various terms, details of the various embodiments are now described below. Embodiments described in the context of the photoelectrochemical cell are analogously valid for the method of fabricating such a photoelectrochemical cell, and vice versa.

[0084] The present disclosure provides a photoelectrochemical cell for wastewater treatment comprising at least one cathode and at least one anode. The anode may comprise a material configured for an anodic oxidation reaction in the presence of the wastewater. At least one of the anode and cathode may comprise an optically pervious material according to various embodiments. The cathode may be configured for cooperating with the anode to drive one or more cathodic reduction reactions in the presence of the wastewater. The anode and the cathode may be disposed to allow irradiation of at least a portion of a space between the anode and the cathode by a light source through the optically pervious material to activate at least one photon based reaction in the wastewater.

[0085] In various embodiments, the photoelectrochemical cell may consist of a cathode and an anode. Both the cathode and anode may be independently optically pervious or opaque. The cathode may possess a hydrogen evolution overpotential below -0.6 V/SHE (i.e. standard hydrogen electrode). This range of overpotential improves production of hydrogen peroxide and in turn the ΌΗ. The cathode may be made from any carbon based materials or platinum or a combination of these materials. In various embodiments, the cathode may be made of a material selected from the group consisting of carbon/graphite felt, carbon fiber brush, carbon cloth, boron-doped diamond (BDD), graphene, 3D porous carbon/graphite felt, and their combinations thereof.

[0086] As for the anode, it may be configured to comprise the optically pervious material coated with the material for anodic oxidation. The optically pervious material may act as a support or substrate for the anodic oxidation material. The latter may be a conducting film. The material configured for anodic oxidation (and thus the anode) may be selected from the group consisting of fluorine-doped tin oxide (FTO), indium tin oxide (ITO), boron-doped diamond (BDD), tin oxide (Sn0₂), lead oxide (Pb0₂), sub-stoichiometric titanium oxide (e.g. Ti₄0₇) and combinations thereof. These materials may allow light to pass through partially or entirely. In various embodiments, the anode may also possess an oxygen evolution potential of at least 1.5 V/SHE, or preferably at least 1.9 V/SHE, which leads to production of ΌΗ.

[0087] The wastewater or water treated by the photoelectrochemical cell optionally comprises Fe²⁺, Fe³⁺ and/or ferric hydroxyl complexes. When these substances are present in the wastewater/water, Fenton's reaction and photolysis of ferric complexes can then proceed and these accounts for two ·ΟΗ sources. If the wastewater/water does not contain such iron constituents, then these substances may be added in manually. The present photoelectrochemical cell is thus versatile in that it can process various types of water and wastewater while providing multiple sources of hydroxyl radicals.

[0088] As mentioned above, the anode and/or cathode may comprise the optically pervious material. The optically pervious material may be transparent or translucent as long as it allows light to pass through sufficient to activate light dependent reactions or photon based reactions for water and wastewater treatment. Transparent materials may include glass etc. while translucent materials may include sand-blasted glass, amber glass, quartz etc. The optically previous material may comprise glass or quartz according to various embodiments disclosed herein.

[0089] Apart from anodic oxidation, one or more cathodic reduction reactions may occur in the photoelectrochemical cell. The one or more cathodic reduction reactions may comprise reduction of oxygen, reduction of Fe³⁺ and/or electro-activation of hydrogen peroxide.

[0090] Having discussed the materials used for the anode and cathode, the configuration of the photoelectrochemical cell is now described. In the photoelectrochemical cell, the anode and the cathode may be disposed to face each other while remaining spaced apart by a distance of about 10 mm to about 30 mm or a distance of less than about 10 mm. In various embodiments, the anode and cathode may be kept apart at any distance (e.g. about 30 mm or less) as long as the provision of multiple sources of ·ΟΗ is not hindered. Advantageously, this reduces footprint of the photoelectrochemical cell.

[0091] The photoelectrochemical cell may further comprise a chamber having a base portion and a wall portion extending from the base portion, wherein the anode and the cathode may be disposed in the chamber. The chamber may be an open chamber in that it may comprise an opening defined by the wall portion. This opening may be arranged opposing to the base portion. In other embodiments, the chamber may be a closed chamber.

[0092] In some embodiments, the chamber may be integrally formed with the anode and the cathode defining part of the wall portion of the chamber. For such configuration, the anode and/or cathode may be constructed as the walls of the cell. In other words, the present photoelectrochemical cell may be constructed of a single wall corresponding to the thickness of the anode and/or cathode. This single wall configuration is advantageous compared to double walls where there is a reactor wall in addition to the anode. In the case of double walls, more photons tend to be absorbed before reaching the active surface, photocatalyst and/or at least a portion of the space between the anode and cathode, thereby resulting in lower quantum yield (as photons are lost).

[0093] The photoelectrochemical cell may further comprise an inlet and an outlet at the wall portion of the chamber, wherein the inlet and the outlet may be in fluid communication with the chamber and may be disposed at opposing ends of the chamber. With the inlet and outlet, the photoelectrochemical cell may be used as a continuous system instead of a batch system.

[0094] In some embodiments, the base portion of the chamber may comprise one or more openings, and when more than one openings are present, the openings may be arranged in order of increasing cross-sectional area with increasing distance from the inlet to the outlet. Advantageously, this arrangement mitigates pressure differences across the chamber. The openings may be distributed evenly across the base portion.

[0095] The photoelectrochemical cell may further comprise a photocatalyst disposed on an inner base portion and/or an inner wall portion of the chamber to allow irradiation of at least the portion of the space between the anode and the cathode. The photocatalyst may be disposed as a layer on the anode or the optically pervious material. In various instances, the amount of photocatalyst present may lead to a resultant transmissivity (in UVA region, e.g. 365 nm) of more than 10% and preferably about 20%. Bearing this consideration in mind, the amount of photocatalyst disposed may be about 0.024 mg/cm² to about 0.4 mg/cm² in some embodiments, while this may also depend on material of photocatalyst used. In this regard, the photocatalyst may be selected from the group consisting of titanium dioxide (T1O2), zinc oxide (ZnO), zinc tungstate (ZnW0₄), bismuth tungstate (Bi₂W0₆), and combinations thereof.

[0096] The photoelectrochemical cell may further comprise an optical medium configured to increase incident light on the optically pervious material. This optical medium may provide light i.e. either directly or indirectly channeling the light towards the photoelectrochemical cell. The optical medium may be a reflective medium such as a mirror. In some instances, the optical medium may be disposed at the side of the anode to channel light through the anode into the photoelectrochemical cell. The light from the optical medium or a light source may be configured to provide light having a wavelength of 10 nm to 400 nm. The light provided may be any form of ultraviolet light such as UVA, UVB and/or UVC (e.g. 254 nm). In preferred embodiments, UVA light is used.

[0097] The photoelectrochemical cell may further comprise an aerator configured to provide oxygen gas to the photoelectrochemical cell, wherein the aerator may be in fluid communication with the one or more openings at the base portion of the chamber. The aerator may also provide other gases to treat water/wastewater.

[0098] The photoelectrochemical cell may further comprise a dispensing device configured to dispense an aqueous solution comprising Fe²⁺, Fe³⁺ and/or ferric hydroxyl complexes to the photoelectrochemical cell. This dispensing device may be configured in any manner as long as it is in fluid communication with the photoelectrochemical cell. That is, the aqueous solution may be dispensed into the cell via a conduit. The aqueous solution may also be added to the water/wastewater through the cell's opening (i.e. when the cell is an open chamber).

[0099] The photoelectrochemical cell may be capable of generating at least one photon based reaction. The photon based reaction may comprise hydrogen peroxide photolysis, ferric hydroxyl complex photolysis, photocatalysis of water and/or photo- oxidation of OH^".

[00100] The photoelectrochemical cell may be in the form of a stirred glass reactor or a 3D printed reactor according to non-limiting exemplary embodiments.

[00101] There is also a method of fabricating the photoelectrochemical cell in the present disclosure. The method may comprise providing at least one cathode and at least one anode, wherein the anode may comprise a material configured for an anodic oxidation in the presence of the wastewater, wherein at least one of the anode and cathode may comprise an optically pervious material. The method may also include configuring the cathode for cooperating with the anode to drive one or more cathodic reduction reactions in the presence of the wastewater, and disposing the anode and the cathode to allow irradiation of at least a portion of a space between the anode and the cathode by a light source through the optically pervious material to activate at least one photon based reaction in the wastewater.

[00102] The embodiments and their advantages as described above in relation to the photoelectrochemical cell are applicable to the present method.

[00103] In the present method, the disposing of the anode and the cathode may comprise arranging the anode and the cathode to face each other in the photoelectrochemical cell while remaining spaced apart by a distance of about 30 mm or less, about 10 mm to about 30 mm or a distance of less than about 10 mm, according to various embodiments.

[00104] The arranging of the anode and the cathode may comprise providing a chamber having a base portion and a wall portion extending from the base portion, and disposing the anode and the cathode in the chamber. The chamber may be an open or close chamber as described above.

[00105] The providing of the chamber having a base portion and a wall portion extending from the base portion may comprise integrally forming the chamber with the anode and the cathode defining part of the wall portion of the chamber. In this manner, a single wall chamber with the anode and/or cathode incorporated as part of the wall may be provided. [00106] In various embodiments, the providing of the chamber may comprise integrally forming the chamber by 3D printing. The providing of the chamber may also comprise forming an inlet and an outlet at the wall portion of the chamber, wherein the inlet and the outlet may be in fluid communication with the chamber and may be disposed at opposing ends of the chamber. Providing an inlet and outlet advantageously configures the cell into a continuous system.

[00107] In the present method, the providing of the chamber may comprise forming one or more openings in the base portion, and wherein forming more than one openings may comprise forming the openings in order of increasing cross-sectional area with increasing distance from the inlet to the outlet. The openings may be evenly distributed.

[00108] The present method may further comprise a step of disposing a photocatalyst on an inner base portion and/or an inner wall portion of the chamber to allow irradiation of at least the portion of the space between the anode and the cathode. The disposition of the photocatalyst may comprise disposing the photocatalyst as a layer on the anode or optically pervious material. The consideration on the amount of photocatalyst for disposition has been discussed above.

[00109] The present method may further comprise providing an optical medium configured to increase incident light on the optically pervious material. The optical medium has been described in the above embodiments. A light source may also be provided.

[00110] The present method may further comprise providing an aerator configured to provide oxygen gas to the photoelectrochemical cell, wherein providing the aerator may comprise disposing the aerator to be in fluid communication with the one or more openings at the base portion of the chamber. Other gases may be provided by through the aerator.

[00111] The present method may further comprise providing a dispensing device configured to dispense an aqueous solution comprising Fe²⁺, Fe³⁺ and/or ferric hydroxyl complexes to the photoelectrochemical cell.

[00112] In summary, the technology as disclosed herein relates to a reactor suitable for water and wastewater treatment with multiple sources of production of hydroxyl radicals. The reactor may be a photo-electrocatalytic reactor. The production sources of hydroxyl radicals may comprise at least two of the processes selected from anodic oxidation, hydrogen peroxide photolysis, ferric-hydroxy complex photolysis, Fenton's reaction, photocatalysis, or their combination thereof.

[00113] In various embodiments, the anode and/or cathode may be opaque, translucent or transparent.

[00114] A process for water and wastewater treatment comprising such a reactor with multiple sources of production of hydroxyl radicals is contemplated.

[00115] While the methods described above are illustrated and described as a series of steps or events, it will be appreciated that any ordering of such steps or events are not to be interpreted in a limiting sense. For example, some steps may occur in different orders and/or concurrently with other steps or events apart from those illustrated and/or described herein. In addition, not all illustrated steps may be required to implement one or more aspects or embodiments described herein. Also, one or more of the steps depicted herein may be carried out in one or more separate acts and/or phases. Examples

[00116] The present disclosure relates to a solution that resolves the drawbacks as described above. The solution involves a photo-electrocatalytic or photoelectrochemical reactor that provides multiple sources of hydroxyl (·ΟΗ) radicals for advanced water and wastewater treatment (see FIG. 13). The expression "photo-electrocatalytic" may be used interchangeably with "photoelectrochemical" in the present disclosure. Such a reactor may be called a cell in the present disclosure. With a reactor configured to provide multiple sources of ·ΟΗ, the multiple sources of ·ΟΗ combine to produce a synergetic effect that enhances treatment efficiency of water and wastewater.

[00117] The reactor may be designed to have two electrodes. Without being limited to the following materials, the first electrode may be a high oxygen evolution overpotential anode coated with an additional layer of photocatalyst(s). The anode may have an oxygen evolution overpotential of at least 1.5 V/SHE, or preferably at least 1.9 V/SHE. The anode may comprise a material composed of fluorine-doped tin oxide (FTO), indium tin oxide (ITO), boron-doped diamond (BDD), tin oxide (Sn0₂), lead oxide (Pb0₂), sub-stoichiometric titanium oxide (e.g. Ti₄0₇) and/or their combinations thereof. The photocatalyst(s) may comprise titanium dioxide (Ti0₂), ZnW0₄, ZnO, Bi₂W06 and/or their combination thereof. The other electrode may be a cathode made of carbon fiber brush, carbon cloth, carbon/graphite felt, boron-doped diamond (BDD), platinum, graphene, 3D porous carbon/graphite felt and/or their combination thereof. The cathode may have a H₂ evolution overpotential below -0.6 V/SHE. Both the anode and cathode may be independently opaque, transparent or translucent. Both electrodes may be separated by a suitable distance between them.

[00118] The present solution also comprises a method of fabricating such a reactor or cell. The method is advantageous because the reactor or cell may be produced as a single piece, such as via 3D printing, to avoid leakages. Aeration within the reactor or cell can be enhanced by including diffusion holes at the bottom.

[00119] Advantageously, the method of making such a reactor and the reactor itself, allow water or wastewater to be effectively treated based on a combination of electrochemical processes involving hydroxyl radicals (·ΟΗ) produced by the anode and/or cathode, and the use of artificial light or sunlight (e.g. UVA) to promote photocatalytic reactions through the optically pervious (transparent or translucent) anode (see FIG. IB) as compared to conventional reactors (see FIG. 1A).

[00120] An embodiment of the overall design of reactor is shown in FIG. 2C with the UV light going through the anode as illustrated in FIG. IB. As an option, a parabolic mirror (see FIG. ID) can focus the light into the reactor, so that natural sunlight can be harnessed for the photolytic processes.

[00121] Compared to conventional reactors or a control with just fluorine-doped tin oxide (FTO) coated on glass, the present cell may comprise a transparent electrode made of glass coated with a transparent film of FTO or indium tin oxide (ITO) and a transparent film of titanium dioxide (Ti0₂). This exemplary configuration improves mineralization efficiency by at least 15%. In fact, this can improve the mineralization rate (or degradation rate constant) by one order of magnitude. In various instances, the mineralization efficiency increased by 60% or even 400% with 5 or 6 sources of ·ΟΗ, respectively, when compared to cells that are configured to produce only one source of ·ΟΗ. Briefly, these sources of ·ΟΗ include anodic oxidation (H₂0 ·ΟΗ + H⁺ + e^"), hydrogen peroxide photolysis (H2O2 + hv 2 ·ΟΗ), ferric hydroxyl complex photolysis ([Fe(OH)²⁺] + hv Fe²⁺ + ·ΟΗ), Fenton's reaction (Fe²⁺+ H2O2 Fe³⁺ + OH^" + ·ΟΗ), heterogenous photocatalysis (photocatalyst (e.g. T1O2) + hv + H2O + O2 -> H⁺ + ·ΟΗ + ·02^"), and electro-activation of hydrogen peroxide (H2O2 + e^"→ ΌΗ + HO^"). The details of these reactions have been described above.

[00122] Examples 1 to 6 relate to the experimental materials and methods while examples 7 to 15 relate to the results and discussion of the experiments.

[00123] Example 1 : Lists of Chemicals Used

[00124] TiCl₄ (99.9%), phenol (> 99%), acetic acid (> 99%), T1O2 (Degussa P25) (> 99.5%), Triton X-100 and H2O2 (30% v/v) were purchased from Sigma- Aldrich (Singapore). Potassium sulfate (99%) was provided by Nacalai Tesque (Singapore). FeS0₄ ^«7H₂0 (> 99%) was supplied by Merck (Singapore) and methanol (99.9%) by Fisher Scientific (Singapore). All the chemicals were of analytical grade and were used as is. All the solutions were prepared with ultrapure water (Milli-Q^® Advantage A10, Singapore) giving a resistivity higher than 18 ΜΩ cm at room temperature.

[00125] Example 2: Assessment of Fluorine-doped Tin Oxide (FTP) Characteristics

[00126] The oxidation characteristics of FTO (Latech, Singapore), such as its O2 evolution overvoltage was assessed by linear scanning voltammetry (LSV) with a potentiostat (Princeton Applied Research VersaSTAT 4, USA) in a three-electrode set-up, using glass coated on one side with FTO (15 cm²) as a working electrode, platinum (Pt, 30 cm²) as a counter electrode, and Ag/AgCl (KC1 3 M) (£ = 0.210 V vs SHE) as a reference electrode. The experiments were conducted in a 0.5 M solution of H2S0₄ at a voltage ranging from 0.5 to 3.0 V vs SHE and at a scan rate of 20 mV s^"1.

[00127] The transmittance of FTO was assessed by performing a scan of wavelength ranging from 200 nm to 435 nm using a DR 5000 (HACH, USA) spectrophotometer.

[00128] Example 3: Preparation and Assessment of T1O2 Deposited on Glass - Preparation of T1O2 Thin Film

[00129] The T1O2 particles were coated as a thin film onto different surfaces. Prior to coating, each surface was cleaned thoroughly with ethanol. T1O2 was coated on either FTO glass (Latech, Singapore) or on the inner wall of a 250 ml cylindrical glass reactor, yielding a coated area of 15 cm² and 92 cm², respectively.

[00130] A diluted acetic acid solution was prepared by adding 0.3 ml of concentrated acetic acid to 100 ml of ultrapure water. A specific amount of T1O2 was then grounded in a mortar with 2 ml of the diluted acetic acid solution. The remaining 100 ml of diluted acetic acid solution was slowly added to the mixture with constant grinding. Finally, 0.5 ml of Triton X-100 surfactant was added and mixed thoroughly. 1 ml of the T1O2 suspension was spread evenly onto the surface of the substrate. For the FTO glass, the mixture was allowed to sit for 10 minutes (mins), while for the curved glass surface, the coating mixture was constantly rotated for 10 mins. After removing the excess mixture, the coating was air dried and then heated for 30 mins at 500°C in an oven. Finally, the mass concentration of T1O2 in mg cm^"2 was determined by weighing the substrate before and after the coating procedure.

[00131] Example 4: Preparation and Assessment of T1O2 Deposited on Glass - Coating Efficiency as a Function of T1O2 Concentration

[00132] To ascertain the optimal concentration of T1O2 for degrading and mineralizing a synthetic wastewater stream, a series of experiments were conducted using different concentrations of T1O2, i.e. 1, 2, 4, 6, 8, 10, 11, 12, 13 and 14 g, each of these corresponding to the respective following yields i.e. 0.023, 0.045, 0.096, 0.125, 0.173, 0.243, 0.269, 0.298, 0.311 and 0.345 mg cm^"2 (in terms of Ti0₂ mass concentration).

[00133] The decrease of transmissivity to UV irradiation caused by the coating of Ti0₂ onto the glass wall was measured with a spectrophotometer (DR 5000, Hach, USA) before and after coating over the range of UV wavelength from 200 nm to 400 nm.

[00134] The photocatalytic response of Ti0₂ was evaluated under the irradiation from a UV lamp (UVP, UVGL-58 Handheld UV Lamp, 365 nm, 6 W) applied 1 cm away from the side of the glass wall coated with Ti0₂. A 250 ml Ti0₂ coated cylindrical glass was filled with 200 ml of 0.01 mM methylene blue (MB), which was used as a substitute dye pollutant with easy degradation monitoring through absorbance measurements. Oxygen gas was bubbled into the medium at a rate of 0.2 litre min^"1 using a gas diffuser. A magnetic stirrer was used to ensure the homogeneity of the solution. The absorbance of each sample was measured by spectrophotometry at the peak wavelength of 668 nm.

[00135] The stability of the coating was then assessed at optimal Ti0₂ concentration by six successive photocatalytic batch treatments of 90 mins each. The decay of MB was monitored by spectrophotometry.

[00136] Example 5: Assessment of Single and Combined Photo-electrocatalytic Treatments with Stirred Glass Reactor

[00137] Electrolysis was performed in a 0.25 litre open undivided cylindrical glass reactor under controlled conditions of current and temperature (28 + 0.1 °C) (see FIG. 1C). Carbon felt (40 cm², SGL Group, USA) was used as a cathode to ensure H₂0₂ production (see equation 5) while the efficiency of FTO coated glass (15 cm²) was compared to Pt (30 cm²) as anode. The distance between the cathode and the anode was fixed at 3 cm and they were immersed into a 200 ml solution of K₂S0₄ (0.05 M) as supporting electrolyte. The solutions were continuously stirred at 500 rpm in batch mode. The initial pH of the solution was adjusted to a value of pH 3 for the Fenton reaction. The air flow rate was set at 0.2 litre min^"1 for 20 mins before starting the electrolysis and until the end of the experiment in order to stay at saturation to provide a continuous 0₂ source for H₂0₂ production. The electrochemical cell was monitored by a power supply (HAMEG 7042-5, Germany) at constant current density (1.25 mA cm^"2) as reported based on the cathode surface area used.

[00138] The test conditions used with the uncoated glass reactor and the respective type of processes are presented in Table 1 below.

10

EA/PAO/PC FTO UV No Fe²⁺

stirred glass reactor

11

EA/EF/AO/T1O2 FTO Dark Fe²⁺

stirred glass reactor

12

EA/PEF/PAO/PC FTO UV Fe²⁺

stirred glass reactor

*EO: electro-oxidation; EA: electro-activation; AO: anodic oxidation; PEO: photo- electro-oxidation; PAO: photo-anodic oxidation; EF: electro-Fenton; PEF: photo- electro-Fenton; PC: photocatalysis.

[00140] Four operating parameters were varied in order to better understand the efficiency of the PEF/AO/PC process systematically: (i) dark/UV, (ii) anode material (Pt/FTO), (iii) Fe²⁺ catalyst (without Fe²⁺/with Fe²⁺) and (iv) T1O2 photocatalyst (without Ti0₂/with T1O2). The UV lamp was set at 365 nm, which corresponds to UVA, the most abundant UV radiation provided by sunlight. FeS0₄ (0.1 mM) was added as a source of Fe²⁺ to implement the Fenton reaction (see equation 1). After determining the desired amounnt of T1O2 coating on the glass reactor, the optimal concentration of T1O2 was applied.

[00141] In each case, the performance was assessed by monitoring phenol mineralization using a TOC-meter (Shimadzu, Japan), where TOC stands for total organic carbon. Phenol (1.4 mM) (TOC = 100 mg-C litre^"1) was used at this stage because it is a well studied model pollutant that allows comparisons with other AOPs commonly applied for wastewater treatment.

[00142] Example 6: Assessment of Single and Combined Photo-electrocatalytic Treatments with Three Dimensional (3D) Printed Reactors

[00143] Three 3D printed reactor were developed to test for the degradation and mineralization of phenol, serving as a proof-of-concept for the treatment feasibility of this technology before scaled-up applications are envisaged (see FIG. 2A to FIG. 2C). The reactors were designed with SolidWorks^® and made of polylactic acid (PLA) filaments in a 3D printer (Makerbot Replicator 2, USA). Reactor (1) in FIG. 2A consisted of a closed cell with 0₂ bubbling in a separate tank, whereas Reactor (2) in FIG. 2B allowed 0₂ bubbling directly within the reactor. Reactor (3) in FIG. 2C was an open cell reactor with 0₂ bubbling in the reactor.

[00144] The desired reactor design should offer several advantages over the stirred glass reactor of FIG. 1C, such as having more effective 0₂ diffusion into the cathode and an optimal distance between the electrodes. H2O2 decomposition from UV irradiation can also be improved by enhancing the UV irradiation of the medium, since less UV would be lost via scattering through the medium. Also, the use of 3D printing has advantages over constructing a similar flow cell by other techniques, as leakages can be prevented due to the single-body nature of the 3D printed reactor.

[00145] The efficiency of the 3D printed reactors was tested with carbon felt cathode (40 cm²) and FTO anode (15 cm²) in the following conditions: (i) dark in absence of Fe²⁺ catalyst (AO), (ii) UV in absence of Fe²⁺ catalyst (PAO), (iii) dark in presence of Fe²⁺ catalyst (EF/AO) and, (iv) UV in presence of Fe²⁺ catalyst (PEF/PAO). The distance between the 2 electrodes was kept at 1 cm in order to minimize UV attenuation through the medium while avoiding the contact of electrodes. When required, the UV lamp was placed directly facing the FTO anode glass at a distance of 1 cm. The same experimental conditions as in the cylindrical glass reactor, i.e. 1.4 mM phenol solution ([K₂S0₄] = 50 mM; pH = 3.0; [Fe²⁺] = 0.1 mM when required) and current density of 1.25 niA cm^"2, were selected in recirculated batch mode at a constant flow rate (100 ml min^"1) using a peristaltic pump (Cole Parmer, Masterflex L/S). Selection of the best performing reactor relied on monitoring phenol decay with high performance liquid chromatography (HPLC) and UV detector (280 nm) (Shimadzu, Japan). The amount of H2O2 accumulated in bulk solution was quantified by spectrophotometry (410 nm) and by performing electrolysis experiments in dark conditions and in absence of Fe²⁺ and T1O2.

[00146] Once the reactor was selected, the operating conditions were optimized by varying the current density (from 0.62 to 2.5 mA cm^"2) and the FeS0₄ concentration (from 0.05 to 0.2 mM).

[00147] Example 7: Results And Discussion - Characteristics of FTO Anode

[00148] One of the most important properties of anode material in electrochemical advanced oxidation processes is the ability to produce available ΌΗ at its surface. LSV was used to assess this characteristic by determining the oxygen evolution overvoltage from the polarization curves portrayed in FIG. 3. It can be seen that the 02-overvoltage in 0.5 M H2S0₄ solution equaled 1.6 V vs SHE, 2.1 V vs SHE and 2.3 V vs SHE for Pt, FTO and BDD anodes, respectively. The values observed for Pt and BDD are in agreement with published records. Though a value of 1.9 V vs SHE was previously determined with Sn02 anode, this is unexpectedly obtained for F-Sn02 in the present disclosure. Therefore, the overpotential value for FTO constituted a baseline for future research with such an electrode. Considering the theoretical 02- overvoltage of 1.23 V vs SHE, the value obtained with Pt showed only a small difference of 0.37 V while more significant differences of 0.87 V and 1.07 V were obtained for FTO and BDD, respectively. For this reason, chemisorbed ΌΗ on the Pt anode surface may only result in O2 production at its surface (see equations 15a and 15b below):

[00149] Pt() + H₂0→ Pt(OH) + H⁺ + e (15a)

[00150] Pt(OH) + H₂0→ Pt() +O2 + 3H⁺ + 3e (15b)

[00151] In contrast, the high overvoltage of FTO allows production of physisorbed ΌΗ from water discharge, as already noticed with BDD anode materials, according to equations 16a and 16b below:

[00152] FTO() + H₂0→ FTO(OH) + H⁺ + e (16a)

[00153] FTO('OH) + organic compound— > FTO() + oxidation products (16b)

[00154] This characteristic is very compelling because it implies the use of FTO as an anode in EAOP technology provides an additional source of ΌΗ that enhances the whole process efficiency. The transmissivity of FTO coated glass is shown in FIG. 4 and compared to the spectrum of uncoated glass (used as a control) for wavelengths ranging from 200 nm to 435 nm. For the purpose of the UV based process as discussed in the present disclosure, the wavelengths from 320 nm to 400 nm, which correspond to the UVA range (the most abundant UV radiation provided by the sun), are of prime importance. All the glass plates show no or little (approximately 1% to 2%) transmittance at wavelengths below 300 nm. At 365 nm, corresponding to the UV lamp wavelength, glass showed about 90% transmittance while 65% transmittance was observed with FTO coated plate. This demonstrates that FTO allows sufficient UV light to pass through in order for photolytic and photocatalytic processes to occur.

[00155] Therefore, FTO anode is not only a non-active anode that produces reactive ΌΗ at its surface but also a sufficiently transparent material to allow for UV penetration. The benefits from these two properties of FTO were further explored in UV based EAOPs, including their combination with T1O2 to promote PC mechanisms.

[00156] Example 8: Results And Discussion - Transmissivity of T1Q2 Coated Cylindrical Glass

[00157] To understand the relationship between concentration of T1O2 and transmissivity of the cylindrical reactor, the transmissivity of T1O2 coated cylindrical glass was first determined at different T1O2 loading (see FIG. 5). It was observed that as the concentration of T1O2 increased from 0 to 0.365 mg cm^"2, the transmissivity of the coated reactor decreased from 80% at 365 nm to 12%. In comparison, the transmittance was 50% at the lowest T1O2 loading (0.0232 mg cm^"2) at 365 nm. When tested with amber glass, which does not let wavelengths below 400 nm pass through, the transmittance achieved was the lowest amongst all tests at 1% at 365 nm. With these findings, increasing the T1O2 concentration excessively would have an adverse effect on the efficiency of pollutant degradation, which relies heavily on UV irradiation. To further demonstrate the relationship between T1O2 loading and efficiency of pollutant removal, this was investigated by monitoring the rates of MB degradation using a variety of T1O2 concentrations.

[00158] Example 9: Results And Discussion - Methylene Blue (MB) Degradation as a

Function of T1O2 Concentration

[00159] As mentioned above, FTO anode is a non-active anode that produces reactive

ΌΗ at its surface and a sufficiently transparent material to allow for UV penetration.

This allowed maximization of T1O2 concentration based on pseudo-first order kinetic model applied to the degradation of MB. The optimal T1O2 loading is 0.311 mg cm^"2.

Overall the degradation rate constant improves from one order of magnitude due to T1O2 (from <0.001 to >0.01 min^"1). The kinetic model is discussed as follows.

[00160] The kinetics of photocatalytic degradation of MB was monitored for different concentrations of T1O2 as a thin film coating. The Langmuir-Hinshelwood model is the most common expression applied to carry out the kinetics of heterogeneous PC batch systems (equation 17):

[00161] _{r =} _ s ₌ k_L__ME£ (17)

[00162] where r represents the rate of PC degradation (mol litre^"1 min^"1), £L-H is the Langmuir-Hinshelwood rate constant (mol litre^"1 min^"1), K is the equilibrium constant for adsorption of the pollutant onto the photocatalyst (litre mol^"1) and C is the concentration of the pollutant (mol litre^"1).

[00163] It is often considered for low pollutant concentration that KC is negligible beyond 1 {KC « 1), which means that equation 17 can be simplified as a first order equation to become equation 18:

[00164] _{r =} _ ££ _{= fe jrc = fe c} (18)

■&t ^,L*' ^^1,

[00165] where k_app is the pseudo-first order kinetic model (k_app = &L-HC).

[00166] After integration of equation 18 from time t = 0 to irradiation time t, the following relation can be obtained as equation 19:

[00167] = ¾^ΐ (19)

[00168] where Co is the initial concentration of the contaminant (mol litre^"1).

[00169] This pseudo-first order kinetic model was applied to the kinetics of PC degradation of MB by plotting the semi-logarithmic graph from equation 19. The model fitted the experimental data well with correlation coefficients (R²) higher than 0.981. This pseudo-first order is consistent with trends found in published works, especially during the T1O2 heterogeneous PC of MB. The kinetics rate constants were then plotted against the respective T1O2 loading as illustrated in FIG. 6A.

[00170] First, it can be seen that T1O2 PC was effective in degrading MB since a kinetics rate of 0.0044 min^"1 was observed with the lowest T1O2 concentration (0.023 mg cm^"2) as compared to the absence of T1O2 (0.0007 min^"1), which constituted a 6.3 fold improvement. Increasing the T1O2 concentration from 0.023 to 0.311 mg cm^"2 further increased the rate of MB degradation from 0.0044 to 0.0103 min^"1, which could be attributed to the increasing number of photoactive sites that raised the ΌΗ production by heterogeneous PC. It is then deduced that the optimal T1O2 concentration was around 0.311 + 0.01 mg cm^"2. At this concentration and degradation rate, the transmissivity was around 20% at 365 nm (FIG. 6B) and overall degradation was almost 65% after 90 mins of PC alone. At higher T1O2 loading (0.345 mg cm^"2) with a transmissivity of 12% at 365 nm, the kinetic rate dropped to 0.0066 min^"1, as further depicted in FIG. 6B. It seems that transmissivities lower than 20% hampered UV light going through the glass reactor which limited the availability of T1O2 photoactive sites with the UV light. The role of transmissivity have been reported in other literatures but not in a quantitative manner as carried out in the present disclosure. The optimal T1O2 loading of 0.311 mg cm^"2 was applied for subsequent experiments combining photo-electrocatalytic processes in stirred glass reactor (see example 11) and in 3D printed flow-cell reactors (see examples 12 and 13).

[00171] Example 10: Results And Discussion - Stability of T1O2 Coating

[00172] Coating stability is an important feature when industrial applications are considered. Thus, it was assessed by performing 6 successive PC experiments and the percentage of MB removed after 90 mins of irradiation is displayed in FIG. 7A. A 16% decrease was observed between the 1^st and 6^th cycle, indicating a loss of treatment efficiency as the T1O2 coating was reused. Observably, the loss of efficiency was higher between the 1^st and 2^nd cycle (10%) and then remained marginal between each of the runs from the 2^nd and the 6^th cycle (6%). This is further in agreement with the transmissivity results displayed in FIG. 7B, with a decrease of transmittance from 19.4% to 17.3% after 2 runs, while it dropped to 16.3% after 6 runs. After 5 runs, the T1O2 coating appeared stabilized. This phenomenon may be because the external layer of T1O2 was too weakly bound to the T1O2 sublayer so it was more easily removed from the glass substrate between the 1^st and 2^nd stage.

[00173] The stability of FTO was also evaluated using phenol. FIG. 7C shows the stability of FTO coating for EA/AO degradation of phenol over 5 successive runs of 90 mins each. By the 5^th run, the FTO coating remains stabilized, demonstrating that the FTO used did not degrade over time.

[00174] Example 11: Results And Discussion - Combination of PEF and PC in Stirred Glass Reactor

[00175] The testing of the electrodes in lab-scale stirred glass reactor conditions was preliminary needed before examining the efficiency of 3D printed reactors in order to figure out whether the FTO transparent electrode employed and the T1O2 coated glass substrate conditions used implied a significant improvement in the pollutant removal efficiency. The kinetics decay rate constants of phenol were determined by considering a pseudo-first order kinetic model for phenol degradation assuming a quasi-steady state approximation of the ΌΗ concentration evolution, which happens to be a frequent model applied for homogeneous catalysis. Good correlations (all R² > 0.980) were noticed between the experimental data and the kinetics model, thus validating the choice of kinetic model used.

[00176] This was also carried out to showcase the synergy achieved with multiple sources of hydroxyl radicals, which demonstrated very high mineralization efficiencies. The combined photo-electrocatalytic Fenton process reaches a degradation rate of 0.0168 min ¹ and a mineralization yield as high as 97% after 8 hours of treatment. This is more superior than each individual process performed.

[00177] The phenol degradation rate and mineralization yield (after 8 hours of treatment) were compared (FIG. 8 A and 8B, respectively) for all 13 types of processes (including the UV control experiment) susceptible to take place under various operating conditions (compare with Table 1): UV, EO/EA, EA/AO, PEO/EA, EA/PAO, EA/EF, EA/EF/AO, EA/PEF, EA/PEF/PAO, EA/AO/T1O2, EA/PAO/PC, EA/EF/AO/T1O2, EA/PEF/P AO/PC. A control experiment was previously performed under UV light but in the absence of current density and without the presence of Fe²⁺ and T1O2.

[00178] In the absence of current density and without the presence of Fe²⁺ and T1O2, UV light alone resulted in no significant degradation and mineralization (0.0003 + 0.0001 min^"1 and 1 + 0.5%, respectively) after 8 hours. This shows that phenol is not photosensitive and thus, in the absence of photocatalyst, H2O2 and/or the ferric - hydroxy complex breaks down to produce ΌΗ, the TOC concentration remained unchanged.

[00179] As more sources of ΌΗ were added to the system, the general trend was that the higher the number of sources of hydroxyl radicals, the greater the rate of degradation and mineralization yield as shown by the following mineralization yield rank efficiency (with number of ΌΗ source in brackets) (see Table 2 below): UV (0) < EO/EA (1) < PEO/EA (2) < EA/AO (2) ~ EA/AO/T1O2 (2) < EA/EF (2) < EA/PAO (3) < EA/EF/AO/T1O2 (3) ~ EA/EF/AO (3) ~ EA/PAO/PC (4) ~ EA/PEF (4) < EA/PEF/PAO (5) < EA/PEF/PAO/PC (6). However, this general trend has to be cautiously applied because not all sources of ΌΗ contribute the same treatment efficiency as discussed below.

0 E_i! C_diitts_peim_eitaonon_s0180] Table 2 - Influence of Different Sources of Hydroxyl Radicals on

[00181] In the EO/EA experiment, the EO process could be considered negligible in the presence of Pt anode that is an active anode and therefore no production of physisorbed ΌΗ occurred. The EO of phenol was then assumed insignificant in all other processes studied. Still, results demonstrate an 0.00231 min^"1 degradation rate constant and an 18.1% mineralization yield after 8 hours of experiment. The reduction of 0₂ to H2O2 still occurred at the carbon cathode, however, H2O2 has an oxidative potential of 1.776 V vs SHE that is insufficient to degrade or mineralize phenol. Therefore, the H2O2 generated at the cathode may not be the explanation for the degradation or mineralization achieved. According to available literatures, it was suggested that in situ generation of ΌΗ was observed via electro-activation of H2O2 (see equation 7). EA is thus a suitable explanation for the 0.00231 min^"1 degradation rate and 18.1% mineralization observed in the EO/EA experiment.

[00182] The introduction of UV irradiation in PEO/EA experiments increased the degradation rate from 0.00231 min^"1 to 0.00779 min^"1 and the mineralization yield from 18.1% to 28.1% due to homolytic cleavage of H2O2 under UV (see equation 14) to give a second source of ΌΗ.

[00183] The yield of ΌΗ produced from AO at the FTO anode in EA/AO and EA/AO/T1O2 processes resulted in a 2.1 times higher degradation efficiency and better mineralization efficiency (around 42%) than UV homolytic cleavage of H2O2 in PEO/EA process after deducing the contribution of EA. As expected, EA/AO and EA/AO/T1O2 processes led to the same degradation rate (around 0.01175 + 0.00005 min^"1) and mineralization yield (around 60.7 + 1.2%) as T1O2 provides no removal in the absence of UV light, which was also apparent by comparing the results of EA/EF/AO and EA/EF/AO/T1O2 with comparable degradation rate (around 0.01398 + 0.00003 min^"1) and mineralization yield (around 75.7 + 0.7%) in both cases. Moreover, the differences of degradation rate and mineralization yield between EA/PAO (0.01325 + 0.0002 min^"1 and 64.4 + 1.4%) and EA/AO (0.0118 + 0.0001 min^"1 and 60.1 + 1.2%) highlighted a slight improvement (12% increase of degradation rate and 4.3% higher mineralization yield), which again could be accredited to the additional source of ΌΗ from H2O2 photolysis (see equation 14).

[00184] The addition of Fenton catalyst (Fe²⁺) in EA/EF process led to a dramatic increase in degradation rate and mineralization yield of 0.0123 + 0.0003 min^"1 and 66.0 + 1.3%, close to EA/PAO process efficiency. This was more than 3.7- to 5.3-fold increase as compared to EO/EA while 4% increase of degradation rate and 6% higher mineralization yield as compared to EA/AO was noticed. Since both EA/EF and EA/AO implement two sources of ΌΗ, the superiority of Fenton reaction over anodic oxidation is emphasized. Therefore, it was clear that Fenton reagent has the ability to greatly increase the efficacy of catalytic treatment systems.

[00185] Furthermore, photocatalytic mineralization through the catalyst T1O2 in EA/PAO/PC experiments demonstrated an increase of degradation rate (0.0136 + 0.0002 min^"1) and mineralization yield (73.2 + 1.2%) efficiency as compared to EA/PAO (0.01325 + 0.0002 min^"1 and 64.4 + 1.4%, respectively).

[00186] The UV irradiation in Fenton process provides an increase of the degradation rate from 0.0123 + 0.0003 min^"1 to 0.0139 + 0.0001 min^"1 and mineralization yield from 66.0 + 1.3% to 75.0 + 0.6% in EA/EF and EA/PEF systems respectively, which was attributed to the two sources of ΌΗ that were introduced from H2O2 photolysis (equation 14) and ferric-hydroxy complex photolysis (equation 2). [00187] In the same way, UV light in EA/PEF/PAO implies enhancement of degradation rate from 0.01395 + 0.0002 mm ¹ to 0.0153 + 0.0003 mm ¹ and mineralization yield from 76.0 + 0.8% to 86.2 + 0.5% due to the same two additional ΌΗ sources. Thus, the additional 10% increase of degradation rate and higher mineralization yield of 10% justify the use of UV irradiation in EF systems. When T1O2 was supplemented in EA/PEF/PAO/PC experiments, the degradation rate and the mineralization degree were further raised to 0.0168 + 0.0003 min^"1 and 96.6 + 0.6% respectively that was attributed to the sixth ΌΗ source from T1O2 PC (see equations 8 to 10). This finding indicates that T1O2 is effective both with and without the application of Fenton reagent, conditional on the use of UV irradiation. To highlight the possible synergetic effect in the presence of UV (Suv), the following ratio has been calculated (equation 20):

[00188] = _{EA ipA 0}+_{nRA iBFiAei} (20) [00189] with ¾4 ? pffF wo ⁼

'^"*" and ^'Ί EA/EF/AO ⁼ _k

[00190] where ?7EA/PEF/PAO, ?7EA/PAO and ?/EA/EF/AO are the percentages of enhancement of EA/PEF/PAO, EA/PAO and EA/EF/AO processes, respectively, compared to EA/AO process, and £EA/PEF/PAO, &EA/PAO, &EA/EF/AO and &EA/AO are the pseudo-first order kinetics rate degradation constants of EA/PEF/PAO, EA/PAO, EA/EF/AO and EA/AO process, respectively (min^-1).

[00191] According to equation 20, S_uv value equaled 0.97 in uncoated stirred glass reactor, meaning that UV did not bring any synergy. In the absence of T1O2, only H2O2 photolysis (equation 14) and Fe(III)hydroxyl complexes (equation 2b) could occur in the combined processes. However, H2O2 and Fe(III) are also required to implement the Fenton reaction (equation 1) and the H2O2 electro-activation (equation 7), which means that UV-based equations (equations 2b; 14) are in competition with equations 1 and 7. To further emphasize the possible synergy in presence of T1O2 photocatalyst (Spc), this was determined as follow:

k ^p. iPBFsPA0 /PC £A fPA O fPC

[00193] with ^ EA iPEF fP&Q fPC ^~~ I and ^EAiPAQfPC ^{~ ~~}l

' ^{:' '} ' ^AEA A0 ' ^' ' ^AEA A0

[00194] where T/EA/PEF/PAO/PC and ?/EA/PAO/PC are the percentages of enhancement of EA/PEF/PAO/PC and EA/PAO/PC processes, respectively, compared to EA/AO process, and ^EA/PEF/PAO/PC and £EA/PAO/PC are the pseudo-first order kinetics rate degradation constants of EA/PEF/PAO/PC and EA/PAO/PC process, respectively (min ¹).

[00195] In a Ti02-coated stirred glass reactor, Spc value could reach 1.26 that was higher than 1. In this case, the synergy brought by the addition of T1O2 could be noticed. T1O2 PC (equations 8 to 10) does not compete with other mechanisms that are sources of ΌΗ and can even increase the rate of ΌΗ production through some other mechanisms (equations 1 and 7) by raising the accumulation of H2O2 (equations 12- 13). [00196] Still the influence of UV light on the whole pollutant removal appears too low, with Suv value lower than 1. It was therefore suggested to increase the contribution attainable from UVA irradiation by improving the reactor design to treat phenol in a 3D printed reactor.

[00197] Notwithstanding the above, the stirred glass reactor has a simple design (batch) which is sufficient to show the synergy of combining electro-Fenton and UV/TiC . When the processes are combined (EA/PEF/P AO/PC; with 6 sources of ΌΗ), an increase of 42% (T/EA/PEF/PAO/PC) is attained, which is 9% higher than what was originally expected based on the improvement observed with the addition of each processes. Originally, the improvement was expected to be a sum of the increase from EA/AO to EA/EF/AO (18%) (//EA/EF/AO) and EA/AO to EA/PAO/PC (15%) (T/EA/PAO/PC), which would have been 33% (see FIG. 8A). Hence, this demonstrates the combination of various processes within a single reactor definitely has an unexpected synergetic effect.

[00198] Example 12: Results And Discussion - Reactor Design Selection

[00199] The 3D printed reactors (see FIG. 2A to 2C) were built with the following criteria in mind to allow for a meaningful comparison with the glass reactor: (i) ensure no leakage of solution, (ii) ensure that the solution flowing through is fully saturated with oxygen, (iii) fully utilize the surface areas of the electrodes and (iv) optimize use of UVA.

[00200] Three flow-cell reactors with different designs were therefore tested in four different operating conditions (EA/AO, EA/PAO, EA/EF/AO, EA/PEF/PAO) and their impacts on phenol degradation efficiency is displayed in FIG. 9A. All R² values were higher than 0.984, which again demonstrated the good correlation between the experimental data and the pseudo-first order kinetics model.

[00201] As mentioned earlier, reactor (1) consisted of a closed cell with 0₂ bubbling in a separate tank. Reactor (2) allowed O2 bubbling directly within the reactor. Reactor (3) is an open cell with O2 bubbling in the reactor. Their performance was evaluated in terms of H2O2 production as a precursor to hydroxyl radicals.

[00202] Reactors (1) and (2) demonstrated the poorer performance because of insufficient availability of gaseous O2 in reactor (1) and buildup of air pressure in reactor (2) (FIG. 9B). These issues were mitigated in Reactor (3).

[00203] Specifically, reactor (1) demonstrated relatively poorer performance out of all the reactor prototypes and showed no change in efficiency regardless of the operating conditions applied. As there was no separate inlet to bubble O2 into the reactor (FIG. 2A), aeration was performed directly into the feeding tank. Though the solution was saturated in dissolved O2, gaseous O2 did not adsorb onto the surface of the cathode, leading to a negligible H2O2 production, with 0.03 mM of maximal H2O2 accumulation concentration as demonstrated by H2O2 concentration measurements in FIG. 9B. This lead to poor phenol degradation regardless of the conditions (between 0.0044 + 0.0002 min ¹ and 0.0051 + 0.0001 min ¹) because negligible ΌΗ could be formed from either Fenton reaction (equation 1), H2O2 electro-activation (equation 7) or H2O2 photolysis (equation 14), with the ferric-hydroxy complex photolysis (equation 2) being a negligible phenomenon with carbon felt cathode as disclosed in example 11. The main source of ΌΗ was formed through AO at the surface of FTO, which was responsible for the background decay rate constant values obtained (0.0044 min ¹). [00204] As an improvement, reactor (2) was conceived with 0₂ bubbling directly into the closed electrochemical cell (FIG. 2B), resulting in a great improvement over reactor (1) as H2O2 accumulation concentration increased (0.58 mM) along with the overall degradation rate constants, ranging from 0.0084 + 0.0003 to 0.0094 + 0.0003 min^"1.

[00205] Reactor (3) is also designed for a continuous process which again shows the synergy of combining Fe and UV as compared to each of the individual processes. In this instance, the unexpected improvement was 73% (^EA/PEF/PAO), which is 82.5% greater than the sum (40%) of 15% improvement from EA/AO to EA/EF/AO (T/EA/EF/AO) and the 25% improvement from EA/AO to EA/PAO (T/EA/PAO) (see FIG. 9C). The synergetic effect is more apparent in reactor (3) because of its design. Bearing the results of FIG. 9C in mind, when T1O2 was supplemented in EA/PEF/PAO/PC experiments, the degradation rate was advantageously raised by 115% as compared to EA/AO due to the benefit of PC.

[00206] The findings based on reactor (2) further highlight the importance of O2 in the gas state for its adsorption onto the cathode and its subsequent reduction into the 2-electrons reduction pathway to form H2O2 (see equation 5). Since carbonaceous cathodes such as carbon felt tend to be hydrophobic, they favour the gaseous O2 adsorption on their surface rather than dissolved O2. Still, reactor (2) suffered from the buildup of air pressure in an enclosed reactor and incomplete utilization of the electrode surface areas. As a solution, reactor (3) was opened at the top to allow the release of air pressure (FIG. 2C). To further improve the contact of O2 bubbles with the cathode, small diffusion holes were added at the bottom of the final reactor (FIG. 2C). To ensure even oxygen diffusion inside the reactor, the holes near the solution inlet were made smaller and they became increasingly bigger towards the solution outlet in order to deal with the changing water pressure. These changes resulted in a vast improvement in reactor (3), with H2O2 accumulation concentration of 0.93 mM and rate constants ranging from 0.0101 + 0.0003 min^"1 to 0.0175 + 0.0003 min^"1 (FIG. 9A). As compared to experiments in reactor (2), a higher enhancement was observed between PAO and PEF/PAO over the AO and EF/AO experiments, and this could be attributed to the higher rates and yields of H2O2 accumulation in reactor (3) as shown in FIG. 9B. This led to the increase of ΌΗ production yield through Fenton reaction, which is responsible for the higher removal efficiency as compared to reactors (1) and (2), and through H2O2 photolysis which is accountable for better performance of UV processes. Therefore, the superiority of reactor (3) was accredited to the two improvement of design: (i) the solution was in contact with the entire electrode surface and (ii) the fine diffusion holes at the bottom of the cathode resulted in smaller oxygen bubbles with higher surface area and improved adsorption onto the cathode.

[00207] Furthermore, the phenol removal efficiency trend for experiments carried out with reactors (2) and (3) was as follow: EA/PEF/PAO > EA/PAO > EA/EF/AO > EA/AO. Interestingly, the UV processes were better than the dark experiments, unlike the ranking established in the stirred glass experiments (see example 11).

[00208] To better assess the performance of UV processes, Suv parameter has been determined according to equation 20 and equaled a value as high as 1.87. Such great synergy can be attributed to the design of the reactor minimizing the distance between the two electrodes (10 mm) while maximizing the efficiency of the photolytic processes (see equations 2 and 14), and thus producing much more ΌΗ. Interestingly, when comparing EA/PEF/PAO process efficiency, it was observed that reactor (3) performed better (0.0175 min^"1) than the equivalent stirred glass reactor (0.0153 min^{" l}) to degrade phenol solutions. Additionally, the improvement of PEF over EF was much greater than that of the stirred glass experiments (50% improvement vs 15%). The synergy between the different processes is more apparent from 0.0101 to 0.0116 min^"1 for EF (15%) and 0.0127 min^"1 for UV (25%). Together, the improvement is equal to 0.0175 (75%), thereby showing an apparent synergertic effect.

[00209] Thus, the configuration of reactor (3) minimizes the distance that UV light would have to travel, thereby preventing attenuation of light intensity while retaining its capability to treat a large volume of effluent. This configuration was utilized for further improving operating conditions such as current density and Fe²⁺ concentration in EA/PEF/PAO process in subsequent example 13.

[00210] Example 13: Results And Discussion - Further Improvement of Reactor (3)

[00211] Improvement of the operating conditions is an important step in order to enhance process efficiency before upscale considerations. The current density was first varied between 0.62 and 2.5 mA cm^"2 and the phenol decay rate constants were determined as shown in FIG. 10A. The R² values were close to 1 (> 0.987) indicating again the reliability of the pseudo-first order kinetic model.

[00212] It can be observed that the rate constants increased from 0.0030 + 0.0002 min^"1 to 0.0214 + 0.0003 min^"1 as the current density increased from 0.62 to 1.9 mA cm^"2. Raising the current density above 1.9 mA cm^"2 decreased the degradation efficiency with rate constant value of 0.0129 + 0.0002 min^"1 at 2.5 mA cm^"2. This phenomenon could be explained by the increased rate of waste reactions including H₂ evolution (see equation 22) and H₂0₂ decomposition at the anode (equations 23a and 23b), at the cathode (equation 24) and in a lesser degree in bulk solution (equation 25):

[00213] 2H⁺ + 2e → H₂ (g) (22)

[00214] H2O2 → H0₂ ^* + FT + e (23a)

[00215] H0₂ ^* → 0₂ + FT + e- (23b)

[00216] H2O2 + 2H⁺ + 2e → 2H₂0 (24)

[00217] 2H2O2 → 0₂ + 2H₂0 (25)

[00218] These parasitic reactions counteracted H2O2 electro-generation (equation 5) and were responsible for the existence of a maximal H2O2 accumulation concentration in solution (example 12). The current density of 1.9 mA cm^"2 was therefore selected when proceeding to further improve the Fenton catalyst concentration (Fe²⁺) from 0.05 to 0.2 mM. Again, a peak for Fe²⁺ concentration is clearly shown in FIG. 10B, corresponding to a maximum kinetic rate of 0.0214 min^"1 at 0.1 mM of Fe²⁺. Above this concentration, the greater extent of the unwanted reaction between Fe²⁺ and ΌΗ (equation 26) resulted in progressive inhibition of ΌΗ generation:

[00219] Fe²⁺ + ΌΗ → Fe³⁺ + HO (26)

[00220] The optimum Fe²⁺ concentration was thus 0.1 mM.

[00221] Further improving the operating conditions, e.g. current density and Fenton catalyst concentration, increases the efficiency of reactor (3) by 1.3 fold.

[00222] Example 14: Summary of Results And Discussion in Examples 7 to 13

[00223] Examples 7 to 13 report the implementation of six sources of ΌΗ in a hybrid photo-electrocatalytic Fenton glass reactor coated with T1O2 as photocatalyst.

[00224] Based on the results, it is observed that without the presence of Fenton' s reagent, anodic oxidation provides a stronger pathway for phenol mineralization than UV homolytic cleavage. Meanwhile, the Fenton' s reagent is highly effective for phenol mineralization, especially when combined with UV irradiation, which would provide the first synergetic effect. The second synergetic effect comes from the T1O2 photocatalyst, which can be synergistically combined to photo-electro-Fenton systems to significantly enhance the phenol mineralization performance. The combination of these two synergies further creates an unexpected synergetic effect as illustrated in the above examples.

[00225] The use of FTO as non-active transparent anode ( -overvoltage of 2.1 V vs SHE) and a 3D carbon felt cathode in a stirred reactor successfully chemically degraded phenol (a model pollutant) with degradation rate constant of 0.0168 min^"1 and 97% of mineralization after 8 hours of treatment. In the present systematic study carried out, Fenton and AO processes have shown great improvement in phenol degradation and mineralization in that reactor. UVA irradiation contribution could not bring synergy (Suv = 0.97) while in presence of T1O2 the PC provided synergy (Spc = 1.26). A 3D printed reactor was designed as a flow-through cell to improve UV-based processes and was then optimized. Aeration was provided directly at the site of H2O2 production, i.e. as close as possible to the carbon cathode with an open air design in one of the 3D reactors (i.e. reactor (3)). The inter-electrode distance was kept as close as possible (1 cm in this case) in order to fully utilized photons energy through the transparent anode. Due to these configurations, the implementation of UV-based processes implied a synergy (Suv = 1.87) and yielded better degradation efficiency as compared to dark experiments and the EA/PEF/PAO process reached 14.4% increase of degradation rate as compared to the stirred glass reactor. This rate could further be increased by 22.3%, i.e. 40% increase in total, under optimized conditions of current density (1.9 mA cm^"2) and Fenton catalyst concentration (0.1 mM). The reactors thus serves as a proof-of-concept design for the novel usage of transparent electrodes, in this case FTO, to improve wastewater treatment in photo-electrocatalytic processes. The preparation of T1O2 coated FTO glass may be further improve to enhance performance of the 3D-printed reactor.

[00226] Example 15: Summary of Stirred Glass Reactor Configuration and 3D Printed Reactor Configurations

[00227] A summarized observation of these configurations include (1) FTO could be classified as a high O2 evolution overvoltage anode (2.1 V vs SHE), (2) transmittance of Ti02-coated FTO was high enough (65%) to involve photo-reactions, (3) photo- electro-catalytic Fenton process was the best process in a stirred glass reactor and (4) optimized 3D-printed flow-cell could improve the UV-based processes efficiency.

[00228] The Ti02-coated stirred glass reactor was designed consisting of a film of fluorine-doped tin oxide (FTO) coated on glass transparent anode and a three- dimensional (3D) porous carbon felt cathode. Linear scan voltammetry (LSV) measurements depicted for FTO an O2 evolution overvoltage of 2.1 V vs SHE, high enough to form available hydroxyl radicals (ΌΗ) through anodic oxidation (AO). By letting the UVA light shine through the glass reactor coated with optimal T1O2 loading (0.311 mg cm^"2), heterogeneous photocatalysis (PC) occured leading to a second source of ΌΗ. Combined to a 3D carbonaceous cathode and addition of catalytic amount of Fe²⁺, four more sources of ΌΗ could be implemented through H2O2 electro-activation (EA), Fenton reaction, H2O2 photolysis and Fe(III)-hydroxy complex photolysis. This combined photo-electro-catalytic Fenton process allow reaching a phenol degradation rate of 0.0168 min^"1 and a mineralization yield as high as 97% after 8 h of treatment It was far better than each individual process performed for comparison. For example, a 37% increase and a 42% increase of phenol degradation rate was observed as compared to conventional EF and AO processes, respectively. The implement of UVA irradiation without photocatalyst could enhance the removal efficiency but still the synergy (Suv = 0.97) could not be demonstrated, unlike in the presence of T1O2 (Spc = 1.26). To further maximize the contribution of UVA irradiation for oxidation efficiency, the 3D printed flow-cell reactor was thus designed and employed. The electrode distance and the contact between gaseous 0₂ and the carbon cathode were considered in the design. The UVA irradiation through the FTO anode (transmissivity of 65%) improves the kinetics of photolytic reactions by being more performant than the dark processes, with synergy value (Suv) as high as 1.87. Due to these enhancement, the global phenol degradation rates were even higher (0.0175 min^-1) than within the stirred glass reactor (0.0153 min^-1). After optimization of current density and Fe²⁺ concentration, the kinetics rate of degradation yielded 0.0214 min^"1, which is a significant improvement even before considering upscaling of such combined process. The illustrated comparison between the stirred glass reactor configuration and an embodiment of the 3D printed cell is shown in FIG. 11.

[00229] Example 16: Commercial Utility and Applications

[00230] The technology as described in the present disclosure may be used in conjunction with prospective applications that utilizes (i) solar energy as a free and infinite source of natural UV light and/or (ii) solar panels as the power source for the photoelectrochemical process. The outcome is a type of photoelectrochemical reactor as described above that harvests energy from the sun and treats water in the process.

[00231] For example, Singapore targets to generate 4 TWh/yr of solar energy. This may be achieved partly via floating photovoltaics (PV) structures on freshwater and seawater. The photoelectrochemical reactor may be coupled to these PV structures and thus the solar photoelectron-Fenton technology as discussed herein may then utilize an infinitesimal amount of this PV electricity to ensure high standards of water quality and public health.

[00232] With the above in mind, the subject matter as disclosed herein may be incorporated in the design and development of a mobile solar photoelectrochemical reactor (MSPER) with various potential applications in both engineered and natural environments.

[00233] Applications in engineered and natural environments may include wastewater treatment plants (especially industrial wastewater for the removal of industrial contaminants), remediation of contaminated and hazardous sites (e.g. landfills, acid mine drainage, SUPERFUND sites (polluted locations requiring a long term response to clean up hazardous material contaminations) etc.), freshwater reservoirs for algal control and removal of pathogens and emerging contaminants, marine environments contaminated by shipping activities to take advantage of the high conductivity of seawater (acting as a natural electrolyte), and/or green buildings (e.g. for decentralized treatment of grey water). In one example, the technology as described in the present disclosure can be used to degrade and mineralize biorefractory solutions such as industrial wastewater or disinfect and control algal blooms in reservoirs by making use of natural sunlight with very fast kinetics and very high percentage removal (>96.5%) in a cost effective way.

[00234] Regarding the MSPER, it may comprise 4 main elements: (i) an electrolytic cell, (ii) a motion system, (iii) an energy supply & storage system and (iv) a supporting structure. Different electrodes making use of conductive materials, either opaque, translucent or transparent (to facilitate the penetration of sunlight), may be tested. A beachhead application which utilizes the present subject matter may be sought. This may be supported by a comprehensive technical-economic analysis and/or a pilot installation may be implemented.

[00235] Other advantages of the technology developed is the portability and non- reliance on a centralized power supply. This falls right within the interests of those focusing on urban solutions and sustainability, and the development of resilient engineering systems. With the uncertainty in demographic changes and disruptive threats (climate change, terrorist threat, end of oil etc.), the subject matter of the present disclosure may serve as a solution that can assist in the preservation of water sources.

[00236] While the invention has been particularly shown and described with reference to specific embodiments, it should be understood by those skilled in the art that various changes in form and detail may be made therein without departing from the spirit and scope of the invention as defined by the appended claims. The scope of the invention is thus indicated by the appended claims and all changes which come within the meaning and range of equivalency of the claims are therefore intended to be embraced.

[00237] For example, while in the described example embodiments the anode is optically pervious, alternatively or additionally the cathode may be optically pervious in different embodiments. For example, a transparent carbon cathode such as graphene coated on glass or quartz may be used.

Claims

1. A photoelectrochemical cell for wastewater treatment comprising

- at least one cathode and at least one anode, wherein the anode comprises a material configured for an anodic oxidation reaction in the presence of the wastewater, wherein at least one of the anode and cathode comprises an optically pervious material,

- the cathode configured for cooperating with the anode to drive one or more cathodic reduction reactions in the presence of the wastewater, and

- wherein the anode and the cathode are disposed to allow irradiation of at least a portion of a space between the anode and the cathode by a light source through the optically pervious material to activate at least one photon based reaction in the wastewater.

2. The photoelectrochemical cell according to claim 1, wherein the material is selected from the group consisting of fluorine-doped tin oxide (FTO), indium tin oxide (ΓΓΌ), boron-doped diamond (BDD), tin oxide (Sn0₂), lead oxide (Pb0₂), Ti₄0₇ and combinations thereof.

3. The photoelectrochemical cell according to claim 1 or 2, wherein the wastewater optionally comprises Fe²⁺, Fe³⁺ and/or ferric hydroxyl complexes.

4. The photoelectrochemical cell according to any one of claims 1 to 3, wherein the optically pervious material comprises glass or quartz.

5. The photoelectrochemical cell according to any one of claims 1 to 4, wherein the one or more cathodic reduction reactions comprise reduction of oxygen, reduction of Fe³⁺ and/or electro-activation of hydrogen peroxide.

6. The photoelectrochemical cell according to any one of claims 1 to 5, wherein the anode and the cathode are disposed to face each other in the photoelectrochemical cell while remaining spaced apart by a distance of about 10 mm to about 30 mm or a distance of less than about 10 mm.

7. The photoelectrochemical cell according to any one of claims 1 to 6, further comprising a chamber having a base portion and a wall portion extending from the base portion, wherein the anode and the cathode are disposed in the chamber.

8. The photoelectrochemical cell according to claim 7, wherein the chamber is integrally formed with the anode and the cathode defining part of the wall portion of the chamber.

9. The photoelectrochemical cell according to any one of claims 1 to 8, further comprising an inlet and an outlet at the wall portion of the chamber, wherein the inlet and the outlet are in fluid communication with the chamber and are disposed at opposing ends of the chamber.

10. The photoelectrochemical cell according to claim 9, wherein the base portion of the chamber comprises one or more openings, and when more than one openings are present, the openings are arranged in order of increasing cross-sectional area with increasing distance from the inlet to the outlet.

11. The photoelectrochemical cell according to any one of claims 1 to 10, further comprising a photocatalyst disposed on an inner base portion and/or an inner wall portion of the chamber to allow irradiation of at least the portion of the space between the anode and the cathode.

12. The photoelectrochemical cell according to claim 11, wherein the photocatalyst is disposed as a layer on the anode.

13. The photoelectrochemical cell according to any one of claims 1 to 12, further comprising an optical medium configured to increase incident light on the optically pervious material.

14. The photoelectrochemical cell according to any one of claims 1 to 13, further comprising an aerator configured to provide oxygen gas to the photoelectrochemical cell, wherein the aerator is in fluid communication with the one or more openings at the base portion of the chamber.

15. The photoelectrochemical cell according to any one of claims 1 to 14, further comprising a dispensing device configured to dispense an aqueous solution comprising Fe²⁺, Fe³⁺ and/or ferric hydroxyl complexes to the photoelectrochemical cell.

16. The photoelectrochemical cell according to any one of claims 1 to 15, wherein the at least one photon based reaction comprises hydrogen peroxide photolysis, ferric hydroxyl complex photolysis, photocatalysis of water and/or photo-oxidation of OH^".

17. A method of fabricating a photoelectrochemical cell, the method comprising providing at least one cathode and at least one anode, wherein the anode comprises a material configured for an anodic oxidation in the presence of the wastewater, wherein at least one of the anode and cathode comprises an optically pervious material,

configuring the cathode for cooperating with the anode to drive one or more cathodic reduction reactions in the presence of the wastewater, and

disposing the anode and the cathode to allow irradiation of at least a portion of a space between the anode and the cathode by a light source through the optically pervious material to activate at least one photon based reaction in the wastewater.

18. The method according to claim 17, wherein disposing the anode and the cathode comprises arranging the anode and the cathode to face each other in the photoelectrochemical cell while remaining spaced apart by a distance of about 10 mm to about 30 mm or a distance of less than about 10 mm.

19. The method according to claim 17 or 18, wherein arranging the anode and the cathode comprises providing a chamber having a base portion and a wall portion extending from the base portion, and disposing the anode and the cathode in the chamber.

20. The method according to claim 19, wherein providing the chamber having a base portion and a wall portion extending from the base portion comprises integrally forming the chamber with the anode and the cathode defining part of the wall portion of the chamber.

21. The method according to claim 19 or 20, wherein providing the chamber comprises integrally forming the chamber by 3D printing.

22. The method according to any one of claims 19 to 21, wherein providing the chamber comprises forming an inlet and an outlet at the wall portion of the chamber, wherein the inlet and the outlet are in fluid communication with the chamber and are disposed at opposing ends of the chamber.

23. The method according to any one of claims 19 to 22, wherein providing the chamber comprises forming one or more openings in the base portion, and wherein forming more than one openings comprises forming the openings in order of increasing cross-sectional area with increasing distance from the inlet to the outlet.

24. The method according to any one of claims 17 to 23, further comprising a step of disposing a photocatalyst on an inner base portion and/or an inner wall portion of the chamber to allow irradiation of at least the portion of the space between the anode and the cathode.

25. The method according to claim 24, wherein disposing the photocatalyst comprises disposing the photocatalyst as a layer on the anode.

26. The method according to any one of claims 17 to 25, further comprising providing an optical medium configured to increase incident light on the optically pervious material.

27. The method according to any one of claims 17 to 26, further comprising providing an aerator configured to provide oxygen gas to the photoelectrochemical cell, wherein providing the aerator comprises disposing the aerator to be in fluid communication with the one or more openings at the base portion of the chamber.

28. The method according to any one of claims 17 to 27, further comprising providing a dispensing device configured to dispense an aqueous solution comprising Fe²⁺, Fe³⁺ and/or ferric hydroxyl complexes to the photoelectrochemical cell.