WO2017136409A1

WO2017136409A1 - Functional polymer binder for sulfur cathode fabrication

Info

Publication number: WO2017136409A1
Application number: PCT/US2017/015990
Authority: WO
Inventors: Gao Liu; Min LING; Changan YANG
Original assignee: University of California Berkeley; University of California San Diego UCSD
Current assignee: University of California Berkeley; University of California San Diego UCSD
Priority date: 2016-02-01
Filing date: 2017-02-01
Publication date: 2017-08-10
Anticipated expiration: 2018-08-01
Also published as: US20180351161A1; US10601030B2

Abstract

A Lithium-Sulfur (Li-S) battery comprising a cathode comprising a polymeric conductive binder (Formula (I)) Poly[(2-ethyldimethylammonioethyl methacrylate ethyl sulfate)-co-(1-vinylpyrrolidone)], a separator, an anode, and an electrolyte.

Description

Functional polymer binder for sulfur cathode fabrication

Inventors: Gao Liu, Min Ling, and Changan Yang

CROSS REFERENCE TO RELATED APPLICATIONS

[0001] This PCT Application claims priority to US Provisional Application Serial No.

62/289,456 filed February 1, 2016, which application is incorporated herein by reference as if fully set forth in its entirety.

STATEMENT OF GOVERNMENTAL SUPPORT

[0002] The invention described and claimed herein was made in part utilizing funds supplied by the U.S. Department of Energy under Contract No. DE-AC02-05CH11231 between the U.S. Department of Energy and the Regents of the University of California for the management and operation of the Lawrence Berkeley National Laboratory. The government has certain rights in this invention.

BACKGROUND OF THE INVENTION

Field of the Invention

[0003] The present invention relates to the field of Lithium-Sulfur (Li-S) Batteries.

Related Art

[0004] Lithium- sulfur (Li-S) has the highest theoretical specific and volumetric energy densities of any rechargeable battery chemistry (2550 Wh/kg and 2862 Wh/L). The best Li-S batteries can offer around 350 Wh/kg and 320 Wh/L currently, which is still significantly better than LIBs (150-200 Wh/kg). The high capacity is based on the conversion reaction of sulfur to form lithium sulfide (Li₂S) by reversibly incorporating two electrons per sulfur atom compared to one or less than one per transition-metal ion in insertion oxide cathodes. A sulfur cathode suffers from poor cyclability, which is mainly due to the shuttling effect of polysulfides and low conductivity. To unlock this potential battery, efforts have been made such as carbon accommodation/coating, electrolyte additives, membrane and lithium anode modification, however, none of these were commercially available until now. The efforts for developing high-performance lithium sulfur batteries can be generalized as follows.

[0005] Appropriate dispersion of active sulfur: Although the solid-phase sulfur transforms into soluble polysulfides during cycling and changes its initial morphology, the utilization of the active material will be low if sulfur has insufficient contact with conductive agents;

[0006] Efficient absorbing materials: Novel multi-functional and porous materials need to be designed for effectively absorbing and accommodating the active material;

[0007] Stable electrolyte system: A more reliable electrolyte is preferred to have a controlled dissolution of the polysulfides and to be compatible with the lithium metal anode;

[0008] Safe anode materials: A lithium metal anode in liquid electrolytes poses safety concerns due to lithium dendrite development during cycling. To address this problem, use of a protected lithium metal anode or alternative Li/M (M=Si, Sn, C, etc.) alloys is a feasible approach for building a safer lithium sulfur battery.

[0009] Since divinyloxyhydroxyolysulphides was first developed as an alternative binder for Li- S batteries, polymers including gelatin, polyethylene oxide, polyacrylic acid, carboxyl methyl cellulose, polyvinylpyrrolidone and carbonyl-P-cyclodextrin were identified as promising binders to address this shuttle issue. Besides the better dispersion and distribution properties, the existence of carbonyl groups play a pivotal role in the improved cycle performance. The electron-rich oxygen with lone pairs is favourable to form lithium-oxygen (Li-O) bond with lithium polysulphides. This phenomenon was further verified by the carbonylation reaction of β- cyclodextrin. The introduction of carbonyl groups promoted the electrochemical performance of sulfur electrode.

BRIEF DESCRIPTION OF THE DRAWINGS

[0010] The foregoing aspects and others will be readily appreciated by the skilled artisan from the following description of illustrative embodiments when read in conjunction with the accompanying drawings.

[0011] Figure 1A illustrates C-S single bond formation between polyvinylsulfate (PVS) and polysu!phides evidenced by Raman spectra. Figure 1 B illustrates polysulphide reservation capability comparison between PVS and PVDF through low rate cycling performance.

[0012] Figures 2A and 2B illustrate characterization of chemical bonds between MPS and polysulphide. Figure 2A illustrates TFY spectra. Figure 2B illustrates FTIR spectra.

[0013] Figures 3 A and 3B illustrate cycling performance of high-loading sulfur electrodes based on MPS at vary C rates. Figure 3C illustrates coulombic efficiency, and Figure 3D illustrates discharge/charge voltage profiles of various C rate.

[0014] Figure 4 illustrates SEM images of sulfur electrodes with different magnification. Fresh sulfur electrode (a, b, c, d); fully discharged electrode (e, f, g, h); Fully charged electrode (i, j, k, 1). (Magnification: a, c. e 1200x; b, f, J 2000x; c, g, k 5000x; d, h, 1 lOOOOx).

[0015] Figure 5 illustrates cycling performance of high-loading sulfur electrodes based on PECH, PVC and PVDF.

[0016] Figures 6A and 6B illustrate cycling performance of high-loading sulfur electrodes based on Poly[(2-ethyldimethylammonioethyl methacrylate ethyl sulfate)-co-(l-vinylpyrrolidone)] at C/20.

[0017] Figure 7 illustrates cycling performance of high-loading sulfur electrodes based on Poly[(2-ethyldimethylammonioethyl methacrylate ethyl sulfate)-co-(l-vinylpyrrolidone)] specifically the dis-charge/charge voltage profiles of the 20th cycle. DETAILED DESCRIPTION

[0018] In the discussions that follow, various process steps may or may not be described using certain types of manufacturing equipment, along with certain process parameters. It is to be appreciated that other types of equipment can be used, with different process parameters employed, and that some of the steps may be performed in other manufacturing equipment without departing from the scope of this invention. Furthermore, different process parameters or manufacturing equipment could be substituted for those described herein without departing from the scope of the invention.

[0019] These and other details and advantages of the present invention will become more fully apparent from the following description taken in conjunction with the accompanying drawings.

[0020] Herein, we demonstrate a class of innovative polymer binder materials and strategy to address the challenge of poly sulphides dissolution and the shuttle effect. A series of functional polymers with potential to have nucleophile reaction with polysulphides were designed to retain polysulphide in the surface electrode. The number of factors governing reactivity in nucleophilic reaction includes polarizabilities of both nucleophile and leaving group, stability of leaving group and interaction between nucleophile and leaving group. To capture the polysulphides, the choice of leaving group is the key issue. Nucleophile reaction involving good leaving groups has low activation barriers. A good leaving group must be able to stabilize a large negative charge in the transition state and product. A good measure of anion stability is the pKa of an anion' s conjugate acid, with lower pKaH's being associated with better leaving group ability. Based on this, sulphate and halide ions, e.g., F, CI, Br, L and related polymers were adopted. The other important factor for the nucleophilic reaction is the location of leaving groups. The leaving groups at the primary carbon are preferred rather than at the secondary carbon, and the least preferred is at the tertiary position.

[00211 Examples of detailed mechanisms are illustrated in scheme 1 .

[0022] Scheme 1. Chemical capture of diffusing lithium polysulphides through nucleophilic attack of lithium polysulphide to sulphate and halide ions in DOL/DME electrolyte. A.

poly vinylsulf ate (PVS). B. λ-carrageenan (MPS). C. Poly(epichlorohydrin) (PECH), D. Polyvinyl Chloride (PVC), E. Poly(epibromohydrin) (PEBH) F. Poly(epiiodhydrine) (PEIH) [0023] Based on the above polymers illustrated in scheme 1, we built and tested high areal capacity electrodes which could buffer the polysulfides shuttle effect and help to maintain the mechanical integrity of the sulfur electrode. A simple, cheap, scalable and versatile way was chosen to obtain sulfur electrodes with high binding capability, the property gain in terms of electrochemical performance (high areal capacity with high current density) is demonstrated, which proves our approach that an effective binder is a key factor to improve the loading of sulfur electrodes. This discovery will enable high capacity, low cost and large scale production of Li-S cells based on binders. The strategy developed here may also be applied to other rechargeable battery systems.

[0024] In various embodiments, we show a polymer strategy with sulfate and halide ions groups that can provide effective binding sites for lithium poly sulfides. The strategy of this approach is not only to limit the outbound diffusion of the soluble Li₂Sn molecules, but also to capture the soluble species in the electrolyte to alleviate the polysulfides shuttle effect to achieve

commercial promising cycle performance.

[0025] To execute this method, micro- sulfur powders were mixed with conductive additives (acetylene black, eg. super C₆5) through various binders to form slurry. The slurry was then coated onto an aluminum foil using doctor blade and dried vacuum to form the working electrode. Li-S batteries are tested with 2325-type coin cell (National Research Council Canada) in an argon-filled glove box using lithium foil as the counter electrode. The size of the sulfur electrode and counter-electrode lithium metal disk is ½ and 11/16 -in. OD, respectively. The Li foil is purchased from FMC-Lithium Co. The separator is polypropylene film (Celgar 2400). The electrolyte used was a freshly prepared solution of lithium bis(trifluoromethanesulfonyl)imide (1M) in 1: 1 v/v 1,2-dimethoxyethane and 1,3-DOL containing L1NO3 (2 wt%). The assembled cells were placed on the channels (Maccor Inc.) at 30 °C for lithiation-delithiation cycles. The voltage window for cell test is 1.8-2.6 V.

[0026] The nucleophilic reaction initiates the connection since the reduction of elemental sulfur to high-order soluble polysulphide resulting in shuttle effect alleviation. Raman spectra in Figure 1 A verify the evolution including leave of sulfate groups and formation of C-S single bond in the intermediate molecules. The peak corresponds to the vso4^2" is centered at 981 cm^"1. The appearance of peak at 675 cm^'1 confirmed the C-S bonding. After mechanism clarification, excellent cyclability with micro-sulfur particles was demonstrated based on PVS at room temperature. The cathode shows high initial discharge capacity of ca. 1500 niAh/g (based on the incorporated sulfur content) with 100% of coulombic efficiency after a few initial cycles. The cathode capacity can hold up to 900 mAh/g after 100 cycles. The capacity retention for PVS based electrode is clearly more advantageous at C/20 than a PVDF based electrode. Since the unicjue variable between PVS and PVDF is sulfate and fluorine, the effect of sulfate can be confirmed accordingly. This observation confirms that the PVS has extremely strong chemical bonding with diffusing polysulphides to achieve improved cycle performance.

[0027] Figure 1A illustrates C-S single bond formation between PVS and polysulphides evidenced by Raman spectra. Figure 1 B illustrates poly sulphide reservation capability comparison between PVS and PVDF through low rate cycling performance.

High areal capacity based on λ-carrageenan (MPS).

[0028] Figures 2A and 2B illustrate characterization of chemical bonds between MPS and polysulphide. Figure 2A illustrates TFY spectra. Figure 2B illustrates FTIR spectra.

[0029] To extend the sulfate function in PVS and a simplified manufacturing process, a sulfated natural polymer λ-carrageenan (MPS), with high binding strength was evaluated to achieve high sulfur loading. The chemical bonding between MPS and polysulphides was initially verified as PVS. We applied S K-edge absorption spectra (XAS ) to monitor the formation of chemical bonds between MPS and S. We simulated sample preparation processes by thermally treating in the DOL/DME electrolyte for 24 hours. The S K-edge XAS data of the mixtures recorded from the total fluorescence yield (TFY) before and after the treatment are presented in Figure 2A. Before annealing, TFY spectra show peaks located at 2481.17 and 2483.56 are attributed to the R-SO3O-S₀* and SO c sr.-. respectively. The emerging peak at 2473.67 after treatment confirms the existence of C-S bond in the bulk material. In order to investing the evolution of the chemical bonding. Fourier Transform Infrared Spectroscopy (FTIR) was performed to demonstrate the leaving of sulfate group and forming of C-S bond. The decrease of easter sulfate and galactose sulfate vibration is indicated in Figure 2B.

[0030] Figures 3 A and 3B illustrate cycling performance of high-loading sulfur electrodes based on MPS at vary C rates. Figure 3C illustrates Coulombic efficiency and Figure 3D illustrates discharge/charge voltage profiles of various C rate.

[0031] To confirm the expected cycle performance of the high loading sulfur electrodes, the galvanostatic charge/discharge profiles are shown in Figures 3A, 3B, 3C, 3D. With MPS. the electrodes suffer both capacity fading and an increasing divergence between the charge and discharge capacity as a result of the polysulphide shuttle mechanism. A discharge capacity of 8.8 mAh/cm² is achieved after the electrolytes penetrate the thick electrodes, afterwards, the capacity is maintained at around 6 mAh/cm² for more than 120 cycles, corresponding to a specific capacity of around 850 mAh/g (Figures 3A, 3B). Specifically, the capture of polysulphides is well evidenced by the cycle performance at 0.05 C. In comparison, cells based on PVDF binder suffered from rapid capacity decay, indicating a greater degree of poly sulfides dissolution into the electrolyte. The average Coulombic efficiency based on MPS is calculated to be more than 96% over 100 cycles, which shows little shuttle effect owing to polysulphides dissolution (Figure 3C). As shown in Figure 3d, two well-defined discharge plateaus were observed, which could be assigned to the multistep reduction mechanism of elemental sulfur.

[0032] To track the morphology evolution during lithiation/delithiation processs, the scaning electron microscopy (SEM) images are shown in Figure 4. A clear porous structure is performed at vary scale for fresh electrode before cycle. When the cells are disassembled at fully discharged state, no delamination is observed in the electrode and none of the reddish color electrolyte, which is typical color of polysulphides. A homogeneous Li₂S precipitation is observed at the top of the electrode, indicating good conductivity of the electrode. Moreover, the good reversibility is well evidenced through the decomposition of Li₂S layer after fully charged. The sulfur and carbon elemental maps also clearly demonstrate that sulfur is homogeneously distributed in the framework of electrode. The increasing content of oxygen after discharge is supposed to be attributed by the leaving sulfate group from the bulk electrode.

[0033] Figure 4 illustrates SEM images of sulfur electrodes with different magnification. Fresh sulfur electrode (a, b, c, d); fully discharged electrode (e, f, g, h); Fully charged electrode (i, j, k, 1). (Magnification: a, c. e 1200x; b, f, J 2000x; c, g, k 5000x; d, h, 1 lOOOOx).

[0034] The molecular structure of Poly(epichlorohydrin) (PECH) and Polyvinyl Chloride (PVC) is demonstrated in scheme 1 . In comparison with PVDF, the chloro group is at the primary carbon position in PECH. Therefore, the chloro group is more active than that of PVC. This will facilitate the nucleophilic attack by polysulfide to PECH. The effect is verified by the comparison of the cycle performance as shown in Figure 5. The PECH binder based sulfur electrode can achieve around 2 times of the areal capacity than that of the PVC binder based sul ur electrode.

[0035] In summary, an innovative class of polymer binders and simple electrode fabrication strategy is first successfully applied to solve the lithium sulfides shuttle effect through nucleophilic attack formed carbon-sulfur (C-S ) bonding. The function of the C-S bonding is evidenced by the achieved areal capacity, i.e., 6 mAh/cm², for more than 100 cycles at C/20. The Coulombic efficiency is maintained up to 96% during the cycling. The nucleophilic attack during the lithiation/delithiation is monitored through Raman, TFY and FTIR spectroscopies. This low cost and efficient design is of significance for the progress of lithium-sulfur batteries.

[0036] Polymeric systems bearing positive charges are synthesized in the presence of novel cationic entities, incorporated on their backbone and/or as side chains, are considered as cationic polymers. Poly(vinylbenzyl chloride)-co-poly(vinylbenzyl trimethylammonium chloride) (PVBNC) and Poly[(2-ethyldimethylammonioethyl methacrylate ethyl sulfate)-co-(l- vinylpyrrolidone)] are promising cationic polymers since its low cost and wide application. (Scheme 2 and 3) As illustrated above, the dissolution and shuttle effect of polysulfides intermediate produced after lithiation/delithiation is the most challenging issue for lithium sulfur batteries. Cationic polymers have the potential to ionically bonded with polysulfides anions.

[0037] Figs. 6A, 6B illustrate cycling performance of high-loading sulfur electrodes based on Poly[(2-ethyldimethylammonioethyl methacrylate ethyl sulfate)-co-(l-vinylpyrrolidone)] C/20.

[0038] Figure 7 illustrates cycling performance of high-loading sulfur electrodes based on Poly[(2-ethyldimethylammonioethyl methacrylate ethyl sulfate)-co-(l-vinylpyrrolidone)] specifically the dis-charge/charge voltage profiles of the 20th cycle.

[0039] The electrochemical performance of the sulfur electrode in Figures 6 A, 6B, and 7 based on cationic polymer Poly[(2-ethyldimethylammonioethyl methacrylate ethyl sulfate)-co-(l- vinylpyrrolidone)]. The specific capacity can be held for more than 1000 mAh/g for 20 cycles, meanwhile, the areal capacity is maintained above 5 mAh/cm². The cycle performance provides strong evidence of alleviation of polysulfides shuttle effect and promotion of sulfur utilization.

Scheme 2. The molecular structure of Poly[(2-ethyldimethylammonioethyl methacrylate ethyl sulfate)-co-(l-vinylpyrrolidone)].

Scheme 3. Binder Poly(vinylbenzyl chloride)-co-poly(vinylbenzyl trimethylammonium chloride) (PVBNC) used for Sulfur electrode.

Claims

What is claimed is:

1. A composition of matter comprising:

Poly[(2-ethyldimethylammonioethyl methacrylate ethyl sulfate)-co-(l-vinylpyrrolidone)].

2. A polymeric conductive binder comprising:

3. An electrode comprising : a polymeric conductive binder

4. A Lithium- Sulfur (Li-S) battery comprising: a cathode further comprising a polymeric conductive binder

Poly[(2-ethyldimethylammonioethyl methacrylate ethyl sulfate)-co-(l-vinylpyrrolidone)]; a separator;

an anode; and

an electrolyte.