WO2017082958A1 - Acoustic prepregs, cores and composite articles and methods of using them - Google Patents
Acoustic prepregs, cores and composite articles and methods of using them Download PDFInfo
- Publication number
- WO2017082958A1 WO2017082958A1 PCT/US2016/031585 US2016031585W WO2017082958A1 WO 2017082958 A1 WO2017082958 A1 WO 2017082958A1 US 2016031585 W US2016031585 W US 2016031585W WO 2017082958 A1 WO2017082958 A1 WO 2017082958A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- expandable graphite
- thermoplastic
- composite article
- graphite material
- article
- Prior art date
Abstract
Description
Claims