WO2017075126A1 - Steam-assisted production of metal silicate cements, compositions and methods thereof - Google Patents

Steam-assisted production of metal silicate cements, compositions and methods thereof Download PDF

Info

Publication number
WO2017075126A1
WO2017075126A1 PCT/US2016/058981 US2016058981W WO2017075126A1 WO 2017075126 A1 WO2017075126 A1 WO 2017075126A1 US 2016058981 W US2016058981 W US 2016058981W WO 2017075126 A1 WO2017075126 A1 WO 2017075126A1
Authority
WO
WIPO (PCT)
Prior art keywords
ground mixture
cement
calcium
temperature
steam
Prior art date
Application number
PCT/US2016/058981
Other languages
French (fr)
Inventor
Vahit Atakan
Original Assignee
Solidia Technologies, Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Solidia Technologies, Inc. filed Critical Solidia Technologies, Inc.
Priority to EP16860743.0A priority Critical patent/EP3368495A4/en
Priority to CN201680076651.6A priority patent/CN108883988B/en
Publication of WO2017075126A1 publication Critical patent/WO2017075126A1/en

Abstract

The invention provides a novel, steam-assisted production methodology and associated compositions and methods of use in the manufacture of carbonatable or non-carbonatable metal silicate or metal silicate hydrate (e.g., calcium silicate or calcium silicate hydrate) compositions. These metal silicate compositions and related phases are suitable for use hydraulic, partially hydraulic or non-hydraulic cement that sets and hardens by a hydration process, a carbonation process or a combination thereof, and may be applied in a variety of concrete components in the infrastructure, construction, pavement and landscaping industries.

Description

STEAM-ASSISTED PRODUCTION OF METAL SILICATE CEMENTS, COMPOSITIONS AND METHODS THEREOF
Priority Claims and Related Patent Applications
[0001] This application claims the benefit of priority from U. S. Provisional Application Serial No. 62/247,590, filed on October 28, 2015, the entire content of which is incorporated herein by reference in its entirety.
Field of the Invention
[0002] The invention generally relates to cement technologies and metal silicate compositions. More particularly, the invention relates to a novel, steam-assisted production methodology in the manufacture of non-carbonatable or carbonatable metal silicate or metal silicate hydrate (e.g., calcium silicate or calcium silicate hydrate) materials, and the associated compositions and methods of use. These metal silicate compositions and related phases (collectively referred to as "cementitious metal silicate compositions") are suitable for use as hydraulic, partially hydraulic or non-hydraulic cement that sets and hardens by a hydration process, a carbonation process or a combination thereof, and may be applied in a variety of concrete components in the
infrastructure, construction, pavement and landscaping industries.
Background of the Invention
[0003] Concrete is the most consumed man-made material in the world. A typical concrete is made by mixing cement, water and aggregates such as sand and crushed stone. Cementitious materials have been synthesized from limestone and shale, which are the calcium and silica sources, respectively. The raw materials are ground either together or separately and then fired together to form calcium rich calcium silicates. This process requires very high temperatures such as 1500 °C. Portland cement, for example, is made by burning a mixture of ground limestone and clay, or materials of similar composition in a rotary kiln at a sintering temperature of 1450 °C. Portland cement manufacturing is thus highly energy-intensive and releases considerable quantities of greenhouse gas.
[0004] There is an ongoing need for improved cement production methods that significantly reduce the energy requirement, are more environmentally friendly, and give rise to improved product performance. For instance, improvements that allow production at lower temperatures and/or with a broader array of source materials are desirable.
Summary of the Invention
[0005] The invention provides a novel, steam-assisted production methodology and relates to compositions of non-carbonatable or carbonatable metal silicate or metal silicate hydrate (e.g., calcium silicate or calcium silicate hydrate) compositions, and methods of their manufacture and use. The cementitious metal silicate compositions are suitable for use as hydraulic, partially hydraulic or non-hydraulic cement that hardens by a hydration process, a carbonation process, or a combination thereof.
[0006] In one aspect, the invention generally relates to a method for producing cement. The method includes: (a) providing a ground mixture comprising source materials of metal oxide (e.g., calcium oxide) and silica; (b) providing a gas comprising a steam of water over the ground mixture of source materials at a pressure, where in the partial pressure of the steam of water ranges from atmospheric pressure to a pressure of supercritical water; and (c) subjecting the ground mixture of source materials (i) to a temperature and for a time sufficient to calcine the ground mixture and (ii) to a temperature and for a time sufficient to fuse the calcined ground mixture to form the cement and/or cement agglomerate.
[0007] In another aspect, the invention generally relates to a cement material produced according to a method of cement production disclosed herein.
[0008] In yet another aspect, the invention generally relates to a powdery cement material produced according to a method of cement production disclosed herein.
[0009] In yet another aspect, the invention generally relates to a method for curing the cement material of the invention. The curing method includes: mixing the powdery cement material and one or more aggregates or fillers with water and allowing the mixture to set for a time and at a temperature sufficient to form a concrete product. [0010] In yet another aspect, the invention generally relates to an article of manufacture produced by a curing method disclosure herein.
Brief Description of the Drawings
[0011] The objects and features of the invention can be better understood with reference to the drawings described below, and the claims. The drawings are not necessarily to scale, emphasis instead generally being placed upon illustrating the principles of the invention. In the drawings, like numerals are used to indicate like parts throughout the various views.
[0012] FIG. 1 is a pressure-temperature phase diagram showing the phases present in the reversible reaction CaC0 +Si02 <→ CaSi0 (calcium silicate) + C02.
[0013] FIG. 2 is a pressure-temperature phase diagram showing the phases present in the reversible reaction 3CaC0 + 2CaSi0 <→ 2Ca2Si04-CaC0 + C02.
[0014] FIG. 3 is a phase diagram of the CaO-Si02-C02 system at a pressure of 1 kilobar.
[0015] FIG. 4 is a pressure-temperature phase diagram showing the phases present in the reversible reaction MgO + C02 → MgC03.
[0016] FIG. 5 is a pressure-temperature phase diagram showing the equilibrium curves for the reversible reaction MgO + C02 → MgC0 as a function of the proportion of C02 in an inert gas.
[0017] FIG. 6 is a temperature-composition phase diagram that illustrates the stability regions for various phases in the CaC0 -MgC0 system.
[0018] FIG. 7 is a tetrahedron diagram illustrating the phase relationships among the compounds CaO, MgO, Si02 and C02, and showing the C02 deficient region below the Cc-Di- Wo and the Cc-Wo-Mo planes (shaded), where Cc denotes calcite, Wo denotes Wollastonite, Ak denotes Akermanite, Di denotes diopside, and Mo denotes monticellite (CaMgSi04).
[0019] FIG. 8 is a pressure-temperature phase diagram illustrating the phase relationships among the compounds CaO, MgO, Si02 and C02, with univariant curves emanating from the quaternary invariant point involving the phases calcite (Cc), diopside (Di), forsterite (Fo), monticellite (Mo), Akermanite (Ak), and C02. The inset is the phase diagram for the three compound systems of CaC0 , MgO and Si02. Detailed Description of the Invention
[0020] The invention is based on a novel, steam-assisted production methodology and relates to compositions of non-carbonatable or carbonatable metal silicate or metal silicate hydrate (e.g., calcium silicate or calcium silicate hydrate) compositions, and methods of manufacture and use thereof.
[0021] In one aspect, the invention generally relates to a method for producing cement. The method includes: (a) providing a ground mixture comprising source materials of metal oxide (e.g., calcium oxide) and silica; (b) providing a gas comprising a steam of water over the ground mixture of source materials at a pressure, wherein the steam of water has a partial pressure that ranges from atmospheric pressure to a pressure of supercritical water; and (c) subjecting the ground mixture of source materials (i) to a temperature and for a time sufficient to calcine the ground mixture and (ii) to a temperature and for a time sufficient to fuse the calcined ground mixture to form the cement and/or cement agglomerate.
[0022] Any suitable steam source may be used to provide a water steam over the ground mixture of source materials. The pressure of the production chamber may have a pressure from atmospheric pressure to that of supercritical water. Without wishing to be bound by the theory, it is believed that steam acts as a reaction enhancer allowing lowed reaction temperature. In certain preferred embodiments, the temperature sufficient to calcine the ground mixture is lower than about 1,200 °C, for example, from 400 °C to 800 °C (e.g., about 500 °C, 600 °C, 700 °C, 800 °C). In certain preferred embodiments, the temperature sufficient to fuse the calcined ground mixture is lower than about 1,200 °C, for example, from 400 °C to 800 °C (e.g., about 500 °C, 600 °C, 700 °C, 800 °C). It is noted that the temperature may be controlled as a function of time, for example, in the form of a loop to start from ambient temperature to a temperature of about 500 °C to 600 °C and to end at ambient temperature upon cooling. It is also noted that the pressure control may be in the form of a loop as well, in particular correlation with the temperature control.
[0023] In certain preferred embodiments, the steam of water is substantially in supercritical condition.
[0024] In certain preferred embodiments, the method further includes a step of cooling the cement to ambient temperature. In certain preferred embodiments, the method further includes a step of grinding the cement agglomerates to form powdery cement. In certain preferred embodiments, the method further includes, before grinding, a step of adding one or more set- controlling admixtures to the mixture.
[0025] The cementitious metal silicate compositions can be made from widely available, low cost raw materials by a process suitable for large-scale production. Any suitable sources of metal oxide and silica may be used. In certain preferred embodiments, the source materials of metal oxide and silica are selected from magnesium silicates, magnesium oxide and silica source, calcium oxide and silica source, magnesium carbonate and silica source, calcium carbonate and silica source, low-grade limestone and silica, magnesium calcium aluminates, magnesium calcium aluminum silicates, and magnesium calcium silicates. Thus, while the metal silicate used herein is primarily referring to calcium silicate, other metal silicates such as magnesium calcium aluminates, magnesium calcium aluminum silicates, and magnesium calcium silicates may constitute significant percentages of the materials.
[0026] The production method of the invention is flexible in equipment and production requirements and is readily adaptable to manufacturing facilities of conventional cement. The unique approach offers substantially reduced production temperature and energy consumption.
[0027] For example, cementitious metal silicate compositions can be produced in commercial cement rotary kilns using the raw materials used for Ordinary Portland Cement (OPC) clinker. An important feature of the cementitious metal silicate compositions is that they be suitable for hardening by a hydration process (i.e., in combination with water), a carbonation process (i.e., in combination with C02 and non-reactive water) or a combination thereof (i.e., in combination with C02 and reactive water).
[0028] In another aspect, the invention generally relates to a cement material produced according to a method of cement production disclosed herein.
[0029] In yet another aspect, the invention generally relates to a powdery cement material produced according to a method of cement production disclosed herein.
[0030] In yet another aspect, the invention generally relates to a method for curing the cement material of the invention. The curing method includes: mixing the powdery cement material and one or more aggregates or fillers with water and allowing the mixture to set for a time and at a temperature sufficient to form a concrete product.
[0031] In certain embodiments, the curing process is performed in a C02-rich atmosphere, for example, under a C02 concentration ranging from about 25% to about 99.5% (e.g., from about 50% to about 99.5%, from about 70% to about 99.5%, from about 80% to about 99.5%, from about 90% to about 99.5%).
[0032] The cementitious metal silicate compositions of the invention are suitable for use as hydraulic, partially hydraulic or non-hydraulic cement that hardens by a hydration process, a carbonation process, or a combination thereof. The cementitious metal silicate compositions of the invention may be applied in a variety of concrete components in the infrastructure, construction, pavement and landscaping industries.
[0033] In yet another aspect, the invention generally relates to an article of manufacture produced by a curing method disclosure herein.
[0034] Various parameters of production such as material sources, temperatures, pressures, reaction times, admixtures, etc., may be selected to achieve desired cement properties.
[0035] FIG. 1 is a pressure-temperature phase diagram showing the phases present in the reversible reaction CaC0 +Si02 <→ CaSi0 (calcium silicate) + C02.
[0036] FIG. 2 is a pressure-temperature phase diagram showing the phases present in the reversible reaction 3CaC0 + 2CaSi0 <→ 2Ca2Si04-CaC0 + C02.
[0037] FIG. 3 is a phase diagram of the CaO-Si02-C02 system at a pressure of 1 kilobar.
[0038] FIG. 4 is a pressure-temperature phase diagram showing the phases present in the reversible reaction MgO + C02 → MgC03.
[0039] FIG. 5 is a pressure-temperature phase diagram showing the equilibrium curves for the reversible reaction MgO + C02 → MgC0 as a function of the proportion of C02 in an inert gas.
[0040] FIG. 6 is a temperature-composition phase diagram that illustrates the stability regions for various phases in the CaC0 -MgC0 system.
[0041] FIG. 7 is a tetrahedron diagram illustrating the phase relationships among the compounds CaO, MgO, Si02 and C02, and showing the C02 deficient region below the Cc-Di- Wo and the Cc-Wo-Mo planes (shaded), where Cc denotes calcite, Wo denotes Wollastonite, Ak denotes Akermanite, Di denotes diopside, and Mo denotes monticellite (CaMgSi04).
[0042] FIG. 8 is a pressure-temperature phase diagram illustrating the phase relationships among the compounds CaO, MgO, Si02 and C02, with univariant curves emanating from the quaternary invariant point involving the phases calcite (Cc), diopside (Di), forsterite (Fo), monticellite (Mo), Akermanite (Ak), and C02. The inset is the phase diagram for the three compound systems of CaC03, MgO and Si02.
[0043] The cement material of the invention may be produced under conditions that result in primarily noncarbonatable hydraulic calcium silicate materials. The cement material of the invention may be also produced under conditions that result in partially carbonatable and partially hydraulic calcium silicate materials. The cement material of the invention may further be produced under conditions resulting in primarily carbonatable non-hydraulic calcium silicate materials.
[0044] Hydrating phases include Ca3Si05 (C3 S), Ca2Si04 (C2S), Ca3Al206 (C3A),
Ca4Al2Fe2Oio (C4AF), CaS04.2H20 (C52H), CaSO4.0.5H2O (C5O.5H), 4Ca0.3Al203.S03 (C4A35), CaO (C), amorphous calcium silicate, amorphous calcium aluminum silcate, and amorphous mellilite groups. When reacted with water these hydrating phases form hydration products such as Ca(OH)2 (portlandite), Ca6Al2(S04)3(OH)i2 26H20 (ettringite) and calcium silicate hydrate (CSH) gel, hydrated amorphous mellilites.
[0045] Carbonatable (reactive) phases include CS (wollastonite or pseudowollastonite), C3 S2 (rankinite) and (belite or larnite or bredigite). The C2S phase present within the calcium silicate composition may exist as (Ca7Mg(Si04)4) (bredigite) or as any of a-Ca2Si04, -Ca2Si04 or γ- Ca2Si04 polymorph or combination thereof. The carbonatable calcium silicate cement may additionally have a reactive amorphous phase of varying composition. The carbonatable calcium silicate compositions may also include small quantities of residual CaO (lime) and Si02 (silica) from raw materials after sintering. The calcium silicate composition may also include small quantities of C3 S (alite, Ca3Si05). The carbonatable calcium silicate compositions may additionally include quantities of inert phases (i.e., non-carbonatable under typical carbonation conditions) such as melilite type minerals (melilite or gehlenite or akermanite) with the general formula (Ca,Na,K)2[(Mg, Fe2+,Fe +,Al,Si)307] and ferrite type minerals (ferrite or brownmillerite or C4AF) with the general formula Ca2(Al,Fe +)205.
[0046] Discussions of various features of a controlled Hydrothermal Liquid Phase Sintering (HLPS)-based carbonation can be found in U.S. Patent No. 8, 1 14,367, U.S. Pub. No. US
2009/014321 1 (Appl. Serial No. 12/271,566), U.S. Pub. No. US 201 1/0104469 (Appl. Serial No. 12/984,299), U.S. Pub. No. 2009/0142578 (Appl. Serial No. 12/271,513), U. S. Pub. No.
2013/0122267 (Appl. Serial No. 13/41 1,218), U.S. Pub. No. 2012/0312194 (Appl. Serial No. 13/491,098), WO 2009/102360 (PCT/US2008/083606), WO 2011/053598
(PCT/US2010/054146), WO 2011/090967 (PCT/US2011/021623), U.S. Provisional Patent Application No. 61/708,423 filed October 1, 2012, and U.S. Pub. Nos. 2014/0127450 (Appl. Serial No. 14/045,758), 2015/0266778 (Appl. Serial No. 14/045,519), 2014/0127458 (Appl. Serial No. 14/045,766), 2014/0342124 (Appl. Serial No. 14/045,540), 2014/0272216 (Appl. Serial No. 14/207,413), 2014/0263683 (Appl. Serial No. 14/207,421), 2014/0314990 (Appl. Serial No. 14/207,920), 2014/0322083 (Appl. Serial No. 14/209,238), 2014/0363665 (Appl. Serial No. 14/295,601), 2014/0361471 (Appl. Serial No. 14/295,402), 2015/0225295 (Appl. Serial No. 14/602,313), 2015/0056437 (14/463,901), WO 2015/051243 (PCT/US2014/059024), WO 2015/103107 (PCT/US2014/072494), WO 2016/022485 (PCT/2015/043452), WO
2016/022522 (PCT/2015/043540), WO 2016/154021 (PCT/US2016/023181), WO 2016/054602 (PCT/US2015/053879), WO 2016/154024 (PCT/US2016/023193), each of which is expressly incorporated herein by reference in its entirety for all purposes.
[0047] Applicant's disclosure is described herein in preferred embodiments with reference to the Figures, in which like numbers represent the same or similar elements. Reference throughout this specification to "one embodiment," "an embodiment," or similar language means that a particular feature, structure, or characteristic described in connection with the embodiment is included in at least one embodiment of the present invention. Thus, appearances of the phrases "in one embodiment," "in an embodiment," and similar language throughout this specification may, but do not necessarily, all refer to the same embodiment.
[0048] The described features, structures, or characteristics of Applicant's disclosure may be combined in any suitable manner in one or more embodiments. In the following description, numerous specific details are recited to provide a thorough understanding of embodiments of the invention. One skilled in the relevant art will recognize, however, that Applicant's composition and/or method may be practiced without one or more of the specific details, or with other methods, components, materials, and so forth. In other instances, well-known structures, materials, or operations are not shown or described in detail to avoid obscuring aspects of the disclosure.
[0049] In this specification and the appended claims, the singular forms "a," "an," and "the" include plural reference, unless the context clearly dictates otherwise. [0050] Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art. Although any methods and materials similar or equivalent to those described herein can also be used in the practice or testing of the present disclosure, the preferred methods and materials are now described.
Methods recited herein may be carried out in any order that is logically possible, in addition to a particular order disclosed.
Incorporation by Reference
[0051] References and citations to other documents, such as patents, patent applications, patent publications, journals, books, papers, web contents, have been made in this disclosure. All such documents are hereby incorporated herein by reference in their entirety for all purposes. Any material, or portion thereof, that is said to be incorporated by reference herein, but which conflicts with existing definitions, statements, or other disclosure material explicitly set forth herein is only incorporated to the extent that no conflict arises between that incorporated material and the present disclosure material. In the event of a conflict, the conflict is to be resolved in favor of the present disclosure as the preferred disclosure.
Equivalents
[0052] The representative examples are intended to help illustrate the invention, and are not intended to, nor should they be construed to, limit the scope of the invention. Indeed, various modifications of the invention and many further embodiments thereof, in addition to those shown and described herein, will become apparent to those skilled in the art from the full contents of this document, including the examples and the references to the scientific and patent literature included herein. The examples contain important additional information, exemplification and guidance that can be adapted to the practice of this invention in its various embodiments and equivalents thereof.

Claims

1. A method for producing metal silicate, or metal silicate hydrate product capable of
carbonation or hydration to form a cementitious product, comprising:
(a) providing a ground mixture comprising source materials of metal oxide and silica;
(b) providing a gas comprising a steam of water over the ground mixture of source materials at a pressure, wherein the steam of water has a partial pressure that ranges from atmospheric pressure to supercritical water pressure; and
(c) subjecting the ground mixture of source materials (i) to a temperature and for a time sufficient to calcine the ground mixture, and (ii) to a temperature and for a time sufficient to fuse the calcined ground mixture to form the cementitious product.
2. The method of claim 1, wherein the temperature sufficient to heat the ground mixture is lower than about 1,200 °C.
3. The method of claim 1 or 2, wherein the temperature sufficient to heat the ground
mixture is lower than about 800 °C.
4. The method of any of claims 1-3, wherein the temperature sufficient to fuse the ground mixture is lower than about 1,200 °C.
5. The method of any of claims 1-4, wherein the temperature sufficient to fuse the ground mixture is lower than about 800 °C.
6. The method of any of claims 1-5, wherein the steam of water is substantially in
supercritical condition.
7. The method of any of claims 1-6, further comprising cooling the cement product to
ambient temperature.
8. The method of any of claims 1-7, further comprising grinding the cement agglomorate to form powdery cement.
9. The method of claim 8, further comprising, before grinding, adding one or more set- controlling admixtures to the cementitious product.
10. The method of any of claims 1-9, wherein the source materials of metal oxide and silica are selected from magnesium silicates, magnesium oxide and silica source, calcium oxide and silica source, magnesium carbonate and silica source, calcium carbonate and silica source, low grade limestone having calcium and silicone, magnesium calcium aluminates, magnesium calcium aluminum silicates, and magnesium calcium silicates.
11. A cement material produced according to any of claims 1-10.
12. A powdery cement material produced according to any of claims 1-10.
13. A method for curing the cement material of claim 11 or 12, comprising mixing the powdery cement material and one or more aggregates or fillers with water and allowing the mixture to set for a time and at a temperature sufficient to form a concrete product.
14. The method of claim 13, wherein the curing process is performed in a CCh-rich
atmosphere.
15. An article of manufacture produced by the method of claim 13 or 14.
PCT/US2016/058981 2015-10-28 2016-10-27 Steam-assisted production of metal silicate cements, compositions and methods thereof WO2017075126A1 (en)