WO2017052108A1 - 슬림형 건축마감용 질석보드 - Google Patents

슬림형 건축마감용 질석보드 Download PDF

Info

Publication number
WO2017052108A1
WO2017052108A1 PCT/KR2016/009928 KR2016009928W WO2017052108A1 WO 2017052108 A1 WO2017052108 A1 WO 2017052108A1 KR 2016009928 W KR2016009928 W KR 2016009928W WO 2017052108 A1 WO2017052108 A1 WO 2017052108A1
Authority
WO
WIPO (PCT)
Prior art keywords
vermiculite
weight
board
vermiculite board
slim
Prior art date
Application number
PCT/KR2016/009928
Other languages
English (en)
French (fr)
Inventor
강석영
Original Assignee
주식회사 버미코리아
강석영
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 버미코리아, 강석영 filed Critical 주식회사 버미코리아
Priority to US15/762,756 priority Critical patent/US10450229B2/en
Priority to CN201680055427.9A priority patent/CN108026725A/zh
Publication of WO2017052108A1 publication Critical patent/WO2017052108A1/ko

Abstract

본 발명은 슬림형 건축마감용 질석보드에 관한 것으로, 소성된 질석 100중량부에 첨가제 2.5~3.5중량부 및 바인더 100~120중량부를 포함하는 것을 기술적 특징으로 하며, 질석의 자연스러운 무늬 및 다양한 색의 제품으로 미려하고 고급스러운 실내 조성이 가능하고, 건축폐기물이 발생하지 않고 농업용 토지개량제로 사용이 가능하고, 중량이 가볍고 시공이 간편하며 백화현상이 발생하지 않는 장점이 있고, 변형이 없고 친환경적이며 탈취성, 항균성, 내화성 및 흡음률이 우수한 장점이 있다.

Description

슬림형 건축마감용 질석보드
본 발명은 슬림형 건축마감용 질석보드에 관한 것으로, 보다 상세하게는 바인더로 액상규산칼륨을 사용함으로써 흐름성이 좋아 배합이 원활하고, 백화현상이 발생하지 않으며, 성형시 정량투입이 용이하게 함으로써 성형시간을 최소한으로 단축하여 대량생산이 가능하고 강도를 높이고 변형률을 최소화한 슬림형 건축마감용 질석보드에 관한 것이다.
질석(Vermiculite)은 인체에 유익한 원적외선을 방사하며, 탈취성과 항균성이 우수하고 내화성이 뛰어난 특징이 있어 건축용 자재, 전동차 및 기차의 천정, 벽체의 자재, 전자 제품의 자재 등으로 널리 사용되며, 분말의 형태로 방화용 불연성 페인트, 코팅재 및 충진재 등에 첨가하기도 한다.
특히, 질석은 고온으로 소성하면 팽창하는 특성이 있으며, 팽창한 질석은 밀도가 낮으면서도 탈취성, 항균성, 내화성이 우수하므로, 이를 보드(판) 형상으로 제조하여 다양한 건축물 내·외장재로 사용하고 있다.
질석은 여러 가지 장점을 가지고 있으나 입자의 크기가 일정하지 않고 기공이 많으며 기공의 크기도 일정하지 않아 변형률이 매우 높은 광물질로 모래알처럼 접착력(응집력)이 전혀 없어 바인더를 사용하여 질석보드를 제조한다.
대한민국등록특허공보 제10-0695910호(2007.03.20.)에는 팽창질석 100중량부, 에폭시수지 70-90중량%와 페놀수지 10-30중량%로 이루어진 유기바인더 50-90중량부, 점토 1-10중량부를 함유하는 질석보드가 개시되어 있다.
상기 질석보드는 강도가 높은 장점이 있지만, 상기 유기바인더는 연소되는 경우에 심한 매연(유독가스)를 발생시키는 단점이 있다.
대한민국등록특허공보 제10-0760149호(2007.09.18.)에는 질석을 발포성형한 발포석과 규산나트륨과 혼합교반한 후에 압축성형하고 건조한 건축용 내장재가 개시되어 있다.
상기 건축용 내장재는 난연성이 우수한 장점이 있지만, 규산나트륨 바인더는 흐름성이 좋지 않아 균일한 배합이 어려워 한쪽에 뭉쳐지고 덩어리가 지는 단점이 있고, 혼합물의 상태가 매우 끈적거려 금형에 정량투입이 어려워 생산하는 시간이 오래 소요되는 단점이 있다.
[선행기술문헌]
[특허문헌]
(특허문헌 1) KR 10-0695910 B1 2007.03.20.
(특허문헌 2) KR 10-0760149 B1 2007.09.18.
본 발명의 목적은 바인더로 액상규산칼륨을 사용함으로써 흐름성이 좋아 배합이 원활하고, 백화현상이 발생하지 않으며, 성형시 정량투입이 용이하게 함으로써 성형시간을 최소한으로 단축하여 대량생산이 가능하고 강도를 높이고 변형률을 최소화한 슬림형 건축마감용 질석보드를 제공하는 것이다.
상기 목적을 달성하기 위하여 본 발명은 다음과 같은 수단을 제공한다.
본 발명은 소성된 질석 100중량부에 첨가제 2.5~3.5중량부 및 바인더 100~120중량부를 포함하되, 상기 첨가제는 이산화티타늄인 슬림형 건축마감용 질석보드를 제공한다.
상기 소성된 질석은 질석을 1,000~1,100℃에서 소성시킨다.
상기 바인더는 액상규산칼륨이다.
상기 액상규산칼륨은 비중(20℃)이 1.381~1.394이고, SiO2 대 K2O의 몰비가 3.15~3.35이며, 20℃에서의 점도가 0.7~0.9cps이다.
상기 액상규산칼륨은 K2O가 11.5중량%이고, SiO2가 24중량% 이다.
상기 액상규산칼륨은 온도 25~30℃, 습도 54~56%로 유지시킨다.
본 발명에 따른 슬림형 건축마감용 질석보드는 질석의 자연스러운 무늬 및 다양한 색의 제품으로 미려하고 고급스러운 실내 조성이 가능하고, 건축폐기물이 발생하지 않고 농업용 토지개량제로 사용이 가능하고, 중량이 가볍고 시공이 간편하며 백화현상이 발생하지 않는 장점이 있다.
또한 본 발명의 슬림형 건축마감용 질석보드는 변형이 없고 친환경적이며 탈취성, 항균성, 내화성 및 흡음률이 우수한 장점이 있다.
도 1은 질석보드 제조장치에서 질석, 이산화티타늄 및 바인더를 연속식으로 혼합하기 위한 원료 혼합 및 저장 장치를 도시한 개념도이다.
도 2는 도 1에 도시된 원료 혼합 장치에서 혼합된 최종 혼합물을 이용하여 질석보드를 성형하는 성형 장치를 도시한 개념도이다.
도 3은 질석보드의 제조방법을 도시한 일련의 공정 흐름도이다.
도 4는 실시예 1에서 제조된 질석보드의 표면을 다양하게 성형한 슬림형 건축마감용 질석보드의 사진이다.
도 5는 비교예 1에서 제조된 질석보드의 사진이다.
도 6은 실시예 1에서 제조된 질석보드의 함수율, 휨파괴하중, 열저항 시험성적서이다.
도 7 및 도 8은 실시예 1에서 제조된 질석보드의 흡음계수 시험성적서이다.
도 9 및 도 10은 실시예 1에서 제조된 질석보드의 불연성시험 및 가스유해성시험 시험성적서이다.
도 11 및 도 12는 실시예 1에서 제조된 질석보드의 중금속 및 유해물질 함유 시험성적서이다.
도 13은 실시예 1에서 제조된 질석보드의 총휘발성유기화합물, 톨루엔, 폼알데하이드 함유 시험성적서이다.
도 14는 실시예 1에서 제조된 질석보드의 원적외선 방사율 및 원적외선 방사에너지 시험성적서이다.
도 15는 실시예 1에서 제조된 질석보드의 방사능지수 시험성적서이다.
이하, 본 발명을 상세히 설명하면 다음과 같다.
종래 질석을 주재료로 사용한 질석보드는 산업용 단열재, 심재로 주로 사용되었다.
종래 질석보드는 물이나 공기 중에 습기를 만나면 질석보드가 백화현상이 발생하고, 질석보드의 변형으로 인한 붕괴현상이 발생해 건축용 마감재로는 사용되지 못했다.
종래 건축용 마감재는 펄라이트를 주원료로 사용하고 질석은 30% 이내 포함되었다.
본 발명은 펄라이트를 사용하지 않고 질석만을 건축용 마감재로 사용함에도 불구하고 조해성(deliquescence)을 해결하여 백화현상이 발생하지 않고 질석보드의 변형이 발생하지 않는 장점이 있다.
먼저, 본 발명에 따른 슬림형 건축마감용 질석보드를 설명한다.
본 발명의 슬림형 건축마감용 질석보드는,
소성된 질석 100중량부에 첨가제 2.5~3.5중량부 및 바인더 100~120중량부를 포함하는 것이 바람직하다.
상기 소성된 질석은 질석을 1,000~1,100℃에서 소성시키는 것이 바람직하며, 1,000℃ 미만의 온도에서 소성시키면 부분적으로 소성이 덜 된 질석이 섞여 중량이 무겁고 흡음성능이 떨어지고 색이 일정하지 않는 문제가 있고, 1,100℃ 초과의 온도에서 소성시키면 입자가 푸석거리고 바스러지며, 배합시 가루가 날리고 덩어리로 뭉쳐지는 문제가 있다.
상기 소성된 질석 100중량부에 첨가제 2.5~3.5중량부 포함하는 것이 바람직하며, 2.5중량부 미만 포함하면 응집력이 약해져 강도가 떨어지는 문제가 있고, 3.5중량부 초과 포함하면 강도는 약간 좋아지나 배합시 덩어리가 뭉쳐지고 가루가 기공을 막아 흡음성능이 떨어지는 문제가 있다.
상기 첨가제는 이산화티타늄(Titanium Dioxide)을 사용하는 것이 바람직하나, 이에 한정되지는 아니한다.
상기 이산화티타늄은 휘도가 높아 다른 혼합물과 잘 섞이고 강도를 높이는 장점이 있다.
본 발명에서는 소성된 질석의 기공 사이사이에 이산화티타늄을 투입함으로써, 응집력(접착성)을 높이고 균일한 기공 상태를 유지하도록 하는 것에 특징이 있다.
본 발명에서는 상기 바인더로 액상규산칼륨(Potassium silicate solutions)을 사용하는 것에 특징이 있다.
액상규산나트륨을 바인더로 사용하는 경우에는 흐름성이 좋지 않아 균일한 배합이 어려워 한쪽에 뭉쳐지고 덩어리가 지는 단점이 있고, 혼합물의 상태가 매우 끈적거려 금형에 정량투입이 어려워 생산하는 시간이 오래 소요되는 단점이 있다.
본 발명은 액상규산칼륨을 바인더로 사용함으로써 겉은 뽀송뽀송하고 안은 점도가 있는 상태의 혼합물이 되게 하며, 흐름성이 좋아 배합이 원활하고, 백화현상이 발생하지 않으며, 성형시 정량투입이 용이하게 함으로써 성형시간을 최소한으로 단축하여 대량생산이 가능하고 강도를 높이고 변형률을 최소화한 장점이 있다.
본 발명에서는 액상규산칼륨의 비중과 SiO2 대 K2O의 몰비와 점도를 조절하여 최적의 질석보드의 바인더를 개발한 것에 특징이 있다.
본 발명의 액상규산칼륨은 pH가 11~12이고, 비중(20℃)이 1.381~1.394이고, SiO2 대 K2O의 몰비가 3.15~3.35이고, 20℃에서의 점도가 0.7~0.9cps인 것이 바람직하다.
본 발명에 따른 액상규산칼륨은 비중(20℃)이 1.381~1.394인 것이 바람직하고, 비중(20℃)이 1.381 미만이면 접착력이 떨어져 강도가 약해지는 문제가 있고, 비중(20℃)이 1.394 초과이면 바인더가 끈적거려 배합 및 성형이 어려운 문제가 있다.
액상규산칼륨의 몰비 계산은 다음과 같다.
규산칼륨의 몰비 = (SiO2/K2O)의 중량비 × 1.568
본 발명에 따른 액상규산칼륨은 SiO2 대 K2O의 몰비가 3.15~3.35인 것이 바람직하고, SiO2 대 K2O의 몰비가 3.15 미만이면 내열성은 약간 높아지나 접착력이 떨어지는 문제가 있고, SiO2 대 K2O의 몰비가 3.35 초과이면 점도가 높아져 접착력이 좋아지나 바인더가 끈적거려 배합 및 성형이 어려운 문제가 있다.
본 발명에 따른 액상규산칼륨은 K2O가 11.5중량%이고, SiO2가 24중량% 인 것이 더 바람직하다.
본 발명에 따른 액상규산칼륨은 20℃에서의 점도가 0.7~0.9cps인 것이 바람직하고, 20℃에서의 점도가 0.7cps 미만이면 흐름성이 좋아 배합하기는 좋으나 접착력이 떨어져 강도가 낮아지는 문제가 있고, 20℃에서의 점도가 0.9cps 초과이면 접착력은 좋아지나 바인더가 끈적거려 배합 및 성형이 어려운 문제가 있다.
상기 액상규산칼륨은 질석의 특성에 가장 적합한 상태인 온도 25~30℃, 습도 54~56% 를 유지하는 것이 바람직하다.
상기 소성된 질석 100중량부에 바인더 100~120중량부 포함하는 것이 바람직하며, 100중량부 미만 포함하면 접착력이 현저히 떨어지고 내열성이 저하되는 문제가 있고, 120중량부 초과 포함하면 중량이 무겁고 배합이 질어져 성형이 어려운 문제가 있다.
본 발명자는 질석보드 제조장치 및 제조방법을 출원하여 등록된 바 있다. (대한민국등록특허공보 제10-1132034호, 2012.04.02.)
도 1은 질석보드 제조장치에서 질석, 이산화티타늄 및 바인더를 연속식으로 혼합하기 위한 원료 혼합 및 저장 장치를 도시한 개념도이고,
도 2는 도 1에 도시된 원료 혼합 장치에서 혼합된 최종 혼합물을 이용하여 질석보드를 성형하는 성형 장치를 도시한 개념도이고,
도 3은 질석보드의 제조방법을 도시한 일련의 공정 흐름도이다.
본 발명자가 기출원한 질석보드 제조장치 및 제조방법(10-1132034호)은 연속적인 혼합 공정에서 질석과 바인더가 균일한 혼합이 이루어지도록 함과 동시에, 혼합물에서 바인더가 뭉치지 않도록 하여 프레스로 투입시에 정량 공급이 가능하고 또한 상온에서 한 번의 프레스 공정으로 질석보드를 제조함으로써 균일한 품질을 얻을 수 있으며 대량생산에 능동적으로 대응할 수 있는 질석보드 제조장치 및 제조방법에 관한 것이다.
본 발명에서는 상기 기출원된 질석보드 제조장치 및 제조방법을 이용하여 질석보드를 제조하며, 상기 특허(10-1132034호)에 질석보드 제조장치 및 제조방법이 기재되어 있으므로 상세한 설명은 생략한다.
이하, 실시 예를 통하여 본 발명의 구성 및 효과를 더욱 상세히 설명하고자 한다. 이들 실시 예는 오로지 본 발명을 예시하기 위한 것일 뿐 본 발명의 범위가 이들 실시 예에 의해 제한되는 것은 아니다.
[실시예 1]
질석을 1,000℃에서 소성시켜 소성된 질석을 제조하였다. 상기 소성된 질석 100중량부에 이산화티타늄 3중량부가 제1 믹싱기로 공급되어 질석 및 이산화티타늄 혼합물로 혼합 배출되면, 제1 이송스크류는 이들 혼합물을 제2 믹서기로 공급한다(S10). 다음, 제2 믹서기로 공급된 질석 및 이산화티타늄 혼합물에 온도 27℃, 습도 55%인 액상규산칼륨을 공급하되, 액상규산칼륨이 투입되는 방향의 직각방향으로 액상규산칼륨에 고압의 공기를 분사하여 액상규산칼륨이 뭉쳐지지 않고 작은 입자로 분산시켜서 공급한다(S20). 상기 소성된 질석 100중량부에 상기 액상규산칼륨 100중량부를 사용하였다. 상기 액상규산칼륨은 비중(20℃)이 1.390이고, SiO2 대 K2O의 몰비가 3.25이며, 20℃에서의 점도가 0.8cps가 되도록 제조하여 사용하였다. 이때, 제2 믹서기는 이송스크류 타입으로 이루어져 이송스크류를 통해 연속적으로 이동하는 질석 및 이산화티타늄 혼합물의 흐름율(flowrate)에 일정량의 액상규산칼륨 역시 연속적으로 공급된다. 다음, 제2 믹서기로 배출되는 질석, 이산화티타늄 및 액상규산칼륨의 최종 혼합물은 송풍팬 어셈블리와 유입되어져 송풍팬의 송풍력에 의해 주름관을 통해 저장조로 압송된다. 이때, 최종 혼합물은 송풍팬과 1차 충돌이 이루어지고 다음에 주름관의 주름부와 2차 충돌하면서 몽우리 형태로 뭉쳐진 바인더가 최종적으로 작은 입자로 흩어져서 균일한 혼합이 이루어지게 된다(S30). 다음, 저장조에 저장된 최종 혼합물을 프레스로 가압하여 압축된 질석보드를 성형한다(S40). 이를 보다 상세하게 설명하면, 먼저 저장조의 배출관에 길게 연장된 호스 등을 통해 프레스의 성형틀 내부로 채워넣는다(S41). 다음, 프레스의 성형틀 내부에 최종 혼합물이 채워진 상태에서 상부 가동금형을 하강시켜서 최종 혼합물을 가압하면 최종 혼합물이 압축 성형되어 판 형태의 성형된 질석보드가 제조된다(S42). 이후에, 성형틀의 바닥을 이루는 하부 고정금형의 승강판이 승강 실린더의 동작에 의해 승강하면서(S43) 질석보드가 성형틀 상부로 상승하게 되면(S44) 취출 장치의 취출 실린더 로드의 전진 동작에 의해(S45) 취출판이 질석보드를 프레스 외부로 배출한다(S46). 다음, 프레스 외부로 배출된 질석보드는 프레스의 일측에 대기하고 있는 리프터에 적재된다. 이때, 리프터는 그 높이가 조절이 가능하여 프레스에서 질석보드가 배출되는 높이와 리프터에 적재된 직석보드의 적층 높이에 따라 그 높이를 조절하면서 다수의 질석보드를 적재할 수 있게 된다(S50). 다음, 리프터에 다수 개의 질석보드가 적재된 경우에 이를 제1 건조기로 이동시켜서 각각의 질석보드를 제1 건조기의 건조대에 올려놓아 일정 시간 동안 자연건조를 시킨다(S60). 마지막으로, 1차 건조기에서 자연 건조된 질석보드를 2차 건조기로 옮겨서 일정 시간 동안에 열풍 건조를 시킴으로써 최종 제품을 이루는 질석보드가 제조된다(S70).
상기와 같이 제조된 질석보드의 표면을 다양하게 성형한 슬림형 건축마감용 질석보드의 사진을 도 4에 나타내었다.
[비교예 1]
펄라이트 70중량%와 질석 30중량%를 혼합한 혼합물 100중량부에 바인더 50중량부를 혼합하여 제조한 질석보드의 사진을 도 5에 나타내었다. 상기 바인더는 액상규산나트륨을 사용하였다.
[실험예 1]
실시예 1에서 제조한 질석보드와 비교예 1에서 제조한 질석보드의 물성을 표 1에 나타내었다.
구분 비교예 1 실시예 1 실시예 1 특징
소성온도 1,150℃ 1,000℃
성질 강질 연질
압축시 부서짐 부서지지 않음(눌림 흔적)
후가공 필요(코팅, 연마 등) 불필요
문양/디자인 평면 다양 질석의 자연스러운 무늬 및 다양한 색의 제품으로 미려하고 고급스러운 실내 조성 가능
접착제 백화현상 백화현상 없음
내충격성 약함 강함
운반/이동 부서짐 운반 용이
로스율 40% 이상 1% 내외
재활용성 불가 가능 건축폐기물이 발생하지 않고 농업용 토지개량제로 사용 가능
가공성 미흡(수작업 불가) 우수(수작업 절단 가능)
시공성 시공장비 사용 시공성 용이 중량이 가볍고 톱, 칼, 나사, 못 등의 일반적인 공구로 쉽게 시공할 수 있어 작업성 우수
색상 일부 가능 유색 가능
장마철(수분노출) 단시간 이내 부풂 3개월 이상
밀도 밀도 약함 고밀도 조정 가능
금형작업 가공성 달라 붙음 붙지 않음(에어로 잔존물 제거)
피부접촉성 피부에 접촉되면 따가움 피부에 접촉되어도따가움 없음 인체 및 환경에 유해하지 않은 100% 자연광물
내열성 약함 강함
성형상태 백화현상 빈번 양호
실시예 1의 질석보드는 비교예 1의 질석보드에 비해 질석의 자연스러운 무늬 및 다양한 색의 제품으로 미려하고 고급스러운 실내 조성이 가능하고, 건축폐기물이 발생하지 않고 농업용 토지개량제로 사용이 가능하고, 중량이 가볍고 시공이 간편하며 백화현상이 발생하지 않는 장점이 있다.
[실험예 2]
실시예 1에서 제조한 질석보드의 제품 성능을 평가하여 표 2에 나타내었고, 함수율, 휨파괴하중, 열저항 시험성적서는 도 6에, 흡음계수 시험성적서는 도 7 및 도 8에, 불연성시험 및 가스유해성시험 시험성적서는 도 9 및 도 10에, 중금속 및 유해물질 함유 시험성적서는 11 및 도 12에, 총휘발성유기화합물, 톨루엔, 폼알데하이드 함유 시험성적서는 도 13에, 원적외선 방사율 및 원적외선 방사에너지 시험성적서는 도 14에, 방사능지수 시험성적서는 도 15에 나타내었다.
평가항목 평가방법 판정기준 성능 성적서번호
함수율 (%) KS L 9105:20009 3.0이하 0.5 CTS13-72286
휨파괴하중(N) 40이상 68
열저항(㎡·K)/W 0.28이상 0.12
NRC (Noise Reduction Coefficent) KS F 2805:2004ASTM C 423:2009a 0.41~0.60 0.50 CT13-72294
불연성시험 질량감소율(%) KD FISO 1182:2004 9:00 이상 13:34 CT13-72278
불연성시험 최고온도와 최종평형온도의 차(℃) 20을 초과하지 않을 것 1.4
가스유해성시험 행동정지시간(min:s) KS F 2271:2006 30 이하 6.9
납(㎎/ℓ) 폐기물공정시험기준(환경부 고시 제2011-160호) 3 미만 불검출 CT13-72248
6가크롬(㎎/ℓ) 1.5 미만 불검출
구리(㎎/ℓ) 3 미만 0.056
카드륨(㎎/ℓ) 0.3 미만 불검출
비소(㎎/ℓ) 1.5 미만 불검출
수은(㎎/ℓ) 0.005 미만 불검출
시안(㎎/ℓ) 1 미만 불검출
유기인(이피엔)(㎎/ℓ) 1 미만 불검출
유기인(파라티온)(㎎/ℓ) 1 미만 불검출
유기인(메틸디메톤)(㎎/ℓ) 1 미만 불검출
유기인(다이아지논)(㎎/ℓ) 1 미만 불검출
유기인(펜토에이트)(㎎/ℓ) 1 미만 불검출
트리클로로에틸렌(㎎/ℓ) 0.3 미만 불검출
테트라클로로에틸렌(㎎/ℓ) 0.1 미만 불검출
기름성분(%) 5 미만 불검출
석면함유량 KS L 5300 1 미만 검출안됨
총휘발성유기화합물(TVOC)(㎎/(㎡·h)) 실내공기질공정시험기준(환경부고시제2010-24호) 0.4 이하 0.045 CT13-72260
톨루엔(Toluene)(㎎/(㎡·h)) 0.080 이하 0.002
폼알데하이드(Formaldehyde)(㎎/(㎡·h)) 0.120 이하 0.002
원적외선 방사율 KCL-FIF-1005:2011 - 0.909 CT13-66163
원적외선 방사에너지(W/㎡) - 3.67×102
방사능지수 HASL-300 Ga-01-R:1997 1.0 이하 0.53187 CT-RM-13-0283
표 2에 의하면, 본 발명에 따른 질석보드는 변형이 없고 친환경적이며 탈취성, 항균성, 내화성 및 흡음률이 우수한 것을 확인할 수 있다.

Claims (3)

  1. 소성된 질석 100중량부에 첨가제 2.5~3.5중량부 및 바인더 100~120중량부를 포함하되,
    상기 소성된 질석은 질석을 1,000~1,100℃에서 소성시킨 것이며,
    상기 첨가제는 이산화티타늄이며,
    상기 바인더는 비중(20℃)이 1.381~1.394이고, SiO2 대 K2O의 몰비가 3.15~3.35이며, 20℃에서의 점도가 0.7~0.9cps인 액상규산칼륨인,
    슬림형 건축마감용 질석보드.
  2. 제 1항에 있어서,
    상기 액상규산칼륨은 K2O가 11.5중량%이고, SiO2가 24중량%인 슬림형 건축마감용 질석보드.
  3. 제 2항에 있어서,
    상기 액상규산칼륨은 온도 25~30℃, 습도 54~56%로 유지시키는 슬림형 건축마감용 질석보드.
PCT/KR2016/009928 2015-09-23 2016-09-05 슬림형 건축마감용 질석보드 WO2017052108A1 (ko)