WO2017012632A1 - A wind turbine blade having an erosion shield - Google Patents
A wind turbine blade having an erosion shield Download PDFInfo
- Publication number
- WO2017012632A1 WO2017012632A1 PCT/EP2015/066397 EP2015066397W WO2017012632A1 WO 2017012632 A1 WO2017012632 A1 WO 2017012632A1 EP 2015066397 W EP2015066397 W EP 2015066397W WO 2017012632 A1 WO2017012632 A1 WO 2017012632A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- wind turbine
- thermoplastic material
- turbine blade
- blade
- erosion shield
- Prior art date
Abstract
Description
Claims