WO2017009301A1 - Antifouling composition - Google Patents

Abstract

A binder for a marine coating composition comprising the reaction product of a polysiloxane unit A' and at least one second monomer B' that undergoes a polymerisation reaction with said polysiloxane unit A' so as to form a copolymer of structure -[ABAB]-wherein the backbone of said copolymer comprises a plurality of hydrolysable functional groups such as acetals that will hydrolyse in the presence of seawater.

Description

ANTIFOULING COMPOSITION

Field of the Invention

The present invention relates to marine antifouling coating compositions, more specifically to marine antifouling coating compositions comprising a particular binder and to the binder itself. The invention further relates to kits suitable for the preparation of the antifouling coating compositions and to surfaces coated with the antifouling coating compositions.

Background

Surfaces that are submerged in seawater are subjected to fouling by marine organisms such as green and brown algae, barnacles, mussels, tube worms and the like. On marine constructions such as vessels, oil platforms, buoys, etc. such fouling is undesired and has economical consequences. The fouling may lead to biological degradation of the surface, increased load and accelerated corrosion. On vessels the fouling will increase the frictional resistance which will cause reduced speed and/or increased fuel consumption. It can also result in reduced manoeuvrability.

Also underwater structures, e.g. industrial, plant, pipes and tanks for fresh water storage that are exposed to an aqueous environment, likes rivers, lakes, canals and swimming pools, have the similar problem caused by the attachment and growth of living organisms. This causes severe economic losses because of decreased possible operation time.

To prevent settlement and growth of marine organisms antifouling paints are used. These paints generally comprise a film- forming binder, together with different components such as pigments, fillers, solvents and biologically active substances.

The most successful antifouling coating system on the market until 2003 was a tributyltin (TBT) self-polishing copolymer system. The binder system for these antifouling coatings was a linear acrylic copolymer with tributyltin pendant groups. In seawater the polymer was gradually hydrolysed releasing tributyltin, which is an effective biocide. The remaining acrylic copolymer, now containing carboxylic acid groups, became sufficiently soluble or dispersible in seawater to be washed out or eroded away from the coating surface. This self-polishing effect provided a controlled release of the biologically active compounds in the coating resulting in excellent antifouling efficiency and smooth surfaces and hence reduced frictional resistance.

The IMO Convention "International Convention on the Control of Harmful Anti- fouling Systems on Ships" of 2001 prohibited the application of new TBT containing antifouling coatings from 2003 and TBT containing antifouling coatings are prohibited on ship hulls from 2008.

In recent years new antifouling coating systems have been developed and introduced as a consequence of the TBT ban. One broad group of biocidal antifouling coatings on the market today is the self-polishing antifouling coatings which mimic the TBT self-polishing copolymer coatings. Those antifouling coatings are based on (meth)acrylic copolymers having pendant hydrolysable groups without biocidal properties. The hydrolysis mechanism is the same as in the TBT containing

copolymers. This gives the same controlled dissolution of the polymers and thereby the controlled release of antifouling compounds from the coating film, resulting in similar performance as the TBT containing antifouling coating systems. The most successful self-polishing antifouling systems today are based on silyl ester functional

(meth)acrylic copolymers. These coating compositions are for example described in, EP 0 646 630, EP 0 802 243, EP 1 342 756, EP 1 479 737, EP 1 641 862, WO 00/77102, WO 03/070832 and WO 03/080747. The hydrolysable binder provides a continuous renewal of the coating film and efficient release of biocides at the coating surface, and thereby keeping the surface free of organisms.

The above mentioned antifouling coating systems degrade by hydrolysis of pendant groups on the polymer backbone, which results in a water erodable polymer. The hydrolysis of the pendant groups on the polymer backbone results in the formation of carboxylic acid salts which make the polymer hydrophilic and thereby erodable. A certain amount of hydrolysable groups are needed to get sufficient hydrophilicity and an erodable polymer after hydrolysis.

Another way of obtaining water erodable polymers is by introducing hydrolysable groups in the polymer backbone, resulting in degradation of the polymer structure, which gives erosion of the polymer film or coating film. Polyanhydrides are a class of polymers that degrade by backbone hydrolysis. The polyanhydrides are well documented for their surface degradation properties. Surface degradation is one of the most important factors for obtaining a successful antifouling coating. The use of specific aromatic polyanhydrides as binders in antifouling coating compositions is, for example, described in WO 2004/096927.

However, the anhydride group is extremely labile in the presence of moisture and it is therefore difficult to design a coating system based on polyanhydrides that exhibits a slow, controlled hydrolysis for use in antifouling coatings. Accordingly, the polyanhydrides used for antifouling coating compositions generally have a high content of aromatic units in order to control the hydrolysis.

In recent years, polyoxalates have emerged as a class of polymers that are well suited for use as binders in antifouling coatings. Backbone hydrolysis in these compounds is more controlled than for the polyanhydrides.

The use of self-polishing binders in which the polymer backbone hydro lyses in sea water makes it possible to obtain erodable cross-linked polymers and high molecular weight polymers.

An alternative to the anti- fouling coatings (which necessarily contain a biocide), are the so called fouling release coatings. These coatings have low surface tension and low modulus of elasticity and work by providing a "non-stick" surface to which sea organisms cannot stick or if they can stick are washed off by the motion of the water against the surface. Coatings are often based on polysiloxane/silicone/

polydimethylsiloxane (PDMS) that generally have very low toxicity. There are disadvantages of the fouling release system. For example, when applied to boat hulls the accumulation of marine organisms is reduced but relatively high vessel speeds are needed to remove all fouling species. Thus, in some instances, it has been shown that for effective release from a hull that has been treated with such a polymer, it is necessary to sail with a speed of at least 14 knots.

Such "non-stick" coatings have however, not shown good resistance to soft fouling such as slime and algae over time. Adding biocides in combination with a hydrophilic modified PDMS oil to such PDMS coatings has been suggested to overcome this problem in WO2011/076856. WO2013/00479 relies on the same principles of addition of biocides, but here hydrophilic modified polysiloxane moieties are covalently bonded to the polysiloxane binder.

These mixed materials have found limited commercial success however, as diffusion of biocides to the surface is too fast at the start of the coating lifetime, and then diffusion stops as the coating ages. More recently, Azemar, in Progress in Organic coatings 87, 2015, 10-19 discusses hybrid coatings based on a triblock copolymer of polycapro lactone and PDMS. A PDMS block is co-polymerized with caprolactone to obtain polycaprolactone polymer blocks on each end of a PDMS block. The polymers therefore contain only one PDMS block with two polyester blocks formed from the caprolactone meaning that any hydrolysis occurs only at the end of the molecule and not in the centre of any chain. Poly(caprolactone units) cannot be used in the manufacture of a copolymer as we claim as it does not contain two identical functional groups.

There remain problems to be solved, in particular, with regard to fouling release coating performance over time.

The present inventors have appreciated that it would be beneficial to have a fouling release coating surface that is renewable. The use of a renewable surface means that slime/algae and other soft fouling are physically removed with or without the need for biocides. It would therefore be useful if the fouling release coating composition could offer a renewable surface like that of an anti- fouling coating composition. This can be achieved with or without the addition of biocides. Biocides might be employed for example where a substrate, such as a ship's hull might be exposed to low speed or heavy fouling conditions.

The object of the present invention is to provide a new binder for a coating composition that can prevent marine organisms, both animals such as barnacles and algae/slime, adhering to the surface of underwater structures such as ship hulls. The idea of the invention is to combine the benefits of the fouling release type coating and the self-polishing anti- fouling coating, to provide, inter alia, a renewable non-stick surface on a substrate. The binder may or may not be provided with a biocide to potentially prolong the anti- fouling effect of the coating.

The invention therefore combines the benefits of the two technologies to provide a renewable coating with low surface tension optionally with biocides. The invention achieves this aim using a copolymer made by polymerising polysiloxane units with shorter comonomer molecules which are not polysiloxanes to provide a polymer containing hydrolysable units in its backbone. Alternatively, the invention envisages the combination of two (different) polysiloxane reactants that combine together to generate a hydrolysable linkage there between. The hydrolysable units may be organic compounds containing functional groups such as alkoxy (e.g. acetals, hemiacetals, ketals)).

The inventors have surprisingly found that the polymers designed herein are able to hydrolyse in sea water to renew the surface and, if desired, allow leaching of any biocide within the coating. Also, the binders of the invention provide a coating composition that has low VOC, low surface energy and low modulus of elasticity.

Summary of the Invention Thus, viewed from one aspect the invention provides a binder for a marine coating composition comprising the reaction product of at least one polysiloxane of general formula (Α'):

wherein each Ri is the same or different and represents an unsubstituted or substituted Ci_₂o alkyl, C₂_₂o alkenyl, C₃_₂o cycloalkyl, C₆-₂o aryl, C₇-₂o arylalkyl group, or a polyoxyalkylene chain; X and Y can be the same or different and represent H, OH, (CR"2)_X'-OH, (CR"₂) _X NH₂, (CR"₂) _X NR₂, epoxy, halide, -( CR"₂) _x COR, _( CR"₂) _x OCH=CH₂, - (CR"₂)_X -C=CH₂, -C=CH₂ or -(CR"₂)_x -(OR¹¹)_a-(OR¹¹)_b-OH;

R" may independently be Ci_₆ alkyl or H, especially H;

x' is 1 to 10, such as 1 to 5, especially 2 to 5, especially 3 to 5;

R is H, Ci_₂₀ alkyl, C₂_₂₀ alkenyl, C₃_₂₀ cycloalkyl, C₆_₂o aryl, C₇_₂₀ arylalkyl group;

R¹¹ are each independently C₂_₆ alkylene;

a= 0-50, b= 0-50 and a+b = 1-50; and

n is 1-500, more preferably 10-300, especially 15-100;

or n' + m add to 1-500, more preferably 10-300, especially 15-100;

and at least one second monomer B' of formula

wherein each Ri is the same or different and represents an unsubstituted or substituted Ci_₂o alkyl, C₂_₂o alkenyl, C₃_₂o cycloalkyl, C₆-₂o aryl, C₇_₂o arylalkyl group, or a polyoxyalkylene chain;

X and Y can be the same or different and represent H, OH, -( CR"₂) _X'COR, , (CR"₂)_x -OH, (CR"₂) _X NH₂, (CR"₂) _X NR₂, epoxy, halide, _( CR"₂) _x OCH=CH₂, - (CR"₂)_X -C=CH₂, -C=CH₂ or -(CR"₂)_x -(OR¹¹)_a-(OR¹¹)_b-OH;

R" may independently be Ci_₆ alkyl or H, especially H;

x' is 1 to 10, such as 1 to 5, especially 2 to 5, especially 3 to 5;

R is H, Ci_₂₀ alkyl, C₂_₂₀ alkenyl, C₃_₂₀ cycloalkyl, C₆_₂o aryl, C₇_₂₀ arylalkyl group; R¹¹ are each independently C₂_₆ alkylene;

a= 0-50, b= 0-50 and a+b = 1-50; and

n is 1-500, more preferably 10-300, especially 15-100;

or n' + m add to 1-500, more preferably 10-300, especially 15-100;

with the proviso that the X and Y groups in monomer B' are selected to react with the X and Y groups in monomer A' to form a hydro lysable group. That group is preferably not an ester. Preferably the hydrolysable group is an acetal.

These monomers undergo a polymerisation reaction to form a copolymer of structure -[ABAB]-.

In monomer A', it is preferred if X and Y can be the same or different and represent (CH₂)_x<-OH, epoxy, halide, -( CH₂) _x COR_, _(CH₂) _x OCH=CH₂, -(CH₂)_X>- C=CH₂, -C=CH₂ or -(CR'yHOR¹ V(OR^H)b-OH. X and Y are ideally the same.

In this embodiment of monomer B' itis preferred if X and Y can be the same or different and represent (CH₂)_x -OH, epoxy, halide, - (CH₂) _x COR, -OCH=CH_2, _(CH₂) _x<OCH=CH₂, -(CH₂)_X -C=CH₂, -C=CH₂ or -(CH₂)_x -(OR¹¹)_a-(OR¹¹)_b-OH. X and Y are ideally the same.

It is particularly preferred if the X/Y group on one monomer contains a vinyl group and the X/Y group on the other monomer is an alcohol.

It is particularly preferred if the X/Y group on one monomer contains an aldehyde and the X/Y group on the other monomer is an alcohol.

Viewed from another aspect the invention provides a binder for a marine coating composition comprising the reaction product of at least one polysiloxane of general formula (Α')

wherein each Ri is the same or different and represents an unsubstituted or substituted Ci_₂o alkyl, C₂_₂o alkenyl, C3-20 cycloalkyl, C₆-₂o aryl, C7-20 arylalkyl group, or a polyoxyalkylene chain;

X and Y can be the same or different and represent H, OH, -( CR"₂) _X'COR , (CR"₂)_x -OH, (CR"₂) _X NH₂, (CR"₂) _X NR₂, epoxy, halide, (CR"₂) _x OCH=CH₂, - (CR"₂)_X -C=CH₂ group, -C=CH₂ group or -(CR"₂)_x -(OR¹¹)_a-(OR¹¹)_b-OH;

R" may independently be Ci_₆ alkyl or H, especially H;

x' is 1 to 10, such as 1 to 5, especially 2 to 5, especially 3 to 5;

R is H, Ci_₂₀ alkyl, C₂_₂₀ alkenyl, C₃_₂o cycloalkyl, C₆_₂o aryl, C₇_₂₀ arylalkyl group;

R¹¹ are each independently C₂_₆ alkylene;

a= 0-50, b= 0-50 and a+b = 1-50; and

n is 1-500, more preferably 10-300, especially 15-100;

or n' + m add to 1-500, more preferably 10-300, especially 15-100;

and (i) at least one second monomer B' of formula

W-Q-Z B' wherein W and Z are each independently OH, OR, COR, (CR"₂)_x<-OH, (CR"₂) _X>NH₂, (CR"₂) _X NR₂, epoxy, halide, -OCH=CH₂, _( CR"₂) _x OCH=CH₂, -(CR"₂)_X>- C=CH₂, -C=CH₂, or -(CR"₂)_x -(OR¹¹)_a-(OR¹¹)_b-OH;

Q is an aliphatic, cycloalkyl, cycloalkenyl, polyoxyalkylene, amine ether or aromatic group having up to 20 carbon atoms,

R¹¹ are each independently C₂_₆ alkylene;

a= 0-50, b= 0-50 and a+b = 1-50; and

with the proviso that the W and Z groups in monomer B' are selected to react with the X and Y groups in monomer A' to form a hydro lysable group such as an acetal.

The monomer B' may also be an acetal of formula

Ri₅0-CH(R₁₆)-0-CH(R₁₆)-ORi₅ B2 where R₁₅ is H or Ci_₆ alkyl and Ri₆ is H, Ci_₆ alkyl or two Ri₆ groups taken together form a ring having 4 to 8 members. Where a structure B2 is employed, the X/ group is ideally a carbinol.

Monomer B' may also be a group

wherein W and Z are each independently OH, COH, CO-Ci_₆ alkyl, halide, - OCH=CH₂, (CH₂) _x<OCH=CH₂ or a (CH₂) _X<C=CH₂, or -C=CH₂;

x' is 1 to 10, such as 1 to 5, especially 2 to 5, especially 3 to 5;

and Q_w is an Ci_₂o alkyl, C₂_₂o alkenyl, C₆-₂o aryl, C₇-₂o arylalkyl interrupted by one or more ester groups- O-CO or CO-O-.

Preferred is the reaction of PDMS-(CH₂)_x -OH with either CH₂=CH-0-Q-0- CH=CH₂ or RO-Qw-OR (R=Me,Et and Q contains an acetal).

Viewed from another aspect the invention provides a fouling release coating composition comprising a binder as hereinbefore defined and at least one of filler, pigment, solvent, additive, curing agent and catalyst, preferably in the absence of a biocide.

Viewed from another aspect the invention provides an anti- fouling coating composition comprising a binder as hereinbefore defined and at least one anti- fouling agent.

Viewed from another aspect the invention provides a process for protecting an object from fouling comprising coating at least a part of said object which is subject to fouling with a coating composition as hereinbefore described and preferably curing the composition.

Viewed from another aspect the invention provides an object coated with a coating composition as hereinbefore defined, preferably a cured composition. Viewed from another aspect the invention provides a process for the preparation of a binder for a marine coating composition comprising copolymerising a polysiloxane monomer A' and at least one second monomer B' as herein defined so as to form an - ABAB- copolymer in which hydro lysable functional groups are present in the backbone of the copolymer.

Viewed from another aspect the invention provides use of a binder as hereinbefore defined for use in a fouling release composition or a marine anti- fouling coating composition.

Definitions

The terms biocide and anti- fouling agent are used interchangeably herein and are defined below.

It will be appreciated that second monomer B' is necessarily different from polysiloxane monomer A'. Even if monomer B' is itself a polysiloxane it must be different from polysiloxane unit A' in order to allow a copolymerisation reaction to occur.

The binder of the invention contains at least one hydro lysable functional group in the backbone of the polymer, preferably multiple hydrolysable groups. The term hydro lysable functional group refers to a group that undergoes hydrolysis in seawater. Groups that undergo hydrolysis are well known to any skilled chemist and we describe groups that are representative of hydrolysable groups below. The polymer should preferably contain a plurality of hydrolysable groups in the backbone of the polymer, such as 3 or more.

It will be understood that the hydrolysis reaction is one whose rate is highly dependent on both the chemical structure/composition of a compound/binder as well as the surrounding environmental conditions (salinity, pH, temperature, moisture content, etc.). The hydrolysable group should be one which hydrolyses at a temperature of 0- 35°C, and at a pH and salinity reflective of natural sea water.

The term "hydrolysable group" should be one that undergoes a hydrolysis reaction at a rate sufficient as to cause a coating surface polishing effect when said surface is moving through sea water, i.e. undergo hydrolysis in sea water at a temperature range of 0-35°C, and at a pH and salinity reflective of natural sea water. Preferred hydro lysable groups include: alkoxy based groups such as a-hydroxy esters, , ortho ester, acetal, hemiacetal, ketal, carbamate, and carbonate.

Most preferred hydro lysable groups include: acetal, ketal, hemi-ketal or hemi acetal.

For the avoidance of doubt, ethers, thioethers, amides and amines are not considered sufficiently hydrolysable in this respect. The siloxane group is not considered sufficiently hydrolysable.

Hydrolysable groups need to be present in the backbone of the polymer, i.e. not in a side chain off the main polmer chain. The hydrolysable groups repeat in the backbone. Whilst there may be hydrolysable groups in side chains of the polymer, hydrolysable groups must be present in the backbone of the polymer.

In order to be effective, the hydrolysable groups should be spread throughout the polymer molecule, rather than located only at the ends of the molecule for example. The copolymer of the invention is preferably not a block copolymer in which there are blocks of siloxane and end blocks of another material such as a polyester, i.e. a polymer of structure AAAABBBBBBAAAA. Rather, the copolymer of the invention is of structure -[ABAB]-, with at least two repeating units of monomer A' and at least two repeating units of monomer B'. It will be appreciated that there can be many repeating units and the formula -[ABAB]- is intended to encompass copolymers with any number of AB repeating units. We define molecular weights below.

The monomers A' and B' react together to form polymer repeating units A and

B.

The term amine ether refers to the structure alkylene-NPv2o-alkylene, such as Ci_ 6-alkylene-NH-Ci_6 alkylene. R₂o may be Ci_₆ alkyl or H.

In any embodiment of the invention, alkyl or alkylene groups are preferably linear.

The term epoxy preferably refers to a compound

x' is 1 to 10, such as 1 to 5, especially 2 to 5, especially 3 to 5;

R" may independently be CI -6 alkyl or H;

Both n' and m have values of 0 to 500 such as n' + m add to 1-500, more preferably 10-300, especially 15-100.

In any embodiment the subscripts a, b or the total of a+b is preferably 1 to 10.

Detailed Description

This invention relates to a new binder that can be used in a fouling release coating composition or an anti-fouling coating composition. The fouling release composition is preferably free of anti-fouling agent and is formed from a coating composition comprising the binder of the invention, ideally via crosslinking of that composition. The term anti-fouling coating composition refers to a composition comprising the binder of the invention and at least one marine anti-fouling agent. The fact that the binder contains hydrolysable groups makes the binder ideal for use in either type of coating. The slow hydrolysis also allows regeneration of the coating surface. This regeneration effectively deals with the issue of algae/slime formation on a fouling release coating composition. The hydrolysis reaction allows controlled release of the anti-fouling agent in an anti-fouling coating.

We use the term coating composition below to refer to either anti-fouling or fouling release coating compositions.

The term binder is a term of this art. The binder is the actual film forming component of the coating composition. The coating composition comprises the binder as well as other components as discussed in detail below. The binder imparts adhesion and binds the components of the coating composition together.

Polysiloxane Component A'

The polymer binder of the invention is made up from multiple monomers, e.g. at least two monomers. There is at least one polysiloxane unit A' (which may be considered a polysiloxane monomer) and at least one other monomer unit (called the second monomer herein) B', that reacts with the polysiloxane unit A' to generate a copolymer with a plurality of hydrolysable linkages in the polymer backbone. The polymer is of the type -ABABA- and is not a block copolymer of the type

AAABBBBBBAAA. It is the hydrolysable linkages that hydro lyse over time in seawater and allow regeneration of the surface of a fouling release coating and allow renewal and leaching of the biocide present in the anti- fouling composition of the invention.

As discussed in detail below, there are many hydrolysable linkages that can be introduced into the backbone of the polymer, such as acetal, hemiacetal, hemiketal and ketal. These hydrolysable links may be formed during an actual polymerisation reaction or they may also be present within the backbone of the polymerising units before polymerisation and hence become part of the copolymer backbone during

polymerisation. It is also possible for there to be hydrolysable groups formed during the copolymerisation as well as hydrolysable groups present within the monomer backbone and hence polymer backbone. In a preferred embodiment therefore monomer B' contains at least one hydrolysable group within the backbone of the monomer which will become part of the polymer backbone on copolymerisation with the polysiloxane.

In one embodiment therefore, the introduction of these hydrolysable groups relies on a reaction between the polysiloxane unit A' and the second monomer B' so as to generate the hydrolysable linkage. That reaction can be carried out in many ways depending on the end group on a polysiloxane and the end group on the second monomer. The chemistry involved in coupling the two reactants is therefore broadly defined but chemically quite simple. The skilled person knows many ways of developing an acetal linkage for example. It will be appreciated that the polysiloxane unit can act as the nucleophile or may act as the electrophile depending on the functional groups present. It may be easier to use the polysiloxane unit as a nucleophile but the invention could easily be adapted to place an electrophilic group at the end of the polysiloxane unit and allow attack on the polysiloxane unit by the second monomer. The polymerisation is preferably a condensation polymerisation or addition

polymerisation but other types of polymerisation familiar to the skilled person can also be used.

In a second embodiment, the second monomer might contain one or more hydrolysable groups in its backbone that become part of the polymer backbone upon copolymerisation with the polysiloxane. Again, the invention provides a polymer with such a hydrolysable group.

In a third embodiment, the second monomer might contain one or more hydrolysable groups in its backbone that become part of the polymer backbone upon copolymerisation with the polysiloxane and a hydrolysable link is developed between the A' and B' monomers on copolymerisation.

The crux of the invention is the appreciation that a valuable marine binder can be prepared by introducing hydrolysable linkages into the backbone of a polysiloxane polymer and the skilled person is aware that there are many ways of introducing such a group.

The polysiloxane unit which is copolymerised to generate a binder of the invention is preferably of general formula (Α'):

wherein each Ri is the same or different and represents an unsubstituted or substituted Ci_₂o alkyl, C₂_₂o alkenyl, C₃_₂o cycloalkyl, C₆-₂o aryl, C₇-₂o arylalkyl group, or a polyoxyalkylene chain;

X and Y can be the same or different and represent H, OH, -( CR"₂) _X'COR, (CR"₂)_x -OH, (CR"₂) _X NH₂, (CR"₂) _X NR₂, epoxy, halide, , _( CR"₂) _x OCH=CH₂, - (CR"₂)_X -C=CH₂, -C=CH₂ or -(CR"₂)_x -(OR¹¹)_a-(OR¹¹)_b-OH;

x' is 1 to 10, such as 1 to 5, especially 2 to 5, especially 3 to 5;

R" may independently be CI -6 alkyl or H;

R is H, Ci_₂₀ alkyl, C₂_₂₀ alkenyl, C₃_₂₀ cycloalkyl, C₆_₂o aryl, C₇_₂₀ arylalkyl group; and

n is 1-500, more preferably 10-300, especially 15-100.

The term arylalkyl group is used herein to cover both benzyl type linkers (CH₂- Ph) where the bond to the Si is via the alkyl portion or methylphenyl type groups where the bond to the silicon is via the aryl group. It is preferred if all Ri groups are the same. It is preferred if Ri _ls Ci_₂o alkyl, C₂_ 20 alkenyl, C₆-₂o aryl, C₇-₂o arylalkyl. It is preferred if Ri is unsubstituted. It is preferred if Ri is a Ci_6 alkyl group or C₇_i₂ arylalkyl. It is preferred if Ri is a Ci_₆ alkyl group such as ethyl or especially methyl. The use of a PDMS is therefore especially preferred. It is also possible however for at least one Ri group to be a polyoxyalkylene chain. The presence of such a chain enhances the hydrophilicity of the molecule. A suitable polyoxyalkylene chain may be one of formula:

where R¹⁰ and R^{1 1} are each independently C₂_₆ alkylene and R¹² is H, CH₃CO-, CH₃CH₂CO-, HCO-, or Ci_₆alkyl and a= 0-50, b= 0-50 and a+b = 1-50. It is preferred if R¹² is not H to avoid any reaction of the side chain. R¹² is preferably CH₃CO-, CH₃CH₂CO-, HCO-, or Ci_₆alkyl, especially CH₃CO- or CH₃CH₂CO-,

Thus, suitable materials include those selected from polyoxy ethylene, polyoxypropylene and poly(oxyethylene-co-oxypropylene). A preferred polysiloxane monomer is polydimethylsiloxane (PDMS). It will be appreciated that the repeating unit -Si-O-Si- is not regarded as hydrolysable.

The end groups X and Y are preferably the same. It is preferred if all R groups are the same. It is preferred if R is a Ci_₆ alkyl group such as ethyl or methyl.

It is preferred if X and/or Y are a carbinol, i.e. an (CH₂)_XOH chain or

(CH₂)_x COH.

The subscript x' is preferably 1 to 10, such as 2 to 5 or 3 to 5.

The use of PDMS carbinol is a preferred option.

In a preferred option, the number average molecular weight (Mn) of the polysiloxane monomer A' may be at least 700, such as at least 1 ,200, such as at least 2,000. An upper limit of 40,000 such as 20,000, e.g. 17,000 is appropriate, such as at most 15,000.

In theory, a branched polysiloxane monomer could be used in which therefore there are more end groups than just X and Y identified in formula (Α') above. The use of a branched structure allows the generation of a branched copolymer with the second monomer. It is believed however, that the use of a bifunctional polysiloxane containing essentially two reactive ends groups is preferred as such a monomer allows the generation of an essentially linear polymer. Any polymer of the invention will contain at least two residues derived from a polysiloxane unit.

A preferred polysiloxane is therefore of formula (A"):

wherein each Ri is methyl,

X and Y are the same and represent (CH₂)_X'-OH, -(CH₂)_X'-COH,

>OCH=CH₂, -(CH₂) _X C=CH₂ group, or -C=CH₂ group;

x' is 1 to 10, especially 2 to 5, such as 3 to 5; and

n is 10-300, especially 15-100.

A more preferred polysiloxane is therefore of formula (Al):

wherein each Ri is methyl,

X and Y are the same and represent -(CH₂)_X'-OH or -(CH

x' is 1 to 5, especially 2 to 5, such as 3 to 5; and

n is 10-300, especially 15-100.

A preferred polysiloxane is therefore of formula (A3):

(A3) wherein each Ri is methyl,

X and Y are the same and represent (CH₂)_x -OH;

x' is 1 to 5; and

n is 15-300.

A more preferred polysiloxane is therefore of formula (A2):

wherein each Ri is methyl,

X and Y are the same and represent (CH₂)_X'-OH;

x' is 1 to 5, especially 2 to 5, such as 3 to 5; and

n is 10-300, especially 15-100.

Potential siloxane units that may be used include:

R' =Ph, -CH₂-Ph, -CH₂(CH₃)-Ph, C_1-6-alkyl

where the variables are as herein defined. The first option is the most preferred.

In order to manufacture the binder of the invention, the polysiloxane is reacted with at least one further monomer B'. This is the second monomer. Hydro lysable groups are typically generated during the polymerisation reaction and may also become part of the polymer backbone during the polymerisation process. The hydro lysable group is preferably an acetal group.

It is preferred if the polysiloxane backbone in the polysiloxane of the invention is free from any groups of formula -Si-O-CO-. It is also preferred if the polysiloxane backbone in the polysiloxane of the invention is free of lactide links, i.e. -CO-alkyl-O- groups, such as -CO-Ci_3-alkyl-0-.

It is preferred to use a multifunctional second monomer in an addition copolymerisation reaction with the polysiloxane unit. In such a polymerisation reaction, the two "monomers" react to generate a copolymer having the structure - [ABAB]- in which a hydro lysable linkage is present between each A and B residues. In essence therefore the end group of the polysiloxane monomer reacts with the end group of the second monomer to generate a functional group that both links the two units and hydro lyses in sea water and therefore ensures that the binder of the invention is one that self polishes.

The second monomer is preferably therefore a divinyl compound such as a divinyl ether. It is possible to use a trifunctional or tetrafunctional second monomer (and so on) to create a branched structure if desired. It is however preferred, if the second monomer is bifunctional and therefore generates an essentially linear polymer. In a most preferred embodiment therefore, both polysiloxane unit and second monomer are bifunctional and therefore have two groups only that undergo copolymerisation.

It is possible to have a monomer with differing reactive groups. It will be preferred that where different groups are present, both are nucleophiles or both are electrophiles. Variations of the chemistry here will be apparent to the person skilled in the art.

In one embodiment, the second monomer B' can itself be based on a

polysiloxane that copolymerises with polysiloxane unit A' to form a copolymer in which the polysiloxane units are linked via hydrolysable groups. .

Thus, in one aspect the monomer B' is of formula

wherein each Ri is the same or different and represents an unsubstituted or substituted Ci_₂o alkyl, C₂_₂o alkenyl, C₃_₂o cycloalkyl, C₆-₂o aryl, C₇-₂o arylalkyl group, or a polyoxyalkylene chain;

X and Y can be the same or different and represent H, OH, (CR"₂)_X'COR, (CR"₂)_x -OH, (CR"₂) _X NH₂, (CR"₂) _X NR₂, epoxy, halide, , _( CR"₂) _x OCH=CH₂, - (CR"₂)_X -C=CH₂, -C=CH₂ or -(CR"₂)_x -(OR^{1 1})_a-(OR^{1 1})_b-OH;

x' is 1 to 10, such as 1 to 5, especially 2 to 5, especially 3 to 5;

R" may independently be CI -6 alkyl or H R is H, Ci_2o alkyl, C2-20 alkenyl, C₆_2o aryl, C7-20 arylalkyl group;

R^{1 1} are each independently C2-6 alkylene;

a= 0-50, b= 0-50 and a+b = 1-50; and

n is 1-500, more preferably 10-300, especially 15-100;

with the proviso that the X and Y groups in monomer B' are selected to react with the X and Y groups in monomer A' to form a hydrolysable group such as an acetal group.

When monomer B' is a polysiloxane, preferred structural options for monomer B' are the same as those for monomer A'.

In preferred options the monomer B' is as defined for A", Al, A3 or A2 with the proviso that the X and Y groups in monomer B' are selected to react with the X and Y groups in monomer A' to form a hydrolysable group such as an acetal group.

Ideally, one mononer is provided with a (0¼)_χΌΗ chain and the other an -OCH=CH2 group. Alternatively, one monomer has a (CH₂)_X'COH group and the other (CH₂)_XOH.

Where the second monomer is not a polysiloxane, the second monomer is preferably of lower molecular weight than the polysiloxane unit so that the majority, by weight, of the binder polymer is formed from the polysiloxane residues. It is therefore preferred if the number average Mn of the second monomer, when other than a polysiloxane is less than 2,000, such as less than 1,000, especially less than 500, such as less than 400.

In other embodiments, especially where the second monomer comprises a polysiloxane, the number average molecular weight (Mn) of the polysiloxane monomer B' may be at least 700, such as at least 1,200, such as at least 2,000. An upper limit of 40,000 such as 20,000, e.g. 17,000 is appropriate, such as at most 15,000.

The second monomer may have the general formula (Β')

W-Q-Z (Β') where W and Z are the same or different and are functional groups that can react with the end groups X and Y on the polysiloxane monomer, to form a hydrolysable group such as a acetal group; and Q is an aliphatic, cycloalkyl, cycloalkenyl. polyoxyalkylene, amine ether or aromatic group having up to 20 carbon atoms. The term aromatic group refers to a group containing an aromatic ring. It may also contain other components such as an alkyl chain.

W and Z arc preferably OH, ( OH, CO-C _l alkyl, halide, -OCH=CH₂, (CH₂) _x>OCB=CH₂ or a (CH₂) _X.C=CH₂, or -C=CH₂;

The Mw of the W-Q-Z molecule is preferably less than 2,000, such as less than 1 .000, especially less than 500, such as less than 300.

Q is preferably a C_3-10 alkylenc or a polyoxyalkene group.

If Q is a polyoxyalkylene it may have the structure

-R¹⁰-(ORⁿ)_a-(OR^{1 !})b- vvhere R¹⁰ and R^{1 1} are each independently C₂^ alkylene and a= 0-50, b= 0-50 and a + b = 1 -50.

The group linking the W and Z groups may comprise further hydrolysable links within the molecule such as ester linkages. These ester links would become part of the polymer backbone upon reaction with the monomer A'. The linker could be provided with additional hydrolysable groups within its backbone to tune the hydrolysabilty of the polymer. That hydrolysable group could be designed to differ from the

hydrolysable group that forms from the reaction of the polysiloxane unit and the second monomer.

For example, if the monomer B' was represented by the ester vinyl ether compound below, you can introduce both ester and acetal linkages into the binder backbone to tailor the hydrolysabil ity of the binder:

Combinat ion of poly( acetal- and poly(ester-siloxane) copolymers

O

r indicates a repeating unit. The value of r is a function of the Mn of the polymer. Scheme 1

This affords a dual mode of hydrolysis to tune the polishing efficiency.

A suitable monomer B' may therefore comprise groups W and Z as hereinbefore defined linked by a linker group comprising one or more ester functional groups and up to 20 carbon atoms.

Thus, monomer B' may be a group

wherein W and Z are each independently OH, COH, CO-Ci_₆ alkyl, halide, - OCH=CH₂, (CH₂) _x<OCH=CH₂ or a (CH₂) _X<C=CH₂, or -C=CH₂;

x' is 1 to 10, such as 1 to 5, especially 2 to 5, especially 3 to 5;

and Q_w is an Cl-20-alkylene, C2-20-alkenyl, C6-20 aryl, or C7-20 arylalkyl interrupted by one or more ester groups- O-CO or CO-0-. The ester groups should not be adjacent the W or Z groups. Ideally an alkylene linker separates any ester group from the W and Z groups.

More preferably monomer B' might be

wherein W and Z are each independently OH, -COH, -OCH=CH₂, or -C=CH₂; and Q_w is an Cl-6-alkylene or C7-20 arylalkyl interrupted by one or more ester groups- O-CO or CO-0-. The ester groups should not be adjacent the W or Z groups. Ideally an alkylene linker separates any ester group from the W and Z groups

More preferably monomer B' might be

wherein W and Z are -OCH=CH₂;

and Qw is an Cl-10-alkylene or a polyoxyalkylene -R¹⁰-(ORⁿ)_a- where R¹⁰ and R¹¹ are each independently C₂-alkylene and a= 1-10.

For example, the linker might comprise diethylene vinyl ether terephthalate, diethylene vinyl ether phthalate, diethylene vinyl ether isophthalate, dipropylene vinyl ether phthalate, dipropylene vinyl ether terephthalate, dipropylene vinyl ether isophthalate, diethylene vinyl ether maleate, diethylene vinyl ether fumarate, and diethylene vinyl ether itaconate, bis[4-(vinyloxy)butyl] 1,6-hexanediylbiscarbamate, bis[4-(vinyloxy)butyl] isophtalate, bis[4-(vinyloxy)butyl] succinate, bis[4- (vinyloxy)butyl] terephthalate, bis[4-(vinyloxymethyl)cyclohexylmethyl] glutarate.

In a further embodiment the monomer B' is itself an acetal. For example, a compound of formula

Ri₅0-CH(R₁₆)-0-CH(R₁₆)-ORi5 where R15 is H or Ci_₆ alkyl and Ri₆ is H, Ci_₆ alkyl or two Ri₆ groups taken together form a ring having 4 to 8 members. R15 is preferably Me. An acetal might be generated via a dialkoxy tetrahydrofuran or dialkoxy pentahydropyran, such as dimethoxy tetrahydrofuran.

In one embodiment Q is linear.

W and Z groups are selected so as to produce a bond, preferably a hydrolysable linker with the X and Y atoms of the polysiloxane. In some of the examples, W and Z represent vinyl ether and that vinyl ether reacts with a carbinol to form an acetal. The definition therefore of the W and Z groups are tied to the nature of the X and Y groups in the polysiloxane as will be readily appreciated by the organic chemist.

W and Z can therefore be selected from OH, COH, (CH₂)x'-OH, Hal, epoxy, - 0-CH=CH₂ , or a (CH₂)x'-C=CH₂ group, x' are as hereinbefore defined, i.e. x' is 1 to 10.

As noted above, one option for a hydrolysable linkage is an acetal linkage: e.g. - 0-CR^e ₂-0- where R^e is the same or different selected from CI -6 alkyl or H, especially H or Me, or 0-CR^e ₂-0-CR^f ₂-0- where R^e and R^f is the same or different selected from CI -6 alkyl or H, especially H or Me, or in the second option one R^e and one R^f taken together form a ring. Such a link can be constructed in various ways. One method involves the condensation of an aldehyde and an alcohol. A preferred method involves an ene reaction of a carbinol and a vinyl ether. In one embodiment therefore W and Z present CH₂=CH-0- and X and Y represent -(CH₂)_XOH (or vice versa). In one embodiment therefore W and Z present -COH and X and Y represent -(CH₂)_XOH (or vice versa).

Illustrative, non- limiting examples of the alkenyl ether monomers B' which can form acetal linkers are ethylene glycol divinyl ether, triethylene glycol divinyl ether, 1,2-propanediol divinyl ether, 1,3 -propanediol divinyl ether, 1,3-butanediol divinyl ether, 1,4-butanediol divinyl ether, tetramethylene glycol divinyl ether, neopentyl glycol divinyl ether, trimethylolpropane trivinyl ether, trimethylolethane trivinyl ether, hexanediol divinyl ether, 1,4-cyclohexanediol divinyl ether, 1,4-divinyloxymethyl cyclohexane, tetraethylene glycol divinyl ether, pentaerythritol divinyl ether, pentaerythritol trivinyl ether, pentaerythritol tetravinyl ether, sorbitol tetravinyl ether, sorbitol pentavinyl ether, ethylene glycol diethylene vinyl ether, triethylene glycol diethylene vinyl ether, ethylene glycol dipropylene vinyl ether, triethylene glycol diethylene vinyl ether, trimethylolpropane triethylene vinyl ether, trimethylolpropane diethylene vinyl ether, pentaerythritol diethylene vinyl ether, pentaerythritol triethylene vinyl ether, pentaerythritol tetraethylene vinyl ether, adipic acid divinyl ester, 1,4- cyclohexanedimethanol divinyl ether, divinyloxy 1,4-cyclohexanedimethanol and PEG- divinyl ethers with different Mn.

In a preferred embodiment Q includes a polyether. It may therefore be that the Q linker includes a (-0-CH₂CH₂)- repeating unit such as in tri(ethylene glycol) divinylether.

If the siloxane is provided with an epoxy end group then the second monomer could be a diol. Any HO-Q-OH diol could be used where Q is as hereinbefore defined such as an alkylene chain having up to 10 carbon atoms. It is within the scope of the invention for more than one second monomer to be used in the preparation of the binder of the invention. Ideally, however, only one second monomer is used.

It is preferred if the second monomer is mixed in a roughly stoichiometric molar ratio with the polysiloxane or perhaps with a slight excess of the polysiloxane. The second monomer might also be a carbonate such as diallyl carbonate, pyrocarbonic acid diallyl ester or diallyl pyrocarbonate.

As previously noted, the use of polyalkylene glycol side chains is a possibility, for example using a polysiloxane unit:

wherein m and n', R, X and Y are as hereinbefore defined.

Introduction of polyether

In a preferred embodiment, the second monomer is designed so that it introduces a polyether group into the backbone of the molecule, e.g. a PEG or PPG group. The incorporated poly(oxyalkylene) such as PEG, PPG might have a Mw: 50- 5,000, such as 50-2,000, more preferably less than 1,000 . Preferably PEG with 1-100, more preferably 1-50, especially 2-30 repeating units.

The presence of the polyether will help regulate the water-uptake of the polymer film formed using the binder and may add hydrogel-like properties with PEG giving inertness towards protein adsorption.

In a preferred option therefore, the monomer B' comprises an ethylene glycol or propylene glycol repeating unit.

The explanations above allow the person skilled in the art to design a variety of binders that meet the requirements of the functional definitions in the claims.

Binder It will be appreciated that devising a general formula to cover all possible options is difficult. In a preferred embodiment, the binder of use in the invention comprises a backbone of formula C

wherein the variables are as herein before defined.,

A preferred binder might have a backbone comprising a plurality of units

wherein the variables are as hereinbefore defined;

Rp and Rs represent the atoms of a 5 or 6 membered carbocyclic ring.

n is 1-500, more preferably 10-300 especially 15-100.

The binder of the invention preferably has a number average molecular weight Mn of 2,000 to 100,000 such as 5,000 to 80,000, especially 10,000 to 50,000. The binder of the invention has a very low glass transition temperature, such as 0°C or less, preferably -50°C or less, especially -100°C or less.

End Capping

The polymer may have end groups represented by F and G. Groups F and G are as defined above for X and Y (or W and Z) or groups F and G can be derived via a post polymerisation end capping or end modifying of the copolymer. By end capping/end modifying, we mean a post polymerisation functionalisation of the end groups that form naturally during the copolymerisation, e.g. to contain curable end groups or end groups that can react with a crosslinker. Crosslinking might also be encouraged through functionalisation of Ri side groups.

F and G can be the same or different, typically the same as a slight excess of one of the monomers are used in the polymerisation. Preferably, F and G are alkoxy, hydroxyl group, or hydrolysable group(s) such as alkoxysilane or other functional groups such as amine or epoxy.

Ideally groups F and G are crosslinking groups, i.e. they are curable with or without the addition of a crosslinking agent. We discuss the option of end capping the polymer in detail below.

It will be appreciated also that the binder could involve different polysiloxane monomers and second and third monomers. The possibility of forming a terpolymer and so on is therefore within the scope of the invention.

Copolymer binders may be obtained by mixing all starting materials before polymerisation or by dosing one of the monomers during the reaction. It will be appreciated that the skilled person will know how to carry out polymerisations depending on the monomers employed. The binder which forms is typically an alternating ABABAB polymer of the units used, since units A and B are only able to react with each other and not themselves. If there is more than one of either type of unit then the pattern can change but it will be appreciated that a polysiloxane unit should not polymerise with itself and the second monomer should not polymerise with itself. It requires the presence of a second monomer to cause a polymerisation. The polymer is preferably not a block copolymer. If there are two second monomers B and C then the pattern is AXAXAX where X is randomly selected from B or C. The amounts of B and C present would depend in the stoichiometry of the polymerisation.

The polymerisation conditions can be widely varied although typically temperatures of 0 to 250°C are employed, e.g. 40 to 220°C. In the case that the polymerisation in question is a condensation polymerisation a condensate (normally water or an alcohol) is formed. This is preferably removed by distillation as the polymerisation continues. This can be achieved under reduced pressure. The polymerisation is preferable carried out in an inert atmosphere, e.g. nitrogen. In the case the polymerisation in question is an addition polymerisation, feeding of one of the monomers is preferred due to control of exothermic reaction.

The binder of the present invention have a number average molecular weight (Mn) of at least 5,000 g/mol, preferably at least 10,000 g/mol, more preferably at least 15,000 g/mol, especially greater than 20,000 g/mol. In an especially preferred embodiment, values of more than 10,000 g/mol are preferred. The number average molecular weight is preferably up to 100,000 g/mol, such as up to 80,000 g/mol.

There is however, a trade off here as increasing the Mn too far increases viscosity and means that more solvent is required to ensure that the coating composition can be applied. More solvent increases volatile organic content which is not desired. It will be appreciated of course, that the binder as a whole can be made from a mixture of two or more binders with different Mn and/or different hydrolysing properties/rates, i.e. different hydrolysing groups and (content of hydrolysing groups). By varying the nature of the binder components, we can vary the speed of hydrolysis.

It is preferred if the binder forms at least 30 wt%, e.g. at least 40 wt%, such as at least 50 wt%, of the coating composition. The binder may form up to 70 wt% or less, such as 60% or less of the coating composition.

Crosslinking and curing agent

In some embodiments on the invention, it is preferred to crosslink the binder polymer in use. The binder polymer of the invention may possess a curable end group due to the nature of the groups used to form the binder polymer. Such groups include silanol, carbinol, hydride, alkenyl, vinyl ether, allyl ether, alkoxysilane and alkoxy groups. Alternatively, the end group of the polymer can be end capped with a reactive group to allow a crosslinking reaction to occur.

The binder of the invention can be crosslinked in the absence or in the presence of a curing agent.

Examples of curing agents well known in the art include, for example, monomeric isocyanates, polymeric isocyanates and isocyanate prepolymers.

Polyisocyanates are preferred over monomeric isocyanates because of lower toxicity. Polyisocyanates can for example be based on diphenylmethane diisocyanate (MDI), toluene diisocyanate (TDI), hexamethylene diisocyanate (HDI) and isophorone diisocyanate (IPDI) chemistry. These are for example supplied under the tradename Desmodur by Bayer Material Science and Tolonate by Vencorex. Examples of polyisocyanates are Desmodur N3400, Desmodur N3300, Desmodur N3600 Desmodur N75, Desmodur XP2580, Desmodur Z4470, Desmodur XP2565 and Desmodur VL, supplied by Bayer Material Science.

Polyisocyanates can be made with different NCO-functionality. The NCO- functionality is the amount of NCO-groups per polyisocyante molecule or isocyanate prepolymer molecule. Polyisocyanates curing agents with different NCO-functionality can be used.

The curing agent is preferably present in an amount of 0.8-1.5 equivalents (equiv) NCO groups relative the amount of hydroxyl groups, preferably 0.9-1.4 equiv, more preferably 0.95-1.3 equiv, even more preferably 1-1.2 equiv.

The functionality of the end-groups of the binder will depend on the starting monomers. The end groups can easily be modified to other functional groups suitable for a wide range of curing reactions. Examples of other curable end groups include epoxy groups.

Ethylenically unsaturated groups such as (meth)acrylate groups may be introduced, for example, by reacting the hydroxyl groups in the binder with

ethylenically unsaturated carboxylic acids, such as acrylic acid or methacrylic acid.

It is preferred therefore if the binder inherently contains curable end groups or are modified to contain curable end groups. Compounds which have been modified to contain curable end groups may be referred to specifically as end group modified binders (or end capped modified binders). An alternative end group modifying agent is one comprising an alkoxysilane such as monoalkoxysilane, dialkoxysilane or trialkoxysilane. Current commercial fouling release coatings are commonly cured by a condensation curing mechanism involving hydrolysis of silane-(m)ethoxy compounds. This has advantages compared to e.g. isocyanate-based crosslinking as it minimizes the amount of polar entities introduced (which may cause increased polar interactions with fouling species). In order to facilitate a similar condensation curing mechanism for the binders of the invention, an end-capping reaction of the terminal functional groups may be performed.

For example, an alkoxysilane such as 3-isocyanatopropenyltrimethoxysilane can be employed to alter a terminal hydroxyl group.

In a further embodiment therefore, the binder is end capped with a compound comprising the group -SiR"d(OR')3-d where d=0-2, R" and R' independently selected from Ci_6 alkyl. Examples are trimethoxysilyl, triethoxysilyl, methyldiethoxysilyl, methyldimethoxysilyl, dimethylmethoxysilyl and dimethylethoxysilyl. The compound as a whole comprises this siloxy group and a further functional group capable of reacting with the end group on the formed copolymer binder. The end capping unit is ideally a low Mw compound having a Mw of up to 400.

Examples of compounds used include 3-isocyanatopropyltrimethoxysilane, 3- isocyanatopropyltriethoxysilane, 3 -aminopropyltrimethoxysilane, 3 - aminopropyltriethoxysilane, (3 -glycidoxypropyl)trimethoxysilane, 3 - chloropropyltrimethoxysilane, 3-mercaptopropyltrimethoxysilane,

allyltrimethoxysilane and vinyltrimethoxysilane. In the presence of moisture, the siloxy end groups present at the end of the binder will then begin to crosslink. In some instances the end groups may be mono(m)ethoxysilane in which case a separate crosslinking agent may be used to cure the coating (e.g. alkoxysilane such as methyl trimethoxysilane or condensation products thereof (e.g. WACKER® TES 40 WN)).

The cross-linking agent preferably constitutes 0-10 % by dry weight of the coating composition and is, e.g. an organosilicon compound represented by the general formula (2) shown below, a partial hydrolysis-condensation product thereof, or a mixture of the two:

Rd-Si-X₄-_d (2) wherein, each R represents, independently, an unsubstituted or substituted monovalent hydrocarbon group of 1 to 6 carbon atoms, each X represents,

independently, a hydrolysable group, and d represents an integer from 0 to 2, such as from 0 to 1.

The mixing of the binder polymer and the curing agent can be carried out shortly before application of the coating to an object, e.g. an hour or less before coating or the binder can be supplied in curable form but kept dry in order to prevent premature curing. In some embodiments the curing agent/end capping agent is supplied separately to the rest of the coating composition to prevent curing before the coating has been applied to the object. In case the ends are mono(m)ethoxysilane a (m)etoxy silane crosslinker, e.g. TES 40 WN, may be used in combination with the binder. Hence the coating composition of the invention can be supplied as a multipack (preferably two pack) formulation.

Viewed from another aspect therefore the invention provides a kit comprising (I) a binder polymer as described herein and (II) a curing or end capping agent. It would preferably be supplied with instructions on mixing the components shortly before application. One or other component may also be supplied with a catalyst to encourage the crosslinking process.

Coating Composition

The coating composition of the invention contains the binder or a mixture of binders. The composition may also contain other conventional components of a fouling release composition.

The polysiloxane-based binder typically constitutes 20-90% by dry weight, at least 40% by dry weight, in particular 50-90%) by dry weight, of the coating

composition.

The binder of the present invention will degrade in sea water. It will be understood that the degradation reactions which the binder undergoes is a hydrolysis reaction which occurs in the polymer backbone, i.e. the hydrolysable bonds are present in the polymer backbone. In addition to the binder, the coating composition of the invention may include other components such as additive oils, catalysts, biocides, enzymes and cobinders. Other conventional components include solvents, additives, pigments and fillers.

Additive oils

The coating composition might contain well known hydrophilic-mo dified additive oils e.g. as described in WO2011/076856. The composition may further include hydrophilic-modified polysiloxane oils, i.e. constituents which do not form covalent bonds to the polysiloxane-based binder matrix. Hydrophilic- modified polysiloxane oils are widely used as surfactants and emulsifiers due to the content of both hydrophilic and lipophilic groups in the same molecule. In contrast to the polysiloxane components discussed above, the hydrophilic-modified polysiloxane oils are selected so that they do not contain groups that can react with the binder (or binder components) or the cross-linker (if present), hence the hydrophilic-modified

polysiloxane oils are intended to be non-reactive, in particular with respect to the binder components. In particular, the hydrophilic-modified polysiloxane oils are devoid of any silicon-reactive groups such as Si-OH groups, hydrolysable groups such as Si-OR (such as alkoxy, oxime, acetoxy etc.) groups, so as to avoid reaction with constituents of the polysiloxane-based binder system.

The non-reactive hydrophilic-modified polysiloxane oils are typically modified by the addition of non- ionic oligomeric or polymeric groups which can be polar and/or capable of hydrogen bonding, enhancing their interaction with polar solvents, in particular with water, or with other polar oligomeric or polymeric groups. Examples of these groups include, amides (e.g. poly(vinyl pyrrolidone), poly[N-(2- hydroxypropyl)methacrylamide]), poly(N,N- dimethacrylamide), acids (e.g.

poly(acrylic acid)), alcohols (e.g. poly(glycerol), polyHEMA, polysaccharides, poly(vinyl alcohol)), ketones (polyketones), aldehydes (e.g. poly(aldehyde guluronate), amines (e.g. polyvinylamine), esters (e.g. polycaprolactones, poly( vinyl acetate)), ethers (e.g. polyoxyalkylenes like poly( ethylene glycol), poly(propylene glycol)), imides (e.g. poly(2-methyl-2-oxazoline)), etc., including copolymers of the foregoing.

Preferably the hydrophilicity is obtained by modification with polyoxyalkylene groups. In a preferred embodiment, the hydrophilic-modified polysiloxane oil (if present) has a number average molecular weight (Mn) in the range of 100-100,000 g/mol, such as in the range of 250-75,000 g/mol, in particular in the range of 500- 50,000 g/mol.

The one or more hydrophilic-modified polysiloxane oils are included in the coating composition in an amount of 0.01-30 %, e.g. 0.05-10 %, by dry weight. In certain embodiments, the one or more hydrophilic-modified polysiloxane oils constitutes 0.05-7 % by dry weight, e.g. 0.1-5 % by dry weight, in particular 0.5-3 % by dry weight, of the coating composition.

Other additive oils of interest are described in WO2008132196. Suitable unreactive fluids are silicone oils such as methylphenyl silicone oil,

polydimethylsiloxane, carboxyl- functional organisiloxanes as disclosed in WO

2008/132195; petroleum oils, polyolefm oils, polyaromatic oils, fluoro resins such as polytetra- fluoroethylene or fluid fluorinated alkyl- or alkoxy-containing polymers, or lanolin and lanolin derivatives and other sterol(s) and/or sterol derivative(s) as disclosed in PCT Application No PCT/EP2012/065920 or combinations thereof. A preferred unreactive fluid is methylphenyl silicone oil. Also of interest are fluorinated amphiphilic polymers/oligomers described in WO2014131695. The proportion of unreacted fluid is preferably 5-25 wt%, more preferably 5-10 wt%, based on the solids content of the coating composition.

Biocides/Anti-fouling agent

In one embodiment, a biocide can be used in the binder of the invention.

Suitable biocides are well known and can be found in WO2013/000479.

In the present context, the term "biocide" is intended to mean an active substance intended to destroy, deter, render harmless, prevent the action of, or otherwise exert a controlling effect on any harmful organism by chemical or biological means. Illustrative examples of biocides are those selected from metallo- dithiocarbamates such as bis(dimethyldithiocarbamato)zinc, ethylene- bis(dithiocarbamato)zinc, ethylene-bis(dithio-carbamato)manganese, and complexes between these; bis(l-hydroxy-2(lH)-pyridine- thionato-0,S)-copper; copper acrylate; bis(l-hydroxy-2(lH)-pyridinethionato-0,S)-zinc; phenyl(bispyridyl)-bismuth dichloride; metal biocides such as copper(I)oxide, cuprous oxide, metallic copper, copper metal alloys such as copper-nickel alloys; metal salts such as cuprous thiocyanate, basic copper carbonate, copper hydroxide, barium metaborate, and copper sulphide;

heterocyclic nitrogen compounds such as 3a,4,7,7a-tetrahydro-2-((trichloro- methyl)- thio)-lH-isoindole-l,3(2H)-dione, pyridine-triphenylborane, l-(2,4,6-trichloro- phenyl)- lH-pyrrole-2,5-dione, 2,3,5,6-tetrachloro-4-(methylsulfonyl)-pyridine, 2-methylthio- 4- tert-butylamino-6-cyclopropylamine-s-triazin, and quinoline derivatives; heterocyclic sulfur compounds such as 2-(4-thiazolyl)benzimidazole, 4,5-dichloro-2-n-octyl-4- isothiazolin-3-one, 4,5-dichloro-2-octyl-3(2H)-isothiazoline (Sea-Nine<®>-21 IN), 1,2- benzisothiazolin-3-one, and 2-(thiocyanatomethylthio)-benzothiazole; urea derivatives such as N-(l,3- bis(hydroxymethyl)-2,5-dioxo-4-imidazolidinyl)-N,N'- bis(hydroxymethyl)urea, and N-(3,4- dichlorophenyl)-N,N-dimethylurea, N,N- dimethylchlorophenylurea; amides or imides of carboxylic acids; sulfonic acids and of sulfenic acids such as 2,4,6-trichlorophenyl maleimide, 1.1- dichloro-N- ((dimethylamino)sulfonyl)-l-fluoro-N-(4-methylphenyl)-methanesulfenamide, 2.2- dibromo-3-nitrilo-propionamide, N-(fluorodichloromethylthio)-phthalimide, N,N- dimethyl- N'-phenyl-N'-(fluorodichloromethylthio)-sulfamide, and N-methylol formamide; salts or esters of carboxylic acids such as 2-((3-iodo-2-propynyl)oxy)- ethanol phenylcarbamate and N,N- didecyl-N-methyl-poly(oxyethyl)ammonium propionate; amines such as dehydroabiethyl- amines and cocodimethylamine;

substituted methane such as di(2-hydroxy-ethoxy)methane, 5,5'-dichloro-2,2'- dihydroxydiphenylmethane, and methylene-bisthiocyanate; substituted benzene such as 2,4,5, 6-tetrachloro-l,3-benzenedicarbonitrile, l,l-dichloro-N-((dimethyl- amino)- sulfonyl)-l-fluoro-N-phenylmethanesulfenamide, and l-((diiodomethyl)sulfonyl)-4- methyl-benzene; tetraalkyl phosphonium halogenides such as tri-n-butyltetradecyl phosphonium chloride; guanidine derivatives such as n-dodecylguanidine

hydrochloride; disulfides such as bis-(dimethylthiocarbamoyl)-disulfide,

tetramethylthiuram disulfide; phenylcapsaicin;

imidazole containing compound, such as medetomidine; 2-(p-chlorophenyl)-3- cyano-4- bromo-5-trifluoromethyl pyrrole and mixtures thereof. Presently, it is preferred that the biocide does not comprise tin. Currently preferred biocides are those selected from the group consisting of 2,4,5, 6-tetra- chloroisophtalonitrile (Chlorothalonil), copper thiocyanate (cuprous sulfocy anate) , N-dichloro - fluoromethylthio -N' ,Ν'- dimethy 1-N-pheny lsulfamide (Dichlofluanid), 3-(3,4-dichlorophenyl)- 1, 1-dimethylurea (Diuron), N2-tert-butyl-N4- cyclopropyl-6-methylthio-l,3,5-triazine-2,4- diamine (Cybutryne), 4-bromo-2-(4- chlorophenyl)-5-(trifluoromethyl)-lH-pyrrole-3- carbonitrile, (2-(p-chlorophenyl)-3- cyano-4-bromo-5-trifluoromethyl pyrrole; Tralopyril), Cybutryne, (RS)-4-[l-(2,3- dimethylphenyl)ethyl]-3H-imidazole (Medetomidine), 4,5-dichloro-2-n-octyl-4- isothiazolin-3-one (DCOIT, Sea-Nine® 21 IN), dichlor-N- ((dimethylamino)sulfonyl)fluor-N-(p- tolyl)methansulfenamid (Tolylfluanid), 2- (thiocyanomethylthio)-l,3-benzothiazole ((2- benzothiazolylthio)methyl thiocyanate; TCMTB), triphenylborane pyridine (TPBP); bis(l- hydroxy-2(lH)-pyridinethionato- 0,S)-(T-4) zinc (zinc pyridinethione; zinc pyrithione), bis(l- hydroxy-2(lH)- pyridinethionato-0,S)-T-4) copper (copper pyridinethione; copper pyrithione; Copper Omadine), zinc ethylene-l,2-bis-dithiocarbamate (zinc-ethylene-N-N'- dithiocarbamate; Zineb), copper(i) oxide, metallic copper, 3-(3,4-dichlorophenyl)-l, 1- dimethylurea (Diuron) and diiodomethyl-p-tolylsulfone; Amical 48, phenylcapsaicin. Preferably at least one biocide is selected from the above list.

In a particularly preferred embodiment, the biocides are preferably selected among biocides which are effective against soft fouling such as slime and algae.

Examples of such biocides are N2-tert-butyl-N4-cyclopropyl-6-methylthio- 1,3,5- triazine-2,4-diamine (Cybutryne), 4,5- dichloro-2-n-octyl-4-isothiazolin-3-one

(DCOIT, Sea-Nine® 21 IN), bis(l-hydroxy-2(lH)- pyridinethionato-0,S)-(T-4) zinc (zinc pyridinethione; zinc pyrithione), bis(l-hydroxy-2(lH)- pyridinethionato-0,S)-T-4) copper (copper pyridinethione; copper pyrithione) and zinc ethylene- 1,2-bis- dithiocarbamate (zinc-ethylene-N-N'-dithiocarbamate; Zineb), copper(I) oxide, metallic copper, copper thiocyanate, (cuprous sulfocyanate), bis(l-hydroxy-2(lH)- pyridinethionato-0,S)-T-4) copper (copper pyridinethione; copper pyrithione; Copper Omadine).

In a further particularly preferred embodiment, the biocide is an organic biocide, such as a pyrithione complex, such as zinc pyrithione, or such as copper pyrithione. Organic biocides are those either fully or in part being of organic origin. Optionally the marine anti- fouling agents may be encapsulated or adsorbed on an inert carrier or bonded to other materials for controlled release.

The total amount of organic biocide in the antifouling compositions of the invention may be in the range 0.1 to 40 wt%, such as 0.1 to 20 wt%, such as 0,5 to 10 wt% (dry weight of the coating composition), e.g. 1-8 wt%. The total amount of inorganic biocides such as cuprous oxide, copper (I) oxide, metallic copper etc. in the antifouling composition of the invention may be in the range of 0,5-80% by dry weight, such as 1-70. It will be appreciated that the amount of this component will vary depending on the end use and the marine anti- fouling agent used.

Catalyst

In order to assist the curing process, the coating composition of the invention might contain a catalyst. WO2014/131695 gives an extensive list of possible catalysts. Examples of catalysts that can be used include transition metal compounds, metal salts and organometallic complexes of various metals, such as tin, iron, lead, barium, cobalt, zinc, antimony, cadmium, manganese, chromium, nickel, aluminium, gallium, germanium and zirconium. The salts preferably are salts of long-chain carboxylic acids and/or chelates or organometal salts. Examples of suitable catalysts include for example, dibutyltin dilaurate, dibutyltin dioctoate, dibutyl tin diacetate, dibutyl tin 2- ethylhexanoate, dibutyltin di neodecanoate, dibutyl tin dimethoxide, dibutyltin dibenzoate, dibutyltin acetoacetonate, dibutyltin acetylacetonate, dibutyltin

alkylacetoacetonate, dioctyltin dilaurate, dioctyltin dioctoate, dioctyl tin diacetate, dioctyl tin 2-ethylhexanoate, dioctyltin di neodecanoate, dioctyl tin dimethoxide, dioctyltin dibenzoate, dioctyltin acetoacetonate, dioctyltin acetylacetonate, dioctyltin alkylacetoacetonate, dimethyltin dibutyrate, dimethyltin bisneodecanoate, dimethyltin dineodecanoate, tin naphthenate, tin butyrate, tin oleate, tin caprylate, tin octanoate, tin strearate, tin octoate, iron stearate, iron 2-ethylhexanoate, lead octoate, lead 2- ethyloctoate, cobalt-2-ethylhexanoate, cobalt naphthenate, manganese 2- ethylhexanoate, zinc 2-ethylhexanoate, zinc naphthenate, zinc stearate, metal triflates, triethyl tin tartrate, stannous octoate, carbomethoxyphenyl tin trisuberate, isobutyl tin triceroate. Further examples of suitable catalysts include organobismuth compounds, such as bismuth 2-ethylhexanoate, bismuth octanoate and bismuth neodecanoate. Further examples of suitable catalysts include organotitanium, organzirconium and

organohafnium compounds and titanates and zirconate esters such as, titanium naphthenate, zirconium naphthenate, tetrabutyl titanate, tetrakis(2- ethylhexyl)titanate, triethanolamine titanate, tetra(isopropenyloxy)-titanate, titanium tetrabutanolate, titanium tetrapropanolate, titanium tetraisopropanolate, tetrabutyl zirconate, tetrakis(2- ethylhexyl) zirconate, triethanolamine zirconate, tetra(isopropenyloxy)-zirconate, zirconium tetrabutanolate, zirconium tetrapropanolate, zirconium tetraisopropanolate and chelated titanates such as diisopropyl bis(acetylacetonyl)titanate, diisopropyl bis(ethylacetoacetonyl)titanate and diisopropoxytitanium bis(ethylacetoacetate), and the like.

Preferably the catalyst is present in an amount of 0.01 to 5wt% based on the total weight of the coating composition, especially 0.05 to 4 wt%.

Solvent, Pigments, Fillers and Additives

The coating may contain solvents. Suitable solvents include aliphatic, cycloaliphatic and aromatic hydrocarbons, alcohols, ketones, esters, and mixtures of the above. Examples of suitable solvents are white spirit, cyclohexane, toluene, xylene and naphtha solvent, esters such as methoxypropylacetate, n-butyl acetate and 2- ethoxyethylacetate; octamethyltrisiloxane, and mixtures thereof. The solvents, if any, typically constitute 5 to 50 wt% based on the total weight of the coating composition. The solid content may be determined in accordance with ASTM method D2697.

The coating composition of the invention may also comprise pigments.

Examples of pigments include black iron oxide, red iron oxide, yellow, iron oxide, titanium dioxide, zinc oxide, carbon black, graphite, red molybdate, yellow molybdate, zinc sulfide, antimony oxide, sod ium alumin ium sulfosil icates, quinacridones, phthalocyanine blue, phthalocyanine green, indanthrone blue, cobalt aluminium oxide, carbazoledioxazine, chromium oxide, isoindoline orange, bis-acetoaceto-tolidiole, benzimidazolone, quinaphthalone yellow, isoindoline yellow, tetrachloroisoindolinone, and quinophthalone yellow, metallic flake materials (e.g. aluminium flakes) or other so- called barrier pigments or anticorrosive pigments such as zinc dust or zinc alloys or other so-call lubricant pigments such as graphite, molybdenum disulfide, tungsten disulphide or boron nitride. Preferred pigments are black iron oxide, red iron oxide, yellow iron oxide, sodium aluminium sulfosilicate and titanium dioxide.

The proportion of pigment may be in the range of from 0 to 25 wt% by weight, based on the total weight of the coating composition, preferably in the range 0 to 15 wt%.

The coating composition of the invention may also comprise fillers. Examples of fillers that can be used in the coating composition according to the present invention are zinc oxide, barium sulphate, calcium sulphate, calcium carbonate, silicas or silicates (such as talc, feldspar, and china clay) including pyrogenic silica, bentonite and other clays, and solid silicone resins, which are generally condensed branched polysiloxanes. Some fillers such as fumed silica may have a thixotropic effect on the coating composition. The proportion of fillers may be in the range of from 0 to 25 wt% by weight, based on the total weight of the coating composition, preferably in the range 0 to 10 wt% and more preferably in the range 0 to 5 wt%.

The coating composition according to the present invention optionally comprises one or more components selected among other surfactants, wetting agents, thickeners, antisettling agents, and dyes.

An additional binder can be used to adjust the self-polishing properties and the mechanical properties of the coating film. Examples of binders that can be used in addition to the binder of the invention in the coating composition according to the present invention include other polysiloxanes.

Application of the coating composition

The coating composition of the invention can be applied to a whole or part of any object surface which is subject to fouling. The surface may be permanently or intermittently underwater (e.g. through tide movement, different cargo loading or swell). The object surface will typically be the hull of a vessel or surface of a fixed marine object such as an oil platform or buoy. Application of the coating composition can be accomplished by any convenient means, e.g. via painting (e.g. with brush or roller) or spraying the coating onto the object. Typically the surface will need to be separated from the seawater to allow coating. The application of the coating can be achieved as conventionally known in the art.

The coating composition can be applied by normal techniques, such as brushing, roller coating, or spraying (airless and air-assisted). To achieve proper adhesion to the substrate it is preferred to apply the coating composition to a primed substrate. The primer can be any conventional primer/sealer coating system suitable for PDMS coating. It is also possible to apply the coating composition according to the present invention on a substrate containing an aged anti- fouling coating layer or fouling release layer. Before the coating composition according to the present invention is applied to such an aged layer, this old layer is cleaned by high-pressure water washing to remove any fouling. The primer disclosed in WO 99/33927 can be used as a tie coat between the aged coating layer and the coating composition according to the present invention. Optionally the primer may comprise adhesion promoters as disclosed in WO

2010/018164.

Optionally the primer may comprise a biocide. After the coating has been cured it can be immersed immediately and gives immediate anti- fouling or fouling-release protection. As indicated above, the coating composition according to the present invention has very good anti-fouling and fouling-release properties. This makes these coating compositions very suitable for use as anti-fouling or fouling release coatings for marine applications. The coating can be used for both dynamic and static structures, such as boat hulls, buoys, drilling platforms, dry dock equipment, oil and/or gas production rigs, floating oil and gas processing, storage and offloading vessels, aqua culture equipment, netting and cages, energy generation devices such as offshore wind turbines and tidal and wave energy devices, cooling water intakes for power plants and power stations and pipes which are immersed in water and tanks, pipes and conduits used to store and transport water. The coating can be applied on any substrate that is used for these structures, such as metal, concrete, wood, plastic or fibre-reinforced plastic.

The invention will now be defined with reference to the following non limiting examples.

Determination of solids content of the polymer solutions The solids content in the polymer solutions are determined in accordance with ISO 3251 :2008. A test sample of 0.6 g ± 0.1 g are taken out and dried in a ventilated oven at 150°C for 30 minutes. The weight of the residual material is considered to be the non- volatile matter (NVM). The non- volatile matter content is expressed in weight percent. The value given is the average of three parallels.

Determination of polymer molar mass distribution

The polymers are characterized by Gel Permeation Chromatography (GPC) measurement. The molecular weight distribution (MWD) was determined using a Polymer Laboratories PL-GPC 50 instrument with two PLgel 5 μιη Mixed-D columns (300 x 7.5 mm) from Polymer Laboratories in series, Tetrahydrofuran as eluent at ambient temperature and at a constant flow rate of 1 mL/min and with a refractive index (RI) detector. The columns were calibrated using polystyrene standards Easivials PS-M from Polymer Laboratories. The data were processed using Cirrus software from Polymer Labs.

Samples were prepared by dissolving an amount of polymer solution corresponding to 5 mg dry polymer in 5 mL Tetrahydrofuran. The samples were kept for minimum 4 hours at room temperature prior to sampling for the GPC

measurements.

The weight-average molecular weight (Mw), the number-average molecular weight (Mn) and the dispersity ( £>_M), equivalent to Mw/Mn, are reported.

Water uptake and film loss

The water uptake was determined by gravimetric method. The coatings were applied on pre-weighed and numbered glass panels using film applicator with 300 μιη gap size. The films were dried under ambient conditions for at least 1 day, at 50°C overnight and then in desiccator under vacuum for 24 h. After drying the coated glass panels were weighed and placed in containers filled with artificial seawater. The artificial seawater was prepared by dissolving NaCl in deionized water (33.3 g/L) and, if necessary, adjusting the pH to 8.1-8.4 using 2M HCl(aq) or NaOH (aq) solutions.

At the reading, the panels and coating surfaces were quickly dried using compressed air. The panels were weighed and thereafter dried at 50°C for 2 days and then placed in a desiccator under vacuum for 24 hours before they were weighted again. The difference in weight before and after drying relative to the dry weight of the coating film after exposure is expressed as the water uptake in percentage. The difference in weight of the dried films at a reading relative to the initial dry film weight before exposure is expressed as the film loss in percentage. The results are presented as an average of three parallels.

Determination of polishing rates of coating films in seawater

The polishing rate was determined by measuring the reduction in film thickness of a coating film over time. For this test PVC discs were used. The PVC discs were pre- coated with suitable primer/tie-coat for the coating compositions. The coating compositions were applied as radial stripes on the disc using a film applicator. The thickness of the dry coating films were measured by means of a laser surface profiler. The PVC discs were mounted on a shaft and rotated in a container in which seawater is flowing through. Natural seawater which has been filtered and temperature-adjusted to 25°C ± 2°C was used. The PVC discs were taken out at regular intervals for measuring the film thickness. The discs were rinsed and allowed to dry overnight at room temperature before measuring the film thickness.

Chemicals

Alpha, omega-carbinol siloxane, e.g. Tegomer H-Si 2115 (n=10) or Tegomer H-Si 2315 (n=30), Evonik.

Tri(ethylene glycol) divinyl ether (CAS: 765-12-8), 1,4-Butanediol divinyl ether (CAS: 3891-33-6), Dimethoxytetrahydrofurane (CAS: 696-59-3), e.g. Sigma-Aldrich

3-isocyanatpropyl trimethoxysilane, e.g. Wacker

Dibutyltin dilaurate , e.g Sigma-Aldrich.

Example 1-2: Acetal- siloxane binders by addition polymerisation of carbinol terminated polydimethylsiloxane and divinyl ether monomers

(-C₂H₄-) or

(-OC₂H₄-)₂

Table 1.

Polymerisation procedure: Carbinol-terminated PDMS (n=50) and organic divinyl ether monomers (tri(ethylene glycol) divinyl ether or 1,4-butanediol divinyl ether) were dissolved in xylene and heated to 60°C under N₂(g) atmosphere. A catalytic amount of p-toluenesulfonic anhydride was added from a 5% (w/w) stock solution and the temperature was raised to 80°C. The reaction was allowed to proceed for 40 min after which the reaction was terminated by addition of a neutralizing amount of

trimethylamine and the reaction mixtures were allowed to cool to room temperature. GPC analysis of the starting carbinol-terminated PDMS (n=50) showed a Mn of 3620 g/mol and Mw of 6020 g/mol. The significantly higher molecular weights obtained for Example 1-2 (GPC: Mn / Mw, Table 1) indicate that polymerization was successful for both binders. Example 3-5: Acetal-siloxane binders by trans esterification polymerisation of carbinol terminated polydimethylsiloxanes and 2, 5 -dimethoxytetrahydrofuran monomer

Table 2.

Polymerisation procedure: The carbinol terminated PDMS and 2,5

dimethoxytetrahydrofuran were loaded in a three necked flask together with catalyst (para-toluene sulphonic acid) under stirring. The reaction mixture was heat slowly to 100 °C. A slow nitrogen stripping promoted the boiling of methanol. Vacuum of 10 mbar was applied to finalize the reaction. Example 3-5 binders were collected and analysed by GPC. The significant increase in molecular weight, compared to the starting carbinol terminated PDMS monomers (Table 2) confirmed that polymerisation was successful for all three binders.

Example 6: Water uptake and film loss in artificial seawater

Clear coat films of the poly(acetal-siloxane) binders from example 1-5 were cured using a isocyanate based cross-linker, 3-isocyanatopropyltrimethoxysilane, and dibutyltin dilaurate catalyst in xylene. Coating films were formed using a ratio of terminal hydroxyl group (binder) to isocyanate (crosslinker) of 1 : 1.5 (OH:NCO) with 0.1 % (w/w) catalyst and 30% (w/w) xylene. Films were applied on glass test panels using a film applicator with 300 μιη clearing. The water uptake and film loss in artificial seawater was studied over 30 days. A non-polishing reference ("PDMS reference") was prepared by curing a silanol-terminated PDMS 66% (w/w) (DMS-S33, Gelest) with ethyl silicate crosslinker 3% (w/w) (TES 40 WN, Wacker) using 1% (w/w) dibutyltin dilaurate catalyst in 30% (w/w) xylene. The non-polishing PDMS reference was chosen due to its resemblance to the binder systems used in classical commercial fouling release coatings.

Table 3.

The results show that all coatings of this invention (Example 1-5) have higher film loss after 30 days compared to the non-polishing PDMS reference. Notably, Example 2 which comprises hydrophilic PEG units in the backbone of the binder has the highest water uptake and film loss. Example 7: Coating compositions

Four different coating compositions were prepared by mixing the components shown in Table 4. The first composition, "FRC reference", represents a typical foul-release coating composition. Coating 1-2 are similar compositions where the silanol terminated polydimethylsiloxane binder (non-hydro ly sing) has been replaced by the poly(acetal- siloxane)s of Example 1-2. Coating 3 corresponds to a variant of Coating 2 with the addition of Copper Pyrithione biocide.

Table 4.

(1) DMS-S33 (Gelest)

(2) Aerosil R972 (Evonik)™

(3) Wacker® TES 40 WN

Example 8: Polishing

The first three coating compositions in Table 4 (FRC reference, coating 1-2) were applied as radial stripes on a PVC disc using a film applicator of 300 μιη clearance. The PVC disc had been pre-coated with one coat of Jotun Safeguard Universal ES primer and one coat of Jotun SeaLion tiecoat using airless spray within specified conditions. The test stripes were allowed to cure for a period of at least 24h under ambient conditions before testing commenced. In Table 5 the polishing of the three

compositions is presented. Each reading represents an average of three parallel stripes.

Table 5

The results show that coating 1-2 of this invention experience continuous surface polishing and film thickness reduction over time. The FRC reference has a minor initial loss of film thickness after which it stabilizes without showing any signs of continuous polishing. Notably, Coating 1, which comprises PEG in the backbone, polishes at a higher rate than Coating 2 without PEG.

Example 9: Antifouling testing

The coating compositions of Example 7 (Coating 1-3 and FRC reference) were applied using a film applicator with a 300 μιη clearance on PVC marine test panels. The panels had been pre-coated with one coat of Jotun Safeguard Universal ES primer and one coat of Jotun SeaLion tiecoat using airless spray within specified conditions. A panel coated with the 'ES primer only was used as a negative control.

Antifouling testing (1)

Test site: Sandefjord, Norway

Panels with dimensions of 20x40 cm were used for static testing on raft which were attached to frames and suspended vertically 0.5-1.5 m below the water surface. Fouling coverage was assessed according to four ecologically derived fouling categories: Slime (microfouling), Weed, Soft-bodied animal, and Hard-bodied animal. The panels were analysed by visual inspection for fouling coverage and coating integrity after eighteen weeks. The results are shown in the table below

Slime Weed Soft Hard Total

Coating

Sandefjord 18 weeks fouling fouling fouling fouling fouling

integrity

(%) (%) (%) (%) (%) FRC reference 40 0 10 0 50 Good

Coating 1 10 0 0 0 10 Good

Coating 2 15 0 5 0 20 Good

Coating 3 5 0 0 0 5 Good

Primer 60 0 25 10 95 Good

This table shows that after 18 weeks of static immersion the coatings of this invention (coating 1-3) show a fouling resistance which is better than the FRC reference. The results show a particular excellent fouling resistance for the acetal-siloxane coatings which contain PEG in the backbone and the coating which comprise biocide (Coating 1 and 3, respectively).

Antifouling testing (2)

Test site: Batelle, Florida (US)

Panels with dimensions of 7.5x17cm were used for dynamic rotor testing by attaching the coated panels to a rotary drum which was completely submerged and rotated at a rate of 7 knots (3.6m /s) through the water. Fouling coverage was assessed according to four ecologically derived fouling categories: Slime (micro fouling), Weed, Soft- bodied animal, and Hard-bodied animal. The panels were analysed by visual inspection for fouling coverage and coating integrity after 13 weeks. The results are shown in the table below;

This table shows that after 13 weeks of dynamic testing the coatings of this invention (coating 2-3) show a fouling resistance which is better than the FRC reference. The results show a particular excellent fouling resistance for the Acetal-siloxane coating which contains biocide (Coating 3).

Claims

Claims

A binder for a marine coating composition comprising the reaction product of at one polysiloxane of general formula (Α')

wherein each Ri is the same or different and represents an unsubstituted or substituted Ci_₂o alkyl, C₂_₂o alkenyl, C3-20 cycloalkyl, C₆-₂o aryl, C7-20 arylalkyl group, or a polyoxyalkylene chain;

X and Y can be the same or different and represent H, OH, (CR"₂)_X'-COR, (CR"₂)_x -OH, (CR"₂) _X NH₂, (CR"₂) _X NR₂, epoxy, halide, , _( CR"₂) _x OCH=CH₂, - (CR"₂)_X -C=CH₂, -C=CH₂ or -(CR"₂)_x -(OR^{1 1})_a-(OR^{1 1})_b-OH;

R" may independently be Ci_₆ alkyl or H, especially H;

x' is 1 to 10, such as 1 to 5, especially 2 to 5, especially 3 to 5;

R is H, Ci_₂₀ alkyl, C₂_₂₀ alkenyl, C₃_₂o cycloalkyl, C₆_₂o aryl, C₇_₂₀ arylalkyl group;

R^{1 1} are each independently C₂_₆ alkylene;

a= 0-50, b= 0-50 and a+b = 1-50; and

n is 1-500, more preferably 10-300, especially 15- 100;

or n' + m add to 1-500, more preferably 10-300, especially 15-100;

and (i) at least one second monomer B' of formula

W-Q-Z B' wherein W and Z are each independently OH, COR, (CR"₂)_x<-OH, (CR"₂) _X>NH₂, (CR"₂) _X NR₂, epoxy, halide, -OCH=CH₂, _( CR"₂) _x OCH=CH₂, -(CR"₂)_X>- C=CH₂ group, -C=CH₂ group or -(CR"₂)_x -(OR^{1 1})_a-(OR^{1 1})_b-OH;

Q is an aliphatic, cycloalkyl, cycloalkenyl, polyoxyalkylene, amine ether or aromatic group having up to 20 carbon atoms, and

R^{1 1} are each independently C₂_₆ alkylene;

a= 0-50, b= 0-50 and a+b = 1-50; or (ii)

a monomer B' of formula

Ri₅0-CH(R₁₆)-0-CH(R₁₆)-ORi₅ B2 where R₁₅ is H or Ci_₆ alkyl and Ri₆ is H, Ci_₆ alkyl or two Ri₆ groups taken together form a ring having 4 to 8 members; or (iii)

a monomer B' of formula

wherein W and Z are each independently OH, COH, CO-Ci_₆ alkyl, halide, - OCH=CH₂, (CH₂) _x OCH=CH₂ or a (CH₂) _X<C=CH₂, or -C=CH₂;

x' is 1 to 10, such as 1 to 5, especially 2 to 5, especially 3 to 5;

and Q_w is an Ci_₂o alkyl, C₂_₂o alkenyl, C₆-₂o aryl, C₇-₂o arylalkyl interrupted by one or more ester groups- O-CO or CO-O-.

with the proviso that the W and Z groups in monomer B' are selected to react with the X and Y groups in monomer A' to form a hydro lysable group such as an acetal.

A binder for a marine coating composition comprising the reaction product of at one polysiloxane of general formula (Α'):

wherein each Ri is the same or different and represents an unsubstituted or substituted Ci_₂o alkyl, C₂_₂o alkenyl, C3-20 cycloalkyl, C₆-₂o aryl, C7-20 arylalkyl group, or a polyoxyalkylene chain;

X and Y can be the same or different and represent H, OH, (CR"₂)_X'-COR, (CR"₂)_x -OH, (CR"₂) _X NH₂, (CR"₂) _X NR₂, epoxy, halide_, _( CR"₂) _x OCH=CH₂, - (CR"₂)_X -C=CH₂, -C=CH₂ or -(CR"₂)_x -(OR^{1 1})_a-(OR^{1 1})_b-OH;

R" may independently be Ci_₆ alkyl or H, especially H;

x' is 1 to 10, such as 1 to 5, especially 2 to 5, especially 3 to 5;

R is H, Ci_₂₀ alkyl, C₂_₂₀ alkenyl, C₃_₂o cycloalkyl, C₆_₂o aryl, C₇_₂₀ arylalkyl group;

R^{1 1} are each independently C₂_₆ alkylene;

a= 0-50, b= 0-50 and a+b = 1-50; and

n is 1-500, more preferably 10-300, especially 15-100;

or n' + m add to 1-500, more preferably 10-300, especially 15-100;

and at least one second monomer B' of formula

or

wherein each Ri is the same or different and represents an unsubstituted or substituted Ci_₂o alkyl, C₂_₂o alkenyl, C₃_₂o cycloalkyl, C₆-₂o aryl, C₇-₂o arylalkyl group, or a polyoxyalkylene chain;

X and Y can be the same or different and represent H, OH, (CR"₂)_X'-COR, (CR"₂)_x -OH, (CR"₂) _X NH₂, (CR"₂) _X NR₂, epoxy, halide, _, _(CR"₂) _x OCH=CH₂, - (CR"₂)_X -C=CH₂, -C=CH₂ or -(CR"₂)_x -(OR¹¹)_a-(OR¹¹)_b-OH;

R" may independently be Ci_₆ alkyl or H, especially H;

x' is 1 to 10, such as 1 to 5, especially 2 to 5, especially 3 to 5;

R is H, Ci_₂₀ alkyl, C₂_₂₀ alkenyl, C₃_₂₀ cycloalkyl, C₆_₂o aryl, C₇_₂₀ arylalkyl group;

R¹¹ are each independently C₂_₆ alkylene;

a= 0-50, b= 0-50 and a+b = 1-50; and

n is 1-500, more preferably 10-300, especially 15-100;

or n' + m add to 1-500, more preferably 10-300, especially 15-100;

with the proviso that the X and Y groups in monomer B' are selected to react with the X and Y groups in monomer A' to form a hydro lysable group.

A binder for a marine coating composition comprising the reaction product of at one polysiloxane of general formula (Α')

wherein each Ri is the same or different and represents an unsubstituted or substituted Ci_₂o alkyl, C₂_₂o alkenyl, C3-20 cycloalkyl, C₆-₂o aryl, C7-20 arylalkyl group, or a polyoxyalkylene chain;

X and Y can be the same or different and represent H, OH, (CR"₂)_X'COR, (CR"₂)_x -OH, (CR"₂) _X NH₂, (CR"₂) _X NR₂, epoxy, halide, _, _(CR"₂) _x OCH=CH₂, - (CR"₂)_X -C=CH₂ group, -C=CH₂ group or -(CR"₂)_x -(OR^{1 1})_a-(OR^{1 1})_b-OH;

R" may independently be Ci_₆ alkyl or H, especially H;

x' is 1 to 10, such as 1 to 5, especially 2 to 5, especially 3 to 5;

R is H, Ci_₂₀ alkyl, C₂_₂₀ alkenyl, C₃_₂o cycloalkyl, C₆_₂o aryl, C₇_₂₀ arylalkyl group;

R^{1 1} are each independently C₂_₆ alkylene;

a= 0-50, b= 0-50 and a+b = 1-50; and

n is 1-500, more preferably 10-300, especially 15-100;

or n' + m add to 1-500, more preferably 10-300, especially 15-100;

and (i) at least one second monomer B' that reacts with the X and Y groups in monomer A' to form a hydrolysable acetal group.

A binder as claimed in any preceding claim where A' is of formula

R' =Ph, -CH₂-Ph, -CH₂(CH₃)-Ph, C_1-6-alkyl

x' is 1 to 10, such as 1 to 5, especially 2 to 5, especially 3 to 5;

each Rio and Rn are independently C₂_₆ alkylene

a= 0-50, b= 0-50 and a+b = 1-50; and

n is 1-500, more preferably 10-300, especially 15- 100;

or n' + m add to 1-500, more preferably 10-300, especially 15-100.

5. A binder as claimed in any preceding claim where monomer A' is of formula

wherein each Ri is methyl, X and Y are the same and represent H, (CH₂)_x<-OH, (CR"₂)_x<-COH, (CH₂) >OCH=CH₂, -(CH₂) _X C=CH₂ group, or -C=CH₂ group;

x' is 1 to 10, especially 2 to 5, such as 3 to 5; and

n is 10-300, especially 15-100.

6. A binder as claimed in any preceding claim where monomer A' is of formula (A2):

wherein each Ri is methyl,

X and Y are the same and represent (CH₂)_X'-OH;

x' is 1 to 5, especially 2 to 5, such as 3 to 5; and

n is 10-300, especially 15-100.

7. A binder as claimed in any preceding claim where monomer A' is a polydimethylsilo xane .

8. A binder as claimed in claim 5 wherein X and/or Y in monomer A'are a carbinol, i.e. an (CH₂)x'OH chain.

9. A binder as claimed in any preceding claim wherein in the second monomer (Β') W and Z are OH, COH, -OCH=CH₂, (CH₂) _XOCH=CH₂ or (CH₂) _X<C=CH₂, or - C=CH₂.

10. A binder as claimed in any preceding claim wherein Q comprises a polyoxyalkylene of formula

-^-(OR^HOR^{1 1}),,- where R¹⁰ and R¹¹ are each independently C₂_₆ alkylene and a= 0-50, b= 0-50 and a+b = 1-50, preferably 1 to 10.

11. A binder as claimed in any preceding claim wherein the second monomer (Β') is diethylene vinyl ether terephthalate, diethylene vinyl ether phthalate, diethylene vinyl ether isophthalate, dipropylene vinyl ether phthalate, dipropylene vinyl ether terephthalate, dipropylene vinyl ether isophthalate, diethylene vinyl ether maleate, diethylene vinyl ether fumarate, and diethylene vinyl ether itaconate, bis [4- (vinyloxy)butyl] 1 ,6-hexanediylbiscarbamate, bis[4-(vinyloxy)butyl] isophtalate, bis[4- (vinyloxy)butyl] succinate, bis[4-(vinyloxy)butyl] terephthalate, bis[4-

(viny lo xymethy l)cy clo hexy lmethy 1] glutarate .

12. A binder as claimed in any preceding claim wherein the second monomer (Β') is a compound of formula

Ri₅0-CH(R₁₆)-0-CH(R₁₆)-ORi₅ where R₁₅ is H or Ci_₆ alkyl and Ri₆ is H, Ci_₆ alkyl or two Ri₆ groups taken together form a ring having 4 to 8 members, preferably when X and Y on monomer A' are an (CH₂)x'OH chain.

13. A binder as claimed in any preceding claim comprising a plurality of acetal groups in the polymer backbone.

14. A binder as claimed in any preceding claim wherein an acetal link is prepared from the reaction of a carbinol and a vinyl ether.

15. A binder as claimed in any preceding claim wherein the second monomer (Β') is ethylene glycol divinyl ether, triethylene glycol divinyl ether, 1,2-propanediol divinyl ether, 1,3-propanediol divinyl ether, 1,3-butanediol divinyl ether, 1,4-butanediol divinyl ether, tetramethylene glycol divinyl ether, neopentyl glycol divinyl ether, trimethylolpropane trivinyl ether, trimethylolethane trivinyl ether, hexanediol divinyl ether, 1,4-cyclo hexanediol divinyl ether, 1,4-divinyloxymethyl cyclohexane, tetraethylene glycol divinyl ether, pentaerythritol divinyl ether, pentaerythritol trivinyl ether, pentaerythritol tetravinyl ether, sorbitol tetravinyl ether, sorbitol pentavinyl ether, ethylene glycol diethylene vinyl ether, triethylene glycol diethylene vinyl ether, ethylene glycol dipropylene vinyl ether, triethylene glycol diethylene vinyl ether, trimethylolpropane triethylene vinyl ether, trimethylolpropane diethylene vinyl ether, pentaerythritol diethylene vinyl ether, pentaerythritol triethylene vinyl ether, pentaerythritol tetraethylene vinyl ether, adipic acid divinyl ester, 1,4- cyclohexanedimethanol divinyl ether, divinyloxy 1,4-cyclohexanedimethanol and PEG- divinyl ether.

16. A binder as claimed in any preceding claim wherein W and Z are CH₂=CH-0- and Q is an C3-10 alkylene chain or a polyoxyalkylene -R¹⁰-(ORⁿ)_a- where R¹⁰ and R¹¹ are each independently C₂_₆ alkylene and a= 1-5.

17. A binder as claimed in any preceding claim wherein the second monomer (Β') is a compound of formula

Ri₅0-CH(R₁₆)-0-CH(R₁₆)-ORi₅ where R₁₅ is Ci_₆ alkyl and two Ri₆ groups taken together form a ring having 4 to 8 members, preferably when X and Y on monomer A' are an (CH₂)x'OH chain .

18. A binder as claimed in any preceding claim wherein the second monomer (Β') is a compound of formula

W-Q_w-Z B5 wherein W and Z are -OCH=CH₂;

and Q_w is an Cl-10-alkylene or a polyoxyalkylene of formula -R¹⁰-(ORⁿ)_a- where R¹⁰ and R¹¹ are each independently C₂_alkylene and a= 1-10.

19. A fouling release coating composition comprising a binder as claimed in any one of claims 1 to 18, and at least one of filler, pigment, solvent, additive, curing agent and catalyst, preferably in the absence of an anti-fouling agent.

20. An anti-fouling coating composition comprising a binder as claimed in any one of claims 1 to 18 and at least one anti-fouling agent.

21. A process for protecting an object from fouling comprising coating at least a part of said object which is subject to fouling with a coating composition as claimed in any one of claims 1 to 18 and preferably curing the composition.

22. An object coated with a cured coating composition as claimed in any one of claims 1 to 18.

23. A process for the preparation of a binder for a marine coating composition comprising copolymerising a polysiloxane unit A' and at least one second monomer B' as defined in any one of claims 1 to 18 so as to form a copolymer -[ABAB]- in which hydro lysable functional groups are present in the backbone of the copolymer.

24. Use of a binder as claimed in any one of claims 1 to 18 for use in a fouling release composition or a marine anti-fouling coating composition.