WO2016077109A2 - Flexographic printing plate with improved cure efficiency - Google Patents
Flexographic printing plate with improved cure efficiency Download PDFInfo
- Publication number
- WO2016077109A2 WO2016077109A2 PCT/US2015/058917 US2015058917W WO2016077109A2 WO 2016077109 A2 WO2016077109 A2 WO 2016077109A2 US 2015058917 W US2015058917 W US 2015058917W WO 2016077109 A2 WO2016077109 A2 WO 2016077109A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- photoinitiator
- photocurable
- wavelength
- layer
- photocurable composition
- Prior art date
Abstract
Description
Claims