WO2016074116A1 - Method for manufacturing interior material of fireproof door using fire retardant coating paint and process for manufacturing fireproof door using the interior material - Google Patents
Method for manufacturing interior material of fireproof door using fire retardant coating paint and process for manufacturing fireproof door using the interior material Download PDFInfo
- Publication number
- WO2016074116A1 WO2016074116A1 PCT/CN2014/090663 CN2014090663W WO2016074116A1 WO 2016074116 A1 WO2016074116 A1 WO 2016074116A1 CN 2014090663 W CN2014090663 W CN 2014090663W WO 2016074116 A1 WO2016074116 A1 WO 2016074116A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- board
- boards
- fire
- plate
- fireproof door
- Prior art date
Abstract
A method for manufacturing an interior material of a fireproof door using a fire retardant coating paint and a method for manufacturing a fireproof door using the interior material. A fireproof aging coating paint or a flame retardant grade coating paint is applied to boards, such as calcium silicate boards, magnesium oxide boards, calcium oxide boards, ceramic wool boards, pearlite boards, asbestos boards, PU foam wool boards, fiberglass wool boards, glass foam wool boards, ceramic foam wool boards, perlite foam wool boards, solid boards, sandwich boards, duramen boards, dense boards, particle boards, stainless steel boards, steel boards, aluminium boards, copper boards, lead boards, titanium boards, zinc boards, carbon boards and so on. The fireproof aging coating paint or the flame retardant grade coating paint is brush coated and spray coated on the surface layer of the board, thus an interior material of a fireproof door which has a low weight, high effective fire retardancy and high temperature resistance is formed, depending on the coating thickness and the board thickness.
Description
本发明涉及一种防火门之制造及安装方法，尤指一种利用防火时效涂料漆或耐燃等级涂料漆刷涂及喷涂在板材表面层后，依涂层厚度于板材厚度，形成轻量化、且具高效能防火阻燃、耐高温相关作用之利用防火阻燃涂料漆制作防火门内部材料及安装方法。The invention relates to a method for manufacturing and installing a fireproof door, in particular to a method for painting and coating a surface layer of a board with a fireproof aging paint or a flame retardant paint, and forming a lightweight according to the thickness of the plate. The fireproof door interior material and installation method are made of fire retardant paint with high efficiency, fire retardant and high temperature resistance.
市售防火门材料里，常见者不外乎为硅酸钙板、氧化镁板、氧化钙板、陶瓷棉板、真珠岩板、石棉板、PU发泡棉板、玻璃纤维棉板、玻璃发泡棉板，应用于防火门内部隔层板，作为防火阻燃隔热材料之用，其有一些长久存在之缺失，例如：In the commercially available fire door materials, the common ones are nothing but calcium silicate board, magnesium oxide board, calcium oxide board, ceramic wool board, pearlite board, asbestos board, PU foam board, glass fiber board, glass hair. Foam board, used in the inner partition of fire door, as a fire retardant insulation material, it has some long-standing defects, such as:
1.石膏、硅酸钙、氧化镁、氧化钙经氧化作用易有粉尘掉落及酸化，若经吸入，长久下来对人体肺部及眼睛相对有害，其阻火性方面佳但不具隔热，且结构笨重强度不足易破碎。1. Gypsum, calcium silicate, magnesium oxide and calcium oxide are easy to be dusted and acidified by oxidation. If inhaled, it will be harmful to human lungs and eyes for a long time, and its fire resistance is good but not insulated. And the structure is cumbersome and not strong enough to be broken.
2.陶瓷棉板、真珠岩板、石棉板、PU发泡棉板、玻璃纤维棉板、玻璃发泡棉板阻火性差隔热性佳，强度不足易破碎，且易因环境相对湿度而形成水斑甚至浸烂损坏、产生重量增加。2. Ceramic cotton board, pearlite board, asbestos board, PU foamed cotton board, glass fiber cotton board, glass foamed cotton board, poor fire resistance, good heat insulation, insufficient strength, easy to break, and easy to form due to environmental relative humidity Water spots are even damaged by infiltration and increase in weight.
3.实木板、夹心板、木心板、密集板、塑合板无阻火性不具隔热、强度佳，易因环境相对湿度而形成水斑，甚至浸烂损坏、且产生重量增加。3. Solid wood board, sandwich board, wooden core board, dense board, and plywood have no fire resistance, good heat insulation, easy to form water spots due to relative humidity of the environment, and even impregnation damage, and increase weight.
除此之外，其它材料中，如不锈钢板、钢板、铝、铜、铅、钛、锌、碳板等金属材料，为实际构成防火门隔层之材料，上述材料虽有防火但隔热不佳，
且结构笨重不适用于防火门内部材料中，因此如何提供一种质轻又兼顾环保，且具防火阻燃、隔热、强度高等特点之材料，实为相关者所要探讨的课题。In addition, other materials, such as stainless steel plate, steel plate, aluminum, copper, lead, titanium, zinc, carbon plate and other metal materials, are the materials that actually constitute the fire door compartment. Although the above materials are fireproof but not insulated. Good,
The structure is cumbersome and unsuitable for use in the interior material of the fire door. Therefore, how to provide a material that is light in weight and environmentally friendly, and has the characteristics of fire retardant, heat insulation and high strength is a subject to be discussed.
由此可见，上述习用市售防火门材料仍有诸多缺失，实非一良善之设计，而亟待加以改良。It can be seen that there are still many shortcomings in the above-mentioned commercially available fire door materials, which is not a good design and needs to be improved.
本案发明人鉴于上述习用市售防火门材料所衍生的各项缺点，乃亟思加以改良创新，并经苦心孤诣潜心研究后，终于成功研发完成本件利用防火阻燃涂料漆制作防火门内部材料及安装方法。In view of the shortcomings derived from the above-mentioned commercially available fire door materials, the inventor of the present invention has improved and innovated, and after painstaking research, finally successfully developed and completed the fireproof door interior material and installation using the fire retardant paint. method.
发明内容Summary of the invention
本发明之主要目的系在于提供一种防火阻燃性佳且耐高温的利用防火阻燃涂料漆制作防火门内部材料及安装方法。The main object of the present invention is to provide a fireproof door interior material and a mounting method using a fire retardant paint with good fire retardant and high temperature resistance.
本发明之次要目的系在于提供一种有效增加防火门强度并减少防火门重量的利用防火阻燃涂料漆制作防火门内部材料及安装方法。A secondary object of the present invention is to provide a fire door interior material and a mounting method using the fire retardant paint to effectively increase the strength of the fire door and reduce the weight of the fire door.
为达上述目的，本发明利用防火阻燃涂料漆制作防火门内部材料及安装方法，主要系利用不锈钢金属板、不锈钢金属板条及不锈钢金属C型钢条分别加工制作防火门板、防火门内框及防火门内支架，然后以玻璃纤维棉及蜂巢纸制作防火门内空间隔层，再以硅酸钙板、氧化镁板、氧化钙板、陶瓷棉板、真珠岩板、石棉板、PU发泡棉板、玻璃纤维棉板、玻璃发泡棉板、陶瓷发泡棉板、真珠岩发泡棉板、实木板、夹心板、木心板、密集板、塑合板、不锈钢板、钢板、铝、铜、铅、钛、锌、碳板等板材加工制作防火门内支撑板材，经防火时效涂料漆或耐燃等级涂料漆，刷涂或喷涂于上述防火门内部支撑任何一种板材上、再将防火门板、防火门内框、防火门内支架、防火门内空间隔层及板材组合安装，并以防火阻燃发泡棉条、防火阻燃板条于组合安装过程中做接缝间细的填缝补强工作，以完成防火门的制造及安装工作。
In order to achieve the above object, the invention utilizes fireproof and flame retardant paint to make the inner material and installation method of the fire door, and mainly uses the stainless steel metal plate, the stainless steel metal strip and the stainless steel metal C-shaped steel strip to respectively process the fire door panel and the fire door inner frame and The fire door inner bracket, then the glass fiber cotton and honeycomb paper are used to make the inner space partition layer of the fire door, and then the calcium silicate board, the magnesium oxide board, the calcium oxide board, the ceramic cotton board, the bead rock board, the asbestos board, the PU foam Cotton board, glass fiber cotton board, glass foamed cotton board, ceramic foamed cotton board, Zhenzhuyan foamed cotton board, solid wood board, sandwich board, wooden core board, dense board, plywood, stainless steel board, steel plate, aluminum, Copper, lead, titanium, zinc, carbon plate and other plates are processed to produce fireproof door support plates, which are fire-resistant paint or fire-resistant paint, brushed or sprayed on the inside of the fire door to support any kind of plate, and then fireproof Door panel, fire door inner frame, fire door inner bracket, fire door inner space partition layer and plate combination installation, and fireproof flame-retardant foamed cotton sliver, fire-retardant slats in the combined installation process Sutural fine caulking reinforcement work to complete the manufacture and installation of fire doors.
图1为本发明利用防火阻燃涂料漆制作防火门内部材料及安装方法流程图；1 is a flow chart of a method for manufacturing a fire door interior material and a mounting method using the fire retardant paint of the present invention;
图2为本发明用防火阻燃涂料漆制作防火门内部材料及安装方法之实施例示意图；2 is a schematic view showing an embodiment of a fire door interior material and a mounting method using the fire retardant paint of the present invention;
图3为本发明用防火阻燃涂料漆制作防火门内部材料及安装方法之另一实施例示意图；3 is a schematic view showing another embodiment of a fire door interior material and a mounting method using the fire retardant paint of the present invention;
图4为本发明用防火阻燃涂料漆制作防火门内部材料及安装方法之又一实施例示意图；4 is a schematic view showing still another embodiment of a fire door interior material and a mounting method using the fire retardant paint of the present invention;
图5为本发明用防火阻燃涂料漆制作防火门内部材料及安装方法之再一实施例示意图。FIG. 5 is a schematic view showing still another embodiment of a fire door interior material and a mounting method using the fire retardant paint of the present invention.
附图标记说明：Description of the reference signs:
S01-S09步骤流程S01-S09 step process
1 不锈钢金属板加工制作防火门板1 stainless steel metal plate processing to make fire door panels
2 玻璃纤维棉及蜂巢纸加工制作防火门内空间隔层2 Glass fiber cotton and honeycomb paper processing to make the air gap inside the fire door
3 漆涂刷层3 paint layer
41 硅酸钙板、氧化镁板或氧化钙板41 calcium silicate board, magnesium oxide board or calcium oxide board
42 PU发泡棉板、玻璃纤维棉板、玻璃发泡棉板、陶瓷发泡棉板或真珠岩发泡棉板42 PU foamed cotton board, glass fiber cotton board, glass foamed cotton board, ceramic foamed cotton board or Zhenzhuyan foamed cotton board
43 实木板、夹心板、木心板、密集板或塑合板43 solid wood panels, sandwich panels, wooden core panels, dense panels or plywood
44 不锈钢板、钢板或铝、铜、铅、钛、锌、碳等元素所制成之合金金属板44 stainless steel plate, steel plate or alloy metal plate made of aluminum, copper, lead, titanium, zinc, carbon and other elements
请参阅图1所示，本发明利用防火阻燃涂料漆制作防火门内部材料及安装方法，其主要流程步骤包括：Referring to FIG. 1 , the present invention utilizes a fire retardant paint to make a fire door interior material and a mounting method thereof. The main process steps include:
S01、选用厚度在1.0-1.2mm间之不锈钢金属板加工制作防火门板1；S01, selecting a stainless steel metal plate with a thickness of 1.0-1.2 mm to manufacture a fire door panel 1;
S02、选用厚度在2.0-5.0mm间之不锈钢金属板条加工制作防火门内框(图中未示)；S02, using a stainless steel metal strip with a thickness of 2.0-5.0 mm to process the inner frame of the fire door (not shown);
S03、利用不锈钢金属C型钢条加工制作防火门内支架(图中未示)；S03, using a stainless steel metal C-shaped steel bar to manufacture a fire door bracket (not shown);
S04、以玻璃纤维棉及蜂巢纸加工制作防火门内空间隔层2，防火门内空间隔层2之厚度为25mm以下；S04, processing the inner space partition layer 2 of the fireproof door by using glass fiber cotton and honeycomb paper, and the thickness of the inner space partition layer 2 of the fireproof door is 25 mm or less;
S05、漆涂刷层3刷涂或喷涂于板材上，漆涂刷层3系为防火时效涂料漆(防火时效1、2、3小时以上)或耐燃等级涂料漆(耐燃三级、二级、一级以上)；S05, the paint brush layer 3 is brushed or sprayed on the board, and the paint brush layer 3 is a fireproof aging paint (fireproof aging for 1, 2, 3 hours or more) or a flame resistant grade paint (flame-resistant third, second, Level 1 or above);
S06、将板材加工制作防火门内支撑板材；S06, processing the plate to make a support plate in the fire door;
S07、利用防火门板1、防火门内框、防火门内支架，防火门内空间隔层2及防火门内支撑板材进行防火门之组合安装；S07, using fire door panel 1, fire door inner frame, fire door inner bracket, fire door inner space compartment 2 and fire door inner support plate for fireproof door combination installation;
S08、以防火阻燃发泡棉条、防火阻燃板条于组合安装过程中做接缝间细的填缝补强工作；S08, with fire-retardant foamed slivers and fire-retardant slats in the combined installation process to make a fine joint filling work between the joints;
S09、完成防火门的制作及安装。S09, complete the production and installation of fire doors.
在本发明中，防火门内支撑板材及漆涂刷层至少包括下列各实施例之态样：In the present invention, the inner support plate and the paint brush layer in the fire door include at least the following embodiments:
请参阅图2所示，在本发明之第一实施例中，防火门内支撑板材系可为硅酸钙板、氧化镁板或氧化钙板41，其板材厚度3mm以下，漆涂刷层3须双面涂装，各漆涂刷层3之厚度0.8-1.0mm之间。Referring to FIG. 2, in the first embodiment of the present invention, the support plate in the fire door may be a calcium silicate board, a magnesium oxide board or a calcium oxide board 41, and the thickness of the board is less than 3 mm, and the paint layer is 3 It must be coated on both sides, and the thickness of each paint coating layer 3 is between 0.8 and 1.0 mm.
请参阅图3所示，在本发明之第二实施例中，防火门内支撑板材系可为PU发泡棉板、玻璃纤维棉板、玻璃发泡棉板、陶瓷发泡棉板或真珠岩发泡棉板42，
其板材厚度30mm以下，漆涂刷层3须双面涂装，各漆涂刷层3之厚度0.8-1.0mm之间。Referring to FIG. 3, in the second embodiment of the present invention, the support plate in the fire door can be PU foamed cotton board, glass fiber cotton board, glass foamed cotton board, ceramic foamed cotton board or pearlite. Foamed cotton board 42,
The thickness of the sheet is 30 mm or less, and the paint layer 3 is coated on both sides, and the thickness of each paint layer 3 is between 0.8 and 1.0 mm.
请参阅图4所示，在本发明之第三实施例中，防火门内支撑板材系可为实木板、夹心板、木心板、密集板或塑合板43，其板材厚度:3mm以下，漆涂刷层3须双面涂装，各漆涂刷层3之厚度0.8-1.0mm之间。Referring to FIG. 4, in the third embodiment of the present invention, the support plate in the fire door may be a solid wood board, a sandwich board, a wooden core board, a dense board or a plywood 43, and the thickness of the board is less than 3 mm, and the paint is The coating layer 3 must be coated on both sides, and the thickness of each of the lacquer coating layers 3 is between 0.8 and 1.0 mm.
请参阅图5所示，在本发明之第四实施例中，防火门内支撑板材系可为不锈钢板、钢板或铝、铜、铅、钛、锌、碳等元素所制成之合金金属板44，其板材厚度0.2mm以下，漆涂刷层3须双面涂装，各漆涂刷层层3之厚度0.8-1.0mm之间。Referring to FIG. 5, in the fourth embodiment of the present invention, the support plate in the fire door may be a stainless steel plate, a steel plate or an alloy metal plate made of elements such as aluminum, copper, lead, titanium, zinc, carbon, and the like. 44, the thickness of the plate is less than 0.2mm, the paint layer 3 must be coated on both sides, and the thickness of each paint layer 3 is between 0.8 and 1.0 mm.
本发明利用防火阻燃涂料漆制作之防火门内部材料及安装方法，利用防火时效涂料漆或耐燃等级涂料漆应用于硅酸钙板、氧化镁板、氧化钙板、陶瓷棉板、真珠岩板、石棉板、PU发泡棉板、玻璃纤维棉板、玻璃发泡棉板、陶瓷发泡棉板、真珠岩发泡棉板、实木板、夹心板、木心板、密集板、塑合板、不锈钢板、钢板、铝、铜、铅、钛、锌、碳板等板材，经防火时效涂料漆或耐燃等级涂料漆刷涂及喷涂在上述板材表面层后，依涂层厚度及板材厚度等，进而形成一轻量化、且具高效能防火阻燃、耐高温相关作用之防火门内部材料等，且经由本发明之实施，可帮助改善现有防火门结构笨重问题，并可提高拉长防火阻燃时效性、改善隔热降低温度及降低重量的途径。The invention discloses a fire door internal material and a mounting method made by using a fire retardant paint, and uses a fireproof aging paint or a flame resistant grade paint to be applied to a calcium silicate board, a magnesium oxide board, a calcium oxide board, a ceramic cotton board, a pearlite board. , asbestos board, PU foamed cotton board, glass fiber cotton board, glass foamed cotton board, ceramic foamed cotton board, real pearl rock foamed cotton board, solid wood board, sandwich board, wooden core board, dense board, plywood, Stainless steel plates, steel plates, aluminum, copper, lead, titanium, zinc, carbon plates, etc., after being painted and sprayed on the surface layer of the above-mentioned plates by fire-resistant paint or fire-resistant paint, depending on the thickness of the coating and the thickness of the plate, etc. Further, a light-weight, interior material of a fireproof door having high-efficiency fire-retardant and high-temperature-resistant effects is formed, and the implementation of the present invention can help improve the cumbersome problem of the existing fire door structure and improve the elongated fire resistance. Time-dependent, improved insulation, reduced temperature and reduced weight.
综上所述，上列详细说明系针对本发明之一可行实施例之具体说明，惟该实施例并非用以限制本发明之专利范围，凡未脱离本发明技艺精神所为之等效实施或变更，均应包含于本案之专利范围中。本案不但在空间型态上确属创新，并能较习用物品增进上述多项功效，应已充分符合新颖性及进步性之法定发明专利要件，爰依法提出申请，恳请贵局核准本件发明专利申请案，以励发明，至感德便。
The detailed description above is a detailed description of a possible embodiment of the present invention, and is not intended to limit the scope of the invention, and the equivalent of Changes should be included in the scope of the patent in this case. This case is not only innovative in terms of space type, but also can enhance the above-mentioned multiple functions compared with the conventional articles. It should fully comply with the statutory invention patent requirements of novelty and progressiveness, and apply for it according to law. You are requested to approve the patent application for this invention. The case, in order to invent, to the sense of virtue.
Claims (11)
- 利用防火阻燃涂料漆制作防火门内部材料及安装方法，其特征在于，包括：The fireproof door interior material and the installation method using the fire retardant paint are characterized in that:a.利用不锈钢金属板加工制作防火门板；a. Using stainless steel metal plate processing to make fire door panels;b.利用不锈钢金属板条制作防火门内框；b. making a fire door inner frame by using stainless steel metal strips;c.利用不锈钢金属C型钢条制成防火门内支架；c. using a stainless steel metal C-shaped steel bar to make a fire door bracket;d.以玻璃纤维棉及蜂巢纸加工制作防火门内空间隔层；d. Fabricating the inner space partition of the fire door with glass fiber cotton and honeycomb paper;e.利用防火时效涂料漆或耐燃等级涂料漆刷涂或喷涂于板材上；e. Brush or spray on the board with a fire-resistant paint or a flame-resistant paint;f.将板材加工制作防火门内支撑板材；f. processing the sheet into a fireproof door support sheet;g.利用防火门板、防火门内框、防火门内支架，防火门内空间隔层及防火门内支撑板材进行防火门之组合安装；g. Using fire door panels, fire door inner frame, fire door inner bracket, fire door inner space partition and fire door inner support plate for fireproof door combination installation;h.防火门组合安装过程中防火阻燃发泡棉条、防火阻燃板条进行接缝间细补强。h. Fireproof flame-retardant foamed slivers and fire-retardant slats during the installation of fire door combination to make fine joint reinforcement.
- 如权利要求1所述之利用防火阻燃涂料漆制作防火门内部材料及安装方法，其特征在于，所述板材为硅酸钙板、氧化镁板、氧化钙板、陶瓷棉板、真珠岩板、石棉板、PU发泡棉板、玻璃纤维棉板、玻璃发泡棉板、陶瓷发泡棉板、真珠岩发泡板、实木板、夹心板、木心板、密集板、塑合板、不锈钢板、钢板、铝板、铜板、铅板、钛板、锌板或碳板。The fireproof door internal material and the installation method using the fire retardant paint according to claim 1, wherein the plate is a calcium silicate board, a magnesium oxide board, a calcium oxide board, a ceramic cotton board, and a pearlite board. , asbestos board, PU foamed cotton board, glass fiber cotton board, glass foamed cotton board, ceramic foamed cotton board, real pearl rock foam board, solid wood board, sandwich board, wooden core board, dense board, plywood, stainless steel Plate, steel plate, aluminum plate, copper plate, lead plate, titanium plate, zinc plate or carbon plate.
- 如权利要求2所述之利用防火阻燃涂料漆制作防火门内部材料及安装方法，其特征在于，所述硅酸钙板、氧化镁板、氧化钙板、陶瓷棉板、真珠岩板、石棉板之厚度小于9mm。 The fireproof door inner material and the installation method using the fire retardant paint according to claim 2, wherein the calcium silicate board, the magnesium oxide board, the calcium oxide board, the ceramic cotton board, the bead rock board, the asbestos The thickness of the board is less than 9mm.
- 如权利要求2所述之利用防火阻燃涂料漆制作防火门内部材料及安装方法，其特征在于，所述PU发泡棉板、玻璃纤维棉板、玻璃发泡棉板、陶瓷发泡棉板、真珠岩发泡板之厚度小于50mm。The fireproof door internal material and the installation method using the fire retardant paint according to claim 2, wherein the PU foamed cotton board, the glass fiber cotton board, the glass foamed cotton board, the ceramic foamed cotton board The thickness of the Zhenzhuyan foam board is less than 50mm.
- 如权利要求2所述之利用防火阻燃涂料漆制作防火门内部材料及安装方法，其中实木板、夹心板、木心板、密集板、塑合板之厚度小于9mm。The fireproof door internal material and the installation method using the fire retardant paint according to claim 2, wherein the thickness of the solid wood board, the sandwich board, the wooden core board, the dense board and the plastic board is less than 9 mm.
- 如权利要求2所述之利用防火阻燃涂料漆制作防火门内部材料及安装方法，其特征在于，所述不锈钢板、钢板、铝板、铜板、铅板、钛板、锌板或碳板之厚度小于1mm。The fireproof door internal material and the mounting method using the fire retardant paint according to claim 2, wherein the thickness of the stainless steel plate, the steel plate, the aluminum plate, the copper plate, the lead plate, the titanium plate, the zinc plate or the carbon plate Less than 1mm.
- 如权利要求1所述之利用防火阻燃涂料漆制作防火门内部材料及安装方法，其特征在于，所述防火时效涂料漆之防火时效为1小时或高于1小时。The fireproof door interior material and the method for installing the fireproof door paint according to claim 1, wherein the fireproofing paint has a fireproofing effect of 1 hour or more.
- 如权利要求1所述之利用防火阻燃涂料漆制作防火门内部材料及安装方法，其特征在于，所述耐燃等级涂料漆为耐燃三级或三级以上。The fireproof door interior material and the mounting method using the fire retardant paint according to claim 1, wherein the flameproof grade paint is three or more flame resistant.
- 如权利要求1所述之利用防火阻燃涂料漆制作防火门内部材料及安装方法，其特征在于，所述该防火时效涂料漆或耐燃等级涂料漆之刷涂或喷涂厚度小于3mm。The fireproof door interior material and the installation method using the fire retardant paint according to claim 1, wherein the fireproof paint or the flameproof paint is sprayed or sprayed to a thickness of less than 3 mm.
- 如权利要求1所述之利用防火阻燃涂料漆制作防火门内部材料及安装方法，其特征在于，所述该不锈钢金属板厚度为1.0-1.2mm。The fireproof door inner material and the mounting method using the fire retardant paint according to claim 1, wherein the stainless steel metal plate has a thickness of 1.0 to 1.2 mm.
- 如权利要求1所述之利用防火阻燃涂料漆制作防火门内部材料及安装方法，其特征在于，所述该不锈钢金属板条厚度为2.0-5.0mm。 The fireproof door inner material and the mounting method using the fire retardant paint according to claim 1, wherein the stainless steel metal strip has a thickness of 2.0-5.0 mm.