WO2015067533A1 - Process for modifying ethylene-based polymers and copolymers - Google Patents

Process for modifying ethylene-based polymers and copolymers Download PDF

Info

Publication number
WO2015067533A1
WO2015067533A1 PCT/EP2014/073418 EP2014073418W WO2015067533A1 WO 2015067533 A1 WO2015067533 A1 WO 2015067533A1 EP 2014073418 W EP2014073418 W EP 2014073418W WO 2015067533 A1 WO2015067533 A1 WO 2015067533A1
Authority
WO
WIPO (PCT)
Prior art keywords
polymer
ethylene
peroxide
process according
azide
Prior art date
Application number
PCT/EP2014/073418
Other languages
French (fr)
Inventor
Waldo Joseph Elisabeth BEEK
Auke Gerardus Talma
Original Assignee
Akzo Nobel Chemicals International B.V.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Akzo Nobel Chemicals International B.V. filed Critical Akzo Nobel Chemicals International B.V.
Priority to CN201480058504.7A priority Critical patent/CN105705563B/en
Priority to MX2016005599A priority patent/MX2016005599A/en
Priority to US15/034,720 priority patent/US9688783B2/en
Priority to RU2016121181A priority patent/RU2671352C2/en
Priority to KR1020167014339A priority patent/KR20160084842A/en
Priority to JP2016527298A priority patent/JP6306176B2/en
Priority to CA2928332A priority patent/CA2928332A1/en
Priority to EP14792803.0A priority patent/EP3066151A1/en
Publication of WO2015067533A1 publication Critical patent/WO2015067533A1/en
Priority to ZA2016/02832A priority patent/ZA201602832B/en
Priority to SA516371025A priority patent/SA516371025B1/en

Abstract

Process for functionalising an ethylene-based (co)polymer comprising the step of contacting an ethylene-based (co)polymer at a temperature in the range 100- 250°C with an azide of formula (I) wherein Y is either (Ia) or (Ib) m is 0 or 1, n is 0 or 1, n+m=1 or 2, and X is a linear or branched, aliphatic or aromatic hydrocarbon moiety with 1 -12 carbon atoms, optionally containing heteroatoms.

Description

PROCESS FOR MODIFYING ETHYLENE-BASED POLYMERS AND COPOLYMERS
The present invention relates to processes for functionalising and modifying ethylene-based (co)polymers, functionalised and modified ethylene-based (co)polymers obtainable by these processes, and their use of the production of power cables.
Typical cable and cable-in-wire applications comprise at least one conductor surrounded by one or more layers of polymeric material.
In some power cables, including medium voltage (MV), high voltage (HV) and extra high voltage (EHV) cables, the conductor is surrounded by several layers, including an inner semiconductive layer, an insulation layer and an outer semiconductive layer. The outer semiconductive layer of the power cable can be non-strippable (i.e. bonded and non-peelable) or strippable (i.e. non-bonded and peelable). The conductor can be surrounded by an inner semiconductive layer which generally comprises crosslinked ethylene-based copolymer filled with conductive carbon black. The insulation layer is generally made of low density polyethylene (LDPE) that is crosslinked to give it desirable long term properties. The outer semiconductive layer is again a crosslinked semiconductive ethylene-based copolymer layer and this is often reinforced by metal wiring or covered by a sheet (metallic screening material).
Power cables are commonly produced by extruding the layers on a conductor. One or more of said polyethylene or ethylene-based copolymer layers are then crosslinked to improve its/their deformation resistance at elevated temperatures, mechanical strength and/or chemical resistance. A free radical initiator, such as a peroxide, is typically incorporated in the layer material prior to or during extrusion of the iayer(s). After extrusion and formation of the cable, the cable is subjected to a crosslinking step, initiated by the free radical initiator.
In the conventional way of free radical ethylene-based ( copolymer crosslinking, residual volatiles stemming from peroxide decomposition products, such as methane, remain in the cable as voids or are released as highly flammable gaseous substances. An object of the present invention is to provide a process for crosslinking polyethylene which allows the use of lower amounts of peroxide, resulting in lower amounts of volatiles, with still good crosslinking performance.
It has now been found that if an ethylene-based ( copolymer is first functionalized with a citraconimide-type azide, the free radical crosslinking occurs faster and more efficient, meaning that it requires lower amounts of peroxide.
Furthermore, it has been found that the said functionalisation with a citraconimide- type azide can affect the polarity of the (co)polymer, resulting in, for instance, a better compatibility with paint layers.
In addition, said functionalisation can be used to increase the number of long chain branches, thereby changing the rheology of the ( copolymer, resulting in an enhanced melt strength.
The present invention therefore relates to a process for preparing a functionalised ethylene-based (co)polymer comprising the step of contacting an ethylene-based (co)polymer at a temperature in the range 100-250°C with an azide of formula (I)
Figure imgf000004_0001
wherein s e t er 0
Figure imgf000004_0002
m is 0 or 1 , n is 0 or 1 , n+m=1 or 2, and X is a linear or branched, aliphatic or aromatic hydrocarbon moiety with 1 -12 carbon atoms, optionally containing heteroatoms. The invention also relates to a process for modifying an ethylene-based (co)polymer comprising the steps of:
preparing a functionalised ethylene-based (co)polymer according to the process described above,
contacting the functionalised ethylene-based (co)polymer with an organic peroxide to form a polymer/peroxide mixture, and
heating said polymer/peroxide mixture at a temperature in the range 140- 300°C.
This process results in a modification of the rheology of the (co)polymer. Depending on the exact conditions, the result is either a crosslinked (co)polymer or a (co)polymer with increased melt strength. Crosslinking will be achieved by high peroxide levels and increased melt strength will be achieved at low peroxide levels. The precise levels depend on the type of (co)polymer, the type of peroxide, and the level of functionalisation of the (co)polymer
The term ethylene-based (co)polymer includes both ethylene homopolymers and copolymers based on ethylene and one or more additional monomers.
Examples of ethylene-based copolymers are ethylene-propylene based copolymers (EPM), ethylene-propylene-diene terpolymer (EPDM), ethylene vinylacetate (EVA, ethylene butyl acrylate (EBA), ethylene ethyl acrylate (EEA), and polyolefin elastomers (POE); the latter being copolymers of ethylene with octene or butene.
Ethylene homopolymers, i.e. polyethylenes, are generally classified according to their density. High density polyethylene (HDPE) is defined by a density of greater that or equal to 0.941 g/cm3; medium density polyethylene (MDPE) is defined by a density range of 0.926-0.940 g/cm3; low linear density polyethylene (LLDPE) is defined by a density range of 0.915-0.925 g/cm3; low density polyethylene (LDPE) is defined by a density range of 0.910-0.940 g/cm3; very low density polyethylene (VLDPE) is defined by a density range of 0.880-0.915 g/cm3.
All these ethylene homopolymers can be used in the process of the present invention. LDPE is, however, the most preferred type to be used. LDPE is the preferred ethylene-based (co)polymer because of its flexibility and good mechanical strength.
The azide to be used in the process of the present invention has the formula:
Figure imgf000006_0001
wherein Y is either
Figure imgf000006_0002
m is 0 or 1 , n is 0 or 1 , n+m=1 or 2, preferably 1 , and
X is a linear or branched, aliphatic or aromatic hydrocarbon moiety with 1 -12 carbon atoms, optionally containing heteroatoms. The citraconazide of formula (I) can be used in pure form, but also in admixture with the corresponding itaconazide.
When X contains heteroatoms, it preferably has one of the following structures:
Figure imgf000006_0003
wherein Z, Q and P are integers ranging from 1 to 6 and R is selected from the group consisting of H, alkyl, aryl, phenyl, and substituted phenyl groups.
More preferably, however, X is an aliphatic alkanediyl group with 1 -12, more preferably 1 -6, and most preferably 2-4 carbon atoms.
The most preferred azide for use in the process according to the present invention is
Figure imgf000007_0001
i.e. 4-(3-methyl-2,5-dioxo-2,5-dihydro-1 H-pyrrol-1 -yl)benzenesulfonyl azide (also called citraconimide benzenesulfonylazide) and 2-(3-methyl-2,5-dioxo-2,5-dihydro- 1 H-pyrrol-1 -yl)ethyl carbonazidate (also called citraconimide-C2-azidoformate), respectively.
There are several mechanisms of reacting an azide with a polymer, depending on the type of azide and the type of polymer. Azides generally decompose thermally into two types of nitrenes: singlet (majority) and triplet (minority). A reaction of the singlet state of the nitrene with a fully saturated polymer chain results in insertion of the azide into the polymer chain. Reaction of singlet and triplet nitrene with unsaturations results in addition reactions onto carbon-carbon double bonds which also leads to grafting. Polyethylene is a saturated polymer with only few unsaturations, which stem from imperfections during polymerization. In EPDM the unsaturations are deliberately built-in into the polymer backbone by the use of a third monomer.
Reaction with unsaturated polymers can also be done by grafting at fairly low temperature in a "click" reaction, followed by a heating step during which nitrogen is removed.
The ethylene-based (co)polymer and the azide are contacted at a temperature ranging from 100 to 250°C, preferably 140-230°C, and most preferably 150-220 °C. Contacting can be performed in different ways, including melt-blending, mixing in two roll mills, extrusion, mixing from a common solvent, etc. It is also possible to mix the azide into a compounded ethylene-based (co)polymer, i.e. an ethylene- based (co)polymer already blended with oils, fillers, and other optional additives such as anti-degradants, colorants, etc.
The azide is mixed with the ethylene-based (co)polymer in a preferred amount of 0.1 -5 phr (weight parts per hundred weight parts (co)polymer), more preferably 0.2- 4 phr, and most preferably 0.3-3 phr.
In the process for crosslinking the ethylene-based (co)polymer, the initial contacting of the functionalised ethylene-based (co)polymer with the organic peroxide is to be performed below the safe processing temperature of the peroxide. The safe processing temperature of a peroxide is the temperature at which the scorch time (ts2) is longer than 20 minutes. The scorch time is measured according to ISO 6502:1991 in a rheometer using a moving die. Safe processing temperatures measured in this way can also be found in the AkzoNobel brochure "Crosslinking elastomers and thermoplastics (201 1 )".
Suitable organic peroxides include dialkyi peroxides and trioxepanes. Specifically preferred peroxides are 3,3,5,7,7-pentamethyl-1 ,2,4 trioxepane (safe processing temperature: 180°C), 2,5-dimethyl-2,5-di(tertbutylperoxy)hexyne-3 (safe processing temperature: 145°C), 2,5-dimethyl-2,5-di(tertbutylperoxy)hexane (safe processing temperature: 135°C), di(tert-butylperoxyisopropyl)benzene (safe processing temperature: 135°C), dicumyl peroxide (safe processing temperature: 170°C), and tert-butyl cumyl peroxide (safe processing temperature: 135°C).
The peroxide can be added in liquid or molten form to beads or granules of the functionalised ethylene-based (co)polymer and allowed to diffuse into said beads or granules. This is preferably done at a temperature below 80°C, more preferably below 60°C, and most preferably in the range 20-40°C.
Alternatively, the peroxide and the functionalised ethylene-based (co)polymer are extruded or melt mixed below the safe processing temperature of the peroxide. Another method involves mixing the peroxide and the grafted ethylene-based (co)polymer on a two roll mill.
The organic peroxide is used in the process of the present invention in a preferred amount of 0.1 -5 wt%, more preferably 0.2-4 wt%, and most preferably 0.3-3 wt%, based on the total weight of the peroxide-containing mixture, including peroxide, functionalised ethylene-based (co)polymer, fillers, and additives.
Additional components can be added at this stage, such as anti-oxidants, flame retardants, scorch retarding agents, co-agents, anti-static agents, pigments, colorants, water tree retarding agents, lubricants, and/or slip agents. In case of polyethylene, all of these additives are generally used in relatively small amounts, usually less than 3 wt% with respect to the total mixture.
Examples of a water tree retarding agent are polyethylene glycols (PEG), for instance PEG-2000; a polyethylene glycol with a molecular weight of 2000 Da. Examples of scorch retarding agents are tert-butylhydroquinone and alfa- methylstyrene dimer (4,4-Dimethyl-2,4-diphenyl-1 -butene).
Examples of coagents are: TMAIC (trimethallyl isocyanurate), TAIC (triallyl isocyanurate), TAC (triallycyanurate), TRIM (trimethylol propane trimethacrylate), divinylbenzene, HVA-2 (Ν,Ν'-phenylene bismaleimide), and Perkalink 900 (1 ,3- bis(citraconimidomethyl)benzene).
Other additives, which may be used in higher amounts, are reinforcing fillers like carbon black and silica (particular for ethylene-based copolymers) or non- reinforcing mineral fillers. The latter can be added in amounts up to 60 wt%. Electron conductive carbon black can be added in amounts up to 8 wt%.
After contacting the peroxide with the functionalised ethylene-based (co)polymer and prior to any further thermal treatment, the peroxide/(co)polymer mixture can be shaped in a desired form. For shaping, heat is required to melt or soften the ethylene-based (co)polymer. This shaping can be performed in a mould (compression, injection or transfer moulding); an extruder, (where shaping dies can be installed at the extruder head); or a calender (to process a polymer melt into a sheet or thin film), or by film blowing or thermoforming. Any method can be used to heat the mixture to the required temperature. Examples are: heating in the mould (compression, injection or transfer moulding); heating in (saturated steam, or nitrogen filled) tubular ovens, heating in salt baths, and heating in hot air using ovens or infrared irradiation. The temperature is preferably in the range 140 to 300°C, preferably 150 to 250°C, and most preferably 160 to 230°C.
In one preferred embodiment, the process according to the invention is applied in the production of a cable comprising an electrical conductor (i.e. one or more wires) surrounded by one or more layers, wherein at least one layer comprises the crosslinked ethylene-based (co)polymer. Preferably, the crosslinked ethylene- based (co)polymer is part of the insulation layer, and/or a jacketing layer of said cable.
This cable production comprises the steps of applying, preferably by (co)extrusion, one or more layers comprising a polymer composition on a conductor, wherein at least one layer comprises the crosslinked ethylene-based (co)polymer. If the cable has to contain two or more layers, each layer can be extruded in a separate step, or two or more of said layers can be co-extruded in the same extrusion step.
According to this embodiment, the functionalised ethylene based-(co)polymer, the organic peroxide, and any other optional components can be mixed in a mixer prior to introduction into the extruder. Alternatively, they can be added separately to the extruder and mixed therein. In the extruder, the mixture is subjected to elevated temperature, typically above the melting point of the polymer, and is (co)extruded on a conductor to form the cable layer(s).
After the formation of cable layer(s), the polymer is crosslinked at a temperature in the range 140-300°C, preferably 150-250°C, and most preferably 160-230°C. The pressure during the crosslinking step is preferably up to 20 bar, more preferably up to 13 bar, and most preferably 10-15 bar. The atmosphere is preferably inert, e.g. nitrogen or saturated steam. The crosslinked cable is then preferably cooled under pressurized conditions in a cooling medium such as N2, oil or water. EXAMPLES
Example 1 : Modification of LDPE
LDPE (BPD2000 ex Ineos) was extruded together with 0, 1 , or 2 phr citracon benzenesulfonylazide on a Thermo Scientific Haake PTW16, 40L/D lab extruder. The temperature in the extruder mixing zones ranged from 180 to 230°C, the screw speed was 150 rpm, the output was 1 kg/hr, and the residence time in the extruder was about 90 seconds. These settings were sufficient to fully decompose the azide, as confirmed by FT-IR spectrometry.
After extrusion, the grafted LDPE extrudates were chopped and liquid tert-butyl cumyl peroxide (Trigonox® T, ex-AkzoNobel) was added at different dosage levels to the chopped polymer beads at 60°C to allow fast and homogeneous incorporation of the peroxide into the polymer particles. After absorption of the peroxide on the LDPE, the cure speed and crosslink density were evaluated at 180°C using rheometry (Alfa technologies rheometer MDR 2000).
In a separate experiment, the gel percentage of the crosslinked LDPE was measured by immersion of a specific amount of crosslinked LDPE in refluxing xylenes (approximately 140°C) to determine the insolubles (=gel) content. This is an industrial method to determine the ultimate state of cure.
The results are indicated in the table below. Recorded are the indication for cure speed: t5, t50 and t90, these are the times needed to reach 5, 50 or 90% of the ultimate maximal crosslink density. The delta torque (AS) as measured in the rheometer is used as an indication of the crosslink density of the crosslinked LDPE. Table 1
Figure imgf000013_0001
It can be observed from the experiments that the grafting of the azide has two advantages: enhancement of the cure speed (shortening of t90) and enhancement of the level of cure (increase in AS and gel%). The effect of the citraconazide content depends on the level of peroxide dosage. At low peroxide dosage levels, an increase in citraconazide level from 1 to 2 phr is not leading to a further enhancement of the properties. When increasing the peroxide level, the effect of the increase in citraconazide on the crosslink density becomes more apparent. This shows that the amount of citraconazide and the amount of peroxide can be fine-tuned to allow control over cure speed and crosslink density.
Example 2: modification of EPM
An ethylene-propylene copolymer (EPM), without unsaturations, was modified with the citraconazide used in Example 1 . To achieve this, an EPM-based compound containing carbon black fillers and oil (see Table 2 for the composition) was mixed with 2 parts per hundred rubber (phr) of the citracon benzenesulfonylazide and heat treated at 150-180°C in a Banbury type internal mixer to allow grafting of the azide onto the EPM.
After modification of the EPM compound with the azide, 3 phr of Perkadox® 14- 40B-pd ex-AkzoNobel (= 40 wt% di(tert-butylperoxyisopropyl)benzene on calcium carbonate), corresponding to 0.4 wt% pure peroxide, was mixed with the EPM using a two-roll-mill.
The EPM was cured by heating at 170°C.
The cure speed and crosslink density were evaluated using rheometry (Alfa technologies rheometer MDR 2000). The results are indicated in Table 2.
As a comparative experiment, an unmodified EPM was mixed with peroxide and crosslinked in the same manner. Table 2
Figure imgf000014_0001
The delta torque (AS) as measured in the rheometer is an indication of the crosslink density of the crosslinked EPM. It can be observed that the grafting of the azide has two advantages: to enhance the speed of cure (shorter t90) and to enhance the level of cure (increase in AS).

Claims

1. Process for functionalising an ethylene-based (co)polymer comprising the step of contacting an ethylene-based (co)polymer at a temperature in the range 100-250°C with an azide of formula (I)
Figure imgf000016_0001
wherein Y is either
Figure imgf000016_0002
m is 0 or 1 , n is 0 or 1 , n+m=1 or 2, and X is a linear or branched, aliphatic or aromatic hydrocarbon moiety with 1 -12 carbon atoms, optionally containing heteroatoms.
Process according to claim 1 or 2 wherein the ethylene based (co)polymer is LDPE.
Process according to claim 1 or 2 wherein the ethylene-based (co)polymer is EPM.
Process according to any one of the preceding claims wherein the azide is selected from 4-(3-methyl-2,5-dioxo-2,5-dihydro-1 H-pyrrol-1 -yl)benzene sulfonyl azide (also called citraconimide benzenesulfonylazide) and 2-(3- methyl-2,5-dioxo-2,5-dihydro-1 H-pyrrol-1 -yl)ethyl carbonazidate (also called citraconimide-C2-azidoformate).
Process according to any one of the preceding claims wherein the ethylene- based (co)polymer and the azide are contacted at a temperature in the range 140-230°C.
Process according to any one of the preceding claims wherein the azide is mixed with the ethylene-based (co)polymer in an amount of 0.1 -5 phr.
Process for modifying an ethylene-based (co)polymer comprising the steps of:
- preparing a functionalised ethylene-based (co)polymer according to the process of any one of claims 1 -6,
- contacting the functionalised ethylene-based (co)polymer with an organic peroxide to form a polymer/peroxide mixture, and
- heating said polymer/peroxide mixture at a temperature in the range 140- 300°C.
Process according to claim 7 wherein the polymer/peroxide mixture is shaped prior to heating.
Process according to claim 8 wherein the polymer/peroxide mixture is shaped by extrusion.
Process according to any of claims 7-8 wherein the organic peroxide is a dialkyl peroxide or a trioxepane. Process according to claim 10 wherein the peroxide is selected from the group consisting of 3,3,5,7,7-pentamethyl-1 ,2,4 trioxepane, 2,5-dimethyl- 2,5-di(tertbutylperoxy)hexyne-3, 2,5-dimethyl-2,5-di(tertbutylperoxy)hexane, di(tert-butylperoxyisopropyl)benzene, dicumyl peroxide, and tert-butyl cumyl peroxide.
Functionalised ethylene-based (co)polymer obtainable by the process according to any one of claims 1 -6.
Modified ethylene-based (co)polymer obtainable by the process according to any one of claims 7-1 1.
Use of the functionalised ethylene-based (co)polymer of claim 12 for making power cables.
Power cable comprising one or more layers of the modified ethylene-based (co)polymer of claim 13.
PCT/EP2014/073418 2013-11-07 2014-10-31 Process for modifying ethylene-based polymers and copolymers WO2015067533A1 (en)