WO2015017490A1 - Flexible white reflective dielectric for electronic circuits - Google Patents

Flexible white reflective dielectric for electronic circuits Download PDF

Info

Publication number
WO2015017490A1
WO2015017490A1 PCT/US2014/048770 US2014048770W WO2015017490A1 WO 2015017490 A1 WO2015017490 A1 WO 2015017490A1 US 2014048770 W US2014048770 W US 2014048770W WO 2015017490 A1 WO2015017490 A1 WO 2015017490A1
Authority
WO
WIPO (PCT)
Prior art keywords
white reflective
thick film
flexible dielectric
organic medium
polymer thick
Prior art date
Application number
PCT/US2014/048770
Other languages
French (fr)
Inventor
Jay Robert Dorfman
Original Assignee
E. I. Du Pont De Nemours And Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by E. I. Du Pont De Nemours And Company filed Critical E. I. Du Pont De Nemours And Company
Priority to JP2016531846A priority Critical patent/JP2016528346A/en
Priority to CN201480037386.1A priority patent/CN105339429B/en
Priority to EP14750291.8A priority patent/EP3027687B1/en
Publication of WO2015017490A1 publication Critical patent/WO2015017490A1/en

Abstract

This invention is directed to a polymer thick film white reflective flexible dielectric composition comprising urethane resin, thermoplastic phenoxy resin, and white reflective powder. Dielectrics made from the composition can be used in various electronic applications to protect electrical elements and particularly to reflect light in 3D circuits containing LED's.

Description

TITLE
FLEXIBLE WHITE REFLECTIVE DIELECTRIC FOR ELECTRONIC
CIRCUITS
FIELD OF THE INVENTION
This invention is directed to a polymer thick film white reflective flexible dielectric composition. Dielectrics made from the composition can be used in various electronic applications to protect electrical elements and particularly to provide reflectance to maximize LED lighting.
BACKGROUND OF THE INVENTION
Dielectrics have long been used to protect electrical elements. They have also been used as isolating layers. Although they have been used for years in these types of applications, the use of dielectrics as reflective elements is not common. This is particularly important in circuits containing LED lighting where one wants to maximize the available brightness through reflectivity. Additionally, more and more circuitry is being developed where the base substrate that the LED's are attached to needs to be bent and shaped in a non-planar fashion. Thus, the white reflective dielectric must also be flexible i.e., it must withstand a 90 degree bend with no cracking. One of the purposes of this invention is to alleviate this issue and produce a flexible reflective construction in which the light generated from LED's can be maximized.
SUMMARY OF THE INVENTION
This invention relates to a polymer thick film white reflective flexible dielectric composition comprising:
(a) 15-50 wt% of a first organic medium comprising 10-50 wt%
urethane resin dissolved in 50-90 wt% first organic solvent, wherein the weight percent of the urethane resin and the first organic solvent are based on the total weight of the first organic medium;
(b) 15-50 wt% of a second organic medium comprising 10-50 wt% thermoplastic phenoxy resin dissolved in 50-90 wt% second organic solvent wherein the weight percent of the thermoplastic (c) phenoxy resin and the second organic solvent are based on the total weight of the second organic medium; and
(d) 1 -70 wt% of a white reflective powder;
wherein the weight percent of the first organic medium, the second organic medium and the white reflective powder are based on the total weight of the composition.
The invention is further directed to using the white reflective flexible dielectric to form a protective and/or insulating layer in electrical circuits.
DETAILED DESCRIPTION OF INVENTION
The invention relates to a polymer thick film white reflective flexible dielectric composition for use in electrical circuits.
The substrate commonly used in the types of circuits considered here is usually polyimide or a polyimide laminate construction such as DuPont™ CooLam® (DuPont Co., Wilmington, DE). DuPont™ CooLam® is used for thermal conductivity purposes when high-brightness LED's are present. Further, DuPont™ CooLam® 3D (DuPont Co., Wilmington, DE) is used for circuits which are non-planar.
The polymer thick film white reflective flexible dielectric composition can also be used in thermoforming electrical circuits, e.g., capacitive switch circuits. The substrate commonly used in polymer thick film thermoformable capacitive circuits is polycarbonate (PC). PC is generally preferred since it can be readily thermoformed. However, PC is very sensitive to the solvents used in the layers deposited on it. An
inappropriate solvent can and will cause cracking or crazing in the PC substrate. In the course of producing a 3-dimensional capacitive circuit, after the thermoforming step, the final step will often be a molding step in which the finished circuit is formed by injection molding using a resin such as polycarbonate. This process is referred to as in-molding and involves higher temperatures. Depending on the resin chosen, these temperatures can typically exceed 250°C for 10-30 sec. Thus the choice of the resins used in the PTF composition is critical. The combination of the resins used in the instant PTF composition has been shown to survive the in- mold process and produce fully functional circuitry whereas most resins typically used in PTF compositions will not.
The polymer thick film (PTF) white reflective flexible dielectric composition is comprised of (i) two organic mediums comprising two polymer resins dissolved in a first organic solvent and a second organic solvent, respectively, and (ii) white reflective powder. Additionally, powders and printing aids may be added to improve the composition. Herein weight percent will be written as wt%.
ORGANIC MEDIUM
The first organic medium is comprised of a urethane elastomer resin dissolved in a first organic solvent. The urethane resin must help achieve good adhesion to the underlying substrate. The urethane elastomer must also provide flexibility for the required bending of the circuit. It must be compatible with and not adversely affect the
performance of the electrical element.
In one embodiment the urethane resin is 10-50 wt% and the first organic solvent is 50-90 wt% of the total weight of the first organic medium. In another embodiment the urethane resin is 25-45 wt% and the first organic solvent is 55-75 wt% of the total weight of the first organic medium. In still another embodiment the urethane resin is 15-25 wt% and the first organic solvent is 75-85 wt% of the total weight of the first organic medium. In one embodiment the urethane resin is a urethane elastomer. In another embodiment urethane resin is a polyester-based copolymer.
The second organic medium is composed of a phenoxy resin dissolved in a second organic solvent that may be the same as the first organic solvent. Different solvents may also be used. The phenoxy resin adds high temperature capability to the composition which aids in the use of this dielectric as a solder mask if required, and also improves moisture permeability. That is, it helps impede the progress of moisture through the composition. In one embodiment the phenoxy resin is 10-50 wt% and the second organic solvent is 50-90 wt% of the total weight of the second organic medium. In another embodiment the phenoxy resin is 20-35 wt% and the second organic solvent is 65-80 wt% of the total weight of the second organic medium.
In one embodiment, each medium is 15-50 wt% based on the total weight of the composition. In another embodiment, each medium is 15-40 wt% based on the total weight of the composition. In still another embodiment, the first organic medium is 15-25 wt% and the second organic medium is 25-45 wt% based on the total weight of the
composition.
Although the preparation of two separate organic media are preferred, if the same solvent is to be used for both media a single organic medium equivalent to the two organic media described above may be used.
The polymer resin is typically added to the organic solvent by mechanical mixing to form the medium. Solvents suitable for use in the polymer thick film composition are recognized by one of skill in the art and include acetates and terpenes such as carbitol acetate and alpha- or beta-terpineol or mixtures thereof with other solvents such as kerosene, butyl carbitol, butyl carbitol acetate, hexylene glycol and high boiling alcohols and alcohol esters. In addition, volatile liquids for promoting rapid hardening after application on the substrate may be included. In many embodiments of the present invention, solvents such as glycol ethers, ketones, esters and other solvents of like boiling points (in the range of 180°C to 250°C), and mixtures thereof may be used. Various
combinations of these and other solvents are formulated to obtain the viscosity and volatility requirements desired. The solvents used must solubilize the resin.
WHITE REFLECTIVE POWDER
The white reflective powder includes such powders as titanium dioxide, barium titanate, alumina, or mixtures thereof. In one embodiment, the amount of white reflective powder is 1 -70% of the total weight of the entire composition. In another embodiment the white reflective powder is 20-60 wt% of the total weight of the entire composition and in still another embodiment the white reflective powder is 30-55 wt% of the total weight of the entire composition. In one embodiment the powder is titanium dioxide. It is preferable to keep the particle size of the reflective powder in the range of 0.3-5 microns so as to avoid any cracking issues.
ADDITIONAL POWDERS
Various powders may be added to the PTF dielectric composition to improve adhesion, modify the rheology and increase the low shear viscosity thereby improving the printability. One such powder is fumed silica where it has been found to significantly improve the resistance to moisture penetration.
APPLICATION OF THE PTF WHITE REFLECTIVE FLEXIBLE DIELECTRIC COMPOSITION
The PTF white reflective flexible dielectric composition, also referred to as a "paste", is typically deposited on a substrate, such as polyimide or a laminate of polyimide, such as DuPont™ CooLam® 3D, that is somewhat impermeable to gases and moisture. In other
constructions, the white reflective flexible dielectric may be deposited over an existing silver/dielectric construction.
The deposition of the PTF white reflective flexible dielectric composition is performed typically by screen printing, but other deposition techniques such as stencil printing, syringe dispensing or coating techniques can be utilized. In the case of screen-printing, the screen mesh size controls the thickness of the deposited thick film.
Generally, a thick film composition comprises a functional phase that imparts appropriate functional properties to the
composition. The functional phase comprises functional powders dispersed in an organic medium that acts as a carrier for the
functional phase. Generally, the composition is fired to burn out both the polymer and the solvent of the organic medium and to
impart the electrically functional properties. However, in the case of a polymer thick film, the polymer portion of the organic medium
remains as an integral part of the composition after drying.
The PTF white reflective flexible dielectric composition is processed for a time and at a temperature necessary to remove all solvent. For example, the deposited thick film is dried by exposure to heat at 130°C for typically 10-15 min.
CIRCUIT CONSTRUCTION
The substrate used is typically polyimide-based as further processing steps involve exposure to soldering temperatures. The white reflective flexible dielectric is printed and dried as per the conditions described above. Several layers can be printed and dried. A subsequent step which may include bending of the entire unit is typical in the
production of 3D circuits with as much as a 90 degree bend required. In one embodiment, the circuit is used as a solder mask.
EXAMPLE AND COMPARATIVE EXPERIMENT EXAMPLE 1
The PTF white reflective flexible dielectric composition was prepared in the following manner. The first organic medium was prepared by mixing 20.0 wt% Desmocoll 540 polyurethane (Bayer MaterialScience LLC, Pittsburgh, PA) with 80.0 wt% dibasic esters (DuPont Co.,
Wilmington, DE) organic solvent. The molecular weight of the resin was approximately 40,000. This mixture was heated at 90°C for 1 -2 hours to dissolve all the resin. The second organic medium was prepared by adding 27.0 wt% PKHH (phenoxy) resin (InChem Corp.) to 73.0 wt% dibasic esters and heating as above. The above weight percent are based on the total weight of each of the media, respectively. All following weight percent are based on the total weight of the PTF white reflective flexible dielectric composition. 40.0 wt% titanium dioxide powder (DuPont Co., Wilmington, DE) was then added as the white reflective powder and the entire composition was mixed. The composition was then subjected to the three-roll-mill for two cycles at 150 psi.
The composition, based on the total weight of the composition, was:
25.0 wt% First Organic Medium
35.0 wt% Second Organic Medium
40.0 wt% Titanium Dioxide Powder A circuit was then fabricated as follows: On a DuPont™ CooLam® 3D substrate, a blanket print of the white reflective flexible dielectric composition prepared as described above was printed with a 200 stainless steel screen and dried at 130°C for 10 min. A second print of the composition was then printed and dried. The part was inspected and no evidence of crazing or deformation of the underlying substrate was found. The circuit was then subjected to a 90 degree bend and tested for cracking/adhesion. No visible signs of cracking were detected, and adhesion before and after the bend was outstanding (5B on ASTM Tape Test). Reflectivity was measured at 90%.
COMPARATIVE EXPERIMENT A
A circuit was produced exactly as described in Example 1 . The only difference was that the white reflective flexible dielectric composition was not used. Instead, a standard PTF dielectric, DuPont 5036 (DuPont Co., Wilmington, DE), was used. Here, cracking and adhesion loss was observed after the 90 degree bending. Additionally, reflectivity was only 30%.

Claims

What is claimed is: 1 . A polymer thick film white reflective flexible dielectric composition
comprising:
(a) 15-50 wt% of a first organic medium comprising 10-50 wt% urethane resin dissolved in 50-90 wt% first organic solvent, wherein the weight percent of said urethane resin and said first organic solvent are based on the total weight of said first organic medium;
(b) 15-50 wt% of a second organic medium comprising 10-50 wt% thermoplastic phenoxy resin dissolved in 50-90 wt% second organic solvent wherein the weight percent of said thermoplastic phenoxy resin and said second organic solvent are based on the total weight of said second organic medium; and
(c) 1 -70 wt% of a white reflective powder;
wherein the weight percent of said first organic medium, said second organic medium and said white reflective powder are based on the total weight of said composition.
2. The polymer thick film white reflective flexible dielectric composition of claim 1 , wherein said urethane resin is a urethane elastomer or a polyester-based copolymer and said white reflective powder is selected from the group consisting of titanium dioxide, barium titanate, alumina, or mixtures thereof.
3. The polymer thick film white reflective flexible dielectric composition of claim 1 , said polymer thick film white reflective flexible dielectric composition comprising:
(a) 15-40 wt% of a first organic medium comprising 15-25 wt% urethane resin dissolved in 75-85 wt% first organic solvent, wherein the weight percent of said urethane resin and said first organic solvent are based on the total weight of said first organic medium;
(b) 15-40 wt% of a second organic medium comprising 20-35 wt% thermoplastic phenoxy resin dissolved in 65-80 wt% second organic solvent wherein the weight percent of said thermoplastic phenoxy resin and said second organic solvent are based on the total weight of said second organic medium; and
(c) 20-60 wt% of a white reflective powder;
wherein the weight percent of said first organic medium, said second organic medium and said white reflective powder are based on the total weight of said composition.
4. A polymer thick film white reflective flexible dielectric composition comprising:
(a) urethane resin;
(b) thermoplastic phenoxy resin
(c) white reflective powder.
5. The polymer thick film white reflective flexible dielectric composition of claim 7, wherein said thermoplastic urethane resin is a urethane elastomer or a polyester-based copolymer and said white reflective powder is selected from the group consisting of titanium dioxide, barium titanate, alumina, or mixtures thereof.
6. A circuit comprising a substrate and a polymer thick film white reflective flexible dielectric formed from the polymer thick film white reflective flexible dielectric composition of claim 1 , wherein said circuit is fabricated on a polyimide-based substrate and wherein said urethane resin and said thermoplastic phenoxy resin remain as an integral part of said polymer thick film white reflective flexible dielectric.
7. The circuit of claim 6, wherein said circuit is used as a solder mask.
8. The circuit of claim 6, wherein said circuit contains LED lighting.
9. A capacitive switch circuit comprising a polymer thick film white reflective flexible dielectric formed from the polymer thick film white reflective flexible dielectric composition of claim 1 , wherein said urethane resin and said thermoplastic phenoxy resin remain as an integral part of said polymer thick film white reflective flexible dielectric and said circuit has been thermoformed.
10. The capacitive switch circuit of claim 9, wherein said capacitive switch circuit has been subsequently subjected to an injection molding process.
PCT/US2014/048770 2013-07-31 2014-07-30 Flexible white reflective dielectric for electronic circuits WO2015017490A1 (en)