WO2014168245A1 - 酸化錫インジウム粉末、その分散液または塗料、透明導電性膜、及び酸化錫インジウム粉末の製造方法 - Google Patents

酸化錫インジウム粉末、その分散液または塗料、透明導電性膜、及び酸化錫インジウム粉末の製造方法 Download PDF

Info

Publication number
WO2014168245A1
WO2014168245A1 PCT/JP2014/060545 JP2014060545W WO2014168245A1 WO 2014168245 A1 WO2014168245 A1 WO 2014168245A1 JP 2014060545 W JP2014060545 W JP 2014060545W WO 2014168245 A1 WO2014168245 A1 WO 2014168245A1
Authority
WO
WIPO (PCT)
Prior art keywords
tin oxide
oxide powder
indium tin
film
hydroxide
Prior art date
Application number
PCT/JP2014/060545
Other languages
English (en)
French (fr)
Inventor
真也 白石
洋利 梅田
鈴夫 佐々木
Original Assignee
三菱マテリアル株式会社
三菱マテリアル電子化成株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 三菱マテリアル株式会社, 三菱マテリアル電子化成株式会社 filed Critical 三菱マテリアル株式会社
Publication of WO2014168245A1 publication Critical patent/WO2014168245A1/ja

Abstract

本発明は、良好な透明性と高い導電性を備えた透明導電性膜を形成することができる酸化錫インジウム粉末の提供を目的・課題とする。 本発明の酸化錫インジウム粉末は、Ｘ線回折測定において立方晶のみからなり、長軸４０ｎｍ以下の複数の一次粒子が棒状に凝集して結合した凝集晶であり、長軸が９０ｎｍ以上１６５ｎｍ以下、短軸が３０ｎｍ以上６０ｎｍ以下とされ、ＢＥＴ法による比表面積が３０．０ｍ２／ｇ以上、かさ密度が０．６８ｇ／ｃｍ３以上である。この酸化錫インジウム粉末は、水に、塩化インジウムおよび四塩化錫を混合した混合水溶液と、アルカリ水溶液とを投入して反応させて水酸化物を生成させ、その水酸化物の粉末を焼成することによって得られる。

Description

酸化錫インジウム粉末、その分散液または塗料、透明導電性膜、及び酸化錫インジウム粉末の製造方法
　本発明は、透明導電性膜を形成するための酸化錫インジウム粉末、その分散液または塗料、透明導電性膜、及び酸化錫インジウム粉末の製造方法に関する。
　本願は、２０１３年４月１２日に日本に出願された特願２０１３－０８４２９９号に基づき優先権を主張し、その内容をここに援用する。
　酸化錫インジウム（以下、ＩＴＯということもある）は、導電性材料として知られており、スパッタリングを用いて成膜した透明導電性膜が広く用いられている。しかし、スパッタリングは真空系のため高コストとなる。そこで、ＩＴＯ粉末を樹脂に分散させた分散液を用いて透明導電性膜を形成する方法が検討されている（特許文献１～５など）。
　例えば、特許文献１では、所定の製法によりＩＴＯ粒子間の焼結や凝集を防止し、透明度が高く、表面抵抗率が小さい透明導電性膜を得ている。特許文献２，３では、ＩＴＯ粉末の粒子形状による影響が検討されている。特許文献４では、ＩＴＯ粉末における残留塩素量の低減が検討されている。特許文献５では、ＩＴＯの透明導電性膜に圧力をかけることで、低抵抗化が図られている。
　また、ＩＴＯは熱線遮蔽膜の材料としても広く利用されている（特許文献６など）。
特許第４６１７４９９号公報 特許第４６８６７７６号公報 特許第３２５１０６６号公報 特開２０１１－１６２３７５号公報 特許第４６９７３６０号公報 特開２０１１－０６３４９５号公報
　透明導電性膜には、透明性と導電性が要求されるところ、従来のＩＴＯ粉末を用いた膜は、スパッタ法に比べて導電性に劣る傾向があった。
　本発明は、上記事情に鑑み提案されたもので、良好な透明性と高い導電性を備えた透明導電性膜を形成することができる酸化錫インジウム粉末、その分散液または塗料、透明導電性膜、及び酸化錫インジウム粉末の製造方法を提供することを目的とする。
　本発明者は、透明性と導電性に優れる透明導電性膜を形成することができるＩＴＯ粉末について鋭意研究した結果、微細なＩＴＯの一次粒子を凝集させ、一部が結合した棒状の凝集晶の状態の粉末とすることにより、そのＩＴＯ粉末を用いて所定の方法で作製した透明導電性膜は、良好な透明性と高い導電性を備えることを見出した。
　本発明は、かかる知見の下、以下の解決手段とした。
　本発明の酸化錫インジウム粉末は、Ｘ線回折測定において立方晶のみからなり、長軸４０ｎｍ以下の複数の一次粒子が棒状に凝集して結合した凝集晶であり、長軸が９０ｎｍ以上１６５ｎｍ以下、短軸が３０ｎｍ以上６０ｎｍ以下とされ、ＢＥＴ法による比表面積が３０．０ｍ２／ｇ以上、かさ密度が０．６８ｇ／ｃｍ３以上であることを特徴とする。
　この酸化錫インジウム粉末は、一次粒子を微細な粒子とすることにより膜にしたときの透明性が確保されるとともに、その一次粒子を凝集させて棒状の凝集晶とすることにより膜の導電性が高められる。棒状の凝集晶のない球状の粉末では十分な透明性を得られず、一部に球状粒子が混在している場合でも、透明性及び低抵抗の透明導電性膜を得ることが難しい。
　この場合、立方晶のみからなることが必要であり、六方晶が混在していると、十分な透明性と導電性を有する膜が得られない。
　凝集晶を構成する一次粒子は長軸４０ｎｍを超えていると、膜にしたときの透明性が低下する。また、凝集晶としては、長軸が９０ｎｍ未満であると、粒子どうしの接触が悪く、膜の導電性が低下する。長軸が１６５ｎｍを超えると、一次粒子径も長軸４０ｎｍを超えることになり、膜の透明性が悪くなる。短軸が３０ｎｍ未満であると、一次粒子径も小さくなり、膜の導電性が低下する。短軸が６０ｎｍを超えると、粒子サイズが大きくなり、膜の透明性が悪くなるので、好ましくない。
　また、比表面積が３０．０ｍ２／ｇ未満であると、一次粒子径が大きいので、膜の透明性が低下する。一方、粉体かさ密度が０．６８ｇ／ｃｍ３未満であると、充填性が不足するため膜の導電性が低下する。
　また、本発明は、前記酸化錫インジウム粉末を溶媒に分散させてなる分散液または塗料、あるいは前記酸化錫インジウム粉末を含有する透明導電性膜とすることができる。
　そして、本発明の酸化錫インジウム粉末の製造方法は、前記酸化錫インジウム粉末の製造方法であって、水に、塩化インジウムおよび四塩化錫を混合した混合水溶液と、アルカリ水溶液とを投入して、塩化インジウムおよび四塩化錫とアルカリとをｐＨ５．５～６．５で反応させて、その反応液中に水酸化物を生成させる反応工程と、反応工程の後、反応液にアルカリ水溶液を添加して、ｐＨ８～１０に調整するｐＨ調整工程と、ｐＨ調整工程におけるアルカリ水溶液の添加開始から５分以内に実施され、水酸化物を洗浄する洗浄工程と、洗浄工程で得られた水酸化物の粉末を焼成して酸化錫インジウム粉末を得る焼成工程とを備えることを特徴とする。
　本発明の酸化錫インジウム粉末の製造方法において、前記焼成工程で得られた酸化錫インジウム粉末を非酸化雰囲気で加熱処理して表面改質する改質工程をさらに備えるとよい。
　本発明の酸化錫インジウム粉末によれば、良好な透明性と高い導電性を備えた透明導電性膜を得ることができる。
本発明の実施例１のＩＴＯ粉末の顕微鏡写真である。 比較例７のＩＴＯ粉末の顕微鏡写真である。
　以下、本発明の実施形態に基づいて具体的に説明する。なお、含有量を示す単位の“％”は、特に示さない限り、質量％である。
［ＩＴＯ粉末］
　本発明のＩＴＯ粉末は、Ｘ線回折測定において立方晶のみからなり、比表面積（ＢＥＴ）が３０．０ｍ２／ｇ以上、かさ密度が０．６８ｇ／ｃｍ３以上である。また、個々のＩＴＯ粉末は、図１に示すように、粒径（長軸径）４０ｎｍ以下の多数の一次粒子が棒状に凝集して結合した凝集晶を形成しており、凝集晶としてのサイズは、長軸が９０ｎｍ以上１６５ｎｍ以下、短軸が３０ｎｍ以上６０ｎｍ以下とされる。
　このＩＴＯ粉末は、少なくともＸ線回折測定において六方晶のピークが観察されず、立方晶のみからなることが必要である。六方晶が混在していると、十分な透明性と導電性を有する膜が得られない。
　また、一次粒子径が１００ｎｍ以下と小さいので、膜にしたときに高い透明性を示す。一般には、粒子径が小さく比表面積の大きい粉末は、かさ密度が低くなり、かさ密度が低いと充填性が不足するため膜の導電性が低下する。しかし、本発明のＩＴＯ粉末では、一次粒子が凝集し、その一部が結合した凝集晶の状態となっており、比表面積とかさ密度の両方が高いという特徴を有する。このため、本発明のＩＴＯ粉末によれば、比表面積が高いにもかかわらず、高いかさ密度により高い導電性が発揮され、良好な透明性と高い導電性を備えた透明導電性膜を作成することができる。凝集晶でなく、一次粒子が集まった単なる凝集体であると、そのＩＴＯ粉末を分散媒に分散して塗料を作製する際に、凝集が解かれてしまい、膜として導電性を発揮することが困難になる。凝集晶であることは、超音波振動等の振動や衝撃を付与することによって確認することができ、単なる凝集体の場合は粒状の粉末に分散するが、凝集晶の場合は、凝集晶としての形態のまま分散する。
　この凝集晶は、長軸が９０ｎｍ未満であると、粒子どうしの接触が悪く、膜の導電性が低下する。長軸が１６５ｎｍを超えると、一次粒子も長軸４０ｎｍを超えることになり、膜の透明性が悪くなる。短軸が３０ｎｍ未満であると、一次粒子径も小さくなり、膜の導電性が低下する。短軸が６０ｎｍを超えると、粒子サイズが大きくなり、膜の透明性が悪くなるので、好ましくない。
　また、比表面積が３０．０ｍ２／ｇ未満であると、一次粒子径が大きいので、膜の透明性が低下する。一方、粉体かさ密度が０．６８ｇ／ｃｍ３未満であると、充填性が不足するため膜の導電性が低下する。
［製造方法］
　このＩＴＯ粉末の製造方法は、水に、塩化インジウムおよび四塩化錫を混合した混合水溶液と、アルカリ水溶液とを投入して、塩化インジウムおよび四塩化錫とアルカリとをｐＨ５．５～６．５で反応させて、その反応液中に水酸化物を生成させる反応工程と、反応工程の後、反応液にアルカリ水溶液を添加して、ｐＨ８～１０に調整するｐＨ調整工程と、ｐＨ調整工程におけるアルカリ水溶液の添加開始から５分以内に実施され、水酸化物を洗浄する洗浄工程と、洗浄工程で得られた水酸化物の粉末を焼成してＩＴＯ粉末を得る焼成工程と、得られたＩＴＯ粉末を非酸化性雰囲気で加熱処理して表面改質する改質工程とを備えている。
　以下、工程順に説明する。
＜反応工程＞
　この反応工程は、水に、塩化インジウムおよび四塩化錫を混合した混合水溶液と、アルカリ水溶液とを徐々に投入して、塩化インジウムおよび四塩化錫とアルカリとを反応させて水酸化物を生成させるとともに、生成された水酸化物を反応液中において熟成させる工程である。以下では、便宜上、水酸化物を生成させる反応処理と、生成された水酸化物を熟成させる熟成処理とに分けて説明する。
（反応処理）
　反応処理においては、水に、塩化インジウムおよび四塩化錫を混合した混合水溶液とアルカリ水とを徐々に投入して、塩化インジウムおよび四塩化錫とアルカリとを反応させることにより、インジウム水酸化物と錫水酸化物とが共沈する。アルカリとしてアンモニアを用いた場合は、以下の（１）（２）で示す反応となる。
（１）ＩｎＣｌ３＋３ＮＨ４ＯＨ→Ｉｎ（ＯＨ）３＋３ＮＨ４Ｃｌ
（２）ＳｎＣｌ４＋４ＮＨ４ＯＨ→Ｓｎ（ＯＨ）４＋４ＮＨ４Ｃｌ
　この共沈殿物であるインジウム錫水酸化物は、後述するように生成後に熟成させることにより棒状の粒子となり、焼成することにより、棒状の凝集晶の状態の酸化錫インジウム粉末を得ることができ、棒状のため、導電性、透明性の高い膜を形成することができる。
　この反応処理において反応液のｐＨを５．５～６．５の範囲内とすることにより、生成される水酸化物の粒度分布を小さくして、粒子サイズを均一化することができるとともに、結晶系にて立方晶を得ることができ、得られた粉末を膜にしたときの導電性および透明性を良好にすることができる。
　ｐＨ５．５未満であると、粒子のサイズが大きくなり、膜の透明性が低下するため好ましくない。一方、ｐＨが６．５を超えると、ＩＴＯ粉末に、導電性及び透明性悪化の原因となる六方晶が混入し、また、棒状凝集晶でなく球状の粉末が多くなるため、十分な導電性を有する膜が得られない。立方晶であることはＸ線回折（ＸＲＤ）により確認することができる。この場合、水に、塩化インジウムおよび四塩化錫の混合水溶液と、アルカリ水溶液とを徐々に投入することにより、反応液のｐＨを容易に制御することができ、ｐＨを５．５～６．５に確実に保持した状態で反応を進めることができる。
　単位時間当たりの投入量は、反応液のｐＨを５．５～６．５に保持できる量であれば特に限定されるものではなく、原料の水溶液の濃度等にもよるが、例えばＩＴＯ粉末６５０ｇを製造する場合に、原料としては１０～２００ｇ／分、アルカリ水溶液としては原料の時間当たり投入量の１／１０～１倍の投入量（１～２００ｇ／分）とされ、いずれも滴下による方法が好適である。
　なお、反応初期においてはｐＨが安定しないため、ｐＨ５．５～６．５の範囲から外れる場合もある。このような場合でも、ｐＨが所定の範囲から外れた時間が、工程全体の時間に対して十分に短ければ（例えば、原料又はアルカリ水溶液の投入開始からこれらの投入終了までの時間の１／１０以内程度であれば）、ＩＴＯ粉末への影響はなく、本発明の優れた効果を得ることができる。
　ｐＨをこの範囲に維持するために、反応初期においては塩化インジウムおよび四塩化錫の混合水溶液をアルカリ水溶液より多めに投入するとよい。なお、反応が進むと、水酸化物および原料由来のイオンの濃度が上昇して、緩衝液となるため、ｐＨは安定する。
　この場合、原料とアルカリ水溶液とを水に徐々に投入する方法ではなく、原料の塩化インジウムおよび四塩化錫の混合水溶液を反応器に貯留しておき、これにアルカリ水溶液を投入する方法では、生成する粒子の粒度分布が広く、不均一サイズの粒子になる。粗大な粒子も多数できるため、膜にしたときの透明性が低下する。
　四塩化錫は、この棒状粒子を得るために必要であり、２価の錫（例えばＳｎＣｌ２）を用いると、希薄溶液中においては棒状粒子の生成が可能であるが、実用上好ましい濃度においては棒状の粒子を得ることができず、棒状凝集晶のない球状の粉末となるため、十分な透明性を有する膜が得られない。
　この反応処理における反応液の温度は２０～８０℃とする。反応液の温度が２０℃未満であると、生成する水酸化物が棒状にならず、棒状凝集晶のない球状の粉末となるため、透明性も悪く、かつ、低抵抗の膜を得ることができない。一方、温度が８０℃を超えると、アルカリ水溶液としてアンモニア水を用いる場合に、アンモニアの蒸発が大量に生じるため、経済的観念から好ましくない。
　また、反応処理終了後（原料及びアルカリ水溶液の投入終了後）の水酸化物濃度は５％以下となるようにする。水酸化物濃度を５％以下とすることにより、水酸化物の成長を制御して棒状に成長させることができ、凝集晶の状態のＩＴＯ粉末を得ることができるからである。５％を超えると、塩濃度が高くなる為、反応時に水酸化物の溶解・析出による棒状成長が阻害され、球状粒子が混在し、透明性並びに低抵抗の透明導電性膜を得ることができない。
（熟成処理）
　熟成処理で水酸化物の粒子を成長させることにより、焼成工程後に好ましい棒状凝集晶の状態のＩＴＯ粉末が得られる。
　前述したように反応処理と熟成処理とに便宜的に分けて説明しているが、反応処理において原料を徐々に反応器に投入するので、反応で生成した水酸化物は、生成すると同時に熟成を開始することになり、反応と熟成とが同時に進行する。
　この場合、反応処理の初期に生成した水酸化物と、反応処理の終期に生成した水酸化物とで、熟成の時間が変わることになる。このため、反応処理の終期に生成した水酸化物の熟成の時間を確保するには、原料及びアルカリ水溶液の投入終了から５分間以上の熟成の時間を設けることがよい。好ましくは、３０分の熟成の時間を確保できるとよい。
　しかし、反応処理の時間（原料又はアルカリ水溶液の投入開始からこれらの投入終了までの時間）が長ければ（例えば、１２０分以上であれば）、反応処理と別個に熟成処理を設けなくても、熟成時間の短い水酸化物はごくわずかであるため、全体としてのＩＴＯ粉末への影響は実質的になく、本発明の優れた効果を得ることができる。反応処理の時間が短い場合には、別途、反応処理の後に反応液を静置して熟成させる時間を設ければよい。これにより、反応終了間際に滴下した原料も熟成時間が確保されるので、全ての水酸化物の粒子を成長させ、焼成工程後に好ましい凝集晶の状態のＩＴＯ粉末をより確実に得ることができる。
　熟成処理の時間（原料及びアルカリ水溶液の投入開始からの経過時間）が１８０分を超えると、粒子のサイズが大きくなり、膜の透明性が低下するため、好ましくない。この１８０分の範囲内で熟成時間をどの程度確保するかは、反応処理で投入される原料及びアルカリ水溶液の量、その量全部の投入に要する時間等により定まる。
　なお、熟成処理における温度は反応処理における温度をそのまま維持し、２０～８０℃とする。
＜ｐＨ調整工程、洗浄工程＞
　ｐＨ調整工程および洗浄工程により、ＩＴＯ粉末における残留塩素量を低減することができる。
　反応工程における反応初期に生成された水酸化物の熟成時間を１８０分以内とするために、ｐＨ調整工程においては、反応工程の原料又はアルカリ水溶液の投入開始から１８０分以内にアルカリ水溶液を添加する。そして、このアルカリ水溶液を添加して得られる合成液のｐＨを８～１０に調整する。この合成液のｐＨが８未満であると、塩素を十分に除去することができず、ＩＴＯ粉末における残留塩素量が増加するとともに、後の焼成工程で焼結が促進されて焼成工程後に得られるＩＴＯ粉末の粒径が大きくなる。一方、ｐＨが１０を超えても、ｐＨ８～９と同等の塩素低減効果であるため、アンモニアの使用量が増加するのみで、経済的観点より好ましくない。
　一方、洗浄工程では、ｐＨ調整工程後の合成液に水を加えて攪拌した後に静置し、その上澄み液を流し去るデカンテーション操作により、塩（塩素、アンモニウムイオン）を除去して沈殿物（インジウム錫水酸化物）を洗浄する。洗浄工程の終了は、流し去られる上澄み液の電気伝導率が例えば１００μＳ／ｃｍ以下になったことで判断し、１００μＳ／ｃｍ以下になるまでデカンテーション操作を繰り返す。
　また、この洗浄工程は、合成液を水で希釈して粒子の成長を停止させる処理であり、ｐＨ調整工程におけるアルカリ水溶液の添加開始から５分以内に実施する。５分以内でないと、六方晶のＩＴＯ粉末が生成するとともに、凝集晶以外に微細な球状のＩＴＯ粉末も生成し、十分な透明性と導電性を有する膜が得られない。
　なお、ｐＨ調整工程及び洗浄工程における温度は、特に限定されず常温でよい。
＜焼成工程＞
　洗浄工程で洗浄されたインジウム錫水酸化物をろ過して取出し、これを乾燥した後、大気中で４００～８００℃で１～６時間焼成する。
　この焼成工程では、インジウム錫水酸化物が酸化してＩＴＯ粉末となる。この場合、水酸化物の脱水が生じる２００～３５０℃の領域における昇温速度を、２００℃／ｈｒ以上とすることで、急速な脱水によって生じた空隙がそのまま残留することにより、凝集晶の状態のＩＴＯ粉末を得ることができる。昇温速度が２００℃／ｈｒ未満であると、脱水により生じた空隙が消えて、凝集晶の状態ではない単純な大粒径の棒状粒子となり、膜の透明性が低下する。
＜改質工程＞
　焼成工程で得られたＩＴＯ粉末を非酸化雰囲気で加熱することでさらに導電性を高くする。具体的には、ＩＴＯ粉末にエタノールを含む表面処理液を含浸させ、非酸化性雰囲気（例えば窒素雰囲気）で加熱処理する。アルコール蒸気を含有した非酸化性雰囲気で加熱処理してもよい。加熱条件としては２５０～８００℃で３０分～６時間とする。
　ＩＴＯ粉末を改質することにより還元され、低抵抗の透明導電性膜を得ることができる。また、この改質工程でアルコールを使うと、ＩＴＯ粉末の有機溶媒への分散性が向上し、膜の透明性も改善される。
［分散液、塗料、透明導電性膜］
　本発明のＩＴＯ粉末は、これを分散媒に分散した分散液または塗料とし、その分散液または塗料を塗布して圧縮することにより透明導電性膜を得ることができる。具体的には、分散液を支持体上に塗布して乾燥させた後、その塗布層を所定の圧力で圧縮することにより、透明性と導電性に優れる透明導電性膜とすることができる。
　この場合、支持体や分散媒は特に限定されるものではない。例えば、支持体としては、ポリエチレンテレフタレート（ＰＥＴ）、ポリエチレン、ポリプロピレン等の樹脂フィルムを用いることができる。分散媒としては、メタノール、エタノール等のアルコール類を好適に用いることができる。ＩＴＯ粉末を分散媒に分散する場合、均一に分散するため超音波振動をかけながら分散するとよい。
　このＩＴＯ粉末を分散させた分散液を支持体上に塗布する方法としては、特に限定されるものではなく、バーコーターなど、塗料の塗布方法として公知の方法を適用することができる。
　支持体に塗布して乾燥させた塗布層を圧縮する場合、ロールプレス、シートプレスいずれも用いることができる。加圧力としては、ロールプレスの場合１０Ｎ／ｍｍ２以上が好ましい。温度は常温でよい。
　ＩＴＯ粉末が棒状凝集晶からなるので、圧縮して膜を形成すると、棒状凝集晶が複雑にからみ合うとともに、その一部が破壊されて隙間を埋めることにより、相互に緊密に密接し、緻密な膜を形成することができる。例えば、膜密度が０．７８ｇ／ｍｌ以上の膜が得られる。この膜の表面に保護層等を積層し、支持体から剥離すれば、透明導電性膜が得られる。
　この透明導電性膜は、棒状凝集晶と、これが破壊されて生じる凝集晶や単一の棒状粒子とからなるＩＴＯ粉末が密接して得られたものであり、良好な透明性と高い導電性を備えた透明導電性膜である。
　以下、本発明の実施例を比較例と共に示す。
　２４％濃度のＩｎＣｌ３水溶液１９２０ｇと５５％濃度のＳｎＣｌ４水溶液１９４ｇとを混合した。この混合水溶液と、アルカリ水溶液として２５％アンモニア水とを２４Ｌの水中に６０分かけてそれぞれ一定量ずつ同時に滴下した。尚、反応液の温度、ｐＨ（滴下初期の不安定時を除く）、滴下開始から終了までの時間（反応時間と表記する）、滴下終了からの熟成の時間（熟成時間と表記する）は表１の通りとした。熟成中の反応液の温度は反応処理時と同じ温度に維持した。原料滴下終了後の水酸化物濃度をＩＣＰ発光分析により測定したところ、表１の通りであった。なお、表１において、比較例８は原料にＳｎＣｌ２を使用した。また、比較例１２は、原料とアルカリ水溶液との反応方法を変えたものであり、反応器に原料を張り込んでおき、その原料にアルカリ水溶液を滴下した。この場合、アルカリ水溶液の滴下終了時点でｐＨが５．５となった。
　以上のように反応させ熟成させた後、ｐＨ調整のためのアルカリ水溶液としてアンモニア水を添加した。添加後所定時間（表１の「アルカリｐＨ調整時間」）内に、洗浄工程に移り、生成した沈殿物をイオン交換水によって傾斜法にて繰り返し洗浄した。上澄み液の電気伝導率が１００μＳ／ｃｍ以下になったところで、沈殿物（Ｉｎ／Ｓｎ共沈水酸化物）を濾別し、１１０℃で一晩乾燥した。乾燥後、焼成する前に水酸化物の塩素濃度をＩＣＰ発光分析により測定したところ、表１の「焼成前のＣｌ濃度」の欄に示す通りであった。その後、大気中５５０℃で３時間焼成した。この場合、２００～３５０℃の温度領域における昇温速度を表１の通りの条件とした。
　得られた凝集体を解砕し、ＩＴＯ粉末約６５０gを得た。
　上記ＩＴＯ粉末４０ｇを、無水エタノールと蒸留水を混合（混合比率はエタノール９５重量部に対して蒸留水５重量部）した表面処理液に入れて含浸させた後、ガラスシャーレに入れて窒素ガス雰囲気下、３３０℃にて２時間加熱処理した。この表面の改質処理を１回ずつ１０バッチ実施し、合計約４００ｇの改質処理ＩＴＯ粉末を得た。なお、処理バッチ毎の特性差をなくすため、ＩＴＯ粉末が良く冷えてからビニール袋に入れて、改質処理したＩＴＯ粉末が均一になるよう混合した。
Figure JPOXMLDOC01-appb-T000001
　このようにして製造したＩＴＯ粉末の結晶系、形状、短軸径、長軸径、かさ密度、比表面積は以下の方法によって測定した。
〔結晶系〕
　Ｘ線回折装置（リガク社製ＭｉｎｉＦｌｅｘＩＩ）にて、３２．７°のピーク強度（六方晶）と３０．６°のピーク強度（立方晶）との比（３２．７°のピーク強度／３０．６°のピーク強度）を測定した。
〔形状・短軸径・長軸径〕
　透過型電子顕微鏡（ＴＥＭ）によって粉体の形状を把握し、棒状凝集晶の有無、及び棒状凝集晶以外の単粒子（棒状粒子、球状粒子、立方体等）の存在を確認した。また、一次粒子及び棒状凝集晶の短軸径および長軸径は、２０万倍の倍率で観察視野内の全粒子を測定して、それぞれの平均値を求めた。
〔かさ密度〕
　ＪＩＳ　Ｋ　５１０１－１２－１にて求めた。
〔比表面積〕
　ＢＥＴ比表面積は、島津製作所社製の装置(フローソーブＩＩＩ　２３１０)を用いて測定した。
　これらの測定結果を表２に示す。
Figure JPOXMLDOC01-appb-T000002
　図１は実施例１のＩＴＯ粉末の顕微鏡写真であり、微細な一次粒子が結合して棒状の凝集晶となっていることがわかる。
　これに対して、図２は比較例７のＩＴＯ粉末の顕微鏡写真であり、棒状の凝集晶とならず、棒状の単体粒子が生成されている。
　次いで、ＩＴＯ粉末をエタノール中で超音波振動を１０分間付与することにより分散させ、分散した液を、予め重量を測定したＰＥＴフィルム上にバーコーターＮＯ．１６で成膜した。７０℃で１分乾燥後、ＰＥＴフィルムの重量を測定し、単位面積当りの膜重量を算出した。次に、直径５０ｍｍの金型により、ＩＴＯ粉末を塗布したＰＥＴフィルムを３４ＭＰａの圧力にて荷重した。出来たＩＴＯフィルムの膜厚、表面抵抗率、ヘーズ、凝集晶の破壊割合を下記にて求めた。
〔膜の密度〕
　成膜前後のフィルムの単位面積当りの重量差を測定するとともに、ＰＥＴフィルムからＩＴＯ膜の一部を剥離して、レーザ顕微鏡にてＰＥＴフィルム上のＩＴＯ膜の膜厚（ＰＥＴフィルム表面からの高さ）を測定し、膜密度を算出した。
〔膜の凝集晶破壊割合〕
　膜に成形する前（圧力をかける前）の状態と、圧力をかけて成膜した後の状態とをそれぞれＳＥＭにて５万倍で観察した写真から、面積５ｃｍ２の観察視野内の破壊された凝集晶と破壊されていない凝集晶の個数を数え、数値化した。
〔膜の透明度〕
　スガ試験機社製ヘーズメーターＨＺ－２を用いてヘーズ値を測定した。
〔膜の表面抵抗率〕
　三菱化学アナリティック社製ロレスタＭＣＰ－Ｔ６１０にて測定した。
　これらの測定結果を表３に示す。表３中、「棒状凝集晶の破壊割合」の欄で、「＊」印は球状もしくは立方体の粒子が混在しているため、棒状凝集晶が不明であったことを示し、「＊＊」は棒状凝集晶が存在しないことを示す。
Figure JPOXMLDOC01-appb-T000003
　表３から明らかなように、本実施例のＩＴＯ粉末は、棒状の凝集晶であることから、比表面積が大きい割にかさ密度が大きく、その結果、膜にしたときの抵抗率が低く、高い導電性を有する膜が得られている。また、透明性にも優れている。さらに、膜の密度も高く、棒状凝集晶が緻密に充填された膜となっていることがわかる。特に、棒状凝集晶であることから、これらが複雑に絡み合うとともに、膜形成時の圧力によって一部破壊され、その破壊された粒子が隙間を埋めて、緻密な膜を形成するものと考えられる。したがって、このＩＴＯ粉末は、膜に成形するときの圧縮性に優れ、高密度かつ高強度の膜を形成することができる。
　これに対して、比較例１のＩＴＯ粉末は、粒子サイズが大きくなり、比表面積が小さくなって膜の透明性が悪くなっている。
比較例２は、六方晶が混入し、膜の導電性が悪化している。
比較例３は、棒状凝集晶として生成されずに球状や立方体の粒子となり、膜としての抵抗率が高く、透明性も低い。
　比較例４は、棒状粒子の生成がなされず、一部、球状もしくは立方体状のＩＴＯ粉末が存在し、膜としての透明性が低下した。
　比較例５は、粒子サイズが大きくなり、比表面積が小さく、膜としての透明性が低い。
　比較例７は、棒状凝集晶とならずに、棒状の単粒子として成長しており、かさ密度、比表面積とも小さく、膜の抵抗率が高い。比較例８は、棒状凝集晶にならず、球状や立方体の粒子が生成された。その結果、かさ密度が低く、膜の透明性が悪くなった。
　比較例９は、ＩＴＯ粉末の粒子サイズが大きくなり、比表面積が小さく、膜としての透明性が低い。
　比較例１０は、六方晶が混在し、膜の導電性が悪くなっている。
　比較例１１は、棒状凝集晶に球状粒子が混在し、膜の透明性、導電性が悪くなっている。
　比較例１２は、粒子サイズが大きく、比表面積が小さいため、膜としての透明性が低い。
　比較例１３は、六方晶が混入しているとともに、棒状凝集晶ではない棒状あるいは球状の単粒子のＩＴＯ粉末となった。このため、膜の透明性が悪くなっている。
　本発明の酸化錫インジウム粉末は、これを溶媒に分散させた分散液または塗料の形態とし、タッチパネル等の透明導電膜の電極を形成する際の材料として好適に利用することができる。

Claims (5)

  1. 　Ｘ線回折測定において立方晶のみからなり、長軸４０ｎｍ以下の複数の一次粒子が棒状に凝集して結合した凝集晶であり、長軸が９０ｎｍ以上１６５ｎｍ以下、短軸が３０ｎｍ以上６０ｎｍ以下とされ、ＢＥＴ法による比表面積が３０．０ｍ２／ｇ以上、かさ密度が０．６８ｇ／ｃｍ３以上であることを特徴とする酸化錫インジウム粉末。
  2. 　請求項１記載の酸化錫インジウム粉末を溶媒に分散させてなる分散液または塗料。
  3. 　請求項１記載の酸化錫インジウム粉末を含有する透明導電性膜。
  4. 　請求項１記載の酸化錫インジウム粉末の製造方法であって、水に、塩化インジウムおよび四塩化錫を混合した混合水溶液と、アルカリ水溶液とを投入して、塩化インジウムおよび四塩化錫とアルカリとをｐＨ５．５～６．５で反応させて、その反応液中に水酸化物を生成させる反応工程と、反応工程の後、反応液にアルカリ水溶液を添加して、ｐＨ８～１０に調整するｐＨ調整工程と、ｐＨ調整工程におけるアルカリ水溶液の添加開始から５分以内に実施され、水酸化物を洗浄する洗浄工程と、洗浄工程で得られた水酸化物の粉末を焼成して酸化錫インジウム粉末を得る焼成工程とを備えることを特徴とする酸化錫インジウム粉末の製造方法。
  5. 　前記焼成工程で得られた酸化錫インジウム粉末を非酸化雰囲気で加熱処理して表面改質する改質工程をさらに備えることを特徴とする請求項４記載の酸化錫インジウム粉末の製造方法。
PCT/JP2014/060545 2013-04-12 2014-04-11 酸化錫インジウム粉末、その分散液または塗料、透明導電性膜、及び酸化錫インジウム粉末の製造方法 WO2014168245A1 (ja)