WO2014116309A1 - Delayed gelling agents - Google Patents
Delayed gelling agents Download PDFInfo
- Publication number
- WO2014116309A1 WO2014116309A1 PCT/US2013/066288 US2013066288W WO2014116309A1 WO 2014116309 A1 WO2014116309 A1 WO 2014116309A1 US 2013066288 W US2013066288 W US 2013066288W WO 2014116309 A1 WO2014116309 A1 WO 2014116309A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- composition
- nanoparticle
- zirconium
- sodium
- less
- Prior art date
Abstract
Description
Claims