WO2014100320A1 - Method for preparing fine powders for use in selective laser sintering processes - Google Patents
Method for preparing fine powders for use in selective laser sintering processes Download PDFInfo
- Publication number
- WO2014100320A1 WO2014100320A1 PCT/US2013/076361 US2013076361W WO2014100320A1 WO 2014100320 A1 WO2014100320 A1 WO 2014100320A1 US 2013076361 W US2013076361 W US 2013076361W WO 2014100320 A1 WO2014100320 A1 WO 2014100320A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- particles
- feedstock
- polyaryletherketone
- microns
- particle size
- Prior art date
Abstract
A process for preparing a feedstock having polyaryletherketone particles for using in selective laser sintering. The process includes the steps of determining a particle size distribution of the polyaryletherketone particles in the feedstock based on a number of particles corresponding to each of a plurality of particle size ranges to obtain a particle size distribution determination. The process further includes the step of reducing the number of particles in the feedstock corresponding to one or more size ranges having a depressed melting temperature relative to the average melting temperature of the polyaryletherketone particles in the feedstock based on the particle size distribution determination.
Description
TITLE OF INVENTION
METHOD FOR PREPARING FINE POWDERS FOR USE IN SELECTIVE LASER SINTERING
PROCESSES
FIELD OF THE INVENTION
[0001] The present invention relates to an additive manufacturing process. More specifically, the present invention relates to a method of preparing polymer powders for use in selective laser sintering.
BACKGROUND OF THE INVENTION
[0002] The use of additive manufacturing processes, sometimes referred to as 3D printing, has become more popular in recent years.
Selective laser sintering (SLS) is an additive manufacturing process that uses a high power laser (for example, a carbon dioxide laser) to fuse small particles of plastic, metal (direct metal laser sintering), ceramic, or glass powders into a mass having a desired three-dimensional shape. The laser is controlled to selectively fuse the powdered layer by scanning portions of the cross-section corresponding to a three-dimensional digital description of the part on the surface of a powder bed. After each cross-section is scanned, the powder bed is lowered by one layer thickness, the bed is recoated with a new layer of powder, and the bed is scanned again by the laser. The process is repeated until the desired three-dimensional shape is achieved.
[0003] An example of a material used for feedstock for SLS is polyaryletherketones (PAEK). Parts that have been manufactured from PAEK powder or PAEK granulates are characterized by a low flammability, a good biocompatibility as well as a high resistance against hydrolysis and radiation. It is the thermal resistance also at elevated temperatures as well as the
chemical resistance that distinguishes PAEK powders from ordinary plastic powders. A PAEK polymer powder may be a powder from the group consisting of polyetheretherketone (PEEK), polyetherketoneketone (PEKK), polyetherketone (PEK), polyetheretherketoneketone (PEEKK) or
polyetherketoneetherketoneketone (PEKEKK).
[0004] In preparing powder materials, also referred to as feedstock, for the SLS process, it is known to use particle size distributions (PSD) of the feedstock to ensure that a uniform part is made and to ensure the SLS machine runs without interruption. The PSD of a feedstock powder is used to illustrate the mass of particles in a feedstock having a certain size range relative to the total mass of the feedstock. The PSD of a particular lot of powder can be plotted, for example, on a histogram to illustrate the
distribution relative amount of different size particles by mass.
[0005] A disadvantage of SLS feedstock, and more specifically PAEK feedstock, is that it becomes more difficult to control the quality of the SLS process when a diameter of the particles in the feedstock is small, for example, less than 30 microns. It has been found that such particles having a smaller diameter typically melt at a depressed temperature compared particles having a larger diameter. Larger diameter particles, typically greater than 30 microns, melt, or fuze, at a specific temperature, sometimes referred to as a glazing point. At the glazing point, a visible change in the powder indicates the onset of fusion (also referred to as auto-sintering) of the powder. Smaller particles, for example having a diameter of less than 30 microns, can melt from 5 to 50 degrees Celsius below the glazing point. This is a
disadvantage because such particles begin melting prematurely during the recoating process, for example before and while they are being dispersed on the layer-wise bed prior to laser sintering. The premature melting may cause pilling, sticking, and other forms of fouling in steps of the SLS process in
which smooth flowing powder are preferred and expected, and make built parts more susceptible to structural failure.
[0006] It is known to overcome the aforementioned disadvantages associated with premature melting of the feedstock by controlling the lower size limit of particles in the feedstock. This control can be achieved by setting and maintaining a particle size cut-off. Typically with such cutoff methods, particles below the cutoff diameter, for example 30 microns, are excluded from the feedstock or are reduced from the feedstock. A disadvantage of this solution is that it reduces the yield of the powder grinding operation because it excludes particles below a certain size. This is a disadvantage, especially when the feedstock is relatively expensive to procure. A further disadvantage of this known solution is that the aforementioned problems may continue to persist even after the cut-off.
[0007] What is desired therefore is a method for overcoming the problems associated with the prior art.
SUMMARY OF THE INVENTION
[0008] The present invention resides in one aspect in a process for preparing a feedstock for selective laser sintering. The feedstock comprises polyaryletherketone particles. The process includes the steps of determining a particle size distribution of the polyaryletherketones particles in the feedstock based on a number of particles corresponding to each of a plurality of particle size ranges to obtain a particle size distribution determination. The process further includes the step of reducing the number of particles in the feedstock corresponding to one or more size ranges having a depressed melting temperature relative to the average melting temperature of the
polyaryletherketone particles in the feedstock based on the particle size distribution determination.
[0009] In another embodiment, the depressed temperature is 5 or more degrees Celsius below the average melting temperature of the
polyaryletherketone particles in the feedstock.
[0010] In yet a further embodiment of the present invention, the depressed temperature is between 5 and 50 degrees Celsius below the average melting temperature of the polyaryletherketone particles in the feedstock.
[0011] In yet another embodiment of the present invention, the process includes the step of reducing the number of particles in the feedstock corresponding to any of the size ranges having particle diameters of 10 microns or less.
[0012] In yet another embodiment of the present invention, the process includes the step of reducing the number of particles in the feedstock corresponding to any of the size ranges having particle diameters of 10 microns or less.
[0013] In yet another embodiment of the present invention, the process includes the step of reducing the number of particles in the feedstock corresponding to any of the size ranges having particle diameters of 10 microns or less.
[0014] In yet another embodiment of the present invention, the process includes the step of reducing the number of particles in the feedstock corresponding to any of the size ranges having particle diameters of 10 microns or less.
[0015] In yet another embodiment of the present invention, the process includes the step of reducing the number of particles in the feedstock
corresponding to any of the size ranges having particle diameters of 10 microns or less.
[0016] In yet a further embodiment of the present invention, the feedstock consists essentially of polyetherketoneketone.
[0017] The present invention resides in yet another aspect in a process for preparing a polymer for selective laser sintering. The polymer includes one or more polyaryletherketones. The process includes the step of pulverizing the one or more polyaryletherketones to form a powder comprising
polyaryletherketone particles. The process includes the further step of determining a particle size distribution of the polyaryletherketone particles based on a number of particles. The process further includes the steps of creating a feedstock from the polyaryletherketone particles and limiting the number of particles in the feedstock based on the particle size distribution determination.
[0018] In one embodiment of the disclosed invention, the process includes the further step of limiting the number of particles in the feedstock having a depressed melting temperature relative to the average melting temperature of the polyaryletherketone particles.
[0019] In yet a further embodiment of the present invention, the depressed temperature is between 5 and 50 degrees Celsius below the average melting temperature of the polyaryletherketone particles.
[0020] In yet another embodiment of the present invention, the process includes the step of limiting the number of particles in the feedstock corresponding to one or more size ranges in the particle size distribution having particle diameters of 10 microns or less.
[0021] In yet another embodiment of the present invention, the process includes in the step of limiting the number of particles in the feedstock corresponding to one or more size ranges in the particle size distribution having particle diameters of 15 microns or less.
[0022] In yet another embodiment of the present invention, the process includes in the step of limiting the number of particles in the feedstock corresponding to one or more size ranges in the particle size distribution having particle diameters of 20 microns or less.
[0023] In yet another embodiment of the present invention, the process includes in the step of limiting the number of particles in the feedstock corresponding to one or more size ranges in the particle size distribution having particle diameters of 25 microns or less.
[0024] In yet another embodiment of the present invention, the process includes in the step of limiting the number of particles in the feedstock corresponding to one or more size ranges in the particle size distribution having particle diameters of 30 microns or less.
[0025] In yet a further embodiment of the present invention, the feedstock consists essentially of polyetherketoneketone.
BRIEF DESCRIPTION OF THE DRAWINGS
[0026] FIG. 1 is a chart illustrating a particle size distribution of a first feedstock and a second feedstock.
DETAILED DESCRIPTION OF THE INVENTION
[0027] The inventors have discovered that the known procedure for preparing polyaryletherketone feedstock to inhibit premature melting, namely
excluding or linniting undesirably sized particles from the feedstock based on a PSD using relative mass or relative volume, obscures the far more important characteristic of the powders that causes the premature melting. The inventors have discovered that the count, or number, of the small particles in the feedstock is a more significant factor in premature melting of the particles during SLS than is the relative mass of the small particles, or the relative volume of the small particles. The relative number of small particles, specifically those less than 30 microns, and more specifically those less than 15 microns, is far more significant than the relative mass or relative volume of such small particles in preparing a feedstock that inhibits premature melting during SLS.
[0028] The collective mass of such fine particles is relatively small compared to the overall mass of the feedstock. Similarly, the collective volume of such fine particles is relatively small compared to the overall volume of the feedstock. As a result, the existence of such small particles is minimized, or becomes statistically irrelevant, when a feedstock is analyzed using a PSD determination based on relative mass or relative volume. The inventors have discovered, however, that by analyzing a PSD by relative particle number it is possible understand the distribution of the number of small particles, and prepare a feedstock which addresses such distribution to inhibit premature melting during SLS.
[0029] The count of small particles below a determined critical threshold can be enormous when compared to the overcall particle count of the feedstock. The small particles can contribute largely to the
aforementioned fouling behaviors by creating an enormous number of sticking points throughout the powder bed during the SLS process. The count of small particle and the effects thereof are not accounted for and are not understood with the known feedstock processing methods.
[0030] To inhibit premature melt, it is currently known to reduce the weight or volume of particles below a certain diameter. For example, using known methods, the mass of particles having a diameter less than a critical size, for example 30 microns, are reduced relative to the overall mass of the sample. Typically, however, the reduction in the mass of particles below the critical value would not fully solve the problem associated with premature particle melt because it does not address the root cause of the problem, namely, controlling the number of small particles relative to the overall number of particles of the feedstock.
[0031] Therefore, because the problem of premature melting tended to persist despite best efforts to account for it, it was known to increase the critical size, for example to 35 of 40 microns, or to further reduce the mass or volume of particles below the critical size. While such actions may inhibit some of the disadvantages associated with premature particle melt, they also reduce the yield of the powder grinding operation because additional particles are excluded from the feedstock. This exclusion can significantly impact the economics of the SLS process. This is especially true when using a relatively expensive feedstock such as polyetherketoneketone.
[0032] The disadvantages associated with the known methods are overcome by employing a PSD based on the relative number of particles. By determining a particle size distribution of a feedstock, for example one comprising polyaryletherketone particles, based on a number of particles corresponding to each of a plurality of particle size ranges it is possible to more accurately identify the source of premature particle melting and adjust the feedstock accordingly to inhibit premature particle melting during SLS.
[0033] In one embodiment in accordance with the present invention a feedstock is prepared from one or more polymers selected from the
polyaryletherketone family. The one or more polyaryletherketones are
pulverized to form a powder comprising polyaryletherketone particles. It should be understood that the polyaryletherketones may be pulverized using any method or machine known to a person having ordinary skill in the art. In this embodiment, the pulverized particles vary in size, typically from a diameter of 8 microns to a diameter of more than 100 microns. It will be understood by a person of ordinary skill in the art that although the term diameter is used in reference to the size of the particles, particles are not limited to a spheroid as their shape may vary.
[0034] A particle size distribution of the polyaryletherketone particles based on a number of particles is determined. The determination may be made using any technique known to a person of ordinary skill in the art. Next, a feedstock for SLS is assembled from the polyaryletherketone particles using the results of the particle size distribution determination. The results of the particle size distribution determination by relative particle are used to limit the number of small particles, i.e. below a selected size threshold, that are included in the feedstock, thereby inhibiting premature melting during the SLS process.
[0035] In some embodiments of the present invention, the number of particles in the feedstock having a depressed melting temperature relative to the average melting temperature of the polyaryletherketone particles is limited. In some embodiments, the depressed temperature is between 5 and 50 degrees Celsius below average melting temperature of the
polyaryletherketone particles. In some embodiments, the step of limiting the number of particles removes a portion of the particles having a diameters of 10 microns or less. In other embodiments, the removal of particles is limited to diameters of 15 microns or less.
[0036] In reference to FIG. 1 , a chart 100 illustrating the difference between a first feedstock and a second feedstock is shown. The first
feedstock was assembled based on the results of a PSD relative mass determination. The second feedstock was assembled based on a PSD relative particle count determination. The first feedstock and the second feedstock were subsequently analyzed to determine a PSD based on relative particle count. The chart 100 shows the two PSD determinations 130, 140, each based on particle count. The x-axis 1 10 of the chart corresponds to the particle diameter and is shown in logarithmic scale. The y-axis 120 of the chart 100 corresponds to the percentage of particles in a specific size range relative to the overall number of particles.
[0037] The first PSD 130 corresponds to the first feedstock. The first feedstock was assembled in accordance with the prior art using a PSD based on relative mass so as to inhibit premature melting. The first PSD 130 is illustrated by gray rectangles. The second PSD 140 corresponds to the second feedstock. The second feedstock was assembled in accordance with the present invention using a PSD based on relative particle count so as to inhibit premature melting. The second PSD 140 is illustrated by black rectangles.
[0038] In reference to FIG. 1 , it is evident that first feedstock and the second feedstock each have a center hump. However, at the far left of the chart 100, representing the smaller particles in each respective feedstock, the number of fine particles is much higher for the first feedstock as compared to the second feedstock. This is because the first feedstock was assembled based on mass sum PSD and the small particles contribute very little to this, and therefore were not accounted for in preparation of the second lot. By using the PSD based on particle number 140, it is possible to account for the small particles and adjust the feedstock accordingly. In this manner, it is possible to accurately account for the particles that significantly impact premature melting and adjust the feedstock accordingly, while at the same time increasing the overall yield of the process.
[0039] Although the present invention has been disclosed and described with reference to certain embodiments thereof, it should be noted that other variations and modifications may be made, and it is intended that the following claims cover the variations and modifications within the true scope of the invention.
Claims
1 . A process for preparing a feedstock for selective laser sintering comprising polyaryletherketone particles, comprising the steps of determining a particle size distribution of the polyaryletherketone particles in the feedstock based on a number of particles corresponding to each of a plurality of particle size ranges, and reducing the number of particles in the feedstock
corresponding to one or more size ranges having a depressed melting temperature relative to the average melting temperature of the
polyaryletherketone particles in the feedstock based on the particle size distribution determination.
2. The process of claim 1 wherein the depressed temperature is 5 or more degrees Celsius below the average melting temperature of the polyaryletherketone particles in the feedstock.
3. The process of claim 2 wherein the depressed temperature is between 5 and 50 degrees Celsius below the average melting temperature of the polyaryletherketone particles in the feedstock.
4. The process of claim 1 further comprising the step of reducing the number of particles in the feedstock corresponding to any of the size ranges including particles diameters of 10 microns or less.
5. The process of claim 1 further comprising the step of reducing the number of particles in the feedstock corresponding to any of the size ranges including particles diameters of 15 microns or less.
6. The process of claim 1 further comprising the step of reducing the number of particles in the feedstock corresponding to any of the size ranges including particles diameters of 20 microns or less.
7. The process of claim 1 further comprising the step of reducing the number of particles in the feedstock corresponding to any of the size ranges including particles diameters of 25 microns or less.
8. The process of claim 1 further comprising the step of reducing the number of particles in the feedstock corresponding to any of the size ranges including particles diameters of 30 microns or less.
9. The process of claim 1 wherein the feedstock consists essentially of polyetherketoneketone.
10. The process of claim 9 wherein the depressed temperature is 5 or more degrees Celsius below the average melting temperature of the polyaryletherketone particles in the feedstock.
1 1 . A process for preparing a polymer for selective laser sintering comprising one or more polyaryletherketones, comprising the steps of pulverizing the one or more polyaryletherketones to form a powder comprising polyaryletherketone particles, determining a particle size distribution of the polyaryletherketone particles based on a number of particles, creating a feedstock from the polyaryletherketone particles, limiting the number of particles in the feedstock based on the particle size distribution determination.
12. The process of claim 1 1 further comprising the step of limiting the number of particles in the feedstock having a depressed melting temperature relative to the average melting temperature of the polyaryletherketone particles.
13. The process of claim 12 wherein the depressed temperature is between 5 and 50 degrees Celsius below average melting temperature of the polyaryletherketone particles.
14. The process of claim 1 1 further comprising the step of limiting the number of particles in the feedstock corresponding to one or more size ranges in the particle size distribution having particle diameters of 10 microns or less.
15. The process of claim 1 1 further comprising the step of limiting the number of particles in the feedstock corresponding to one or more size ranges in the particle size distribution having particle diameters of 15 microns or less.
16. The process of claim 1 1 further comprising the step of limiting the number of particles in the feedstock corresponding to one or more size ranges in the particle size distribution having particle diameters of 20 microns or less.
17. The process of claim 1 1 further comprising the step of limiting the number of particles in the feedstock corresponding to one or more size ranges in the particle size distribution having particle diameters of 25 microns or less.
18. The process of claim 1 1 further comprising the step of limiting the number of particles in the feedstock corresponding to one or more size ranges in the particle size distribution having particle diameters of 30 microns or less.
19. The process of claim 18 wherein the feedstock consists essentially of polyetherketoneketone.
20. The process of claim 19 wherein the depressed temperature is 5 or more degrees Celsius below the average melting temperature of the polyaryletherketone particles.