WO2014003800A1

WO2014003800A1 - Fracturing fluids and methods for treating- hydrocarbonbearing formations

Info

Publication number: WO2014003800A1
Application number: PCT/US2012/046460
Authority: WO
Inventors: Hong Sun; Frances Debenedictis; Jia Zhou; Scott Nelson; Tom N. ROYCE; Qi Qu
Original assignee: Baker Hughes Incorporated
Priority date: 2012-06-29
Filing date: 2012-07-12
Publication date: 2014-01-03
Also published as: IN2014DN11165A; EP2867458A4; AU2012383503A1; CA2877676A1; CA2877676C; CN104508239A; AU2012383503B2; US9676995B2; US20140000890A1; EP2867458A1; CO7160105A2

Abstract

Disclosed herein is a fracturing fluid comprising a carrier fluid; a polymer that is soluble in the carrier fluid; the polymer being a synthetic polymer; the synthetic polymer being operative to increase the viscosity of the carrier fluid to about 5 to about 50 centipoise; the fracturing fluid being operative to reduce friction during a downhole fracturing operation and to transport a proppant during the downhole fracturing operation.

Description

FRACTURING FLUIDS AND METHODS FOR TREATING HYDROCARBON- BEARING FORMATIONS

CROSS REFERENCE TO RELATED APPLICATIONS

This application claims the benefit of U.S. Application No. 13/537800, filed on June 29, 2012, which is incorporated herein by reference in its entirety.

BACKGROUND

[0001] Hydraulic fracturing increases fluid (e.g., hydrocarbons, and the like) flow from a subterranean zone by creating new fractures and facilitating connectivity of the existing pores and natural channels contained in the subterranean zone. Hydraulic fracturing is a process by which cracks or fractures in the subterranean zone are created by pumping a fracturing fluid at a pressure that exceeds the parting pressure of the rock. The fracturing fluid creates or enlarges fractures in the subterranean zone and a particulate proppant material suspended in the fracturing fluid may be pumped into the created fracture. This process is also known as "frac-packing". The created fracture continues to grow as more fluid and proppant are introduced into the formation.

[0002] The proppants remain in the fractures in the form of a permeable "pack" that serves to hold open or "prop" the fractures open. After placement of the proppant materials, the fracturing fluid may be "broken" and recovered by adding a breaker or using a delayed breaker system already present in the fracturing fluid to facilitate a reduction in the viscosity of the fracturing fluid. The reduction in fluid viscosity along with fluid leak-off from the created fracture into permeable areas of the formation allows for the fracture to close on the proppants following the treatment. By maintaining the fracture open, the proppants provide a highly conductive pathway for hydrocarbons and/or other formation fluids to flow into the borehole.

[0003] Slickwater fracturing is a type of treatment used in the stimulation of unconventional formations. Due to extremely low formation permeability, fluid leak-off is normally not of concern. During the slickwater hydraulic fracturing process, the pumping rate is generally very high to help facilitate the placement of proppants into the formation in conjunction with the use of the low viscosity fluid. At such fluid velocities the proppants in the fracturing fluids can be very abrasive, leading to reduced service life for fracturing equipment. In addition, friction between various components of the fracturing equipment can produce wear of the equipment. It is therefore desirable to reduce the wear on the equipment during fracturing. Guar is often used to increase the viscosity in fracturing fluids to reduce the amount of wear. Large amounts of guar in the form of linear polymers are employed for this purpose.

[0004] As a naturally occurring material, guar is a limited natural resource, the demand for which has increased greatly in recent years. In addition to significant supply limitations, guar-based fracturing fluids are also limited by other significant disadvantages, including but not limited to, the hydration limitations of the guar polymer, formation damage, i.e., undesirable coating of proppant materials and/or formation surfaces with the guar polymer or residue, and instability of the guar polymer at elevated temperatures in certain types of fracturing applications.

[0005] It is therefore desirable to provide an alternative to commercially available guar-based fracturing fluids, which solves one or more of the above problems associated with these guar-based fracturing fluids.

SUMMARY OF THE DISCLOSURE

[0006] Disclosed herein is a fracturing fluid comprising a carrier fluid; a polymer that is soluble in the carrier fluid; the polymer being a synthetic polymer; and the synthetic polymer being operative to increase the viscosity of the carrier fluid to about 5 to about 50 centipoise; the fracturing fluid being operative to reduce friction during a downhole fracturing operation and to transport a proppant during the downhole fracturing operation.

[0007] Disclosed herein too is a method for treating a hydrocarbon-bearing formation comprising blending a carrier fluid with a polymer to form a fracturing fluid, the fracturing fluid having a viscosity of about 5 to about 50 centipoise; the polymer being a synthetic polymer; and discharging the fracturing fluid into a downhole fracture in the hydrocarbon- bearing formation, wherein the fracturing fluid is operative to reduce friction during a hydrocarbon-bearing treatment operation.

BRIEF DESCRIPTION OF THE DRAWINGS

[0008] For a detailed understanding of the present disclosure, references should be made to the following detailed description, taken in conjunction with the accompanying drawings in which like elements have generally been designated with like numerals and wherein: [0009] Figure 1 is a graph depicting the dynamic hydration viscosity versus time for a) guar and b) the synthetic polymer at different concentrations in water;

[0010] Figure 2 is a graph depicting the dynamic hydration viscosity at temperatures of 45°F and 80°F versus time for the synthetic polymer in water;

[0011] Figure 3 is a graph depicting the effective permeability of a simulated fracture surface when contacted with a fracturing fluid that contains the synthetic polymer; and

[0012] Figure 4 is a graph depicting the effective permeability of a simulated fracture surface when contacted with a comparative fracturing fluid that contains the guar.

DESCRIPTION OF EMBODIMENTS

[0013] Slickwater fracturing is a type of treatment used in the stimulation of unconventional formations. Due to extremely low formation permeability, fluid leak-off is normally not of concern, and therefore low viscosity fluids can be used for slickwater fracturing. During the slickwater fracturing process, the pumping rate is generally very high to help prevent settlement of the proppants in the fluid. When pumping at such a high rate or velocity, there is a high frictional pressure generated during the fluid flow in the surface pipes as well as inside the borehole. A high molecular weight synthetic polymer is added to the slickwater fracturing fluid as a friction reducer to reduce such fluid flow friction. The concentration of the synthetic polymer friction reducer is controlled such that the fluid viscosity is less than 2 centipoise (cP). Higher concentration of the friction reducing polymer to lead to viscosity higher than 3 centipoise often resulting in increased friction which defies the purpose of using a friction reducer in slickwater fracturing applications. At such fluid velocities the proppants in the fracturing fluids can be very abrasive, leading to reduced service life for fracturing equipment. In addition, friction between various components of the fracturing equipment can produce wear of the equipment. Increasing the viscosity of the fracturing fluid by the addition of a polymer, even at relatively low viscosities, helps to make it possible to pump the fracturing fluid with reduced proppant settling and thus to lessen this abrasive effect and consequently to reduce friction and equipment wear.

[0014] Disclosed herein is a fracturing fluid that comprises a polymer and a carrier fluid. In one embodiment, the polymer is a synthetic polymer (i.e., it is a man-made polymer) and can rapidly dissolve in the carrier fluid thereby increasing the viscosity of the carrier fluid so as to reduce friction between the various components of fracturing equipment used in the hydraulic fracturing process. [0015] In an exemplary embodiment, the fracturing fluid primarily reduces friction between components of the fracturing equipment during an early stage as well as during subsequent stages of dissolution of the polymer in the carrier fluid. It also prevents the proppants from settling out of solution (phase separating) during subsequent stages of dissolution of the polymer in the carrier fluid. The ability of the polymer to rapidly dissolve into the carrier fluid minimizes the use of pre-dissolution procedures and hydration equipment, thus reducing capital costs and maintenance costs. This rapid dissolution ability also permits the carrier fluid to transport proppants downhole while permitting them to remain slurried in the carrier fluid (i.e., with reduced settling or falling out of solution) while it is being transported to the fracture. In an exemplary embodiment, the fracturing fluid reaches its maximum viscosity within 10 to 40 seconds after introduction of the polymer into the carrier fluid, which allows slower settling of proppant within the fluids at lower pumping rate, and permits to reduce friction between the various components of the fracturing equipment.

[0016] The polymer is soluble in a carrier fluid, for example, an aqueous medium such as water or slickwater to form the fracturing fluid. In an exemplary embodiment, the polymer is an organic water-soluble synthetic polymer (i.e., it is a polymer that is man-made). In addition to the synthetic polymer, the polymer may comprise a naturally occurring polymer. A "naturally occurring" polymer is one that is derived from a living being such as an animal, a plant, a microorganism, or the like. The polymer can therefore comprise a naturally occurring polymer so long as it is blended with or copolymerized with the synthetic polymer.

[0017] In one embodiment, the polymer also comprises a labile group that can be decomposed upon activation. The decomposition of the labile group permits a reduction in the viscosity of the fracturing fluid and also permits its removal from the fracture after a conductive path is established through the proppants in the fracture. The conductive path permits the extraction of hydrocarbons from the fracture.

[0018] The polymer can comprise a blend of polymers, a copolymer, a terpolymer, an oligomer, a homopolymer, a block copolymer, an alternating block copolymer, a random copolymer, a random block copolymer, a graft copolymer, a star block copolymer, a dendrimer, an ionomer, a terpolymer, an elastomer, a polyelectrolyte, or the like, or a combination comprising at least one of the foregoing polymers. [0019] In one embodiment, the polymer may be a linear polymer, a branched polymer or a crosslinked polymer. In another embodiment, the polymer can comprise a blend of two or more synthetic polymers or a copolymer of two or more synthetic polymers. For example, the polymer can comprise a first synthetic polymer and a second synthetic polymer that are blended together or are that are copolymerized together. The copolymerization may involve covalent bonding and/or ionic bonding. In one embodiment, the first synthetic polymer is hydrophilic, while the second synthetic polymer is hydrophobic. In yet another embodiment, the polymer may comprise a copolymer of a synthetic polymer and a naturally occurring polymer, where the naturally occurring polymer can be either hydrophilic or hydrophobic.

[0020] In one embodiment, the polymer is a water soluble polymer. Examples of the water soluble polymer are polyacrylates, polyacrylamides, polyvinylacetates, polyvinyl acetamides, polyvinyl alcohols, neutralized and un-neutralized polymeric acids (e.g., neutralized and un-neutralized polyacrylics acids, neutralized and un-neutralized polysulfonic acids, neutralized and un-neutralized polystyrene sulfonic acids, or the like) polydiallyl dimethyl ammonium chlorides, poly(l -glycerol methacrylate)s, poly(2-dimethylaminoethyl methacrylate)s, poly(2-ethyl-2-oxazoline), poly(2-hydroxyethyl methacrylate/methacrylic acid)s, poly(2-hydroxypropyl methacrylate)s, poly(2-methacryloxyethyltrimethylammonium halide)s, poly(2-vinyl-l-methylpyridinium halide)s, poly(2-vinylpyridine N-oxide)s, poly(2- vinylpyridine)s, poly(3-chloro-2-hydroxypropyl-2-methacryloxyethyldimethylammonium chloride)s, or the like, or a combination comprising at least one of the foregoing water soluble polymers.

[0021] In one embodiment, the polymer can comprise one or more of the foregoing water soluble polymers and a synthetic polymer that is hydrophobic so long as the resulting polymer is soluble in the carrier fluid. In an exemplary embodiment, the polymer can comprise one or more of the foregoing water soluble polymers and a synthetic polymer that is hydrophobic so long as the resulting polymer is soluble in an aqueous carrier fluid. The foregoing water soluble polymers can be copolymerized or blended with the hydrophobic synthetic polymer.

[0022] Examples of hydrophobic synthetic polymers are polyacetals, polyolefins, polycarbonates, polystyrenes, polyesters, polyamides, polyamideimides, polyarylates, polyarylsulfones, polyethersulfones, polyphenylene sulfides, polyvinyl chlorides,

polysulfones, polyimides, polyetherimides, polytetrafluoroethylenes, polyetherketones, polyether etherketones, polyether ketone ketones, polybenzoxazoles, polyphthalides, polyacetals, polyanhydrides, polyvinyl ethers, polyvinyl thioethers, polyvinyl ketones, polyvinyl halides, polyvinyl nitriles, polyvinyl esters, polysulfonates, polysulfides, polythioesters, polysulfones, polysulfonamides, polyureas, polyphosphazenes, polysilazanes, polyethylene terephthalate, polybutylene terephthalate, polyurethane, polytetrafluoroethylene, polychlorotrifluoroethylene, polyvinylidene fluoride, polyoxadiazoles,

polybenzothiazinophenothiazines, polybenzothiazoles, polypyrazinoquinoxalines,

polypyromellitimides, polyquinoxalines, polybenzimidazoles, polyoxindoles,

polyoxoisoindolines, polydioxoisoindolines, polytriazines, polypyridazines, polypiperazines, polypyridines, polypiperidines, polytriazoles, polypyrazoles, polypyrrolidines,

polycarboranes, polyoxabicyclononanes, polydibenzofurans, polyphtalides, polyacetals, polyanhydrides, polyvinyl ethers, polyvinyl thioethers, polyvinyl ketones, polyvinyl halides, polyvinyl nitriles, polyvinyl esters, polysulfonates, polysulfides, polythioesters, polysulfones, polysulfonamides, polyureas, polyphosphazenes, polysilazanes, polysiloxanes, polyolefms, or the like, or a combination comprising at least one of the foregoing hydrophobic synthetic polymers.

[0023] As noted above, the polymer can comprise a blend or a copolymer of a synthetic polymer and a naturally occurring polymer. Examples of naturally occurring polymers include polysaccharides, derivatives of polysaccharides (e.g., hydroxyethyl guar (HEG), carboxymethyl guar (CMG), carboxyethyl guar (CEG), carboxymethyl

hydroxypropyl guar (CMHPG), cellulose, cellulose derivatives ((i.e., derivatives of cellulose such as hydroxyethylcellulose (HEC), hydro xypropylcellulose (HPC),

carboxymethylcellulose (CMC), carboxyethylcellulose (CEC), carboxymethyl hydroxyethyl cellulose (CMHEC), carboxymethyl hydroxypropyl cellulose (CMHPC)), karaya, locust bean, pectin, tragacanth, acacia, carrageenan, alginates (e.g., salts of alginate, propylene glycol alginate, and the like), agar, gellan, xanthan, scleroglucan, or the like, or a

combination comprising at least one of the foregoing.

[0024] The polymer comprises a labile group that is operative to facilitate degradation of the polymer upon activation of the labile group. It is desirable for the labile group to be water soluble or otherwise soluble in the carrier fluid. Labile groups include ester groups, amide groups, carbonate groups, azo groups, disulfide groups, orthoester groups, acetal groups, etherester groups, ether groups, silyl groups, phosphazine groups, urethane groups, esteramide groups, etheramide groups, anhydride groups, and any derivative or combination thereof. In some embodiments, the labile links are derived from oligomeric or short chain molecules that include poly(anhydrides), poly(ortho esters), orthoesters, poly(lactic acids), poly(glycolic acids), poly(capro lactones), poly(hydroxybutyrates), polyphosphazenes, poly(carbonates), polyacetals, polyetheresters, polyesteramides, polycyanoacrylates, polyurethanes, polyacrylates, or the like, or a combination comprising at least one of the foregoing oligomeric or short chain molecules. In some embodiments, the labile links may be derived from a hydrophilic polymeric block comprising at least one compound selected from the group consisting of: a poly(alkylene glycol), a poly(alcohol) made by the hydrolysis of polyvinyl acetate), poly( vinyl pyrrolidone), a polysaccharide, a chitin, a chitosan, a protein, a poly(amino acid), a poly(alkylene oxide), a poly(amide), a poly(acid), a polyol, any derivative, copolymer, or combination thereof.

[0025] The polymer can be manufactured via emulsion (or inverse emulsion) polymerization to obtain high molecular weights. In emulsion polymerization or inverse emulsion polymerization, the polymers are suspended in a fluid. In one embodiment, the fluid in which the polymer is suspended is water. The manufacturing and use of the polymer in emulsion form makes it possible to be used as a liquid additive thereby simplifying it use in the fracturing fluid.

[0026] Depending on the particular labile group, the polymer can be degraded by oxidation, reduction, photo-degradation, thermal degradation, hydrolysis, chemical degradation or microbial degradation. The rates at which the polymer degrades is dependent on at least the type of labile group, composition, sequence, length, molecular geometry, molecular weight, stereochemistry, hydrophilicity, hydrophobicity, additives and

environmental conditions such as temperature, presence of moisture, oxygen,

microorganisms, enzymes, pH, and the like.

[0027] The synthetic polymer has a number average molecular weight of about 2,000,000 to about 20,000,000 specifically about 10,000,000 to about 18,000,000 grams per mole.

[0028] In an exemplary embodiment, the polymer (used in the fracturing fluid) is a linear synthetic polymer and comprises a polyacrylamide. A commercially available synthetic polymer is MaxPerm-20^® commercially available from Baker Hughes, Inc.

[0029] In an embodiment, the polymer is employed in an amount of about 0.01 to about 20 percent by weight (hereinafter "wt%"), specifically about 0.1 to about 10 wt%, and more specifically about 0.05 to about 5 wt%, based on the total weight of the fracturing fluid. [0030] In one embodiment, it is desirable for the polymer to be soluble in an aqueous carrier fluid. When the polymer comprises a hydrophobic and a hydrophilic portion, it is desirable for the polymer to have an overall structure that lends itself to solubilization in an aqueous carrier fluid. In order to accomplish this, it is desirable for the polymer to have a solubility parameter that is proximate to that of the carrier fluid so that the polymer can rapidly dissolve in the carrier fluid.

[0031] The selection of the chemical constituents of the polymer used in a given fracturing application is determined, in part, using the solubility parameter of the chemical constituents. The Hildebrand solubility parameter is a numerical parameter, which indicates the relative solvency behavior of a polymer or a combination of polymers in a specific solvent. Here, the solvent is the carrier fluid. The solubility parameter is derived from the cohesive energy density of the polymer. From the heat of vaporization in calories per cubic centimeter of liquid, the cohesive energy density (c) can be derived by the following equation

(1):

c = AH - RT (1)

V_m

where c = cohesive energy density; ΔΗ = heat of vaporization, R = gas constant, T = temperature; and V_m = molar volume. In general terms, when two materials having similar cohesive energy density values, the solubility parameter values are proximate to each other, since the solubility parameter is the square root of the cohesive energy density. Two materials are considered to be miscible with one another when they have similar solubility parameters. By tailoring the polymer structure (i.e., by combining the appropriate amount of a hyrophillic polymer with a hydrophobic polymer) the solubility parameter of the polymer can be tailored to be proximate to that of a particular carrier fluid.

[0032] In metric units, the solubility parameter (δ) can be calculated in calories per cubic centimeter in metric units (cal ^1/2cm^~3/2). In SI units, the solubility parameter is expressed is megapascals (MPa 1/2 ). The conversion of the solubility parameter from SI units to metric units is given by the equation (2):

δ (MPa^1/2) = 2.0455 x δ (cal ^1/2cm^"3/2) (2) [0033] The solubility parameter can be used to predict the solvency of a particular combination of polymers (i.e., copolymers or blends of polymers) in a solvent. A solvent will generally swell the polymer when the solubility parameter is proximate to that of the polymer. The solubility parameter of the polymer can be calculated based on the relative weight fractions of each constituent of the polymer according to equation (3): 0polymer = + W₂5₂ (3) where S_poi_ymei is the solubility parameter of the copolymer or blend of polymers, δι is the solubility parameter the hydrophilic polymer, wi is the weight fraction of the hydrophilic polymer, ¾is the solubility parameter of the hydrophobic polymer and W₂ is the weigh fraction of the hydrophobic polymer. In one embodiment, the solubility parameter of the carrier fluid can be tailored to be proximate to that of the combination of polymers if so desired.

[0034] In an embodiment, the solubility parameter of the polymer is within about 25% of the solubility parameter of the carrier fluid. In another embodiment, the solubility parameter of the synthetic polymer is within about 20% of the solubility parameter of the carrier fluid.

[0035] The carrier fluid solvates the polymer and in addition transports the proppant materials downhole to the hydrocarbon bearing formation. The carrier fluid is a liquid carrier that is generally suitable for use in hydrocarbon (i.e., oil and gas) producing wells. In an embodiment, the carrier fluid is an aqueous solution. In another embodiment, the carrier fluid may be slickwater. Slickwater, for example, has a viscosity of less than 3 centipoise. Water is generally a major component by total weight of the carrier fluid. The water is potable, i.e., drinkable, or non-potable. In an embodiment, the water is brackish or contains other materials that may be present in water found in or near oil fields, e.g., slickwater. In another embodiment, the carrier fluid comprises a salt such as an alkali metal or alkali earth metal salt (e.g., NaC0₃, NaCl, KCl, CaCl₂, and the like) in an amount of from about 0.1 wt% to about 5 wt%, based on the total weight of the carrier fluid. In still yet another

embodiment, the carrier fluid is recycled fracturing fluid water or its residue.

[0036] In an embodiment, the fracturing fluid is a slurry, a gel, an emulsion or foam, e.g., hydrogel. As used herein, the term "emulsion" refers to a mixture of two or more normally immiscible liquids which results in a two-phase colloidal system wherein a liquid dispersed phase is dispersed in a liquid continuous phase. In an embodiment, the fracturing fluid is an oil-in- water emulsion. As used herein, the term "slurry" refers to a thick suspension of solids in a liquid. As used herein, the term "gel" refers to a solid, jelly-like material. In one embodiment, gels are mostly liquid. Their solid-like behavior is the result of the formation of a three-dimensional crosslinked network within the liquid wherein the liquid molecules are dispersed in a discontinuous phase within a solid continuous phase. In one embodiment, the fracturing fluid is a slurry or a gelled slurry. [0037] The fracturing fluid generally comprises the carrier fluid in an amount of about 95 to about 99.9 wt%, based upon the total weight of the fracturing fluid. In an exemplary embodiment, the fracturing fluid comprises the carrier fluid in an amount of about 99 to about 99.5 wt%, based upon the total weight of the fracturing fluid.

[0038] In an embodiment, the fracturing fluid further comprises a proppant, i.e., proppant materials or particulate materials, which is carried into the hydrocarbon formation by the fracturing fluid and remain in the fracture created, thus propping open the fracture when the fracturing pressure is released and the well is put into production. Examples of proppant materials include sand, resin coated sands, plastic or plastic composite such as a thermoplastic or thermosetting composite or a resin or an aggregate containing a binder, walnut shells, sintered bauxite, glass beads, ceramic materials, synthetic organic particles such as, for example, nylon pellets, naturally occurring materials, or the like, or a

combination comprising at least one of the foregoing proppant materials. Suitable proppants further include those set forth in U.S. Patent Publication No. 2007/0209794 and U.S. Patent Publication No. 2007/0209795, herein incorporated by reference.

[0039] The fracturing fluid generally comprises the proppant in an amount of about 0.01 to about 60 wt%, specifically about 0.03 to about 40 wt%, based upon the total weight of the fracturing fluid.

[0040] As noted above, the polymer may be crosslinkable and is sometimes crosslinked during a fracturing operation. In one embodiment, the polymer is co-polymerized with a cross-linkable polymer and the cross-linkable polymer is crosslinked. Crosslinking the fracturing fluid further increases the viscosity of the carrier fluid, traps proppant materials and prevents settling of proppant materials.

[0041] Non-limiting examples of crosslinking agents include crosslinking agents comprising a metal such as boron, titanium, zirconium and/or aluminum complexes.

Crosslinking increases the molecular weight and is particularly desirable in high-temperature wells to avoid degradation, or other undesirable effects of high-temperature applications.

[0042] In an embodiment, the crosslinking agent is included in the fracturing fluid in an amount of from about 0.01 wt% to about 2.0 wt%, specifically about 0.02 wt% to about 1.0 wt% of the fracturing fluid, based on the total weight of the fracturing fluid

[0043] In an embodiment, the fracturing fluid further comprises a breaking agent to activate the labile group and facilitate degradation of the polymer. Breaking agents "break" or diminish the viscosity of the fracturing fluid so that the fracturing fluid is more easily recovered from the formation during cleanup, e.g., using flowback. Breaker agents include oxidizers, enzymes, or acids. Breaker agents reduce the polymer's molecular weight by the action of an acid, an oxidizer, an enzyme, or some combination of these on the polymer itself. Non- limiting examples of breaking agents include persulfates, ammonium persulfate, sodium persulfate, potassium persulfate, bromates such as sodium bromate and potassium bromate, periodates, peroxides such as calcium peroxide, hydrogen peroxide, bleach such as sodium perchlorate and organic percarboxylic acids or sodium salts, organic materials such as enzymes and lactose, or the like; chlorites, or the like, or a combination comprising at least one of the foregoing breaking agents. Breaking agents can be introduced into the fracturing fluid in live form or encapsulated.

[0044] In an embodiment, the breaking agent is used to activate the controlled degradation of the polymer. In an embodiment, the breaking agent is added to the fracturing fluid to instantly begin reducing the viscosity of the fracturing fluid. In another embodiment, the breaking agent is already present in the fracturing fluid and is activated by some external or environmental condition. In an embodiment, an oilfield breaking agent is used to break the fracturing fluid using elevated temperatures downhole. For example, the breaking agent may be activated at temperatures of 50 degrees C or greater.

[0045] In an embodiment, the fracturing fluid further comprises other additives as desired and needed depending upon the particular conditions of the fracturing operation. Non-limiting examples of such additives include pH agents, buffers, mineral, oil, alcohol, biocides, clay stabilizers, surfactants, viscoelastic surfactants, emulsifiers, non-emulsifiers, scale-inhibitors, fibers, fluid loss control agents and combinations comprising at least one of the foregoing additives.

[0046] In one embodiment, in one method of manufacturing the fracturing fluid, the polymer is dissolved into the carrier fluid in an amount effective to increase the viscosity of the carrier fluid. Other additives such as the proppant, surfactants, breaking agents, and the like, may be present in the carrier fluid either prior to the addition of the polymer or may be added to the carrier fluid after the addition of the polymer. The polymer rapidly dissolves into the carrier fluid increasing its viscosity. The increase in viscosity indirectly reduces friction between components of the fracturing equipment and provides buoyancy for the proppants in the carrier fluid as it travels to the fracture in the subterranean zone.

[0047] In an embodiment, the viscosity of the carrier fluid is increased by about 100% to about 900% in about 10 to about 100 seconds upon introduction of the polymer to the carrier fluid. In another embodiment, the viscosity of the carrier fluid is increased by about 500% to about 800%) in about 20 to about 90 seconds upon introduction of the polymer to the carrier fluid. In yet another embodiment, the viscosity of the carrier fluid is increased by about 550%) to about 750%> in about 70 to about 100 seconds upon introduction of the polymer to the carrier fluid.

[0048] In an embodiment, the fracturing fluid has a viscosity of about 5 to about 50 centipoise, specifically about 6 to about 30 centipoise, and more specifically about 7 to about 20 centipoise, upon introduction of the polymer to the carrier fluid. In another embodiment, the viscosity if the carrier fluid begins increasing upon introduction of the synthetic polymer to the carrier fluid.

[0049] Although not wishing to be bound by theory, it is thought that the polymer increases the viscosity of the carrier fluid due to not only the molecular weight and structure of the polymer itself but also due to the formation of a network of physical bonds (e.g., hydrogen bonds or ionic bonds) between the polymers, resulting in a gel-like fluid, without cross linking.

[0050] In one method of using the fracturing fluid, the polymer is added to the carrier fluid and undergoes rapid dissolution upon contacting the carrier fluid. The fracturing fluid is pumped downhole almost as soon as the polymer is introduced into the carrier fluid. Because the polymer undergoes rapid hydration upon introduction into the carrier fluid, the fracturing fluid is immediately pumped downhole. The rapid hydration of the polymer by the carrier fluid promotes an increase in the viscosity of the fracturing fluid as it is pumped thereby reducing friction between the various mechanical components (e.g., components of the drilling and fracturing equipment) as it travels downhole. As the fracturing fluid travels downhole, the increase in viscosity and density of the fracturing fluid causes it to provide buoyancy to the proppants and other additives that may be added to the fracturing fluid.

[0051] The fracturing fluid generally reaches its maximum viscosity when it penetrates the fracture. Once in the fracture, the proppants present in the fracturing fluid are disposed in the fracture and are used to prop open the fracture. When the fracture is supported by the proppants, the labile groups in the fracturing fluid are activated to decompose the fracturing fluid. The decomposition of the fracturing fluid causes a reduction in its viscosity, which permits its removal from the fracture. The removal of the fracturing fluid from the fracture leaves behind a conductive path way in the proppants through which hydrocarbons may be removed from the fracture. [0052] The polymer used in the fracturing fluid has a number of advantages over other commercially available polymers that are presently used in fracturing fluids. Since the polymer is synthetic (i.e., man-made) is not subject to some of the production constraints of naturally occurring polymers. It undergoes rapid dissolution when mixed with the carrier fluid. It exhibits a maximum viscosity at ambient temperature of equal to or greater than about 8 centipoise after about 30 seconds following the introduction of the polymer into the carrier fluid. The ability of the polymer to rapidly dissolve in the carrier fluid causes the fracturing fluid to reach about 85% or greater of the maximum viscosity at about 45 °F after about 30 seconds.

[0053] In another embodiment, the fracturing fluid comprises a breaking agent exhibits maximum viscosity at ambient temperature of equal to or greater than 5 centipoise, about 30 seconds after the introduction of the polymer into the carrier fluid and exhibits a viscosity at temperature equal to or above 100°F less than 2 centipoise.

[0054] In another embodiment, in one method for treating a hydrocarbon-bearing formation the carrier fluid is blended with a synthetic polymer to form a fracturing fluid, where the fracturing fluid has a viscosity of about 5 to about 50 centipoise. Following the blending, the fracturing fluid is discharged into a downhole fracture in the hydrocarbon- bearing formation. The fracturing fluid acts to reduce friction between components of the drilling and fracturing equipment during a hydrocarbon-bearing treatment operation. In an embodiment, the carrier fluid is discharged into the hydrocarbon-bearing formation, i.e., downhole, and the synthetic polymer and optional additives are introduced into the carrier fluid downhole.

[0055] The invention is further described by the following non-limiting examples.

EXAMPLES

Example 1

[0056] This example was conducted to show the rapid hydration of the polymer when compared with guar which is a commercially available naturally occurring polymer. In this example, hydraulic fracturing fluids comprising the synthetic polymer disclosed herein were compared with hydraulic fracturing fluids that use guar (a naturally occurring polymer). The polymer is a synthetic polymer and comprises a polyacrylamide. It is commercially available as MaxPerm-20^® from Baker Hughes, Inc. The carrier fluid is water. [0057] For this example, the synthetic polymer MaxPerm-20 was dissolved in water as shown in the Table 1 and viscosity measurements were made. The viscosity

measurements were made at ambient temperature using an Ofite rheometer at 300 revolutions per minute (rpm) and performed according to American Petroleum Institute standard API RP- 39. The viscosity results are provided in the Table 1 and in the Figure 1. The comparative samples contain guar dissolved in water. These results are also provided in the Table 1 and in the Figure 1. The Figure 1 is a graph of viscosity (in centipoise) measured at 300 rpm versus time (in minutes) for the respective samples.

[0058] In the Table 1, Samples 1 and 2 are comparative examples that contain 2.5 gpt (gallons per thousand) and 3.75 gpt guar slurry respectively. Samples 3, 4 and 5 are examples that display the viscosity properties of samples that contain 2, 3 and 4 gpt respectively of the synthetic polymer MaxPerm-20^®. From the Table 1 and the Figure 1 it may be seen that the synthetic polymer reaches a maximum viscosity at lower loading levels than the guar.

Table 1

"^Comparative Examples

[0059] For example, in comparing Sample #2 with Sample #4, it may be seen that a concentration of 3.75 gpt of guar (in water) produces a maximum viscosity of 8.2 centipoise, while 3 gpt of the synthetic polymer (in water) produces a maximum viscosity of 9 centipoise. In addition, it may be seen that while the guar takes about 8 to 10 minutes to undergo hydration, the synthetic polymer undergoes hydration in less than 30 seconds. Thus, fracturing fluids using the synthetic polymer described herein demonstrate a much more rapid hydration in much less time than the guar-based comparative fracturing fluid.

Example 2

[0060] This example was conducted to demonstrate the dynamic hydration properties of the synthetic polymer. This polymer used in this example is the synthetic polymer MaxPerm-20^®. The carrier fluid was water.

[0061] In this example, the viscosity was measured upon the introduction of different amounts of the synthetic polymer to the water. The viscosity thus measured during the hydration of the synthetic polymer by water. The resulting viscosity is therefore a measure of dynamic hydration of the synthetic polymer by water. The polymer was dissolved in the water at 45°F (7.2°C) and 80°F (26.6°C), during which the viscosity was measured. The results are shown in the Figure 2. The Figure 2 is a graph depicting the dynamic hydration viscosity at temperatures of 45°F and 80°F versus time for the synthetic polymer in water. The concentration of the polymer in the water at each of the foregoing temperatures was 0.75 gpt, 1 gpt, 2 gpt or 3 gpt respectively.

[0062] From the Figure 2 it may be seen that synthetic polymer hydrates rapidly in the water in a time period of less than 200 seconds irrespective of the temperature or the concentration. For each concentration, the fracturing fluid reaches a 85% of the maximum viscosity attainable within about 40 seconds of the introduction of the synthetic polymer into the water.

Example 3

[0063] This example was conducted to evaluate possible formation damage from the use of the synthetic polymer in a fracturing fluid and to compare it with the damage caused by the use of guar in a comparative fracturing fluid. In this example, the permeability of a simulated fracture surface comprising 81% quartz, 2% K- feldspar, and 11% MILIS is first measured. The simulated fracture surface is then contacted with the respective fracturing fluid (i.e., a fracturing fluid comprising the synthetic polymer MaxPerm-20^® or a comparative fracturing fluid comprising linear guar). The fracturing fluid was then oxidized, decomposed and removed from the simulated fracture surface following which the permeability of the simulated fracture surface is once again measured. The difference between the initial permeability and the final permeability is a measure of the formation damage that the polymer imparts to the fracture surface. The gas used to check the permeability is nitrogen. It is generally desirable for this damage to be as small possible. In short, it is desirable that the initial permeability of the simulated fracture surface be almost similar to the permeability of the simulated fracture surface after the fracturing fluid is removed from contact with the simulated fracture surface.

[0064] In this example, the synthetic polymer (MaxPerm-20^®) and the comparative polymer (guar) were each separately dissolved in a carrier fluid to form the fracturing fluid. Added to these fracturing fluids is an oxidizer to break down the fracturing fluid after it contacts the simulated fracture surface. The respective fracturing fluids contact the simulated fracture surface at 180°F (82.22°C) under an injection pressure of 60 psi (pounds per square inch) (4.2 kilograms per square centimeter (kg/cm²)) and a confining pressure of 1,500 psi (105.46 kg/cm²) for period of 20 hours. After the confining period of 20 hours, the oxidizer was activated to decompose the respective polymers and the fracturing fluid was removed from contact with the simulated fracture surface. The permeability of the simulated fracture surface was measured before and after contact with the respective fracturing fluids and the results are shown in the Figures 3 and 4 for the fracturing fluid containing the synthetic polymer and the guar respectively.

[0065] Figure 3 shows the permeability for the fracturing fluid containing the synthetic polymer disclosed herein, i.e., the MaxPerm-20^®. From the Figure 3, it may be seen that the permeability regained after removal of the fracturing fluid is 92%. Figure 4 shows the permeability for the fracturing fluid containing the linear guar. From the Figure 4, it may be seen that the permeability regained after removal of the fracturing fluid is 78.3%.

[0066] In comparing the Figures 3 and 4, it may be seen that there is substantially less residue left in the simulated fracture surface using the MaxPerm-20^® especially when compared with the guar. The synthetic polymer can thus be used to produce a fracturing fluid that produces fewer detrimental effects on fracture surfaces than other naturally occurring polymers such as guar.

[0067] From the results seen in the Examples 1, 2 and 3, it may be seen that the synthetic polymer disclosed herein can rapidly dissolve in an aqueous carrier fluid. It can dissolve more rapidly and produces less formation damage than other polymers such as, for example guar. The fracturing fluids that contain the synthetic polymer therefore provide an effective and economical alternative to guar-based fracturing fluids, demonstrate fast hydration with almost an instantaneous increase in viscosity following hydration, allows for rapid and easy adjustments of fluid viscosity and for switching the polymers used to produce the viscosity increasing additive, protect well fracturing equipment and leave little to no formation damage upon being activated and decomposed with a commercially available oilfield breaking agent.

[0068] The fracturing fluid may be used in a stimulation treatment, a fracturing treatment, an acidizing treatment, a friction reducing operation or a downhole completion operation. The fracturing fluid can be used as a gel, a slurry or a combination of at least one of the foregoing.

[0069] This invention may be embodied in many different forms, and should not be construed as limited to the embodiments set forth herein. Rather, these embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the scope of the invention to those skilled in the art. Like reference numerals refer to like elements throughout.

[0070] The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting. As used herein, the singular forms "a," "an" and "the" are intended to include the plural forms as well, unless the context clearly indicates otherwise. It will be further understood that the terms "comprises" and/or

"comprising," or "includes" and/or "including" when used in this specification, specify the presence of stated features, regions, integers, steps, operations, elements, and/or components, but do not preclude the presence or addition of one or more other features, regions, integers, steps, operations, elements, components, and/or groups thereof.

[0071] As used herein, the term "fracturing operation" shall include a stimulation treatment, a fracturing treatment, an acidizing treatment, a friction reducing operation or a completion operation, downhole, or the like.

[0072] Unless otherwise defined, all terms (including technical and scientific terms) used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this disclosure belongs. It will be further understood that terms, such as those defined in commonly used dictionaries, should be interpreted as having a meaning that is consistent with their meaning in the context of the relevant art and the present disclosure, and will not be interpreted in an idealized or overly formal sense unless expressly so defined herein.

[0073] The transition term "comprising" is inclusive of the transition terms

"consisting of and "consisting essentially of. [0074] All numerical ranges included herein are interchangeable and are inclusive of end points and all numerical values that lie between the endpoints.

[0075] As used herein a "borehole" may be any type of well, including, but not limited to, a producing well, a non-producing well, an experimental well, an exploratory well, a well for storage or sequestration, and the like. Boreholes may be vertical, horizontal, some angle between vertical and horizontal, diverted or non-diverted, and combinations thereof, for example a vertical borehole with a non-vertical component.

[0076] The terms "decompose", "degradation" and/or "degradable" refer to the conversion of materials into smaller components, intermediates, or end products.

[0077] The term and/or is used herein to mean both "and" as well as "or". For example, "A and/or B" is construed to mean A, B or A and B.

[0078] As used herein, the term "treatment" or "treating" refers to any hydrocarbon- bearing formation operation that uses a fluid in conjunction with a desired function or purpose. The term "treatment" or "treating" does not imply any particular action by the fluid or any particular constituent thereof.

[0079] While the invention has been described in detail in connection with a number of embodiments, the invention is not limited to such disclosed embodiments. Rather, the invention can be modified to incorporate any number of variations, alterations, substitutions or equivalent arrangements not heretofore described, but which are commensurate with the scope of the invention. Additionally, while various embodiments of the invention have been described, it is to be understood that aspects of the invention may include only some of the described embodiments. Accordingly, the invention is not to be seen as limited by the foregoing description, but is only limited by the scope of the appended claims.

Claims

CLAIMS What is claimed is:

1. A fracturing fluid comprising:

a carrier fluid; and

a polymer that is soluble in the carrier fluid; the polymer being a synthetic polymer; the synthetic polymer being operative to increase the viscosity of the carrier fluid to about 5 to about 50 centipoise; the fracturing fluid being operative to reduce friction during a downhole fracturing operation and to transport a proppant during the downhole fracturing operation.

2. The fracturing fluid of Claim 1, wherein the synthetic polymer comprises a labile group that is operative to facilitate degradation of the synthetic polymer upon activation of the labile group.

3. The fracturing fluid of Claim 1, wherein the fracturing fluid primarily reduces friction during an early stage of dissolution of the polymer in the carrier fluid and primarily reduces friction.

4. The fracturing fluid of Claim 1, wherein the viscosity of the carrier fluid is increased by about 100% to about 900% in about 50 to about 100 seconds upon introduction of the polymer to the carrier fluid.

5. The fracturing fluid of Claim 1, wherein the carrier fluid is an aqueous solution.

6. The fracturing fluid of Claim 1, wherein the carrier fluid comprises fresh water, salt water, brine, seawater, or a combination comprising at least one of the foregoing.

7. The fracturing fluid of Claim 1, wherein the polymer is a water-soluble polymer.

8. The fracturing fluid of Claim 1, where the synthetic polymer comprises polyacrylamide, polyvinyl alcohol, poly(acrylamide/acrylic acid), potassium salt, poly acrylic acid, polydiallyl dimethyl ammonium chloride, poly(l -glycerol methacrylate), poly(2- dimethylamino ethyl methacrylate), poly(2-ethyl-2-oxazoline), poly(2-ethyl-2-oxazoline). poly(2-hydroxyethyl methacrylate/methacrylic acid), poly(2-hydroxypropyl methacrylate), poly(2-methacryloxyethyltrimethylammonium bromide), poly(2-vinyl- 1 -methylpyridinium bromide), poly(2-vinylpyridine N-oxide), poly(2-vinylpyridine), poly(3-chloro-2- hydroxypropyl-2-methacryloxyethyldimethylammonium chloride) or a combination comprising at least one of the foregoing.

9. The fracturing fluid of Claim 1, wherein the polymer is devoid of guar.

10. The fracturing fluid of Claim 1, further comprising a breaking agent operative to activate and facilitate decomposition of the polymer, wherein upon activation of the labile group, the viscosity of the fracturing fluid is reduced to 2 centipoise or less.

11. The fracturing fluid of Claim 10, wherein the breaking agent is an oxidant, acid or an enzyme.

12. The fracturing fluid of Claim 1, wherein the fracturing fluid exhibits a maximum viscosity at ambient temperature of equal to or greater than about 8 centipoise after about 30 seconds following an introduction of the polymer into the carrier fluid.

13. The fracturing fluid of Claim 1, wherein the fracturing fluid reaches about 85% or greater of a maximum viscosity attainable for a given concentration of the polymer in the carrier fluid, where the maximum viscosity is measured at about 45 °F, about 30 seconds after the polymer first contacts the carrier fluid.

14. The fracturing fluid of Claim 1, wherein the polymer is present in an amount of about 0.1 wt% to about 10 wt%, based on the total weight of the fracturing fluid.

15. The fracturing fluid of Claim 1, wherein the polymer further comprises a naturally occurring polymer; and wherein the naturally occurring polymer is copolymerized with the synthetic polymer.

16. The fracturing fluid of Claim 1, wherein the polymer further comprises a naturally occurring polymer; and wherein the naturally occurring polymer is blended with the synthetic polymer.

17. The fracturing fluid of Claim 1, wherein the fracturing fluid is used in a stimulation treatment, a fracturing treatment, an acidizing treatment, a friction reducing operation or a downhole completion operation.

18. The fracturing fluid of Claim 1, wherein the fracturing fluid is a gel, a slurry or a combination of at least one of the foregoing.

19. A method for treating a hydrocarbon-bearing formation comprising:

blending a carrier fluid with a polymer to form a fracturing fluid, the fracturing fluid having a viscosity of about 5 to about 50 centipoise; the polymer being a synthetic polymer; and

discharging the fracturing fluid into a downhole fracture in the hydrocarbon-bearing formation, wherein the fracturing fluid is operative to reduce friction during a hydrocarbon- bearing treatment operation.

20. A method for treating a hydrocarbon-bearing formation of claim 19, where the synthetic polymer comprises a labile group that is operative to facilitate degradation of the synthetic polymer upon activation of the labile group.

21. The method for treating a hydrocarbon-bearing formation of Claim 19, further comprising decomposing the polymer and removing the polymer from the hydrocarbon- bearing formation.