WO2013158160A1 - Method for producing solid carbon by reducing carbon dioxide - Google Patents

Method for producing solid carbon by reducing carbon dioxide Download PDF

Info

Publication number
WO2013158160A1
WO2013158160A1 PCT/US2013/000077 US2013000077W WO2013158160A1 WO 2013158160 A1 WO2013158160 A1 WO 2013158160A1 US 2013000077 W US2013000077 W US 2013000077W WO 2013158160 A1 WO2013158160 A1 WO 2013158160A1
Authority
WO
WIPO (PCT)
Prior art keywords
carbon
tail gas
mixture
gas
water
Prior art date
Application number
PCT/US2013/000077
Other languages
French (fr)
Inventor
Dallas B. Noyes
Original Assignee
Seerstone Llc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Seerstone Llc filed Critical Seerstone Llc
Priority to US14/389,600 priority Critical patent/US9090472B2/en
Priority to EP13778060.7A priority patent/EP2838839B1/en
Priority to CN201380020323.0A priority patent/CN104302575B/en
Priority to MX2014012549A priority patent/MX354529B/en
Priority to JP2015506978A priority patent/JP2015514669A/en
Publication of WO2013158160A1 publication Critical patent/WO2013158160A1/en
Priority to US14/806,401 priority patent/US9637382B2/en

Abstract

A two-stage reaction process includes reacting gaseous carbon dioxide with a reducing agent to form carbon monoxide and water. At least a portion of the water is condensed to form a dry tail gas. The dry tail gas, with the possible addition of a reducing agent, reacts to convert at least a portion of the carbon monoxide to solid carbon and water. Other methods include reacting a feed gas mixture to form a reaction mixture, condensing water from the reaction mixture to form a dried reaction mixture, mixing the dried reaction mixture with a recirculating gas to form a catalytic converter feed gas mixture, flowing the catalytic converter feed gas mixture through a catalytic converter to form solid carbon and a tail gas mixture containing water, and flowing the tail gas mixture through a heat exchanger.

Description

METHODS FOR PRODUCING SOLID CARBON
BY REDUCING CARBON DIOXIDE
PRIORITY CLAIM
This application claims the benefit of the filing date of United States Provisional Patent Application Serial Number 61/624,723, filed April 16, 2012, for "Method for Producing Solid Carbon by Reducing Carbon Oxides," the disclosure of which is hereby incorporated herein in its entirety by this reference.
TECHNICAL FIELD
Embodiments of the disclosure relate to the conversion of a carbon-containing feedstock into solid carbon and more specifically, to methods of converting mixtures containing carbon monoxide, carbon dioxide, or combinations thereof to solid carbon of various morphologies.
BACKGROUND
U.S. Patent Publication No. 2012/0034150 Al, published February 9, 2012, the disclosure of which is hereby incorporated herein in its entirety by this reference, discloses background information hereto.
Additional information is disclosed in the following documents, the disclosure of each of which is hereby incorporated herein in its entirety by this reference:
1. International Application No. (attorney docket No. 3525-P 10945.1 PC), filed on even date herewith, for "Methods and Structures for Reducing Carbon Oxides with Non-Ferrous Catalysts," which claims the benefit of
U.S.S.N. No. 61/624,702, filed April 16, 2012, in the name of Dallas B. Noyes;
2. International Application No. (attorney docket No. 3525-P 10946.1 PC), filed on even date herewith, for "Methods and Systems for Thermal Energy Recovery from Production of Solid Carbon Materials by Reducing Carbon
Oxides," which claims the benefit of U.S.S.N. No. 61/624,573, filed April 16, 2012, in the name of Dallas B. Noyes; 3. International Application No. (attorney docket No. 3525-P1 1001. IPC), filed on even date herewith, for "Methods and Reactors for Producing Solid Carbon Nanotubes, Solid Carbon Clusters, and Forests," which claims the benefit of U.S.S.N. 61/624,753, filed April 16, 2012, in the name of Dallas B. Noyes;
4. International Application No. (attorney docket No. 3525-P1 1002.1PC), filed on even date herewith, for "Methods for Treating an Offgas Containing Carbon Oxides," which claims the benefit of U.S.S.N. 61/624,513, filed April 16, 2012, in the name of Dallas B. Noyes; 5. International Application No. (attorney docket No. 3525-P1 1248. IPC), filed on even date herewith, for "Methods for Using Metal Catalysts in Carbon Oxide Catalytic Converters," which claims the benefit of U.S.S.N. 61/624,848, filed April 16, 2012, in the name of Dallas B. Noyes;
6. International Application No. (attorney docket No. 3525-P11249.1PC), filed on even date herewith, for "Methods and Systems for Capturing and
Sequestering Carbon and for Reducing the Mass of Carbon Oxides in a Waste Gas Stream," which claims the benefit of U.S.S.N. 61/624,462, filed April 16, 2012, in the name of Dallas B. Noyes;
7. International Application No. (attorney docket No. 3525-P11361.IPC), filed on even date herewith, for "Methods and Systems for Forming
Ammonia and Solid Carbon Products," which claims the benefit of U.S.S.N. 61/671,464, filed July 13, 2012, in the name of Dallas B. Noyes; and
8. International Application No. (attorney docket No. 3525-P1 1771PC), filed on even date herewith, for "Carbon Nanotubes Having a Bimodal Size
Distribution," which claims the benefit of U.S.S.N. 61/637,229, filed April 23, 2012, in the name of Dallas B. Noyes.
Solid carbon has numerous commercial applications. These applications include longstanding uses such as uses of carbon black and carbon fibers as a filler material in tires, inks, etc., many uses for various forms of graphite {e.g., pyrolytic graphite in heat shields) and innovative and emerging applications for buckminsterfullerene and carbon nanotubes. Conventional methods for the manufacture of various forms of solid carbon typically involve the pyrolysis of hydrocarbons in the presence of a suitable catalyst. Hydrocarbons are typically used as the carbon sources due to an abundant availability and relatively low cost. The use of carbon oxides as the carbon source in the production of solid carbon has largely been unexploited.
Carbon oxides, particularly carbon dioxide, are abundant gases that may be extracted from point-source emissions such as the exhaust gases of hydrocarbon combustion or from some process off-gases. Carbon dioxide may also be extracted from the air. Because point-source emissions have much higher concentrations of carbon dioxide than does air, they are often economical sources from which to harvest carbon dioxide. However, the immediate availability of air may provide cost offsets by eliminating transportation costs through local manufacturing of solid carbon products from carbon dioxide in air.
Carbon dioxide is increasingly available and inexpensive as a byproduct of power generation and chemical processes in which an object may be to reduce or eliminate the emission of carbon dioxide into the atmosphere by capture and subsequent sequestration of the carbon dioxide (e.g., by injection into a geological formation). For example, the capture and sequestration of carbon dioxide is the basis for some "green" coal-fired power stations. In current practice, capture and sequestration of the carbon dioxide entails significant cost.
There is a spectrum of reactions involving carbon, oxygen, and hydrogen wherein various equilibria have been identified. Hydrocarbon pyrolysis involves equilibria between hydrogen and carbon that favors solid carbon production, typically with little or no oxygen present. The Boudouard reaction, also called the "carbon monoxide disproportionation reaction," is the range of equilibria between carbon and oxygen that favors solid carbon production, typically with little or no hydrogen present. The Bosch reaction is within a region of equilibria where all of carbon, oxygen, and hydrogen are present under reaction conditions that also favor solid carbon production.
The relationship between the hydrocarbon pyrolysis, Boudouard, and Bosch reactions may be understood in terms of a C-H-O equilibrium diagram, as shown in FIG. 1. The C-H-O equilibrium diagram of FIG. 1 shows various known routes to solid carbon, including carbon nanotubes ("CNTs"). The hydrocarbon pyrolysis reactions occur on the equilibrium line that connects H and C and in the region near the left edge of the triangle to the upper left of the dashed lines. Two dashed lines are shown because the transition between the pyrolysis zone and the Bosch reaction zone may change with reactor temperature. The Boudouard, or carbon monoxide disproportionation reactions, occur near the equilibrium line that connects O and C (i.e., the right edge of the triangle). The equilibrium lines for various temperatures that traverse the diagram show the approximate regions in which solid carbon will form. For each temperature, solid carbon may form in the regions above the associated equilibrium line, but will not generally form in the regions below the equilibrium line. The Boudouard reaction zone appears at the right side of the triangle. In this zone, the Boudouard reaction is thermodynamically preferred over the Bosch reaction. In the region between the pyrolysis zone and the Boudouard reaction zone and above a particular reaction temperature curve, the Bosch reaction is thermodynamically preferred over the Boudouard reaction.
CNTs are valuable because of their unique material properties, including strength, current-carrying capacity, and thermal and electrical conductivity. Current bulk use of CNTs includes use as an additive to resins in the manufacture of composites. Research and development on the applications of CNTs is very active with a wide variety of applications in use or under consideration. One obstacle to widespread use of CNTs has been the cost of manufacture.
U.S. Patent 7,794,690 (Abatzoglou et al.) teaches a dry reforming process for sequestration of carbon from an organic material. Abatzoglou discloses a process utilizing a 2D carbon sequestration catalyst with, optionally, a 3D dry reforming catalyst. For example, Abatzoglou discloses a two-stage process for dry reformation of an organic material (e.g., methane, ethanol) and C02 over a 3D catalyst to form syngas, in a first stage, followed by carbon sequestration of syngas over a 2D carbon steel catalyst to form CNTs and carbon nanofilaments. The 2D catalyst may be an active metal (e.g., Ni, Rh, Ru, Cu-Ni, Sn-Ni) on a nonporous metallic or ceramic support, or an iron-based catalyst (e.g., steel), on a monolith support. The 3D catalyst may be of similar composition, or may be a composite catalyst (e.g., Ni/Zr02-Al203) over a similar support. Abatzoglou teaches preactivation of a 2D catalyst by passing an inert gas stream over a surface of the catalyst at a temperature beyond its eutectic point, to transform the iron into its alpha phase. Abatzoglou teaches minimizing water in the two-stage process or introducing water in low concentrations (0 to 10 wt%) in a reactant gas mixture during the dry reformation first stage.
DISCLOSURE
In some embodiments, a two-stage reaction process includes reacting a first feed mixture having a carbon source with a reducing agent under first reaction conditions to convert at least a portion of the first feed mixture to a first product mixture comprising carbon monoxide and water. At least a portion of the water is condensed from the first product mixture to form a first dried product mixture. The first dried product mixture reacts under second reaction conditions to convert at least a portion of the carbon monoxide in the first dried product mixture to solid carbon and a second product mixture including water.
In some embodiments, a method for two-stage reduction of carbon dioxide includes reacting a feed gas mixture having carbon dioxide and a reducing gas to form a reaction mixture having carbon monoxide and water. A portion of the water is condensed from the reaction mixture to form a dried reaction mixture. The dried reaction mixture is mixed with a recirculating gas to form a catalytic converter feed gas mixture. The catalytic converter feed gas mixture flows through a catalytic converter in the presence of a metal to form solid carbon and a catalytic converter tail gas mixture including water. The catalytic converter tail gas mixture flows through a heat exchanger to condense a portion of the water and form the recirculating gas.
In certain embodiments hereof, the partial pressure of water in the reaction is regulated by various means, including recycling and condensation of water, to influence, for example, the structure or other aspects of the composition of carbon products produced. The partial pressure of water appears to assist in obtaining certain desirable carbon allotropes.
In certain embodiments, a broad range of inexpensive and readily-available catalysts, including steel-based catalysts, are described, without the need for activation of the catalyst before it is used in a reaction. Iron alloys, including steel, may contain various allotropes of iron, including alpha-iron (austenite), gamma iron, and delta-iron. In some embodiments, reactions disclosed herein advantageously utilize an iron-based catalyst, wherein the iron is not in an alpha phase. In certain embodiments, a stainless steel containing iron primarily in the austenitic phase is used as a catalyst.
Catalysts, including an iron-based catalyst (e.g., steel, steel wool), may be used without a need for an additional solid support. In certain embodiments, reactions disclosed herein proceed without the need for a ceramic or metallic support for the catalyst. Omitting a solid support may simplify the setup of the reactor and reduce costs.
In certain embodiments, a two-stage reaction process for converting carbon dioxide to a solid carbon product includes reacting a first feed mixture having gaseous carbon dioxide and hydrogen under first reaction conditions to convert at least a portion of the carbon dioxide and hydrogen to carbon monoxide and water and form a first product mixture. At least a portion of the water is condensed from the first product mixture to form a dried first product mixture. The dried first product mixture is mixed with a recirculatory stream of a dried second product mixture to form a second feed mixture including carbon monoxide. The second feed mixture reacts under second reaction conditions to convert at least a portion of the carbon monoxide in the second feed mixture to solid carbon and a second gaseous product including water and unreacted gases from the second feed mixture. At least a portion of the water from the second gaseous reaction product is condensed to form the dried second product mixture.
BRIEF DESCRIPTION OF THE DRAWINGS
Features and advantages of the disclosure will be apparent from reference to the following detailed description taken in conjunction with the accompanying drawings, in which:
FIG. 1 depicts a C-H-O equilibrium diagram; and
FIGS. 2 through 4 each illustrate simplified process-flow diagrams indicating how processes of the current disclosure may be performed. MODE(S) FOR CARRYING OUT THE INVENTION
The disclosure includes methods for reacting a carbon source with a reducing agent. The methods may be used to manufacture solid carbon products in various morphologies, and to convert carbon oxides into solid carbon and water. Solid carbon products may include graphite (e.g., pyrolytic graphite), graphene, carbon black, fibrous carbon, buckminsterfullerenes, single-wall CNTs, or multi-wall CNTs. The type, purity, and homogeneity of solid carbon products may be controlled by the reaction conditions (time, temperature, pressure, partial pressure of reactants, and/or catalyst properties).
The methods use the Bosch reaction to produce solid carbon products by the reduction of carbon dioxide with any of a variety of reducing gases such as hydrogen or methane in the presence of a catalyst and under reaction conditions optimized for any particular desired type of solid carbon. This catalytic conversion process may be incorporated with a variety of separation technologies, and with a variety of carbon dioxide generation processes.
The methods, based generally on the Bosch reaction, include reactions in the interior region of the phase diagram shown in FIG. 1 (i.e., the region between the Boudouard reaction zone and the pyrolysis zone), where equilibrium may be established between solid carbon, compounds of carbon, hydrogen and oxygen. The central region of FIG. 1 has several points that are favorable for the formation of CNTs and other forms of solid carbon. The type of solid carbon produced can be selectively controlled through selection and processing of catalysts, reaction gases, and reaction conditions. Thus these methods open new routes to the production of valuable solid carbon products such as CNTs.
The process uses two abundant feedstocks, carbon oxides (e.g., carbon dioxide, carbon monoxide) and a reducing agent. The reducing agent is preferably a hydrocarbon gas (e.g., natural gas, methane, ethane, ethylene, etc.), an alcohol (e.g., methanol, ethanol, etc.) hydrogen (H2) gas, or a mixture thereof. A hydrocarbon gas may serve a dual function as both an additional carbon source and as the reducing agent for the carbon oxides. "Syngas" comprises primarily carbon monoxide and hydrogen, and syngas has both the carbon oxide and the reducing gas in a mixture. Syngas may be used as all or a portion of the reaction gas mixture.
The reduction process of this method results in the formation of solid carbon product and water. The water may subsequently be condensed and the latent heat extracted for heating purposes, or as part of a low-pressure power extraction cycle. The water may be extracted as a useful co-product, and the associated latent heat of the water may be used for another process.
The methods disclosed herein use the carbon dioxide as an economically valuable feed stock. In many industrial processes, carbon dioxide is an undesirable waste product, and may have associated disposal costs. Use of carbon dioxide as a feed in solid carbon production may reduce or eliminate disposal costs, and may simultaneously convert carbon dioxide to a salable product. Thus, the methods may be incorporated with fossil fuel combustion processes. Combining the processes disclosed herein with fossil fuel combustion processes may also be beneficial because formation of solid carbon products by such processes may be more economical than existing separation and sequestration methods.
Carbon dioxide is present in many natural gas deposits at various concentrations, such as at concentrations of up to 5% by volume, up to 20% by volume, up to 60% by volume, or even higher. Other compounds, such as H2S, S02, and other sulfur compounds are often present in natural gas. Removal of sulfur-containing compounds is often done at a well site to form "sweet gas" (i.e., gas with little or no sulfur content). Removal of carbon dioxide before the natural gas is delivered to a consumer may be effectively accomplished via the techniques disclosed herein.
The methods disclosed produce solid carbon products such as buckminsterfullerene and carbon nanotubes using carbon oxides as the primary carbon source. The methods thus involve catalytic conversion of carbon oxides to solid carbon and water. The methods may use carbon oxides from various sources, such as the atmosphere, combustion gases, process off-gases, well gas, and other natural and industrial sources of carbon oxides. The carbon oxides may be separated from these sources and concentrated as needed, such as by amine absorption and regeneration.
The Bosch reactions, as described herein, use a reducing agent (e.g., hydrogen, a hydrocarbon, etc.) to reduce carbon oxides to solid carbon (e.g., graphite, graphene, carbon black, fibrous carbon, buckminsterfullerene, single-wall CNTs, multi-wall CNTs, carbon platelets, nanodiamond, etc.) and water. The reactions may be conducted at temperatures in excess of approximately 650°C, such as in excess of about 680° C, in the presence of a catalyst. In the formation of CNTs, graphite, or C60 fullerene, the Bosch reaction of carbon dioxide with hydrogen is mildly exothermic (heat producing) and proceeds with the stoichiometry:
C02 + 2H2 <→ C(s) + 2H20 (Equation 1 ).
The formation of CNTs in Equation 1 releases approximately 24.9 kcal/mol at 650°C (i.e., ΔΗ = -24.9 kcal/mol). The formation of graphite in Equation 1 releases approximately 23.8 kcal/mol at 650°C. The formation of C^ fullerene in Equation 1 releases approximately 13.6 kcal/mol at 650°C. The formation of carbon lamp black in Equation 1 is endothermic, consuming approximately 147.5 kcal/mol at 650°C (i.e., ΔΗ is +147.5 kcal/mol). The Bosch reactions are reversible; in the reverse of Equation 1, solid carbon is oxidized by water to form carbon dioxide and hydrogen in an oxygen shift reaction.
The Bosch reactions are actually two-step reactions having an overall release of energy (i.e., the net reactions are exothermic). In the first step of the reaction shown in Equation 1 , carbon dioxide reacts with hydrogen to create carbon monoxide and water in a reverse water-gas shift reaction:
C02 + H2 *→ CO + H20 (Equation 2).
Equation 2 is slightly endothermic at 650°C, requiring a heat input of about 8.47 kcal/mol (i.e., ΔΗ = +8.47 kcal/mol). In the second step of the reaction shown in Equation 1, carbon monoxide reacts with hydrogen to form solid carbon and water:
CO + H2 <→ C(s) + H20 (Equation 3).
Equation 3 may occur with stoichiometric amounts of reactants, or with excess C02 or H2. Equation 3 is exothermic at 650°C, releasing 33.4 kcal/mol (1.16 xlO4 joules/gram of C(s)) when CNTs are formed (i.e., ΔΗ = -33.4 kcal/mol). Values of ΔΗ for Equation 3 may be calculated for other carbon products by the difference between the ΔΗ value for Equation 1 for that particular carbon product and the ΔΗ value for Equation 2.
The method involves the creation of solid carbon, and in particular, CNTs of different shapes or morphologies, from carbon oxides. The carbon oxides may be a product of combustion of a primary hydrocarbon, from the atmosphere, or from some other source. The carbon oxides and a reducing agent may be injected into a reaction zone that has been preheated to a reaction temperature. The reaction typically occurs in the presence of a catalyst. The catalyst composition and grain size may affect the morphology of the resulting solid carbon products. The reaction conditions, including the temperature and pressure of the reactor, the residence time of the reaction gases, and the grain size of the catalyst, may be controlled to obtain solid carbon products having selected characteristics. Feed and product mixtures may pass through one or more condensers to remove excess water and to control the partial pressure of water vapor in the reaction gas mixture. The partial pressure of water is one factor that appears to affect the type and character (e.g., morphology) of solid carbon formed, as well as the kinetics of carbon formation.
Carbon activity (Ac) can be used as an indicator of whether solid carbon will form under particular reaction conditions (e.g., temperature, pressure, reactants, concentrations). Without being bound to any particular theory, it is believed that carbon activity is the key metric for determining which allotrope of solid carbon is formed. Higher carbon activity tends to result in the formation of CNTs, lower carbon activity tends to result in the formation of graphitic forms.
Carbon activity for a reaction forming solid carbon from gaseous reactants can be defined as the reaction equilibrium constant times the partial pressure of gaseous products, divided by the partial pressure of reactants. For example, in the reaction, CO(g) + H2(g) ^ C(S) + H20(g), with a reaction equilibrium constant of K, the carbon activity Ac is defined as K (Pc&Pm./Pmo)- Thus, Ac is directly proportional to the partial pressures of CO and H2, and inversely proportional to the partial pressure of H20. Higher Pmo tends to inhibit CNT formation. The carbon activity of this reaction may also be expressed in terms of mole fractions and total pressure:
Figure imgf000011_0001
where JV is the total pressure and 7 is the mole fraction of a species. Carbon activity generally varies ^with temperature because reaction equilibrium constants vary generally with temperature. Carbon activity also varies with total pressure for reactions in which a different number of moles of gas are produced than are consumed. Mixtures of solid carbon allotropes and morphologies thereof can be achieved by varying the catalyst and the carbon activity of the reaction gases in the reactor.
Solid carbon may be produced in many different morphologies through the carbon oxide reduction process of the method. Some of the solid carbon morphologies that may be produced include graphite (e.g., pyrolytic graphite), graphene, carbon black, fibrous carbon, buckminsterfullerene, single-wall CNTs, multi-wall CNTs, platelets, or nanodiamond.
Reducing agents suitable for the reduction reaction may include hydrogen or hydrocarbon gases. Hydrocarbon gases may provide both hydrogen and a portion of the carbon. A reducing gas mixture of one or more of the commonly available hydrocarbon gases such as lower hydrocarbon alkanes (e.g., methane, ethane, propane, butane, pentane, and hexane), including those found in natural gas, may be economical in some applications. In one embodiment, the reducing gas comprises methane and releases heat in an exothermic reaction:
C02 + CH4 <→ 2C(s) + 2H20 (Equation 4).
The reaction kinetics favorable to the formation of the desired species of solid carbon may be established through the use of suitable catalysts. For example, metals from groups 2 through 15 of the periodic table, such as from groups 5 through 10 (e.g., nickel, molybdenum, chromium, cobalt, tungsten, vanadium, ruthenium, platinum, iridium, iron, etc.) actinides, lanthanides, or compounds containing any such metals (e.g., iron carbide) may accelerate the reaction rates of any of Equations 1 through 4. Note that the periodic table may have various group numbering systems. As used herein, group 2 is the group including Be, group 3 is the group including Sc, group 4 is the group including Ti, group 5 is the group including V, group 6 is the group including Cr, group 7 is the group including Mn, group 8 is the group including Fe, group 9 is the group including Co, group 10 is the group including Ni, group 11 is the group including Cu, group 12 is the group including Zn, group 13 is the group including B, group 14 is the group including C, and group 15 is the group including N. In some embodiments, commercially available metals are used without special preparation. Catalysts may facilitate operations at lower temperatures. In reactions forming CNTs, higher reaction rates may correspond to smaller diameter CNTs, and lower reaction rates may correspond to larger diameter CNTs.
Catalysts may be in the form of nanoparticles or in the form of domains or grains and grain boundaries within a solid material. Catalysts may be selected to have a grain size related to a characteristic dimension of a desired diameter of the solid carbon product (e.g., a CNT diameter). Catalyst powder may be formed in or near the reaction zone by injecting an aerosol solution such that upon evaporation or a carrier solvent, a selected particle size distribution results. Alternatively, powdered catalyst may be entrained in a carrier gas and delivered to the reactor. By selecting the catalyst and the reaction conditions, the process may be tuned to produce selected morphologies of solid carbon product. In some embodiments, the catalyst may be formed over a substrate or support, such as an inert oxide that does not participate in the reactions. However, the substrate is not necessary; in other embodiments, the catalyst material is an unsupported material, such as a bulk metal or particles of metal not connected to another material {e.g., loose particles, shavings, or shot, such as may be used in a fluidized-bed reactor).
Catalysts can be formed from a wide variety of catalyst precursors. Such catalyst precursors may decompose to form a desired catalyst. The catalyst precursors may be selected such that their decomposition temperature is below the temperature of a reaction zone, so that when the catalyst precursors are introduced into the reaction zone, they decompose to form catalyst particles. The size of the catalyst particles may be controlled by the use of catalyst precursors. That is, by forming catalyst particles in situ, the catalyst particles may be kept to a smaller and/or more uniform size than is possible by other means. The morphology and diameter of the CNTs may be controlled by controlling the properties of the catalyst particles.
Catalyst precursors may be mixed and dissolved in water or another solvent to make a solution of the catalyst precursors. The resulting solution may be dried to form the catalyst. In some embodiments, the solution may be sprayed to form an aerosol in a heated chamber, such as by atomization in a flow of gas, direct spraying of the solution through a nozzle, electrostatic spraying, dispersing the solution from the surface of a rotating fixture, and combinations thereof. In some embodiments, catalyst precursors may be combusted by disposing a solution of catalyst precursor on a heated surface, allowing the solvent to evaporate, then allowing the catalyst precursor to combust. Other methods include creating the catalyst by a vacuum-deposition process at high vacuum {e.g., 10"6 to 10"8 Torr) and high temperatures {e.g., 900°C to 1300°C). Catalysts may be supplied as metal nanoparticles supported on solid supports via secondary dispersion and extraction. Suitable catalysts are described in, for example, U.S. Patent Application Publication No. 2012/0034150 Al . The catalyst may be mobilized, as in a fluidized bed, or may be stationary in the reactor as the carbon-containing gases flow through the reactor and react with the catalyst.
The catalyst particles may be nucleating sites from which CNTs grow. The catalyst particles may be domains or grains in a piece of metal material or discrete nanoparticles of catalytic metal deposited on an inert substrate (e.g., a quartz disk). The size of CNTs may be proportional to the size of the nucleating site. The ratio between a catalyst particle size and the diameter of a CNT formed thereon may be from about 1.2 to about 1.6. One possible theoretical basis for the correlation of particle size and CNT diameter is disclosed in Nasibulin et al., Correlation Between Catalyst Particle and Single-walled Carbon Nanotube Diameters, 43 Carbon 2251 -57 (2005).
The catalyst may be any metal suitable for the progression of a carbon-forming reaction. Various commercially available grades of nickel, molybdenum, platinum, chromium, cobalt, and tungsten, and alloys thereof may be useful as catalysts. Various grades of chromium-, molybdenum-, cobalt-, tungsten-, or nickel-containing alloys or superalloys may be used, for example materials commercially available from Special Metals Corp., of New Hartford, New York, under the trade name INCONEL®, or materials commercially available from Haynes International, Inc., of Kokomo, Indiana, under the trade name HASTELLOY® (e.g., HASTELLOY® B-2, HASTELLOY® B-3, HASTELLOY® C-4, HASTELLOY® C-2000, HASTELLOY® C-22, HASTELLOY® C-276, HASTELLOY® G-30, HASTELLOY® N, or HASTELLOY® W). The catalyst may be in solid form, such as plates, cylinders, pellets, spheres of various diameters (e.g., as steel shot), or combinations thereof.
304 stainless steel appears to catalyze the formation of CNTs under a wide range of temperatures, pressures, and gas compositions. However, the rate of formation of CNTs on 304 stainless steel appears to be relatively low, such that 304 stainless steel may be used effectively as a construction material for process equipment, with minimal deposition on surfaces thereof in normal operations. 316L stainless steel, in contrast, appears to catalyze the formation of solid carbon at significantly higher rates than 304 stainless steel, but may also form various morphologies of carbon. Thus, 316L stainless steel may be used as a catalyst to achieve high reaction rates, but particular reaction conditions may be maintained to control product morphology. Catalysts may be selected to include Cr, such as in amounts of about 22% or less by weight. For example, 316L stainless steel contains from about 16% to about 18.5% Cr by weight. Catalysts may also be selected to include Ni, such as in amounts of about 8% or more by weight. For example, 316L stainless steel contains from about 10% to about 14% Ni by weight. Catalysts of these types of steel have iron in an austenitic phase, in contrast to alpha-phase iron used as a catalyst in conventional processes. Given the good results observed with 316L stainless steel, the Ni and/or Cr may have a synergistic effect with Fe.
In one embodiment, substantially spherical catalyst material may be used in conjunction with a fluidized-bed reactor. The morphology of CNTs grown on metal catalyst may be dependent on the chemistry of the metal catalyst and the way the catalyst was processed. For example, CNT morphology may be related to grain size and grain boundary shapes within the metal. For example, the characteristic size of these features may influence the characteristic diameter of CNTs formed in the presence of such metal catalysts.
The grain size of a catalyst material may at least partially determine the size of the CNT product. Metals with smaller grain sizes may produce smaller diameter CNTs. The grain size may be a function both of the chemistry of the metal catalyst and the heat-treating methods under which the grains are formed.
The grain size of the metal crystalline surface may also at least partially determine the size of the CNT product. The grain distribution, including the crystalline grain size and grain boundaries, may be controlled by methods known in the art. For example, grain size may be controlled by controlling nucleation of the metal, such as by grain refinement or inoculation. Inoculants for promoting nucleation may include titanium, boron, aluminum titanium (Al3Ti), titanium diboride (TiB2), etc.
In general, the grain structure of a metal surface may be changed by methods known in the art. For example, a metal structure may be heated to a temperature sufficient to recrystallize the metal structure to form multiple randomly oriented grains. Alternatively, the metal may be heat-treated or annealed to change the grain structure, grain boundary, and grain size. For example, the metal may be annealed by heating the metal to a temperature above its recrystallization temperature, maintaining the temperature for a period of time, then cooling the metal. As another example, metal may be annealed by heating it for a period of time to allow grains within the microstructure of the metal to form new grains through recrystallization.
Recrystallization is a process in which a metal may be plastically deformed, annealed, or otherwise heat-treated. When the metal is heated, the heat-treatment affects grain growth in the metal structure. The size of a crystalline structure may vary with the temperature above the critical temperature and the time at that temperature. Additionally, a faster cooling rate from the recrystallization temperature may provide a larger maximum undercooling and a greater number of nucleation sites, thus producing a finer-grained metal. Thus, in one embodiment, crystal grain size— and thus, nanotube size— may be controlled by nucleation of the catalyst metal, the temperature of the catalyst heat-treatment, the length of time the catalyst metal is above the crystallization temperature, and the cooling process of the metal.
Nucleation of a catalyst may be promoted by the use of pulsed laser light, such as by passing electromagnetic pulses through the catalyst or through catalyst precursors. This use of laser light may enhance the size uniformity of the resulting catalyst nanoparticles.
Oxidation and subsequent reduction of the catalyst surface alter the grain structure and grain boundaries. Without being bound by any particular theory, oxidation appears to alter the surface of the metal catalyst in the oxidized areas. Subsequent reduction may result in further alteration of the catalyst surface. Thus, the grain size and grain boundary of the catalyst may be controlled by oxidizing and reducing the catalyst surface and by controlling the exposure time of the catalyst surface to the reducing gas and the oxidizing gas. The oxidation and/or reduction temperatures may be in the range from about 500°C to about 1,200°C, from about 600°C to about 1 ,000°C, or from about 700°C to about 900 °C. The resulting grain size may range from about 0.1 μιη to about 500 μπι, from about 0.2 μπι to about 100 μιη, from about 0.5 μηι to about 10 μηι, or from about 1.0 μπι to about 2.0 μιη. In some embodiments, the catalyst may be an oxidized metal (e.g., rusted steel) that is reduced before or during a reaction forming solid carbon. Without being bound to any partcular theory, it is believed that removal of oxides leaves voids or irregularities in the surface of the catalyst material, and increases the overall surface area of the catalyst material. In some embodiments, the catalyst may be pulverized or ball-milled. Powder from the pulverization or ball-milling process may be collected and sieved to increase the uniformity of the catalyst particle size. If the catalyst is in powder or particulate form, the catalyst may be carried into the reactor by a carrier gas or a reactant gas. Catalyst in particulate form may also be used in a fluidized-bed reactor. Dynamic action of metal catalyst particles within the fluidized bed may continually cause fresh catalyst surfaces to be exposed as carbon nanotubes are formed and spalled off of the catalyst particle surface. Catalyst particles may be configured to increase the surface area of the catalyst in contact with the carbon oxide gases and the reducing gases as the reaction proceeds.
Reaction temperatures may depend on the composition of the catalyst or on the size of the catalyst particles. Catalyst materials having small particle sizes tend to catalyze reactions at lower temperatures than the same catalyst materials with larger particle sizes. For example, the Bosch reaction may occur at temperatures in the range of approximately 400°C to 800°C for iron-based catalysts, depending on the particle size and composition and the desired solid carbon product. In general, graphite and amorphous solid carbon form at lower temperatures, and CNTs form at higher temperatures. CNTs may form at temperatures above about 680°C. In general, the reactions described herein proceed at a wide range of pressures, from near vacuum, to pressures of 4.0 Pa (580 psi) or higher. For example, CNTs may form in pressure ranges of from about 0.28 MPa (40 psi) to about 6.2 MPa (900 psi). In some embodiments, CNTs may form at pressures from about 0.34 MPa (50 psi) to about 0.41 MPa (60 psi), or at a pressure of about 4.1 MPa (600 psi). Typically, increasing the pressure increases the reaction rate.
When using a solid bulk catalyst, such as a wafer of metal catalyst, CNTs may appear to grow in a series of generations. For example, CNTs may form clumps, pillows, forests, fibers, piles, etc., as described in U.S. Patent Application Publication No. 2012/0034150 Al.
A wide variety of reactor designs may be used to facilitate the formation and collection of the desired solid carbon products. Aerosol and fluidized-bed reactors are well-suited for high-volume continuous production of solid carbon products. A fluid- wall reactor has the advantages of providing for the introduction of various substances (catalysts, additional reactants) and of minimizing or eliminating the accumulation of solid carbon products on reactor walls.
In some embodiments, the reactor may be an aerosol reactor in which the catalyst is formed in a gas phase or in which the catalyst is preformed and selected for a specific size distribution, mixed into a liquid or carrier gas solution, and then sprayed into the reactor (e.g., via electrospray). The catalyst may then remain distributed in the gas phase or be deposited on solid surfaces in the reaction zone for the growth phase of the carbon product. The catalyst may subsequently transport the product out of the reaction zone. In another embodiment, one or more reactors may be fluidized-bed reactors in which the catalyst or catalyst-coated particles are introduced into the reactor and the solid carbon product is grown on the surface of the particles. The solid carbon may be either elutriated in the reactor, and carried out of the reactor entrained in the reaction gases, or the catalyst particles may be harvested and the solid carbon removed from the surface.
The reactors may be batch reactors in which the catalyst is either a fixed solid surface or is mounted on a fixed solid surface (e.g., catalyst nanoparticles deposited on an inert substrate), with the solid carbon grown on the catalyst, and the catalyst and solid carbon product periodically removed from the reactor. Alternatively, the reactors may be continuous, wherein a solid catalyst or catalyst mounted on a solid substrate passes through a flowing gas stream, the resulting solid carbon product is harvested, and the solid surface is reintroduced to the reactor. The solid substrate may be the catalyst material (e.g., a solid piece of a chromium-, molybdenum-, cobalt-, or nickel- containing alloy or superalloy) or a surface on which the catalyst is mounted.
In one embodiment, a fluidized-bed reactor may be designed to retain the catalyst while allowing the solid CNT product to be entrained in the gas flow and to be lofted out of the reaction zone upon reaching a desired size. The shape of the reactor, the gas flow rates, or shape and flow rates in combination may control the residence time of the elutriates and the corresponding size of the solid carbon product (such as the length of the carbon nanotubes).
In one embodiment, particles in a fluidized-bed reactor are of a substantially uniform diameter. The diameter of the catalyst in the fluidized bed may be chosen based on the particular reactor configuration, the flow rate of the reactants through the reactor, the shape of the catalyst, the density of the catalyst, and the density of the reactant gases and any inert carrier gases. The diameter of the catalyst particles may be chosen to avoid entrainment of the catalyst with the reaction product and also to avoid channeling of the reactants through the bed. A diffuser or sparger may distribute the gaseous reactants to provide a uniform flow pattern through the bed particles and limit or prevent channeling of gases through the particle bed.
When the catalyst is a sheet or plate over an object of manufacture, the entire surface of the object of manufacture need not be uniformly coated with the carbon product. The carbon deposition area on the solid surface optionally may be limited to one or more regions by masking, or by selectively depositing the catalyst to promote the formation of the solid carbon on portions of the solid surface.
Solid carbon products may be collected and separated from the gas stream or from solid surfaces on which they form, such as by elutriation, centrifugation, electrostatic precipitation, or filtration. The techniques for separation of the solid product from the gas stream and the catalyst may depend on the type of reactor. For example, the solid carbon product may be harvested directly from a gas stream using electrophoretic or thermophoretic collectors, filters, etc., or by collecting the elutriates as they exit the reactor.
In one embodiment, a cyclone separator is used to separate and collect the solid carbon product. For a solid catalyst or solid-surface-mounted catalyst, the solid carbon product may be scraped or otherwise abraded from the surface of the solid carrier material. Alternatively, when using a solid catalyst, the solid carbon product may be rinsed off a surface with a solvent for further processing.
In some cases, it may be beneficial to remove the solid carbon product from the reaction gas mixture prior to cooling {e.g., by withdrawing the solid carbon product from the reactor through a purge chamber wherein the reaction gases are displaced by an inert purging gas such as argon, nitrogen, or helium). Purging prior to cooling helps reduce the deposit or growth of undesirable morphologies on the desired solid carbon product during the cooling process.
In aerosol or fluidized-bed reactors, the residence time in the growth zone may be controlled by one or more forces (such as gravitational, electromagnetic, or centrifugal forces) counteracting the motion of the gas stream. These forces counterbalance the gas flow to help control the residence time, so that the size of the solid carbon product may be controlled.
In another embodiment, catalysts are introduced into an aerosol reactor by an electrospray process. Coulomb forces separate a suspension or solution containing a catalyst powder into small droplets from which individual particles form. The electrospray helps keep the particles separated so that they do not tend to clump or fuse. The electrospray also tends to charge the resulting carbon particles and make them easier to harvest from the aerosol using electrostatic collectors.
In aerosol reactors, catalyst particles may be sprayed into a carrier gas or fluid for transport into the reaction zone. The catalyst may be preconditioned in a catalyst-conditioning process prior to mixing with the reaction gases. Catalyst conditioning by heating in an inert carrier gas may promote the growth of specific chiralities of single wall CNTs. For example, heating catalyst material in a helium environment may promote the growth of chiralities of CNTs having metallic properties. One or more substances may be introduced into the reaction zone to modify the physical properties of the desired solid carbon product, either through incorporation in the solid carbon product, or by surface deposition on the solid carbon product.
The physical properties of the solid carbon products may be substantially modified by the application of additional substances to the surface of the solid carbon. Modifying agents (e.g., ammonia, thiophene, nitrogen gas, and/or surplus hydrogen) may be added to the reaction gases to modify the physical properties of the resulting solid carbon. Modifications and functionalizations may be performed in the reaction zone or after the solid carbon products have been removed.
Some modifying agents may be introduced into the reduction reaction chamber near the completion of the solid carbon formation reaction by, for example, injecting a water stream containing a substance to be deposited, such as a metal ion. The substances may also be introduced as a component of a carrier gas. For example, surplus hydrogen may cause hydrogenation of a carbon lattice in some CNTs, causing the CNTs to have semiconductor properties.
Small amounts of substances (e.g., sulfur) added to the reaction zone may be catalyst promoters that accelerate the growth of carbon products on the catalysts. Such promoters may be introduced into the reactor in a wide variety of compounds. Such compounds may be selected such that the decomposition temperature of the compound is below the reaction temperature. For example, if sulfur is selected as a promoter for an iron-based catalyst, the sulfur may be introduced into the reaction zone as a thiophene gas, or as thiophene droplets in a carrier gas. Examples of sulfur-containing promoters include thiophene, hydrogen sulfide, heterocyclic sulfide, and inorganic sulfide. Other promoters include lead compounds and bismuth.
In some embodiments, a catalyst particle is removed from the surrounding matrix as a CNT grows, and the catalyst particle may become embedded in one of the ends of the CNT. Thus, some of the catalyst material may be physically removed during the reaction, and the catalyst may need to be continually replenished. The material on which a CNT grows may not be considered a catalyst in the classical sense, but is nonetheless referred to herein and in the art as a "catalyst," because the carbon is not believed to react with the material. Furthermore, CNTs may not form at all absent the catalyst. In scanning electron microscope images, catalyst ends appear significantly larger (e.g., 1.2 to 1.6 times the diameter) than the tubes that grow from them. This difference may be due to a carbon shell surrounding the catalyst, it may be indicative of a fundamental relationship between the catalyst particle size and that of the CNT that grows from it, or it may be due to some other factor or coincidence. Whatever the reason, one way to control the size of the CNTs appears to be through the control of the catalyst particle size, or grain size, keeping the catalyst particle size somewhat larger than the desired nanotube size.
A process for converting a carbon source to a solid carbon product may be advantageously performed in two or more stages. For example, FIG. 2 shows a system 100 that may be used in such a method. A carbon source 102 and a reducing agent 104 enter a first reactor 106. The carbon source 102 may include a feed mixture comprising gaseous C02, CO, and/or another carbon-containing compound. The reducing agent 104 may include H2, a hydrocarbon such as C¾, or any mixture thereof. The carbon source 102 and the reducing agent 104 may be combined before entering the first reactor 106 or may be mixed within the first reactor 106. In some embodiments, a single source material (e.g., syngas, a mixture of CO and H2) may serve as both the carbon source 102 and the reducing agent 104. The first reactor 106 may be any vessel configured to contain, mix, and/or react the carbon source 102 and the reducing agent 104. For example, the first reactor 106 may be a fluidized bed. The first reactor 106 may be adapted to provide conditions in which the carbon source 102 and the reducing agent 104 react to form a first reaction product mixture 108. For example, the first reactor 106 may include appropriate means for material handling, mixing, controlling temperature, controlling pressure, etc. The first reactor 106 may include one or more sensors, controllers, etc., and the conditions within the first reactor 106 may remain constant or may vary during processing. For example, controllers may be configured to maintain selected conditions, as indicated by signals received from the one or more sensors.
The first reaction product mixture 108 may include products of the reaction of the carbon source 102 and the reducing agent 104, and one or more of the reactants, such as CO, ¾0, C02, etc. In some embodiments, the carbon source 102 and the reducing agent 104 may react substantially to completion in the first reactor 106, consuming one or both of the carbon source 102 and the reducing agent 104. For example, the carbon source 102 may be provided in excess, and the reducing agent 104 may be substantially or entirely consumed stoichiometrically in the first reactor 106. In such embodiments, the first reaction product mixture 108 may include products (e.g., CO and H20) and a portion of the carbon source 102; the first reaction product mixture 108 leaving the first reactor 106 may be substantially free of the reducing agent 104.
The first reaction product mixture 108 may enter a first separator 110. The first separator 1 10 may be, for example, a condenser configured to separate a condensate 112 from a dry first reaction product mixture 114. The condensate 112 may include water or other condensable matter formed in the first reactor 106 or otherwise present in the first reaction product mixture 108. The dry first reaction product mixture 114 may include gases that do not condense at operating conditions of the first separator 110. For example, the dry first reaction product mixture 114 may include CO formed in the first reactor 106 and unreacted C02 remaining from the carbon source 102.
The dry first reaction product mixture 114 may enter a second reactor 116 with one or more of a second reducing agent 115 and a recirculated mixture 126. The second reducing agent 1 15 may include H2, a hydrocarbon such as CH4, or any mixture thereof. In some embodiments, the second reducing agent 115 may have the same composition as the reducing agent 104 introduced into the first reactor 106.
The second reactor 1 16 may be any vessel configured to contain, mix, and/or react the dry first reaction product mixture 1 14, the second reducing agent 115, and/or the recirculated mixture 126. For example, the second reactor 116 may be a fluidized bed. The second reactor 116 may be adapted to provide conditions in which the dry first reaction product mixture 114, the second reducing agent 115, and/or the recirculated mixture 126 may react to form solids 118 and a second reaction product mixture 120. For example, the second reactor 116 may include appropriate means for material handling, mixing, controlling temperature, controlling pressure, etc. The second reactor 116 may include one or more sensors, controllers, etc., and the conditions within the second reactor 116 may remain constant or may vary during processing. For example, controllers may be configured to maintain selected conditions, as indicated by signals received from the one or more sensors.
The solids 118 formed in the second reactor 116 may include one or more forms of solid carbon. For example, solids 118 may include graphite {e.g., pyrolytic graphite), graphene, carbon black, fibrous carbon, buckminsterfullerenes, single-wall CNTs, multi-wall CNTs, platelets, or nanodiamond. The type of solid carbon product formed may depend on various parameters of the reaction conditions, such as temperatures, pressures, flow rates, reactant compositions, etc. The solids 118 may be separated from the second reaction product mixture 120 within the second reactor 116 or in another device, by any appropriate separation methods.
The second reaction product mixture 120 may include products of the reaction of the dry first reaction product mixture 1 14, the second reducing agent 115, or the recirculated mixture 126, and one or more of the reactants, such as CO, H20, C02, H2, etc. In some embodiments, the dry first reaction product mixture 114 and the second reducing agent 115 may react substantially to completion in the second reactor 116, consuming one or both of the dry first reaction product mixture 114 and the second reducing agent 1 15. For example, the dry first reaction product mixture 114 may be provided in excess, and the second reducing agent 115 may be substantially or entirely consumed stoichiometrically in the second reactor 116. In such embodiments, the second reaction product mixture 120 may include products (e.g., H20) and a portion of the dry first reaction product mixture 1 14; the second reaction product mixture 120 leaving the second reactor 1 16 may be substantially free of the second reducing agent 115.
The second reaction product mixture 120 may enter a second separator 122.
The second separator 122 may be, for example, a condenser configured to separate a condensate 124 from the recirculated mixture 126. The condensate 124 may include water or other condensable matter formed in the second reactor 116 or otherwise present in the second reaction product mixture 120. The recirculated mixture 126 may include gases that do not condense at operating conditions of the second separator 122. For example, the recirculated mixture 126 may include CO and/or C02 that has not reacted to form solids 118.
FIG. 3 shows another system 140 that may be used in a method for converting gaseous carbon dioxide to solid carbon. Like the system 100 shown in FIG. 2, the system 140 includes a first reactor 106, a first separator 110, and a second reactor 116. The first reactor 106 and the first separator 110 may operate substantially as described above with respect to FIG. 2.
The dry first reaction product mixture 114 enters the second reactor 116 with one or more of the second reducing agent 115 and a compressed recirculated mixture 158. The second reducing agent 115 may include H2, a hydrocarbon such as CH4, or any mixture thereof.
The second reactor 116 may be any vessel configured to contain, mix, or react the dry first reaction product mixture 114, the second reducing agent 115, and the recirculated mixture 126, for example, a fluidized bed. An output 142 from the second reactor 1 16 may include reactants and/or products of the reaction, such as solid carbon, CO, H20, C02, H2, etc. The output 142 may enter a solid separator 144, where solids 146 may be separated from gases 148. For example, the solid separator 144 may be a cyclone. The solids 146 removed from the gases 148 in the solid separator 144 may include one or more forms of solid carbon, such as graphite (e.g., pyrolytic graphite), graphene, carbon black, fibrous carbon, buckminsterfullerenes, single- wall CNTs, or multi-wall CNTs. The gases 148 may include products of the reaction of the dry first reaction product mixture 1 14, the second reducing agent 1 15, or the compressed recirculated mixture 158, and one or more of the reactants. The gases 148 may enter a condenser 150. The condenser 150 may be configured to separate a condensate 152 from a recirculated mixture 154. The condensate 152 may include water or other condensable matter formed in the second reactor 1 16 or otherwise present in the gases 148. The recirculated mixture 154 may include gases that do not condense at operating conditions of the condenser 150. For example, the recirculated mixture 154 includes CO or C02 that has not reacted to form solids 146. The recirculated mixture 154 may enter a compressor 156. The compressor 156 may produce the compressed recirculated mixture 158 by increasing the pressure of the recirculated mixture 154. The pressure increase imparted by the compressor 156 may compensate for pressure drops within the system 140, such as within the second reactor 116, the cyclone 144, or the condenser 150. Though not shown in FIG. 3, the system 140 may include one or more additional compressors configured to provide materials at selected pressures (e.g., a compressor configured to compress the carbon source 102 and/or the reducing agent 104).
Components of the systems 100, 140 shown and described herein may operate at various temperatures and pressures. For example, the first reactor 106 or the second reactor 116 may operate at a temperature of at least 450°C, such as a temperature of at least 650°C, or a temperature of from about 680°C to about 700°C. The first reactor 106 or the second reactor 1 16 may operate at a pressure from about 0.28 MPa (40 psi) to about 0.41 MPa (60 psi), or at a pressure of about 4.1 MPa (600 psi). The first separator 110, the second separator 122, the solid separator 144, and the condenser 150 may operate at lower temperatures than the first reactor 106 and/or the second reactor 1 16. For example, the first separator 1 10, the second separator 122, the solid separator 144, and the condenser 150 may operate at temperatures of less than about 100°C, less than about 80°C, or even less than about 50°C. In some embodiments, heat may be recovered from one material and transferred to another.
For example, FIG. 4 shows a system 200 having heat-recovery features. A carbon source 102 and a reducing agent 104 enter a first heat exchanger 202. The first heat exchanger 202 may be a shell-and-tube heat exchanger, a plate heat exchanger, a plate-fin heat exchanger, a spiral heat exchanger, or any other type of heat transfer apparatus. The first heat exchanger 202 may be configured to operate in co-current flow, countercurrent flow, or cross flow. The carbon source 102 and the reducing agent 104 may be combined before entering the first heat exchanger 202, within the first heat exchanger 202, or after leaving the first heat exchanger 202. In the embodiment shown in FIG. 4, the carbon source 102 and the reducing agent 104 are mixed within the first heat exchanger 202, and a heated reactant mixture 204 leaves the first heat exchanger 202. The heated reactant mixture 204 may be hotter than either the carbon source 102 or the reducing agent 104 entering the first heat exchanger 202. For example, the heated reactant mixture 204 may be at a temperature of at least 300°C, such as a temperature of at least 500°C, or a temperature of from about 550°C to about 600°C. The heated reactant mixture 204 may be at a pressure from about 0.28 MPa (40 psi) to about 0.41 MPa (60 psi), or at a pressure of about 4.1 MPa (600 psi).
The heated reactant mixture 204 enters a first reactor 206, which may be similar to the first reactor 106, as shown and described in FIG. 2. That is, the first reactor 206 may be adapted to operate at conditions in which the carbon source 102 and the reducing agent 104 react to form a first reaction product mixture 208. The first reactor 206 may be heated to a temperature higher than the temperature of the heated reactant mixture 204 entering the first reactor 206. For example, the first reactor 206 may be heated to a temperature of at least 450°C, such as a temperature of at least 650°C, or a temperature of from about 680°C to about 700°C.
The first reaction product mixture 208 may leave the first reactor 206 at approximately the same temperature as the operating temperature of the first reactor 206. The first reaction product mixture 208 returns to the first heat exchanger 202 to recover heat from the first reaction product mixture 208. The heat from the first reaction product mixture 208 is transferred to the carbon source 102 and/or the reducing agent 104. Recovery of heat in the first heat exchanger 202 reduces the heating load necessary to maintain the first reactor 206 at a selected operating temperature. Thus, a system 200 having a first heat exchanger 202 as shown in FIG. 4 may have lower energy costs than a system without such a first heat exchanger 202. A cooled first reaction product mixture 210 leaves the first heat exchanger 202 at a temperature of less than about 200°C, such as a temperature of less than about 150°C, or a temperature of from about 80°C to about 120°C, and enters a condenser 212. The condenser 212 separates a condensate 214 (e.g., liquid water) from a dry first reaction product mixture 216 (e.g., gaseous C02, CO, etc.). The condenser 212 may be similar to the first separator 1 10, as shown and described in FIG. 2.
The condenser 212 may operate at a temperature of less than about 100°C, less than about 80°C, or even less than about 50°C. The condenser 212 may include one or more cooling 'means to control the operating temperature. Removal of heat from the first reaction product mixture 208 in the first heat exchanger 202 reduces the cooling load of the condenser 212 by reducing the temperature of the cooled first reaction product mixture 210. Thus, the first heat exchanger 202 may reduce cooling needs of the system 200.
The dry first reaction product mixture 216 enters a second heat exchanger 218, and may be heated or mixed with a reducing agent 220 or a recirculated mixture 240. The second heat exchanger 218 may be a shell-and-tube heat exchanger, a plate heat exchanger, a plate-fin heat exchanger, a spiral heat exchanger, or any other type of heat transfer apparatus. The second heat exchanger 218 may be configured to operate in co-current flow, countercurrent flow, or cross flow. The dry first reaction product mixture 216, the reducing agent 220, and the recirculated mixture 240 may be combined before entering the second heat exchanger 218, within the second heat exchanger 218, or after leaving the second heat exchanger 218. In the embodiment shown in FIG. 4, the dry first reaction product mixture 216, the reducing agent 220, and the recirculated mixture 240 are mixed within the second heat exchanger 218, and a heated second reactant mixture 222 leaves the second heat exchanger 218. The heated second reactant mixture 222 may be hotter than the dry first reaction product mixture 216, the reducing agent 220, or the recirculated mixture 240 entering the second heat exchanger 218. For example, the heated second reactant mixture 222 may be at a temperature of at least about 300°C, such as a temperature of at least about 500°C, or a temperature of from about 550°C to about 600°C. The heated second reactant mixture 222 may be at a pressure from about 0.28 MPa (40 psi) to about 0.41 MPa (60 psi), or at a pressure of about 4.1 MPa (600 psi).
The heated second reactant mixture 222 enters a second reactor 224, which may be similar to the second reactor 1 16, as shown and described in FIG. 2. That is, the second reactor 224 may be adapted to operate at conditions in which components of the heated second reactant mixture 222 react to form solid carbon and other products. The reaction products may leave the second reactor 224 as second reaction product mixture 226. The second reactor 224 may be heated to a temperature higher than the temperature of the heated second reactant mixture 222 entering the second reactor 224. For example, the second reactor 224 may be heated to a temperature of at least 450°C, such as a temperature of at least 650°C, or a temperature of from about 680°C to about 700°C. Recovery of heat in the second heat exchanger 218 may reduce the heating load necessary to maintain the second reactor 224 at a selected operating temperature. Thus, a system 200 having a second heat exchanger 218 as shown in FIG. 4 may have lower energy costs than a system without such a second heat exchanger 218.
The second reaction product mixture 226 may enter a cyclone 228, and solids 230 may be separated from gases 232. The gases 232 enter the second heat exchanger 218, and heat from the gases 232 may be recovered and transferred to the dry first reaction product mixture 216, the reducing agent 220, and/or the recirculated mixture 240. Cooled gases 234 leaving the second heat exchanger 218 enter a second condenser 236, where condensate 238 is separated from the recirculated mixture 240.
The system 200 may include one or more compressors to compensate for the pressure drop within the system 200. For example, pressure drop may occur within the heat exchangers 202, 218, the reactors 206, 224, the condensers 212, 236, cyclone 228, and/or related piping, valves, sensors, controllers, etc.
Separating the process for converting gaseous carbon dioxide into two or more stages, as shown in FIGS. 2 through 4, may have various benefits. For example, because of thermodynamics or kinetics, a single reactor in which the entire conversion process occurs may be technically difficult or economically infeasible for some applications. As described above, the Bosch reaction of carbon dioxide with hydrogen is a two-step reaction. The first reaction:
C02 + H2 <→ CO + H20 (Equation 2), the reverse water-gas shift reaction, may have a reaction rate much faster than the second reaction. The second reaction:
CO + H2 <→ C(s) + H20 (Equation 3),
may control the overall reaction rate of the process. By separating the process into two stages, the two reactions may be isolated. The first reactors 106, 206 may be relatively smaller than the second reactors 1 16, 224, yet the first reaction may still proceed substantially to completion in the first reactors 106, 206. Smaller reactors may be less costly to produce, maintain, and operate.
Furthermore, the removal of condensate between the two reactions may allow the second reaction to occur in an environment having a lower overall water vapor concentration than would occur in a single reactor. A lower water vapor concentration may be beneficial because water is a product of both Equation 2 and Equation 3. Thus, to the extent the reactions are governed by thermodynamics (i.e., by equilibrium conditions), lower water vapor concentrations drive the reactions further to completion (i.e., to the right). Lower water vapor concentrations may also be beneficial in limiting or preventing oxidation of metals (e.g., of reaction vessels or catalysts). Thus, a lower water vapor concentration may contribute to the efficiency of the process and to lower maintenance costs.
A reactor may be coupled with heating and cooling mechanisms to control the temperature of the reactor. For example, a reactor may be configured such that products and excess reactant are recycled through a cooling mechanism to condense water vapor. The products and/or excess reactant may then be reheated and recycled through the reactor. By removing some of the water vapor in the recycled gases, the morphology of solid carbon formed may be controlled. Changing the partial pressure of water vapor changes the carbon activity of a mixture. The reactor may also be coupled to a carbon collector in which water and unreacted reactants are separated from the carbon products. The separated carbon products are collected and removed from the system.
The methods disclosed herein may be incorporated into power production, chemical processes, and manufacturing processes in which the combustion of a primary hydrocarbon fuel source is the primary source of heat. The resulting combustion gases from such processes contain carbon oxides that may act as sources of carbon for the manufacture of the desired solid carbon product. The methods are scalable for many different production capacities so that, for example, plants designed with this method in mind may be sized to handle the carbon oxide emissions from the combustion processes of a large coal-fired power plant or those from an internal combustion engine. For example, the methods may be used to reduce carbon dioxide from the atmosphere, combustion gases, process off-gases, exhaust gases from the manufacture of Portland cement, and well gases, or from separated fractions thereof.
In another embodiment, the carbon oxides from a source gas mixture are separated from the source mixture and concentrated to form the carbon oxide feedstock for the reduction process. The carbon oxides in the source gases may be concentrated through various means known to the art. In yet another embodiment, the catalytic conversion process may be employed as an intermediate step in a multi-stage power extraction process wherein the first stages cool the combustion gases to the reaction temperature of the reduction process for the formation of the desired solid carbon product. The cooled combustion gases, at the desired temperature of the reduction reaction, may then be passed through the reduction process and subsequently passed through additional power extraction stages.
Coupling this method with a hydrocarbon combustion process for electrical power production has the additional advantage that the hydrogen required for the reduction process may be formed by the electrolysis of water using off-peak power. The oxygen formed in the electrolysis process may be used as at least a portion of the combustible mixture for the combustion process.
When the methods disclosed herein are coupled with a combustion or chemical process that uses hydrocarbons, a portion of the hydrocarbons of the process may be used as the reducing agent gas. This may include the pyrolysis of the hydrocarbons to form a hydrogen gas that is provided as the reducing agent gas. The process of this disclosure may be adapted to various available hydrocarbon sources.
EXAMPLE
Methane gas is mixed with carbon dioxide gas in a ratio of 1 :1 inside a first tube furnace lined with a ceramic material, maintained at about 680°C, and containing steel wool therein. The methane gas reacts with the carbon dioxide gas in the presence of the steel wool to form a reaction gas mixture of carbon monoxide, water, and hydrogen. The reaction gas mixture enters a condenser operating at about 50°C to remove liquid water from the reaction gas mixture. The dried reaction gas mixture enters a second tube furnace lined with a ceramic material, maintained at about 680°C, and containing steel wool therein. The carbon monoxide and hydrogen in the dried reaction gas mixture react in the presence of the steel wool to form single-wall carbon nanotubes and a tail gas mixture of water with some residual hydrogen and carbon monoxide. The carbon nanotubes collect on surfaces of the steel wool. The tail gas mixture enters a condenser operating at about 50°C to remove liquid water from the tail gas mixture. The dried tail gas mixture is recycled to the second tube furnace.
After the process has proceeded for a period of time, flow of gas is stopped, furnaces and condensers are cooled to room temperature, and the system is purged with an inert gas. The steel wool is removed from the second tube furnace, and the carbon nanotubes are physically removed from the steel wool. Any remaining metal on the carbon nanotubes may be removed, if desired, by washing with acid.
Although the foregoing description contains specific details, these are not to be construed as limiting the scope of the present invention, but merely as providing certain embodiments. Similarly, other embodiments of the invention may be devised which do not depart from the scope of the present invention. For example, features described herein with reference to one embodiment also may be provided in others of the embodiments described herein. The scope of the invention is, therefore, indicated and limited only by the appended claims and their legal equivalents, rather than by the foregoing description. All additions, deletions, and modifications to the invention, as disclosed herein, which fall within the meaning and scope of the claims, are encompassed by the present invention.

Claims

What is claimed is: 1. A two-stage reaction process comprising:
reacting a first feed mixture comprising carbon dioxide with a hydrogen-containing reducing agent under first reaction conditions to convert at least a portion of the first feed mixture to a first tail gas comprising carbon monoxide and water vapor;
condensing at least a portion of the water from the first tail gas to form a dried first tail gas; and
reacting the dried first tail gas under second reaction conditions to convert at least a portion of the carbon monoxide in the dries first tail gas to solid carbon and a second tail gas comprising water vapor.
2. The process of claim 1, wherein reacting carbon dioxide with a hydrogen-containing reducing agent comprises reacting a molar quantity of the carbon dioxide higher than a molar quantity of the reducing agent.
3. The process of claim 1 , wherein reacting the carbon dioxide with the hydrogen-containing reducing agent comprises reacting the carbon dioxide with hydrogen gas (H2).
4. The process of claim 1 , wherein reacting the carbon dioxide with the hydrogen-containing reducing agent comprises reacting the carbon dioxide with a hydrocarbon.
5. The process of claim 1, further comprising condensing at least a portion of the water from the second tail gas to form a dried second tail gas.
6. The process of claim 5, further comprising mixing the second tail gas with the dried first tail gas.
7. The process of claim 1 , wherein the first reaction conditions include a temperature range adapted to promote formation of carbon monoxide in the presence of a first metal.
8. The process of claim 7, wherein the temperature range is from about 400°C to about 1,200°C.
9. The process of claim 7, wherein the first metal comprises a material selected from the group consisting of elements of groups 5, 6, 7, 8, 9, and 10 of the periodic table, lanthanides, and actinides, and oxides, alloys, and mixtures of any such elements.
10. The process of claim 1 , wherein the second reaction conditions include a temperature range adapted to promote formation of the solid carbon in the presence of a second metal.
11. The process of claim 10, wherein the temperature range is from about 400°C to about 1000°C.
12. The process of claim 10, wherein the temperature range is from about 550°C to about 700°C.
13. The process of claim 10, wherein the second metal comprises a material selected from the group consisting of elements of groups 5, 6, 7, 8, 9, and
10 of the periodic table, lanthanides, and actinides, and oxides, alloys, and mixtures of any such elements.
14. A method for two-stage reduction of carbon dioxide, the method comprising:
reacting a feed gas mixture comprising carbon dioxide and a reducing gas to form a reaction mixture comprising carbon monoxide and water; condensing at least a portion of the water from the reaction mixture to form a dried reaction mixture;
mixing the dried reaction mixture with a recirculating gas stream to form a catalytic converter feed gas mixture;
flowing the catalytic converter feed gas mixture through a catalytic converter in the presence of a catalyst to form solid carbon and a tail gas comprising water; and
flowing the tail gas through a heat exchanger to condense a portion of the water therefrom and form the recirculating gas stream.
15. The method of claim 14, wherein the catalyst comprises a metal.
16. The method of claim 14, wherein flowing the catalytic converter feed gas mixture through a catalytic converter in the presence of a catalyst comprises converting at least a portion of the carbon monoxide and at least a portion of the reducing gas to solid carbon and water.
17. The method of claim 14, wherein flowing the catalytic converter feed gas mixture through a catalytic converter in the presence of a catalyst comprises forming carbon nanotubes.
18. The method of claim 14, further comprising mixing an additional reducing gas with the catalytic converter feed gas mixture.
19. The method of claim 14, wherein the reducing gas comprises at least one of hydrogen, a hydrocarbon, and an alcohol.
20. The method of claim 14, further comprising separating the solid carbon from the tail gas mixture.
21. A two-stage reaction process for converting gaseous carbon dioxide and hydrogen to solid carbon and water, the process comprising: reacting a first feed mixture comprising gaseous carbon dioxide and hydrogen under first reaction conditions to convert at least a portion of the carbon dioxide and the hydrogen therein to carbon monoxide and water vapor in a first tail gas;
condensing at least a portion of the water from the first tail gas to form a dried first tail gas;
mixing the dried first tail gas with a dried second tail gas to form a second feed mixture;
reacting the second feed mixture under second reaction conditions to convert at least a portion of carbon oxides in the second feed mixture to solid carbon and a second tail gas comprising water and unreacted gases from the second feed mixture; and
condensing at least a portion of the water from the second tail gas to form the dried second tail gas.
22. The process of claim 21 , wherein reacting a first feed mixture comprises reacting the first feed mixture in a first reaction zone, and reacting the second feed mixture comprises reacting the second feed mixture in a second reaction zone.
23. A two-stage reaction process for converting gaseous carbon dioxide and methane to solid carbon and water, the process comprising:
reacting a first feed mixture comprising gaseous carbon dioxide and methane under first reaction conditions to convert at least a portion of the carbon dioxide and the methane therein to carbon monoxide and water vapor in a first tail gas;
condensing at least a portion of the water from the first tail gas to form a dried first tail gas;
mixing the dried first tail gas with a dried second tail gas to form a second feed
mixture;
reacting the second feed mixture under second reaction conditions to convert at least a portion of carbon oxides in the second feed gas to solid carbon and a second tail gas comprising water and unreacted gases from the second feed mixture; and
condensing at least a portion of the water from the second tail gas to form the dried second tail gas.
24. The process of claim 21 or claim 23, further comprising venting a vent gas to control the buildup of inert gases in the second feed mixture, wherein the vent gas comprises a portion of a gas selected from the group consisting of the first tail gas, the second tail gas, the dried first tail gas, the dried second tail gas, and the second feed mixture.
25. The process of claim 21 or claim 23, further comprising compressing the dried second tail gas.
26. The process of claim 21 or claim 23, wherein the solid carbon comprises carbon nanotubes.
27. The process of claim 21 or claim 23, wherein the solid carbon comprises at least one allotrope and morphology of essentially pure carbon comprising at least one material selected from the group consisting of graphite, graphene, carbon black, soot, fibrous carbon, buckminsterfullerenes, carbon nanotubes, carbon platelets, amorphous carbon, and nanodiamond.
PCT/US2013/000077 2012-04-16 2013-03-15 Method for producing solid carbon by reducing carbon dioxide WO2013158160A1 (en)