WO2013117757A1 - Composition and method for removal of organic paint coatings from substrates - Google Patents
Composition and method for removal of organic paint coatings from substrates Download PDFInfo
- Publication number
- WO2013117757A1 WO2013117757A1 PCT/EP2013/052678 EP2013052678W WO2013117757A1 WO 2013117757 A1 WO2013117757 A1 WO 2013117757A1 EP 2013052678 W EP2013052678 W EP 2013052678W WO 2013117757 A1 WO2013117757 A1 WO 2013117757A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- composition
- foregoing
- stripping
- composition according
- surfactants
- Prior art date
Abstract
Description
Claims