WO2013005409A1 - Procédé pour fabriquer une feuille de verre - Google Patents

Procédé pour fabriquer une feuille de verre Download PDF

Info

Publication number
WO2013005409A1
WO2013005409A1 PCT/JP2012/004262 JP2012004262W WO2013005409A1 WO 2013005409 A1 WO2013005409 A1 WO 2013005409A1 JP 2012004262 W JP2012004262 W JP 2012004262W WO 2013005409 A1 WO2013005409 A1 WO 2013005409A1
Authority
WO
WIPO (PCT)
Prior art keywords
wall surface
molten glass
glass
molded body
guides
Prior art date
Application number
PCT/JP2012/004262
Other languages
English (en)
Japanese (ja)
Inventor
浩幸 苅谷
Original Assignee
ＡｖａｎＳｔｒａｔｅ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ＡｖａｎＳｔｒａｔｅ株式会社 filed Critical ＡｖａｎＳｔｒａｔｅ株式会社
Priority to KR1020127021627A priority Critical patent/KR101372609B1/ko
Priority to JP2012530017A priority patent/JP5452724B2/ja
Priority to CN201280003051.9A priority patent/CN103140447B/zh
Publication of WO2013005409A1 publication Critical patent/WO2013005409A1/fr

Abstract

Selon l'invention, un ruban de verre est formé à partir de verre liquide de telle manière que le verre liquide est amené à déborder d'une rainure d'alimentation dans la partie supérieure d'un corps de formation, que le verre liquide est autorisé à s'écouler vers le bas le long des surfaces de paroi des deux côtés de la partie inférieure du corps de formation, tandis que l'écoulement du verre liquide est restreint par une paire de guides faisant saillie à partir des surfaces de paroi du corps de formation, que le verre liquide est conduit vers l'extrémité la plus basse du bord de formation, et que les courants du verre liquide s'écoulant le long des surfaces de paroi des deux côtés se réunissent à l'extrémité la plus basse. Les surfaces de paroi du corps de formation le long desquelles s'écoule le verre liquide comprennent : des surfaces de paroi verticales le long desquelles le verre liquide s'écoule vers le bas dans la direction verticale ; et des surfaces de paroi inclinées pour conduire le verre liquide, qui s'est écoulé vers le bas le long des surfaces de paroi verticales, jusqu'à l'extrémité la plus basse du corps de formation. Dans la totalité de la région dans laquelle les guides font saillie à partir des surfaces de paroi inclinées, la hauteur de la paire de guides à partir des surfaces de paroi est établie de façon à être inférieure à l'épaisseur du verre liquide.
PCT/JP2012/004262 2011-07-01 2012-06-29 Procédé pour fabriquer une feuille de verre WO2013005409A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
KR1020127021627A KR101372609B1 (ko) 2011-07-01 2012-06-29 유리판의 제조 방법
JP2012530017A JP5452724B2 (ja) 2011-07-01 2012-06-29 ガラス板の製造方法
CN201280003051.9A CN103140447B (zh) 2011-07-01 2012-06-29 玻璃板的制造方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2011-147781 2011-07-01
JP2011147781 2011-07-01

Publications (1)

Publication Number Publication Date
WO2013005409A1 true WO2013005409A1 (fr) 2013-01-10

Family

ID=47436774

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2012/004262 WO2013005409A1 (fr) 2011-07-01 2012-06-29 Procédé pour fabriquer une feuille de verre

Country Status (5)

Country Link
JP (1) JP5452724B2 (fr)
KR (1) KR101372609B1 (fr)
CN (1) CN103140447B (fr)
TW (1) TWI429602B (fr)
WO (1) WO2013005409A1 (fr)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2014163063A1 (fr) * 2013-04-01 2014-10-09 日本電気硝子株式会社 Procédé de formation d'un verre en feuille et dispositif associé
KR20150112895A (ko) * 2014-03-29 2015-10-07 아반스트레이트 가부시키가이샤 유리판의 제조 방법 및 유리판의 제조 장치
WO2016054130A1 (fr) * 2014-09-30 2016-04-07 Corning Incorporated Goulotte d'écoulement avec bordure à l'extrémité de compression et procédé pour former un ruban de verre
WO2017087556A1 (fr) 2015-11-16 2017-05-26 Q30 Sports Science, Llc Dispositifs de protection de lésions cérébrales traumatiques
WO2024010704A1 (fr) * 2022-07-08 2024-01-11 Corning Incorporated Procédés et appareil de fabrication d'un ruban de verre

Families Citing this family (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2017087585A1 (fr) 2015-11-20 2017-05-26 Corning Incorporated Rubans de verre feuilleté et appareils pour former des rubans de verre feuilleté
TW201722863A (zh) * 2015-11-24 2017-07-01 康寧公司 形成玻璃物件的方法
WO2017091524A1 (fr) * 2015-11-24 2017-06-01 Corning Incorporated Appareil et procédé pour la mise en forme d'un article en verre
JP2017119617A (ja) * 2015-12-28 2017-07-06 ＡｖａｎＳｔｒａｔｅ株式会社 ガラス基板の製造方法、及び、ガラス基板の製造装置
KR20200078677A (ko) 2017-11-22 2020-07-01 코닝 인코포레이티드 유리 리본들을 성형하기 위한 에지 디렉터들을 포함하는 장치
CN108996895B (zh) * 2018-08-01 2021-10-08 彩虹显示器件股份有限公司 一种玻璃基板溢流成型析晶控制装置

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2009132595A (ja) * 2007-10-29 2009-06-18 Nippon Electric Glass Co Ltd ガラス製造用耐火材、その製造方法、ガラス熔融炉及びガラス物品の製造方法
JP2010189220A (ja) * 2009-02-18 2010-09-02 Avanstrate Inc ガラス成形装置

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8397538B2 (en) * 2009-02-26 2013-03-19 Corning Incorporated Apparatus and method for drawing a ribbon of glass

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2009132595A (ja) * 2007-10-29 2009-06-18 Nippon Electric Glass Co Ltd ガラス製造用耐火材、その製造方法、ガラス熔融炉及びガラス物品の製造方法
JP2010189220A (ja) * 2009-02-18 2010-09-02 Avanstrate Inc ガラス成形装置

Cited By (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2014163063A1 (fr) * 2013-04-01 2014-10-09 日本電気硝子株式会社 Procédé de formation d'un verre en feuille et dispositif associé
JPWO2014163063A1 (ja) * 2013-04-01 2017-02-16 日本電気硝子株式会社 板ガラスの成形方法、及び板ガラスの成形装置
KR20150112895A (ko) * 2014-03-29 2015-10-07 아반스트레이트 가부시키가이샤 유리판의 제조 방법 및 유리판의 제조 장치
KR101661062B1 (ko) 2014-03-29 2016-09-28 아반스트레이트 가부시키가이샤 유리판의 제조 방법 및 유리판의 제조 장치
WO2016054130A1 (fr) * 2014-09-30 2016-04-07 Corning Incorporated Goulotte d'écoulement avec bordure à l'extrémité de compression et procédé pour former un ruban de verre
US10703664B2 (en) 2014-09-30 2020-07-07 Corning Incorporated Isopipe with curb at the compression end and method for forming a glass ribbon
WO2017087556A1 (fr) 2015-11-16 2017-05-26 Q30 Sports Science, Llc Dispositifs de protection de lésions cérébrales traumatiques
WO2024010704A1 (fr) * 2022-07-08 2024-01-11 Corning Incorporated Procédés et appareil de fabrication d'un ruban de verre

Also Published As

Publication number Publication date
JPWO2013005409A1 (ja) 2015-02-23
KR20130024881A (ko) 2013-03-08
TW201309605A (zh) 2013-03-01
JP5452724B2 (ja) 2014-03-26
CN103140447B (zh) 2016-02-17
TWI429602B (zh) 2014-03-11
KR101372609B1 (ko) 2014-03-10
CN103140447A (zh) 2013-06-05

Similar Documents

Publication Publication Date Title
JP5452724B2 (ja) ガラス板の製造方法
KR101300980B1 (ko) 글래스 기판의 제조 방법
US9061931B2 (en) Methods for reducing zirconia defects in glass sheets
KR102483260B1 (ko) 무알칼리 유리 기판의 제조방법
JP5890559B2 (ja) ガラス基板の製造方法
JP7197835B2 (ja) ガラス板の製造方法
TW201739714A (zh) 玻璃
KR102291453B1 (ko) 유리 기판의 제조 방법 및 유리 기판의 제조 장치
KR101559198B1 (ko) 글래스판의 제조 방법
JP2014189483A (ja) ガラス板製造方法、および、ガラス板製造装置
JP6489783B2 (ja) ガラス基板の製造方法、および、ガラス基板の製造装置
JP6577215B2 (ja) ガラス基板の製造方法
KR20170003405A (ko) 유리 기판의 제조 방법
JP6498933B2 (ja) ディスプレイ用ガラス基板の製造方法および製造装置
JP5192100B2 (ja) ガラス基板の製造方法
JP6352755B2 (ja) ガラス基板の製造方法、および、ガラス基板の製造装置
KR20130115118A (ko) 유리판의 제조 방법
US20170044044A1 (en) Apparatus and method of manufacturing composite glass articles

Legal Events

Date Code Title Description
ENP Entry into the national phase

Ref document number: 2012530017

Country of ref document: JP

Kind code of ref document: A

WWE Wipo information: entry into national phase

Ref document number: 201280003051.9

Country of ref document: CN

ENP Entry into the national phase

Ref document number: 20127021627

Country of ref document: KR

Kind code of ref document: A

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 12807283

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 12807283

Country of ref document: EP

Kind code of ref document: A1