WO2012159032A1 - Feminine hygiene absorbent article comprising a superabsorbent foam of high swell rate - Google Patents
Feminine hygiene absorbent article comprising a superabsorbent foam of high swell rate Download PDFInfo
- Publication number
- WO2012159032A1 WO2012159032A1 PCT/US2012/038573 US2012038573W WO2012159032A1 WO 2012159032 A1 WO2012159032 A1 WO 2012159032A1 US 2012038573 W US2012038573 W US 2012038573W WO 2012159032 A1 WO2012159032 A1 WO 2012159032A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- absorbent article
- feminine hygiene
- hygiene absorbent
- article according
- foam
- Prior art date
Abstract
Description
Claims