Publication number: WO2012102944A1
Application number: PCT/US2012/021953
Authority: WO
Inventors: Abhishek Roy; Steven D. Jons; Joseph D. KOOB; Mou PAUL; XiaoHua Sam QIU; Steven Rosenberg
Original assignee: Dow Global Technologies LLC
Current assignee: Dow Global Technologies LLC
Priority date: 2011-01-24
Filing date: 2012-01-20
Publication date: 2012-08-02
Anticipated expiration: 2013-07-24
Also published as: CN103328081A; KR101920194B1; EP2632577B1; US8968828B2; CN103328081B; ES2523453T3; EP2632577A1; JP5912133B2; JP2014510619A; US20130287945A1; KR20140016274A

Abstract

A method for making a composite polyamide membrane comprising the steps of applying a polyfunctional amine monomer and polyfunctional acyl halide monomer to a surface of the porous support and interfacially polymerizing the monomers to form a thin film polyamide layer, wherein the method is includes at least one of the following steps: i) conducting the interfacial polymerization in the presence of a C₂-C₂₀ aliphatic monomer comprising at least one carboxylic acid functional group or salt thereof, and a single amine-reactive functional group; and ii) applying a C₂-C₂₀ aliphatic monomer comprising at least one carboxylic acid functional group or salt thereof, and a single amine-reactive functional group to the thin film polyamide layer. Many additional embodiments are described including applications for such membranes.

Description

COMPOSITE POLY AMIDE MEMBRANE

FIELD:

The present invention is generally directed toward composite polyamide membranes along with methods for making and using the same.

INTRODUCTION:

Composite polyamide membranes are used in a variety of fluid separations. One common class of membranes includes a porous support coated with a "thin film" polyamide layer. The thin film layer may be formed by an interfacial polycondensation reaction between polyfunctional amine (e.g. m-phenylenediamine) and poly-functional acyl halide (e.g. trimesoyl chloride) monomers which are sequentially coated upon the support from immiscible solutions, see for example US 4277344 to Cadotte. Various constituents may be added to one or both of the coating solutions to improve membrane performance. For example, US 4259183 to Cadotte describes the use of combinations of bi- and tri-functional acyl halide monomers, e.g. isophthaloyl chloride or terephthaloyl chloride with trimesoyl chloride. US 6878278 to Mickols describes the addition of a wide range of complexing agents to the acyl halide coating solution, including various phosphorous containing species. US 2011/0049055 describes the addition of moieties derived from sulfonyl, sulfinyl, sulfenyl, sulfuryl, phosphoryl, phosphonyl, phosphinyl, thiophosphoryl, thiophosphonyl and carbonyl halides. US 6521130 describes the addition of a carboxylic acid (e.g. aliphatic and aromatic carboxylic acids) or carboxylic acid ester to one or both monomer coating solutions prior to polymerization. Similarly, US 6024873, US 5989426, US 5843351 and US 5576057 describes the addition of selected alcohols, ethers, ketones, esters, halogenated hydrocarbons, nitrogen- containing compounds and sulfur-containing compounds having solubility parameters of 8 to 14 (cal/cm³)^{1 2} to one of the coating solutions. US 2009/0107922 describes the addition of various "chain capping reagents" to one or both coating solutions, e.g. 1,3 propane sultone, benzoyl chloride, 1 ,2-bis(bromoacetoxy) ethane, etc. US 4606943 and US 6406626 describe the formation of a thin film polyamide using a polyfunctional amine and polyfunctional acyl halide along with a polyfunctional acid anhydride halide (e.g. trimelletic anhydride acid chloride). US 2009/0272692, US 2010/0062156, US 2011/0005997, WO 2009/129354, WO 2010/120326 and WO 2010/120327 describe the use of various polyfunctional acyl halides and their corresponding partially hydrolyzed counterparts. US 4812270 to Cadotte describes post-treating the membrane with phosphoric acid. US 5582725 describes a similar post treatment with an acyl halide such as benzoyl chloride. SUMMARY:

The invention includes a method for making a composite polyamide membrane comprising the steps of applying a polyfunctional amine and acyl halide monomer to a surface of a porous support and interfacially polymerizing the monomers to form a thin film polyamide layer. The method further includes at least one of the following steps: i) conducting the interfacial polymerization in the presence of a C₂-C₂o aliphatic monomer comprising at least one carboxylic acid functional group or salt thereof and a single amine-reactive functional group; and/or ii) applying a such an aliphatic monomer to the thin film polyamide layer. The invention includes many additional embodiments.

DETAILED DESCRIPTION:

The invention is not particularly limited to a specific type, construction or shape of composite membrane or application. For example, the present invention is applicable to flat sheet, tubular and hollow fiber polyamide membranes useful in a variety of applications including forward osmosis

(FO), reverse osmosis (RO), nano filtration (NF), ultra filtration (UF) and micro filtration (MF) fluid separations. However, the invention is particularly useful for membranes designed for RO and NF separations. RO composite membranes are relatively impermeable to virtually all dissolved salts and typically reject more than about 95% of salts having monovalent ions such as sodium chloride. RO composite membranes also typically reject more than about 95% of inorganic molecules as well as organic molecules with molecular weights greater than approximately 100 Daltons. NF composite membranes are more permeable than RO composite membranes and typically reject less than about 95% of salts having monovalent ions while rejecting more than about 50% (and often more than 90%) of salts having divalent ions - depending upon the species of divalent ion. NF composite membranes also typically reject particles in the nanometer range as well as organic molecules having molecular weights greater than approximately 200 to 500 Daltons.

Examples of composite polyamide membranes include FilmTec Corporation FT-30™ type membranes, i.e. a flat sheet composite membrane comprising a bottom layer (back side) of a nonwoven backing web (e.g. PET scrim), a middle layer of a porous support having a typical thickness of about 25-125 μιη and top layer (front side) comprising a thin film polyamide layer having a thickness typically less than about 1 micron, e.g. from 0.01 micron to 1 micron but more commonly from about 0.01 to 0.1 μιη. The porous support is typically a polymeric material having pore sizes which are of sufficient size to permit essentially unrestricted passage of permeate but not large enough so as to interfere with the bridging over of a thin film polyamide layer formed thereon. For example, the pore size of the support preferably ranges from about 0.001 to 0.5 μιη. Non-limiting examples of porous supports include those made of: polysulfone, polyether sulfone, polyimide, polyamide, polyetherimide, polyacrylonitrile, poly(methyl methacrylate), polyethylene, polypropylene, and various halogenated polymers such as polyvinylidene fluoride. For RO and NF applications, the porous support provides strength but offers little resistance to fluid flow due to its relatively high porosity.

Due to its relative thinness, the polyamide layer is often described in terms of its coating coverage or loading upon the porous support, e.g. from about 2 to 5000 mg of polyamide per square meter surface area of porous support and more preferably from about 50 to 500 mg/m . The polyamide layer is preferably prepared by an interfacial polycondensation reaction between a polyiunctional amine monomer and a polyiunctional acyl halide monomer upon the surface of the porous support as described in US 4277344 and US 6878278. More specifically, the polyamide membrane layer may be prepared by interfacially polymerizing a polyiunctional amine monomer with a polyiunctional acyl halide monomer, (wherein each term is intended to refer both to the use of a single species or multiple species), on at least one surface of a porous support. As used herein, the term "polyamide" refers to a polymer in which amide linkages (— C(0)NH— ) occur along the molecular chain. The polyiunctional amine and polyiunctional acyl halide monomers are most commonly applied to the porous support by way oi a coating step from solution, wherein the polyiunctional amine monomer is typically coated from an aqueous-based or polar solution and the polyiunctional acyl halide from an organic-based or non-polar solution. Although the coating steps need not follow a specific order, the polyiunctional amine monomer is preierably first coated on the porous support followed by the polyiunctional acyl halide. Coating can be accomplished by spraying, film coating, rolling, or through the use oi a dip tank among other coating techniques. Excess solution may be removed from the support by air kniie, dryers, ovens and the like.

The polyiunctional amine monomer comprises at least two primary or secondary amino groups and may be aromatic (e.g., m-phenylenediamine, p-phenylenediamine, 1,3,5-triaminobenzene, 1,3,4-triaminobenzene, 3,5-diaminobenzoic acid, 2,4-diaminotoluene, 2,4-diaminoanisole, and xylylenediamine) or aliphatic (e.g., ethylenediamine, propylenediamine, and tris (2-diaminoethyl) amine). Examples oi preierred polyiunctional amine monomers include primary amines having two or three amino groups, for example, m-phenylene diamine, and secondary aliphatic amines having two amino groups such as piperazine. One preierred polyiunctional amine is m-phenylene diamine (mPD). The polyiunctional amine monomer may be applied to the porous support as a polar solution. The polar solution may contain from about 0.1 to about 20 weight percent and more preierably from about 0.5 to about 6 weight percent polyiunctional amine monomer. Once coated on the porous support, excess solution may be optionally removed.

The polyiunctional acyl halide monomer comprises at least two acyl halide groups and is preierably coated from an organic-based or non-polar solvent although the polyiunctional acyl halide may be delivered from a vapor phase (e.g., for polyiunctional acyl halides having sufficient vapor pressure). The polyiunctional acyl halide is not particularly limited and aromatic or alicyclic polyiunctional acyl halides can be used along with combinations thereoi. Non-limiting examples of aromatic polyiunctional acyl halides include: trimesic acid chloride, terephthalic acid chloride, isophthalic acid chloride, biphenyl dicarboxylic acid chloride, and naphthalene dicarboxylic acid dichloride. Non-limiting examples oi alicyclic polyiunctional acyl halides include: cyclopropane tri carboxylic acid chloride, cyclobutane tetra carboxylic acid chloride, cyclopentane tri carboxylic acid chloride, cyclopentane tetra carboxylic acid chloride, cyclohexane tri carboxylic acid chloride, tetrahydrofuran tetra carboxylic acid chloride, cyclopentane dicarboxylic acid chloride, cyclobutane dicarboxylic acid chloride, cyclohexane dicarboxylic acid chloride, and tetrahydrofuran dicarboxylic acid chloride. One preferred polyfunctional acyl halide is trimesoyl chloride (TMC). The polyfunctional acyl halide may be dissolved in a non-polar solvent in a range from about 0.01 to 10 weight percent, preferably 0.05 to 3 weight percent and may be delivered as part of a continuous coating operation. Suitable solvents are those which are capable of dissolving the polyfunctional acyl halide and which are immiscible with water, e.g. hexane, cyclohexane, heptane and halogenated hydrocarbons such as the FREON series. Preferred solvents include those which pose little threat to the ozone layer and which are sufficiently safe in terms of flashpoints and flammability to undergo routine processing without taking special precautions. A preferred solvent is ISOPAR™ available from Exxon Chemical Company.

The non-polar solution may include additional materials including co-solvents, phase transfer agents, solubilizing agents and complexing agents wherein individual additives may serve multiple functions. Representative co-solvents include: benzene, toluene, xylene, mesitylene, ethyl benzene- diethylene glycol dimethyl ether, cyclohexanone, ethyl acetate, butyl carbitol™ acetate, methyl laurate and acetone. US 6878278, US 6723241, US 6562266 and US 6337018 describe the addition of a broad range of representative complexing agents that may combined with the non-polar solution prior to conducting the interfacial polymerization. A class of such complexing agents is represented by Formula (I).

Formula (I):

α( _χβ) _y

where a is a non-sulfur containing binding core selected from elements falling within: (a) Group IIIA-VIB (i.e., Groups IIIA, IVA, VA, VIA, VIIA, VIIIA, IB, IIB, IIIB, IVB, VB, VIB) and (b) Periods 3-6 (i.e., Periods starting with Na, K, Rb, and Cs) of the conventional IUPAC periodic table. Groups IIIA through VIB of the conventional IUPAC form of the Periodic Table corresponds to: Groups 3-16 of the "new notation" IUPAC Periodic Table and Groups IIIB-VIA of the CAS version of the Periodic Table. In order to avoid any confusion further reference herein will utilize the conventional IUPAC Periodic Table, i.e., Group IIIA corresponds to the column starting with Sc, Y, La, etc, and Group VIB corresponds to the column starting with O, S, Se, Te, Po. Specific examples include: (1) the following metals: aluminum, scandium, titanium, vanadium, chromium, manganese, iron, cobalt, nickel, copper, zinc, gallium, germanium, arsenic, yttrium, zirconium, niobium, molybdenum, technetium, ruthenium, rhodium, palladium, silver, cadmium, indium, tin, antimony, tellurium, lanthanum, cerium, praseodymium, neodymium, promethium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium, lutetium, hafnium, tantalum, tungsten, rhenium, osmium, iridium, platinum, gold, mercury, thallium, lead, bismuth (bismuth is not typically preferred), and polonium; (2) the following semi-conductors: silicon, selenium, and germanium and (3) phosphorous. Particularly preferred binding cores include: Al, Si, P, As, Sb, Se and Te and metals such as: Fe, Cr, Co, Ni, Cu, and Zn. L is an optional chemical linking group, the same or different, selected from linkages such as: carbon containing moieties, e.g., aromatic groups, alkanes, alkenes,— O— ,— S— ,— N— ,— H— ,— P— ,— O— P— , and— O— P— O— , (each of which may be substituted or unsubstituted). β is solubilizing group, the same or different, and includes from 1 to 12 carbon atoms which may be substituted or unsubstituted and which may include internal linking groups as defined by L. Examples include aliphatic and arene groups having 1 to 6 carbon atoms, aromatic groups, heterocyclic groups, and alkyl groups, "x" is an integer from 0 to 1 and "y" is an integer from 1 to 5, preferably from 2 to 4. Although dependent upon the specific solvent(s) and acyl halide species utilized, the following complexing agents are generally useful in the subject invention: tri-phenyl derivatives of phosphorous (e.g., phosphine, phosphate), bismuth, arsenic and antimony; alkane oxy esters of phosphorous including tributyl and dibutyl phosphite; organo-metallic complexes such as ferrocene and tetraethyl lead and acetylacetonate complexes of iron (II), iron (III), cobalt (III) and Cr (III). A preferred class of such complexing agents is represented by Formula (II). Formula (II):

OP I

R₂0— P=0

I

OR₃ wherein "P" is phosphorous, "O" is oxygen and Ri, R₂ and R₃ are independently selected from carbon containing moieties. The term "carbon containing moiety" is intended to mean branched and unbranched acyclic groups, e.g., methyl, ethyl, propyl, isopropyl, butyl, isobutyl, pentyl, 2-pentyl, 3-pentyl, tert-butyl, etc., which may be unsubstituted or substituted (e.g., substituted with amide groups, ether groups, ester groups, sulfone groups, carbonyl groups, anhydrides, cyanide, nitrile, isocyanate, urethane, beta-hydroxy ester, double and triple bonds etc.), and cyclic groups, e.g., cyclo pentyl, cyclo hexyl, aromatics, e.g., phenyl, heterocyclic (e.g., pyridine), etc., which may be unsubstituted or substituted, (e.g., substituted with methyl, ethyl, propyl, hydroxyl, amide, ether, sulfone, carbonyl, ester, etc.). Cyclo moieties may be linked to the phosphorous atom by way of an aliphatic linking group, e.g., methyl, ethyl, etc. Preferred carbon containing moieties include unsubstituted, branched or unbranched C i-C i₂ groups, and more preferably C i-C ₈ aliphatic groups such as: methyl, ethyl, propyl, isopropyl, butyl, 2-methyl butyl, 3-methyl butyl, 2-ethyl butyl, pentyl, hexyl, etc. Additionally, moieties include phenyl groups. When used, the aforementioned complexing agents are preferred added to the organic -based or non-polar coating solution containing the polyiunctional acyl halide in a ratio with the polyiunctional acyl halide monomer of from about 1 :5 to 5: 1 with 1 : 1 to 3: 1 being preferred. In another preferred embodiment, the concentration of the complexing agent within the coating solutions is from about 0.001 to 2 weight percent. Once brought into contact with one another, the polyfunctional acyl halide and polyfunctional amine monomers react at their surface interface to form a polyamide layer or film. This layer, often referred to as a polyamide "discriminating layer" or "thin film layer," provides the composite membrane with its principal means for separating solute (e.g. salts) from solvent (e.g. aqueous feed ).

The reaction time of the polyfunctional acyl halide and the polyfunctional amine monomer may be less than one second but contact times typically range from about 1 to 60 seconds, after which excess liquid may be optionally removed by way of an air knife, water bath(s), dryer or the like. The removal of the excess solvent can be achieved by drying at elevated temperatures, e.g. from about 40°C to about 120°C, although air drying at ambient temperatures may be used.

In one embodiment, the subject method includes the step of applying a polyfunctional amine monomer and polyfunctional acyl halide monomer to a surface of the porous support and interfacially polymerizing the monomers to form a thin film polyamide layer. The subject method is characterized by including at least one of the following steps: i) conducting the interfacial polymerization in the presence of a C₂-C₂o aliphatic monomer comprising at least one carboxylic acid functional group or salt thereof and a single amine-reactive functional group; and ii) applying a C₂-C₂o aliphatic monomer comprising at least one carboxylic acid functional group or salt thereof and a single amine-reactive functional group to the thin film polyamide layer after the interfacial polymerization is substantially complete. The term "amine-reactive" functional group refers to a functional group that is reactive with the amine functional groups of the polyfunctional amine monomer during the interfacial polymerization, i.e. during the time period and conditions present during formation of the thin film polyamide layer. This generally requires substantial reaction within a few seconds of contact at room temperature under standard atmospheric pressure. Representative examples of amine-reactive functional groups include: acyl halide, anhydride, isocyanate and epoxy. In a preferred embodiment, the amine-reactive functional group is an acyl halide and preferably an acid chloride.

When present during the interfacial polymerization, the subject aliphatic monomer is believed to be incorporated within the resulting polyamide structure (i.e. the subject aliphatic monomer and polyfunctional amine and acyl halide monomers form a reaction product). When applied after the polyamide is formed, the subject aliphatic monomer is believed to react with residual amine groups present in the thin film polyamide.

The aliphatic monomer is distinct from the aforementioned polyfunctional acyl halide and polyfunctional amine monomers and preferably comprises from 2 to 20 carbon atoms and may be alicyclic or acyclic and may be saturated or unsaturated. In addition to including at least one carboxylic acid functional group and an amine-reactive functional group, the aliphatic monomer may be unsubstituted or substituted with non amine-reactive functional groups such as halo, hydroxyl, ether, nitrile, nitro and vinyl (ethenyl). If alicyclic, the compound may be straight or branched. In one preferred embodiment, the aliphatic monomer is acyclic and unsaturated. In another embodiment, the aliphatic monomer includes a single carboxylic acid functional group. A class of preferred aliphatic monomers is represented below in Formula (III).

Formula (III):

wherein X is a halogen (preferably chlorine) and n is an integer from 1 to 10. Representative species include: 4-(chlorocarbonyl) butanoic acid; 5-(chlorocarbonyl) pentanoic acid; 6- (chlorocarbonyl) hexanoic acid; 7-(chlorocarbonyl) heptanoic acid; 8-(chlorocarbonyl) octanoic acid; 9-(chlorocarbonyl) nonanoic acid and lO-(chlorocarbonyl) decanoic acid. While the acyl halide and carboxylic acid groups are shown in terminal positions, one or both may be located at alternative positions along the aliphatic chain. While not shown in Formula (III), the aliphatic monomer may include additional carboxylic acid functional groups along with optional non amine -reactive functional groups as described above.

Another preferred class of aliphatic monomers comprises acyclic compounds. Examples of such compounds include five and six member acyclic compounds along with fused ring structures. In one set of embodiments, the acyclic compound comprises a single carboxylic acid functional group. A class of preferred embodiments is represented below in Formulae (IV and V).

Formula (IV): Formula (V):

wherein X is a halogen (preferably chlorine). The positions of the carboxylic acid and acyl halide functional groups on the rings are not particularly limited, (e.g. meta, para and ortho). While not shown, the rings may include saturated carbons but are preferably not aromatic. The rings may also include non amine -reactive functional groups, e.g. halogen, hydroxyl and alkyl and alkenyl groups having from 1 to 12 carbon atoms which may be unsubstituted or substituted with moieties such as hydroxyl, nitrile and ether groups.

As previously described, the step of applying the polyfunctional monomers to the surface of the porous support preferably involves applying a polar solution comprising the polyfunctional amine monomer and a non-polar solution comprising the polyfunctional acyl halide monomer. The step of applying the solutions preferably involves coating by way of spraying, film coating, rolling, or through the use of a dip tank. In one embodiment, the subject aliphatic monomer is added to the non-polar solution prior to the application step, e.g. prior to coating the non-polar solution upon the porous support. In such an embodiment, the non-polar solution preferably comprises at least 0.001 weight/volume of the aliphatic monomer. In another embodiment, the non-polar solution comprises from about 0.001 to 0.1 weight/volume of the aliphatic monomer. In still another embodiment, the non-polar solution comprises the aliphatic monomer and polyfunctional acyl halide in a molar ratio of from about 0.0001 :1 to 1: 1, preferably from 0.001 :1 to 0.1 : 1 and more preferably from 0.001 : 1 to 0.01 : 1. The non-polar solution may include additional constituents including the complexing agents described above along with small quantities of water (e.g. from 50 to 500 ppm and in some embodiments at least 100 ppm).

In another embodiment, the subject aliphatic monomer is separately applied to the surface of the porous support (e.g. from a separate solution), either before, during or after the substantial completion of the interfacial polymerization. In this embodiment, the coating solution is preferably a non-polar solution as previously described and preferably comprises a concentration of the aliphatic monomer from about 0.5 to 5 % weight/volume, or more preferably from about 1 to 3 % weight /volume. The solution may include additional constituents including the complexing agents described above along with small quantities of water (e.g. from 50 to 500 ppm and in some embodiments at least 100 ppm).

The subject aliphatic monomer may be formed in-situ within the coating solution, e.g. via a hydrolysis reaction of an acyl halide functional group, or be pre-formed and added to the coating solution.

Membranes prepared with the subject aliphatic monomers exhibit lower solute passage when compared with substantially similar membranes prepared without. Surprising, membranes prepared with the subject aliphatic monomers exhibit higher flux when compared with substantially similar membranes prepared with similar aliphatic monomers that include two amine reactive functional groups rather than one.

While not limited to a particular type of polyamide membrane, the subject invention is particularly suited for application to composite membranes such as those commonly used in RO and NF applications, and more particularly to flat sheet composite polyamide membranes used in RO and NF applications. The thin film polyamide layer may optionally include hygroscopic polymers upon at least a portion of its surface. Such polymers include polymeric surfactants, polyacrylic acid, polyvinyl acetate, polyalkylene oxide compounds, poly(oxazoline) compounds, polyacrylamides and related reaction products as generally described in US 6280853; US 7815987; US 2009/0220690 and US 2008/0185332 to Mickols and Niu. In some embodiments, such polymers may be blended and/or reacted and may be coated or otherwise applied to the polyamide membrane from a common solution, or applied sequentially. Many embodiments of the invention have been described and in some instances certain embodiments, selections, ranges, constituents, or other features have been characterized as being "preferred." Characterizations of "preferred" features should in no way be interpreted as deeming such features as being required, essential or critical to the invention. The entire subject matter of each of the aforementioned US patent documents is incorporated herein by reference.

EXAMPLES:

Unless otherwise indicated, all sample membranes were produced using pilot scale membrane manufacturing line. Polysulfone supports were casts from 16.5wt. % solutions in dimethylformamide (DMF) and subsequently soaked in 3.5 wt. % aqueous solutions of meta-phenylene diamine (mPD). The resulting support was then pulled through a reaction table at constant speed while a thin, uniform layer of a non-polar solution was applied. The non-polar solution included isoparaffinic (ISOPAR L), trimesoyl acid chloride (TMC) and an additional monomer identified below. The non-polar solution also contained TBP (tri butyl phosphate) at a stoichiometric ratio of 1 : 1.4 with respect to TMC (except for Example 3 where the ratio was 1 : 1.1 and Example 7 where no TBP was included). Excess non-polar solution was removed and the resulting composite membrane was passed through water rinse tanks and drying ovens. Coupons of the sample membranes were then subject to standard testing using an aqueous salt solution (2000 ppm NaCl) at 150 psi, pH 8 and at room temperature. The testing results are summarized in the tables provided below.

Example 1 :

Sample composite polyamide membranes were prepared using 4-(chlorocarbonyl)butanoic acid as the "subject monomer." The total acid chloride content of the non-polar solutions used to prepare each sample was held constant at 0.24 % w/v. The concentration of the subject monomer was varied from 0 to 0.03% w/v while the remaining acid chloride content was contributed solely by TMC. As shown in Table 1, salt passage decreased from 0.99% to 0.52% with increasing

concentrations of 4-(chlorocarbonyl)butanoic acid.

Table 1 :

Example 2:

Sample composite polyamide membranes were prepared using 2-(chlorocarbonyl)ethanoic acid as the subject monomer. The total acid chloride content of the non-polar solutions used to prepare each sample was held constant at 0.24 % w/v. The concentration of the subject monomer was varied from 0 to 0.03% w/v while the remaining acid chloride content was contributed solely by TMC. As shown in Table 2, salt passage decreased from 1.46% to 0.73% with increasing concentrations of 2- (chlorocarbonyl)ethanoic acid.

Table 2:

Example 3:

Sample composite polyamide membranes were prepared using 5-chlorocarbonyl pentanoic acid as the subject monomer (Samples 10 and 12). For comparison, membranes were also prepared with 1 ,4-dichlorocarbonyl butane and TMC (Comparison Samples 9 and 11). The total acid chloride content of the non-polar solutions used to prepare each sample was held constant at 0.175 % w/v. The concentration of the subject monomer was varied from 0 to 0.02% w/v while the remaining acid chloride content was contributed solely by TMC. As shown in table 3, membranes prepared with the subject monomer, 5-chlorocarbonyl pentanoic acid (Samples 10 and 12) demonstrated a 30% improvement in salt passage as compared with samples prepared with structurally similar 1,4-dichloro carbonyl butane additive.

Table 3:

Example 4:

A sample composite polyamide membrane was prepared using 9-chlorocarbonyl nonanoic acid as the subject monomer. For comparison, a control membrane was also made without the subject monomer. The total acid chloride content of the non-polar solutions used to prepare each sample was held constant at 0.21 % w/v. The concentration of the subject monomer was 0.011% w/v while the remaining acid chloride content was contributed solely by TMC. As shown in Table 4, membranes prepared with 9-chlorocarbonyl nonanoic acid showed over 26% improvement in salt passage over the control membrane.

Table 4:

Example 5:

Sample composite polyamide membranes were made using 2,4-dioxo-3-oxabicyclo[3.3.1] nonane-7-carboxylic acid as the subject monomer. For comparison, a control membrane was also prepared without the subject monomer. The total acid chloride content of the non-polar solutions used to prepare each sample was held constant at 0.24 % w/v. The concentration of the subject monomer was 0.03% w/v while the remaining acid chloride content was contributed solely by TMC. As shown in Table 6, the subject monomer showed improvement in salt passage compared with membrane made with only TMC.

Table 5:

Example 6: (Comparison)

A sample composite polyamide membrane was prepared using 1,8-dichlorocarbonyloctane. For comparison, a control membrane was also prepared without 1,8-dichlorocarbonyloctane. The total acid chloride content of the non-polar solutions used to prepare each sample was held constant at 0.21 % w/v. The concentration of the comparison monomer was 0.011% w/v while the remaining acid chloride content was contributed solely by TMC. As shown in Table 6, the comparison monomer showed no substantive improvement in salt passage.

Table 6:

Example 7:

Sample composite polyamide membranes were made using an aqueous 3.5 wt. % mPD solution and a non-polar solution including TMC and 4-(chlorocarbonyl)butanoic acid as the subject monomer within an isoparaffinic solvent (ISOPAR L). The TMC content of the non-polar solutions used to prepare each sample was held constant at 0.11 % w/v. No samples included TBP. The concentration of the subject monomer was approximately 0.01% w/v in Sample 16 and 0% in control. The non-polar solution also contained 4 % mesitylene as a co-solvent. Salt passage decreased in the sample prepared with o4-(chlorocarbonyl)butanoic acid.

Table 7

Claims

CLAIMS:

1. A method for making a composite polyamide membrane comprising a porous support and a thin film polyamide layer, wherein the method comprises the step of applying a polyfunctional amine monomer and polyfunctional acyl halide monomer to a surface of the porous support and interfacially polymerizing the monomers to form a thin film polyamide layer, wherein the method is characterized by including at least one of the following steps:

i) conducting the interfacial polymerization in the presence of a C₂-C₂o aliphatic monomer comprising at least one carboxylic acid functional group or salt thereof and a single amine - reactive functional group; and

ii) applying a C₂-C₂o aliphatic monomer comprising at least one carboxylic acid functional group or salt thereof and a single amine -reactive functional group to the thin film polyamide layer.

2. The method of claim 1 wherein the amine -reactive functional group is selected from: acyl halide, anhydride, isocyanate and epoxy.

3. The method of claim 1 wherein the aliphatic monomer comprises a single carboxylic acid functional group.

4. The method of claim 1 wherein the aliphatic monomer is an alicyclic compound.

5. The method of claim 1 wherein the aliphatic monomer is an acyclic compound.

6. The method of claim 1 wherein the aliphatic monomer is represented by Formula

(III):

Formula (III):

wherein X is a halogen and n is an integer from 1 to 10.

7. The method of claim 1 wherein the aliphatic monomer is selected from: 4-(chlorocarbonyl) butanoic acid; 5-(chlorocarbonyl) pentanoic acid; 6-(chlorocarbonyl) hexanoic acid; 7-(chlorocarbonyl) heptanoic acid; 8-(chlorocarbonyl) octanoic acid; 9-(chlorocarbonyl) nonanoic acid and lO-(chlorocarbonyl) decanoic acid.

8. The method of claim 1 wherein the aliphatic monomer is represented by at least one of Formulae (IV and V):

Formula

wherein X is a halogen.

9. The method of claim 1 wherein the step of applying the polyfunctional monomers to the surface of the porous support comprises applying a polar solution comprising the polyfunctional amine monomer and a non-polar solution comprising the polyfunctional acyl halide monomer; and wherein the non-polar solution further comprises the aliphatic monomer.