WO2012023737A2 - Light emitting device having surface-modified silicate luminophores - Google Patents
Light emitting device having surface-modified silicate luminophores Download PDFInfo
- Publication number
- WO2012023737A2 WO2012023737A2 PCT/KR2011/005842 KR2011005842W WO2012023737A2 WO 2012023737 A2 WO2012023737 A2 WO 2012023737A2 KR 2011005842 W KR2011005842 W KR 2011005842W WO 2012023737 A2 WO2012023737 A2 WO 2012023737A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- light emitting
- luminophore
- emitting device
- fluorinated
- emitting diode
- Prior art date
Abstract
Description
Claims