WO2012015639A1 - Method for making uv-absorbing ophthalmic lenses - Google Patents
Method for making uv-absorbing ophthalmic lenses Download PDFInfo
- Publication number
- WO2012015639A1 WO2012015639A1 PCT/US2011/044618 US2011044618W WO2012015639A1 WO 2012015639 A1 WO2012015639 A1 WO 2012015639A1 US 2011044618 W US2011044618 W US 2011044618W WO 2012015639 A1 WO2012015639 A1 WO 2012015639A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- group
- divalent radical
- lens
- linear
- absorbing
- Prior art date
Abstract
Description
Claims