WO2012014455A1 - 共役ジエン化合物と非共役オレフィンとの共重合体、ゴム組成物、架橋ゴム組成物、及びタイヤ - Google Patents
共役ジエン化合物と非共役オレフィンとの共重合体、ゴム組成物、架橋ゴム組成物、及びタイヤ Download PDFInfo
- Publication number
- WO2012014455A1 WO2012014455A1 PCT/JP2011/004225 JP2011004225W WO2012014455A1 WO 2012014455 A1 WO2012014455 A1 WO 2012014455A1 JP 2011004225 W JP2011004225 W JP 2011004225W WO 2012014455 A1 WO2012014455 A1 WO 2012014455A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- group
- conjugated
- copolymer
- conjugated diene
- olefin
- Prior art date
Abstract
Description
特に、共役ジエンと非共役オレフィンの共重合体を配合ゴムへ適用することで、共重合体中の共役ジエン部分(共役ジエン化合物由来部分)の二重結合が共役重合体に比べて少なくなるため、耐オゾン性が向上する。また、ゴム組成物を様々な用途(タイヤやベルトコンベア、防振ゴムなど)に適用したときに求められる耐オゾン性以外の要求特性の一つとして耐亀裂成長性を良好にすることが挙げられる。
ここで、シス1,4-結合含量とは、共役ジエン化合物(共役ジエン化合物由来部分)中の共役ジエン単位における1,4-シス結合の割合を意味する。
本発明の共役ジエン化合物と非共役オレフィンとの共重合体は、共役ジエン部分(共役ジエン化合物由来部分)のシス1,4-結合含量が70.5%より大きく、好ましくは80%以上、更に好ましくは90%以上であり、非共役オレフィン(非共役オレフィン由来部分)の含有量を10mol%以上、好ましくは15mol%以上、更に好ましくは20mol%以上とすることを特徴とする。
非共役オレフィン(非共役オレフィン由来部分)の含有量を10mol%以上とすることにより、耐候性に優れたゴムを提供することが可能となる。
シス1,4-結合含量(シス量)が70.5%より大きいとガラス転移温度が低くなるため、耐亀裂成長性が良好となる。また、非共役オレフィン(非共役オレフィン由来部分)の含有量が10mol%以上だと共重合体中の二重結合の量が少なくなるため、耐候性が良好となる。
前記シス-1,4結合含量は、前記共役ジエン化合物由来部分中の量であって、共重合体全体に対する割合ではない。
上述した共役ジエン化合物の具体例のいずれを用いても、同様のメカニズムで本発明の共重合体を調製することができる。
ここで、平均分子量及び分子量分布は、ゲルパーミエーションクロマトグラフィー(GPC)によりポリスチレンを標準物質として求めることができる。
本発明の共重合体は、下記に示す重合触媒または重合触媒組成物の存在下、共役ジエン化合物と非共役オレフィンとを重合させることができる。なお、重合方法としては、溶液重合法、懸濁重合法、液相塊状重合法、乳化重合法、気相重合法、固相重合法等の任意の方法を用いることができる。また、重合反応に溶媒を用いる場合、用いられる溶媒は重合反応において不活性であればよく、例えば、トルエン、シクロヘキサン、ノルマルヘキサン、またそれらの混合物等が挙げられる。
上記重合触媒組成物としては、下記一般式(I):
(式中、Mは、ランタノイド元素、スカンジウム又はイットリウムを示し、CpRは、それぞれ独立して無置換もしくは置換インデニルを示し、Ra~Rfは、それぞれ独立して炭素数1~3のアルキル基又は水素原子を示し、Lは、中性ルイス塩基を示し、wは、0~3の整数を示す)で表されるメタロセン錯体、及び下記一般式(II):
(式中、Mは、ランタノイド元素、スカンジウム又はイットリウムを示し、CpRは、それぞれ独立して無置換もしくは置換インデニルを示し、X’は、水素原子、ハロゲン原子、アルコキシド基、チオラート基、アミド基、シリル基又は炭素数1~20の炭化水素基を示し、Lは、中性ルイス塩基を示し、wは、0~3の整数を示す)で表されるメタロセン錯体、並びに下記一般式(III):
(式中、Mは、ランタノイド元素、スカンジウム又はイットリウムを示し、CpR’は、無置換もしくは置換シクロペンタジエニル、インデニル又はフルオレニルを示し、Xは、水素原子、ハロゲン原子、アルコキシド基、チオラート基、アミド基、シリル基又は炭素数1~20の炭化水素基を示し、Lは、中性ルイス塩基を示し、wは、0~3の整数を示し、[B]-は、非配位性アニオンを示す)で表されるハーフメタロセンカチオン錯体からなる群より選択される少なくとも1種類の錯体を含む重合触媒組成物(以下、第一重合触媒組成物ともいう)が挙げられ、該重合触媒組成物は、更に、通常のメタロセン錯体を含む重合触媒組成物に含有される他の成分、例えば助触媒等を含んでいてもよい。ここで、メタロセン錯体は、一つ又は二つ以上のシクロペンタジエニル又はその誘導体が中心金属に結合した錯体化合物であり、特に、中心金属に結合したシクロペンタジエニル又はその誘導体が一つであるメタロセン錯体を、ハーフメタロセン錯体と称することがある。なお、重合反応系において、第一重合触媒組成物に含まれる錯体の濃度は0.1~0.0001mol/Lの範囲であることが好ましい。
(式中、Rは水素原子、メチル基又はエチル基を示す。)
(式中、X’’はハライドを示す。)
(式中、X’’はハライドを示す。)
また、上記重合触媒組成物としては、
(A)成分:希土類元素化合物又は該希土類元素化合物とルイス塩基との反応物であって、希土類元素と炭素との結合を有さない該希土類元素化合物又は反応物と、
(B)成分:非配位性アニオンとカチオンとからなるイオン性化合物(B-1)、アルミノキサン(B-2)、並びにルイス酸、金属ハロゲン化物とルイス塩基との錯化合物及び活性ハロゲンを含む有機化合物のうち少なくとも一種のハロゲン化合物(B-3)よりなる群から選択される少なくとも一種とを含む重合触媒組成物(以下、第二重合触媒組成物ともいう)を好適に挙げることができ、
該第二重合触媒組成物が、イオン性化合物(B-1)及びハロゲン化合物(B-3)の少なくとも一種を含む場合、該重合触媒組成物は、更に、
(C)成分:下記一般式(X):
YR1 aR2 bR3 c ・・・ (X)
[式中、Yは、周期律表第1族、第2族、第12族及び第13族から選択される金属であり、R1及びR2は、同一又は異なり、炭素数1~10の炭化水素基又は水素原子で、R3は炭素数1~10の炭化水素基であり、但し、R3は上記R1又はR2と同一又は異なっていてもよく、また、Yが周期律表第1族から選択される金属である場合には、aは1で且つb及びcは0であり、Yが周期律表第2族及び第12族から選択される金属である場合には、a及びbは1で且つcは0であり、Yが周期律表第13族から選択される金属である場合には、a,b及びcは1である]で表される有機金属化合物を含むことを特徴とする。
(C)成分:下記一般式(X):
YR1 aR2 bR3 c ・・・ (X)
[式中、Yは、周期律表第1族、第2族、第12族及び第13族から選択される金属であり、R1及びR2は、同一又は異なり、炭素数1~10の炭化水素基又は水素原子で、R3は炭素数1~10の炭化水素基であり、但し、R3は上記R1又はR2と同一又は異なっていてもよく、また、Yが周期律表第1族から選択される金属である場合には、aは1で且つb及びcは0であり、Yが周期律表第2族及び第12族から選択される金属である場合には、a及びbは1で且つcは0であり、Yが周期律表第13族から選択される金属である場合には、a,b及びcは1である]で表される有機金属化合物を含むことを要する。上記イオン性化合物(B-1)及び上記ハロゲン化合物(B-3)は、(A)成分へ供給するための炭素原子が存在しないため、該(A)成分への炭素供給源として、上記(C)成分が必要となる。なお、上記重合触媒組成物が上記アルミノキサン(B-2)を含む場合であっても、該重合触媒組成物は、上記(C)成分を含むことができる。また、上記第二重合触媒組成物は、通常の希土類元素化合物系の重合触媒組成物に含有される他の成分、例えば助触媒等を含んでいてもよい。
M11X11 2・L11w ・・・ (XI)
M11X11 3・L11w ・・・ (XII)
[式中、M11は、ランタノイド元素、スカンジウム又はイットリウムを示し、X11は、それぞれ独立して、水素原子、ハロゲン原子、アルコキシド基、チオラート基、アミド基、シリル基、アルデヒド残基、ケトン残基、カルボン酸残基、チオカルボン酸残基又はリン化合物残基を示し、L11は、ルイス塩基を示し、wは、0~3を示す]で表されることができる。
上記活性ハロゲンを含む有機化合物としては、ベンジルクロライド等が挙げられる。
YR1 aR2 bR3 c ・・・ (X)
[式中、Yは、周期律表第1族、第2族、第12族及び第13族から選択される金属であり、R1及びR2は、同一又は異なり、炭素数1~10の炭化水素基又は水素原子で、R3は炭素数1~10の炭化水素基であり、但し、R3は上記R1又はR2と同一又は異なっていてもよく、また、Yが周期律表第1族から選択される金属である場合には、aは1で且つb及びcは0であり、Yが周期律表第2族及び第12族から選択される金属である場合には、a及びbは1で且つcは0であり、Yが周期律表第13族から選択される金属である場合には、a,b及びcは1である]で表される有機金属化合物であり、下記一般式(Xa):
AlR1R2R3 ・・・ (Xa)
[式中、R1及びR2は、同一又は異なり、炭素数1~10の炭化水素基又は水素原子で、R3は炭素数1~10の炭化水素基であり、但し、R3は上記R1又はR2と同一又は異なっていてもよい]で表される有機アルミニウム化合物であることが好ましい。式(X)の有機アルミニウム化合物としては、トリメチルアルミニウム、トリエチルアルミニウム、トリ-n-プロピルアルミニウム、トリイソプロピルアルミニウム、トリ-n-ブチルアルミニウム、トリイソブチルアルミニウム、トリ-t-ブチルアルミニウム、トリペンチルアルミニウム、トリヘキシルアルミニウム、トリシクロヘキシルアルミニウム、トリオクチルアルミニウム;水素化ジエチルアルミニウム、水素化ジ-n-プロピルアルミニウム、水素化ジ-n-ブチルアルミニウム、水素化ジイソブチルアルミニウム、水素化ジヘキシルアルミニウム、水素化ジイソヘキシルアルミニウム、水素化ジオクチルアルミニウム、水素化ジイソオクチルアルミニウム;エチルアルミニウムジハイドライド、n-プロピルアルミニウムジハイドライド、イソブチルアルミニウムジハイドライド等が挙げられ、これらの中でも、トリエチルアルミニウム、トリイソブチルアルミニウム、水素化ジエチルアルミニウム、水素化ジイソブチルアルミニウムが好ましい。以上に述べた(C)成分としての有機アルミニウム化合物は、1種単独で使用することも、2種以上を混合して用いることもできる。なお、上記第二重合触媒組成物における有機アルミニウム化合物の含有量は、(A)成分に対して1~50倍モルであることが好ましく、約10倍モルであることが更に好ましい。
上記重合触媒としては、共役ジエン化合物と非共役オレフィンとの重合用であり、下記
式(A):
RaMXbQYb ・・・ (A)
[式中、Rはそれぞれ独立して無置換もしくは置換インデニルを示し、該RはMに配位しており、Mはランタノイド元素、スカンジウム又はイットリウムを示し、Xはそれぞれ独立して炭素数1~20の炭化水素基を示し、該XはM及びQにμ配位しており、Qは周期律表第13族元素を示し、Yはそれぞれ独立して炭素数1~20の炭化水素基又は水素原子を示し、該YはQに配位しており、a及びbは2である]で表されるメタロセン系複合触媒が挙げられる。
[式中、M1は、ランタノイド元素、スカンジウム又はイットリウムを示し、CpRは、それぞれ独立して無置換もしくは置換インデニルを示し、Ra及びRbは、それぞれ独立して炭素数1~20の炭化水素基を示し、該Ra及びRbは、M1及びAlにμ配位しており、Rc及びRdは、それぞれ独立して炭素数1~20の炭化水素基又は水素原子を示す]で表されるメタロセン系複合触媒が挙げられる。
以下に、上記メタロセン系複合触媒を詳細に説明する。上記メタロセン系複合触媒は、ランタノイド元素、スカンジウム又はイットリウムの希土類元素と周期律表第13族元素とを有し、下記式(A):
RaMXbQYb ・・・ (A)
[式中、Rはそれぞれ独立して無置換もしくは置換インデニルを示し、該RはMに配位しており、Mはランタノイド元素、スカンジウム又はイットリウムを示し、Xはそれぞれ独立して炭素数1~20の炭化水素基を示し、該XはM及びQにμ配位しており、Qは周期律表第13族元素を示し、Yはそれぞれ独立して炭素数1~20の炭化水素基又は水素原子を示し、該YはQに配位しており、a及びbは2である]で表されることを特徴とする。上記メタロセン系重合触媒を用いることで、共役ジエン化合物と非共役オレフィンとの共重合体を製造することができる。また、上記メタロセン系複合触媒、例えば予めアルミニウム触媒と複合させてなる触媒を用いることで、共重合体合成時に使用されるアルキルアルミニウムの量を低減したり、無くしたりすることが可能となる。なお、従来の触媒系を用いると、共重合体合成時に大量のアルキルアルミニウムを用いる必要がある。例えば、従来の触媒系では、金属触媒に対して10当量以上のアルキルアルミニウムを用いる必要があるところ、上記メタロセン系複合触媒であれば、5当量程度のアルキルアルミニウムを加えることで、優れた触媒作用が発揮される。
(式中、M2は、ランタノイド元素、スカンジウム又はイットリウムを示し、CpRは、それぞれ独立して無置換もしくは置換インデニルを示し、RE~RJは、それぞれ独立して炭素数1~3のアルキル基又は水素原子を示し、Lは、中性ルイス塩基を示し、wは、0~3の整数を示す)で表されるメタロセン錯体を、AlRKRLRMで表される有機アルミニウム化合物と反応させることで得られる。なお、反応温度は室温程度にすればよいので、温和な条件で製造することができる。また、反応時間は任意であるが、数時間~数十時間程度である。反応溶媒は特に限定されないが、原料及び生成物を溶解する溶媒であることが好ましく、例えばトルエンやヘキサンを用いればよい。なお、上記メタロセン系複合触媒の構造は、1H-NMRやX線構造解析により決定することが好ましい。
また、上記重合触媒組成物は、上記メタロセン系複合触媒と、ホウ素アニオンとを含むことを特徴とし、更に、通常のメタロセン系触媒を含む重合触媒組成物に含有される他の成分、例えば助触媒等を含むことが好ましい。なお、上記メタロセン系複合触媒とホウ素アニオンとを合わせて2成分触媒ともいう。上記第三重合触媒組成物によれば、上記メタロセン系複合触媒と同様に、更にホウ素アニオンを含有するため、各単量体成分の共重合体中での含有量を任意に制御することが可能となる。
非共役オレフィンの濃度/共役ジエン化合物の濃度 ≧ 1.0
の関係を満たすことが好ましく、更に好ましくは下記式:
非共役オレフィンの濃度/共役ジエン化合物の濃度 ≧ 1.3
の関係を満たし、一層好ましくは下記式:
非共役オレフィンの濃度/共役ジエン化合物の濃度 ≧ 1.7
の関係を満たす。非共役オレフィンの濃度/共役ジエン化合物の濃度の値を1以上とすることで、反応混合物中に非共役オレフィンを効率的に導入することができる。
本発明のゴム組成物としては、本発明の共重合体を含む限り、特に制限はなく、目的に応じて適宜選択することができるが、本発明の共重合体以外のゴム成分、無機充填剤、カーボンブラック、架橋剤、などを含むことが好ましい。
本発明の共重合体のゴム成分中の含有量としては、特に制限はなく、目的に応じて適宜選択することができるが、3質量%以上が好ましい。
前記共重合体のゴム成分中の含有量が、3質量%未満であると、本発明の特徴が小さかったり、またはその特徴を発揮しなかったりすることがある。
前記ゴム成分としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、本発明の共重合体、天然ゴム、各種ブタジエンゴム、各種スチレン-ブタジエン共重合体ゴム、イソプレンゴム、ブチルゴム、イソブチレンとp-メチルスチレンの共重合体の臭化物、ハロゲン化ブチルゴム、アクリロニトリロブタジエンゴム、クロロプレンゴム、エチレン-プロピレン共重合体ゴム、エチレン-プロピレン-ジエン共重合体ゴム、スチレン-イソプレン共重合体ゴム、スチレン-イソプレン-ブタジエン共重合体ゴム、イソプレン-ブタジエン共重合体ゴム、クロロスルホン化ポリエチレン、アクリルゴム、エピクロルヒドリンゴム、多硫化ゴム、シリコーンゴム、フッ素ゴム、ウレタンゴム、などが挙げられる。これらは、1種単独で使用してもよいし、2種以上を併用してもよい。
<無機充填剤>
前記無機充填剤としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、シリカ、水酸化アルミニウム、クレー、アルミナ、タルク、マイカ、カオリン、ガラスバルーン、ガラスビーズ、炭酸カルシウム、炭酸マグネシウム、水酸化マグネシウム、炭酸カルシウム、酸化マグネシウム、酸化チタン、チタン酸カリウム、硫酸バリウム、などが挙げられる。これらは、1種単独で使用してもよいし、2種以上を併用してもよい。
なお、無機充填剤を用いる時は適宜シランカップリング剤を使用してもよい。
前記補強性充填剤の含有量が、5質量部未満であると、補強性充填剤を入れる効果があまりみられないことがあり、200質量部を超えると前記ゴム成分に補強性充填剤が混ざり込まなくなる傾向があり、ゴム組成物としての性能を低下させることがある。
前記架橋剤としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、硫黄系架橋剤、有機過酸化物系架橋剤、無機架橋剤、ポリアミン架橋剤、樹脂架橋剤、硫黄化合物系架橋剤、オキシム-ニトロソアミン系架橋剤硫黄、などが挙げられるが、中でもタイヤ用ゴム組成物としては硫黄系架橋剤がより好ましい。
前記架橋剤の含有量が0.1質量部未満では、架橋がほとんど進行しなかったり、20質量部を超えると一部の架橋剤により混練り中に架橋が進んでしまう傾向があったり、加硫物の物性が損なわれたりすることがある。
その他に加硫促進剤を併用することも可能であり、加硫促進剤としては、グアジニン系、アルデヒド-アミン系、アルデヒド-アンモニア系、チアゾール系、スルフェンアミド系、チオ尿素系、チウラム系、ジチオカルバメート系、ザンテート系等の化合物が使用できる。
また必要に応じて、補強剤、軟化剤、充填剤、加硫助剤、着色剤、難燃剤、滑剤、発泡剤、可塑剤、加工助剤、酸化防止剤、老化防止剤、スコーチ防止剤、紫外線防止剤、帯電防止剤、着色防止剤、その他の配合剤など公知のものをその使用目的に応じて使用することができる。
本発明の架橋ゴム組成物は、本発明のゴム組成物を架橋して得られたものである限り、特に制限はなく、目的に応じて適宜選択することができる。
前記架橋の条件としては、特に制限はなく、目的に応じて適宜選択することができるが、温度120℃~200℃、加温時間1分間~900分間が好ましい。
本発明のタイヤは、本発明のゴム組成物、又は、本発明の架橋ゴム組成物を用いたものである限り、特に制限はなく、目的に応じて適宜選択することができる。
本発明のゴム組成物、又は、本発明の架橋ゴム組成物のタイヤにおける適用部位としては、例えば、トレッド、ベーストレッド、サイドウォール、サイド補強ゴム及びビードフィラーなどが挙げられるが、これに限定されない。
前記タイヤを製造する方法としては、慣用の方法を用いることができる。例えば、タイヤ成形用ドラム上に未加硫ゴムからなるカーカス層、ベルト層、トレッド層等の通常タイヤ製造に用いられる部材を順次貼り重ね、ドラムを抜き去ってグリーンタイヤとする。次いで、このグリーンタイヤを常法に従って加熱加硫することにより、所望のタイヤを製造することができる。
タイヤ用途以外にも、防振ゴム、免震ゴム、ベルト(コンベアベルト)、ゴムクローラ、各種ホース、モランなどに本発明のゴム組成物、又は、本発明の架橋ゴム組成物を使用することができる。
十分に乾燥した400mL耐圧ガラス反応器に、1,3-ブタジエン13.58g(0.25mol)を含むトルエン溶液325mLを添加した後、エチレンを0.4MPaで導入した。一方、窒素雰囲気下のグローブボックス中で、ガラス製容器にビス(2-フェニルインデニル)ガドリニウムビス(ジメチルシリルアミド)[(2-PhC9H6)2GdN(SiHMe2)2]18.0μmol、ジメチルアニリニウムテトラキス(ペンタフルオロフェニル)ボレート(Me2NHPhB(C6F5)4)36.0μmol、及びジイソブチルアルミニウムハイドライド0.90mmolを仕込み、トルエン10mlに溶解させて触媒溶液とした。その後、グローブボックスから触媒溶液を取り出し、ガドリニウム換算で17.5μmolとなる量をモノマー溶液へ添加し、室温で180分間重合を行った。重合後、2,2’-メチレン-ビス(4-エチル-6-t-ブチルフェノール)(NS-5)5質量%のイソプロパノール溶液1mLを加えて反応を停止させ、さらに大量のメタノールで共重合体を分離し、70°Cで真空乾燥し共重合体Aを得た。得られた共重合体Aの収量は12.00gであった。
十分に乾燥した200mL耐圧ガラス反応器に、1,3-ブタジエン3.38g(0.063mol)を含むトルエン溶液20mLを添加した後、エチレンを2.45g(0.088mol)導入した。一方、窒素雰囲気下のグローブボックス中で、ガラス製容器にビス(2-フェニルインデニル)ガドリニウムビス(ジメチルシリルアミド)[(2-PhC9H6)2GdN(SiHMe2)2]5.5μmol、ジメチルアニリニウムテトラキス(ペンタフルオロフェニル)ボレート(Me2NHPhB(C6F5)4)11.0μmol、及びトリイソブチルアルミニウム0.41mmolを仕込み、トルエン10mLに溶解させて触媒溶液とした。その後、グローブボックスから触媒溶液を取り出し、ガドリニウム換算で17.5μmolとなる量をモノマー溶液へ添加し、室温で240分間重合を行った。重合後、2,2’-メチレンービス(4-エチル-6-t-ブチルフェノール)(NS-5)5質量%のイソプロパノール溶液1mLを加えて反応を停止させ、さらに大量のメタノールで共重合を分離し、70℃で真空乾燥し共重合体Bを得た。得られた共重合体Bの収量は4.15gであった。
十分に乾燥した400mL耐圧ガラス反応器に、1,3-ブタジエン18.20g(0.34mol)を含むトルエン溶液300mLを添加した後、エチレンを0.8MPaで導入した。一方、窒素雰囲気下のグローブボックス中で、ガラス製容器にトリスビストリメチルシリルアミドガドリニウム〔Gd[N(SiMe3)2]3〕34.0μmol、ジメチルアニリニウムテトラキス(ペンタフルオロフェニル)ボレート(Me2NHPhB(C6F5)4)41.0μmol、及びトリイソブチルアルミニウム1.l9mmolを仕込み、トルエン8mLに溶解させて触媒溶液とした。その後、グローブボックスから触媒溶液を取り出し、ガドリニウム換算で33.7μmolとなる量をモノマー溶液へ添加し、室温で180分間重合を行った。重合後、2,2-メチレン-ビス(4-エチル-6-t-ブチルフェノール)(NS-5)5質量%のイソプロパノール溶液1mLを加えて反応を停止させ、さらに大量のメタノールで共重合体を分離し、70℃で真空乾燥し共重合体Cを得た。得られた共重合体Cの収量は29.50gであった。
十分に乾燥した400mL耐圧ガラス反応器に、1,3-ブタジエン23.79g(0.44mol)を含むトルエン溶液300mLを添加した後、エチレンを0.8MPaで導入した。一方、窒素雰囲気下のグローブボックス中で、ガラス製容器にトリスビスジメチルシリルアミドスカンジウム〔(Sc[N(SiHMe2)2]3-(THF)2〕を500μmol、Me2NHPhB(C6F5)4600μmol、及びジイソブチルアルミニウムハイドライド10.0mmolを仕込み、トルエン25mLに溶解させて触媒溶液とした。その後、グローブボックスから触媒溶液を取り出し、ネオジウム換算で440μmolとなる量をモノマー溶液へ添加し、室温で180分間重合を行った。重合後、NS-5の5質量%のイソプロパノール溶液1mLを加えて反応を停止させ、さらに大量のメタノールで共重合体を分離し、70℃で真空乾燥し共重合体Dを得た。得られた共重合体Dの収量は37.40gであった。
十分に乾燥した400mL耐圧ガラス反応器に、1,3-ブタジエン3.95g(0.073mol)を含むトルエン溶液320mLを添加した後、エチレンを0.6MPaで導入した。一方、窒素雰囲気下のグローブボックス中で、ガラス製容器にジメチルアルミニウム(μ-ジメチル)ビス(2-フェニルインデニル)ネオジウム[(2-PhC9H6)2Nd(μ-Me)2AlMe2]204.0μmol、トリフェニルカルボニウムテトラキス(ペンタフルオロフェニル)ボレート(Ph3CB(C6F5)4)195.0μmolを仕込み、トルエン20mLに溶解させて触媒溶液とした。その後、グローブボックスから触媒溶液を取り出し、モノマー溶液へ添加し、室温で90分間重合を行った。重合後、2,2’-メチレン-ビス(4-エチル-6-t-ブチルフェノール)(NS-5)5質量%のイソプロパノール溶液1mLを加えて反応を停止させ、さらに大量のメタノールで共重合体を分離し、70℃で真空乾燥し共重合体Eを得た。得られた共重合体Eの収量は3.60gであった。
ゲルパーミエーションクロマトグラフィー[GPC:東ソー製HLC-8121GPC/HT、カラム:東ソー製GMHHR-H(S)HT×2本、検出器:示差屈折率計(RI)]を用いて、測定温度140℃で単分散ポリスチレンを基準として、重合体のポリスチレン換算の重量平均分子量(Mw)及び分子量分布(Mw/Mn)を求めた。
(2)シス-1,4結合含量
共重合体中のブタジエン部分のミクロ構造を、1H-NMRスペクトル(1,2-ビニル結合の結合量)及び13C-NMRスペクトル(シス-1,4結合とトランス-1,4結合の含有量比)の積分比より求めた。シス-1,4結合量(%)の計算値を表1に示す。
(3)エチレンの含有率
共重合体中のエチレン部分の含有率(mol%)を 13C-NMRスペクトル(100℃、d-テトラクロロエタン標準:73.8ppm)により全体のエチレン結合成分(28.5-30.0ppm)と全体のブタジエン結合成分(26.5-27.5ppm+31.5-32.5ppm)の積分比より求めた。エチレン部分の含有率(mol%)を表1に示す。
比較例2では、実施例5の共重合体Eで、重合温度を50℃とし、重合時問を30分とすること以外は、実施例5と同様方法で重合を行ったところ、共重合体Fを収量3.65g得た。
比較例3では、実施例1において、最初にエチレンを導入する際の圧力を0.2MPaとすること以外は、同様の方法で重合を行ったところ、共重合体Gを収量11.05g得た。
※1:N-(1,3-ジメチルブチル)-N’-p-フェニレンジアミン、大内新興化学(株)製、ノックラック6C
※2:N-シクロヘキシル-2-ベンゾチアゾリルスルフェンアミド、大内新興化学(株)製、ノクセラーCZ-G
※3:ジベンゾチアジルジスルフィド、大内新興化学(株)製、ノクセラーDM-P
JIS3号試験片中心部に0.5mmの亀裂を入れ、室温で0%~100%の歪みで繰り返し疲労を与え、サンプルが切断するまでの回数を測定した。表4においてはブタジエン重合体を配合した。比較例1を100として、それぞれを指数表示した。指数値が大きい程、耐亀裂成長性が良好であることを示す。
なお、表中>200は比較例1に対し2倍の回数の繰り返し疲労を与えても、サンプルの切断が起こらなかったことを示す。
JIS K 6259に従って、耐オゾン性を測定した。短冊状試験片を30%の動的伸張を与えながら、40℃、オゾン濃度50pphm条件で暴露し、24時間後の試料の状況(亀裂の有無)を目視で判断した。結果を表4に示す。
Claims (15)
- 共役ジエン化合物と、非共役オレフィンとの共重合体において、
共役ジエン部分のシス1,4-結合含量が70.5%より大きく、前記非共役オレフィンの含有量が10mol%以上であることを特徴とする共役ジエン化合物と非共役オレフィンとの共重合体。 - 前記非共役オレフィンの含有量が、50mol%以下である請求項1に記載の共役ジエン化合物と非共役オレフィンとの共重合体。
- 前記非共役オレフィンの含有量が20mol%未満である請求項1または2に記載の共役ジエン化合物と非共役オレフィンとの共重合体。
- 分子量分布(Mw/Mn)が10以下である請求項1~3のいずれかに記載の共役ジエン化合物と非共役オレフィンとの共重合体。
- 前記非共役オレフィンが、非環状オレフィンである請求項1~4のいずれかに記載の共役ジエン化合物と非共役オレフィンとの共重合体。
- 前記非共役オレフィンは、炭素数が2~10のαオレフィンである請求項1~5のいずれかに記載の共役ジエン化合物と非共役オレフィンとの共重合体。
- 前記非共役オレフィンが、エチレン、プロピレン及び1-ブテンよりなる群から選択される少なくとも一種である請求項1~6のいずれかに記載の共役ジエン化合物と非共役オレフィンとの共重合体。
- 前記非共役オレフィンが、エチレンである請求項7に記載の共役ジエン化合物と非共役オレフィンとの共重合体。
- 前記共役ジエン化合物は、炭素数が4~8である請求項1~8のいずれかに記載の共役ジエン化合物と非共役オレフィンとの共重合体。
- 前記共役ジエン化合物が、1,3-ブタジエン及びイソプレンよりなる群から選択される少なくとも一種である請求項9のいずれかに記載の共役ジエン化合物と非共役オレフィンとの共重合体。
- 請求項1~10に記載の共重合体を含むことを特徴とするゴム組成物。
- ゴム成分中に、前記共重合体を含む請求項11に記載のゴム組成物。
- ゴム成分100質量部に対し、補強性充填剤5質量部~200質量部と、架橋剤0.1質量部~20質量部とを含む請求項11または12に記載のゴム組成物。
- 請求項11~13に記載のゴム組成物を架橋して得られたことを特徴とする架橋ゴム組成物。
- 請求項11~13に記載のゴム組成物、又は、請求項14に記載の架橋ゴム組成物を用いたことを特徴とするタイヤ。