WO2012009653A1 - Injection molding process and product produced using the same - Google Patents
Injection molding process and product produced using the same Download PDFInfo
- Publication number
- WO2012009653A1 WO2012009653A1 PCT/US2011/044215 US2011044215W WO2012009653A1 WO 2012009653 A1 WO2012009653 A1 WO 2012009653A1 US 2011044215 W US2011044215 W US 2011044215W WO 2012009653 A1 WO2012009653 A1 WO 2012009653A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- invention according
- generally cylindrical
- plunger
- syringe
- Prior art date
Abstract
Description
Claims