WO2011135004A2 - Catalysts - Google Patents
Catalysts Download PDFInfo
- Publication number
- WO2011135004A2 WO2011135004A2 PCT/EP2011/056672 EP2011056672W WO2011135004A2 WO 2011135004 A2 WO2011135004 A2 WO 2011135004A2 EP 2011056672 W EP2011056672 W EP 2011056672W WO 2011135004 A2 WO2011135004 A2 WO 2011135004A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- catalyst
- alkyl
- group
- groups
- hydrocarbyl
- Prior art date
Abstract
Description
Claims