WO2011131501A1 - Radiation curable amino(meth)acrylates - Google Patents
Radiation curable amino(meth)acrylates Download PDFInfo
- Publication number
- WO2011131501A1 WO2011131501A1 PCT/EP2011/055604 EP2011055604W WO2011131501A1 WO 2011131501 A1 WO2011131501 A1 WO 2011131501A1 EP 2011055604 W EP2011055604 W EP 2011055604W WO 2011131501 A1 WO2011131501 A1 WO 2011131501A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- meth
- acrylate
- amino
- acrylates
- weight
- Prior art date
Abstract
Description
Claims