WO2011112335A2 - Coated pcbn cutting insert, coated pcbn cutting tool using such coated pcbn cutting insert, and method for making the same - Google Patents
Coated pcbn cutting insert, coated pcbn cutting tool using such coated pcbn cutting insert, and method for making the same Download PDFInfo
- Publication number
- WO2011112335A2 WO2011112335A2 PCT/US2011/025179 US2011025179W WO2011112335A2 WO 2011112335 A2 WO2011112335 A2 WO 2011112335A2 US 2011025179 W US2011025179 W US 2011025179W WO 2011112335 A2 WO2011112335 A2 WO 2011112335A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- coating layer
- alumina
- boron nitride
- cubic boron
- mpa
- Prior art date
Abstract
Description
Claims