WO2011079125A1 - Etheramines containing flexible and rigid segments and their use as intermediates for polymer synthesis - Google Patents
Etheramines containing flexible and rigid segments and their use as intermediates for polymer synthesis Download PDFInfo
- Publication number
- WO2011079125A1 WO2011079125A1 PCT/US2010/061581 US2010061581W WO2011079125A1 WO 2011079125 A1 WO2011079125 A1 WO 2011079125A1 US 2010061581 W US2010061581 W US 2010061581W WO 2011079125 A1 WO2011079125 A1 WO 2011079125A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- etheramine mixture
- epoxy resin
- mixture
- weight
- etheramine
- Prior art date
Abstract
Description
Claims