WO2011073944A1 - Pigment powder comprising lanthanides - Google Patents

Pigment powder comprising lanthanides Download PDF

Info

Publication number
WO2011073944A1
WO2011073944A1 PCT/IB2010/055886 IB2010055886W WO2011073944A1 WO 2011073944 A1 WO2011073944 A1 WO 2011073944A1 IB 2010055886 W IB2010055886 W IB 2010055886W WO 2011073944 A1 WO2011073944 A1 WO 2011073944A1
Authority
WO
WIPO (PCT)
Prior art keywords
powder
article
security
security element
lanthanide
Prior art date
Application number
PCT/IB2010/055886
Other languages
French (fr)
Inventor
Axelle Quinsac
Olivier Tillement
Henri Rosset
Cédric LOUIS
Original Assignee
Arjowiggins Security
Universite Claude Bernard Lyon 1 (Ucbl)
Centre National De La Recherche Scientifique
Nano H
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arjowiggins Security, Universite Claude Bernard Lyon 1 (Ucbl), Centre National De La Recherche Scientifique, Nano H filed Critical Arjowiggins Security
Publication of WO2011073944A1 publication Critical patent/WO2011073944A1/en

Abstract

The present invention relates to a pigment powder comprising lanthanide(s), characterized in that the lanthanide takes the form of lanthanide hydroxide, oxide and/or oxyhydroxide nanoparticles having a size less than 200 nm and a density greater than 6 and comprising more than 65 wt% lanthanide element, said lanthanide being chosen from holmium, neodymium and mixtures thereof.

Description

Poudre pigmentaire à base de lanthanides  Pigment powder based on lanthanides
La présente invention se rapporte au domaine des articles à authentifier, par exemple des documents de sécurité. Elle concerne une poudre pigmentaire à base de lanthamde(s), un élément de sécurité comportant une telle poudre et un article le comportant, ainsi qu'un procédé de sécurisation et un procédé d'authentification associés. The present invention relates to the field of articles to be authenticated, for example security documents. It relates to a pigment powder based lanthamde (s), a security element comprising such a powder and an article comprising it, and a security method and an associated authentication method.
Arrière-plan Background
Dans le domaine de l'authentification, notamment de documents de sécurité, une approche classique consiste à utiliser à des fins d'éléments de sécurité, des poudres fluorescentes qui, sous éclairage ultraviolet (UV) par exemple, émettent une couleur visible rouge ou verte et sont en revanche, indétectables sous un autre éclairage.  In the field of authentication, including security documents, a conventional approach is to use for security purposes, fluorescent powders which, under ultraviolet (UV) light for example, emit a visible red or green color and are, on the other hand, undetectable under a different light.
Parmi, les pigments fluorescents considérés pour un tel usage, les poudres à base de lanthanides s'avèrent tout particulièrement intéressantes.  Among the fluorescent pigments considered for such use, lanthanide powders are particularly interesting.
En effet, du fait de leurs propriétés physico-chimiques spécifiques, liées en particulier à la présence d'électrons dans leurs orbitales f et au remplissage partiel de ces orbitales f, les composés à base de lanthanides apparaissent généralement, sous éclairage naturel ou éclairage incandescent classique, faiblement colorés. En outre, compte-tenu de leurs numéros atomiques élevés et de leurs, indices optiques, ils diffusent fortement la lumière lorsqu'ils sont à l'état de poudre, ce qui diminue encore davantage leur potentielle coloration.  Indeed, because of their specific physicochemical properties, particularly related to the presence of electrons in their orbital f and the partial filling of these orbital f, the lanthanide-based compounds generally appear under natural lighting or incandescent lighting. classic, faintly colored. In addition, given their high atomic numbers and their optical indices, they strongly diffuse the light when they are in the form of powder, which further reduces their potential coloration.
Or, d'une manière générale, les lanthanides présentent par ailleurs, dans le domaine du visible, une zone d'absorption spécifique dans des domaines étroits de longueur d'onde avec dans ces domaines un coefficient d'extinction molaire assez faible. Ainsi, sous certains types d'éclairage fluorescent, lorsque la zone d'absorption spécifique du lanthanide chevauche une des couleurs du spectre d'émission, l'absorption se manifeste visuellement et le composé apparaît alors fortement coloré.  However, in general, the lanthanides also have, in the visible range, a specific absorption zone in narrow wavelength domains with in these areas a relatively low molar extinction coefficient. Thus, under certain types of fluorescent lighting, when the specific absorption zone of the lanthanide overlaps one of the colors of the emission spectrum, the absorption is manifested visually and the compound then appears strongly colored.
En conséquence, les lanthanides sont avantageusement aptes à manifester une variation de couleur au regard d'un changement d'éclairage et notamment lors du passage d'un éclairage du type lumière du jour à un éclairage fluorescent. Ce comportement optique est communément appelé « métamérisme » et correspond au phénomène par lequel deux surfaces, paraissant de même couleur sous un certain éclairage ou illuminant, peuvent apparaître de couleurs différentes sous un autre éclairage. Le document WO 2007/04179 propose ainsi de mettre en œuvre des pigments dopés en terres rares, à des fins de marquage de sécurité au regard précisément de leur aptitude à manifester ce comportement métamérique. Ces pigments sont plus particulièrement des phosphates de lanthanides ou encore se présentent sous la forme de nano-composites d'oxyde de Ianthanide encapsulé dans du verre. As a result, the lanthanides are advantageously capable of exhibiting a color variation with regard to a change of lighting and in particular when passing from daylight type lighting to fluorescent lighting. This optical behavior is commonly called "metamerism" and corresponds to the phenomenon by which two surfaces, appearing in the same color under a certain illumination or illuminant, can appear in different colors in a different light. The document WO 2007/04179 thus proposes to use pigments doped with rare earths, for purposes of security marking with regard precisely to their ability to manifest this metameric behavior. These pigments are more particularly lanthanide phosphates or are in the form of nano-composites of glass-encapsulated lanthanide oxide.
Les inventeurs ont pour leur part constaté qu'il est possible d'exacerber le comportement métamérique des lanthanides sous réserve de les mettre en œuvre sous une forme spécifique.  The inventors have for their part found that it is possible to exacerbate the metameric behavior of lanthanides provided they are implemented in a specific form.
Résume Summary
Un premier but de l'invention est de proposer une nouvelle famille de pigments de lanthanides particulièrement intéressante au regard de son comportement en terme d'effet métamérique.  A first object of the invention is to provide a new family of lanthanide pigments particularly interesting in terms of its behavior in terms of metameric effect.
Un second but de la présente invention est de proposer un nouveau type d'élément de sécurité afin d'accroître ou de renouveler la sécurité de documents.  A second object of the present invention is to provide a new type of security element to increase or renew the security of documents.
Un autre but de la présente invention est de proposer un élément de sécurité optiquement variable facile d'utilisation.  Another object of the present invention is to provide an optically variable security element easy to use.
L'invention a ainsi pour objet, selon l'un de ses aspects, une poudre pigmentaire à base de lanthanide(s), caractérisée en ce que ledit Ianthanide y est présent à l'état de nanoparticules d'hydroxyde, d'oxyde et/ou d'oxohydroxyde de Ianthanide,- lesdites nanoparticules possédant une densité supérieure à 6 et étant formées à plus de 65 % massique en élément Ianthanide.  The invention thus has, according to one of its aspects, a pigmentary powder based on lanthanide (s), characterized in that said lanthanide is present in the state of nanoparticles of hydroxide, oxide and and / or of lanthanide oxohydroxide, - said nanoparticles having a density greater than 6 and being formed at more than 65% by weight of lanthanide element.
Plus particulièrement, la présente invention a pour objet une poudre pigmentaire à base de lanthanide(s), caractérisée en ce que ledit Ianthanide y est présent à l'état de nanoparticules d'hydroxyde, d'oxyde et/ou d'oxohydroxyde de Ianthanide, lesdites nanoparticules présentant une taille inférieure à 200 nm, possédant une densité supérieure à 6 et étant formées à plus de 65 % massique en élément Ianthanide, ledit Ianthanide étant choisi parmi l'holmium, le néodyme et leurs mélanges.  More particularly, the subject of the present invention is a pigmentary powder based on lanthanide (s), characterized in that the said lanthanide is present in the state of nanoparticles of hydroxide, of oxide and / or of oxohydroxide of lanthanide. said nanoparticles having a size of less than 200 nm, having a density greater than 6 and being formed at greater than 65 wt.% of lanthanide element, said lanthanide being selected from holmium, neodymium and mixtures thereof.
La présente invention découle notamment de l'observation par les inventeurs qu'un ajustement d'une poudre de Ianthanide en termes de taille de ses particules, nature chimique du composé Ianthanide la formant et de la teneur de ses particules en élément Ianthanide permet contre toute attente d'optimiser le spectre d'absorption de la poudre correspondante et d'en tirer profit en termes de comportement métamérique. L'ajustement du spectre d'absorption de par le choix des paramètres précités, permet de se placer dans ou entre les zones d'émission fluorescente et d'exacerber ainsi l'amplitude du changement métamérique de la coloration lors de la modification d'éclairage. The present invention derives in particular from the observation by the inventors that an adjustment of a lanthanide powder in terms of the size of its particles, the chemical nature of the lanthanide compound forming it and the content of its particles in lanthanide element makes it possible waiting to optimize the absorption spectrum of the corresponding powder and to take advantage of it in terms of metameric behavior. The adjustment absorption spectrum by the choice of the aforementioned parameters, can be placed in or between the fluorescent emission zones and thus exacerbate the magnitude of the metameric change in color during the illumination modification.
Ainsi, comme il ressort des exemples qui suivent, une poudre selon l'invention et à base d'oxyde d'holmium. présente avantageusement une coloration exacerbée sous certains types d'éclairage en l'occurrence un éclairage fluorescent de type tube ou fluo- compact, et est en revanche apte à montrer une transition de couleur nette quand on l'expose à d'autres types d'éclairages, par exemple un illuminant Des- Ainsi, elle apparaît alors blanche/beige/rosée lorsqu'elle est exposée à la lumière du jour ou à une lampe à spectre large du type lampe à incandescence, c'est-à-dire un éclairage basé sur une variation continue en fonction de la longueur d'onde de l'énergie des photons émis par un corps noir.  Thus, as is apparent from the examples which follow, a powder according to the invention and based on holmium oxide. advantageously exhibits an exacerbated coloration under certain types of lighting, in this case fluorescent lighting of the tube or fluo-compact type, and is, on the other hand, able to show a clear color transition when exposed to other types of lighting. For example, it appears white / beige / pink when it is exposed to daylight or to a broad-spectrum lamp of the incandescent lamp type, that is to say a light. based on a continuous variation as a function of the wavelength of the energy of the photons emitted by a black body.
Au regard de ce comportement métamérique optimisé, une poudre conforme à la présente invention est particulièrement avantageuse à titre d'élément de sécurité.  In view of this optimized metameric behavior, a powder according to the present invention is particularly advantageous as a security element.
Poudre pigmentaire Pigmentary powder
Comme précisé ci-dessus, une poudre pigmentaire selon l'invention est formée de nanoparticuies d'hydroxyde, d'oxyde et/ou d'oxohydroxyde de lanthanide, lesdites nanoparticules possédant une densité supérieure à 6, étant formées à plus de 65 % massique en élément lanthanide.  As specified above, a pigment powder according to the invention is formed of nanoparticles of hydroxide, oxide and / or lanthanide oxohydroxide, said nanoparticles having a density greater than 6 being formed at more than 65% by mass. in lanthanide element.
Par poudre « pigmentaire », on entend une poudre apte à manifester un effet coloriel.  "Pigmentary" powder means a powder capable of manifesting a color effect.
De préférence, les nanoparticules présentent une taille inférieure à 500 nm, inférieure à 400 nm, inférieure à 300 nm, inférieure à 200 nm, voire inférieure à 100 nm et/ou de préférence supérieure à 50 nm. Avantageusement, une diminution de la taille des nanoparticules permet d'atténuer le phénomène de diffusion de la lumière par lesdites nanoparticules. La couleur de la poudre apparaît ainsi d'autant plus intense.  Preferably, the nanoparticles have a size less than 500 nm, less than 400 nm, less than 300 nm, less than 200 nm, or even less than 100 nm and / or preferably greater than 50 nm. Advantageously, a decrease in the size of the nanoparticles makes it possible to attenuate the phenomenon of diffusion of light by said nanoparticles. The color of the powder appears all the more intense.
La taille des particules est celle déterminée, soit à partir de l'élargissement des raies en diffraction des rayons X, soit à partir d'une somme d'observations au microscope électronique à transmission ou à balayage, soit par granulométrie laser, par exemple du type diffusion laser DLS.  The size of the particles is that determined, either from the broadening of the lines in X-ray diffraction, or from a sum of observations with a transmission or scanning electron microscope, or by laser particle size, for example DLS laser diffusion type.
De manière avantageuse, les nanoparticules sont de forme sphérique ou quasi- sphérique. Le ianthanide est au sens de l'invention une terre rare choisie parmi Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu et leurs mélanges. Advantageously, the nanoparticles are spherical or quasi-spherical. For the purposes of the invention, the ianthanide is a rare earth chosen from Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu and their mixtures.
De préférence, il est choisi parmi l'holmium, le néodyme et leurs mélanges. Preferably, it is chosen from holmium, neodymium and their mixtures.
De manière encore plus préférée, le lanthanide est l'holmium. Even more preferably, the lanthanide is holmium.
Comme précisé au dessus, le lanthanide est présent dans la poudre à l'état d'un mélange d'hydroxyde, d'oxyde et d'oxohydroxyde dudit lanthanide.  As specified above, the lanthanide is present in the powder in the form of a mixture of hydroxide, oxide and oxohydroxide of said lanthanide.
Selon un autre mode de réalisation, le lanthanide est présent dans la poudre à l'état d'oxyde dudit lanthanide.  According to another embodiment, the lanthanide is present in the powder in the oxide state of said lanthanide.
Comme précisé plus haut, une poudre pigmentaire selon l'invention est notamment remarquable en ce que les nanoparticules sont formées à plus de 65% massique en élément(s) lanthanide(s). De préférence encore, elles sont formées à plus de 70 % en masse, plus de 75 %, plus de 80 % en masse voire plus de 85 % en masse d!élément(s) lanfhanide(s). As mentioned above, a pigment powder according to the invention is particularly remarkable in that the nanoparticles are formed at more than 65% by weight of lanthanide element (s). More preferably, they are formed at more than 70% by weight, more than 75%, more than 80% by weight or even more than 85% by weight of d ! element (s) lanfhanide (s).
Au regard de cette forte teneur, il est possible de tirer profit du phénomène métamérique à de faibles quantités de poudre, ce qui peut s'avérer avantageux dans certaines applications.  Given this high content, it is possible to take advantage of the metameric phenomenon at low amounts of powder, which may be advantageous in some applications.
Lesdites nanoparticules présentent une densité supérieure à 6, de préférence une densité supérieure à 7.  Said nanoparticles have a density greater than 6, preferably a density greater than 7.
Par « densité » des nanoparticules, on entend la densité particulaire des nanoparticules, c'est-à-dire la densité calculée en , ne tenant compte que du volume des nanoparticules, sans tenir compte du volume de la densité ouverte. Ce volume peut être obtenu en mesurant le déplacement d'un liquide lors de l'immersion de la poudre. Cette densité est très proche de la densité d'un monocristal massif du même matériau.  By "density" of the nanoparticles is meant the particle density of the nanoparticles, that is to say the density calculated in, taking into account only the volume of the nanoparticles, without taking into account the volume of the open density. This volume can be obtained by measuring the displacement of a liquid during the immersion of the powder. This density is very close to the density of a solid single crystal of the same material.
Comme précisé ci-dessus, les composés lanthanides formant une poudre pigmentaire selon l'invention présentent une absorption spécifique dans des domaines étroits de longueur d'onde, avec dans ces domaines un coefficient d'extinction molaire assez faible et quasiment pas d'absorption dans les autres domaines visibles.  As specified above, the lanthanide compounds forming a pigment powder according to the invention have a specific absorption in narrow wavelength domains, with in these areas a relatively low molar extinction coefficient and almost no absorption in the other visible domains.
Selon une première variante, un des domaines d'absoiption de ladite poudre est commun avec une des bandes d'émissions étroite d'un éclairage fluorescent (basé pour simplification sur un éclairage « blanc » fait par combinaison de 3 couleurs). Ainsi, lorsque la poudre est exposée à cet éclairage fluorescent, une coloration exacerbée apparaît. Par contre, sous un éclairage du type lumière du jour ou une lampe à incandescence, la faible absorption dans les zones étroites du. spectre n'est pas sensible et ladite' poudre apparaît alors très peu colorée, et généralement blanche et/ou beige. According to a first variant, one of the areas of absoiption of said powder is common with one of the narrow emission bands of fluorescent lighting (based for simplification on a "white" lighting made by combination of 3 colors). Thus, when the powder is exposed to this fluorescent lighting, an exacerbated coloration appears. On the other hand, under daylight type lighting or incandescence, the low absorption in the narrow areas of the . spectrum is not sensitive and said ' powder appears then very little color, and usually white and / or beige.
Les poudres conformes à l'invention à base d'holmium sont particulièrement intéressantes à ce titre.  The powders according to the invention based on holmium are particularly interesting in this respect.
Ainsi la bande d'absorption de l'holmium dans le domaine 550 nm est quasiment indécelable sous éclairage naturel (Des) ou incandescent (A). Par contre, elle chevauche fortement des bandes d'émission d'éclairages fluorescents et apparaît alors rose sous certains types d'éclairage, notamment sous certains tubes fluorescents.  Thus the absorption band of the holmium in the 550 nm range is almost undetectable under natural lighting (Des) or incandescent (A). On the other hand, it strongly overlaps emission bands of fluorescent lighting and appears pink under certain types of lighting, especially under certain fluorescent tubes.
Selon une seconde variante, la poudre pigmentaire selon l'invention présente des bandes étroites d'absorption situées entre les bandes d'émission de l'éclairage fluorescent, ou réparties de façon homogène sur les pics d'émission de l'éclairage fluorescent. Dans ces conditions, la poudre n'apparaît pas ou peu colorée alors que sous un éclairage du type lumière du jour ou une lampe à incandescence, elle apparaît plus colorée. L'écart de couleur observé suite au changement d'illuminant peut couespondre à une différence de couleur ou écart colorimétrique ΔΕ (selon l'espace colorimétrique C1E Lab 1976) supérieure à 0,2 et de préférence supérieure à 1.  According to a second variant, the pigment powder according to the invention has narrow absorption bands situated between the emission bands of the fluorescent lighting, or distributed homogeneously over the emission peaks of the fluorescent lighting. Under these conditions, the powder does not appear or little color while under a daylight type of lighting or incandescent lamp, it appears more colorful. The color difference observed following the change in illuminant may correspond to a difference in color or color difference ΔΕ (according to the C1E Lab 1976 color space) greater than 0.2 and preferably greater than 1.
Les poudres conformes à l'invention à base de néodyme sont particulièrement intéressantes à ce titre, en particulier avec la présence de bandes d'absorption autour de 580 nm et plus généralement dans les zones 535, 580, 600 et 670 nm. Sous éclairage du type lumière du jour ομ incandescent, une telle poudre apparaît légèrement colorée en violet alors que sous certains types d'éclairage, notamment produit par des tubes fluorescents, la poudre apparaît blanche.  The powders according to the invention based on neodymium are particularly interesting in this respect, in particular with the presence of absorption bands around 580 nm and more generally in the zones 535, 580, 600 and 670 nm. Under lighting of the daylight type ομ incandescent, such a powder appears slightly colored purple while under certain types of lighting, in particular produced by fluorescent tubes, the powder appears white.
De préférence, les nanoparticules de lanthanide considérées selon l'invention et plus particulièrement celles à base, d'oxyde d'holmium présentent un spectre d'absorption montrant un pic d'absorption localisé entre 530 et 560 nm, de préférence entre 540 et 555 nm.  Preferably, the lanthanide nanoparticles considered according to the invention and more particularly those based on holmium oxide have an absorption spectrum showing an absorption peak located between 530 and 560 nm, preferably between 540 and 555 nm. nm.
D'une manière avantageuse, la poudre pigmentaire de l'inventaire est préparée selon un procédé comprenant au moins les étapes successives consistant en :  Advantageously, the inventory pigment powder is prepared according to a process comprising at least the successive steps consisting of:
a) dissoudre des précurseurs de lanthanide dans un solvant ou mélange de solvants organiques polaires dont la température d'ébullition à pression atmosphérique est supérieure à 200 °C, en présence d'eau de manière à former l'hydroxyde, oxyde et/ou oxohydroxyde de lanthanide souhaité, et b) chauffer la solution obtenue à l'étape a) à une température variant de 170 à 250 °C de manière à obtenir la précipitation d'une poudre de l'hydroxyde, oxyde et/ou oxohydroxydc de lanthanide souhaité, sous la forme de nanoparticules. a) dissolving lanthanide precursors in a solvent or mixture of polar organic solvents whose boiling point at atmospheric pressure is greater than 200 ° C, in the presence of water so as to form the hydroxide, oxide and / or oxohydroxide desired lanthanide, and b) heating the solution obtained in step a) to a temperature ranging from 170 to 250 ° C so as to obtain the precipitation of a powder of the desired hydroxide, oxide and / or oxohydroxide of lanthanide, in the form of nanoparticles.
Les nanoparticules ainsi formées et isolées peuvent le cas échéant subir un traitement thermique complémentaire entre 500 et 1500 °C, de préférence supérieure à 800 °C, qui peut être suivi d'un broyage mécanique.  The nanoparticles thus formed and isolated may optionally undergo additional heat treatment between 500 and 1500 ° C, preferably greater than 800 ° C, which may be followed by mechanical grinding.
Les précurseurs de lanthanide plus particulièrement considérés sont composés pour plus de 50 % molaire, de préférence pour plus de 90 % molaire, de nitrate(s) de lanthanide(s).  The lanthanide precursors more particularly considered are composed for more than 50 mol%, preferably more than 90 mol%, of nitrate (s) of lanthanide (s).
Le solvant organique polaire est avantageusement choisi parmi les alcools, glycines, huiles ou de préférence les polyols, seuls ou en mélange. De préférence, le solvant organique est le diéthylène glycol.  The polar organic solvent is advantageously chosen from alcohols, glycines, oils or preferably polyols, alone or as a mixture. Preferably, the organic solvent is diethylene glycol.
La dissolution des précurseurs au sein d'un tel solvant est généralement réalisée par chauffage à une température généralement comprise entre 120 et 150 °C.  The dissolution of the precursors in such a solvent is generally carried out by heating at a temperature generally between 120 and 150 ° C.
Comme précisé ci-dessus, cette solution doit contenir au moins une quantité d'eau suffisante pour la formation de Γ oxohydroxydc, hydroxyde et/ou oxyde souhaité. Avantageusement, on utilise une quantité d'eau comprise entre 1 et 200 g, de préférence entre 10 et 100 g, d'eau par litre de solvant. Après homogénéisation de la solution et en fonction de la composition souhaitée, de l'eau et/ou une base de type NaOH, KOH, Ca(OH)2, NH3. aminés, glymes, acétates ou autres composés basiques organiques peuvent donc être ajoutées au mélange réactionnel. Les quantités sont variables et peuvent dépasser la stœchiométrie, l'utilisation de 0,01 à 1 mol de base par litre de solvant est néanmoins préférée. De manière avantageuse, la solution obtenue à l'étape a) est portée selon l'étape b), à une température variant de 175 à 185 °C, notamment d'environ 180 °C. As stated above, this solution should contain at least a sufficient amount of water for the formation of the desired oxohydroxide, hydroxide and / or oxide. Advantageously, a quantity of water of between 1 and 200 g, preferably between 10 and 100 g, of water per liter of solvent is used. After homogenization of the solution and depending on the desired composition, water and / or a base of NaOH, KOH, Ca (OH) 2 , NH 3 type. Amines, glymes, acetates or other organic basic compounds can therefore be added to the reaction mixture. The amounts are variable and can exceed the stoichiometry, the use of 0.01 to 1 mol of base per liter of solvent is nevertheless preferred. Advantageously, the solution obtained in step a) is carried according to step b), at a temperature ranging from 175 to 185 ° C, in particular about 180 ° C.
De pi'éférence, le chauffage est effectué à pression atmosphérique. Il est avantageusement maintenu au moins 30 minutes, en particulier au moins 1 heure, et de préférence 2 heures.  Preferably, the heating is carried out at atmospheric pressure. It is advantageously maintained at least 30 minutes, in particular at least 1 hour, and preferably 2 hours.
De manière particulièrement avantageuse, l'étape b) consiste en un chauffage selon plusieurs paliers. En particulier, le chauffage peut comprendre au moins les paliers suivants : . . - un premier palier à une température comprise entre 50 et 70 °C, de préférence d'environ 60 °C ; Particularly advantageously, step b) consists of heating in several stages. In particular, the heating may comprise at least the following levels: . a first stage at a temperature of between 50 and 70 ° C., preferably of approximately 60 ° C .;
~ un second palier à une température comprise entre 120 et 150 °C, de préférence d'environ 140 °C ; et  a second step at a temperature between 120 and 150 ° C, preferably about 140 ° C; and
- un troisième palier à une température comprise entre 170 °C et 250 °C, de préférence entre 175 °C et 185 °C et avantageusement d'environ 180 DC. - a third stage at a temperature between 170 ° C and 250 ° C, preferably between 175 ° C and 185 ° C and preferably about 180 D C.
En particulier, le premier palier décrit précédemment peut être maintenu pendant une durée de 30 minutes à 60 minutes, en particulier pendant 45 minutes.  In particular, the first stage described above can be maintained for a period of 30 minutes to 60 minutes, in particular for 45 minutes.
Le second palier décrit précédemment peut être maintenu pendant une durée d'au moins 30 minutes, en particulier durant 60 minutes.  The second stage described above can be maintained for a period of at least 30 minutes, in particular for 60 minutes.
Selon un mode de réalisation particulier, une solution comprenant au moins une base peut être ajoutée à la solution chauffée lors du second palier.  According to a particular embodiment, a solution comprising at least one base can be added to the heated solution during the second stage.
De manière avantageuse, la solution ajoutée est une solution de soude, de préférence de concentration allant de 0,5 à 10 mol/L, notamment d'environ 3 mol/L.  Advantageously, the solution added is a sodium hydroxide solution, preferably of concentration ranging from 0.5 to 10 mol / l, in particular of approximately 3 mol / l.
Selon un mode de réalisation particulièrement préféré, le troisième palier décrit précédemment est maintenu au moins 60 minutes, de préférence environ 120 minutes.  According to a particularly preferred embodiment, the third stage described above is maintained at least 60 minutes, preferably about 120 minutes.
Avantageusement, l'étape b) consiste en un chauffage de la solution seton les trois paliers décrits précédemment. Advantageously, step b) consists of heating the solution according to the three steps described above.
Le passage d'un palier de température à un autre est avantageusement opéré par chauffage progressif, de préférence à une vitesse allant de 1 à 2 °C par minute. Ainsi, le second palier peut être atteint à partir du premier palier en environ une heure de chauffage progressif. De même, le troisième palier peut être atteint à partir du second palier en environ 30 minutes de chauffage progressif.  The transition from one temperature step to another is advantageously carried out by progressive heating, preferably at a rate ranging from 1 to 2 ° C. per minute. Thus, the second step can be reached from the first step in about one hour of progressive heating. Similarly, the third step can be reached from the second step in about 30 minutes of progressive heating.
Un tel procédé de préparation permet avantageusement d'obtenir des nanoparticules présentant la taille et la densité souhaitées selon l'invention.  Such a preparation method advantageously makes it possible to obtain nanoparticles having the desired size and density according to the invention.
Le colloïde formé à l'issue de l'étape b) présente directement après synthèse une charge massique en solide comprise entre 5 et 200 g de poudre par litre de solvant et de préférence entre 20 et 50 g de poudre par litre de solvant. En outre, plus de 50 %, voire même plus de 90 % en moles des ions de lanthanides introduits dans la solution initiale se retrouvent dans la poudre. The colloid formed at the end of step b) has, directly after synthesis, a solids mass load of between 5 and 200 g of powder per liter of solvent and preferably between 20 and 50 g of powder per liter of solvent. In addition, more than 50% or even more than 90 mol% of the lanthanide ions introduced into the initial solution are found in the powder.
Bien entendu, la suspension colloïdale obtenue à l'issue de l'étape b) peut subir différentes étapes de purification, extraction, traitement et redispersion avec ou sans modificateur de surface dans le solvant d'origine ou tout type de solvant aqueux ou organique.  Of course, the colloidal suspension obtained at the end of step b) may undergo different purification, extraction, treatment and redispersion steps with or without a surface modifier in the original solvent or any type of aqueous or organic solvent.
Ainsi, la poudre peut être séparée de la solution par filtration' ou par centrifugation. Plusieurs étapes de centrifugation peuvent être nécessaires, avec à chaque fois, une redispersion dans un solvant approprié aqueux ou organique, de préférence un alcool, éther ou acétone, en particulier l'éthanol.  Thus, the powder can be separated from the solution by filtration or centrifugation. Several centrifugation steps may be necessary, with each time a redispersion in a suitable aqueous or organic solvent, preferably an alcohol, ether or acetone, in particular ethanol.
La poudre ainsi obtenue peut ensuite être séchée par chauffage doux, à l'air ou sous vide. Par exemple, la poudre peut être séchée pendant 1 heure dans une étuve.  The powder thus obtained can then be dried by gentle heating, in air or under vacuum. For example, the powder can be dried for 1 hour in an oven.
En ce qui concerne le traitement thermique complémentaire réalisé à haute température, sous atmosphère inerte ou en conditions oxydantes ou réductrices, il permet notamment de décomposer les composés organiques restant à la surface des particules ou les hydroxydes, modifier la structure cristalline, la taille des cristallites, les valences des éléments ou même la taille des poudres. With regard to the complementary heat treatment carried out at high temperature, under an inert atmosphere or under oxidizing or reducing conditions, it makes it possible in particular to decompose the organic compounds remaining on the surface of the particles or the hydroxides, to modify the crystalline structure, the crystallite size , the valences of the elements or even the size of the powders.
Selon un mode particulièrement avantageux, ce traitement thermique complémentaire peut être réalisé par chauffage progressif, entre 300 °C et 900 °C, en particulier par paliers tous les 200 °C.  According to a particularly advantageous embodiment, this additional heat treatment can be carried out by progressive heating, between 300 ° C. and 900 ° C., in particular in steps every 200 ° C.
De préférence, chaque palier dure au moins une heure, en particulier entre une heure et 12 heures.  Preferably, each step lasts at least one hour, in particular between one hour and 12 hours.
Les exemples 1 et 3 qui suivent illustrent la mise en œuvre du procédé selon l'invention pour l'obtention de poudres composées d'un mélange d'hydroxyde, d'oxyde et d'oxohydroxyde de lanthanide(s). Les exemples 2 et 4 illustrent quant à eux l'obtention de poudres composées majoritairement d'oxyde de lanthanide(s).  Examples 1 and 3 which follow illustrate the implementation of the process according to the invention for obtaining powders composed of a mixture of hydroxide, oxide and lanthanide oxohydroxide (s). Examples 2 and 4 illustrate the production of powders composed mainly of lanthanide oxide (s).
Bien entendu, l'homme du métier est à même d'opérer les ajustements nécessaires du procédé de l'invention pour obtenir les autres variantes de poudres selon l'invention, telles que des poudres composées majoritairement d'hydroxyde de lanthanide(s) ου d'oxohydroxyde de lanthanide(s). La poudre pigmentaire peut comprendre en outre un composant fluorescent, par exemple tel que Eu, Tb, Yb, Nd, phosphorescent ou à effet interférentiel. Ce composant peut constituer de 1 à 15 % en masse, de préférence de 4 à 8 % en masse, de ladite poudre pigmentaire. Of course, those skilled in the art are able to make the necessary adjustments of the process of the invention to obtain the other variants of powders according to the invention, such as powders composed mainly of lanthanide hydroxide (s) of lanthanide oxohydroxide (s). The pigment powder may further comprise a fluorescent component, for example such as Eu, Tb, Yb, Nd, phosphorescent or interferential effect. This component may constitute from 1 to 15% by weight, preferably from 4 to 8% by weight, of said pigmentary powder.
Elément de sécurité Security element
L'invention concerne également l'utilisation d'une poudre selon l'invention à titre d'élément de sécurité, en particulier comme élément de sécurité visuellement détectable.  The invention also relates to the use of a powder according to the invention as a security element, in particular as a visually detectable security element.
Plus particulièrement, l'invention a pour objet, selon un autre de ses aspects, un élément de sécurité, notamment un élément de sécurité à effet optique métamérique, comportant une poudre conforme à l'invention.  More particularly, according to another of its aspects, the subject of the invention is a security element, in particular a metameric optical effect security element, comprising a powder according to the invention.
Un tel élément peut être destiné à être incorporé dans ou sur un article, par exemple un document de sécurité et/ou de valeur.  Such an element may be intended to be incorporated in or on an article, for example a security document and / or value.
L'élément de sécurité peut se présenter sous diverses formes. Il peut notamment être sous une forme supportée ou non. Il peut notamment s'agir d'une composition de revêtement, une encre, une particule, un agglomérat de particules, une planchette, d'un adhésif, une fibre, un fil ' ou une bande de sécurité, un fil au sens « textile » du terme, une planchette, un laminât, un foil, un patch, un film de sécurité, une pochette de sécurité, entre autres. The security element can be in various forms. It can in particular be in a supported form or not. It may especially be a coating composition, an ink, a particle, an agglomerate of particles, a board, an adhesive, a fiber, a yarn "or a security strip, a thread within the meaning" textile "Of the term, a board, a laminate, a foil, a patch, a security film, a security pouch, among others.
Composition de revêtement Coating composition
L'élément de sécurité peut être figuré par- une composition de revêtement, du type composition de couchage, de surfaçage, vernis ou primaire d'accrochage.  The security element can be represented by a coating composition, such as coating composition, surfacing, varnish or primer.
La poudre pigmentaire selon l'invention peut notamment être intégrée à une application de couchage de pigments à effet interférentiel et/ou de pigments iridescents.  The pigment powder according to the invention may in particular be incorporated into a coating application of interference-effect pigments and / or iridescent pigments.
Elle peut encore être intégrée à un primaire d'accrochage, par exemple destiné à être appliqué en dépassement d'un foil décrit ci-après.  It can also be integrated in a bonding primer, for example intended to be applied in excess of a foil described below.
Encre Ink
Lorsque l'élément de sécurité est une encre, celle-ci peut en tant que telle être appliquée par diverses techniques d'impression connues dans le domaine de la sécurité comme par exemple l'impression taille douce, l'impression offset, la sérigraphie, la flexographie, l'héliogravure, la typographie, l'impression numérique, comme par exemple Félectrophotographie ou l'impression jet d'encre. When the security element is an ink, it can as such be applied by various printing techniques known in the field of security such as for example intaglio printing, offset printing, screen printing, the flexography, rotogravure, typography, digital printing, such as electrophotography or inkjet printing.
L'encre peut notamment être appliquée sur un support d'impression de nature papier ou polymère.  The ink may especially be applied to a printing medium of a paper or polymer nature.
Selon un mode de réalisation particulier, une encre constituée à titre de pigments d'une poudre de lanthanides selon l'invention apparaît incolore sous éclairage incandescent ou lumière du jour et apparaît en revanche fortement colorée sous un éclairage fluorescent. Ainsi, un motif imprimé avec une telle encre n'est pas décelable en lumière du jour, mais peut être révélé sous illuminant adapté. Une telle encre peut par exemple être constituée à titre de pigments d'une poudre d'hydroxyde, d'oxyde et/ou d'oxohydroxyde d'holmium selon l'invention.  According to a particular embodiment, an ink constituted as pigments of a lanthanide powder according to the invention appears colorless under incandescent lighting or daylight and appears on the other hand strongly colored under fluorescent lighting. Thus, a pattern printed with such an ink is not detectable in daylight, but can be revealed under suitable illuminant. Such an ink may for example be constituted as pigments of a hydroxide powder, oxide and / or holmium oxohydroxide according to the invention.
Selon un autre mode de réalisation particulier, une encre constituée à titre de pigments d'une poudre de lanthanides selon l'invention apparaît colorée sous éclairage incandescent ou lumière du jour et apparaît blanche ou incolore sous éclairage fluorescent. L'encre peut alors être imprimée sur un article présentant sensiblement la même coloration sous éclairage incandescent ou lumière du jour. La présence de l'encre est ainsi rendue indétectable en lumière du jour. Une telle encre peut par exemple être constituée à titre de pigments d'une poudre d'hydroxyde, d'oxyde et d'oxohydroxyde de néodyme selon l'invention. .  According to another particular embodiment, an ink constituted as pigments of a lanthanide powder according to the invention appears colored under incandescent or daylight and appears white or colorless under fluorescent lighting. The ink can then be printed on an article having substantially the same color under incandescent or daylight. The presence of the ink is thus rendered undetectable in daylight. Such an ink may for example be constituted as pigments of a hydroxide powder, oxide and neodymium oxohydroxide according to the invention. .
Selon un autre mode de réalisation, une encre constituée à titre de pigments d'une poudre de lanthanides selon l'invention apparaît d'une première couleur sous éclairage incandescent ou lumière du jour et apparaître d'une deuxième couleur sous éclairage fluorescent. Une telle encre peut par exemple être constituée à titre de pigments d'une poudre d'oxyde mixte de néodyme selon l'invention, notamment une poudre d'oxydes de terres rares comprenant majoritairement du néodyme.  According to another embodiment, an ink constituted as pigments of a lanthanide powder according to the invention appears in a first color under incandescent lighting or daylight and appear a second color under fluorescent lighting. Such an ink may for example be constituted as pigments of a mixed neodymium oxide powder according to the invention, in particular a rare earth oxide powder mainly comprising neodymium.
11 est entendu que la présence concomitante d'autres pigments éventuels, avec une poudre de lanthanides selon l'invention, peut pondérer le changement de couleur associé au comportement métamérique de ladite poudre. L'homme de l'art est à même de procéder au choix de ces pigments de manière à tirer profit du phénomène métamérique au niveau de l'encre correspondante.  It is understood that the concomitant presence of other possible pigments, with a lanthanide powder according to the invention, can weight the color change associated with the metameric behavior of said powder. Those skilled in the art are able to proceed with the choice of these pigments so as to take advantage of the metameric phenomenon at the corresponding ink level.
Particule L'élément de sécurité selon l'invention peut être une particule, formée notamment par l'agglomération de nanoparticules formant la poudre selon l'invention. Particle The security element according to the invention may be a particle, formed in particular by the agglomeration of nanoparticles forming the powder according to the invention.
De préférence, une telle particule est fabriquée suivant le procédé de fabrication d'une Hilite1 M. Ladite particule peut notamment être obtenue par agglomération de nanoparticules d'oxyde d'holmium sous lit fîuidisé. Preferably, such a particle is produced by the method of manufacturing a Hilite 1M. Said particle may in particular be obtained by agglomeration of holmium oxide nanoparticles under a fluidized bed.
La particule peut être destinée à être couchée sur ou noyée dans un article, notamment un document de sécurité et/ou de valeur.  The particle may be intended to be lying on or embedded in an article, including a security document and / or value.
Fibre Fiber
Un élément de sécurité selon l'invention peut également être une fibre, notamment une fibre de sécurité.  A security element according to the invention may also be a fiber, in particular a security fiber.
Dans le cas particulier d'une fibre de sécurité à matrice polymérique. la poudre pigraentaire selon l'invention peut être incorporée dans ladite matrice, après y avoir été introduite lors de l'extrusion.  In the particular case of a polymeric matrix security fiber. the pigmentation powder according to the invention can be incorporated into said matrix, after having been introduced during the extrusion.
La fibre peut être incorporée dans ou sur un article selon un motif, ou sous forme de bande ou de semis.  The fiber may be incorporated in or on an article in a pattern, or in strip or seed form.
Lorsque la fibre est incorporée dans un article de type papier, elle peut, sous illuminant adapté, être révélée en lumière transmise. Une telle fibre peut ainsi, par analyse d'image, constituer un moyen de signature unique de l'article dans lequel elle est présente. Fil ou bande de sécurité  When the fiber is incorporated in a paper-type article, it can, under suitable illuminant, be revealed in transmitted light. Such a fiber can thus, by image analysis, constitute a unique signature means of the article in which it is present. Wire or security tape
L'élément de sécurité selon l'invention peut être un fil ou une bande de sécurité.  The security element according to the invention may be a wire or a security band.
Un tel fil ou bande de sécurité peut être incorporé totalement, notamment en masse, ou partiellement, notamment en surface ou en fenêtre(s), dans un article, notamment un document de sécurité. L'incorporation en fenêtre(s) peut permettre une meilleure visibilité de l'élément de sécurité et une meilleure tenue dans l'article. L'élément de sécurité est alors situé à la surface de l'article et en masse dans ce dernier, par exemple d'une façon alternée. En particulier, les fenêtres ainsi formées peuvent être traversantes ou non, selon que l'élément de sécurité apparaît respectivement sur deux ou sur une seule face de l'article. L'introduction d'un fil de sécurité en fenêtre(s) dans un seul jet est par exemple décrite dans les demandes de brevet EP 059 056 pour une machine à papier à forme ronde et EP 0 609 252 pour une machine à papier à table plate. L'introduction en fenêtre(s) entre deux jets d'un matériau fibreux multijet est quant à elle décrite dans la demande de brevet EP 0 229 645. Such a wire or security band can be incorporated totally, especially in bulk, or partially, especially in surface or window (s), in an article, including a security document. The incorporation into window (s) can allow a better visibility of the security element and a better hold in the article. The security element is then located on the surface of the article and mass in the latter, for example in an alternating manner. In particular, the windows thus formed may or may not be through, depending on whether the security element appears respectively on two or on one side of the article. The introduction of a safety wire window (s) in a single jet is for example described in patent applications EP 059 056 for a paper machine with round shape and EP 0 609 252 for a paper machine at the table flat. The introduction into window (s) between two jets of a multijet fibrous material is described in the patent application EP 0 229 645.
Le fil ou la bande de sécurité peut s'étendre d'un bord à l'autre de l'article, par exemple selon la longueur et/ou la largeur de l'article, notamment selon sa plus grande dimension.  The thread or the security band may extend from one edge to the other of the article, for example according to the length and / or the width of the article, in particular according to its largest dimension.
La poudre pigmentaire selon l'invention peut figurer sur tout ou partie du fil ou bande de sécurité. La poudre pigmentaire selon l'invention peut figurer sur une seule face ou plusieurs faces du fil ou bande de sécurité.  The pigment powder according to the invention may appear on all or part of the security thread or strip. The pigment powder according to the invention may appear on one or more faces of the security thread or strip.
La poudre pigmentaire selon l'invention peut par exemple être appliquée ou imprimée sur le fil ou bande de sécurité, par exemple par un des procédés décrits précédemment.  The pigment powder according to the invention can for example be applied or printed on the security thread or strip, for example by one of the methods described above.
La poudre' pigmentaire selon l'invention peut figurer sur le fil ou bande de sécurité sous la forme d'un ou plusieurs motifs, par exemple du type caractère alphanumérique, symbole, logo, dessin, entre autres, ou sous la forme d'un revêtement uniforme. The powder pigment according to the invention may be on the thread or security band in the form of one or more units, for example of the alphanumeric character, symbol, logo, drawing, among others, or as a uniform coating.
Selon un mode de réalisation particulier, le fil ou bande de sécurité comporte une couche supérieure métallisée, par exemple en aluminium, comportant des 'zones métallisées et démétallisées, et une couche inférieure, de telle sorte que les zones non métallisées de la couche supérieure laissent transparaître la couche inférieure. Un tel fil ou bande de sécurité est notamment connu sous le nom de Cleartext®. Dans le cadre de la présente invention, la poudre pigmentaire peut être intégrée au niveau de la couche inférieure. De la sorte, il est possible d'observer un changement d'aspect de la poudre pigmentaire en fonction de l'éclairage au niveau des zones non métallisées de la couche supérieure. L'éclairage et l'observation du fil ou bande de sécurité peut par exemple se faire au-dessus de la couche supérieure métallisée. Dans ce cas, on pourra observer en réflexion un changement d'aspect uniquement au niveau des zones non métallisées de la couche supérieure. L'éclairage peut encore se faire au-dessus de la couche supérieure et l'observation en-dessous de la couche inférieure, ou bien l'éclairage au-dessous de la couche inférieure et l'observation au-dessus de la couche supérieure. Dans ces deux derniers cas, l'observation en transmission du fil ou bande de sécurité peut permettre d'observer un changement d'aspect également uniquement au niveau des zones non métallisées de la couche supérieure. L'éclairage et l'observation du fil ou bande de sécurité peuvent encore se faire en-dessous de la couche inférieure. Dans ce cas, tout le fil ou toute la bande de sécurité pourra présenter un changement d'aspect par observation en réflexion. According to a particular embodiment, the thread or security strip comprises a metallized upper layer, for example aluminum, having metallised and demetallised areas, and a lower layer, such that the non-metallized areas of the top layer allow to show the lower layer. Such a thread or security tape is known in particular as Cleartext ® . In the context of the present invention, the pigment powder can be integrated at the level of the lower layer. In this way, it is possible to observe a change in appearance of the pigment powder as a function of the illumination at the level of the non-metallized zones of the upper layer. Lighting and observation of the security thread or strip can for example be done above the metallized upper layer. In this case, it will be possible to observe in reflection a change of appearance only at the level of the non-metallized zones of the upper layer. Lighting can still be done above the upper layer and observation below the lower layer, or lighting below the lower layer and observation above the upper layer. In the latter two cases, the observation in transmission of the security thread or strip can make it possible to observe an appearance change also only at the level of the non-metallized zones of the upper layer. Lighting and observation of the security thread or strip can still be done below the lower layer. In this case, all the wire or the safety band may have a change of appearance by observation in reflection.
Dans le cas où le fil ou bande de sécurité est introduit en fenêtre(s) dans un document, deux niveaux de révélation de la coloration métamérique peuvent être possibles : par observation en réflexion sous illuminant adapté, la coloration est révélée au niveau des fenêtres de l'article, sur les zones démétallisées du fil ou bande. Par observation en lumière transmise sous illuminant adapté, la coloration apparaît au niveau de toutes les zones démétallisées du fil ou bande, y compris celles incorporées totalement dans l'article, entre les fenêtres.  In the case where the thread or security band is introduced in window (s) in a document, two levels of revelation of the metameric coloration may be possible: by observation in reflection under suitable illuminant, the color is revealed at the windows of the article, on the demetallized zones of the wire or strip. By observation in transmitted light under suitable illuminant, the coloration appears at all the demetallized zones of the wire or strip, including those totally incorporated in the article, between the windows.
Dans le cas où le fil ou bande de sécurité est incorporé totalement dans un article, la coloration métamérique n'est observable qu'en lumière transmise sous illuminant adapté :.. elle apparaît ainsi au niveau des zones démétallisées du fil ou bande. Ce mode est avantageux lorsque l'environnement lumineux ambiant présente des rayons lumineux parasites qui risqueraient de faire . apparaître, en réflexion, la coloration métamérique de façon involontaire.  In the case where the thread or security band is totally incorporated in an article, the metameric coloration is observable only in transmitted light under suitable illuminant: it thus appears at the demetallized zones of the wire or strip. This mode is advantageous when the ambient light environment has parasitic light rays that might do. to appear, in reflection, the metameric coloration in an involuntary way.
Film de sécurité, foil et patch Security film, foil and patch
L'élément de sécurité selon l'invention peut être un film de sécurité (ou laminât), formé notamment à partir d'un film de polyester ou polypropylène ou encore de polyuréthane transférable à chaud ou par contrecollage (adhésivité).  The security element according to the invention may be a security film (or laminate), formed in particular from a polyester or polypropylene film or heat transferable polyurethane or laminating (adhesiveness).
L'élément de sécurité selon l'invention peut encore être un foil, c'est-à-dire un ruban pouvant s'étendre sur une partie de l'article, notamment une feuille ou un document, généralement selon la largeur ou la longueur.  The security element according to the invention may also be a foil, that is to say a ribbon may extend over a portion of the article, in particular a sheet or a document, generally according to the width or the length .
L'élément de sécurité selon l'invention peut encore être un patch. En particulier, l'élément de sécurité peut comporter de préférence un support, et au moins une couche d'une composition comprenant une poudre pigmentaire selon l'invention.  The security element according to the invention can still be a patch. In particular, the security element may preferably comprise a support, and at least one layer of a composition comprising a pigment powder according to the invention.
L'élément de sécurité peut par exemple être une étiquette de sécurité, comportant, un support adhésif ou non.  The security element may for example be a security tag, comprising, an adhesive support or not.
Avantageusement, le support peut être agencé pour être séparé de ladite couche avant application de l'élément de sécurité sur un article, par exemple un document de sécurité et/ou de valeur. Selon cette variante, l'élément de sécurité peut comporter une couche supérieure partiellement opaque, une couche inférieure comprenant mie poudre pigmentaire selon l'invention et un support. La couche supérieure présente au moins une zone transparente. Le support est au contact de la couche inférieure et est agencé pour être séparé de ladite couche inférieure avant application de l'élément de sécurité sur un article, par exemple un document de sécurité et/ou de valeur. En réflexion, la révélation décoloration métamérique est donc observable au niveau de la ou des zones transparentes de la couche supérieure de l'élément de sécurité. L'éclairage et l'observation de l'élément de sécurité peut par exemple se faire au-dessus de la couche supérieure partiellement opaque. Dans ce cas, on pourra observer en réflexion un changement d'aspect uniquement au niveau de la ou des zones transparentes de la couche supérieure. L'éclairage peut encore se faire au-dessus de la couche supérieure et l'observation en-dessous de la couche inférieure, ou bien l'éclairage au-dessous de la couche inférieure et l'observation au- dessus de la couche supérieure. Dans ces deux derniers cas, l'observation en transmission de l'élément de sécurité peut permettre d'observer un changement d'aspect également uniquement au niveau de la ou des zones transparentes de la couche supérieure. Advantageously, the support may be arranged to be separated from said layer before application of the security element to an article, for example a security document and / or value. According to this variant, the security element may comprise a partially opaque upper layer, a lower layer comprising a pigmentary powder according to the invention and a support. The upper layer has at least one transparent zone. The support is in contact with the lower layer and is arranged to be separated from said lower layer before application of the security element on an article, for example a security document and / or value. In reflection, the revelation metameric discoloration is therefore observable at the level or the transparent areas of the upper layer of the security element. The illumination and observation of the security element can for example be done above the partially opaque upper layer. In this case, it will be possible to observe in reflection a change of appearance only at the level of the transparent zone (s) of the upper layer. Lighting can still be done above the upper layer and observation below the lower layer, or illumination below the lower layer and observation above the upper layer. In the latter two cases, the observation in transmission of the security element can make it possible to observe a change in appearance also only at the level of the transparent zone or zones of the upper layer.
L'éclairage et l'observation de l'élément de sécurité peuvent encore se faire en-dessous de la couche inférieure. Dans ce cas, tout l'élément de sécurité pourra présenter un changement d'aspect par observation en réflexion.  Lighting and observation of the security element can still be done below the lower layer. In this case, the entire security element may have a change of appearance by observation in reflection.
La couche supérieure opaque peut notamment être métallisée et sa ou ses zones transparentes peuvent être démétallisées, de préférence de manière à former des motifs.  The opaque upper layer may in particular be metallized and its transparent zone or zones may be demetallized, preferably so as to form patterns.
Selon une variante préférée,, l'élément de sécurité est un fil de sécurité, un foil, un laminât ou un patch et comporte une couche supérieure métallisée présentant des zones démétallisées et une couche inférieure comprenant une poudre pigmentaire selon l'invention.  According to a preferred variant, the security element is a security thread, a foil, a laminate or a patch and comprises a metallized upper layer having demetallized zones and a lower layer comprising a pigment powder according to the invention.
L'élément de sécurité peut encore comporter, en surface de la poudre de lanthanide selon l'invention, une couche intermédiaire, par exemple une couche fibreuse. Dans ce cas précis, une observation en réflexion sous illuminant adapté ne permet pas le virage au rose. En revanche, en lumière transmise, le virage au rose s'opère. Avantageusement, on peut alors utiliser deux sources lumineuses distinctes juxtaposées. Le virage au rose s'effectuera sur la zone correspondant au bon illuminant. Sous l'autre illuminant, le virage au rose sera inexistant. L'avantage de cette double illumination est de créer un contraste encore plus marqué de transition colorée. La détection du changement d'aspect pourra se faire par réflexion, l'éclairage et l'observation s' effectuant d'un même côté de l'élément de sécurité, ou en transmission, l'éclairage et l'observation s' effectuant de part et d'autre de l'élément de sécurité. The security element may also comprise, on the surface of the lanthanide powder according to the invention, an intermediate layer, for example a fibrous layer. In this case, an observation in reflection under suitable illuminant does not allow the turn to pink. On the other hand, in transmitted light, the pink turn takes place. Advantageously, one can then use two separate light sources juxtaposed. The pink turn will take place on the area corresponding to the good illuminant. Under the other illuminant, the pink turn will be nonexistent. The advantage of this double illumination is to create an even more marked contrast of color transition. The detection of the change of appearance can be done by reflection, the lighting and the observation being carried out on the same side of the security element, or in transmission, the lighting and the observation being done of both sides of the security element.
L'élément de sécurité peut encore comporter un substrat comportant un filigrane ou pseudo-filigrane ayant un degré de transparence suffisant pour laisser apparaître un article, sur lequel est appliqué l'élément de sécurité, à travers le filigrane ou pseudo-filigrane, et une poudre pigmentaire selon l'invention se superposant au moins partiellement au filigrane ou pseudo-filigrane, située entre le filigrane ou pseudo-filigrane et l'article. Lors d'une observation en transmission et/ou en réflexion, le changement d'aspect, notamment de couleur, peut permettre de mettre en évidence les variations d'opacité du filigrane ou pseudo-filigrane.  The security element may further comprise a substrate comprising a watermark or pseudo-watermark having a degree of transparency sufficient to reveal an article, on which the security element is applied, through the watermark or pseudo-watermark, and a pigment powder according to the invention is at least partially superimposed on the watermark or pseudo-watermark, located between the watermark or pseudo-watermark and the article. During an observation in transmission and / or reflection, the change in appearance, especially color, can highlight the variations in opacity of the watermark or pseudo-watermark.
Le caractère translucide de l'article peut se caractériser par la mesure du facteur d'opacité de l'article. En particulier, la translucidité est l'aptitude d'un objet à laisser passer la lumière et un objet translucide à une opacité strictement inférieure à 100 %. L'opacité peut se mesurer selon la norme ISO 2471. Elle peut être inférieure ou égale à 80 %, de préférence 60 %, mieux 40 %, mieux encore 30 %.  The translucent nature of the article can be characterized by measuring the opacity factor of the article. In particular, translucency is the ability of an object to let light and a translucent object to an opacity strictly less than 100%. The opacity can be measured according to the ISO 2471 standard. It can be less than or equal to 80%, preferably 60%, better 40%, better still 30%.
Le terme « substrat » désigne une feuille pouvant comporter une ou plusieurs couches fibreuses et/ou polymères.  The term "substrate" refers to a sheet which may comprise one or more fibrous and / or polymeric layers.
Le substrat peut comporter une couche fibreuse, par exemple à base de fibres végétales, par exemple de cellulose, en particulier des fibres de coton, et/ou de fibres synthétiques comme par exemple des fibres de polyamide et/ou de polyester.  The substrate may comprise a fibrous layer, for example based on plant fibers, for example cellulose fibers, in particular cotton fibers, and / or synthetic fibers such as, for example, polyamide and / or polyester fibers.
Le substrat peut encore comporter une couche polymère qui peut par exemple être sous la forme d'un film. Le film peut être un film alvéolaire ou non. A titre d'exemple, la couche polymère peut comporter un film de polychlorure de vinyle (PVC), du polyéthylène téréphtalate (PET), du polycarbonate (PC), du polyester carbonate (PEC), du polyéthylène téréphtalate glycol (PETG), de l'acrylonitrile butadiène styrène (ABS) ou un film collecteur de lumière, par exemple du type « guide d'ondes », par exemple un film luminescent à base de polycarbonate, commercialisé par la société BAYER sous la dénomination LISA®. Le substrat peut comporter un ou plusieurs filigranes ou pseudo-filigranes présentant des caractéristiques identiques ou différentes. The substrate may also comprise a polymer layer which may for example be in the form of a film. The film may be an alveolar film or not. By way of example, the polymer layer may comprise a polyvinyl chloride (PVC) film, polyethylene terephthalate (PET), polycarbonate (PC), polyester carbonate (PEC), polyethylene terephthalate glycol (PETG), acrylonitrile butadiene styrene (ABS) or a light-collecting film, for example of the type "wave guide", for example a luminescent film based on polycarbonate, sold by the company Bayer under the name LISA ®. The substrate may comprise one or more watermarks or pseudo-watermarks having identical or different characteristics.
L'élément de sécurité, notamment sous forme d'étiquette, peut comporter une couche adhésive, notamment sur le verso du substrat, comportant un adhésif assurant le collage de l'élément de sécurité sur l'article. La couche adhésive peut ou non comporter une poudre pigmentaire selon l'invention. La couche adhésive peut être colorée ou opaque. La couche adhésive peut être translucide.  The security element, particularly in the form of a label, may include an adhesive layer, particularly on the back of the substrate, comprising an adhesive ensuring the bonding of the security element on the article. The adhesive layer may or may not comprise a pigment powder according to the invention. The adhesive layer may be colored or opaque. The adhesive layer can be translucent.
L'adhésif peut être un adhésif sensible à la pression (PSA - « Pression Sensitive Adhesive »).  The adhesive may be a Pressure Sensitive Adhesive (PSA).
L'adhésif peut encore être un enduit thermoscellant, par exemple un vernis thermosceilant, un agent réticulable aux UV, un adhésif à irradier, un vernis avec une base solvant, du type polyester par exemple, ou un adhésif en phase aqueuse, entre autres. L'adhésif peut être un acétate de polyvinyle ou du PVA.  The adhesive may also be a heat-sealing coating, for example a heat-resistant varnish, a UV curable agent, an adhesive to be irradiated, a varnish with a solvent base, of the polyester type, for example, or an adhesive in aqueous phase, among others. The adhesive may be polyvinyl acetate or PVA.
L'adhésif peut par exemple être un film de matière thermoplastique, par exemple de polyéthylène, qui peut servir à assembler l'élément de sécurité à l'article.  The adhesive may for example be a film of thermoplastic material, for example polyethylene, which can be used to assemble the security element to the article.
Le substrat peut par exemple être préencollé sur son verso avec une composition adhésive sensible à la pression ou réactivable à chaud, cette composition étant appliquée à froid ou à chaud, sous forme liquide, par extrusion ou par lamination.  The substrate may, for example, be precoated on its back with a pressure-sensitive or heat-reactive adhesive composition, this composition being applied cold or hot, in liquid form, by extrusion or by lamination.
Le substrat peut comporter une première feuille portant le filigrane ou pseudo- filigrane, une seconde feuille et une couche adhésive comportant la poudre pigmentaire liant les deux feuilles. La couche adhésive peut être telle que décrite précédemment. Une autre couche adhésive peut être portée par la deuxième feuille, à l'opposé de la première, pour assurer la fixation à l'article. La seconde feuille peut être colorée, opaque ou translucide, et la couche adhésive entre les deux feuilles peut par exemple être transparente.  The substrate may comprise a first sheet bearing the watermark or pseudo-watermark, a second sheet and an adhesive layer comprising the pigment powder binding the two sheets. The adhesive layer may be as previously described. Another adhesive layer may be carried by the second sheet, opposite the first, to provide attachment to the article. The second sheet may be colored, opaque or translucent, and the adhesive layer between the two sheets may for example be transparent.
L'article peut présenter une opacité ou une couleur, de préférence foncée, lui permettant d'être visible à travers le filigrane ou pseudo-filigrane du substrat.  The article may have opacity or a color, preferably dark, allowing it to be visible through the filigree or pseudo-watermark of the substrate.
L'article peut ainsi présenter toute nuance d'opacité et/ou de couleur permettant de se différencier de l'opacité et/ou de la couleur du substrat, de sorte que l'aspect, couleur ou opacité, de l'objet soit visible à travers le filigrane ou pseudofiligrane. L'article peut par exemple être recouvert au moins partiellement sur sa surface d'un revêtement opaque ou coloré sur lequel on colle l'élément de sécurité. Le revêtement peut encore être translucide. The article can thus have any shade of opacity and / or color that makes it possible to differentiate itself from the opacity and / or the color of the substrate, so that the appearance, color or opacity of the object is visible. through the watermark or pseudofiligrane. The article may for example be covered at least partially on its surface with an opaque or colored coating on which the security element is glued. The coating can still be translucent.
L'article peut encore être transparent ou translucide, au moins partiellement, et contenir un produit opaque.  The article may still be transparent or translucent, at least partially, and contain an opaque product.
Article article
Une poudre et/ou un élément de sécurité comportant une poudre selon l'invention peuvent être utiles pour fonctionnaliser un article, par exemple un billet de banque, un papier de sécurité, un feuillet ou une couverture de passeport, un visa, un coupon, un document de valeur autre qu'un billet de banque, par exemple un chèque ou une carte de crédit, une étiquette de protection et/ou d'authentification, une étiquette de traçabilité, un ticket.  A powder and / or a security element comprising a powder according to the invention may be useful for functionalizing an article, for example a banknote, a security paper, a leaflet or a passport cover, a visa, a coupon, a valuable document other than a bank note, for example a check or a credit card, a protection and / or authentication label, a traceability label, a ticket.
Selon un autre de ses aspects, l'invention a pour objet un article comportant un élément de sécurité tel que décrit précédemment.  According to another of its aspects, the subject of the invention is an article comprising a security element as described above.
L' authentification et/ou P identification d'un article comportant un élément de sécurité selon l'invention peut faire appel à l'observation d'aspects différents en fonction de l'éclairage, ce qui renforce la protection de l'article contre la falsification.  The authentication and / or identification of an article comprising a security element according to the invention may involve the observation of different aspects depending on the lighting, which reinforces the protection of the article against the falsification.
L'article peut comporter une zone à effet optique métamérique comportant un élément de sécurité selon l'invention.  The article may comprise a metameric optical effect zone comprising a security element according to the invention.
L'article peut être un document de sécurité, par exemple une feuille de sécurité.  The article can be a security document, for example a security sheet.
L'article peut être choisi parmi les documents d'identité, en particulier une carte d'identité, un visa, un permis de conduire ou. un passeport, les moyens de paiement, en particulier les billets de banque, les tickets restaurant ou les chèques, les tickets de loterie ou d'entrée à des manifestations culturelles ou sportives, les billets de transports, entre autres.  The article can be chosen from identity documents, in particular an identity card, a visa, a driving license or. a passport, means of payment, especially banknotes, restaurant vouchers or checks, lottery or entrance tickets to cultural or sports events, transport tickets, among others.
L'article peut également être choisi parmi les emballages, notamment pour les médicaments ou pour des aliments ou pour des cosmétiques ou parfums ou pour des pièces électroniques ou des pièces détachées, les étiquettes de sécurité, de protection et/ou d'authentification et les étiquettes de traçabilité, les feuilles utilisées dans le domaine médical ou hospitalier, notamment les papiers utilisés pour faire des emballages de stérilisation, les papiers d'art, les bouteilles, par exemple les bouteilles de vin ou d'alcool, entre autres. The article may also be selected from packaging, in particular for drugs or for food or for cosmetics or perfumes or for electronic parts or spare parts, safety, protection and / or authentication labels and traceability labels, sheets used in the medical or hospital field, in particular the papers used to make packaging sterilization, art papers, bottles, for example bottles of wine or alcohol, among others.
L'élément de sécurité selon l'invention peut être incorporé sur une grande partie de la surface de l'article, voire sur la totalité de la surface de l'article.  The security element according to the invention may be incorporated over a large part of the surface of the article, or even over the entire surface of the article.
L'élément de sécurité peut être disposé sur l'article selon au moins un motif, par exemple un caractère alphanumérique, un dessin, un logo, ou un symbole.  The security element may be disposed on the article in at least one pattern, for example an alphanumeric character, a design, a logo, or a symbol.
L'article peut comporter un élément de sécurité selon l'invention sur au moins l'une de ses faces.  The article may comprise a security element according to the invention on at least one of its faces.
L'élément de sécurité peut être sous la forme d'une impression.  The security element may be in the form of an impression.
L'élément de sécurité peut encore être incorporé dans ime couche de revêtement déposée en surface d'une face de l'article ou d'une face d'un élément matériel annexe fixé en surface d'une face de l'article, par exemple un patch, un foil, un fil ou une bande de sécurité, des planchettes, un film de sécurité ou une pochette de sécurité.  The security element may also be incorporated in a coating layer deposited on the surface of a face of the article or a face of an auxiliary material element attached to the surface of a face of the article, for example a patch, a foil, a wire or a safety band, boards, a security film or a safety bag.
L'élément de sécurité peut encore être incorporé en masse dans l'article, par exemple lorsqu'il s'agit d'une fibre ou d'une particule.  The security element can still be incorporated en masse in the article, for example when it is a fiber or a particle.
L'article peut être opaque ou translucide, coloré ou non.  The article may be opaque or translucent, colored or not.
Procédé de sécurisation Securing process
Selon encore un autre de ses aspects, l'invention a pour objet un procédé de sécurisation d'un article comportant les étapes suivantes :  According to yet another of its aspects, the subject of the invention is a method of securing an article comprising the following steps:
a) disposer d'une poudre ou d'un élément de sécurité conforme à l'invention, et  a) have a powder or a security element according to the invention, and
b) incorporer ou transférer, au moins partiellement, ladite poudre et/ou ledit élément de sécurité dans ou sur l'article.  b) at least partially incorporating or transferring said powder and / or said security element into or onto the article.
Il est entendu que l'homme de l'art choisit, selon la nature de l'élément de sécurité ou de l'article, la méthode la plus appropriée pour effectuer l'étape b).  It is understood that one skilled in the art chooses, depending on the nature of the security element or article, the most appropriate method for performing step b).
L'étape b) peut ainsi consister à noyer, au moins partiellement, notamment entièrement,, ladite poudre et/ou ledit élément de sécurité dans l'article.  Step b) can thus consist in drowning, at least partially, in particular completely, said powder and / or said security element in the article.
Plus particulièrement, lorsque l'élément de sécurité est une composition de revêtement, l'étape b) peut encore consister à appliquer une couche, notamment en surface, de ladite poudre et/ou dudit élément de sécurité dans ou sur l'article.  More particularly, when the security element is a coating composition, step b) may still consist in applying a layer, especially at the surface, of said powder and / or said security element in or on the article.
De préférence, l'article est une feuille de sécurité, notamment cellulosique. Ladite poudre peut être apposée en surface de l'article sous la forme d'une encre, via une technique d'impression choisie parmi l'impression offset, la sérigraphie, la flexographie, l'héliogravure et/ou la typographie. Preferably, the article is a security sheet, in particular cellulose. Said powder may be affixed to the surface of the article in the form of an ink, via a printing technique chosen from offset printing, screen printing, flexography, gravure printing and / or typography.
Lorsque l'article est une feuille de sécurité, notamment cellulosique, ladite poudre peut être déposée en surface de ladite feuille via une composition de couchage ou de surfaçage l'incorporant.  When the article is a security sheet, in particular cellulose, said powder may be deposited on the surface of said sheet via a coating or surfacing composition incorporating it.
Elle peut être mise également en œuvre sous la forme d'un fil ou d'une bande de sécurité, d'une fibre de sécurité, d'une planchette et/ou d'une particule l'incorporant.  It can also be implemented in the form of a wire or a security band, a security fiber, a board and / or a particle incorporating it.
Ladite poudre et/ou l'élément de sécurité peut être incorporé(e) totalement ou partiellement dans l'article, et notamment en fenêtre(s).  Said powder and / or the security element may be incorporated (e) totally or partially in the article, and in particular in window (s).
Procédé d'authentifîcation Authentication process
Selon encore un autre de ses aspects, l'invention a pour objet un procédé d'authentification d'un article conforme à l'invention comportant les étapes consistant à :  According to yet another of its aspects, the subject of the invention is a method of authenticating an article according to the invention comprising the steps of:
a) observer l'élément de sécurité sous un éclairage à spectre continu du type lumière du jour ou incandescent et sous un éclairage à raies d'émission du type fluorescent,  (a) observe the security element under daylight or incandescent type continuous-spectrum lighting and under fluorescent-type emission line illumination,
b) conclure quant à l'authenticité de l'article au moins en fonction du métamérisme observé.  b) conclude as to the authenticity of the article at least according to the observed metamerism.
Deux paities distinctes de l'élément de sécurité peuvent être éclairées simultanément avec les deux éclairages de façon à permettre l'observation d'un contraste lié au métamérisme.  Two separate halves of the security element can be illuminated simultaneously with the two lights so as to allow the observation of a contrast related to metamerism.
Pour authentifier et/ou identifier un article sécurisé selon l'invention, on utilise de préférence un détecteur apte à procurer une illumination capable de révéler un comportement métamérique au niveau dudit article.  To authenticate and / or identify a secure article according to the invention, a detector capable of providing an illumination capable of revealing a metameric behavior at the level of said article is preferably used.
L'observation du comportement métamérique peut se faire, selon le type d'article sécurisé, en lumière transmise ou en réflexion. Il suffit d'exposer l'article au détecteur puis d'apprécier si un contraste de couleur intervient, la manifestation de ce contraste cautionnant l'authenticité et/ou l'identité de l'article.  The observation of the metameric behavior can be done, according to the type of secure article, in transmitted light or in reflection. It is enough to expose the article to the detector then to appreciate if a color contrast intervenes, the manifestation of this contrast guaranteeing the authenticity and / or the identity of the article.
Le détecteur procure de préférence une lumière fluorescente. Le détecteur peut notamment être un tube fluorescent ou une lampe fluo-compacte, notamment de type « blanc de luxe », présentant une température de couleur de 4000 K. Le modèle OSRAM Duluxe mini s'avère particulièrement adapté. En particulier, l'homme du métier pourra adapter le spectre d'émission du détecteur à la poudre pigmentaire sécurisant ledit article. The detector preferably provides a fluorescent light. The detector may especially be a fluorescent tube or a compact fluorescent lamp, especially of "luxury white" type, having a color temperature of 4000 K. The OSRAM Duluxe mini model is particularly suitable. In particular, the skilled person can adapt the emission spectrum of the detector to the pigment powder securing said article.
Le détecteur peut comporter au moins deux illuminants : un premier illuminant inactif sur la poudre pigmentaire et un deuxième illuminant permettant de révéler le comportement métamérique de la poudre pigmentaire. En outre, le détecteur peut comporter un illuminant supplémentaire, par exemple destiné à révéler d'autre(s) élément(s) de sécurité, notamment des fibres fluorescentes.  The detector may comprise at least two illuminants: a first inactive illuminant on the pigment powder and a second illuminant to reveal the metameric behavior of the pigment powder. In addition, the detector may comprise an additional illuminant, for example intended to reveal other element (s) security, including fluorescent fibers.
Selon un mode de réalisation particulier, le détecteur peut comporter une section éclairante plane munie d'une première et d'une deuxième sources de lumière blanche adjacentes, seule ladite première source de lumière blanche étant apte à révéler la couleur métamérique de la poudre selon l'invention présente dans l'article.  According to a particular embodiment, the detector may comprise a plane illuminating section provided with a first and second adjacent white light sources, only said first white light source being able to reveal the metameric color of the powder according to the invention. present invention in the article.
Un tel détecteur est particulièrement avantageux pour l'observation en transmission d'un article de sécurité, notamment lorsqu'il intègre à titre d'élément de sécurité un fil de sécurité selon l'invention et plus particulièrement lorsqu'un tel fil comporte une couche métallisée présentant des zones démétallisées qui se superposent à une couche intégrant une poudre pigmentaire selon l'invention.  Such a detector is particularly advantageous for observation in transmission of a security article, especially when it incorporates as a security element a security thread according to the invention and more particularly when such a wire comprises a layer. metallized having demetallized zones which are superimposed on a layer incorporating a pigment powder according to the invention.
Lorsque le fil est appliqué sur la section éclairante plane de ladite deuxième source (inapte à révéler la coloration métamérique), on voit en transmission les zones démétallisées du fil, notamment un éventuel motif formé par ces dernières. Lorsque le fil est appliqué sur la section éclairante plane de ladite première source (apte à révéler la coloration métamérique), on voit en outre la couleur métamérique dans lesdites zones démétallisées. Ce double illuminant permet de pallier aux essais basiques de contrefaçons qui pourraient consister à simuler un fil Cleartext® réactif par l'application d'une simple coloration rose. L'authentification peut également être réalisée en réflexion. When the wire is applied to the plane illuminating section of said second source (unable to reveal the metameric coloration), the demetallized zones of the wire are seen in transmission, in particular a possible pattern formed by the latter. When the wire is applied to the flat illuminating section of said first source (capable of revealing the metameric coloration), the metameric color is also seen in said demetallized zones. This dual illuminating alleviates the basic tests of counterfeits that could be to simulate a wire Cleartext ® reagent by applying a simple pink coloring. Authentication can also be done in reflection.
Eléments) de sécurité supplementairc(s) Additional security features
L'article et/ou l'élément de sécurité selon l'invention peut comporter un ou plusieurs éléments de sécurité supplémentaires.  The article and / or the security element according to the invention may comprise one or more additional security elements.
L'article et/ou l'élément de sécurité selon l'invention peut par exemple comporter un autre composé réactif, notamment un agent de marquage, notamment un agent luminescent, par exemple un pigment fluorescent, un pigment phosphorescent, un pigment à effet interférentiel." Parmi les éléments de sécurité, certains sont détectables à l'œil nu, en lumière visible, sans utilisation d'un appareil particulier. Ces éléments de sécurité comportent par exemple un filigrane, des fibres ou planchettes colorées, des fils imprimés, métallisés ou holographiques, des foils holographiques ou des impressions à effet optique variable. The article and / or the security element according to the invention may for example comprise another reactive compound, in particular a marking agent, in particular a luminescent agent, for example a fluorescent pigment, a phosphorescent pigment or an interference effect pigment. . " Some of the security features are detectable to the naked eye, in visible light, without the use of a particular device. These security features include, for example, a watermark, colored fibers or boards, printed, metallized or holographic wires, holographic foils, or optically variable impressions.
Ces éléments de sécurité sont dits de premier niveau.  These security elements are called first level.
D'autres types d'éléments de sécurité sont détectables seulement à l'aide d'un appareil relativement simple tel qu'une lampe émettant dans l'ultraviolet ou l'infrarouge. Ces éléments de sécurité comportent par exemple des fibres, des planchettes, des bandes, des fils ou des particules. Ces éléments de sécurité peuvent être visibles à l'œil nu ou non, étant par exemple luminescents sous un éclairage ultraviolet (UV) ou infrarouge (IR). Ces éléments de sécurité sont dits de deuxième niveau.  Other types of security elements are detectable only with a relatively simple device such as a lamp emitting in the ultraviolet or infrared. These security elements comprise, for example, fibers, boards, strips, wires or particles. These security elements may be visible to the naked eye or not, being for example luminescent under ultraviolet (UV) or infrared (IR). These security elements are said to be second level.
D'autres types d'éléments de sécurité encore nécessitent pour leur détection un appareil de détection plus sophistiqué. Ces éléments de sécurité sont par exemple capables de générer un signal spécifique lorsqu'ils sont soumis, de manière simultanée ou non, à une ou plusieurs sources d'excitation extérieures. La détection automatique du signal permet d'authentifier, le cas échéant, le document.  Other types of security elements still require for their detection a more sophisticated detection device. These security elements are for example capable of generating a specific signal when they are subjected, simultaneously or not, to one or more external excitation sources. The automatic detection of the signal makes it possible to authenticate, if necessary, the document.
Ces éléments de sécurité comportent par exemple des traceurs se présentant sous la forme de matière active, de particules ou de fibres, capables de générer un signal spécifique lorsque ces traceurs sont soumis à une excitation optronique, électrique, magnétique ou électromagnétique.  These security elements comprise for example tracers in the form of active material, particles or fibers, capable of generating a specific signal when these tracers are subjected to optronic, electrical, magnetic or electromagnetic excitation.
Ces éléments de sécurité sont dits de troisième niveau.  These security elements are said to be third level.
Le ou les éléments de -sécurité supplémentaires incorporés à l'article et/ou à l'élément de sécurité selon l'invention peuvent être de premier, de deuxième et/ou de troisième niveau.  The additional security element (s) incorporated in the article and / or the security element according to the invention may be first, second and / or third level.
Les exemples qui suivent, donnés à titre illustratif et sans caractère limitatif, exposent la préparation de poudres pigmentaires selon l'invention.  The examples which follow, given by way of non-limiting illustration, disclose the preparation of pigment powders according to the invention.
Exemples Examples
Poudres pigmentaires à base d'holmium  Holmium-based pigment powders
Exemple 1  Example 1
Dans un ballon de 500 mL surmonté d'un réfrigérant sont introduits 250 mL de diéthylène glycol et 35 g de Ho(N03)3, 6H20 (99,9 %). La solution est chauffée par bain d'huile dans les conditions suivantes : 500 ml of diethylene glycol and 35 g of Ho (NO 3 ) 3 , 6H 2 O (99.9%) are introduced into a 500 ml flask surmounted by a condenser. The solution is heated by oil bath under the following conditions:
- palier à 60 °C durant 45 minutes, puis  - Bearing at 60 ° C for 45 minutes, then
- l h de chauffage progressif jusqu'à 140 °C,  - 1 h of progressive heating up to 140 ° C,
- palier à 140 °C durant 60 minutes avec addition de 2 mL de soude 3N, - Bearing at 140 ° C for 60 minutes with addition of 2 mL of 3N sodium hydroxide,
- 30 minutes de chauffage progressif jusqu'à 180 °C, - 30 minutes of progressive heating up to 180 ° C,
— palier à 180°C durant 120 minutes.  - Bearing at 180 ° C for 120 minutes.
La solution obtenue est refroidie à température ambiante. Elle est ensuite diluée par ajout d'éthanol sous agitation et filtrée avec un filtre présentant une taille de tamis de 200 nm. La poudre obtenue est redispersée dans 100 mL d'éthanol sous agitation puis filtrée. Cette dernière opération est répétée 2 fois et la poudre finale est séchée à l'étuve pendant 1h.  The resulting solution is cooled to room temperature. It is then diluted by addition of ethanol with stirring and filtered with a filter having a sieve size of 200 nm. The powder obtained is redispersed in 100 ml of ethanol with stirring and then filtered. This last operation is repeated twice and the final powder is dried in an oven for 1 hour.
La poudre obtenue peut alors être directement utilisée en tant que poudre pigmentaire. Elle est composée principalement d'un mélange d'hydroxyde, d'oxyde et d'oxobydroxyde d'holmium,  The powder obtained can then be used directly as a pigment powder. It is composed mainly of a mixture of hydroxide, oxide and holmium oxobydroxide,
La poudre est constituée de nanoparticules de taille moyenne égale à 70 nm ± The powder consists of nanoparticles of average size equal to 70 nm ±
20 nm. 20 nm.
Elle présente une densité de 7,2 ± 0,4, et est formée à 83 % ± 5 % massique d'élément holmium.  It has a density of 7.2 ± 0.4, and is formed at 83% ± 5% by mass of holmium element.
Elle présente une transition colorimétrique de blanc cassé à la lumière du soleil à rose sous éclairage fluorescent de type blanc de luxe, à une température de couleur Tc=4000 K.  It presents a color transition from off-white to sunlight to pink under fluorescent white luxury lighting, at a color temperature Tc = 4000 K.
On prépare une poudre pigmentaire selon le même protocole que l'exemple 1. Puis, à la sortie de l'étuve, 3a poudre obtenue subit les traitements thermiques suivants : A pigment powder is prepared according to the same protocol as in Example 1. Then, at the exit of the oven, 3a powder obtained undergoes the following heat treatments:
- 300 °C pendant 12 h,  - 300 ° C for 12 hours,
- 500 °C pendant 1 h,  - 500 ° C for 1 hour,
- 700 °C pendant 1 h,  700 ° C for 1 hour,
900 °C pendant 2 h. Après refroidissement, la poudre subit un léger broyage mécanique puis peut être utilisée en tant que poudre pigmentaire. Elle est composée principalement d'oxyde d'holmium. 900 ° C for 2 hours. After cooling, the powder undergoes a slight mechanical grinding and can be used as a pigment powder. It is composed mainly of holmium oxide.
Elle présente une transition colorimétrique de blanc cassé à la lumière du soleil à rose sous éclairage fluorescent de type blanc de luxe, à une température de couleur Tc=4000 K.  It presents a color transition from off-white to sunlight to pink under fluorescent white luxury lighting, at a color temperature Tc = 4000 K.
La poudre est constituée de nanoparticules de taille moyenne égale à 50 nm ± The powder consists of nanoparticles of average size equal to 50 nm ±
30 nm. 30 nm.
Elle présente une densité de 8,3 ± 0,2, et est formée à 85 % ± 3 % massique d'élément holmium.  It has a density of 8.3 ± 0.2, and is formed at 85% ± 3% by mass of holmium element.
Poudres pigmentaires à base de néodyme Powdered powders based on neodymium
Exemple 3 Example 3
Dans un ballon de 500 mL surmonté d'un réfrigérant sont introduits 250 mL de diéthylène glycol, 35 g de Nd(N03)3, 6H20 (99,9 %) et 3,5g de Y(N03)3, 6H20 (99,9 %). 500 ml of diethylene glycol, 35 g of Nd (NO 3 ) 3, 6H 2 O (99.9%) and 3.5 g of Y (NO 3 ) 3 are introduced into a 500 ml flask surmounted by a condenser, 6H 2 O (99.9%).
La solution est chauffée par bain d'huile dans les conditions suivantes :  The solution is heated by oil bath under the following conditions:
- palier à 60 °C durant 45 minutes, puis  - Bearing at 60 ° C for 45 minutes, then
- 1 h de chauffage progressif jusqu'à 140 °C,  - 1 h of progressive heating up to 140 ° C,
- palier à 140 °C durant 60 minutes avec addition de 2 mL de soude 3N, puis - Bearing at 140 ° C for 60 minutes with addition of 2 mL of 3N sodium hydroxide, then
- 30 minutes de chauffage progressif jusqu'à 180 °C, - 30 minutes of progressive heating up to 180 ° C,
- palier à 180 °C durant 120 minutes.  - Bearing at 180 ° C for 120 minutes.
La solution obtenue est refroidie à température ambiante. Elle est ensuite diluée par ajout d'éthanol sous agitation et filtrée avec un filtre présentant une taille de tamis de 200 nm. La poudre obtenue est redispersée dans 100 mL d'éthanol sous agitation puis filtrée. Cette dernière opération est répétée 2 fois et la poudre fmale est séchée à i'étuve pendant lh.  The resulting solution is cooled to room temperature. It is then diluted by addition of ethanol with stirring and filtered with a filter having a sieve size of 200 nm. The powder obtained is redispersed in 100 ml of ethanol with stirring and then filtered. This last operation is repeated twice and the final powder is dried in the oven for 1 h.
La poudre obtenue peut alors être directement utilisée en tant que poudre pigmentaire. Elle est composée principalement d'un mélange d'hydroxyde, d'oxyde et d'oxohydroxyde de néodyme et d'yttrium. Elle présente une transition colorimétrique de violet à la lumière du soleil à blanc sous éclairage fluorescent de type blanc de luxe, à une température de couleur Tc=4000 K. The powder obtained can then be used directly as a pigment powder. It is composed mainly of a mixture of hydroxide, oxide and oxohydroxide of neodymium and yttrium. It has a color transition from violet to sunlight to white under fluorescent white luxury lighting, at a color temperature Tc = 4000 K.
La poudre est constituée de nanoparticules de taille moyenne égale à 60 nm ± 15 nm.  The powder consists of nanoparticles of average size equal to 60 nm ± 15 nm.
Elle présente une densité de 6,7 ± 0,4, et est formée à 72 % ± 5 % massique d'élément néodyme.  It has a density of 6.7 ± 0.4, and is formed at 72% ± 5% by mass of neodymium element.
Exemple 4 Example 4
On prépare une poudre pigmentaire selon le même protocole que l'exemple 3. A pigment powder is prepared according to the same protocol as Example 3.
Puis, à la sortie de l'étuve, la poudre obtenue subit les traitements thermiques suivants : Then, at the exit of the oven, the powder obtained undergoes the following heat treatments:
- 300 °C pendant 12h,  - 300 ° C for 12 hours,
- 500 °C pendant 1 h,  - 500 ° C for 1 hour,
- 700 °C pendant 1 h,  700 ° C for 1 hour,
- 900 °C pendant 2h.  - 900 ° C for 2 hours.
Après refroidissement, la poudre subit un léger broyage mécanique puis peut être utilisée en tant que poudre pigmentaire. Elle est composée principalement d'oxyde mixte de néodyme et d'yttrium.  After cooling, the powder undergoes a slight mechanical grinding and can be used as a pigment powder. It is composed mainly of mixed oxide of neodymium and yttrium.
Elle présente une transition colorimétrique de bleu-violet à la lumière du soleil à vert océan sous éclairage fluorescent de type blanc de luxe, à une température de couleur Tc=4000 K.  It presents a color transition from blue-violet to ocean-green sunlight under luxury white fluorescent lighting at a color temperature Tc = 4000 K.
La poudre est constituée de. nanoparticules de taille moyenne égale à 50 nm ± The powder consists of. nanoparticles of average size equal to 50 nm ±
30 nm. 30 nm.
Elle présente une densité de 7,î ± 0,2, et est formée à 77 % ± 3 % massique d'élément néodyme.  It has a density of 7 ± 0.2, and is formed at 77% ± 3% by mass of neodymium element.
Mélange de poudres pigmentaires Mixture of pigment powders
Exemple 5  Example 5
On mélange la poudre pigmentaire à base d'holmium de l'exemple 1 avec la poudre pigmentaire à base de néodyme de l'exemple 3. La poudre obtenue peut alors être directement utilisée en tant que poudre pigmentaire. Elle présente une transition colorimétrique de violet à la lumière du soleil à rose sous éclairage fluorescent de type blanc de luxe, à une température de couleur Tc=4000 K. The holmium pigment powder of Example 1 is mixed with the neodymium pigment powder of Example 3. The powder obtained can then be used directly as a pigment powder. It presents a color transition from violet to sunlight to pink under fluorescent white luxury lighting, at a color temperature Tc = 4000 K.
Description des figures Description of figures
L'invention pourra être mieux comprise à la lecture qui va suivre d'exemples non limitatifs de mise en œuvre de celle-ci et à l'examen des figures schématiques et partielles du dessin annexé, sur lequel :  The invention will be better understood on reading the following non-limiting examples of implementation thereof and examining the schematic and partial figures of the accompanying drawing, in which:
- les figures 1A à 3B représentent, en vue de face, des exemples d'observation d'articles comportant un élément de sécurité comportant une poudre pigmentaire selon l'invention,  FIGS. 1A to 3B show, in front view, examples of observation of articles comprising a security element comprising a pigment powder according to the invention,
la figure 4 A représente, en vue de face, un autre exemple d'un article selon 3 'invention,  FIG. 4A represents, in front view, another example of an article according to the invention,
- la figure 4B représente, en coupe, l'élément de sécurité de l'article de la figure 4A,  FIG. 4B represents, in section, the security element of the article of FIG. 4A,
la figure 5 A représente, en vue de face, une variante de réalisation de l'article de la figure 4 A,  FIG. 5A represents, in front view, an alternative embodiment of the article of FIG. 4A,
la figure 5B représente, en coupe, l'élément de sécurité de l'article de la figure 5A,  FIG. 5B represents, in section, the security element of the article of FIG. 5A,
les figures 6A et 6B représentent, respectivement en vue de face et en coupe, un autre exemple d'élément de sécurité comportant une poudre pigmentaire selon l'invention,  FIGS. 6A and 6B show, respectively in front view and in section, another example of a security element comprising a pigment powder according to the invention,
les figures 7 et 8 représentent, en coupe, d'autres exemples d'éléments de sécurité selon l'invention,  FIGS. 7 and 8 show, in section, other examples of security elements according to the invention,
la figure 9 représente, en vue de face, l'observation des éléments de sécurité des figures 7 et 8, et  FIG. 9 represents, in a front view, the observation of the security elements of FIGS. 7 and 8, and
les figures 10 et 11 représentent l'observation d'un exemple d'article comportant un élément de sécurité selon la figure 7 ou 8, sous deux conditions d'éclairage différentes. On a représenté sur les figures 1A et 1B un exemple d'article 1, par exemple un document de sécurité, comportant un élément de sécurité 2 comportant une poudre pigmentaire selon l'invention. Figures 10 and 11 show the observation of an example of an article comprising a security element according to Figure 7 or 8, under two different lighting conditions. FIGS. 1A and 1B show an example of an article 1, for example a security document, comprising a security element 2 comprising a pigment powder according to the invention.
L'élément de sécurité 2 est par exemple formé par impression sur l'article 1 d'une encre constituée à titre de pigments d'une poudre pigmentaire selon l'invention, sous la forme d'un motif représentant par exemple les lettres "AW".  The security element 2 is for example formed by printing on the article 1 of an ink constituted as pigments of a pigment powder according to the invention, in the form of a pattern representing for example the letters "AW ".
La figure 1A représente l'observation de l'article 1 sous un éclairage incandescent ou lumière du jour. Dans ce cas, l'élément de sécurité 2 peut apparaître sensiblement incolore et ne pas être détectable, ce qui est signifié par les lignes en pointillé.  Figure 1A shows the observation of item 1 under incandescent lighting or daylight. In this case, the security element 2 may appear substantially colorless and not be detectable, which is signified by the dashed lines.
La figure 1B représente l'observation de l'article 1 sous un éclairage fluorescent. Dans ce cas, l'élément de sécurité 2 apparaît plus coloré, ce qui peut permettre d'authentifier ef'ou d'identifier l'article 1.  Figure 1B shows the observation of item 1 under fluorescent lighting. In this case, the security element 2 appears more colored, which can make it possible to authenticate ef'or to identify the article 1.
On a représenté sur les figures 2A et 2B un autre exemple d'article 1 selon l'invention.  FIGS. 2A and 2B show another example of article 1 according to the invention.
L'article 1 comporte un élément de sécurité 2 réalisé par exemple par impression d'une encre constituée à titre de pigments d'une poudre pigmentaire selon l'invention.  The article 1 comprises a security element 2 made for example by printing an ink constituted as pigments of a pigment powder according to the invention.
La figure 2A représente l'observation de l'article 1 sous éclairage incandescent ou lumière du jour. L'élément de sécurité 2 peut former un motif coloré présentant la même couleur que l'article 1 de sorte que la présence de l'élément de sécurité 2 est rendue indétectable sous un tel éclairage, ce qui est signifié par les lignes en pointillé.  Fig. 2A shows the observation of article 1 under incandescent lighting or daylight. The security element 2 can form a colored pattern having the same color as the article 1 so that the presence of the security element 2 is made undetectable under such lighting, which is signified by the dashed lines.
La figure 2B réprésente l'observation de l'article 1 sous éclairage fluorescent. L'élément de sécurité 2 peut alors former un motif vi sible, notamment blanc ou incolore, qui contraste avec la couleur du reste de l'article 1 , permettant d'authentifier et/ou d'identifier l'article 1.  FIG. 2B represents the observation of article 1 under fluorescent lighting. The security element 2 can then form a visible pattern, in particular white or colorless, which contrasts with the color of the rest of the article 1, making it possible to authenticate and / or identify the article 1.
On a représenté sur les figures 3A et 3B un autre exemple d'article 1 selon l'invention.  FIGS. 3A and 3B show another example of article 1 according to the invention.
Sur la figure 3 A, l'article 1 comporte un élément de sécurité 2 comportant une encre constituée à titre de pigments d'une poudre pigmentaire selon l'invention formant un motif apparaissant d'une première couleur sous éclairage incandescent ou lumière du jour. Sur la figure 3B, l'élément de sécurité 2 forme un motif apparaissant d'une deuxième couleur, différente de la première couleur, sous un éclairage fluorescent. In FIG. 3A, article 1 comprises a security element 2 comprising an ink constituted as pigments of a pigment powder according to the invention forming a pattern appearing from a first color under incandescent lighting or daylight. In FIG. 3B, the security element 2 forms a pattern appearing from a second color, different from the first color, under fluorescent lighting.
Le changement de couleur du motif formé par l'élément de sécurité 2 en fonction des conditions d'éclairage peut ainsi permettre d'authentifier et/ou d'identifier l'article 1 .  The color change of the pattern formed by the security element 2 according to the lighting conditions can thus make it possible to authenticate and / or identify the article 1.
On a représenté sur la figure 4A un autre exemple d'article 1. selon l'invention comportant un élément de sécurité 2 selon l'invention introduit en fenêtre. ·  FIG. 4A shows another example of article 1 according to the invention comprising a security element 2 according to the invention introduced in a window. ·
L'élément de sécurité 2 comporte, comme illustré à la figure 4B, une couche supérieure 3 comportant des métallisations, par exemple en aluminium, formant par exemple des caractères alphanumériques. En variante, la couche supérieure 3 pourrait être métallisée et comporter des démétallisations, comme représenté sur les figures 5 A -et 5B. De telles réalisations sont notamment connues sous le nom de Cleartext® positif ou négatif L'élément de sécurité 2 comporte encore une couche inférieure 4' comportant une poudre pigmentaire selon l'invention. The security element 2 comprises, as illustrated in FIG. 4B, an upper layer 3 comprising metallizations, for example made of aluminum, forming, for example, alphanumeric characters. Alternatively, the upper layer 3 could be metallized and include demetallizations, as shown in FIGS. 5A and 5B. Such embodiments are particularly known of positive or negative Cleartext ® The security element 2 further comprises a bottom layer 4 'containing a pigment powder according to the invention.
L'élément de sécurité 2 est introduit dans l'article 1 , par exemple en fenêtre(s), comme représenté sur la figure 4A, de telle sorte que les métallisations de la couche supérieure 3 de l'élément de sécurité 2 soient visibles au niveau des fenêtres F.  The security element 2 is introduced into the article 1, for example into a window (s), as represented in FIG. 4A, so that the metallizations of the upper layer 3 of the security element 2 are visible at window level F.
Dans les deux exemples de réalisation des figures 4A, 4B et 5A, 5B, l'élément de sécurité 2 sous forme de fil ou de bande s'étend d'un bord à l'autre de l'article 1 mais il pourrait en être autrement.  In the two exemplary embodiments of FIGS. 4A, 4B and 5A, 5B, the security element 2 in the form of a wire or a strip extends from one edge to the other of article 1, but it could be other.
De plus, dans chaque mode de réalisation des figures 4A, 4B ou 5A, 5B, deux niveaux de révélation de la coloration métamérique sont possibles. Par observation en réflexion sous illuminant adapté de l'article 1, la coloration est révélée au niveau des fenêtres F de l'article 1 , sur les zones démétallisées de l'élément de sécurité 2, c'est-à-dire au niveau de la couche inférieure 4. Par observation en lumière transmise sous illuminant adapté, la coloration apparaît au niveau de toutes les zones démétallisées de l'élément de sécurité 2, y compris celles incorporées totalement dans l'article, entre les fenêtres F.  Moreover, in each embodiment of FIGS. 4A, 4B or 5A, 5B, two levels of revelation of the metameric coloration are possible. By observation in reflection under illuminant adapted to Article 1, the coloring is revealed at the windows F of Article 1, the demetallized zones of the security element 2, that is to say at the level of the lower layer 4. By observation in transmitted light under suitable illuminant, the coloration appears in all the demetallized zones of the security element 2, including those incorporated completely in the article, between the windows F.
Dans une variante de réalisation non représentée dans laquelle l'élément de sécurité 2 est incorporé totalement dans l'article 1, la coloration métamérique n'est observable qu'en lumière transmise sous illuminant adapté, apparaissant au niveau des zones démétallisées de l'élément de sécurité 2. On a représenté sur les figures 6A et 633 un autre exemple d'élément de sécurité 2 comportant une poudre pigmentaire selon l'invention. In a non-represented embodiment in which the security element 2 is fully incorporated in the article 1, the metameric coloration is observable only in transmitted light under suitable illuminant, appearing at the demetallized zones of the element security 2. FIGS. 6A and 633 show another example of security element 2 comprising a pigment powder according to the invention.
L'élément de sécurité 2 comporte une couche supérieure 3 métallisée, par exemple en aluminium et comportant des démétallisations, une couche inférieure 4 comportant une poudre pigmentaire selon l'invention et un support 5. comme on peut le voir sur la figure 6B.  The security element 2 comprises an upper layer 3 metallized, for example aluminum and comprising demetallizations, a lower layer 4 comprising a pigment powder according to the invention and a support 5. as can be seen in Figure 6B.
La figure 6A représente, en vue de face, l'élément de sécurité 2 de la figure 6B. FIG. 6A represents, in front view, the security element 2 of FIG. 6B.
Le support 5 peut être adhésif ou non, étant le cas échéant détaché de l'élément de sécurité 2 avant application de celui-ci sur un article. The support 5 may be adhesive or not, being optionally detached from the security element 2 before application thereof on an article.
On a représenté sur la figure 7, en coupe, un autre exemple d'élément de sécurité 2 comportant une poudre pigmentaire selon l'invention.  FIG. 7 is a sectional view of another example of a security element 2 comprising a pigment powder according to the invention.
L'élément de . sécurité 2 se présente par exemple sous la forme d'une étiquette comportant un substrat 6, un filigrane ou pseudo-filigrane 7, et une couche adhésive 8 placée sur le verso du substrat 6, la couche adhésive 8 comportant une poudre pigmentaire selon l'invention.  The element of. security 2 is for example in the form of a label comprising a substrate 6, a watermark or pseudo-watermark 7, and an adhesive layer 8 placed on the back of the substrate 6, the adhesive layer 8 comprising a pigment powder according to the invention.
La couche adhésive 8 peut par exemple comporter un adhésif sensible à la pression (PSA).  The adhesive layer 8 may for example comprise a pressure-sensitive adhesive (PSA).
L'élément de sécurité 2 sous forme d'étiquette peut ainsi être collé sur un article 1 par l'intermédiaire de la couche adhésive 8 comportant la poudre pigmentaire.  The security element 2 in the form of a label can thus be glued to an article 1 via the adhesive layer 8 comprising the pigment powder.
On a représenté sur la figure 8 une variante de réalisation de l'élément de sécurité 2 sous forme d'étiquette.  FIG. 8 shows an alternative embodiment of the security element 2 in the form of a label.
L'élément de sécurité 2 comporte un substrat 6 sur le verso duquel figure une couche adhésive 8, pouvant par exemple comporter un adhésif du type PSA.  The security element 2 comprises a substrate 6 on the back of which there is an adhesive layer 8, which may for example comprise a PSA type adhesive.
Le substrat. 6 comporte une première feuille 6a comportant un filigrane ou pseudo-filigrane 7, une seconde feuille 6b et une couche adhésive 9 comportant une poudre pigmentaire selon l'invention et liant les deux feuilles 6a et 6b entre-elles.  The substrate 6 comprises a first sheet 6a comprising a watermark or pseudo-watermark 7, a second sheet 6b and an adhesive layer 9 comprising a pigment powder according to the invention and binding the two sheets 6a and 6b together.
L'élément de sécurité 2 peut ainsi être collé sur un article par l'intermédiaire dé la couche adhésive.  The security element 2 can thus be glued to an article via the adhesive layer.
La figure 9 représente, en vue de dessus, un élément de sécurité 2 selon la figure 7 ou 8.  FIG. 9 represents, in a view from above, a security element 2 according to FIG. 7 or 8.
Sur cette figure, on peut voir que le filigrane ou pseudo-filigrane 7 forme par exemple les lettres "AW" répétées plusieurs fois. De préférence, le filigrane 7 correspond à un filigrane tramé ou un filigrane clair, ayant un degré de transparence suffisant pour permettre l'observation de l'article à travers celui-ci. En particulier, le filigrane 7 peut avoir une profondeur maximale allant de 50 à 90 % du vélin. In this figure, it can be seen that the watermark or pseudo-watermark 7 forms for example the letters "AW" repeated several times. Preferably, the watermark 7 corresponds to a screened watermark or a clear watermark, having a degree of transparency sufficient to allow the observation of the article through it. In particular, the watermark 7 may have a maximum depth ranging from 50 to 90% of the vellum.
On a représenté sur la figure 10 un exemple d'article 1 comportant un élément de sécurité 2 selon la figure 7 ou 8.  FIG. 10 shows an example of article 1 comprising a security element 2 according to FIG. 7 or 8.
L'article 1 correspond dans cet exemple à une bouteille, par exemple à une bouteille de vin comportant par exemple un vin rouge présentant une teinte suffisamment foncée pour permettre l'observation de la couleur du vin au travers du filigrane ou pseudo- filigrane 7.  In this example, article 1 corresponds to a bottle, for example a bottle of wine comprising, for example, a red wine having a hue dark enough to allow the observation of the color of the wine through the watermark or pseudo-watermark 7.
La figure 10 représente plus particulièrement l'observation de la bouteille 1 sous éclairage normal, c'est-à-dire à la lumière du jour. Dans ce cas, la poudre pigmentaire peut être incolore et l'on peut voir qu'il est possible d'observer la couleur rouge du vin contenu dans la bouteille 1 au niveau du filigrane ou pseudo-filigrane 7.  Figure 10 shows more particularly the observation of the bottle 1 under normal lighting, that is to say in the light of day. In this case, the pigment powder may be colorless and it can be seen that it is possible to observe the red color of the wine contained in the bottle 1 at the level of the watermark or pseudo-watermark 7.
La figure 11 représente la bouteille 1 et l'élément de sécurité 2 de la figure 10 dans le cas d'une observation sous un éclairage adapté permettant une variation de couleur de la poudre pigmentaire. Dans ce cas, on peut voir qu'il est possible d'observer à la fois la couleur rouge du vin contenu dans la bouteille 1 au niveau du filigrane ou pseudo-filigrane 7 mais également la couleur de la poudre pigmentaire.  FIG. 11 shows the bottle 1 and the security element 2 of FIG. 10 in the case of observation under a suitable illumination allowing a color variation of the pigment powder. In this case, it can be seen that it is possible to observe both the red color of the wine contained in the bottle 1 at the watermark or pseudo-watermark 7 but also the color of the pigment powder.
De la sorte, il est ainsi possible d'obtenir deux niveaux de sécurité à la fois par observation de la couleur de l'opacité de l'article 1 au travers du filigrane ou pseudofiligrane 7 par observation sous éclairage normal, et également par observation de la poudre pigmentaire, éventuellement en combinaison ayec la couleur ou l'opacité de l'article 1 , par observation sous un éclairage adapté,  In this way, it is thus possible to obtain two levels of security at a time by observing the color of the opacity of the article 1 through the watermark or pseudofiligrane 7 by observation under normal lighting, and also by observation of the pigment powder, optionally in combination with the color or opacity of the article 1, by observation under suitable lighting,
Dans toute la description, y compris les revendications, les expressions Throughout the description, including the claims, the expressions
« comportant un » ou « possédant un » doivent respectivement être comprises comme étant synonyme de « comportant au moins un » ou « possédant au moins un », sauf si le contraire est spécifié. "Comprising" or "possessing" must respectively be understood as being synonymous with "having at least one" or "having at least one", unless the contrary is specified.

Claims

REVENDICATIONS
1. Poudre pigmentaire à base de lanthanide(s), caractérisée en ce que ledit Ianthanide y est présent à l'état de nanoparticules d'hydroxyde, d'oxyde et/ou d'oxohydroxyde de Ianthanide, Iesdites nanoparticules présentant une taille inférieure à 200 nm, possédant une densité supérieure à 6 et étant formées à plus de 65 % massique en élément Ianthanide, ledit Ianthanide étant choisi parmi l'holmium, le néodyme et leurs mélanges. 1. Powder pigment based on lanthanide (s), characterized in that said lanthanide is present in the state of nanoparticles of hydroxide, oxide and / or oxohydroxide of lanthanide, said nanoparticles having a size less than 200 nm, having a density greater than 6 and being formed at more than 65 wt% of lanthanide element, said lanthanide being chosen from holmium, neodymium and mixtures thereof.
2. Poudre selon la revendication 3 , dans laquelle Iesdites nanoparticules sont formées à plus de 75 % massique, notamment plus de 85 % massique en élément Ianthanide.  2. The powder according to claim 3, wherein said nanoparticles are formed at more than 75% by weight, in particular more than 85% by mass of lanthanide element.
3. Poudre selon la revendication 1 ou 2, dans laquelle Iesdites nanoparticules possèdent une densité supérieure à 7.  3. The powder of claim 1 or 2, wherein said nanoparticles have a density greater than 7.
4. Poudre selon l'une quelconque des revendications précédentes, dans laquelle Iesdites nanoparticules présentent une taille inférieure à 100 nm, notamment variant de 50 à 100 nm.  4. Powder according to any one of the preceding claims, wherein said nanoparticles have a size less than 100 nm, in particular ranging from 50 to 100 nm.
5. Poudre selon l'une quelconque des revendications précédentes, dans laquelle ledit Ianthanide est l'holmium.  The powder according to any one of the preceding claims, wherein said lanthanide is holmium.
6. Poudre selon la revendication précédente, dans laquelle ledit holmium est présent à l'état d'oxyde.  6. Powder according to the preceding claim, wherein said holmium is present in the oxide state.
7. Poudre selon Tune quelconque des revendications précédentes, dans laquelle Iesdites nanoparticules présentent un spectre d'absorption montrant un pic d'absorption localisé entre 530 et 560 nm, notamment entre 540 et 555 nm.  7. The powder according to any one of the preceding claims, wherein said nanoparticles have an absorption spectrum showing an absorption peak located between 530 and 560 nm, in particular between 540 and 555 nm.
8. Elément de sécurité comportant une poudre pigmentaire selon l'une quelconque des revendications précédentes.  8. Security element comprising a pigment powder according to any one of the preceding claims.
9. Elément selon la revendication précédente, caractérisé en ce qu'il se présente sous la forme d'une composition de revêtement, d'une encre, d'un adhésif, d'une particule, d'une fibre, d'un fil ou d'une bande de sécurité, d'un fil textile, d'une planchette, d'un film de sécurité, d'un patch, d'un foil ou d'un laminât.  9. Element according to the preceding claim, characterized in that it is in the form of a coating composition, an ink, an adhesive, a particle, a fiber, a wire or a safety band, a textile thread, a board, a security film, a patch, a foil or a laminate.
10. Elément selon la revendication précédente, caractérisé en ce qu'il se présente sous la forme d'un fil ou d'une bande de sécurité, d'une planchette, d'un foil, d'un laminât ou d'un patch et en ce qu'il comporte une couche métallisée présentant des zones démétallisées et une couche comprenant ladite poudre pigmentaire. 10. Element according to the preceding claim, characterized in that it is in the form of a wire or a safety band, a board, a foil, laminate or patch and that it comprises a metallized layer having demetallized zones and a layer comprising said pigment powder.
1 1. Elément de sécurité selon l'une quelconque des revendications 8 à 10, comprenant en outre un agent de marquage, notamment un agent luminescent, par exemple un pigment fluorescent, un pigment phosphorescent, un pigment à effet interfèrent] el.  A security element according to any one of claims 8 to 10, further comprising a marking agent, especially a luminescent agent, for example a fluorescent pigment, a phosphorescent pigment, an interfering pigment and the like.
12. Article comportant un élément de sécurité selon l'une quelconque des revendications 8 à 11.  An article comprising a security element according to any one of claims 8 to 11.
13. Article selon la revendication précédente, comportant ledit élément de sécurité sous forme d'une impression ou d'une couche sur au moins l'une de ses faces ou sous forme d'un élément avec un support tel qu'un patch, un foil, un laminât, un fil ou une bande de sécurité, des planchettes, un film de sécurité ou une pochette de sécurité.  13. Article according to the preceding claim, comprising said security element in the form of an impression or a layer on at least one of its faces or in the form of an element with a support such as a patch, a foil, laminate, wire or safety tape, boards, safety film or security pouch.
14. Article selon l'une des revendications 12. et 13, se présentant sous la forme d'un document de sécurité, choisi notamment parmi les documents d'identité, en particulier une carte d'identité ou un passeport, les moyens de paiement, en particulier les billets de banque ou les chèques, les tickets d'entrée à des manifestations culturelles ou sportives et les billets de transports. 14. Article according to one of claims 12 . and 13, in the form of a security document, chosen in particular from identity documents, in particular an identity card or a passport, the means of payment, in particular banknotes or checks, entrance tickets to cultural or sports events and transport tickets.
15. Procédé de sécurisation d'un article comportant les étapes suivantes : c) disposer d'une poudre selon l'une quelconque des revendications 1 à 7 et/ou d'un élément de sécurité selon l'une quelconque des revendications 8 à 11, et  15. A method of securing an article comprising the following steps: c) providing a powder according to any one of claims 1 to 7 and / or a security element according to any one of claims 8 to 11; , and
d) incorporer ou transférer, au moins partiellement, ladite poudre et/ou ledit élément de sécurité dans ou sur l'article.  d) at least partially incorporating or transferring said powder and / or said security element into or onto the article.
16. Procédé selon la revendication précédente, dans lequel ledit article est un matériau cellulosique, de préférence une feuille et ladite poudre est apposée en surface dudit matériau sous la forme d'une encre, via une technique d'impression choisie parmi l'impression offset, la sérigraphie, la flexographie, l'héliogravure et/ou la typographie.  16. Method according to the preceding claim, wherein said article is a cellulosic material, preferably a sheet and said powder is affixed on the surface of said material in the form of an ink, via a printing technique chosen from offset printing. , screen printing, flexography, rotogravure and / or typography.
17. Procédé selon la revendication 15, dans lequel ledit article est un matériau cellulosique, de préférence, une feuille et ladite poudre est déposée en surface de ladite feuille via une composition de couchage ou de surfaçage l'incorporant.  The method of claim 15, wherein said article is a cellulosic material, preferably a sheet and said powder is deposited on the surface of said sheet via a coating or surfacing composition incorporating it.
18. Procédé selon la revendication précédente, dans lequel ladite poudre est mise en œuvre sous la forme d'un fil ou d'une bande de sécurité, d'une fibre de sécurité, d'une planchette et/ou d'une particule l'incorporant. 18. Method according to the preceding claim, wherein said powder is implemented in the form of a thread or a safety band, a safety fiber, a board and / or a particle. incorporating it.
19. Procédé d'authentification d'un article selon l'une des revendications 12 à 14, comportant les étapes consistant à : 19. The method of authenticating an article according to one of claims 12 to 14, comprising the steps of:
a) observer l'élément de sécurité sous un éclairage à spectre continu du type lumière du jour ou incandescent et sous un éclairage à raies d'émission du type fluorescent,  (a) observe the security element under daylight or incandescent type continuous-spectrum lighting and under fluorescent-type emission line illumination,
b) conclure quant à l'authenticité de l'article au moins en fonction du métamérisme observé.  b) conclude as to the authenticity of the article at least according to the observed metamerism.
20. Procédé selon la revendication précédente, dans lequel on utilise un détecteur comportant au moins deux illuminants pour authentifier l'article : un premier illuminant inactif sur la poudre pigmentaire et un deuxième illuminant permettant de révéler le comportement métamérique de la poudre pigmentaire.  20. Method according to the preceding claim, wherein using a detector comprising at least two illuminants to authenticate the article: a first inactive illuminant on the pigment powder and a second illuminant to reveal the metameric behavior of the pigment powder.
PCT/IB2010/055886 2009-12-17 2010-12-16 Pigment powder comprising lanthanides WO2011073944A1 (en)