WO2011028480A2 - Ophthalmic and otorhinolaryngological device materials - Google Patents
Ophthalmic and otorhinolaryngological device materials Download PDFInfo
- Publication number
- WO2011028480A2 WO2011028480A2 PCT/US2010/046345 US2010046345W WO2011028480A2 WO 2011028480 A2 WO2011028480 A2 WO 2011028480A2 US 2010046345 W US2010046345 W US 2010046345W WO 2011028480 A2 WO2011028480 A2 WO 2011028480A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- nothing
- och
- methacrylate
- device material
- formula
- Prior art date
Abstract
Description
Claims