WO2011025931A1 - A fuel cell composite flow field element and method of forming the same - Google Patents
A fuel cell composite flow field element and method of forming the same Download PDFInfo
- Publication number
- WO2011025931A1 WO2011025931A1 PCT/US2010/046935 US2010046935W WO2011025931A1 WO 2011025931 A1 WO2011025931 A1 WO 2011025931A1 US 2010046935 W US2010046935 W US 2010046935W WO 2011025931 A1 WO2011025931 A1 WO 2011025931A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- flow field
- fuel cell
- field element
- element according
- cell composite
- Prior art date
Abstract
Description
Claims